Standard Test Method for Nonvolatile Content of Liquid Phenol, Resorcinol, and Melamine Adhesives

ABSTRACT
This test method covers the determination of nonvolatile content or total solids of liquid phenol, resorcinol, and melamine adhesives with or without hardener added and containing high-boiling and low-boiling volatile organic solvents or water, or both. The equipments to be used in the test shall include a petri dish, circulating-air oven, desiccator, and analytical balance. In determining the nonvolatile content of the liquid adhesives without hardener, the procedure shall include oven-drying, cooling in a desiccator, and weighing of adhesive and quartz sand . The percent nonvolatile content shall be calculated based on the amount remaining. On the other hand, the procedure for the liquid adhesives with hardener shall include oven-drying, cooling in a desiccator, and weighing of mixed adhesives. Also, the percent nonvolatile content shall be calculated based on the amount remaining.
SCOPE
1.1 This test method covers the determination of nonvolatile content or total solids of liquid phenol, resorcinol, and melamine adhesives with or without hardener (Note 1) added and containing high-boiling and low-boiling volatile organic solvents or water, or both.
Note 1—Some low molecular weight materials in the adhesive may be lost if hardener is not used. When a hardener is used, it must be mixed in accordance with the manufacturer's instructions.
1.2 The values stated in SI units are to be regarded as the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific precautions, see 5.2.

General Information

Status
Historical
Publication Date
31-Mar-2004
Technical Committee
Drafting Committee
Current Stage
Ref Project

Relations

Buy Standard

Standard
ASTM D1582-98(2004) - Standard Test Method for Nonvolatile Content of Liquid Phenol, Resorcinol, and Melamine Adhesives
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D1582–98(Reapproved2004)
Standard Test Method for
Nonvolatile Content of Liquid Phenol, Resorcinol, and
Melamine Adhesives
This standard is issued under the fixed designation D1582; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 4.2 With Hardener—A weighed amount of mixed adhesive
is oven dried, cooled in a desiccator, and weighed. The percent
1.1 This test method covers the determination of nonvolatile
nonvolatile content is calculated based on the amount remain-
content or total solids of liquid phenol, resorcinol, and
ing.
melamine adhesives with or without hardener (Note 1) added
and containing high-boiling and low-boiling volatile organic
5. Apparatus
solvents or water, or both.
5.1 Petri Dish, 100 by 22 mm or its equivalent.
NOTE 1—Some low molecular weight materials in the adhesive may be
5.2 Circulating-Air Oven, capable of maintaining tempera-
lost if hardener is not used. When a hardener is used, it must be mixed in
tures of 70 6 1°C, 105 6 1°C, and 150 6 1°C. (Warning—A
accordance with the manufacturer’s instructions.
safety (explosion-proof) oven should be used when volatile
1.2 The values stated in SI units are to be regarded as the
materials are likely to burn or explode.)
standard.
5.3 Desiccator, with drying agent and tray.
1.3 This standard does not purport to address all of the
5.4 Analytical Balance, accurate to 1 mg.
safety concerns, if any, associated with its use. It is the
6. Sampling
responsibility of the user of this standard to establish appro-
priate safety and health practices and determine the applica-
6.1 Except in special cases, take a composite sample from
bility of regulatory limitations prior to use. For specific
three or more separate containers chosen at random.Also, take
precautions, see 5.2.
samples from containers which appear to be nonrepresentative
and test such samples separately. Place the samples immedi-
2. Referenced Documents
ately in airtight containers, filled to prevent excessive air space
2.1 ASTM Standards:
above the adhesive, and take precautions to reduce evaporation
D907 Terminology of Adhesives
or drying to a minimum. Mix the adhesive in the container
thoroughly if there is a tendency for the materials to separate.
3. Terminology
6.2 Test three specimens of each sample.
3.1 Definitions—Many of the terms in this test method are
7. Procedure
defined in Terminology D907.
7.1 70°C Drying Temperature Without Hardener:
4. Summary of Test Method
7.1.1 Place approximately 20 g of the adhesive in a covered
4.1 Without Hardener—A weighed amount of adhesive and
weighing bottle.
quartz sand are oven-dried, cooled in a desiccator, and
7.1.2 Place approximately 10 g of fine, oven-dried quartz
weighed. The percent nonvolatile content is calculated based
sand in an open Petri dish, together with a small glass stirring
on the amount remaining.
rod, and weigh the dish, rod, and contents to the nearest 1 mg
on the analytical balance. Weigh out to the nearest 1 mg
approximately2gofthe adhesive by difference from the
This test method is under the jurisdiction of ASTM Committee D14 on
Adhesives and is the direct responsibility of Subcommittee D 14.30 on Wood
weighing bottle, keeping the bottle covered as much as
Adhesives.
possible. Mix the adhesive and quartz sand intimately by
Current edition approved April 1, 2004. Published April 2004. Originally
means of the stirring rod and distribute uniformly over the
approved in 1958. Last previous edition approved in 1998 as D1582 – 98. DOI:
10.1520/D1582-98R04. b
...