ASTM B753-07

(Specification)

Standard Specification for Thermostat Component Alloys

Standard Specification for Thermostat Component Alloys

ABSTRACT
This specification details the requirements for alloys to be used as components in the manufacture of bonded multi-component thermostat metal strip. It describes alloys having composition, and thermal expansion suitable for application in thermostat metal sheet and strip. The material shall be free of scale, slivers, cracks, seams, corrosion and other defects as best commercial practice will permit. Surfaces shall be uniform and sufficiently clean. Product surface condition can be agreed upon between supplier and purchaser since surface condition can vary for different alloys and because bonding practices vary. The material shall be made of carbon, manganese, silicon, phosphorus, sulfur, chromium, nickel, copper, aluminum, cobalt, and iron. This product shall be supplied in the condition agreed upon by purchaser and seller. Hardness shall be measured on representative samples from each heat treat lot.
SCOPE
1.1 This specification describes requirements for alloys to be used as components in the manufacture of bonded multi-component thermostat metal strip. More specifically it describes alloys having composition, and thermal expansion suitable for application in thermostat metal sheet and strip.
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Apr-2007
ICS
77.120.01 - Non-ferrous metals in general
Technical Committee
B02 - Nonferrous Metals and Alloys
Drafting Committee
B02.10 - Thermostat Metals and Electrical Resistance Heating Materials
Current Stage
Ref Project

Relations

Replaces
ASTM B753-01 - Standard Specification for Thermostat Component Alloys
Effective Date
01-May-2007
Replaced By
ASTM B753-07(2013) - Standard Specification for Thermostat Component Alloys
Effective Date
01-May-2013
Referred By
ASTM B388-06(2018) - Standard Specification for Thermostat Metal Sheet and Strip
Effective Date
01-May-2007

Buy Standard

ASTM B753-07 - Standard Specification for Thermostat Component AlloysASTM B753-07 - Standard Specification for Thermostat Component Alloys
PreviousNext
Technical specification
ASTM B753-07 - Standard Specification for Thermostat Component Alloys
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:B753 −07
StandardSpecification for
1
Thermostat Component Alloys
This standard is issued under the fixed designation B753; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3. Ordering Information
1.1 This specification describes requirements for alloys to 3.1 Orders for this material under this specification shall
be used as components in the manufacture of bonded multi- include the following information:
component thermostat metal strip. More specifically it de- 3.1.1 Alloy type,
scribes alloys having composition, and thermal expansion 3.1.2 Size,
suitable for application in thermostat metal sheet and strip. 3.1.3 Surface finish,
3.1.4 Marking and packaging, and
1.2 The values stated in inch-pound units are to be regarded
3.1.5 Certification, if required.
as the standard. The values given in parentheses are for
information only.
4. General Requirements
1.3 This standard does not purport to address all of the
4.1 The material shall be free of scale, slivers, cracks,
safety concerns, if any, associated with its use. It is the
seams, corrosion and other defects as best commercial practice
responsibility of the user of this standard to become familiar
will permit. Surfaces shall be uniform and sufficiently clean so
with all hazards including those identified in the appropriate
that commonly used methods of surface preparation, or pre-
Material Safety Data Sheet (MSDS) for this product/material
bond cleaning will allow bonding of the entire mating surfaces.
as provided by the manufacturer, to establish appropriate
Since surface condition can vary for different alloys and
safety and health practices, and determine the applicability of
because bonding practices vary, product surface condition can
regulatory limitations prior to use.
be agreed upon between supplier and purchaser.
2. Referenced Documents
5. Chemical Composition
2
2.1 ASTM Standards:
5.1 The material shall be manufactured to the chemical
A480/A480M Specification for General Requirements for
compositions shown in Table 1.
Flat-Rolled Stainless and Heat-Resisting Steel Plate,
5.2 The manufacturer will insure uniformity of composition
Sheet, and Strip
B63 Test Method for Resistivity of Metallically Conducting throughoutaheatlottoprovideuniformthermalexpansionand
electrical resistivity properties. See Specifications B152/
Resistance and Contact Materials
B152/B152M Specification for Copper Sheet, Strip, Plate, B152M and B162.
and Rolled Bar
6. Thermal Expansion Requirements
B162 Specification for Nickel Plate, Sheet, and Strip
B388 Specification for Thermostat Metal Sheet and Strip
6.1 Samples tested in accordance with 6.2 shall exhibit
E18 Test Methods for Rockwell Hardness of Metallic Ma-
thermal expansion properties described in Table 2.
terials
6.2 One test sample representing each heat lot shall be
E228 Test Method for Linear Thermal Expansion of Solid
machined to a suitable specimen configuration, heat treated in
Materials With a Push-Rod Dilatometer
accordance with instructions in Table 2 andTest Method E228.
7. Electrical Resistivity
1
This specification is under the jurisdiction of ASTM Committee B02 on
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee 7.1 The electrical resistivity measured at room temperature
B02.10 on Thermostat Metals and Electrical Resistance Heating Materials.
as in Test Method B63 on suitably prepared and annealed
Current edition approved May 1, 2007. Published June 2007. Originally
specimens shall conform to Table 3.
approved in 1986. Last previous edition approved in 2001 as B753 - 01. DOI:
10.1520/B0753-07.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or 8. Temper
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
8.1 This product will be supplied in the condition agreed
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. upon by purchaser and seller.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
B753−07
TABLE 1 Suggested Compositions For Thermostat Alloys All Elements Indicated As Weight Percent
NOTE 1—Composition requirements show major elements as being nominal. These nominal requirements indicate they are to be adjusted by the
manufacturer so that the alloys meet the requirements for thermal expansion shown in Table 2. Other elements not shown, may be present in residual
amounts. These shall not be present in sufficient quantity as to significantly aff
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM B899-21(Terminology)
Standard Terminology Relating to Non-ferrous Metals and Alloys

SIGNIFICANCE AND USE
2.1 The terms defined in this document are generic in respect to the standards under the jurisdiction of Committee B02 on Nonferrous Metals and Alloys. The same terms may have different definitions in other ASTM technical committees.  
2.2 Some definitions may differ within the committee because of limitations on items such as weights or dimensions. In such cases the terms will be more precisely defined in the Terminology section of the standards in which these terms are used.
SCOPE
1.1 To promote precise understanding and interpretation of standards, reports, and other technical writings promulgated by Committee B02.  
1.2 To standardize the terminology used in these documents.  
1.3 To explain the meanings of technical terms used within these documents for those not conversant with them.  
1.4 Some definitions include a discussion section, which is a mandatory part of the definition and contains additional information that is relevant to the meaning of the defined term.  
1.5 Definitions of terms specific to a particular standard will appear in that standard and will supersede any definitions of identical terms in this standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM B774/B774M-21(Specification)
Standard Specification for Low Melting Point Alloys and Solders

ABSTRACT
This specification covers low-melting point metal alloys and soldiers, including bismuth-tin, bismuth-lead, bismuth-tin-lead, bismuth-tin-lead-cadmium, bismuth-tin-lead-indium-cadmium, bismuth-tin-lead-indium, indium-lead, indium-lead-silver, and indium-tin joining together two or more metals at temperatures below their melting points; blocking for support and removable borders; radiation shielding; fusible plugs; fuses; tube bending; and punch setting. This specification shall include those alloys having liquidus temperature not exceeding the melting point of the tin lead eutectic, and alloys in the form of solid bars, ingots, powder and special forms, and in the form of solid ribbon and wire. The composition of the alloys shall conform to the chemical requirements for bismuth, lead, tin, cadmium, indium, silver, copper, antimony, and zinc. Alloys shall be tested and shall conform to specified values for alloy freezing point, and powder mesh size.
SCOPE
1.1 This specification covers low-melting point metal alloys and solders, including bismuth-tin, bismuth-lead, bismuth-tin-lead, bismuth-tin-lead-cadmium, bismuth-tin-lead-indium-cadmium, bismuth-tin-lead-indium, indium-lead, and indium-lead-silver, and indium-tin joining together two or more metals at temperatures below their melting points; blocking for support and removable borders; radiation shielding; fusible plugs; fuses; tube bending; and punch setting.  
1.1.1 This specification shall include those alloys having a liquidus temperature not exceeding 361 °F [183 °C], the melting point of the tin lead eutectic.  
1.1.2 This specification includes low-melting point alloys in the form of solid bars, ingots, powder and special forms, and in the form of solid ribbon and wire.  
1.2 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM B865-20(Specification)
Standard Specification for Precipitation Hardening Nickel-Copper-Aluminum Alloy Bar, Rod, Wire, Forgings, and Forging Stock

ABSTRACT
This specification covers UNS N05500 nickel-copper-aluminum alloy rounds, squares, hexagons, rectangles, and forgings and forging stocks manufactured by either hot working or cold working, and cold-worked wire. The material should conform to the required mechanical properties in both aged and unaged conditions. Precipitation hardening is accomplished by holding the material at a high temperature, followed by furnace cooling and then air cooling.
SCOPE
1.1 This specification covers nickel-copper-aluminum alloy (UNS N05500) in the form of rounds, squares, hexagons, or rectangles, and forgings and forging stock, manufactured either by hot working or cold working, and cold-worked wire.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B223-08(2018)(Test Method)
Standard Test Method for Modulus of Elasticity of Thermostat Metals (Cantilever Beam Method)

ABSTRACT
This test method covers the determination of the modulus of elasticity of thermostat metals within a particular temperature range. The test is done by mounting the specimen as a cantilever and measuring its deflection when subjected to a mechanical load. Each test specimen should be finished to size by careful machining or filing after being roughly cut, slit, or sheared from the samples. Then the specimen is preformed into a shape approximating the segment of a circle and subsequently heat treated to relieve all internal stresses. To permit maximum sensitivity, any oxide and other foreign substances must be carefully removed from all surfaces of the test specimen which directly affect the electrical resistance of the electronic indicator circuit through the testing apparatus. Extra care should be taken so that the load does not overstress the specimen beyond its elastic limit, if this happens, a new specimen shall be substituted and a lighter load should be used. The modulus of elasticity of each test material is computed using the specimen size and the average deflection for a known load.
SCOPE
1.1 This test method covers the determination of the modulus of elasticity of thermostat metals at any temperature between −300 and +1000°F (−185 and 540°C) by mounting the specimen as a cantilever beam and measuring the deflection when subjected to a mechanical load.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM B77-07(2018)(Test Method)
Standard Test Method for Thermoelectric Power of Electrical-Resistance Alloys

SIGNIFICANCE AND USE
4.1 The purpose of this method is to determine the suitability of different metals for use in resistance apparatus in which a low thermoelectric power is desired. As most electric circuits are largely composed of copper, the thermoelectric power of a resistance metal will generally be measured against copper.
SCOPE
1.1 This test method covers the determination of the thermoelectric power of a metal or alloy with respect to copper when the temperatures of the junctions lie between 0 and 100°C.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM B753-07(2018)(Specification)
Standard Specification for Thermostat Component Alloys

ABSTRACT
This specification details the requirements for alloys to be used as components in the manufacture of bonded multi-component thermostat metal strip. It describes alloys having composition, and thermal expansion suitable for application in thermostat metal sheet and strip. The material shall be free of scale, slivers, cracks, seams, corrosion and other defects as best commercial practice will permit. Surfaces shall be uniform and sufficiently clean. Product surface condition can be agreed upon between supplier and purchaser since surface condition can vary for different alloys and because bonding practices vary. The material shall be made of carbon, manganese, silicon, phosphorus, sulfur, chromium, nickel, copper, aluminum, cobalt, and iron. This product shall be supplied in the condition agreed upon by purchaser and seller. Hardness shall be measured on representative samples from each heat treat lot.
SCOPE
1.1 This specification describes requirements for alloys to be used as components in the manufacture of bonded multi-component thermostat metal strip. More specifically it describes alloys having composition, and thermal expansion suitable for application in thermostat metal sheet and strip.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM B936-23(Specification)
Standard Specification for Copper-Chromium-Iron-Titanium Alloy Plate, Sheet, Strip and Rolled Bar

ABSTRACT
This specification establishes the requirements for plates, sheets, strips, and rolled bars of copper-chromium-iron-titanium alloys with Copper Alloy UNS No. C18080. The material for manufacture shall be a cast bar, cake, slab or so forth of such purity and soundness as to be suitable for processing by hot working, cold working, and subsequent annealing to produce finished products that have a uniform wrought structure and meet the specified temper properties. Products shall be available in the mill hardened temper (TM). Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (mass, thickness, width, length, straightness, and edge), mechanical (tensile strength and Rockwell hardness), electrical (resistivity and equivalent conductivity), and chemical composition requirements.
SCOPE
1.1 This specification covers the requirements for Copper Alloy UNS No. C18080 for plate, sheet, strip, and rolled bar.
Note 1: Since Copper Alloy UNS No. C18080 is frequently used in a variety of applications where yield strength and stress-corrosion resistance may be critical, it is recommended that drawings or samples of the part to be fabricated and details of application be submitted for use in establishing temper and treatment of material.
Note 2: Copper Alloy UNS No. C18080 is covered by a patent. Interested parties are invited to submit information regarding the identification of an alternative(s) to this patented item to ASTM International headquarters. Your comments will receive careful consideration at a meeting of the responsible technical committee,1 which you may attend.  
1.2 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following safety hazard caveat pertains only to the test method(s) described in this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM B928/B928M-15(2023)e1(Specification)
Standard Specification for High Magnesium Aluminum-Alloy Products for Marine Service and Similar Environments

ABSTRACT
This specification covers high magnesium marine application aluminum-alloy in those alloy tempers for flat sheet, coiled sheet, and plate, in the mill finish that are intended for marine and similar environments. An inspection lot shall consist of an identifiable quantity of material of the same mill form, alloy, temper, cast or melt lot, and thickness, subjected to inspection at one time. The material shall be supplied in the mill finish and shall be uniform as defined by the requirements of this specification and shall be commercially sound. Each coil, sheet and plate shall be examined to determine conformance to this specification with respect to general quality and identification marking. One sample shall be taken from each end of each parent coil, or parent plate. Alloy-tempers are manufactured and corrosion tested for intended use in marine hull construction or in marine applications where frequent or constant direct contact with seawater is expected. The specimen shall be capable of exhibiting resistance to intergranular corrosion as indicated by an acceptable mass-loss when tested and shall also be capable of exhibiting no evidence of exfoliation or corrosion. Under metallographic examination, the microstructure of a sample from each production lot shall be compared to that of the producer-established reference photomicrograph of acceptable material, in the same thickness range. Each shipping container shall be marked with the purchase order number, material size, specification number, alloy and temper, gross and net weights, and the producer's name or trademark.
SCOPE
1.1 This specification covers high magnesium aluminum-alloy products in the mill finish condition that are intended for marine hull construction and other marine applications where frequent or constant direct contact with seawater is expected and for similar environments (Note 1). Aluminum alloy products covered by this specification include the alloy-tempers of flat sheet, coiled sheet, and plate shown in Table 2 [Table 3] and Table 4 [Table 5], and alloy-tempers of extruded profiles shown in Table 6 [Table 7].
Note 1: There are other aluminum alloy-temper products that may be suitable for use in marine and similar environments, but which may not require the corrosion resistance testing specified by B928/B928M. See Specification B209/B209M for other aluminum sheet and plate alloy-temper products. For other aluminum extruded alloy-temper products see Specification B221 or B221M and/or other relevant specifications for aluminum extruded products.  
1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1 (M). The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A95083 for 5083 in accordance with Practice E527.  
1.3 The values stated in either SI units (Table 3 and Table 5) or inch-pound units (Table 2 and Table 4) are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of each other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    15 pages
    English language
    sale 15% off
ASTM
ASTM E527-23(Practice)
Standard Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)

SIGNIFICANCE AND USE
4.1 The UNS provides a means of correlating many nationally used numbering systems currently administered by societies, trade associations, and individual users and producers of metals and alloys, thereby avoiding confusion caused by use of more than one identification number for the same material; and by the opposite situation of having the same number assigned to two or more entirely different materials. It also provides the uniformity necessary for efficient indexing, record keeping, data storage and retrieval, and cross referencing.  
4.2 A UNS number is not in itself a specification, since it establishes no requirements for form, condition, quality, etc. It is a unified identification of metals and alloys for which controlling limits have been established in specifications published elsewhere.
Note 5: Organizations that issue specifications should report to appropriate UNS number-assigning offices (3.1.2) any specification changes that affect descriptions shown in published UNS listings.
SCOPE
1.1 This practice (Note 1) covers a unified numbering system (UNS) for metals and alloys that have a “commercial standing” (see Note 2), and covers the procedure by which such numbers are assigned. Section 2 describes the system of alphanumeric designations or “numbers” established for each family of metals and alloys. Section 3 outlines the organization established for administering the system. Section 5 describes the procedure for requesting number assignment to metals and alloys for which UNS numbers have not previously been assigned.
Note 1: UNS designations are not to be used for metals and alloys that are not registered under the system described herein, or for any metal or alloy whose composition differs from those registered.
Note 2: The terms “commercial standing,” “production usage,” and other similar terms are intended to apply to metals and alloys in active commercial production and use, although the actual amount of such use will depend, among other things, upon the type of metals and alloys involved and their application.
The various standardizing organizations involved with the individual industries apply their own established criteria to define the status of a metal or alloy in terms of when a UNS designation number will be assigned. For instance, ASTM Committee A01 requires details of heat analysis, mechanical properties, and processing requirements for addition of a new grade or alloy to its specifications. The Copper Development Association requires that the material be “in commercial use (without tonnage limits);” the Aluminum Association requires that the alloy be “offered for sale (not necessarily in commercial use);” the SAE Aerospace Materials Division calls for “repetitive procurement by at least two users.”
Thus, while no universal definition for usage criteria is established, the UNS numbers are intended to identify metals and alloys that are generally in regular production and use. A UNS number will not ordinarily be issued for a material that has just been conceived or that is still in only experimental trial.  
1.2 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM B899-21(Terminology)
Standard Terminology Relating to Non-ferrous Metals and Alloys

SIGNIFICANCE AND USE
2.1 The terms defined in this document are generic in respect to the standards under the jurisdiction of Committee B02 on Nonferrous Metals and Alloys. The same terms may have different definitions in other ASTM technical committees.  
2.2 Some definitions may differ within the committee because of limitations on items such as weights or dimensions. In such cases the terms will be more precisely defined in the Terminology section of the standards in which these terms are used.
SCOPE
1.1 To promote precise understanding and interpretation of standards, reports, and other technical writings promulgated by Committee B02.  
1.2 To standardize the terminology used in these documents.  
1.3 To explain the meanings of technical terms used within these documents for those not conversant with them.  
1.4 Some definitions include a discussion section, which is a mandatory part of the definition and contains additional information that is relevant to the meaning of the defined term.  
1.5 Definitions of terms specific to a particular standard will appear in that standard and will supersede any definitions of identical terms in this standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off