ASTM D6108-24
(Test Method)Standard Test Method for Compressive Properties of Plastic Lumber and Shapes
Standard Test Method for Compressive Properties of Plastic Lumber and Shapes
SIGNIFICANCE AND USE
4.1 Compression tests provide information about the compressive properties of plastic lumber and shapes when these products are used under conditions approximating those under which the tests are made. In the case of some materials, there will be a specification that requires the use of this test method, but with some procedural modifications that take precedence when adhering to the specification. Therefore, it is advisable to refer to that material specification before using this test method. Table 1 in Classification D4000 lists the ASTM materials standards that currently exist.
4.2 Compressive properties include modulus of elasticity, secant modulus, compressive strength, and stress at a given strain. In the case of a material that fails in compression by a shattering fracture, the compressive strength has a very definite value. In the case of a material that does not fail in compression by a shattering fracture nor exhibits a compressive yield point, the compressive strength is an arbitrary one depending upon the degree of distortion that is regarded as indicating complete failure. Many plastic lumber materials will not exhibit a true yield point. Compressive strength can have no real meaning in such cases. For plastic lumber, the stress at a given strain of 3 % (0.03 in./in. (mm/mm)) is typically used.
4.3 Compression tests provide a standard method of obtaining data for research and development, quality control, acceptance or rejection under specifications, and special purposes. The tests cannot be considered significant for engineering design in applications differing widely from the load-time scale of the standard test. Such applications require additional tests such as impact, creep, and fatigue.
SCOPE
1.1 This test method covers the determination of the mechanical properties of plastic lumber and shapes, when the entire cross-section is loaded in compression at relatively low uniform rates of straining or loading. Test specimens in the “as-manufactured” form are employed. As such, this is a test method for evaluating the properties of plastic lumber or shapes as a product and not a material property test method.
Note 1: This test method was developed for application to plastic lumber materials, but it is generic enough that it would be equally applicable to other plastic composite materials, including wood-plastic composite materials.
1.2 Plastic lumber and plastic shapes are currently made predominantly with recycled plastics. However, this test method would also be applicable to similar manufactured plastic products made from virgin resins, or where the product is non-homogenous in the cross-section.
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 2: There is no known ISO equivalent to this test method.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Buy Standard
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D6108 − 24
Standard Test Method for
1
Compressive Properties of Plastic Lumber and Shapes
This standard is issued under the fixed designation D6108; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 2. Referenced Documents
2
2.1 ASTM Standards:
1.1 This test method covers the determination of the me-
chanical properties of plastic lumber and shapes, when the D618 Practice for Conditioning Plastics for Testing
D883 Terminology Relating to Plastics
entire cross-section is loaded in compression at relatively low
uniform rates of straining or loading. Test specimens in the D4000 Classification System for Specifying Plastic Materi-
als
“as-manufactured” form are employed. As such, this is a test
method for evaluating the properties of plastic lumber or D5033 Guide for Development of ASTM Standards Relating
to Recycling and Use of Recycled Plastics (Withdrawn
shapes as a product and not a material property test method.
3
2007)
NOTE 1—This test method was developed for application to plastic
D5947 Test Methods for Physical Dimensions of Solid
lumber materials, but it is generic enough that it would be equally
Plastics Specimens
applicable to other plastic composite materials, including wood-plastic
composite materials. D6111 Test Method for Bulk Density And Specific Gravity
of Plastic Lumber and Shapes by Displacement
1.2 Plastic lumber and plastic shapes are currently made
E4 Practices for Force Calibration and Verification of Test-
predominantly with recycled plastics. However, this test
ing Machines
method would also be applicable to similar manufactured
E83 Practice for Verification and Classification of Exten-
plastic products made from virgin resins, or where the product
someter Systems
is non-homogenous in the cross-section.
E456 Terminology Relating to Quality and Statistics
1.3 The values stated in inch-pound units are to be regarded
E691 Practice for Conducting an Interlaboratory Study to
as the standard. The values given in parentheses are for
Determine the Precision of a Test Method
information only.
E2935 Practice for Evaluating Equivalence of Two Testing
1.4 This standard does not purport to address all of the Processes
safety concerns, if any, associated with its use. It is the
3. Terminology
responsibility of the user of this standard to establish appro-
priate safety, health, and environmental practices and deter- 3.1 Definitions of Terms:
3.1.1 Definitions of terms applying to this test method
mine the applicability of regulatory limitations prior to use.
appear in Terminology D4000 and Guide D5033. For terms
NOTE 2—There is no known ISO equivalent to this test method.
relating to precision and bias and associated issues, the terms
1.5 This international standard was developed in accor-
used in this test method are in accordance with the definitions
dance with internationally recognized principles on standard-
in Terminology E456.
ization established in the Decision on Principles for the
3.1.2 plastic lumber, n—a manufactured product made pri-
Development of International Standards, Guides and Recom-
marily from plastic materials (filled or unfilled), typically used
mendations issued by the World Trade Organization Technical
as a building material for purposes similar to those of tradi-
Barriers to Trade (TBT) Committee.
tional lumber, which is usually rectangular in cross-section.
(Terminology D883)
1 2
This test method is under the jurisdiction of ASTM Committee D20 on Plastics For referenced ASTM standards, visit the ASTM website, www.astm.org, or
and is the direct responsibility of Subcommittee D20.20 on Plastic Lumber (Section contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
D20.20.01). Standards volume information, refer to the standard’s Document Summary page on
Current edition approved Feb. 1, 2024. Published February 2024. Originally the ASTM website.
3
approved in 1997. Last previous edition approved in 2019 as D6108 – 19. DOI: The last approved version of this historical standard is referenced on
10.1520/D6108-24. www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D6108 − 24
3.1.2.1 Discussion—Plastic lumber is typically supplied in 3.2.10 proportional limit—the greatest compressive st
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D6108 − 19 D6108 − 24
Standard Test Method for
1
Compressive Properties of Plastic Lumber and Shapes
This standard is issued under the fixed designation D6108; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This test method covers the determination of the mechanical properties of plastic lumber and shapes, when the entire
cross-section is loaded in compression at relatively low uniform rates of straining or loading. Test specimens in the
“as-manufactured” form are employed. As such, this is a test method for evaluating the properties of plastic lumber or shapes as
a product and not a material property test method.
NOTE 1—This test method was developed for application to plastic lumber materials, but it is generic enough that it would be equally applicable to other
plastic composite materials, including wood-plastic composite materials.
1.2 Plastic lumber and plastic shapes are currently made predominantly with recycled plastics. However, this test method would
also be applicable to similar manufactured plastic products made from virgin resins, or where the product is non-homogenous in
the cross-section.
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information
only.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of
regulatory limitations prior to use.
NOTE 2—There is no known ISO equivalent to this test method.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
D618 Practice for Conditioning Plastics for Testing
D883 Terminology Relating to Plastics
D4000 Classification System for Specifying Plastic Materials
1
This test method is under the jurisdiction of ASTM Committee D20 on Plastics and is the direct responsibility of Subcommittee D20.20 on Plastic Lumber (Section
D20.20.01).
Current edition approved May 1, 2019Feb. 1, 2024. Published May 2019February 2024. Originally approved in 1997. Last previous edition approved in 20182019 as
D6108 – 18.D6108 – 19. DOI: 10.1520/D6108-19.10.1520/D6108-24.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D6108 − 24
3
D5033 Guide for Development of ASTM Standards Relating to Recycling and Use of Recycled Plastics (Withdrawn 2007)
D5947 Test Methods for Physical Dimensions of Solid Plastics Specimens
D6111 Test Method for Bulk Density And Specific Gravity of Plastic Lumber and Shapes by Displacement
E4 Practices for Force Calibration and Verification of Testing Machines
E83 Practice for Verification and Classification of Extensometer Systems
E456 Terminology Relating to Quality and Statistics
E691 Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
E2935 Practice for Evaluating Equivalence of Two Testing Processes
3. Terminology
3.1 Definitions of Terms:
3.1.1 Definitions of terms applying to this test method appear in Terminology D4000 and Guide D5033. For terms relating to
precision and bias and associated issues, the terms used in this test method are in accordance with the definitions in Terminology
E456.
3.1.2 plastic lumber, n—a manufactured product made primarily from plastic materials (filled or unfilled), typically used as a
building material for purposes similar to those of traditional lumber, which is usually rectangular in cross-section. (Terminology
D883)
3.1.2.1 Discussion—
Plastic lumber is
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.