ISO 6179:1989

Vulcanized rubber sheet, and fabrics coated with vulcanized rubber — Determination of transmission rate of volatile liquids (Gravimetric technique)

Feuilles de caoutchouc vulcanisé et supports textiles revêtus de caoutchouc vulcanisé — Détermination du taux de transmission des liquides volatils (Technique gravimétrique)

General Information

• Status: Withdrawn
• Publication Date: 20-Dec-1989
• Withdrawal Date: 20-Dec-1989
• ICS: 59.080.40 - Coated fabrics
• ICS: 83.140.10 - Films and sheets
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 1 - Physical properties
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 09-Apr-1998

Relations

• Revised: ISO 6179:1998 - Rubber, vulcanized or thermoplastic — Rubber sheets and rubber-coated fabrics — Determination of transmission rate of volatile liquids (gravimetric technique)
• Effective Date: 15-Apr-2008
• Revises: ISO 6179:1981 - Fabrics coated with vulcanized rubber — Determination of vapour transmission rate of volatile liquids (Gravimetric technique)
• Effective Date: 15-Apr-2008

Standards Content (Sample)

I N T E R NAT I O NA L
IS0
STANDARD
6179
Second edition
1989-1 2-1 5
Vulcanized rubber sheet, and fabrics coated
with vulcanized rubber - Determination of
transmission rate of volatile liquids (Gravimetric
technique)
Feuilles de caoutchouc vulcanisé et supports textiles revêtus de caoutchouc
vulcanisé - Détermination du taux de transmission des liquides volatils (Technique
gravimétriquei
Reference number
IS0 6179 : 1989 (E)

---------------------- Page: 1 ----------------------
IS0 6179 : 1989 (E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of preparing International
Standards is normally carried out through IS0 technical committees. Each member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council. They are approved in accordance with IS0 procedures requiring at
least 75 % approval by the member bodies voting.
International Standard IS0 6179 was prepared by Technical Committee ISO/TC 45,
Rubber and rubber products.
This second edition cancels and replaces the first edition (IS0 6179 : 1981 1, of which it
constitutes a minor revision.
O IS0 1989
All rights reserved. No part of this publication may be reproduced or utilized in any form or by any
in
means, electronic or mechanical, including photocopying and microfilm, without permission
writing from the publisher.
International Organization for Standardization
Case postale 56 0 CH-121 1 Genève 20 0 Switzerland
Printed in Switzerland

---------------------- Page: 2 ----------------------
INTERNATIONAL STANDARD IS0 6179 : 1989 (El
Vulcanized rubber sheet, and fabrics coated with
vulcanized rubber - Determination of transmission rate
of volatile liquids (Gravimetric technique)
IS0 4648 : 1978, Rubber, vulcanized - Determination of
1 Scope
dimensions of test pieces and products for test purposes.
This International Standard specifies two methods of determin-
Oing the permeability of vulcanized rubber to volatile liquids dif-
ISO4661-1 : 1986, Rubber, vulcanized - Preparation of
fusing into open air, by measurement of the transmission rate.
samples and test pieces - Part I: Physical tests.
It is applicable only to materials in sheet form, and to coated
NOTE - A method for the determination of water vapour transmission
0,2 mm and 3,O mm.
fabrics, having thicknesses of between IS0 2528 : 1974, Sheet materiais - Determination of
rate is given in
water vapour transmission rate - Dish method.
The methods are particularly useful for comparing the relative
transmission rates of one liquid through different materials, or
of several liquids through one material.
3 Apparatus
Method A, with refilling, is used when testing mixtures of
liquids of different transmission rates.
3.1 Container assembly (see figure I), consisting of a con-
tainer for the test liquid, a suitable clamping device for the test
Method B, with no refilling, is used for a single-component
piece which does not impose a shearing force on the test piece,
liquid.
and a suitable support for the container, so that the test piece
and the test liquid are in contact at all times (with the apparatus
inverted after filling), and such as to permit free circulation of
2 Normative references
air across the surface of the test piece.
The following standards contain provisions which, through
The container shall have a volume of 60 cm3 to 100 cm3.
reference in this text, constitute provisions of this International
Standard. At the time of publication, the editions indicated
The mass of the container, the clamping ring and 50 cm3 of the
were valid. All standards are subject to revision, and parties to
test liquid shall not exceed the capacity of the balance (see 3.2).
agreements based on this International Standard are encour-
aged to investigate the possibility of applying the most recent
The open end of the container and the hole of the clamping ring
editions of the standards indicated below. Members of IEC and
shall have a diameter such that the exposed surface area of the
IS0 maintain registers of currently valid International Stan-
test piece is approximately 1 O00 mm2 on each side.
dards.
IS0 188 : 1982, Rubber, vulcanized - Accelerated ageing or When testing in accordance with method A, the container shall
heat-resistance tests. have two inlet valves on the back for refilling purposes. Such
valves are shown in figure 1.
IS0 471 : 1983, Rubber - Standard temperatures, humidities
and times for the conditioning and testing of test pieces.
When testing materials without fabric, a circular piece of
stainless steel wire mesh of aperture size 1 mm (in accordance
IS0 1826 : 1981, Rubber, vulcanized - Time-intervalbetween
with IS0 3310-1) shall be mounted together with the test piece
vulcanization and testing - Specification.
so as to support the latter on its outer surface during the test.
IS0 2231 : 1989, Rubber- or plastics-coated fabrics - Stan-
dard atmospheres for conditioning and testing.
Balance, with a capacity of at least 200 g and accurate
3.2
to 1 mg.
IS0 2286 : 1986, Rubber- or plastics-coated fabrics - Deter-
mination of roll characteristics.
IS0 3310-1 : 1982, Test sieves - Technical requirements and complying with the requirements of
3.3 Test chamber,
- Part I: Test sieves of metal wire cloth.
testing IS0 188, for tests performed at elevated temperature.
1

---------------------- Page: 3 ----------------------
IS0 6179 : 1989 (E)
7.2 Test temperature
4 Test pieces
The test temperature shall be 23 OC f 2 OC or 27 OC f 2 OC.
4.1 Preparation
If, for technical reasons, mother temperature is required, it
4.1.1 The standard test piece shall be circular and cut from a
shall be chosen from the following list of temperatures:
flat sheet in accordance with IS0 4661-1. The surface shall be
flat, smooth and free from defects. 40 OC f 1 oc
55 OC f
...

NORME
IS0
I N T E R N AT I O N A LE
6179
Deuxième édition
1989-12-1 5
Feuilles de caoutchouc vulcanisé et supports
textiles revêtus de caoutchouc vulcanisé -
Détermination du taux de transmission des
liquides volatils (Technique gravimétrique)
Vulcanized rubber sheet, and fabrics coated with vulcanized rubber -
Determination of transmission rate of volatile liquids (Gravimetric technique)
Numéro de référence
IS0 6179 : 1989 (FI

---------------------- Page: 1 ----------------------
IS0 0179 : 1989 (FI
Avant-propos
L‘ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L‘élaboration
des Normes internationales est en général confiée aux comités techniques de I’ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO participent également aux travaux. L’ISO col-
labore étroitement avec la Commission électrotechnique internationale (CEI) en ce qui
concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
I’ISO. Les Normes internationales sont approuvées confor-
nationales par le Conseil de
mément aux procédures de I‘ISO qui requièrent l’approbation de 75 % au moins des
comités membres votants.
La Norme internationale IS0 6179 a été élaborée par le comité technique ISO/TC 45,
Élastomères et produits à base d‘élastomères.
Cette deuxième édition annule et remplace la première édition (IS0 6179 : 19811, dont
elle constitue une révision mineure.
O IS0 1989
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite ni
utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l’accord écrit de l‘éditeur.
Organisation internationale de normalisation
Case postale 56 CH-121 1 Genève 20 O Suisse
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORM E I NTER NAT1 ON ALE IS0 6179 : 1989 (FI
Feuilles de caoutchouc vulcanisé et supports textiles
revêtus de caoutchouc vulcanisé - Détermination du
taux de transmission des liquides volatils (Technique
gravimétrique)
IS0 2286 : 1986, Supports textiles revêtus de caoutchouc ou
1 Domaine d'application
de plastique - Détermination des caractéristiques des rou-
La présente Norme internationale prescrit deux méthodes pour
leaux.
la détermination de la perméabilité du caoutchouc vulcanisé
aux liquides volatils, à l'air libre, par mesurage du taux de trans- IS0 3310-1 : 1982, Tamis de contrôle - Exigences techniques
mission. et vérifications - Partie I: Tamis de contrôle en tissus métalli-
ques.
Elle n'est utilisable que pour des matériaux en feuille et des sup-
ports textiles revêtus ayant une épaisseur comprise entre
IS0 4648 : 1978, Caoutchouc vulcanisé - Détermination des
0,2 mm et 3,O mm.
dimensions des éprouvettes et des produits en vue des essais.
Ces méthodes sont surtout utiles pour comparer le taux relatif
IS0 4661-1 : 1986, Caoutchouc vulcanisé - Préparation des
de transmission d'un liquide à travers différents matériaux, ou
échantillons et éprouvettes - Partie 7: Essais physiques.
de plusieurs liquides à travers un seul matériau.
NOTE - Une méthode de détermination du coefficient de transmission
La méthode A, avec remplissages répétés, est utilisée lorsque
de la vapeur d'eau est donnée dans I'ISO 2528 : 1974, Produits en
l'on essaie des mélanges de liquides de taux de transmission
feuilles et en plaques - Détermination du coefficient de transmission
différents.
de la vapeur d'eau - Méthode de la capsule.
La méthode 6, sans remplissages répétés, est utilisée pour un
seul composant liquide.
3 Appareillage
3.1 Appareil d'essai (voir figure I), constitué d'un récipient
2 Références normatives
pour le liquide d'essai, d'un dispositif de fixation approprié pour
l'éprouvette, n'exercant pas de force de cisaillement sur cette
Les normes suivantes contiennent des dispositions qui, par
éprouvette, et d'un support approprié pour le récipient, de
suite de la référence qui en est faite, constituent des disposi-
sorte que l'éprouvette et le liquide d'essai soient toujours en
tions valables pour la présente Norme internationale. Au
contact (l'appareil étant retourné après remplissage) et de
moment de la publication, les éditions indiquées étaient en
manière à permettre la libre circulation de l'air à travers la sur-
vigueur. Toute norme est sujette à révision et les parties pre-
face de l'éprouvette.
nantes des accords fondés sur la présente Norme internationale
sont invitées à rechercher la possibilité d'appliquer les éditions
Le récipient doit avoir un volume de 60 cm3 à 100 cm3.
les plus récentes des normes indiquées ci-après. Les membres
de la CE1 et de I'ISO possèdent le registre des Normes interna-
La masse du récipient, de la bague de serrage et de 50 cm3 du
tionales en vigueur à un moment donné.
liquide d'essai ne doit pas dépasser la capacité de la balance
(voir 3.2).
IS0 188 : 1982, Caoutchouc vulcanisé - Essais de résistance
au vieillissement accéléré ou à la chaleur.
L'extrémité ouverte du récipient et l'ouverture de la bague de
serrage doivent avoir un diamètre tel que la surface exposée de
IS0471 : 1983, Caoutchouc - Températures, humidités et
l'éprouvette soit d'environ 1 O00 mm2 sur chacune des faces.
durées normales pour le conditionnement et Fessai des éprou-
vettes.
Lorsque l'essai est réalisé selon la méthode A, le récipient doit
comporter deux vannes d'entrée sur la partie arrière pour que
IS0 1826 : 1981, Caoutchouc vulcanisé - Délai entre vulcani-
soient effectués les remplissages répétés. Ces vannes sont
sation et essai - Spécifications.
représentées à la figure 1.
IS0 2231 : 1989, Supports textiles revêtus de caoutchouc ou
de plastique - Atmosphères normales de conditionnement et Lorsqu'il s'agit d'essayer des matériaux sans support, une pièce
d'essai. circulaire avec toile d'acier inoxydable, d'ouverture de maille
1

---------------------- Page: 3 ----------------------
IS0 6179 : 1989 (FI
Chaque période d'essai commence dès que le récipient a été
égale à 1 mm (conformément à I'ISO 3310-1 1, doit être montée
pesé et placé de manière que le liquide soit en contact avec la
avec l'éprouvette pour la maintenir sur sa surface externe pen-
surface exposée de l'éprouvette. Si l'essai est effectué à tempé-
dant l'essai.
rature élevée, la période d'essai commence immédiatement
après mise de l'appareillage dans l'étuve et, en tous cas, pas
Balance, d'une capacité d'au moins 200 g et précise
3.2
plus de 30 min après pesée, et le récipient doit être laissé à
à 1 mg.
ref
...