EN ISO 9226:2012

(Main)

Corrosion of metals and alloys - Corrosivity of atmospheres - Determination of corrosion rate of standard specimens for the evaluation of corrosivity (ISO 9226:2012)

Corrosion of metals and alloys - Corrosivity of atmospheres - Determination of corrosion rate of standard specimens for the evaluation of corrosivity (ISO 9226:2012)

ISO 9226:2012 specifies methods which can be used for the determination of corrosion rate with standard specimens. The values obtained from the measurements (corrosion rates for the first year of exposure) are intended to be used as classification criteria for the evaluation of atmospheric corrosivity according to ISO 9223. They can also be used for informative evaluation of atmospheric corrosivity beyond the scope of ISO 9223.

Korrosion von Metallen und Legierungen - Korrosivität von Atmosphären - Bestimmung der Korrosionsgeschwindigkeit von Standardproben zur Ermittlung der Korrosivität (ISO 9226:2012)

Diese Internationale Norm legt Verfahren fest, die zur Bestimmung der Korrosionsgeschwindigkeit mit
Standardproben angewendet werden können. Die aus den Messungen erhaltenen Werte (Korrosionsgeschwindigkeiten
nach dem ersten Jahr der Auslagerung) sind dafür vorgesehen, als
Klassifizierungskriterien zur Ermittlung der atmosphärischen Korrosivität nach ISO 9223 verwendet zu
werden. Sie können außerdem zur informativen Ermittlung der atmosphärischen Korrosivität über den
Anwendungsbereich von ISO 9223 hinaus verwendet werden.

Corrosion des métaux et alliages - Corrosivité des atmosphères - Détermination de la vitesse de corrosion d'éprouvettes de référence pour l'évaluation de la corrosivité (ISO 9226:2012)

L'ISO 9226:2012 spécifie les méthodes utilisables pour déterminer la vitesse de corrosion d'éprouvettes de référence. Les valeurs obtenues par mesurage (vitesses de corrosion pour la première année d'exposition) sont destinées à servir de critères de classification pour l'évaluation de la corrosivité des atmosphères conformément à l'ISO 9223. Elles peuvent également servir pour l'évaluation informative de la corrosivité atmosphérique ne relevant pas du domaine d'application de l'ISO 9223.

Korozija kovin in zlitin - Korozivnost v atmosferskem okolju - Ugotavljanje hitrosti korozije s standardnimi vzorci za ocenjevanje korozivnosti (ISO 9226:2012)

Ta mednarodni standard določa metode, ki jih je mogoče uporabiti za ugotavljanje hitrosti korozije s standardnimi vzorci. Vrednosti, pridobljene z meritvami (hitrosti korozije za prvo leto izpostavljenosti) se uporabljajo kot merila za razvrščanje za ocenjevanje korozivnosti v atmosferskem okolju v skladu s standardom ISO 9223. Uporabljajo se lahko tudi za informativno ocenjevanje korozivnosti v atmosferskem okolju, ki presega področje uporabe standarda ISO 9223.

General Information

Status
Published
Publication Date
31-Jan-2012
Withdrawal Date
30-Aug-2012
ICS
77.060 - Corrosion of metals
Technical Committee
CEN/TC 262 - Metallic and other inorganic coatings
Drafting Committee
CEN/TC 262 - Metallic and other inorganic coatings
Current Stage
6060 - Definitive text made available (DAV) - Publishing
Start Date
01-Feb-2012
Completion Date
01-Feb-2012
Ref Project
SIST EN ISO 9226:2012 - Corrosion of metals and alloys - Corrosivity of atmospheres - Determination of corrosion rate of standard specimens for the evaluation of corrosivity (ISO 9226:2012)

Relations

Replaces
EN 12500:2000 - Protection of metallic materials against corrosion - Corrosion likelihood in atmospheric environment - Classification, determination and estimation of corrosivity of atmospheric environments
Effective Date
08-Jun-2022

Buy Standard

EN ISO 9226:2012EN ISO 9226:2012
PreviousNext
Standard
EN ISO 9226:2012
English language
13 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)

SLOVENSKI STANDARD
SIST EN ISO 9226:2012
01-maj-2012
1DGRPHãþD
SIST EN 12500:2000
Korozija kovin in zlitin - Korozivnost v atmosferskem okolju - Ugotavljanje hitrosti
korozije s standardnimi vzorci za ocenjevanje korozivnosti (ISO 9226:2012)
Corrosion of metals and alloys - Corrosivity of atmospheres - Determination of corrosion
rate of standard specimens for the evaluation of corrosivity (ISO 9226:2012)
Korrosion von Metallen und Legierungen - Korrosivität von Atmosphären - Bestimmung
der Korrosionsgeschwindigkeit von Standardproben zur Ermittlung der Korrosivität (ISO
9226:2012)
Corrosion des métaux et alliages - Corrosivité des atmosphères - Détermination de la
vitesse de corrosion d'éprouvettes de référence pour l'évaluation de la corrosivité (ISO
9226:2012)
Ta slovenski standard je istoveten z: EN ISO 9226:2012
ICS:
77.060 Korozija kovin Corrosion of metals
SIST EN ISO 9226:2012 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST EN ISO 9226:2012

---------------------- Page: 2 ----------------------

SIST EN ISO 9226:2012


EUROPEAN STANDARD
EN ISO 9226

NORME EUROPÉENNE

EUROPÄISCHE NORM
February 2012
ICS 77.060 Supersedes EN 12500:2000
English Version
Corrosion of metals and alloys - Corrosivity of atmospheres -
Determination of corrosion rate of standard specimens for the
evaluation of corrosivity (ISO 9226:2012)
Corrosion des métaux et alliages - Corrosivité des Korrosion von Metallen und Legierungen - Korrosivität von
atmosphères - Détermination de la vitesse de corrosion Atmosphären - Bestimmung der Korrosionsgeschwindigkeit
d'éprouvettes de référence pour l'évaluation de la von Standardproben zur Ermittlung der Korrosivität (ISO
corrosivité (ISO 9226:2012) 9226:2012)
This European Standard was approved by CEN on 22 January 2012.

CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.

This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same
status as the official versions.

CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,
Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom.





EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION

EUROPÄISCHES KOMITEE FÜR NORMUNG

Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2012 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 9226:2012: E
worldwide for CEN national Members.

---------------------- Page: 3 ----------------------

SIST EN ISO 9226:2012
EN ISO 9226:2012 (E)
Contents Page
Foreword .3

2

---------------------- Page: 4 ----------------------

SIST EN ISO 9226:2012
EN ISO 9226:2012 (E)
Foreword
This document (EN ISO 9226:2012) has been prepared by Technical Committee ISO/TC 156 "Corrosion of
metals and alloys" in collaboration with Technical Committee CEN/TC 262 “Metallic and other inorganic
coatings” the secretariat of which is held by BSI.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by August 2012, and conflicting national standards shall be withdrawn at
the latest by August 2012.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN 12500:2000.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,
Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
Sweden, Switzerland, Turkey and the United Kingdom.
Endorsement notice
The text of ISO 9226:2012 has b
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

CEN
EN ISO 10062:2022(Main)
Corrosion tests in artificial atmosphere at very low concentrations of polluting gas(es) (ISO 10062:2022)
SIST EN ISO 10062:2023

This document specifies tests which are intended to determine the influence of one or more flowing polluting gas(es) at volume fractions less than or equal to 10−6 on test samples and/or articles of metals and alloys with or without corrosion protection under determined conditions of temperature and relative humidity.
This document is applicable to
a) metals and their alloys,
b) metallic coatings (anodic and cathodic),
c) metals with conversion coatings,
d) metals with anodic oxide coatings, and
e) metals with organic coatings.

  • Standard
    19 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 9227:2022(Main)
Corrosion tests in artificial atmospheres - Salt spray tests (ISO 9227:2022)
SIST EN ISO 9227:2023

This document specifies the apparatus, the reagents and the procedure to be used in conducting the neutral salt spray (NSS), acetic acid salt spray (AASS) and copper-accelerated acetic acid salt spray (CASS) tests for assessment of the corrosion resistance of metallic materials, with or without permanent or temporary corrosion protection.
It also describes the method employed to evaluate the corrosivity of the test cabinet environment.
It does not specify the dimensions or types of test specimens, the exposure period to be used for a particular product, or the interpretation of results. Such details are provided in the appropriate product specifications.
The salt spray tests are particularly useful for detecting discontinuities, such as pores and other defects, in certain metallic, organic, anodic oxide and conversion coatings.
The NSS test is particularly applicable to:
—    metals and their alloys;
—    metallic coatings (anodic and cathodic);
—    conversion coatings;
—    anodic oxide coatings;
—    organic coatings on metallic materials.
The AASS test is especially useful for testing decorative coatings of copper + nickel + chromium, or nickel + chromium. It has also been found suitable for testing anodic and organic coatings on aluminium.
The CASS test is useful for testing decorative coatings of copper + nickel + chromium, or nickel + chromium. It has also been found suitable for testing anodic and organic coatings on aluminium.
The salt spray methods are all suitable for checking that the quality of a metallic material, with or without corrosion protection, is maintained. They are not intended to be used for comparative testing as a means of ranking different materials relative to each other with respect to corrosion resistance or as means of predicting long-term corrosion resistance of the tested material.

  • Standard
    32 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 22479:2022(Main)
Corrosion of metals and alloys - Sulfur dioxide test in a humid atmosphere (fixed gas method) (ISO 22479:2019)
SIST EN ISO 22479:2022

This document specifies a method for assessing the resistance of materials or products to a humid atmosphere containing sulfur dioxide.
This method is applicable to testing metals and alloys, metallic and non-organic coatings and organic coatings.

  • Standard
    22 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 21207:2022(Main)
Corrosion tests in artificial atmospheres - Accelerated corrosion tests involving alternate exposure to corrosion-promoting gases, neutral salt-spray and drying (ISO 21207:2015)
SIST EN ISO 21207:2022

ISO 21207:2015 defines two accelerated corrosion test methods to be used in assessing the corrosion resistance of products with metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or by winter road de-icing salt, and of corrosion-promoting gases from industrial or traffic air pollution.
ISO 21207:2015 specifies both the test apparatus and test procedures to be used in executing the accelerated corrosion tests.
The methods are especially suitable for assessing the corrosion resistance of sensitive products with metals, e.g. electronic components, used in traffic and industrial environments.

  • Standard
    17 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 16539:2022(Main)
Corrosion of metals and alloys - Accelerated cyclic corrosion tests with exposure to synthetic ocean water salt-deposition process - "Dry" and "wet" conditions at constant absolute humidity (ISO 16539:2013)
SIST EN ISO 16539:2022

This International Standard specifies two accelerated corrosion test procedures, Methods A and B, for the evaluation of corrosion behaviour of surface-treated metals and their alloys with and without paint on them in atmospheric environments. It also specifies the apparatus used. The two tests involve salt deposition and dry/wet conditions at a constant absolute humidity.
Method A applies to:
metals and their alloys (including corrosion-resistance alloys)
Method B applies to:
metals and their alloys
metals and their alloys with coatings [including metallic coatings (anodic or cathodic), organic
coatings, and conversion coatings]

  • Standard
    27 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 10270:2022(Main)
Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO 10270:2022)
SIST EN ISO 10270:2022

This document specifies:
a) the determination of mass gain;
b) the surface inspection of products of zirconium and its alloys when corrosion is tested in water at 360 °C or in steam at or above 400 °C;
c) the performance of tests in steam at 10,3 MPa.
This document is applicable to wrought products, castings, powder metallurgy products and weld metals.
This method has been widely used in the development of new alloys, heat-treating practices and for the evaluation of welding techniques. It is applicable for use in its entirety to the extent specified for a product acceptance test, rather than merely a means of assessing performance in service.

  • Standard
    24 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 7539-9:2021(Main)
Corrosion of metals and alloys - Stress corrosion testing - Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement (ISO 7539-9:2021)
SIST EN ISO 7539-9:2021

1.1  This document specifies procedures for designing, preparing and using pre-cracked specimens for investigating the susceptibility of metal to stress corrosion cracking (SCC) by means of tests conducted under rising load or rising displacement. Tests conducted under constant load or constant displacement are dealt with in ISO 7539-6.
The term “metal” as used in this document includes alloys.
1.2  Because of the need to confine plasticity at the crack tip, pre-cracked specimens are not suitable for the evaluation of thin products such as sheet or wire and are generally used for thicker products including plate, bar, and forgings. They can also be used for parts joined by welding.
1.3  Pre-cracked specimens can be stressed quantitatively with equipment for application of a monotonically increasing load or displacement at the loading points.
1.4  A particular advantage of pre-cracked specimens is that they allow data to be acquired from which critical defect sizes, above which stress corrosion cracking can occur, can be estimated for components of known geometry subjected to known stresses. They also enable rates of stress corrosion crack propagation to be determined.
1.5  A principal advantage of the test is that it takes account of the potential impact of dynamic straining on the threshold for stress corrosion cracking.
1.6  At sufficiently low loading rates, the threshold stress intensity factor for susceptibility to stress corrosion cracking, KISCC, determined by this method can be less than or equal to that obtained by constant load or displacement methods and can be determined more rapidly.

  • Standard
    39 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 8407:2021(Main)
Corrosion of metals and alloys - Removal of corrosion products from corrosion test specimens (ISO 8407:2021)
SIST EN ISO 8407:2021

This document specifies procedures for the removal of corrosion products formed on metal and alloy corrosion test specimens during their exposure in corrosive environments. For the purpose of this document, the term "metals" refers to pure metals and alloys.
The specified procedures are designed to remove all corrosion products without significant removal of base metal. This allows an accurate determination of the mass loss of the metal, which occurred during exposure to the corrosive environment.
In some cases, these procedures are also applicable to metal coatings, providing the possible effects from the substrate are considered.

  • Standard
    18 pages
    English language
    sale 10% off
    e-Library read for
    1 day
  • Draft
    13 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 11463:2020(Main)
Corrosion of metals and alloys - Guidelines for the evaluation of pitting corrosion (ISO 11463:2020)
SIST EN ISO 11463:2020

This document gives guidelines for the selection of procedures that can be used in the identification and examination of corrosion pits and in the evaluation of pitting corrosion and pit growth rate.

  • Standard
    20 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 11844-1:2020(Main)
Corrosion of metals and alloys - Classification of low corrosivity of indoor atmospheres - Part 1: Determination and estimation of indoor corrosivity (ISO 11844-1:2020)
SIST EN ISO 11844-1:2020

This document establishes a classification of low corrosivity of indoor atmospheres.
It specifies the reference metals for which a corrosion attack after a defined exposure period is used for determining corrosivity categories of indoor atmospheres of low corrosivity.
It defines corrosivity categories of indoor atmospheres according to corrosion attack on standard specimens.
It indicates important parameters of indoor atmospheres that can serve as a basis for an estimation of indoor corrosivity.
The selection of a method for the determination of corrosion attack, description of standard specimens, exposure conditions and evaluation are given in ISO 11844-2. The measurement of environmental parameters affecting indoor corrosivity is given in ISO 11844-3.

  • Standard
    28 pages
    English language
    sale 10% off
    e-Library read for
    1 day