ASTM D3107-07(2011)
(Test Method)Standard Test Methods for Stretch Properties of Fabrics Woven from Stretch Yarns
Standard Test Methods for Stretch Properties of Fabrics Woven from Stretch Yarns
SIGNIFICANCE AND USE
these test methods are used to determine the stretch, growth and recovery properties that garments made with the fabric tested may be expected to exhibit during use.
these test methods is not recommended for acceptance testing of commercial shipments because the between-laboratory precision is known to be poor.
If there are differences of practical significance between reported test results for two or more laboratories, comparative tests should be performed by those laboratories to determine if there is a statistical bias between them, using competent statistical assistance. Use test samples that are as homogeneous as possible, are drawn from the material from which the disparate test results were obtained, and are randomly assigned in equal numbers to each laboratory for testing. The test results from the two laboratories should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If a bias is found, either its cause must be found and corrected, or future test results for that material must be adjusted in consideration of the known bias.
Some stretch fabrics are constructed with stretch yarns in only the filling direction. Consequently, for those fabrics, only the filling direction needs to be tested.
SCOPE
1.1 These test methods cover the determination of the amount of fabric stretch, fabric growth, and fabric recovery of fabrics woven in whole or in part from stretch yarns after a specified tension and extension.
1.2 These test methods are intended for use with woven fabrics exhibiting high stretch (greater than 12 percent) and good recovery properties from low tension (up to 360 g/cm or 2 lb/in. of fabric width). When agreed upon, these test methods can be used for fabrics woven in whole or in part from non-stretch yarns that exhibit limits within the stretch characteristics shown above.
1.3 These test methods allow the use of two tension options commonly used in the textile industry; 1.35 kg (3 lb.) and 1.8 kg (4 lb). Several calculations are included for fabric stretch, fabric growth and fabric recovery, and can be used individually when required by individual specifications.
1.4 These test methods should not be used to measure breaking elongation of woven fabrics which is covered in Test Method D5035.
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as the standard. Within the text, the inch-pound units are shown in parentheses. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D3107 − 07(Reapproved 2011)
Standard Test Methods for
1
Stretch Properties of Fabrics Woven from Stretch Yarns
This standard is issued under the fixed designation D3107; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope 2. Referenced Documents
2
2.1 ASTM Standards:
1.1 These test methods cover the determination of the
D123 Terminology Relating to Textiles
amount of fabric stretch, fabric growth, and fabric recovery of
D1776 Practice for Conditioning and Testing Textiles
fabrics woven in whole or in part from stretch yarns after a
D2904 Practice for Interlaboratory Testing of a Textile Test
specified tension and extension.
Method that Produces Normally Distributed Data (With-
3
1.2 These test methods are intended for use with woven
drawn 2008)
fabrics exhibiting high stretch (greater than 12 percent) and
D2906 Practice for Statements on Precision and Bias for
3
good recovery properties from low tension (up to 360 g/cm or
Textiles (Withdrawn 2008)
2 lb/in. of fabric width).When agreed upon, these test methods
D4848 Terminology Related to Force, Deformation and
can be used for fabrics woven in whole or in part from
Related Properties of Textiles
non-stretch yarns that exhibit limits within the stretch charac- D4849 Terminology Related to Yarns and Fibers
teristics shown above.
D4850 Terminology Relating to Fabrics and Fabric Test
Methods
1.3 These test methods allow the use of two tension options
D5035 Test Method for Breaking Force and Elongation of
commonly used in the textile industry; 1.35 kg (3 lb) and 1.8
Textile Fabrics (Strip Method)
kg (4 lb). Several calculations are included for fabric stretch,
fabricgrowthandfabricrecovery,andcanbeusedindividually
3. Terminology
when required by individual specifications.
3.1 For all terminology related to Fabric, refer to Terminol-
ogy D4850.
1.4 These test methods should not be used to measure
breaking elongation of woven fabrics which is covered in Test
3.2 For all terminology related to Yarns and Fiber, refer to
Method D5035.
Terminology D4849.
1.5 The values stated in either SI units or inch-pound units
3.3 For all terminology related to Force, Deformation and
are to be regarded separately as the standard. Within the text, Related Properties of Textiles, refer to Terminology D4848
the inch-pound units are shown in parentheses. The values 3.3.1 The following terms are relevant to this standard:
stated in each system are not exact equivalents; therefore, each benchmarks,fabricstretch,fabricgrowth,stretchyarn,tension
system shall be used independently of the other. Combining
3.4 For all other terminology related to textiles, refer to
values from the two systems may result in nonconformance
Terminology D123.
with the specification.
4. Summary of Test Methods
1.6 This standard does not purport to address all of the
4.1 Fabric Stretch under a Specified Tension—Bench marks
safety concerns, if any, associated with its use. It is the
ofaknowndistancearemadeonafabricspecimen.Aspecified
responsibility of the user of this standard to establish appro-
tension is applied to a fabric specimen by a prescribed
priate safety and health practices and determine the applica-
technique and the resulting distance between bench marks
bility of regulatory limitations prior to use.
whilethespecimenisunderthetensionismeasured.Thefabric
1 2
These test methods are under the jurisdiction of ASTM Committee D13 on For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Textiles and is the direct responsibility of Subcommittee D13.59 on Fabric Test contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Methods, General. Current edition approved May 1, 2011. Published June 2011. Standards volume information, refer to the standard’s Document Summary page on
Originally approved in 1975 as D3107–75. Discontinued September 1999 and the ASTM website.
3
reinstated in 2003 as D3107–03. Last previous edition approved in 2007 as The last approved version of this historical standard is referenced on
ε1
D3107–07 . DOI: 10.1520/D3107-07R11. www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D3107 − 07 (2011)
stretch is calculated from the length difference between bench 6.1.2 Separate Clamp, or other means of attaching a weight
marks prior to application of the tension and while under the with a known mass to the bottom of the te
...