ABSTRACT
This specification covers the general and physical requirements for greige fabrics woven from “E” electrical glass fiber yarns. The yarn shall be a continuous filament, free of any free alkali metal salts, such as soda or potash, and foreign particles, dirt, and other impurities. The fabric shall be furnished in rolls and shall be wound in spiral tubes. The materials shall be tested and shall conform to the following requirements: fabric count; yarn numbers for both the warp and filling yarns; filament diameter; strand construction; twist direction wherein the primary twist in the singles strands shall be “Z” twist and the final twist in the plied yarns shall be “S” twist; twist level; fabric weave type which shall include crowfoot, leno, mock leno, plain, eight-harness satin, and twelve-harness satin; mass per unit area; thickness; breaking strength; width including both selvages but excluding any feathered edges; fabric roll length, length between splices, and number of splices per roll; and ignition loss. The fabrics shall also be examined for defects such as bias or bowed filling; baggy, ridged, or wavy cloth; cut or tear; hole; spots, streaks, or stains; foreign inclusions; tender or weak spot; smash; broken, missing ends or picks; floats and skips; light and heavy marks; crease; waste; weave separation; brittle or fused area; selvage defects; selvage leno ends out; and feather edges.
SCOPE
1.1 This practice covers greige fabrics woven from “E” electrical glass fiber yarns. This practice can also be applied to fabrics made of other glass fiber types as agreed upon between the purchaser and the supplier.  
1.2 This practice specifies the terminology, definitions, general requirements and physical requirements for greige glass fiber fabrics. This practice permits the application of organic materials to the glass fiber yarn during manufacture that helps facilitate weaving.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This practice is one of a series to provide a substitute for Military Specifications: MIL-Y-1140 Yarn, Cord, Sleeving, Cloth, and Tape-Glass and MIL-C-9084 Cloth, Glass Finished for Resin Laminates.  
1.5 Additional ASTM practices in this series have been drafted and appear in current editions of the Annual Book of ASTM Standards. These include finished glass fabrics, unfinished glass fabrics, glass tapes, glass sleevings, glass cords, glass sewing threads, and finished laminates made from finished glass fabrics.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

Status
Published
Publication Date
31-Dec-2023
ICS
59.080.30 - Textile fabrics
Technical Committee
D13 - Textiles
Drafting Committee
D13.18 - Glass Fiber and its Products
Current Stage
Ref Project

Relations

Refers
ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass Fabrics
Effective Date
01-Jan-2024
Refers
ASTM D579/D579M-15 - Standard Specification for Greige Woven Glass Fabrics
Effective Date
01-Feb-2015
Referred By
ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass Fabrics
Effective Date
01-Jan-2024
Referred By
ASTM D4595/D4595M-23 - Standard Test Method for Tensile Properties of Geotextiles by the Wide-Width Method
Effective Date
01-Jan-2024
Referred By
ASTM D7556-10(2019) - Standard Test Methods for Determining Small-Strain Tensile Properties of Geogrids and Geotextiles by In-Air Cyclic Tension Tests
Effective Date
01-Jan-2024
Referred By
ASTM E2098/E2098M-13(2023) - Standard Test Method for Determining Tensile Breaking Strength of Glass Fiber Reinforcing Mesh for Use in Class PB Exterior Insulation and Finish Systems (EIFS), after Exposure to a Sodium Hydroxide Solution
Effective Date
01-Jan-2024
Referred By
ASTM D580/D580M-24 - Standard Practice for Greige Woven Glass Tapes and Webbings
Effective Date
01-Jan-2024
Referred By
ASTM D1668/D1668M-97a(2021) - Standard Specification for Glass Fabrics (Woven and Treated) for Roofing and Waterproofing
Effective Date
01-Jan-2024

Buy Standard

ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass FabricsASTM D579/D579M-24 - Standard Practice for Greige Woven Glass Fabrics
PreviousNext
Standard
ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass Fabrics
English language
18 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass FabricsREDLINE ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass Fabrics
PreviousNext
Standard
REDLINE ASTM D579/D579M-24 - Standard Practice for Greige Woven Glass Fabrics
English language
18 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D579/D579M − 24
Standard Practice for
1
Greige Woven Glass Fabrics
This standard is issued under the fixed designation D579/D579M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope Development of International Standards, Guides and Recom-
mendations issued by the World Trade Organization Technical
1.1 This practice covers greige fabrics woven from “E”
Barriers to Trade (TBT) Committee.
electrical glass fiber yarns. This practice can also be applied to
fabrics made of other glass fiber types as agreed upon between
2. Referenced Documents
the purchaser and the supplier.
2
2.1 ASTM Standards:
1.2 This practice specifies the terminology, definitions, gen-
D123 Terminology Relating to Textiles
eral requirements and physical requirements for greige glass
D578/D578M Specification for Glass Fiber Strands
fiber fabrics. This practice permits the application of organic
D579/D579M Specification for Greige Woven Glass Fabrics
materials to the glass fiber yarn during manufacture that helps
D1059 Test Method for Yarn Number Based on Short-
facilitate weaving.
Length Specimens
D1423/D1423M Test Method for Twist in Yarns by Direct-
1.3 The values stated in either SI units or inch-pound units
Counting
are to be regarded separately as standard. The values stated in
D1776/D1776M Practice for Conditioning and Testing Tex-
each system are not necessarily exact equivalents; therefore, to
tiles
ensure conformance with the standard, each system shall be
D1777 Test Method for Thickness of Textile Materials
used independently of the other, and values from the two
D3773/D3773M Test Methods for Length of Woven Fabric
systems shall not be combined.
D3774 Test Method for Width of Textile Fabric
1.4 This practice is one of a series to provide a substitute for
D3775 Test Method for End (Warp) and Pick (Filling) Count
Military Specifications: MIL-Y-1140 Yarn, Cord, Sleeving,
of Woven Fabrics
Cloth, and Tape-Glass and MIL-C-9084 Cloth, Glass Finished
D3776/D3776M Test Methods for Mass Per Unit Area
for Resin Laminates.
(Weight) of Fabric
1.5 Additional ASTM practices in this series have been
D4963/D4963M Test Method for Ignition Loss of Glass
drafted and appear in current editions of the Annual Book of
Fiber Strands and Fabrics
ASTM Standards. These include finished glass fabrics, unfin-
D5035 Test Method for Breaking Force and Elongation of
ished glass fabrics, glass tapes, glass sleevings, glass cords,
Textile Fabrics (Strip Method)
glass sewing threads, and finished laminates made from fin-
D7018/D7018M Terminology Relating to Glass Fiber and
3
ished glass fabrics.
Its Products (Withdrawn 2021)
2.2 ANSI Standards:
1.6 This standard does not purport to address all of the
ANSI/ASQC Z1.4 Sampling Procedures for Inspection by
safety concerns, if any, associated with its use. It is the
4
Attributes
responsibility of the user of this standard to establish appro-
2.3 Military Standard and Specifications:
priate safety, health, and environmental practices and deter-
5
MIL-Y-1140H Yarn, Cord, Sleeving, Cloth and Tape-Glass
mine the applicability of regulatory limitations prior to use.
5
MIL-C-9084C Cloth, Glass Finished for Resin Laminates
1.7 This international standard was developed in accor-
dance with internationally recognized principles on standard-
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
ization established in the Decision on Principles for the
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website.
1 3
This specification is under the jurisdiction of ASTM Committee D13 on The last approved version of this historical standard is referenced on
Textiles and is the direct responsibility of Subcommittee D13.18 on Glass Fiber and www.astm.org.
4
its Products. Available from American National Standards Institute (ANSI), 25 W. 43rd St.,
Current edition approved Jan. 1, 2024. Published February 2024. Originally 4th Floor, New York, NY 10036, http://www.ansi.org.
5
approved in 1940. Last previous edition approved in 2015 as D579/D579M – 15. Available from DLA Document Services, Building 4/D, 700 Robbins Ave.,
DOI: 10.1520/D0579_D0579M-24. Philadelphia, PA 19111-5094, http://quicksearch.dla.mil.
Copyright © ASTM International, 100 Barr Harbor Drive,
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D579/D579M − 15 D579/D579M − 24
Standard SpecificationPractice for
1
Greige Woven Glass Fabrics
This standard is issued under the fixed designation D579/D579M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope
1.1 This specificationpractice covers greige fabrics woven from “E” electrical glass fiber yarns. This specificationpractice can also
be applied to fabrics made of other glass fiber types as agreed upon between the purchaser and the supplier.
1.2 This specificationpractice specifies the terminology, definitions, general requirements and physical requirements for greige
glass fiber fabrics. This specificationpractice permits the application of organic materials to the glass fiber yarn during manufacture
that helps facilitate weaving.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used
independently of the other, and values from the two systems shall not be combined.
1.4 This specificationpractice is one of a series to provide a substitute for Military Specifications: MIL-Y-1140 Yarn, Cord,
Sleeving, Cloth, and Tape-Glass;Tape-Glass and MIL-C-9084 Cloth, Glass Finished for Resin Laminates.
1.5 Additional ASTM specificationspractices in this series have been drafted and appear in current editions of the Annual Book
of ASTM Standards. These include finished glass fabrics, unfinished glass fabrics, glass tapes, glass sleevings, glass cords, glass
sewing threads, and finished laminates made from finished glass fabrics.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and healthsafety, health, and environmental practices and determine
the applicability of regulatory limitations prior to use.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
D123 Terminology Relating to Textiles
D578D578/D578M Specification for Glass Fiber Strands
1
This specification is under the jurisdiction of ASTM Committee D13 on Textiles and is the direct responsibility of Subcommittee D13.18 on Glass Fiber and its Products.
Current edition approved Feb. 1, 2015Jan. 1, 2024. Published March 2015February 2024. Originally approved in 1940. Last previous edition approved in 20102015 as
D579D579/D579M – 10. DOI: 10.1520/D0579-15.15. DOI: 10.1520/D0579_D0579M-24.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D579/D579M − 24
D579/D579M Practice for Greige Woven Glass Fabrics
D1059 Test Method for Yarn Number Based on Short-Length Specimens
D1423D1423/D1423M Test Method for Twist in Yarns by Direct-Counting
D1776D1776/D1776M Practice for Conditioning and Testing Textiles
D1777 Test Method for Thickness of Textile Materials
D3773D3773/D3773M Test Methods for Length of Woven Fabric
D3774 Test Method for Width of Textile Fabric
D3775 Test Method for End (Warp) and Pick (Filling) Count of Woven Fabrics
D3776D3776/D3776M Test Methods for Mass Per Unit Area (Weight) of Fabric
D4963D4963/D4963M Test Method for Ignition Loss of Glass Fiber Strands and Fabrics
D5035 Test Method for Breaking Force and Elongation of Textile Fabrics (Strip Method)
3
D7018D7018/D7018M Terminology Relating to Glass Fiber and Its Products (Withdrawn 2021)
2.2 ANSI Standards:
4
ANSI/ASQC Z1.4 Sampling Procedures for Inspection by Attributes
2.3 Military Standard and Specifications:
5
MIL-
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D5587-15(2024)(Test Method)
Standard Test Method for Tearing Strength of Fabrics by Trapezoid Procedure

SIGNIFICANCE AND USE
5.1 This test method is considered satisfactory for acceptance testing of commercial shipments because current estimates of between-laboratory precision are acceptable, and this test method is used extensively in the trade for acceptance testing.  
5.2 If there are differences of practical significance between test results for two laboratories (or more), comparative test should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, use the samples for such a comparative test that are as homogeneous as possible, drawn from the same lot of material as the samples that resulted in disparate results during initial testing. Randomly assign the samples in equal numbers to each laboratory. The test results from the laboratories involved should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If bias is found, either its cause must be found and corrected, or future test results for that material must be adjusted in consideration of the known bias.  
5.3 The trapezoid tear produces tension along a reasonably defined course such that the tear propagates across the width of the specimen. It is useful for estimating the relative tear resistance of different fabrics or different directions in the same fabric.  
5.4 Depending on the nature of the specimen, the data recording devices will show the tearing force in the form of a peak or peaks. The highest peaks appear to reflect the strength of the yarn components, individually or in combination, needed to stop a tear in fabrics of the same construction. The valleys recorded between the peaks have no specific significance. The minimum tearing force, however, is indicated to be above the lowest valleys.  
5.5 Most textile fabrics can be tested by this test method. Some modification of clamping techniques may be necessary for a given fabric, depending upon its structure. Strong fabrics or fabrics...
SCOPE
1.1 This test method covers the measurement of the tearing strength of textile fabrics by the trapezoid procedure using a recording constant-rate-of-extension-type (CRE) tensile testing machine.  
1.1.1 The CRE-type tensile testing machine has become the preferred test apparatus for determining trapezoid tearing strength. It is recognized that some constant-rate-of-traverse-type (CRT) tensile testing machines continue to be used. Consequently, these test instruments may be used when agreed upon between the purchaser and the supplier. The conditions for use of the CRT-type tensile tester are included in Appendix X1.  
1.2 This test method applies to most fabrics including woven fabrics, air bag fabrics, blankets, napped fabrics, knitted fabrics, layered fabrics, pile, and nonwoven fabrics. The fabrics may be untreated, heavily sized, coated, resin-treated, or otherwise treated. Instructions are provided for testing specimens with or without wetting.  
1.3 Tearing strength, as measured in this test method, requires that the tear be initiated before testing. The reported value obtained is not directly related to the force required to initiate or start a tear.  
1.4 Two calculations for trapezoid tearing strength are provided: the single-peak force and the average of five highest peak forces.  
1.5 The values stated in SI units are to be regarded as the standard. The values stated in inch-pound units may be approximate.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International ...

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D2261-13(2024)(Test Method)
Standard Test Method for Tearing Strength of Fabrics by the Tongue (Single Rip) Procedure (Constant-Rate-of-Extension Tensile Testing Machine)

SIGNIFICANCE AND USE
5.1 This test method is considered satisfactory for acceptance testing of commercial shipments since current estimates of between-laboratory precision are acceptable, and the test method is used extensively in the trade for acceptance testing.  
5.1.1 In case of a dispute arising from differences in reported test results when using this test method for acceptance testing of commercial shipments, the purchaser and the supplier should conduct comparative tests to determine if there is a statistical bias between their laboratories. Competent statistical assistance is recommended for the investigation of bias. As a minimum, the two parties should take a group of test specimens that are as homogeneous as possible and that are from a lot of fabric of the type in question. Test specimens then should be randomly assigned in equal numbers to each laboratory for testing. The average results from the two laboratories should be compared using the appropriate statistical analysis and an acceptable probability level chosen by the two parties before testing is begun. If a bias is found, either its cause must be found and corrected, or the purchaser and the supplier must agree to interpret future test results with consideration to the known bias.  
5.2 The force registered in a tear test is irregular, and as a consequence, empirical methods have had to be developed to obtain usable values related to tear strength. In spite of the empirical nature of the reported values, the values are considered to reflect comparative performance of similar fabrics tested and measured in the same way. No known procedure is available that can be used with all fabrics to determine the minimum tearing strength.  
5.3 Depending on the nature of the specimen, the data recording devices will show the tearing force in the form of a peak or peaks. The highest peaks appear to reflect the strength of the yarn components, fiber bonds, or fiber interlocks, individually or in combination, needed to stop a te...
SCOPE
1.1 This test method covers the measurement of the tearing strength of textile fabrics by the tongue (single rip) procedure using a recording constant-rate-of-extension-type (CRE) tensile testing machine.  
1.1.1 The CRE-type tensile testing machine has become the preferred test apparatus for determining tongue tearing strength. It is recognized that some constant-rate-of-traverse-type (CRT) tensile testing machines continue to be used. As a consequence, these test instruments may be used when agreed upon between the purchaser and the supplier. The conditions for use of the CRT-type tensile tester are included in Appendix X1.  
1.2 This test method applies to most fabrics including woven fabrics, air bag fabrics, blankets, napped fabrics, knit fabrics, layered fabrics, pile fabrics and non-wovens. The fabrics may be untreated, heavily sized, coated, resin-treated, or otherwise treated. Instructions are provided for testing specimens with or without wetting.  
1.3 Tear strength, as measured in this test method, requires that the tear be initiated before testing. The reported value obtained is not directly related to the force required to initiate or start a tear.  
1.4 Two calculations for tongue tearing strength are provided: the single-peak force and the average of five highest peak forces.  
1.5 The values stated in either SI units or inch-pound units are to be regarded as the standard. The inch-pound units may be approximate.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of I...

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D6775-13(2024)(Test Method)
Standard Test Method for Breaking Strength and Elongation of Textile Webbing, Tape and Braided Material

SIGNIFICANCE AND USE
5.1 This test method can be used for acceptance testing of commercial shipments but comparisons should be made with caution because estimates of between-laboratory precision are incomplete.  
5.1.1 If there are differences of practical significance between reported test results for two laboratories (or more), comparative tests should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, use samples for such comparative tests that are as homogeneous as possible, drawn from the same lot of material as the samples that resulted in disparate results during initial testing, and randomly assigned in equal numbers to each laboratory. The test results from the laboratories involved should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If bias is found, either its cause must be found and corrected, or future test results for that material must be adjusted in consideration of the known bias.  
5.2 Elongation is an indication of the ability of a fiber to absorb energy. The elongation of textile materials must be great enough to withstand strains experienced in processing and end use, and to absorb the energies of applied forces repeatedly.
SCOPE
1.1 This test method covers the determination of the breaking strength and elongation of textile webbing, tape and braided materials using a split-drum type specimen clamp.  
1.2 This test method is limited to materials with a maximum width of 90 mm (3.5 in.) and a maximum breaking strength of no more than 89000 N (20000 lb).  
1.3 The values stated in either SI units or U.S. Customary units are to be regarded separately as standard. Within the text, the U.S. Customary units are given in parentheses. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D3938-18(2023)(Guide)
Standard Guide for Determining or Confirming Care Instructions for Apparel and Other Textile Products

SIGNIFICANCE AND USE
4.1 This is a guide to help a manufacturer distributor, or importer establish a reasonable basis for care information.  
4.1.1 The manufacturer, distributor, or importer should possess, prior to sale, reliable evidence that the product was not harmed when refurbished reasonably often according to the instructions. Additionally, they should possess reliable evidence that the product, or a fair sample of the product, would be harmed when refurbished by methods warned against on the label.  
4.2 This guide is intended for general use by those who wish to evaluate whether apparel or other textile products will perform in an acceptable manner when refurbished according to particular care instructions.  
4.3 Refurbished products are evaluated against previously selected product specifications to determine whether the products can be refurbished successfully by following the instructions on the care label or other care instructions.
SCOPE
1.1 This guide may be used to determine and confirm the appropriate care label instructions for apparel, piece goods, and other textile products excluding textile floor coverings and upholstery.  
1.2 This guide encompasses the following care procedures: home laundering, professional textile care, and other alternative cleaning methods.  
1.3 This guide includes provision for evaluating the complete textile product and the product components.  
1.4 This guide covers the performance characteristics as a result of refurbishing that are important in determining the acceptability of a textile product.  
1.5 This guide is appropriate for the evaluation of all garments and household textiles that are sold with care labels.  
1.5.1 This guide may also be used in connection with the evaluation of similar materials that do not have a care label.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    5 pages
    English language
    sale 15% off
ASTM
ASTM D1388-23(Test Method)
Standard Test Method for Stiffness of Fabrics

SIGNIFICANCE AND USE
5.1 In general, these procedures are more suitable for testing woven fabrics than knit fabrics.  
5.2 Both test options in this test method are considered satisfactory for acceptance testing of commercial shipments since current estimates of between-laboratory precision are acceptable and the method is used extensively in the trade for acceptance testing.  
5.2.1 In case of a dispute arising from differences in reported test results when using this test method for acceptance testing of commercial shipments, the purchaser and the supplier should conduct comparative tests to determine if there is a statistical bias between their laboratories. Competent statistical assistance is recommended for the investigation of bias. As a minimum, the two parties should take a group of test specimens that are as homogeneous as possible and that are from a lot of material of the type in question. Test specimens should then be randomly assigned in equal numbers to each laboratory for testing. The average results from the two laboratories should be compared using the appropriate statistical analysis and an acceptable probability level chosen by the two parties before testing is begun. If a bias is found, either its cause must be found and corrected or the purchaser and the supplier must agree to interpret future test results with consideration to the known bias.  
5.3 The stiffness of a fabric may change with storage.  
5.4 No evidence has been found showing that bending length is dependent on the width of the test specimen. The tendency for specimens to curl or twist will affect the result, because of the rigidity provided at the edge of the specimen. Consequently, the wider the strip, the less important is the edge effect. For fabrics having only a slight tendency to curl, a 2.5 cm wide strip has been found to be satisfactory. As the tendency to curl increases, this width may be increased (see Note 10).  
5.5 This method differs from Test Method F3260 which requires tracking of...
SCOPE
1.1 This test method covers the measurement of stiffness properties of fabrics. Bending length is measured and flexural rigidity is calculated. Two procedures are provided.  
1.1.1 Option A—Cantilever Test, employing the principle of cantilever bending of the fabric under its own mass.  
1.1.2 Option B—Heart Loop Test, employing the principle of a loop formed in a fabric strip and hung vertically.  
1.2 This test method applies to most fabrics including woven fabrics, air bag fabrics, blankets, napped fabrics, knitted fabrics, layered fabrics, pile fabrics. The fabrics may be untreated, heavily sized, coated, resin-treated, or otherwise treated.  
1.2.1 This method may be used to determine the stiffness of nonwoven materials (for example, hydroentangled, dry laid, needlepunch, resin bonded, thermal, and wet laid) or refer to Test Method D5732. To determine the stiffness of medical textiles (for example, surgical mesh, films, and membranes), refer to Test Method F3260.  
Note 1: The formula to calculate flexural rigidity in D5732-95 (2001) is incorrect and should not be used. Utilize the formula presented in 11.5 of Test Method D1388.  
1.3 Units—The values stated in SI units are to be regarded as the standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers...

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D3786/D3786M-18(2023)(Test Method)
Standard Test Method for Bursting Strength of Textile Fabrics—Diaphragm Bursting Strength Tester Method

SIGNIFICANCE AND USE
5.1 This method for the determination of diaphragm bursting strength of knitted, nonwoven and woven fabrics is being used by the textile industry for the evaluation of a wide variety of end uses.  
5.2 In cases where test results obtained using the procedures in Test Method D3786 have not been correlated with actual performance, Test Method D3786 is considered satisfactory for acceptance testing of commercial shipments of textile fabrics for bursting strength since the method has been used extensively in the trade for acceptance testing. In cases where disagreement arising from differences in values reported by the purchaser and the supplier when using Test Method D3786 for acceptance testing, the statistical bias, if any, between the laboratory of the purchaser and the laboratory of the supplier should be determined with comparison based on testing specimens randomly drawn from one sample of material of the type being evaluated.
Note 2: The kind of load transfer and stretch that occur when knitted goods and nonwoven fabrics are worn are prevented by clamping them as described in this method.
SCOPE
1.1 This test method describes the measurement of the resistance of textile fabrics to bursting using a hydraulic or pneumatic diaphragm bursting tester. This test method is generally applicable to a wide variety of textile products.  
1.2 This test method may also be applicable for stretch woven and woven industrial fabrics such as inflatable restraints. As new materials that may exceed the range of the instrument are developed, please refer to the reporting section and consider using Test Methods D3787 or D6797 instead.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
Note 1: For the measurement of the bursting strength by means of a ball burst mechanism, refer to Test Method D3787.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D737-18(2023)(Test Method)
Standard Test Method for Air Permeability of Textile Fabrics

SIGNIFICANCE AND USE
5.1 This test method is considered satisfactory for acceptance testing of commercial shipments since current estimates of between-laboratory precision are acceptable, and this test method is used extensively in the trade for acceptance testing.  
5.1.1 If there are differences of practical significance between reported test results for two laboratories (or more), comparative tests should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, ensure the test samples to be used are as homogeneous as possible, are drawn from the material from which the disparate test results were obtained, and are randomly assigned in equal number to each laboratory for testing. The test results from the two laboratories should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If bias is found, either its cause must be found and corrected, or future test results for that material must be adjusted in consideration of the known bias.  
5.2 Air permeability is an important factor in the performance of such textile materials as gas filters, fabrics for air bags, clothing, mosquito netting, parachutes, sails, tentage, and vacuum cleaners. In filtration, for example, efficiency is directly related to air permeability. Air permeability also can be used to provide an indication of the breathability of weather-resistant and rainproof fabrics, or of coated fabrics in general, and to detect changes during the manufacturing process.  
5.3 Performance specifications, both industrial and military, have been prepared on the basis of air permeability and are used in the purchase of fabrics where permeability is of interest.  
5.4 Construction factors and finishing techniques can have an appreciable effect upon air permeability by causing a change in the length of airflow paths through a fabric. Hot calendaring can be used to flatten fabric components, thus reducing...
SCOPE
1.1 This test method covers the measurement of the air permeability of textile fabrics.  
1.2 This test method applies to most fabrics including woven fabrics, nonwoven fabrics, air bag fabrics, blankets, napped fabrics, knitted fabrics, layered fabrics, and pile fabrics. The fabrics may be untreated, heavily sized, coated, resin-treated, or otherwise treated.  
1.3 The values stated in SI units are to be regarded as the standard. The values stated in inch-pound units may be approximate.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D4850-23(Terminology)
Standard Terminology Relating to Fabrics and Fabric Test Methods

SCOPE
1.1 This terminology covers definitions of technical terms used in the industry related to textile fabrics. Terms that are generally understood or adequately defined in other readily available sources are not included. Other terminology standards that have terms related to textile fabrics are shown in 2.1  
1.2 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    11 pages
    English language
    sale 15% off
  • Standard
    11 pages
    English language
    sale 15% off
ASTM
ASTM D3775-17(2023)(Test Method)
Standard Test Method for End (Warp) and Pick (Filling) Count of Woven Fabrics

SIGNIFICANCE AND USE
5.1 This test method is considered satisfactory for acceptance testing of commercial shipments because it has been used extensively in the trade for that purpose.  
5.1.1 If there are differences of practical significance between reported test results for two laboratories (or more), comparative test should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, use the samples for such a comparative test that are as homogeneous as possible, drawn from the same lot of material as the samples that resulted in disparate results during initial testing and randomly assigned in equal numbers to each laboratory. The test results from the laboratories involved should be compared using a statistical test for unpaired data, a probability level chosen prior to the testing series. If bias is found, either its cause must be found and corrected, or future test results for that material must be adjusted in consideration of the known bias.  
5.1.2 This test method is suitable for use with narrow fabrics when the count across the total width is measured in the narrow direction and extrapolated to the number of yarns per centimeter (inch).
SCOPE
1.1 This test method covers the measurement of end (warp) and pick (filling) count and is applicable to all types of woven fabrics.  
Note 1: Historically, the term fabric count has been used to describe the end and pick count of woven fabrics. The terms end count and pick count are replacing the term fabric count, to provide clarity.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.2.1 Throughout this document, there will be some instances in which the units do not convert 1:1. This is to acknowledge that this is a global document and that different parts of the world use different units of measurement. Organizations using the metric system wil report the count per 1 cm. Organizations using the English system will report the count per 1 in.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 2: For a current test method for the wale and course count of weft knitted fabrics, refer to Test Method D8007.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D7507-23(Specification)
Standard Specification for Woven High Stretch Fabrics Used in Apparel

SIGNIFICANCE AND USE
4.1 Upon mutual agreement between the purchaser and the supplier, woven high stretch fabrics used in apparel should meet all of the requirements listed in Table 1 of this specification. (A) See Note 3.  
4.2 It is recognized that, for purposes of fashion or aesthetics, the ultimate consumer of articles made from these fabrics may find acceptable products that do not conform to all of the requirements listed in Table 1. Therefore, one or more of the requirements in Table 1 may be modified by mutual agreement between the purchaser and the supplier.  
4.2.1 In such cases, any references to the specifications should specify that: “This product meets ASTM specifications XXXX except for the following characteristic(s).”  
4.3 Where no pre-purchase agreement has been reached between the purchaser and supplier, and in case of controversy, the requirements listed in Table 1 are intended to be used as a guide only. As noted in 4.2, ultimate consumer demands dictate varying performance parameters for a particular product.  
4.4 The uses and significance of particular properties and test methods are discussed in the appropriate sections of the specified test methods.
SCOPE
1.1 This specification covers the performance requirements for woven high stretch fabrics used in apparel.  
1.2 The following safety hazards caveat pertains only to the test methods described in this performance specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off