ASTM D5449/D5449M-16

(Test Method)

Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders

Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is designed to produce transverse compressive property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the transverse compressive response and should therefore be reported are: material, method of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties in the test direction that may be obtained from this test method are:  
5.1.1 Transverse compressive strength, σ22uc,  
5.1.2 Transverse compressive strain at failure, ε22uc,  
5.1.3 Transverse compressive modulus of elasticity, E22, and  
5.1.4 Poisson's ratio, γ21.
SCOPE
1.1 This test method determines the transverse compressive properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial compression for determination of transverse compressive properties.  
1.2 The technical content of this standard has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this standard, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The standard, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the standard will only be in response to specific requests and performed only as technical support allows.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3.1 Within the text the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Jun-2016
ICS
83.140.20 - Laminated sheets
Technical Committee
D30 - Composite Materials
Drafting Committee
D30.04 - Lamina and Laminate Test Methods
Current Stage
Ref Project

Buy Standard

ASTM D5449/D5449M-16 - Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite CylindersASTM D5449/D5449M-16 - Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders
PreviousNext
Standard
ASTM D5449/D5449M-16 - Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders
English language
10 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM D5449/D5449M-16 - Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite CylindersREDLINE ASTM D5449/D5449M-16 - Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders
PreviousNext
Standard
REDLINE ASTM D5449/D5449M-16 - Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders
English language
10 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D5449/D5449M − 16
Standard Test Method for
Transverse Compressive Properties of Hoop Wound
1
Polymer Matrix Composite Cylinders
This standard is issued under the fixed designation D5449/D5449M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope 2. Referenced Documents
2
1.1 This test method determines the transverse compressive 2.1 ASTM Standards:
D792Test Methods for Density and Specific Gravity (Rela-
properties of wound polymer matrix composites reinforced by
tive Density) of Plastics by Displacement
high-modulus continuous fibers. It describes testing of hoop
D883Terminology Relating to Plastics
wound (90°) cylinders in axial compression for determination
D2584Test Method for Ignition Loss of Cured Reinforced
of transverse compressive properties.
Resins
1.2 The technical content of this standard has been stable
D2734TestMethodsforVoidContentofReinforcedPlastics
since 1993 without significant objection from its stakeholders.
D3171Test Methods for Constituent Content of Composite
Asthereislimitedtechnicalsupportforthemaintenanceofthis
Materials
standard, changes since that date have been limited to items
D3878Terminology for Composite Materials
required to retain consistency with otherASTM D30 Commit-
D5229/D5229MTestMethodforMoistureAbsorptionProp-
tee standards, including editorial changes and incorporation of
erties and Equilibrium Conditioning of Polymer Matrix
updated guidance on specimen preconditioning and environ-
Composite Materials
mental testing. The standard, therefore, should not be consid-
D5448/D5448MTest Method for Inplane Shear Properties
ered to include any significant changes in approach and of Hoop Wound Polymer Matrix Composite Cylinders
practice since 1993. Future maintenance of the standard will
D5450/D5450MTest Method for Transverse Tensile Prop-
only be in response to specific requests and performed only as
erties of Hoop Wound Polymer Matrix Composite Cylin-
technical support allows. ders
E4Practices for Force Verification of Testing Machines
1.3 The values stated in either SI units or inch-pound units
E6Terminology Relating to Methods of Mechanical Testing
are to be regarded separately as standard. The values stated in
E11Specification forWovenWireTest Sieve Cloth andTest
each system are not exact equivalents; therefore, each system
Sieves
must be used independently of the other. Combining values
E122PracticeforCalculatingSampleSizetoEstimate,With
from the two systems may result in nonconformance with the
Specified Precision, the Average for a Characteristic of a
standard.
Lot or Process
1.3.1 Within the text the inch-pound units are shown in
E132Test Method for Poisson’s Ratio at RoomTemperature
brackets.
E177Practice for Use of the Terms Precision and Bias in
ASTM Test Methods
1.4 This standard does not purport to address all of the
E251Test Methods for Performance Characteristics of Me-
safety concerns, if any, associated with its use. It is the
tallic Bonded Resistance Strain Gages
responsibility of the user of this standard to establish appro-
E456Terminology Relating to Quality and Statistics
priate safety and health practices and determine the applica-
E691Practice for Conducting an Interlaboratory Study to
bility of regulatory limitations prior to use.
Determine the Precision of a Test Method
E1237Guide for Installing Bonded Resistance Strain Gages
1
This test method is under the jurisdiction of ASTM Committee D30 on
Composite Materials and is the direct responsibility of Subcommittee D30.04 on
2
Lamina and Laminate Test Methods. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
CurrenteditionapprovedJuly1,2016.PublishedJuly2016.Originallyapproved contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
in 1993. Last previous edition approved in 2011 as D5449/D5449M–11. DOI: Standards volume information, refer to the standard’s Document Summary page on
10.1520/D5449_D5449M-16. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D5449/D5449M − 16
3. Terminology and development, quality assurance, and structural design and
analysis. Factors that influence the transverse compressive
3.1 Definitions—Terminology D3878 defines terms relating
response and should therefore be reported are: material,
to high-modulus fibers and their composites. Terminology
method of material preparation, specimen pre
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D5449/D5449M − 11 D5449/D5449M − 16
Standard Test Method for
Transverse Compressive Properties of Hoop Wound
1
Polymer Matrix Composite Cylinders
This standard is issued under the fixed designation D5449/D5449M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope
1.1 This test method determines the transverse compressive properties of wound polymer matrix composites reinforced by
high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial compression for determination of
transverse compressive properties.
1.2 The technical content of this standard has been stable since 1993 without significant objection from its stakeholders. As there
is limited technical support for the maintenance of this standard, changes since that date have been limited to items required to
retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance
on specimen preconditioning and environmental testing. The standard, therefore, should not be considered to include any
significant changes in approach and practice since 1993. Future maintenance of the standard will only be in response to specific
requests and performed only as technical support allows.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two
systems may result in nonconformance with the standard.
1.3.1 Within the text the inch-pound units are shown in brackets.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2
2.1 ASTM Standards:
D792 Test Methods for Density and Specific Gravity (Relative Density) of Plastics by Displacement
D883 Terminology Relating to Plastics
D2584 Test Method for Ignition Loss of Cured Reinforced Resins
D2734 Test Methods for Void Content of Reinforced Plastics
D3171 Test Methods for Constituent Content of Composite Materials
D3878 Terminology for Composite Materials
D5229/D5229M Test Method for Moisture Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite
Materials
D5448/D5448M Test Method for Inplane Shear Properties of Hoop Wound Polymer Matrix Composite Cylinders
D5450/D5450M Test Method for Transverse Tensile Properties of Hoop Wound Polymer Matrix Composite Cylinders
E4 Practices for Force Verification of Testing Machines
E6 Terminology Relating to Methods of Mechanical Testing
E11 Specification for Woven Wire Test Sieve Cloth and Test Sieves
E122 Practice for Calculating Sample Size to Estimate, With Specified Precision, the Average for a Characteristic of a Lot or
Process
1
This test method is under the jurisdiction of ASTM Committee D30 on Composite Materials and is the direct responsibility of Subcommittee D30.04 on Lamina and
Laminate Test Methods.
Current edition approved Nov. 15, 2011July 1, 2016. Published December 2011July 2016. Originally approved in 1993. Last previous edition approved in 20062011 as
D5449/D5449M – 93 (2006).D5449/D5449M – 11. DOI: 10.1520/D5449_D5449M-11.10.1520/D5449_D5449M-16.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D5449/D5449M − 16
E132 Test Method for Poisson’s Ratio at Room Temperature
E177 Practice for Use of the Terms Precision and Bias in ASTM Test Methods
E251 Test Methods for Performance Characteristics of Metallic Bonded Resistance Strain Gages
E456 Terminology Relating to Quality and Statistics
E691 Practice for Conducting an Interlaboratory Study to Determine the Precision o
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D3479/D3479M-19(2023)(Test Method)
Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 This test method is designed to yield tensile fatigue data for material specifications, research and development, quality assurance, and structural design and analysis. The primary test result is the fatigue life of the test specimen under a specific loading and environmental condition. Replicate tests may be used to obtain a distribution of fatigue life for specific material types, laminate stacking sequences, environments, and loading conditions. Guidance in statistical analysis of fatigue life data, such as determination of linearized stress life (S-N) or strain-life (ε-N) curves, can be found in Practice E739.  
5.2 This test method can be utilized in the study of fatigue damage in a polymer matrix composite such as the occurrence of microscopic cracks, fiber fractures, or delaminations.3 The specimen's residual strength or stiffness, or both, may change due to these damage mechanisms. The loss in stiffness may be quantified by discontinuing cyclic loading at selected cycle intervals to obtain the quasi-static axial stress-strain curve using modulus determination procedures found in Test Method D3039/D3039M. The loss in strength associated with fatigue damage may be determined by discontinuing cyclic loading to obtain the static strength using Test Method D3039/D3039M.  
Note 1: This test method may be used as a guide to conduct tension-tension variable amplitude loading. This information can be useful in the understanding of fatigue behavior of composite structures under spectrum loading conditions, but is not covered in this test method.
SCOPE
1.1 This test method determines the fatigue behavior of polymer matrix composite materials subjected to tensile cyclic loading. The composite material forms are limited to continuous-fiber or discontinuous-fiber reinforced composites for which the elastic properties are specially orthotropic with respect to the test direction. This test method is limited to unnotched test specimens subjected to constant amplitude uniaxial in-plane loading where the loading is defined in terms of a test control parameter.  
1.2 This test method presents two procedures where each defines a different test control parameter.  
1.2.1 Procedure A—A system in which the test control parameter is the load (stress) and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude load cycles. In this procedure, the test control parameter may be described using either engineering stress or applied load as a constant amplitude fatigue variable.  
1.2.2 Procedure B—A system in which the test control parameter is the strain in the loading direction and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude strain cycles. In this procedure, the test control parameter may be described using engineering strain in the loading direction as a constant amplitude fatigue variable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D4762-23(Guide)
Standard Guide for Testing Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
4.1 This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.
SCOPE
1.1 This guide summarizes the application of ASTM standard test methods (and other supporting standards) to continuous-fiber reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included, emphasizing use of standards of Committee D30 on Composite Materials.  
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including non-ASTM test methods, is included in the Composite Materials Handbook (CMH-17).2 Additional specific recommendations for testing textile (fabric, braided) composites are contained in Guide D6856.  
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards with SI units listed first.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    27 pages
    English language
    sale 15% off
  • Guide
    27 pages
    English language
    sale 15% off
ASTM
ASTM D8387/D8387M-23(Test Method)
Standard Test Method for High Bypass – Low Bearing Interaction Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This test method determines the uniaxial high bypass - low bearing interaction response of multi-directional polymer matrix composite laminates reinforced by high-modulus fibers using a two-fastener hard point joint specimen. The scope of this test method is limited to net section (bypass) failure modes. Standard specimen configurations using fixed values of test parameters are described for this procedure. A number of test parameters may be varied within the scope of the standard, provided that the parameters are fully documented in the test report. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced composites for which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1. This test method was previously published under Test Method D7248/D7248M-17 Procedure C.  
1.2 This test method is consistent with the recommendations of Composite Materials Handbook, CMH-17, which describes the desirable attributes of a bearing/bypass interaction response test method.  
1.3 The two-fastener test configurations described in this test method are intended to provide data in the relatively high bypass, low bearing part of the composite bolted joint bearing-bypass interaction diagram. This data complements the data from filled hole tension and compression (Practice D6742/D6742M), bearing (Test Method D5961/D5961M), and low bypass/high bearing interaction (Test Method D7248/D7248M) tests.  
1.4 This test method requires careful specimen design, instrumentation, data measurement, and data analysis. The use of this test method requires close coordination between the test requestor and the test lab personnel. Test requestors need to be familiar with the data analysis procedures of this test method and should not expect test labs who are unfamiliar with this test method to be able to produce acceptable results without close coordination.  
1.5 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5.1 Within the text, the inch-pound units are shown in brackets.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    27 pages
    English language
    sale 15% off
  • Standard
    27 pages
    English language
    sale 15% off
ASTM
ASTM D6873/D6873M-23(Practice)
Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This practice provides instructions for modifying static bearing test methods to determine the fatigue behavior of composite materials subjected to cyclic bearing forces. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.  
1.2 This practice supplements Test Method D5961/D5961M with provisions for testing specimens under cyclic loading. Several important test specimen parameters (for example, fastener selection, fastener installation method, and fatigue force/stress ratio) are not mandated by this practice; however, repeatable results require that these parameters be specified and reported.  
1.3 This practice is limited to test specimens subjected to constant amplitude uniaxial loading, where the machine is controlled so that the test specimen is subjected to repetitive constant amplitude force (stress) cycles. Either engineering stress or applied force may be used as a constant amplitude fatigue variable. The repetitive loadings may be tensile, compressive, or reversed, depending upon the test specimen and procedure utilized.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D8066/D8066M-23(Practice)
Standard Practice Unnotched Compression Testing of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This practice provides supplemental instructions for the use of Test Method D6484/D6484M to determine unnotched compressive strength data for material specifications, research and development, material design allowables, and quality assurance. Factors that influence compressive strengths and shall therefore be reported include the following: material, methods of material fabrication, accuracy of lay-up, laminate stacking sequence and overall thickness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Composite properties in the test direction that may be obtained from this test method include:  
5.1.1 Unnotched compressive (UNC) strength, Fxunc,  
5.1.2 Ultimate compressive strain,  
5.1.3 Compressive (linear or chord) modulus of elasticity, Ec, and  
5.1.4 Poisson's ratio in compression.  
5.2 This practice provides a compression test method for laminates containing fibers in multiple fiber directions, particularly those combining axial (0 degree) fibers and off-axis (± θ degree) fibers. Other compression strength test methods include SACMA SRM-1 (also known as the modified D695), D3410/D3410M, D5467/D5467M, D6641/D6641M, and D7249/D7249M. The SRM-1 test uses 12.6 mm [0.50 in.] wide specimens, which is only appropriate for unidirectional tape, cross-ply [0/90]ns tape, or small unit-cell-size fabrics (e.g. 3K-70-P). Larger cell-size fabrics (for example, spread-tow 12K fabrics) should be tested with wider specimens. The standard D3410/D3410M and D6641/D6641M test fixtures do permit the use of wider specimens, for example, 25.4 mm [1.0 in.] wide, and thus can be used to test laminates containing both axial and off-axis fibers; however their gage lengths are relatively short. Test Method D5467/D5467M is intended to obtain the compressive strength of unidirectional laminates, but is expensive due to the sandwich beam confi...
SCOPE
1.1 This practice provides instructions for using the Test Method D6484/D6484M open hole compression test fixture to determine unnotched compressive strength of multi-directional laminates. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.2.1 Within the text the inch-pound units are shown in brackets.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D8131/D8131M-23(Practice)
Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This test practice is designed to produce tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the tensile response and should therefore be reported include the following: materials (laminates and adhesive), methods of material preparation including surface preparation prior to bonding, lay-ups, specimen stacking sequence, joint taper ratio or step length, ply overlap length, material relative thicknesses and stiffness of the parent and repair laminates, adhesive bond stiffness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Properties in the test direction, which may be obtained from this test practice, include the following:  
5.1.1 Ultimate tensile strength (based on the nominal parent material thickness), (Fptu).  
5.1.2 Ultimate tensile strength (based on the nominal repair material thickness), (Frtu).  
5.1.3 Ultimate running force per repair ply, (Nj).
SCOPE
1.1 This test practice defines the procedure for determination of the tensile strength of a tapered or stepped joint of polymer matrix composite materials. It is applicable to secondary bonded or co-bonded laminates with either unidirectional plies or woven fabric reinforcements. The materials to be bonded may be different material systems. In the bondline, a separate adhesive material may or may not be used (example: adhesives may be used with a prepreg system or may not be used with a wet lay-up repair system). The range of acceptable test laminates and thicknesses is described in 8.2.1.  
1.2 This practice supplements Test Method D3039/D3039M for tensile loading. Several important test specimen parameters (for example, joint length, ply overlaps, step depth, and taper ratio) are not mandated by this practice, however, these parameters are required to be specified and reported to support repeatable results.  
1.3 Unidirectional (0° ply orientation) tape composites, textile composites, as well as multidirectional composite laminates, can be tested.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM D2344/D2344M-22(Test Method)
Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates

SIGNIFICANCE AND USE
5.1 In most cases, because of the complexity of internal stresses and the variety of failure modes that can occur in this specimen, it is not generally possible to relate the short-beam strength to any one material property. However, failures are normally dominated by resin and interlaminar properties, and the test results have been found to be repeatable for a given specimen geometry, material system, and stacking sequence  (4).  
5.2 Short-beam strength determined by this test method can be used for quality control and process specification purposes. It can also be used for comparative testing of composite materials, provided that failures occur consistently in the same mode (5) .  
5.3 This test method is not limited to specimens within the range specified in Section 8, but is limited to the use of a loading span length-to-specimen thickness ratio of 4.0 and a minimum specimen thickness of 2.0 mm [0.08 in.].
SCOPE
1.1 This test method determines the short-beam strength of high-modulus fiber-reinforced composite materials. The specimen is a short beam machined from a curved or a flat laminate up to 6.00 mm [0.25 in.] thick. The beam is loaded in three-point bending.  
1.2 Application of this test method is limited to continuous- or discontinuous-fiber-reinforced polymer matrix composites, for which the elastic properties are balanced and symmetric with respect to the longitudinal axis of the beam.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D5449/D5449M-22(Test Method)
Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is designed to produce transverse compressive property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the transverse compressive response and should therefore be reported are: material, method of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties in the test direction that may be obtained from this test method are:  
5.1.1 Transverse compressive strength, σ22uc,  
5.1.2 Transverse compressive strain at failure, ε22uc,  
5.1.3 Transverse compressive modulus of elasticity, E22, and  
5.1.4 Poisson's ratio, γ21.
SCOPE
1.1 This test method determines the transverse compressive properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial compression for determination of transverse compressive properties.  
1.2 The technical content of this test method has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this test method, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The test method, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the test method will only be in response to specific requests and performed only as technical support allows.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D5450/D5450M-22(Test Method)
Standard Test Method for Transverse Tensile Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is used to produce transverse tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors which influence the transverse tensile response and should, therefore, be reported are: material, methods of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties, in the test direction, which may be obtained from this test method include:  
5.1.1 Transverse Tensile Strength,    
5.1.2 Transverse Tensile Strain at Failure,    
5.1.3 Transverse Tensile Modulus of Elasticity,  E22, and  
5.1.4 Poisson's Ratio,  υ21.
SCOPE
1.1 This test method determines the transverse tensile properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial tension for determination of transverse tensile properties.  
1.2 The technical content of this test method has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this test method, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The test method, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the test method will only be in response to specific requests and performed only as technical support allows.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM E1922/E1922M-22(Test Method)
Standard Test Method for Translaminar Fracture Toughness of Laminated and Pultruded Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 The parameter KTL  determined by this test method is a measure of the resistance of a polymer matrix composite laminate to notch-tip damage and effective translaminar crack growth under opening mode loading. The result is valid only for conditions in which the damage zone at the notch tip is small compared with the notch length and the in-plane specimen dimensions. Alternately, for materials exhibiting distributed damage in a larger volume, observed force-displacement and discrete damage events are still valid structural responses for certain specific engineering applications.  
5.2 This test method can serve the following purposes. In research and development, (a) KTL data can quantitatively establish the effects of fiber and matrix variables and stacking sequence of the laminate on the translaminar fracture resistance of composite laminates; and (b) quantified distributed damage measurements can be used to validate progressive composite damage models. In structural design, KTL data can, within the constraints of the specimen geometry and loading, be used to assess composite laminate resistance to damage growth from edge flaws and notches.  
5.3 The translaminar fracture toughness,  KTL, as well as distributed damage observations, determined by this test method may be a function of the testing speed and temperature. This test method is intended for room temperature and quasi-static conditions, but it can apply to other test conditions provided that the requirements of 13.2 and 13.3 are met. Application of KTL in the design of service components should be made with awareness that the test parameters specified by this test may differ from service conditions, possibly resulting in a different material response than that seen in service. Distributed damage observations are also limited to the material and geometry tested, but may be more generally applied to a variety of structural analysis validation applications.  
5.4 Not all types of laminated polymer matrix...
SCOPE
1.1 This test method covers the determination of translaminar fracture toughness, KTL, for laminated, molded, or pultruded polymer matrix composite materials of various fiber orientations using test results from monotonically loaded notched specimens. If the material response is such that the KTL calculation is not valid, alternate reporting methods are provided.  
1.2 This test method is applicable to room temperature laboratory air environments.  
1.3 Composite materials that can be tested by this test method are not limited by thickness or by type of polymer matrix or fiber, provided that the specimen sizes and the test results meet the requirements of this test method. This test method was developed primarily from test results of various carbon fiber – epoxy matrix laminates and from additional results of glass fiber – epoxy matrix, glass fiber-polyester matrix pultrusions and carbon fiber – bismaleimide matrix laminates (1-4, 5, 6).2  
1.4 A range of eccentrically loaded, single-edge-notch tension, ESE(T), specimen sizes with proportional planar dimensions is provided, but planar size may be variable and adjusted, with associated changes in the applied test load. Specimen thickness is a variable, independent of planar size.  
1.5 Specimen configurations other than those contained in this test method may be used. It is particularly important that the requirements discussed in 5.1 and 5.4 regarding contained notch-tip damage be met when using alternative specimen configurations in conjunction with the KTL calculation.  
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.6.1 Within the text, the inch-pound units are shown ...

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off