ASTM E740/E740M-03(2016)
(Practice)Standard Practice for Fracture Testing with Surface-Crack Tension Specimens
Standard Practice for Fracture Testing with Surface-Crack Tension Specimens
SIGNIFICANCE AND USE
4.1 The surface-crack tension (SCT) test is used to estimate the load-carrying capacity of simple sheet- or plate-like structural components having a type of flaw likely to occur in service. The test is also used for research purposes to investigate failure mechanisms of cracks under service conditions.
4.2 The residual strength of an SCT specimen is a function of the crack depth and length and the specimen thickness as well as the characteristics of the material. This relationship is extremely complex and cannot be completely described or characterized at present.
4.2.1 The results of the SCT test are suitable for direct application to design only when the service conditions exactly parallel the test conditions. Some methods for further analysis are suggested in Appendix X1.
4.3 In order that SCT test data can be comparable and reproducible and can be correlated among laboratories, it is essential that uniform SCT testing practices be established.
4.4 The specimen configuration, preparation, and instrumentation described in this practice are generally suitable for cyclic- or sustained-force testing as well. However, certain constraints are peculiar to each of these tests. These are beyond the scope of this practice but are discussed in Ref. (1).
SCOPE
1.1 This practice covers the design, preparation, and testing of surface-crack tension (SCT) specimens. It relates specifically to testing under continuously increasing force and excludes cyclic and sustained loadings. The quantity determined is the residual strength of a specimen having a semielliptical or circular-segment fatigue crack in one surface. This value depends on the crack dimensions and the specimen thickness as well as the characteristics of the material.
1.2 Metallic materials that can be tested are not limited by strength, thickness, or toughness. However, tests of thick specimens of tough materials may require a tension test machine of extremely high capacity. The applicability of this practice to nonmetallic materials has not been determined.
1.3 This practice is limited to specimens having a uniform rectangular cross section in the test section. The test section width and length must be large with respect to the crack length. Crack depth and length should be chosen to suit the ultimate purpose of the test.
1.4 Residual strength may depend strongly upon temperature within a certain range depending upon the characteristics of the material. This practice is suitable for tests at any appropriate temperature.
1.5 Residual strength is believed to be relatively insensitive to loading rate within the range normally used in conventional tension tests. When very low or very high rates of loading are expected in service, the effect of loading rate should be investigated using special procedures that are beyond the scope of this practice.
Note 1: Further information on background and need for this type of test is given in the report of ASTM Task Group E24.01.05 on Part-Through-Crack Testing (1).2
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Buy Standard
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: E740/E740M − 03 (Reapproved 2016)
Standard Practice for
1
Fracture Testing with Surface-Crack Tension Specimens
This standard is issued under the fixed designation E740/E740M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope each system may not be exact equivalents; therefore, each
system shall be used independently of the other. Combining
1.1 This practice covers the design, preparation, and testing
values from the two systems may result in non-conformance
of surface-crack tension (SCT) specimens. It relates specifi-
with the standard.
cally to testing under continuously increasing force and ex-
1.7 This standard does not purport to address all of the
cludes cyclic and sustained loadings. The quantity determined
safety concerns, if any, associated with its use. It is the
istheresidualstrengthofaspecimenhavingasemiellipticalor
responsibility of the user of this standard to establish appro-
circular-segment fatigue crack in one surface. This value
priate safety and health practices and determine the applica-
dependsonthecrackdimensionsandthespecimenthicknessas
bility of regulatory limitations prior to use.
well as the characteristics of the material.
1.2 Metallic materials that can be tested are not limited by
2. Referenced Documents
strength, thickness, or toughness. However, tests of thick
3
2.1 ASTM Standards:
specimens of tough materials may require a tension test
E4Practices for Force Verification of Testing Machines
machine of extremely high capacity. The applicability of this
E8/E8MTest Methods for Tension Testing of Metallic Ma-
practice to nonmetallic materials has not been determined.
terials
1.3 This practice is limited to specimens having a uniform
E338Test Method of Sharp-Notch Tension Testing of High-
rectangular cross section in the test section. The test section
4
Strength Sheet Materials (Withdrawn 2010)
widthandlengthmustbelargewithrespecttothecracklength.
E399Test Method for Linear-Elastic Plane-Strain Fracture
Crack depth and length should be chosen to suit the ultimate
Toughness K of Metallic Materials
Ic
purpose of the test.
E466Practice for Conducting Force Controlled Constant
1.4 Residual strength may depend strongly upon tempera-
Amplitude Axial Fatigue Tests of Metallic Materials
ture within a certain range depending upon the characteristics
E561Test Method forK Curve Determination
R
of the material. This practice is suitable for tests at any
E1823TerminologyRelatingtoFatigueandFractureTesting
appropriate temperature.
3. Terminology
1.5 Residual strength is believed to be relatively insensitive
to loading rate within the range normally used in conventional
3.1 Definitions:
tension tests. When very low or very high rates of loading are
3.1.1 Definitions given in Terminology E1823 are appli-
expected in service, the effect of loading rate should be
cable to this practice.
investigatedusingspecialproceduresthatarebeyondthescope
3.1.2 crack mouth opening displacement (CMOD), 2v
m
of this practice.
(L)—crack—opening displacement resulting from the total
deformation (elastic plus plastic) measured under force at the
NOTE 1—Further information on background and need for this type of
test is given in the report of ASTM Task Group E24.01.05 on Part- location on the crack surface that has the largest displacement
2
Through-Crack Testing (1).
per unit force.
1.6 The values stated in either SI units or inch-pound units
NOTE 2—In surface-crack tension (SCT) specimens, CMOD is mea-
are to be regarded separately as standard. The values stated in
sured on the specimen surface along the normal bisector of the crack
length.
1
ThispracticeisunderthejurisdictionofASTMCommitteeE08onFatigueand
Fracture and is the direct responsibility of Subcommittee E08.07 on Fracture
3
Mechanics. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Oct. 1, 2016. Published October 2016. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1988. Last previous edition approved in 2010 as E740/ Standards volume information, refer to the standard’s Document Summary page on
ɛ2
E740M–03(2010) . DOI: 10.1520/E0740_E0740M-03R16. the ASTM website.
2 4
Theboldfacenumbersinparenthesesrefertothelistofreferencesattheendof The last approved version of this historical standard is referenced on
this standard. www.astm.org.
Copyright © ASTM International, 100 Barr Harbor
...
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: E740/E740M − 03 (Reapproved 2016)
Standard Practice for
1
Fracture Testing with Surface-Crack Tension Specimens
This standard is issued under the fixed designation E740/E740M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope each system may not be exact equivalents; therefore, each
system shall be used independently of the other. Combining
1.1 This practice covers the design, preparation, and testing
values from the two systems may result in non-conformance
of surface-crack tension (SCT) specimens. It relates specifi-
with the standard.
cally to testing under continuously increasing force and ex-
1.7 This standard does not purport to address all of the
cludes cyclic and sustained loadings. The quantity determined
safety concerns, if any, associated with its use. It is the
is the residual strength of a specimen having a semielliptical or
responsibility of the user of this standard to establish appro-
circular-segment fatigue crack in one surface. This value
priate safety and health practices and determine the applica-
depends on the crack dimensions and the specimen thickness as
bility of regulatory limitations prior to use.
well as the characteristics of the material.
1.2 Metallic materials that can be tested are not limited by
2. Referenced Documents
strength, thickness, or toughness. However, tests of thick
3
2.1 ASTM Standards:
specimens of tough materials may require a tension test
E4 Practices for Force Verification of Testing Machines
machine of extremely high capacity. The applicability of this
E8/E8M Test Methods for Tension Testing of Metallic Ma-
practice to nonmetallic materials has not been determined.
terials
1.3 This practice is limited to specimens having a uniform
E338 Test Method of Sharp-Notch Tension Testing of High-
rectangular cross section in the test section. The test section
4
Strength Sheet Materials (Withdrawn 2010)
width and length must be large with respect to the crack length.
E399 Test Method for Linear-Elastic Plane-Strain Fracture
Crack depth and length should be chosen to suit the ultimate
Toughness K of Metallic Materials
Ic
purpose of the test.
E466 Practice for Conducting Force Controlled Constant
1.4 Residual strength may depend strongly upon tempera-
Amplitude Axial Fatigue Tests of Metallic Materials
ture within a certain range depending upon the characteristics
E561 Test Method forK Curve Determination
R
of the material. This practice is suitable for tests at any
E1823 Terminology Relating to Fatigue and Fracture Testing
appropriate temperature.
3. Terminology
1.5 Residual strength is believed to be relatively insensitive
to loading rate within the range normally used in conventional
3.1 Definitions:
tension tests. When very low or very high rates of loading are
3.1.1 Definitions given in Terminology E1823 are appli-
expected in service, the effect of loading rate should be
cable to this practice.
investigated using special procedures that are beyond the scope
3.1.2 crack mouth opening displacement (CMOD), 2v
m
of this practice.
(L)—crack—opening displacement resulting from the total
deformation (elastic plus plastic) measured under force at the
NOTE 1—Further information on background and need for this type of
test is given in the report of ASTM Task Group E24.01.05 on Part- location on the crack surface that has the largest displacement
2
Through-Crack Testing (1).
per unit force.
1.6 The values stated in either SI units or inch-pound units
NOTE 2—In surface-crack tension (SCT) specimens, CMOD is mea-
are to be regarded separately as standard. The values stated in
sured on the specimen surface along the normal bisector of the crack
length.
1
This practice is under the jurisdiction of ASTM Committee E08 on Fatigue and
Fracture and is the direct responsibility of Subcommittee E08.07 on Fracture
3
Mechanics. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Oct. 1, 2016. Published October 2016. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1988. Last previous edition approved in 2010 as E740/ Standards volume information, refer to the standard’s Document Summary page on
ɛ2
E740M – 03(2010) . DOI: 10.1520/E0740_E0740M-03R16. the ASTM website.
2 4
The boldface numbers in parentheses refer to the list of references at the end of The last approved version of this historical standard is referenced on
this standard. www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´2
Designation: E740/E740M − 03 (Reapproved 2010) E740/E740M − 03 (Reapproved 2016)
Standard Practice for
1
Fracture Testing with Surface-Crack Tension Specimens
This standard is issued under the fixed designation E740/E740M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1
ε NOTE—The units statement (1.6) and the designation were editorially revised in January 2011.
2
ε NOTE—3.1.2 was editorially revised in May 2013.
1. Scope
1.1 This practice covers the design, preparation, and testing of surface-crack tension (SCT) specimens. It relates specifically to
testing under continuously increasing force and excludes cyclic and sustained loadings. The quantity determined is the residual
strength of a specimen having a semielliptical or circular-segment fatigue crack in one surface. This value depends on the crack
dimensions and the specimen thickness as well as the characteristics of the material.
1.2 Metallic materials that can be tested are not limited by strength, thickness, or toughness. However, tests of thick specimens
of tough materials may require a tension test machine of extremely high capacity. The applicability of this practice to nonmetallic
materials has not been determined.
1.3 This practice is limited to specimens having a uniform rectangular cross section in the test section. The test section width
and length must be large with respect to the crack length. Crack depth and length should be chosen to suit the ultimate purpose
of the test.
1.4 Residual strength may depend strongly upon temperature within a certain range depending upon the characteristics of the
material. This practice is suitable for tests at any appropriate temperature.
1.5 Residual strength is believed to be relatively insensitive to loading rate within the range normally used in conventional
tension tests. When very low or very high rates of loading are expected in service, the effect of loading rate should be investigated
using special procedures that are beyond the scope of this practice.
NOTE 1—Further information on background and need for this type of test is given in the report of ASTM Task Group E24.01.05 on
2
Part-Through-Crack Testing (1).
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
3
2.1 ASTM Standards:
E4 Practices for Force Verification of Testing Machines
E8E8/E8M Test Methods for Tension Testing of Metallic Materials
4
E338 Test Method of Sharp-Notch Tension Testing of High-Strength Sheet Materials (Withdrawn 2010)
E399 Test Method for Linear-Elastic Plane-Strain Fracture Toughness K of Metallic Materials
Ic
E466 Practice for Conducting Force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Materials
E561 Test Method forK Curve Determination
R
1
This practice is under the jurisdiction of ASTM Committee E08 on Fatigue and Fracture and is the direct responsibility of Subcommittee E08.07 on Fracture Mechanics.
Current edition approved Oct. 1, 2010Oct. 1, 2016. Published January 2011October 2016. Originally approved in 1988. Last previous edition approved in 20032010 as
ɛ2
E740 – 03.E740/E740M – 03(2010) . DOI: 10.1520/E0740-03R10E02.10.1520/E0740_E0740M-03R16.
2
The boldface numbers in parentheses refer to the list of references at the end of this standard.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
The last approved version of this historical standard is referenced on www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ------------------
...
Questions, Comments and Discussion