ASTM D874-13a(2018)
(Test Method)Standard Test Method for Sulfated Ash from Lubricating Oils and Additives
Standard Test Method for Sulfated Ash from Lubricating Oils and Additives
SIGNIFICANCE AND USE
5.1 The sulfated ash can be used to indicate the concentration of known metal-containing additives in new oils. When phosphorus is absent, barium, calcium, magnesium, sodium and potassium are converted to their sulfates and tin (stannic) and zinc to their oxides (Note 4). Sulfur and chlorine do not interfere, but when phosphorus is present with metals, it remains partially or wholly in the sulfated ash as metal phosphates.
Note 4: Since zinc sulfate slowly decomposes to its oxide at the ignition temperature specified in the test method, samples containing zinc can give variable results unless the zinc sulfate is completely converted to the oxide.
5.2 Because of above inter-element interferences, experimentally obtained sulfated ash values may differ from sulfated ash values calculated from elemental analysis. The formation of such non-sulfated species is dependent on the temperature of ashing, time ashed, and the composition of metal compounds present in oils. Hence, sulfated ash requirement generally should not be used in product specifications without a clear understanding between a buyer and a seller of the unreliability of an ash value as an indicator of the total metallic compound content.4
SCOPE
1.1 This test method covers the determination of the sulfated ash from unused lubricating oils containing additives and from additive concentrates used in compounding. These additives usually contain one or more of the following metals: barium, calcium, magnesium, zinc, potassium, sodium, and tin. The elements sulfur, phosphorus, and chlorine can also be present in combined form.
1.2 Application of this test method to sulfated ash levels below 0.02 % by mass is restricted to oils containing ashless additives. The lower limit of the test method is 0.005 % by mass sulfated ash.
Note 1: This test method is not intended for the analysis of used engine oils or oils containing lead. Neither is it recommended for the analysis of nonadditive lubricating oils, for which Test Method D482 can be used.
Note 2: There is evidence that magnesium does not react the same as other alkali metals in this test. If magnesium additives are present, the data is interpreted with caution.
Note 3: There is evidence that samples containing molybdenum can give low results because molybdenum compounds are not fully recovered at the temperature of ashing.
1.3 Fatty acid methyl ester (FAME) conforming to EN 14213 and EN 14214, when tested using this test method, were shown to meet its precision.
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D874 − 13a (Reapproved 2018) British Standard 4716
Standard Test Method for
1
Sulfated Ash from Lubricating Oils and Additives
This standard is issued under the fixed designation D874; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope 1.6 This international standard was developed in accor-
dance with internationally recognized principles on standard-
1.1 This test method covers the determination of the sul-
ization established in the Decision on Principles for the
fated ash from unused lubricating oils containing additives and
Development of International Standards, Guides and Recom-
from additive concentrates used in compounding. These addi-
mendations issued by the World Trade Organization Technical
tives usually contain one or more of the following metals:
Barriers to Trade (TBT) Committee.
barium, calcium, magnesium, zinc, potassium, sodium, and tin.
The elements sulfur, phosphorus, and chlorine can also be
2. Referenced Documents
present in combined form.
2
2.1 ASTM Standards:
1.2 Application of this test method to sulfated ash levels
D482 Test Method for Ash from Petroleum Products
below 0.02 % by mass is restricted to oils containing ashless
D1193 Specification for Reagent Water
additives. The lower limit of the test method is 0.005 % by
D4057 Practice for Manual Sampling of Petroleum and
mass sulfated ash.
Petroleum Products
NOTE 1—This test method is not intended for the analysis of used
D4177 Practice for Automatic Sampling of Petroleum and
engine oils or oils containing lead. Neither is it recommended for the
Petroleum Products
analysis of nonadditive lubricating oils, for which Test Method D482 can
D6299 Practice for Applying Statistical Quality Assurance
be used.
and Control Charting Techniques to Evaluate Analytical
NOTE 2—There is evidence that magnesium does not react the same as
other alkali metals in this test. If magnesium additives are present, the data Measurement System Performance
is interpreted with caution.
3
2.2 CEN Standards:
NOTE 3—There is evidence that samples containing molybdenum can
EN 14213 Heating Fuels—Fatty Acid Methyl Esters
give low results because molybdenum compounds are not fully recovered
at the temperature of ashing. (FAME)—Requirements and Test Methods
EN 14214 Automotive Fuels—Fatty Acid Methyl Esters
1.3 Fatty acid methyl ester (FAME) conforming to EN
(FAME) for Diesel Engines—Requirements and Test
14213 and EN 14214, when tested using this test method, were
Methods
shown to meet its precision.
1.4 The values stated in SI units are to be regarded as
3. Terminology
standard. No other units of measurement are included in this
3.1 Definitions:
standard.
3.1.1 sulfated ash, n—the residue remaining after the
1.5 This standard does not purport to address all of the
sample has been carbonized, and the residue subsequently
safety concerns, if any, associated with its use. It is the
treated with sulfuric acid and heated to constant weight.
responsibility of the user of this standard to establish appro-
priate safety, health, and environmental practices and deter-
4. Summary of Test Method
mine the applicability of regulatory limitations prior to use.
4.1 The sample is ignited and burned until only ash and
carbon remain. After cooling, the residue is treated with
sulfuric acid and heated at 775 °C until oxidation of carbon is
1
This test method is under the jurisdiction of ASTM Committee D02 on
Petroleum Products, Liquid Fuels, and Lubricants and is the direct responsibility of
Subcommittee D02.03 on Elemental Analysis.
2
Current edition approved April 1, 2018. Published June 2018. Originally For referenced ASTM standards, visit the ASTM website, www.astm.org, or
approved in 1946. Last previous edition approved in 2013 as D874 – 13a. DOI: contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
10.1520/D0874-13AR18. Standards volume information, refer to the standard’s Document Summary page on
In the IP, this test method is under the jurisdiction of the Standardization the ASTM website.
3
Committee. This test method has been approved by the sponsoring committees and Available from European Committee for Standardization (CEN), Avenue
accepted by the cooperating societies in accordance with established procedures. Marnix 17, B-1000, Brussels, Belgium, http://www.cen.eu.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ---------------------
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D874 − 13a D874 − 13a (Reapproved 2018) British Standard 4716
Standard Test Method for
1
Sulfated Ash from Lubricating Oils and Additives
This standard is issued under the fixed designation D874; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope*Scope
1.1 This test method covers the determination of the sulfated ash from unused lubricating oils containing additives and from
additive concentrates used in compounding. These additives usually contain one or more of the following metals: barium, calcium,
magnesium, zinc, potassium, sodium, and tin. The elements sulfur, phosphorus, and chlorine can also be present in combined form.
1.2 Application of this test method to sulfated ash levels below 0.02 mass % 0.02 % by mass is restricted to oils containing
ashless additives. The lower limit of the test method is 0.005 mass % 0.005 % by mass sulfated ash.
NOTE 1—This test method is not intended for the analysis of used engine oils or oils containing lead. Neither is it recommended for the analysis of
nonadditive lubricating oils, for which Test Method D482 can be used.
NOTE 2—There is evidence that magnesium does not react the same as other alkali metals in this test. If magnesium additives are present, the data is
interpreted with caution.
NOTE 3—There is evidence that samples containing molybdenum can give low results because molybdenum compounds are not fully recovered at the
temperature of ashing.
1.3 Fatty acid methyl ester (FAME) conforming to EN 14213 and EN 14214, when tested using this test method, were shown
to meet its precision.
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety safety, health, and healthenvironmental practices and determine the
applicability of regulatory limitations prior to use.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
D482 Test Method for Ash from Petroleum Products
D1193 Specification for Reagent Water
D4057 Practice for Manual Sampling of Petroleum and Petroleum Products
D4177 Practice for Automatic Sampling of Petroleum and Petroleum Products
D6299 Practice for Applying Statistical Quality Assurance and Control Charting Techniques to Evaluate Analytical Measure-
ment System Performance
3
2.2 CEN Standards:
EN 14213 Heating Fuels—Fatty Acid Methyl Esters (FAME)—Requirements and Test Methods
EN 14214 Automotive Fuels—Fatty Acid Methyl Esters (FAME) for Diesel Engines—Requirements and Test Methods
1
This test method is under the jurisdiction of ASTM Committee D02 on Petroleum Products Products, Liquid Fuels, and Lubricants and is the direct responsibility of
Subcommittee D02.03 on Elemental Analysis.
Current edition approved Sept. 1, 2013April 1, 2018. Published September 2013June 2018. Originally approved in 1946. Last previous edition approved in 2013 as
D874 – 13.D874 – 13a. DOI: 10.1520/D0874-13A.10.1520/D0874-13AR18.
In the IP, this test method is under the jurisdiction of the Standardization Committee. This test method has been approved by the sponsoring committees and accepted by
the cooperating societies in accordance with established procedures.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
3
Available from European Committee for Standardization (CEN-CENELEC Management Centre), (CEN), Avenue Marnix 17, B-1000, Brussels, Belgium,
http://www.cenorm.be.http://www.cen.eu.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West C
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.