ASTM C1361-10(2019)
(Practice)Standard Practice for Constant-Amplitude, Axial, Tension-Tension Cyclic Fatigue of Advanced Ceramics at Ambient Temperatures
Standard Practice for Constant-Amplitude, Axial, Tension-Tension Cyclic Fatigue of Advanced Ceramics at Ambient Temperatures
SIGNIFICANCE AND USE
4.1 This practice may be used for material development, material comparison, quality assurance, characterization, reliability assessment, and design data generation.
4.2 High-strength, monolithic advanced ceramic materials are generally characterized by small grain sizes (
4.3 Cyclic fatigue by its nature is a probabilistic phenomenon as discussed in STP 91A and STP 588 (1, 2).4 In addition, the strengths of advanced ceramics are probabilistic in nature. Therefore, a sufficient number of test specimens at each testing condition is required for statistical analysis and design, with guidelines for sufficient numbers provided in STP 91A (1), STP 588 (2), and Practice E739. The many different tensile specimen geometries available for cyclic fatigue testing may result in variations in the measured cyclic fatigue behavior of a particular material due to differences in the volume or surface area of material in the gage section of the test specimens.
4.4 Tensile cyclic fatigue tests provide information on the material response under fluctuating uniaxial tensile stresses. Uniform stress states are required to effectively evaluate any nonlinear stress-strain behavior which may develop as the result of cumulative damage processes (for example, microcracking, cyclic fatigue crack growth, etc.).
4.5 Cumulative damage processes due to cyclic fatigue may be influenced by testing mode, testing rate (related to frequency), differences between maximum and minimum force (R or Α), effects of processing or combinations of constituent materials, or environmental influences, or both. Other factors that influence cyclic fatigue behavior are: void or porosity content, methods of test specimen preparation or fabrication,test specimen conditioning, test environment, force or strain limits during cycling, wave shapes (that is, sinusoidal, trapezoidal, etc.), and failure mode. Some of these effects may be consequences of stress corrosion or sub-critical (slow) crack growth which can...
SCOPE
1.1 This practice covers the determination of constant-amplitude, axial, tension-tension cyclic fatigue behavior and performance of advanced ceramics at ambient temperatures to establish “baseline” cyclic fatigue performance. This practice builds on experience and existing standards in tensile testing advanced ceramics at ambient temperatures and addresses various suggested test specimen geometries, test specimen fabrication methods, testing modes (force, displacement, or strain control), testing rates and frequencies, allowable bending, and procedures for data collection and reporting. This practice does not apply to axial cyclic fatigue tests of components or parts (that is, machine elements with nonuniform or multiaxial stress states).
1.2 This practice applies primarily to advanced ceramics that macroscopically exhibit isotropic, homogeneous, continuous behavior. While this practice applies primarily to monolithic advanced ceramics, certain whisker- or particle-reinforced composite ceramics, as well as certain discontinuous fibre-reinforced composite ceramics, may also meet these macroscopic behavior assumptions. Generally, continuous fibre-reinforced ceramic composites (CFCCs) do not macroscopically exhibit isotropic, homogeneous, continuous behavior and application of this practice to these materials is not recommended.
1.3 The values stated in SI units are to be regarded as the standard and are in accordance with IEEE/ASTM SI 10.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Refer to Section 7 for specific precautions.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established ...
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: C1361 − 10 (Reapproved 2019)
Standard Practice for
Constant-Amplitude, Axial, Tension-Tension Cyclic Fatigue
of Advanced Ceramics at Ambient Temperatures
This standard is issued under the fixed designation C1361; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom-
1.1 This practice covers the determination of constant-
mendations issued by the World Trade Organization Technical
amplitude, axial, tension-tension cyclic fatigue behavior and
Barriers to Trade (TBT) Committee.
performance of advanced ceramics at ambient temperatures to
establish “baseline” cyclic fatigue performance. This practice
2. Referenced Documents
builds on experience and existing standards in tensile testing
advanced ceramics at ambient temperatures and addresses 2
2.1 ASTM Standards:
various suggested test specimen geometries, test specimen
C1145 Terminology of Advanced Ceramics
fabrication methods, testing modes (force, displacement, or
C1273 Test Method for Tensile Strength of Monolithic
strain control), testing rates and frequencies, allowable
Advanced Ceramics at Ambient Temperatures
bending, and procedures for data collection and reporting.This
C1322 Practice for Fractography and Characterization of
practice does not apply to axial cyclic fatigue tests of compo-
Fracture Origins in Advanced Ceramics
nents or parts (that is, machine elements with nonuniform or
E4 Practices for Force Verification of Testing Machines
multiaxial stress states).
E6 Terminology Relating to Methods of Mechanical Testing
1.2 This practice applies primarily to advanced ceramics
E83 Practice for Verification and Classification of Exten-
that macroscopically exhibit isotropic, homogeneous, continu-
someter Systems
ous behavior. While this practice applies primarily to mono-
E337 Test Method for Measuring Humidity with a Psy-
lithic advanced ceramics, certain whisker- or particle-
chrometer (the Measurement of Wet- and Dry-Bulb Tem-
reinforced composite ceramics, as well as certain
peratures)
discontinuous fibre-reinforced composite ceramics, may also
E467 Practice for Verification of Constant Amplitude Dy-
meet these macroscopic behavior assumptions. Generally,
namic Forces in an Axial Fatigue Testing System
continuous fibre-reinforced ceramic composites (CFCCs) do
E468 Practice for Presentation of Constant Amplitude Fa-
not macroscopically exhibit isotropic, homogeneous, continu-
tigue Test Results for Metallic Materials
ous behavior and application of this practice to these materials
E739 PracticeforStatisticalAnalysisofLinearorLinearized
is not recommended.
Stress-Life (S-N) and Strain-Life (ε-N) Fatigue Data
1.3 The values stated in SI units are to be regarded as the
E1012 Practice for Verification of Testing Frame and Speci-
standard and are in accordance with IEEE/ASTM SI 10.
men Alignment Under Tensile and Compressive Axial
Force Application
1.4 This standard does not purport to address all of the
E1823 TerminologyRelatingtoFatigueandFractureTesting
safety concerns, if any, associated with its use. It is the
IEEE/ASTM SI 10 American National Standard for Metric
responsibility of the user of this standard to establish appro-
Practice
priate safety, health, and environmental practices and deter-
mine the applicability of regulatory limitations prior to use.
2.2 Military Handbook:
Refer to Section 7 for specific precautions.
MIL-HDBK-790 Fractography and Characterization of
1.5 This international standard was developed in accor-
Fracture Origins in Advanced Structural Ceramics
dance with internationally recognized principles on standard-
1 2
This practice is under the jurisdiction of ASTM Committee C28 on Advanced For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Ceramics and is the direct responsibility of Subcommittee C28.01 on Mechanical contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Properties and Performance. Standards volume information, refer to the standard’s Document Summary page on
Current edition approved July 1, 2019. Published July 2019. Originally approved the ASTM website.
in 1996. Last previous edition approved in 2015 as C1361 – 10 (2015). DOI: Available from Army Research Laboratory-Materials Directorate, Aberdeen
10.1520/C1361-10R19. Proving Ground, MD 21005.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
C1361 − 10 (2019)
–2
3.2.7 cyclic fatigue limit, S, [FL ], n—thelimitingvalueof
f
the median cyclic fatigue strength as the cyclic fatigue life, N,
f
6 7
becomes very large (for example,N>10 -10 ). (See Termi-
nology E1823.)
3.2.7.1 Discussion—Certain materials and environments
preclude the attainment of a cyclic fatigue limit. Values
tabulated as cyclic fatigue limits in the literature are frequently
(but not always) values of S at 50 % survival at N cycles of
f f
stress in which the mean stress, S , equals zero.
m
–2
3.2.8 cyclic fatigue strength S , [FL ], n—the limiting
N
valueofthemediancyclicfatiguestrengthataparticularcyclic
fatigue life, N. (See Terminology E1823.)
f
3.2.9 gage length, [L], n—the original length of that portion
of the test specimen over which strain or change of length is
FIG. 1 Cyclic Fatigue Nomenclature and Wave Forms
determined. (See Terminology E6.)
3.2.10 load ratio, n—in cyclic fatigue loading, the algebraic
3. Terminology
ratio of the two loading parameters of a cycle; the most widely
3.1 Definitions—Definitions of terms relating to advanced
used ratios (see Terminology E1823):
ceramics, cyclic fatigue, and tensile testing as they appear in
minimum force valley force
Terminology C1145, Terminology E1823, and Terminology
R 5 or R 5
maximumforce peak force
E6, respectively, apply to the terms used in this practice.
Selected terms with definitions non-specific to this practice and:
follow in 3.2, with the appropriate source given in parentheses.
force amplitude maximum force 2 minimum force
~ !
Α 5 orΑ 5
Terms specific to this practice are defined in 3.3.
mean force maximum force1minimum force
~ !
3.2 Definitions of Terms Non-Specific to This Standard: –2
3.2.11 modulus of elasticity [FL ], n—the ratio of stress to
3.2.1 advanced ceramic, n—a highly engineered, high-
corresponding strain below the proportional limit. (See Termi-
performance, predominately non-metallic, inorganic, ceramic
nology E6.)
material having specific functional attributes. (See Terminol-
3.2.12 percent bending, n—the bending strain times 100
ogy C1145.)
divided by the axial strain. (See Practice E1012.)
–1
3.2.2 axial strain [LL ], n—theaveragelongitudinalstrains
measured at the surface on opposite sides of the longitudinal 3.2.13 S-Ndiagram,n—aplotofstressversusthenumberof
cycles to failure. The stress can be maximum stress, S ,
axis of symmetry of the test specimen by two strain-sensing
max
devices located at the mid length of the reduced section. (See minimum stress, S , stress range, ∆S or S , or stress
min r
amplitude, S . The diagram indicates the S-N relationship for a
Practice E1012.)
a
–1
specified value of S , Α, R, and a specified probability of
m
3.2.3 bending strain [LL ], n—the difference between the
survival. For N, a log scale is almost always used, although a
strainatthesurfaceandtheaxialstrain.Ingeneral,thebending
linear scale may also be used. For S, a linear scale is usually
strain varies from point to point around and along the reduced
used, although a log scale may also be used. (See Terminology
section of the test specimen. (See Practice E1012.)
E1823 and Practice E468.)
3.2.4 constant amplitude loading, n—in cyclic fatigue
3.2.14 slow crack growth, n—sub-critical crack growth
loading, a loading in which all peak loads are equal and all of
(extension) that may result from, but is not restricted to, such
the valley forces are equal. (See Terminology E1823.)
mechanisms as environmentally assisted stress corrosion or
3.2.5 cyclic fatigue, n—the process of progressive localized
diffusive crack growth.
permanent structural change occurring in a material subjected
–2
3.2.15 tensile strength [FL ], n—the maximum tensile
to conditions that produce fluctuating stresses and strains at
some point or points and that may culminate in cracks or stress which a material is capable of sustaining. Tensile
completefractureafterasufficientnumberoffluctuations.(See strengthiscalculatedfromthemaximumforceduringatension
Terminology E1823.) See Fig. 1 for nomenclature relevant to test carried to rupture and the original cross-sectional area of
cyclic fatigue testing. the test specimen. (See Terminology E6.)
3.2.5.1 Discussion—In glass technology, static tests of con-
3.3 Definitions of Terms Specific to This Standard:
siderable duration are called static fatigue tests, a type of test
–2
3.3.1 maximum stress, S [FL ], n—the maximum ap-
max
generally designated as stress-rupture.
plied stress during cyclic fatigue.
3.2.5.2 Discussion—Fluctuations may occur both in load
–2
3.3.2 mean stress, S [FL ], n—the average applied
and with time (frequency) as in the case of random vibration.
max
stress during cyclic fatigue such that
3.2.6 cyclic fatigue life, N—thenumberofloadingcyclesof
f
a specified character that a given test specimen sustains before S 1S
max min
S 5 (1)
m
failure of a specified nature occurs. (See Terminology E1823.) 2
C1361 − 10 (2019)
–2
3.3.3 minimum stress, S [FL ], n—the minimum applied test specimen conditioning, test environment, force or strain
min
stress during cyclic fatigue. limits during cycling, wave shapes (that is, sinusoidal,
–2
trapezoidal, etc.), and failure mode. Some of these effects may
3.3.4 stress amplitude, S [FL ], n—the difference between
a
beconsequencesofstresscorrosionorsub-critical(slow)crack
the mean stress and the maximum or minimum stress such that
growth which can be difficult to quantify. In addition, surface
S 2 S
max min
or near-surface flaws introduced by the test specimen fabrica-
S 5 5 S 2 S 5 S 2 S (2)
a max m m min
tion process (machining) may or may not be quantifiable by
–2
3.3.5 stress range, ∆SorS [FL ], n—the difference
r conventional measurements of surface texture. Therefore, sur-
between the maximum stress and the minimum stress such that
face effects (for example, as reflected in cyclic fatigue reduc-
∆S = S = S – S
r max min tion factors as classified by Marin (3)) must be inferred from
the results of numerous cyclic fatigue tests performed with test
3.3.6 time to cyclic fatigue failure, tf [t], n—total elapsed
timefromtestinitiationtotestterminationrequiredtoreachthe specimens having identical fabrication histories.
number of cycles to failure.
4.6 The results of cyclic fatigue tests of specimens fabri-
cated to standardized dimensions from a particular material or
4. Significance and Use
selected portions of a part, or both, may not totally represent
4.1 This practice may be used for material development,
thecyclicfatiguebehavioroftheentirefull-sizeendproductor
material comparison, quality assurance, characterization, reli-
its in-service behavior in different environments.
ability assessment, and design data generation.
4.7 However, for quality control purposes, results derived
4.2 High-strength, monolithic advanced ceramic materials
from standardized tensile test specimens may be considered
are generally characterized by small grain sizes (<50 µm) and
indicativeoftheresponseofthematerialfromwhichtheywere
bulk densities near the theoretical density. These materials are
taken for given primary processing conditions and post-
candidates for load-bearing structural applications requiring
processing heat treatments.
high degrees of wear and corrosion resistance, and high-
4.8 The cyclic fatigue behavior of an advanced ceramic is
temperature strength. Although flexural test methods are com-
dependent on its inherent resistance to fracture, the presence of
monly used to evaluate strength of advanced ceramics, the
flaws, or damage accumulation processes, or both. There can
nonuniform stress distribution in a flexure specimen limits the
be significant damage in the test specimen without any visual
volume of material subjected to the maximum applied stress at
evidence such as the occurrence of a macroscopic crack. This
fracture. Uniaxially loaded tensile strength tests may provide
can result in a specific loss of stiffness and retained strength.
information on strength-limiting flaws from a greater volume
Depending on the purpose for which the test is being
of uniformly stressed material.
conducted, rather than final fracture, a specific loss in stiffness
4.3 Cyclic fatigue by its nature is a probabilistic phenom-
or retained strength may constitute failure. In cases where
enon as discussed in STP91Aand STP588 (1, 2). In addition,
fracture occurs, analysis of fracture surfaces and fractography,
the strengths of advanced ceramics are probabilistic in nature.
though beyond the scope of this practice, are recommended.
Therefore, a sufficient number of test specimens at each testing
condition is required for statistical analysis and design, with
5. Interferences
guidelinesforsufficientnumbersprovidedinSTP91A (1),STP
5.1 Test environment (vacuum, inert gas, ambient air, etc.),
588 (2), and Practice E739. The many different tensile speci-
including moisture content (for example, relative humidity),
men geometries available for cyclic fatigue testing may result
mayhaveaninfluenceonthemeasuredcyclicfatiguebehavior.
in variations in the measured cyclic fatigue behavior of a
In particular, the behavior of materials susceptible to slow
particular material due to differences in the volume or surface
crack growth fracture will be strongly influenced by test
area of material in the gage section of the test specimens.
environment and testing rate. Conduct tests to evaluate the
4.4 Tensile cyclic fatigue tests provide information on the
mechanical cyclic fatigue behavior of a material in inert
material response under fluctuating uniaxial tensile stresses.
environments to minimize slow crack growth effects.
Uniform stress states are required to effectively evaluate any
Conversely, conduct tests in environments or at test modes and
nonlinear stress-strain behavior which may develop as the
rates repres
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.