Metallic coatings — Electrodeposited coatings of nickel plus chromium and of copper plus nickel plus chromium

ISO 1456 specifies the requirements for decorative, electroplated nickel plus chromium, and copper plus nickel plus chromium coatings on iron, steel, zinc alloys, copper and copper alloys, and aluminium and aluminium alloys to provide an attractive appearance and enhanced corrosion resistance. Coating designations are specified that differ in thickness and type, and guidance is given in selecting the coating designation appropriate to the service conditions to which the coated product will be exposed.

Revêtements métalliques — Dépôts électrolytiques de nickel plus chrome et de cuivre plus nickel plus chrome

L'ISO 1456:2002 spécifie les exigences relatives aux dépôts électrolytiques décoratifs de nickel plus chrome et de cuivre plus nickel plus chrome appliqués sur le fer, l'acier, les alliages de zinc, le cuivre et les alliages de cuivre, l'aluminium et les alliages d'aluminium pour leur conférer un aspect agréable et pour améliorer leur résistance à la corrosion. Des désignations de dépôts sont spécifiées pour différentes épaisseurs et différents types de dépôts, et des indications sont données quant au choix du dépôt approprié pour la condition d'utilisation prévue du produit revêtu.

Kovinske prevleke - Galvanske prevleke niklja in kroma ter bakra, niklja in kroma

General Information

Status
Withdrawn
Publication Date
06-Feb-2003
Withdrawal Date
06-Feb-2003
Current Stage
9599 - Withdrawal of International Standard
Start Date
30-Jul-2009
Completion Date
30-Jul-2009

RELATIONS

Buy Standard

Standard
ISO 1456:2003 - Metallic coatings -- Electrodeposited coatings of nickel plus chromium and of copper plus nickel plus chromium
English language
19 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 1456:2004
English language
19 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day
Standard
ISO 1456:2003 - Revetements métalliques -- Dépôts électrolytiques de nickel plus chrome et de cuivre plus nickel plus chrome
French language
20 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (sample)

INTERNATIONAL ISO
STANDARD 1456
Third edition
2003-02-15
Metallic coatings — Electrodeposited
coatings of nickel plus chromium and of
copper plus nickel plus chromium
Revêtements métalliques — Dépôts électrolytiques de nickel plus chrome et
de cuivre plus nickel plus chrome
Reference number
ISO 1456:2003(E)
© ISO 2003
---------------------- Page: 1 ----------------------
ISO 1456:2003(E)
PDF disclaimer

This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not be

edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file,

parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this area.

Adobe is a trademark of Adobe Systems Incorporated.

Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters

were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event

that a problem relating to it is found, please inform the Central Secretariat at the address given below.

© ISO 2003

All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,

electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's

member body in the country of the requester.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Printed in Switzerland
ii ISO 2003 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 1456:2003(E)
Contents Page

1 Scope ............................................................................................................................................................... 1

2 Normative references ....................................................................................................................................... 1

3 Terms and definitions ........................................................................................................................................ 2

4 Information to be supplied by the purchaser to the electroplater ...................................................................... 2

5 Service condition number ................................................................................................................................. 3

6 Designation ....................................................................................................................................................... 3

7 Requirements ................................................................................................................................................. 10

8 Sampling ......................................................................................................................................................... 12

Annexes

A Examples of service conditions for which the various service condition numbers are appropriate ................ 13

B Determination of cracks and pores in chromium coatings .............................................................................. 14

C Methods of test for the determination of thickness ......................................................................................... 15

D Ductility test..................................................................................................................................................... 17

E Determination of the sulfur content of electrodeposited nickel........................................................................ 18

Bibliography........................................................................................................................................................... 19

ISO 2003 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 1456:2003(E)
Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO

member bodies). The work of preparing International Standards is normally carried out through ISO technical

committees. Each member body interested in a subject for which a technical committee has been established has

the right to be represented on that committee. International organizations, governmental and non-governmental, in

liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical

Commission (IEC) on all matters of electrotechnical standardization.

International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.

Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.

Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.

Attention is drawn to the possibility that some of the elements of this International Standard may be the subject of

patent rights. ISO shall not be held responsible for identifying any or all such patent rights.

International Standard ISO 1456 was prepared by Technical Committee ISO/TC 107, Metallic and other inorganic

coatings, Subcommittee SC 3, Electrodeposited coatings and related finishes.

This third edition cancels and replaces the second edition (ISO1456:1988), which has been editorially and

technically revised.

Annexes B to E form a normative part of this International Standard. Annex A is for information only.

iv ISO 2003 – All rights reserved
---------------------- Page: 4 ----------------------
ISO 1456:2003(E)
Introduction

Decorative, electrodeposited nickel plus chromium and copper plus nickel plus chromium coatings are applied to

manufactured articles to enhance their appearance and corrosion resistance. Corrosion resistance depends on the

type and thickness of the coatings. In general, multilayer nickel coatings provide better corrosion resistance than

single-layer nickel coatings of equal thickness, and microdiscontinuous chromium coatings provide better protection

than conventional chromium.
ISO 2003 – All rights reserved v
---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 1456:2003(E)
Metallic coatings — Electrodeposited coatings of nickel plus
chromium and of copper plus nickel plus chromium
1 Scope

This International Standard specifies the requirements for decorative, electroplated nickel plus chromium, and

copper plus nickel plus chromium coatings on iron, steel, zinc alloys, copper and copper alloys, and aluminium and

aluminium alloys to provide an attractive appearance and enhanced corrosion resistance. Coating designations are

specified that differ in thickness and type, and guidance is given in selecting the coating designation appropriate to

the service conditions to which the coated product will be exposed.

This International Standard does not specify the surface condition required by the base metal prior to the coating

process, and is not applicable to coatings on sheet, strip or wire in the non-fabricated form nor to threaded fasteners

or coil springs.

Requirements for decorative, electroplated copper plus nickel plus chromium coatings on plastic materials are

specified in ISO 4525. Similar coatings, except for the absence of a top-coat of chromium, are specified in ISO 1458.

ISO 4526 and ISO 6158 specify requirements for coatings of nickel and chromium, respectively, for engineering

purposes.
2 Normative references

The following normative documents contain provisions which, through reference in this text, constitute provisions of

this International Standard. For dated references, subsequent amendments to, or revisions of, any of these

publications do not apply. However, parties to agreements based on this International Standard are encouraged to

investigate the possibility of applying the most recent editions of the normative documents indicated below. For

undated references, the latest edition of the normative document referred to applies. Members of ISO and IEC

maintain registers of currently valid International Standards.

ISO 1463, Metallic and oxide coatings — Measurement of coating thickness — Microscopical method

ISO 2064, Metallic and other inorganic coatings — Definitions and conventions concerning the measurement of

thickness

ISO 2079, Surface treatment and metallic coatings — General classification of terms

ISO 2080, Surface treatment, metallic and other inorganic coatings — Vocabulary

ISO 2177, Metallic coatings — Measurement of coating thickness — Coulometric method by anodic dissolution

ISO 2361, Electrodeposited nickel coatings on magnetic and non-magnetic substrates — Measurement of coating

thickness — Magnetic method

ISO 2819, Metallic coatings on metallic substrates — Electrodeposited and chemically deposited coatings — Review

of methods available for testing adhesion

ISO 3497, Metallic coatings — Measurement of coating thickness — X-ray spectrometric methods

ISO 3543, Metallic and non-metallic coatings — Measurement of thickness — Beta backscatter method

ISO 2003 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO 1456:2003(E)

ISO 3882, Metallic and other inorganic coatings — Review of methods of measurement of thickness

ISO 4519, Electrodeposited metallic coatings and related finishes — Sampling procedures for inspection by

attributes

ISO 4541:1978, Metallic and other non-organic coatings — Corrodkote corrosion test (CORR test)

ISO 9220, Metallic coatings — Measurement of coating thickness — Scanning electron microscope method

ISO 9227:1990, Corrosion tests in artificial atmospheres — Salt spray tests

ISO 9587, Metallic and other inorganic coatings — Pretreatments of iron or steel to reduce the risk of hydrogen

embrittlement

ISO 9588, Metallic and other inorganic coatings — Post-coating treatments of iron or steel to reduce the risk of

hydrogen embrittlement

ISO 10289:1999, Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates —

Rating of test specimens and manufactured articles subjected to corrosion tests

ISO 10587, Metallic and other inorganic coatings — Test for residual embrittlement in both metallic-coated and

uncoated externally-threaded articles and rods — Inclined wedge method

ISO 16348, Metallic and other inorganic coatings — Definitions and conventions concerning appearance

ASTM B764-94, Standard Test Method for Simultaneous Thickness and Electrochemical Potential Determination of

Individual Layers in Multilayer Nickel Deposit (STEP Test)
3 Terms and definitions

For the purposes of this International Standard, the terms and definitions given in ISO 2064, ISO 2079, ISO 2080

and ISO 16348 apply.
4 Information to be supplied by the purchaser to the electroplater
4.1 Essential information

When ordering articles to be electroplated in accordance with this International Standard, the purchaser shall provide

the following information in writing, in e.g., the contract or purchase order, or on engineering drawings:

a) the designation (see clause 6);

b) the appearance required, e.g., bright, dull or satin (see 6.3 and 7.1). Alternatively, samples showing the required

finish or range of finishes shall be supplied or approved by the purchaser, and used for comparison purposes

(see 7.1);

c) the significant surfaces, to be indicated on drawings of the parts or by providing suitably marked specimens;

d) the type of corrosion test to be used (see 7.5 and Table 8);
e) the type of adhesion test to be used (see 7.4);

f) the extent to which defects shall be tolerated on non-significant surfaces (see 7.1);

g) positions on the significant surface for rack or contact marks, where such marks are unavoidable (see 7.1);

h) sampling methods and acceptance levels (see clause 8);

i) the tensile strength of the steel and any requirement for prior or post treatments of iron or steel to reduce the risk

of hydrogen embrittlement, as well as hydrogen embrittlement test methods (see 7.8 and 7.9).

2 ISO 2003 – All rights reserved
---------------------- Page: 7 ----------------------
ISO 1456:2003(E)
4.2 Additional information

The following additional information may be provided by the purchaser, when appropriate:

a) any requirements for STEP testing (see 7.6);

b) thickness requirements on those areas that cannot be touched by a ball 20 mm in diameter (see 7.2);

c) whether or not a copper undercoat is required (see 6.1 and 6.2).
5 Service condition number

The service condition number is used by the purchaser to specify the degree of protection required, as related to the

severity of the conditions to which a product is to be subjected, in accordance with the following scale:

5 Exceptionally severe
4Very severe
3Severe
2 Moderate
1Mild

Typical service conditions for which the various service condition numbers are appropriate are listed in annex A.

6 Designation
6.1 General

The coating designation specifies the type and thickness of coatings appropriate for each service condition number

(see Tables 1 to 6 for various substrates) and comprises the following:

a) the term, “Electroplated coating”, the number of this International Standard, ISO 1456, followed by a hyphen;

b) the chemical symbol for the base metal (or for the principal metal if an alloy) followed by a solidus ( ) as follows:

— Fe/for iron or steel;
— Zn/for zinc alloys;
— Cu/for copper and copper alloys;
— Al/for aluminium or aluminium alloys;

c) the chemical symbol for copper (Cu), if copper, or brass containing greater than 50 % copper, is used as an

undercoat;

d) a number indicating the minimum local thickness, in micrometres, of the copper coating where applicable;

e) a letter indicating the type of copper, where applicable;
f) the chemical symbol for nickel (Ni);

g) a number indicating the minimum local thickness, in micrometres, of the nickel coating;

h) a letter designating the type of nickel coating (see 6.3);
i) the chemical symbol for chromium (Cr);

j) a letter or letters designating the type of chromium and its minimum local thickness (see 6.4).

ISO 2003 – All rights reserved 3
---------------------- Page: 8 ----------------------
ISO 1456:2003(E)
Table 1 — Nickel plus chromium coatings on iron or steel

Service condition number Partial designation Service condition number Partial designation

Fe/Ni20b Cr r
Fe/Ni20b Cr mc
Fe/Ni20b Cr mp
Fe/Ni20p Cr r
Fe/Ni35d Cr mc
5 2 Fe/Ni20p Cr mc
Fe/Ni35d Cr mp
Fe/Ni20p Cr mp
Fe/Ni20s Cr r
Fe/Ni20s Cr mc
Fe/Ni20s Cr mp
Fe/Ni40d Cr r
Fe/Ni30d Cr mp
Fe/Ni10b Cr r
Fe/Ni30d Cr mc
4 1 Fe/Ni10p Cr r
Fe/Ni40p Cr r
Fe/Ni10s Cr r
Fe/Ni30p Cr mc
Fe/Ni30p Cr mp
Fe/Ni30d Cr r
Fe/Ni25d Cr mp
Fe/Ni25d Cr mc
Fe/Ni30p Cr r
3 Fe/Ni25p Cr mc ——
Fe/Ni25p Cr mp
Fe/Ni40b Cr r
Fe/Ni30b Cr mc
Fe/Ni30b Cr mp
4 ISO 2003 – All rights reserved
---------------------- Page: 9 ----------------------
ISO 1456:2003(E)
Table 2 — Copper plus nickel plus chromium coatings on iron or steel
Service condition number Partial designation
Fe/Cu20a Ni30d Cr mc
Fe/Cu20a Ni30d Cr mp
Fe/Cu20a Ni30d Cr r
Fe/Cu20a Ni25d Cr mp
Fe/Cu20a Ni25d Cr mc
Fe/Cu20a Ni30p Cr r
Fe/Cu20a Ni25p Cr mc
Fe/Cu20a Ni25p Cr mp
Fe/Cu20a Ni30b Cr mc
Fe/Cu20a Ni30b Cr mp
Fe/Cu15a Ni25d Cr r
Fe/Cu15a Ni20d Cr mc
Fe/Cu15a Ni20d Cr mp
Fe/Cu15a Ni25p Cr r
3 Fe/Cu15a Ni20p Cr mc
Fe/Cu15a Ni20p Cr mp
Fe/Cu20a Ni35b Cr r
Fe/Cu20a Ni25b Cr mc
Fe/Cu20a Ni25b Cr mp
Fe/Cu20a Ni10b Cr r
2 Fe/Cu20a Ni10p Cr r
Fe/Cu20a Ni10s Cr r
Fe/Cu10a Ni5b Cr r
1 Fe/Cu10a Ni5p Cr r
Fe/Cu10a Ni20b Cr mp

NOTE An initial copper coating, 5µm1 to 0µm thick, is normally applied to iron and steel

from a copper cyanide solution before electroplating with ductile acid copper to prevent

immersion deposition and poorly adherent deposits. The initial copper coating (copper strike)

may not be substituted for any portion of the ductile acid copper specified in Table 2.

ISO 2003 – All rights reserved 5
---------------------- Page: 10 ----------------------
ISO 1456:2003(E)
Table 3 — Nickel plus chromium coatings on zinc alloys

Service condition number Partial designation Service condition number Partial designation

Zn/Ni25d Cr r
Zn/Ni20d Cr mc
Zn/Ni20d Cr mp
Zn/Ni25p Cr r
Zn/Ni35d Cr mc
5 3 Zn/Ni20p Cr mc
Zn/Ni35d Cr mp
Zn/Ni20p Cr mp
Zn/Ni35b Cr r
Zn/Ni25b Cr mc
Zn/Ni25b Cr mp
Zn/Ni35d Cr r
Zn/Ni25d Cr mc
Zn/Ni25d Cr mp
Zn/Ni15b Cr r
Zn/Ni35p Cr r
4 2 Zn/Ni15p Cr r
Zn/Ni25p Cr mc
Zn/Ni15s Cr r
Zn/Ni25p Cr mp
Zn/Ni35b Cr mc
Zn/Ni35b Cr mp
Zn/Ni8b Cr r
—— 1 Zn/Ni8p Cr r
Zn/Ni8s Cr r

NOTE Zinc alloys must first be electroplated with copper to ensure adhesion of the subsequent nickel coatings. The initial layer

of copper is usually electrodeposited from a copper cyanide solution, but cyanide-free alkaline copper solutions are also being

used. The minimum thickness of the initial copper layer is 8µm1 to 0µm. For articles of complex shape, the minimum copper

thickness may need to be increased to about 15µm to ensure adequate coverage on low-current density areas outside the

significant surfaces. Ductile, levelling copper electrodeposited from acid solutions is usually applied over the initial cyanide

copper deposit when the specified copper thickness is greater than 10µm.
6 ISO 2003 – All rights reserved
---------------------- Page: 11 ----------------------
ISO 1456:2003(E)
Table 4 — Copper plus nickel plus chromium coatings on zinc alloys

Service condition number Partial designation Service condition number Partial designation

Zn/Cu15a Ni25d Cr r
Zn/Cu15a Ni20d Cr mc
Zn/Cu15a Ni20d Cr mp
Zn/Cu15a Ni25p Cr r
Zn/Cu20a Ni30d Cr mc
5 3 Zn/Cu15a Ni20p Cr mc
Zn/Cu20a Ni30d Cr mp
Zn/Cu15a Ni20p Cr mp
Zn/Cu20a Ni30b Cr r
Zn/Cu20a Ni20b Cr mc
Zn/Cu20a Ni20b Cr mp
Zn/Cu20a Ni30d Cr r
Zn/Cu20a Ni20d Cr mc
Zn/Cu20a Ni20d Cr mp
Zn/Cu20a Ni30p Cr r Zn/Cu20a Ni10b Cr r
4 2
Zn/Cu20a Ni20p Cr mc Zn/Cu20a Ni10p Cr r
Zn/Cu20a Ni20p Cr mp Zn/Cu20a Ni10s Cr r
Zn/Cu20a Ni30b Cr mc
Zn/Cu20a Ni30b Cr mp
Zn/Cu10a Ni8b Cr r
—— 1 Zn/Cu10a Ni8p Cr r
Zn/Cu10a Ni8s Cr r

NOTE Zinc alloys must first be electroplated with copper to ensure adhesion of the subsequent nickel coatings. The initial layer

of copper is usually electrodeposited from a copper cyanide solution, but cyanide-free alkaline copper solutions are also being

used. The minimum thickness of the initial copper layer is 8µm1 to 0µm. For articles of complex shape, the minimum copper

thickness may need to be increased to about 15µm to ensure adequate coverage on low-current density areas outside the

significant surfaces. Ductile, levelling copper electrodeposited from acid solutions is usually applied over the initial cyanide

copper deposit when the specified copper thickness is greater than 10µm.
ISO 2003 – All rights reserved 7
---------------------- Page: 12 ----------------------
ISO 1456:2003(E)
Table 5 — Nickel plus chromium coatings on copper and copper alloys
Service condition number Partial designation
Cu/Ni30d Cr r
Cu/Ni25d Cr mc
Cu/Ni25d Cr mp
Cu/Ni30p Cr r
Cu/Ni25p Cr mc
Cu/Ni25p Cr mp
Cu/Ni30b Cr mc
Cu/Ni30b Cr mp
Cu/Ni25d Cr r
Cu/Ni20d Cr mc
Cu/Ni20d Cr mp
Cu/Ni25p Cr r
3 Cu/Ni20p Cr mc
Cu/Ni20p Cr mp
Cu/Ni30b Cr r
Cu/Ni25b Cr mc
Cu/Ni25b Cr mp
Cu/Ni10b Cr r
2 Cu/Ni10p Cr r
Cu/Ni10s Cr r
Cu/Ni5b Cr r
1 Cu/Ni5p Cr r
Cu/Ni5s Cr r
8 ISO 2003 – All rights reserved
---------------------- Page: 13 ----------------------
ISO 1456:2003(E)
Table 6 — Nickel plus chromium coatings on aluminium and aluminium alloys
Service condition number Partial designation
Al/Ni40d Cr mc
Al/Ni40d Cr mp
Al/Ni50d Cr r
4 Al/Ni35d Cr mc
Al/Ni35d Cr mp
Al/Ni30d Cr r
Al/Ni25d Cr mc
Al/Ni25d Cr mp
Al/Ni35p Cr r
Al/Ni30p Cr mc
Al/Ni30p Cr mp
Al/Ni20d Cr r
Al/Ni20d Cr mc
Al/Ni20d Cr mp
Al/Ni25b Cr r
Al/Ni25b Cr mc
Al/Ni25b Cr mp
Al/Ni20p Cr r
Al/Ni20p Cr mc
Al/Ni20p Cr mp
Al/Ni20s Cr r
Al/Ni20s Cr mc
Al/Ni20s Cr mp
1 Al/Ni10b Cr r
NOTE For aluminium and aluminium alloys immersion deposits of zinc or tin, and

electrodeposited copper and other undercoats are used as part of the preparation for

electroplating to ensure adhesion, prior to application of the designated nickel coatings given

in the table.
6.2 Type of copper coating

The type of copper is designated by the symbol “a” for ductile, levelling copper electrodeposited from acid-type

solutions.
6.3 Ty
...

2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Kovinske prevleke - Galvanske prevleke niklja in kroma ter bakra, niklja in kromaRevêtements métalliques -- Dépôts électrolytiques de nickel plus chrome et de cuivre plus nickel plus chromeMetallic coatings -- Electrodeposited coatings of nickel plus chromium and of copper plus nickel plus chromium25.220.40Kovinske prevlekeMetallic coatingsICS:Ta slovenski standard je istoveten z:ISO 1456:2003SIST ISO 1456:2004en01-december-2004SIST ISO 1456:2004SLOVENSKI

STANDARD
SIST ISO 1456:2004

INTERNATIONALSTANDARDISO1456Third edition2003-02-15Reference numberISO1456:2003(E)© ISO2003Metallic coatings— Electrodeposited coatings of nickel plus chromium and of copper plus nickel plus chromiumRevêtements métalliques— Dépôts électrolytiques de nickel plus chrome et de cuivre plus nickel plus chrome

SIST ISO 1456:2004

ISO1456:2003(E)ii© ISO2003–All rights reservedPDF disclaimerThis PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not beedited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file,parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this area.Adobe is a trademark of Adobe Systems Incorporated.Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameterswere optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely eventthat a problem relating to it is found, please inform the Central Secretariat at the address given below.©ISO2003All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO'smember body in the country of the requester.ISO copyright officeCase postale 56  CH-1211 Geneva 20Tel.+ 41 22 749 01 11Fax+ 41 22 749 09 47E-mailcopyright@iso.orgWebwww.iso.orgPrinted in SwitzerlandSIST ISO 1456:2004

ISO1456:2003(E)© ISO2003–All rights reservediiiContents Page1Scope ............................................................................................................................................................... 12Normative references ....................................................................................................................................... 13Terms and definitions ........................................................................................................................................ 24Information to be supplied by the purchaser to the electroplater ...................................................................... 25Service condition number ................................................................................................................................. 36Designation ....................................................................................................................................................... 37Requirements ................................................................................................................................................. 108Sampling ......................................................................................................................................................... 12AnnexesAExamples of service conditions for which the various service condition numbers are appropriate................ 13BDetermination of cracks and pores in chromium coatings.............................................................................. 14CMethods of test for the determination of thickness......................................................................................... 15DDuctility test..................................................................................................................................................... 17EDetermination of the sulfur content of electrodeposited nickel........................................................................ 18Bibliography........................................................................................................................................................... 19SIST ISO 1456:2004

ISO1456:2003(E)iv© ISO2003–All rights reservedForewordISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISOmember bodies). The work of preparing International Standards is normally carried out through ISO technicalcommittees. Each member body interested in a subject for which a technical committee has been established hasthe right to be represented on that committee. International organizations, governmental and non-governmental, inliaison with ISO, also take part in the work. ISO collaborates closely with the International ElectrotechnicalCommission (IEC) on all matters of electrotechnical standardization.International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part3.Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.Publication as an International Standard requires approval by at least 75% of the member bodies casting a vote.Attention is drawn to the possibility that some of the elements of this International Standard may be the subject ofpatent rights. ISO shall not be held responsible for identifying any or all such patent rights.International Standard ISO1456 was prepared by Technical Committee ISO/TC107, Metallic and other inorganiccoatings, Subcommittee SC3, Electrodeposited coatings and related finishes.This third edition cancels and replaces the second edition (ISO1456:1988), which has been editorially andtechnically revised.AnnexesB to E form a normative part of this International Standard. AnnexA is for information only.SIST ISO 1456:2004

ISO1456:2003(E)© ISO2003–All rights reservedvIntroductionDecorative, electrodeposited nickel plus chromium and copper plus nickel plus chromium coatings are applied tomanufactured articles to enhance their appearance and corrosion resistance. Corrosion resistance depends on thetype and thickness of the coatings. In general, multilayer nickel coatings provide better corrosion resistance thansingle-layer nickel coatings of equal thickness, and microdiscontinuous chromium coatings provide better protectionthan conventional chromium.SIST ISO 1456:2004

SIST ISO 1456:2004

INTERNATIONAL STANDARDISO1456:2003(E)© ISO2003–All rights reserved1Metallic coatings— Electrodeposited coatings of nickel plus chromium and of copper plus nickel plus chromium1ScopeThis International Standard specifies the requirements for decorative, electroplated nickel plus chromium, andcopper plus nickel plus chromium coatings on iron, steel, zinc alloys, copper and copper alloys, and aluminium andaluminium alloys to provide an attractive appearance and enhanced corrosion resistance. Coating designations arespecified that differ in thickness and type, and guidance is given in selecting the coating designation appropriate tothe service conditions to which the coated product will be exposed.This International Standard does not specify the surface condition required by the base metal prior to the coatingprocess, and is not applicable to coatings on sheet, strip or wire in the non-fabricated form nor to threaded fastenersor coil springs.Requirements for decorative, electroplated copper plus nickel plus chromium coatings on plastic materials arespecified in ISO4525. Similar coatings, except for the absence of a top-coat of chromium, are specified in ISO1458.ISO4526 and ISO6158 specify requirements for coatings of nickel and chromium, respectively, for engineeringpurposes.2Normative referencesThe following normative documents contain provisions which, through reference in this text, constitute provisions ofthis International Standard. For dated references, subsequent amendments to, or revisions of, any of thesepublications do not apply. However, parties to agreements based on this International Standard are encouraged toinvestigate the possibility of applying the most recent editions of the normative documents indicated below. Forundated references, the latest edition of the normative document referred to applies. Members of ISO and IECmaintain registers of currently valid International Standards.ISO1463, Metallic and oxide coatings— Measurement of coating thickness— Microscopical methodISO2064, Metallic and other inorganic coatings— Definitions and conventions concerning the measurement ofthicknessISO2079, Surface treatment and metallic coatings— General classification of termsISO2080, Surface treatment, metallic and other inorganic coatings— VocabularyISO2177, Metallic coatings— Measurement of coating thickness— Coulometric method by anodic dissolutionISO2361, Electrodeposited nickel coatings on magnetic and non-magnetic substrates— Measurement of coatingthickness— Magnetic methodISO2819, Metallic coatings on metallic substrates— Electrodeposited and chemically deposited coatings— Reviewof methods available for testing adhesionISO3497, Metallic coatings— Measurement of coating thickness— X-ray spectrometric methodsISO3543, Metallic and non-metallic coatings— Measurement of thickness— Beta backscatter methodSIST ISO 1456:2004

ISO1456:2003(E)2© ISO2003–All rights reservedISO3882, Metallic and other inorganic coatings— Review of methods of measurement of thicknessISO4519, Electrodeposited metallic coatings and related finishes— Sampling procedures for inspection byattributesISO4541:1978, Metallic and other non-organic coatings— Corrodkote corrosion test (CORR test)ISO9220, Metallic coatings— Measurement of coating thickness— Scanning electron microscope methodISO9227:1990, Corrosion tests in artificial atmospheres— Salt spray testsISO9587, Metallic and other inorganic coatings— Pretreatments of iron or steel to reduce the risk of hydrogenembrittlementISO9588, Metallic and other inorganic coatings— Post-coating treatments of iron or steel to reduce the risk ofhydrogen embrittlementISO10289:1999, Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates—Rating of test specimens and manufactured articles subjected to corrosion testsISO10587, Metallic and other inorganic coatings— Test for residual embrittlement in both metallic-coated anduncoated externally-threaded articles and rods— Inclined wedge methodISO16348, Metallic and other inorganic coatings— Definitions and conventions concerning appearanceASTMB764-94, Standard Test Method for Simultaneous Thickness and Electrochemical Potential Determination ofIndividual Layers in Multilayer Nickel Deposit (STEP Test)3Terms and definitionsFor the purposes of this International Standard, the terms and definitions given in ISO2064, ISO2079, ISO2080and ISO16348 apply.4Information to be supplied by the purchaser to the electroplater4.1Essential informationWhen ordering articles to be electroplated in accordance with this International Standard, the purchaser shall providethe following information in writing, in e.g., the contract or purchase order, or on engineering drawings:a)the designation (see clause6);b)the appearance required, e.g., bright, dull or satin (see 6.3 and 7.1). Alternatively, samples showing the requiredfinish or range of finishes shall be supplied or approved by the purchaser, and used for comparison purposes(see 7.1);c)the significant surfaces, to be indicated on drawings of the parts or by providing suitably marked specimens;d)the type of corrosion test to be used (see 7.5 and Table8);e)the type of adhesion test to be used (see 7.4);f)the extent to which defects shall be tolerated on non-significant surfaces (see 7.1);g)positions on the significant surface for rack or contact marks, where such marks are unavoidable (see 7.1);h)sampling methods and acceptance levels (see clause8);i)the tensile strength of the steel and any requirement for prior or post treatments of iron or steel to reduce the riskof hydrogen embrittlement, as well as hydrogen embrittlement test methods (see 7.8 and 7.9).SIST ISO 1456:2004

ISO1456:2003(E)© ISO2003–All rights reserved34.2Additional information The following additional information may be provided by the purchaser, when appropriate:a)any requirements for STEP testing (see 7.6);b)thickness requirements on those areas that cannot be touched by a ball

in diameter (see 7.2);c)whether or not a copper undercoat is required (see 6.1 and 6.2).5Service condition numberThe service condition number is used by the purchaser to specify the degree of protection required, as related to theseverity of the conditions to which a product is to be subjected, in accordance with the following scale:5Exceptionally severe4Very severe3Severe2Moderate1MildTypical service conditions for which the various service condition numbers are appropriate are listed in annexA.6Designation6.1GeneralThe coating designation specifies the type and thickness of coatings appropriate for each service condition number(see Tables1 to 6 for various substrates) and comprises the following:a)the term, “Electroplated coating”, the number of this International Standard, ISO1456, followed by a hyphen;b)the chemical symbol for the base metal (or for the principal metal if an alloy) followed by a solidus () as follows:—Fe/for iron or steel;—Zn/for zinc alloys;—Cu/for copper and copper alloys;—Al/for aluminium or aluminium alloys;c)the chemical symbol for copper (Cu), if copper, or brass containing greater than

copper, is used as anundercoat;d)a number indicating the minimum local thickness, in micrometres, of the copper coating where applicable;e)a letter indicating the type of copper, where applicable;f)the chemical symbol for nickel (Ni);g)a number indicating the minimum local thickness, in micrometres, of the nickel coating;h)a letter designating the type of nickel coating (see 6.3);i)the chemical symbol for chromium (Cr);j)a letter or letters designating the type of chromium and its minimum local thickness (see 6.4).20mm/50%SIST ISO 1456:2004

ISO1456:2003(E)4© ISO2003–All rights reservedTable1—Nickel plus chromium coatings on iron or steelService condition numberPartial designationService condition numberPartial designation5Fe/Ni35d Cr mcFe/Ni35d Cr mp2Fe/Ni20b Cr rFe/Ni20b Cr mcFe/Ni20b Cr mpFe/Ni20p Cr rFe/Ni20p Cr mcFe/Ni20p Cr mpFe/Ni20s Cr rFe/Ni20s Cr mcFe/Ni20s Cr mp4Fe/Ni40d Cr r1Fe/Ni10b Cr rFe/Ni10p Cr rFe/Ni10s Cr rFe/Ni30d Cr mpFe/Ni30d Cr mcFe/Ni40p Cr rFe/Ni30p Cr mcFe/Ni30p Cr mp3Fe/Ni30d Cr r——Fe/Ni25d Cr mpFe/Ni25d Cr mcFe/Ni30p Cr rFe/Ni25p Cr mcFe/Ni25p Cr mpFe/Ni40b Cr rFe/Ni30b Cr mcFe/Ni30b Cr mpSIST ISO 1456:2004

ISO1456:2003(E)© ISO2003–All rights reserved5Table2—Copper plus nickel plus chromium coatings on iron or steelService condition numberPartial designation5Fe/Cu20a Ni30d Cr mcFe/Cu20a Ni30d Cr mp4Fe/Cu20a Ni30d Cr rFe/Cu20a Ni25d Cr mpFe/Cu20a Ni25d Cr mcFe/Cu20a Ni30p Cr rFe/Cu20a Ni25p Cr mcFe/Cu20a Ni25p Cr mpFe/Cu20a Ni30b Cr mcFe/Cu20a Ni30b Cr mp3Fe/Cu15a Ni25d Cr rFe/Cu15a Ni20d Cr mcFe/Cu15a Ni20d Cr mpFe/Cu15a Ni25p Cr rFe/Cu15a Ni20p Cr mcFe/Cu15a Ni20p Cr mpFe/Cu20a Ni35b Cr rFe/Cu20a Ni25b Cr mcFe/Cu20a Ni25b Cr mp2Fe/Cu20a Ni10b Cr rFe/Cu20a Ni10p Cr rFe/Cu20a Ni10s Cr r1Fe/Cu10a Ni5b Cr rFe/Cu10a Ni5p Cr rFe/Cu10a Ni20b Cr mpNOTEAn initial copper coating,

thick, is normally applied to iron and steelfrom a copper cyanide solution before electroplating with ductile acid copper to preventimmersion deposition and poorly adherent deposits. The initial copper coating (copper strike)may not be substituted for any portion of the ductile acid copper specified in Table2.5µm10µmSIST ISO 1456:2004

ISO1456:2003(E)6© ISO2003–All rights reservedTable3—Nickel plus chromium coatings on zinc alloysService condition numberPartial designationService condition numberPartial designation5Zn/Ni35d Cr mcZn/Ni35d Cr mp3Zn/Ni25d Cr rZn/Ni20d Cr mcZn/Ni20d Cr mpZn/Ni25p Cr rZn/Ni20p Cr mcZn/Ni20p Cr mpZn/Ni35b Cr rZn/Ni25b Cr mcZn/Ni25b Cr mp4Zn/Ni35d Cr r2Zn/Ni15b Cr rZn/Ni15p Cr rZn/Ni15s Cr rZn/Ni25d Cr mcZn/Ni25d Cr mpZn/Ni35p Cr rZn/Ni25p Cr mcZn/Ni25p Cr mpZn/Ni35b Cr mcZn/Ni35b Cr mp——1Zn/Ni8b Cr rZn/Ni8p Cr rZn/Ni8s Cr rNOTEZinc alloys must first be electroplated with copper to ensure adhesion of the subsequent nickel coatings. The initial layerof copper is usually electrodeposited from a copper cyanide solution, but cyanide-free alkaline copper solutions are also beingused. The minimum thickness of the initial copper layer is

to . For articles of complex shape, the minimum copperthickness may need to be increased to about

to ensure adequate coverage on low-current density areas outside thesignificant surfaces. Ductile, levelling copper electrodeposited from acid solutions is usually applied over the initial cyanidecopper deposit when the specified copper thickness is greater than .8µm10µm15µm10µmSIST ISO 1456:2004

ISO1456:2003(E)© ISO2003–All rights reserved7Table4—Copper plus nickel plus chromium coatings on zinc alloysService condition numberPartial designationService condition numberPartial designation5Zn/Cu20a Ni30d Cr mcZn/Cu20a Ni30d Cr mp3Zn/Cu15a Ni25d Cr rZn/Cu15a Ni20d Cr mcZn/Cu15a Ni20d Cr mpZn/Cu15a Ni25p Cr rZn/Cu15a Ni20p Cr mcZn/Cu15a Ni20p Cr mpZn/Cu20a Ni30b Cr rZn/Cu20a Ni20b Cr mcZn/Cu20a Ni20b Cr mp4Zn/Cu20a Ni30d Cr r2Zn/Cu20a Ni20d Cr mcZn/Cu20a Ni20d Cr mpZn/Cu20a Ni30p Cr rZn/Cu20a Ni10b Cr rZn/Cu20a Ni20p Cr mcZn/Cu20a Ni10p Cr rZn/Cu20a Ni20p Cr mpZn/Cu20a Ni10s Cr rZn/Cu20a Ni30b Cr mcZn/Cu20a Ni30b Cr mp——1Zn/Cu10a Ni8b Cr rZn/Cu10a Ni8p Cr rZn/Cu10a Ni8s Cr rNOTEZinc alloys must first be electroplated with copper to ensure adhesion of the subsequent nickel coatings. The initial layerof copper is usually electrodeposited from a copper cyanide solution, but cyanide-free alkaline copper solutions are also beingused. The minimum thickness of the initial copper layer is

to . For articles of complex shape, the minimum copperthickness may need to be increased to about

to ensure adequate coverage on low-current density areas outside thesignificant surfaces. Ductile, levelling copper electrodeposited from acid solutions is usually applied over the initial cyanidecopper deposit when the specified copper thickness is greater than .8µm10µm15µm10µmSIST ISO 1456:2004

ISO1456:2003(E)8© ISO2003–All rights reservedTable5—Nickel plus chromium coatings on copper and copper alloysService condition numberPartial designation4Cu/Ni30d Cr rCu/Ni25d Cr mcCu/Ni25d Cr mpCu/Ni30p Cr rCu/Ni25p Cr mcCu/Ni25p Cr mpCu/Ni30b Cr mcCu/Ni30b Cr mp3Cu/Ni25d Cr rCu/Ni20d Cr mcCu/Ni20d Cr mpCu/Ni25p Cr rCu/Ni20p Cr mcCu/Ni20p Cr mpCu/Ni30b Cr rCu/Ni25b Cr mcCu/Ni25b Cr mp2Cu/Ni10b Cr rCu/Ni10p Cr rCu/Ni10s Cr r1Cu/Ni5b Cr rCu/Ni5p Cr rCu/Ni5s Cr rSIST ISO 1456:2004

ISO1456:2003(E)© ISO2003–All rights reserved96.2Type of copper coatingThe type of copper is designated by the symbol “a” for ductile, levelling copper electrodeposited from acid-typesolutions.6.3Types of nickel coatingThe types of nickel coating shall be designated by the following symbols:—b, for nickel deposited in the fully bright condition;—p, for dull or semi-bright nickel which has been mechanically polished;—s, for dull, semi-bright or satin nickel that shall not have been mechanically polished;—d, for double- or triple-layer coatings, the requiremen

...

NORME ISO
INTERNATIONALE 1456
Troisième édition
2003-02-15
Revêtements métalliques — Dépôts
électrolytiques de nickel plus chrome et de
cuivre plus nickel plus chrome
Metallic coatings — Electrodeposited coatings of nickel plus chromium and
of copper plus nickel plus chromium
Numéro de référence
ISO 1456:2003(F)
© ISO 2003
---------------------- Page: 1 ----------------------
ISO 1456:2003(F)
PDF — Exonération de responsabilité

Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier peut

être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence autorisant

l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées acceptent de fait la

responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute responsabilité en la

matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.

Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du

fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation de

ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer le

Secrétariat central à l'adresse donnée ci-dessous.
© ISO 2003

Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous

quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de

l'ISO à l'adresse ci-après ou au comité membre de l'ISO dans le pays du demandeur.

ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Imprimé en Suisse
ii ISO 2003 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 1456:2003(F)
Sommaire Page

1 Domaine d'application ...................................................................................................................................... 1

2 Références normatives ..................................................................................................................................... 1

3 Termes et définitions ......................................................................................................................................... 2

4 Informations à fournir par l'acheteur à l'applicateur du dépôt ........................................................................... 2

5 Numéro de condition d'utilisation ...................................................................................................................... 3

6 Désignation ....................................................................................................................................................... 3

7 Exigences ....................................................................................................................................................... 11

8 Échantillonnage .............................................................................................................................................. 13

Annexes

A Exemples de conditions d'utilisation correspondant aux différents numéros de condition d'utilisation........... 14

B Détermination des fissures et des pores dans les dépôts de chrome ............................................................ 15

C Méthodes d'essai pour la détermination de l'épaisseur .................................................................................. 16

D Essai de ductilité............................................................................................................................................. 18

E Dosage du soufre dans les dépôts électrolytiques de nickel........................................................................... 19

Bibliographie.......................................................................................................................................................... 20

ISO 2003 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 1456:2003(F)
Avant-propos

L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de

normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux

comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité

technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en liaison

avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission électrotechnique

internationale (CEI) en ce qui concerne la normalisation électrotechnique.

Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 3.

Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour

vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres

votants.

L'attention est appelée sur le fait que certains des éléments de la présente Norme internationale peuvent faire l'objet

de droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne pas

avoir identifié de tels droits de propriété et averti de leur existence.

La Norme internationale ISO 1456 a été élaborée par le comité technique ISO/TC 107, Revêtements métalliques et

autres revêtements inorganiques, sous-comité SC 3, Dépôts électrolytiques et finitions apparentées.

Cette troisième édition annule et remplace la deuxième édition (ISO 1456:1988), qui a fait l’objet d’une révision

rédactionnelle et technique.

Les annexes B à E constituent des éléments normatifs de la présente Norme internationale. L'annexe A est donnée

uniquement à titre d'information.
iv ISO 2003 – Tous droits réservés
---------------------- Page: 4 ----------------------
ISO 1456:2003(F)
Introduction

Les dépôts électrolytiques décoratifs de nickel plus chrome et de cuivre plus nickel plus chrome sont appliqués sur

des articles fabriqués afin d'améliorer leur aspect et leur résistance à la corrosion. La résistance à la corrosion

dépend du type et de l'épaisseur du dépôt. De façon générale, les dépôts multicouches de nickel ont une résistance

à la corrosion meilleure que les dépôts de nickel constitués d'une seule couche d'épaisseur homogène, et les dépôts

de chrome microdiscontinus offrent une protection meilleure que le chrome ordinaire.

ISO 2003 – Tous droits réservés v
---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 1456:2003(F)
Revêtements métalliques — Dépôts électrolytiques de nickel plus
chrome et de cuivre plus nickel plus chrome
1 Domaine d'application

La présente Norme internationale spécifie les exigences relatives aux dépôts électrolytiques décoratifs de nickel plus

chrome et de cuivre plus nickel plus chrome appliqués sur le fer, l'acier, les alliages de zinc, le cuivre et les alliages

de cuivre, l'aluminium et les alliages d'aluminium pour leur conférer un aspect agréable et pour améliorer leur

résistance à la corrosion. Des désignations de dépôts sont spécifiées pour différentes épaisseurs et différents types

de dépôts, et des indications sont données quant au choix du dépôt approprié pour la condition d'utilisation prévue

du produit revêtu.

La présente Norme internationale ne spécifie pas l'état de surface du métal de base avant dépôt électrolytique et

n'est pas applicable aux dépôts sur tôles, bandes ou fils bruts de laminage, sur éléments de fixation filetés ou sur

ressorts en spirale.

Les exigences concernant les dépôts décoratifs électrolytiques de cuivre plus nickel plus chrome appliqués sur des

produits en matière plastique sont spécifiées dans l'ISO 4525. Les dépôts similaires mais n'ayant pas de dépôt final

de chrome sont spécifiés dans l'ISO 1458.

L'ISO 4526 et l'ISO 6158 spécifient les exigences applicables aux dépôts de nickel et de chrome, respectivement,

pour des usages industriels.
2Références normatives

Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,

constituent des dispositions valables pour la présente Norme internationale. Pour les références datées, les

amendements ultérieurs ou les révisions de ces publications ne s'appliquent pas. Toutefois, les parties prenantes

aux accords fondés sur la présente Norme internationale sont invitées à rechercher la possibilité d'appliquer les

éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière

édition du document normatif en référence s'applique. Les membres de l'ISO et de la CEI possèdent le registre des

Normes internationales en vigueur.

ISO 1463, Revêtements métalliques et couches d'oxyde — Mesurage de l'épaisseur de revêtement — Méthode par

coupe micrographique

ISO 2064, Revêtements métalliques et autres revêtements inorganiques — Définitions et principes concernant le

mesurage de l'épaisseur

ISO 2079, Traitements de surface et revêtements métalliques — Classification générale des termes

ISO 2080, Traitements de surface, revêtements métalliques et autres revêtements inorganiques — Vocabulaire

ISO 2177, Revêtements métalliques — Mesurage de l'épaisseur — Méthode coulométrique par dissolution

anodique

ISO 2361, Revêtements électrolytiques de nickel sur métal de base magnétique et non magnétique — Mesurage de

l'épaisseur — Méthode magnétique

ISO 2819, Revêtements métalliques sur bases métalliques — Dépôts électrolytiques et dépôts par voie chimique —

Liste des différentes méthodes d'essai d'adhérence
ISO 2003 – Tous droits réservés 1
---------------------- Page: 6 ----------------------
ISO 1456:2003(F)

ISO 3497, Revêtements métalliques — Mesurage de l'épaisseur du revêtement — Méthodes par spectrométrie de

rayons X

ISO 3543, Revêtements métalliques et non métalliques — Mesurage de l'épaisseur — Méthode par rétrodiffusion

des rayons bêta

ISO 3882, Revêtements métalliques et autres revêtements inorganiques — Vue d'ensemble sur les méthodes de

mesurage de l'épaisseur

ISO 4519, Dépôts électrolytiques et finitions apparentées — Méthodes d'échantillonnage pour le contrôle par

attributs

ISO 4541:1978, Revêtements métalliques et autres revêtements non organiques — Essai de corrosion Corrodkote

(Essai CORR)

ISO 9220, Revêtements métalliques — Mesurage de l'épaisseur de revêtement — Méthode au microscope

électronique à balayage

ISO 9227:1990, Essais de corrosion en atmosphères artificielles — Essais aux brouillards salins

ISO 9587, Revêtements métalliques et autres revêtements inorganiques — Prétraitements du fer ou de l'acier pour

diminuer le risque de fragilisation par l'hydrogène

ISO 9588, Revêtements métalliques et autres revêtements inorganiques — Traitements après revêtement sur fer ou

acier pour diminuer le risque de fragilisation par l'hydrogène

ISO 10289:1999, Méthodes d'essai de corrosion des revêtements métalliques et inorganiques sur substrats

métalliques — Cotation des éprouvettes et des articles manufacturés soumis aux essais de corrosion

ISO 10587, Revêtements métalliques et autres revêtements inorganiques — Essai de fragilisation résiduelle des

articles et tiges filetés avec et sans revêtement métallique extérieur — Méthode de la cale biaise

ISO 16348, Revêtements métalliques et autres revêtements inorganiques — Définitions et principes concernant

l'apparence

ASTM B764-94, Standard Test Method for Simultaneous Thickness and Electrochemical Potential Determination of

Individual Layers in Multilayer Nickel Deposit (STEP Test)
3 Termes et définitions

Pour les besoins de la présente Norme internationale, les termes et définitions donnés dans l'ISO 2064, l’ISO 2079,

l’ISO 2080 et l’ISO 16348 s'appliquent.
4 Informations à fournir par l'acheteur à l'applicateur du dépôt
4.1 Informations essentielles

Lors de la commande de pièces à revêtir électrolytiquement conformément à la présente Norme internationale,

l'acheteur doit indiquer les informations suivantes par écrit, par exemple dans le contrat ou le bon de commande, ou

sur les plans:
a) la désignation (voir article 6);

b) l'aspect requis, par exemple brillant, mat ou satiné (voir 6.3 et 7.1). L'acheteur peut aussi fournir ou accepter des

échantillons présentant la finition ou la gamme de finition requise et les utiliser à des fins de comparaison

(voir 7.1);

c) les surfaces fonctionnelles, qui seront repérées sur des dessins des pièces ou sur des échantillons spéciaux;

2 ISO 2003 – Tous droits réservés
---------------------- Page: 7 ----------------------
ISO 1456:2003(F)
d) le type d'essai de corrosion à pratiquer (voir 7.5 et Tableau 8);
e) le type d'essai d'adhérence à utiliser (voir 7.4);

f) l'ampleur des défauts éventuels tolérés sur toutes les surfaces non fonctionnelles (voir 7.1);

g) la position des marques de contact ou de support sur les surfaces fonctionnelles, si celles-ci sont inévitables

(voir 7.1);
h) les méthodes d'échantillonnage et les niveaux de réception (voir article 8);

i) la résistance à la traction de l'acier et toute exigence applicable avant ou après les traitements du fer ou de l'acier

pour réduire le risque de fragilisation par l'hydrogène, ainsi que les méthodes d'essai de la fragilisation due à

l'hydrogène (voir 7.8 et 7.9).
4.2 Informations supplémentaires
Si nécessaire, l'acheteur peut fournir les informations suivantes:
a) toutes exigences applicables aux essais STEP (voir 7.6);

b) l'épaisseur requise aux points qui ne peuvent pas être atteints par une bille de 20 mm de diamètre (voir 7.2);

c) la nécessité éventuelle de la présence d'une sous-couche de cuivre (voir 6.1 et 6.2).

5Numéro de condition d'utilisation

Le numéro de condition d'utilisation est donné par l'acheteur pour préciser le degré de protection requis en fonction

de la sévérité des conditions d'utilisation selon l'échelle suivante:
5 Exceptionnellement sévères
4Très sévères
3Sévères
2Modérées
1 Douces

Des conditions d'utilisation types correspondant aux divers numéros de conditions d'utilisation sont indiquées dans

l'annexe A.
6Désignation
6.1 Généralités

La désignation du dépôt permet de spécifier le type et l'épaisseur des dépôts pour chaque condition d'utilisation (voir

les Tableaux 1 à 6 pour les différents substrats) et comprend les éléments suivants:

a) la mention «Dépôt électrolytique», le numéro de la présente Norme internationale, ISO 1456, suivi d'un tiret;

b) le symbole chimique du métal de base (ou du métal principal dans le cas d'un alliage) suivi d'une barre oblique

()/ , comme suit:
— Fe/ pour le fer ou l'acier;
— Zn/ pour les alliages de zinc;
— Cu/ pour le cuivre et les alliages de cuivre;
— Al/ pour l'aluminium et les alliages d'aluminium;
ISO 2003 – Tous droits réservés 3
---------------------- Page: 8 ----------------------
ISO 1456:2003(F)

c) le symbole chimique du cuivre (Cu), si du cuivre ou du laiton à plus de 50 % de cuivre sert de sous-couche;

d) un nombre correspondant à l'épaisseur locale minimale, en micromètres, du dépôt de cuivre éventuel;

e) une lettre désignant le type de cuivre, si nécessaire;
f) le symbole chimique du nickel (Ni);

g) un nombre correspondant à l'épaisseur locale minimale, en micromètres, du dépôt de nickel;

h) une lettre désignant le type de dépôt de nickel (voir 6.3);
i) le symbole chimique du chrome (Cr);

j) une lettre ou des lettres désignant le type de dépôt de chrome et son épaisseur locale minimale (voir 6.4).

Tableau 1 — Dépôts de nickel plus chrome sur le fer ou l’acier
Numéro de condition Numéro de condition
Désignation partielle Désignation partielle
d’utilisation d’utilisation
Fe/Ni20b Cr r
Fe/Ni20b Cr mc
Fe/Ni20b Cr mp
Fe/Ni20p Cr r
Fe/Ni35d Cr mc
5 2 Fe/Ni20p Cr mc
Fe/Ni35d Cr mp
Fe/Ni20p Cr mp
Fe/Ni20s Cr r
Fe/Ni20s Cr mc
Fe/Ni20s Cr mp
Fe/Ni40d Cr r
Fe/Ni30d Cr mp
Fe/Ni10b Cr r
Fe/Ni30d Cr mc
4 1 Fe/Ni10p Cr r
Fe/Ni40p Cr r
Fe/Ni10s Cr r
Fe/Ni30p Cr mc
Fe/Ni30p Cr mp
Fe/Ni30d Cr r
Fe/Ni25d Cr mp
Fe/Ni25d Cr mc
Fe/Ni30p Cr r
3 Fe/Ni25p Cr mc ——
Fe/Ni25p Cr mp
Fe/Ni40b Cr r
Fe/Ni30b Cr mc
Fe/Ni30b Cr mp
4 ISO 2003 – Tous droits réservés
---------------------- Page: 9 ----------------------
ISO 1456:2003(F)
Tableau 2 — Dépôts de cuivre plus nickel plus chrome sur le fer ou l’acier
Numéro de condition d’utilisation Désignation partielle
Fe/Cu20a Ni30d Cr mc
Fe/Cu20a Ni30d Cr mp
Fe/Cu20a Ni30d Cr r
Fe/Cu20a Ni25d Cr mp
Fe/Cu20a Ni25d Cr mc
Fe/Cu20a Ni30p Cr r
Fe/Cu20a Ni25p Cr mc
Fe/Cu20a Ni25p Cr mp
Fe/Cu20a Ni30b Cr mc
Fe/Cu20a Ni30b Cr mp
Fe/Cu15a Ni25d Cr r
Fe/Cu15a Ni20d Cr mc
Fe/Cu15a Ni20d Cr mp
Fe/Cu15a Ni25p Cr r
3 Fe/Cu15a Ni20p Cr mc
Fe/Cu15a Ni20p Cr mp
Fe/Cu20a Ni35b Cr r
Fe/Cu20a Ni25b Cr mc
Fe/Cu20a Ni25b Cr mp
Fe/Cu20a Ni10b Cr r
2 Fe/Cu20a Ni10p Cr r
Fe/Cu20a Ni10s Cr r
Fe/Cu10a Ni5b Cr r
1 Fe/Cu10a Ni5p Cr r
Fe/Cu10a Ni20b Cr mp

NOTE Un dépôt de cuivre initial, de 5µm1 à 0µmd'épaisseur, est normalement appliqué

sur le fer ou l'acier à l'aide d'une solution de cyanure de cuivre avant dépôt électrolytique du

cuivre ductile afin de prévenir une déposition par immersion et des dépôts de faible

adhérence. La couche initiale de cuivre (dépôt amorce de cuivre) ne peut être substituée à

aucune partie du cuivre ductile spécifié dans le Tableau 2.
ISO 2003 – Tous droits réservés 5
---------------------- Page: 10 ----------------------
ISO 1456:2003(F)
Tableau 3 — Dépôts de nickel plus chrome sur alliages de zinc
Numéro de condition Numéro de condition
Désignation partielle Désignation partielle
d’utilisation d’utilisation
Zn/Ni25d Cr r
Zn/Ni20d Cr mc
Zn/Ni20d Cr mp
Zn/Ni25p Cr r
Zn/Ni35d Cr mc
5 3 Zn/Ni20p Cr mc
Zn/Ni35d Cr mp
Zn/Ni20p Cr mp
Zn/Ni35b Cr r
Zn/Ni25b Cr mc
Zn/Ni25b Cr mp
Zn/Ni35d Cr r
Zn/Ni25d Cr mc
Zn/Ni25d Cr mp
Zn/Ni15b Cr r
Zn/Ni35p Cr r
4 2 Zn/Ni15p Cr r
Zn/Ni25p Cr mc
Zn/Ni15s Cr r
Zn/Ni25p Cr mp
Zn/Ni35b Cr mc
Zn/Ni35b Cr mp
Zn/Ni8b Cr r
—— 1 Zn/Ni8p Cr r
Zn/Ni8s Cr r

NOTE Les alliages de zinc doivent tout d'abord être recouverts de cuivre afin de garantir l'adhérence des dépôts ultérieurs de

nickel. La couche initiale de cuivre est généralement déposée à l'aide d'une solution de cyanure de cuivre, mais des solutions

de cuivre alcalin sans cyanure peuvent également convenir. L'épaisseur minimale de cette couche initiale de cuivre est

comprise entre 8µm1 et 0µm. Pour les pièces de forme complexe, il peut être nécessaire de porter l'épaisseur minimale de

cuivre sur la surface fonctionnelle à 15µm environ afin de garantir une couverture correcte des zones à densité de courant bas,

en dehors des surfaces fonctionnelles. Le cuivre nivelant ductile déposé par électrolyse en utilisant des solutions de type acide

est généralement appliqué sur le dépôt initial de cyanure de cuivre lorsque l'épaisseur de cuivre spécifiée est supérieure à

10µm.
6 ISO 2003 – Tous droits réservés
---------------------- Page: 11 ----------------------
ISO 1456:2003(F)
Tableau 4 — Dépôts de cuivre plus nickel plus chrome sur alliages de zinc
Numéro de condition Numéro de condition
Désignation partielle Désignation partielle
d’utilisation d’utilisation
Zn/Cu15a Ni25d Cr r
Zn/Cu15a Ni20d Cr mc
Zn/Cu15a Ni20d Cr mp
Zn/Cu15a Ni25p Cr r
Zn/Cu20a Ni30d Cr mc
5 3 Zn/Cu15a Ni20p Cr mc
Zn/Cu20a Ni30d Cr mp
Zn/Cu15a Ni20p Cr mp
Zn/Cu20a Ni30b Cr r
Zn/Cu20a Ni20b Cr mc
Zn/Cu20a Ni20b Cr mp
Zn/Cu20a Ni30d Cr r
Zn/Cu20a Ni20d Cr mc
Zn/Cu20a Ni20d Cr mp
Zn/Cu20a Ni30p Cr r Zn/Cu20a Ni10b Cr r
4 2
Zn/Cu20a Ni20p Cr mc Zn/Cu20a Ni10p Cr r
Zn/Cu20a Ni20p Cr mp Zn/Cu20a Ni10s Cr r
Zn/Cu20a Ni30b Cr mc
Zn/Cu20a Ni30b Cr mp
Zn/Cu10a Ni8b Cr r
—— 1 Zn/Cu10a Ni8p Cr r
Zn/Cu10a Ni8s Cr r

NOTE Les alliages de zinc doivent tout d'abord être recouverts de cuivre afin de garantir l'adhérence des dépôts ultérieurs de

nickel. La couche initiale de cuivre est généralement déposée à l'aide d'une solution de cyanure de cuivre, mais des solutions

de cuivre alcalin sans cyanure peuvent également convenir. L'épaisseur minimale de cette couche initiale de cuivre est

comprise entre 8µm1 et 0µm. Pour les pièces de forme complexe, il peut être nécessaire de porter l'épaisseur minimale de

cuivre sur la surface fonctionnelle à 15µm environ afin de garantir une couverture correcte des zones à densité de courant bas,

en dehors des surfaces fonctionnelles. Le cuivre nivelant ductile déposé par électrolyse en utilisant des solutions de type acide

est généralement appliqué sur le dépôt initial de cyanure de cuivre lorsque l'épaisseur de cuivre spécifiée est supérieure à

10µm.
ISO 2003 – Tous droits réservés 7
---------------------- Page: 12 ----------------------
ISO 1456:2003(F)
Tableau 5 — Dépôts de nickel plus chrome sur cuivre et alliages de cuivre
Numéro de condition d’utilisation Désignation partielle
Cu/Ni30d Cr r
Cu/Ni25d Cr mc
Cu/Ni25d Cr mp
Cu/Ni30p Cr r
Cu/Ni25p Cr mc
Cu/Ni25p Cr mp
Cu/Ni30b Cr mc
Cu/Ni30b Cr mp
Cu/Ni25d Cr r
Cu/Ni20d Cr mc
Cu/Ni20d Cr mp
Cu/Ni25p Cr r
3 Cu/Ni20p Cr mc
Cu/Ni20p Cr mp
Cu/Ni30b Cr r
Cu/Ni25b Cr mc
Cu/Ni25b Cr mp
Cu/Ni10b Cr r
2 Cu/Ni10p Cr r
Cu/Ni10s Cr r
Cu/Ni5b Cr r
1 Cu/Ni5p Cr r
Cu/Ni5s Cr r
8 ISO 2003 – Tous droits réservés
---------------------- Page: 13 ----------------------
ISO 1456:2003(F)
Tableau 6 — Dépôts de nickel plus chrome sur aluminium et alliages d’aluminium
Numéro de condition d’utilisation Désignation partielle
Al/Ni40d Cr mc
Al/Ni40d Cr mp
Al/Ni50d Cr r
4 Al/Ni35d Cr mc
Al/Ni35d Cr mp
Al/Ni30d Cr r
Al/Ni25d Cr mc
Al/Ni25d Cr mp
Al/Ni35p Cr r
Al/Ni30p Cr mc
Al/Ni30p Cr mp
Al/Ni20d Cr r
Al/Ni20d Cr mc
Al/Ni20d Cr mp
Al/Ni25b Cr r
Al/Ni25b Cr mc
Al/Ni25b Cr mp
Al/Ni20p Cr r
Al/Ni20p Cr mc
Al/Ni20p Cr mp
Al/Ni20s Cr r
Al/Ni20s Cr mc
Al/Ni20s Cr mp
1 Al/Ni10b Cr r

NOTE Sur l'aluminium et les alliages d'aluminium, la déposition par immersion de zinc ou

d'étain et le dépôt par électrolyse de cuivre et d'autres sous-couches sont utilisés dans le

cadre de la préparation de l'électrodéposition afin de garantir l'adhérence avant d'appliquer

les dépôts de nickel désignés spécifiés dans le tableau.
6.2 Type de dépôt de cuivre

Le type de dépôt de cuivre est désigné par le symbole «a» pour le cuivre nivelant ductile déposé électrolytiquement

à l'aide de solutions de type acide.
6.3 Types de dépôt de nickel
Les types de dépôt de nickel doivent être désignés par un symbole, comme suit:
— b, pour le nickel déposé à l'état brillant;

— p, pour le nickel mat ou semi-brillant qui a été poli par des moyens mécaniques;

— s, pour le nickel mat, semi-brillant ou satiné qui ne doit pas avoir été poli par des moyens mécaniques;

— d, pour des dépôts à double ou à triple couche présentant les propriétés données dans le Tableau 7.

ISO 2003 – Tous droits réservés 9
---------------------- Page: 14 ----------------------
ISO 1456:2003(F)

Tableau 7 — Exigences applicables aux dépôts de nickel à double couche ou à triple couche

Allongement
b c
Couche Teneur en soufre Épaisseur
spécifique
en pourcentage de l’épaisseur totale de nickel
(type de dépôt de
%%Fraction massique en Double couche Triple couche
nickel)
Inférieure (s) > 8 < 0,005 � 60 50 à 70
Moyenne (haute
——> 0,15 � 10
teneur en soufre)
Supérieure (b) — > 0,04 et < 0,15 10 à 40 � 30

La méthode d'essai permettant de déterminer l'allongement spécifique (ou ductilité) est décrite dans l'annexe D.

La teneur en soufre est spécifiée pour indiquer le type de solution de dépôt électrolytique de nickel à utiliser. Il n'existe aucune méthode

simple de détermination de la teneur en soufre d'un dépôt de nickel sur pièce revêtue. Un dosage précis est néanmoins possible si l'éprouvette

est préparée spécialement par les méthodes spécifiées dans l'annexe E.

Il est habituellement possible d'identifier le type et de déterminer les rapports d'épaisseur des couches de nickel, par examen au microscope

d'une section polie et décapée à l'acide d'une pièce préparée suivant les indications de l'ISO 1463, ou par l'essai STEP.

6.4 Types et épaisseurs de chrome

Le type et l'épaisseur de chrome doivent être désignés par les symboles suivants, placés derrière le symbole

chimique, Cr, comme suit:
— r, pour le chrome ordinaire ayant une épaisseur locale minimale de 0,3µm;

— mc, pour le chrome microfissuré ayant une épaisseur de 0,3µm, plus de 250 fissures par centimètre dans toutes

les directions, et formant un réseau serré sur toute la surface fonctionnelle, en cas de détermination par l'une des

méthodes spécifiées dans l'annexe B. Certains processus nécessitent une épaisseur de chrome nettement plus

forte (environ 0,8µm) pour donner la microfissuration requise, auquel cas l'épaisseur locale minimale doit être

incluse dans la désignation du dépôt, comme suit: Cr mc (0,8);

— mp, pour le chrome microporeux ayant une épaisseur locale minimale de 0,3µm et contenant au moins

10 000 pores au centimètre carré en cas de détermination par la méthode spécifiée à l'annexe E. Les pores

doivent être invisibles à l'œil nu ou avec une correction oculaire.

NOTE 1 Le chrome microporeux s'obtient souvent par le dépôt de chrome sur une couche mince spéciale de nickel contenant

des particules inertes non conductrices, appliquée elle-même sur du nickel b, s, p ou d.

NOTE 2 Après une certaine période d'utilisation, les dépôts de chrome mp ou mc tendent à perdre leur lustre, perte qui peut être

inacceptable dans certaines utilisations. Cette tendance peut être réduite par augmentation de l'épaisseur minimale du dépôt de

chrome jusqu'à 0,5µm chaque fois qu'un chrome microporeux ou microfissuré est spécifié dans les Tableaux 1 à 6.

6.5 Exemple de désignation

EXEMPLE Un dépôt sur acier comprenant 20µm3 (au minimum) de cuivre nivelant ductile plus 0µm (au minimum) de nickel

brillant plus 0,3µm de chrome microfissuré s'exprime comme suit:
Dépôt électrolytique ISO 1456 - Fe/Cu20a Ni30b Cr mc

NOTE Lors de la commande, il convient que la spécification détaillée du produit comprenne non seulement la désignation, mais

aussi un énoncé explicite de toutes autres exigences essentielles permettant d'assurer l'aptitude à l'emploi du produit concerné

(voir article 4).
10 ISO 2003 – Tous droits réservés
---------------------- Page: 15 ----------------------
ISO 1456:2003(F)
7Exigences
7.1 Aspect

Sur la surface fonctionnelle, le dépôt ne doit pas présenter de défauts visibles tels que cloques, piqûres, rugosités,

fissures ou surfaces non recouvertes, et il ne doit être ni taché, ni décoloré. L'étendue sur laquelle des défauts

peuvent être tolérés sur les surfaces non fonctionnelles doit être spécifiée par l'acheteur. Lorsqu'une marque de

contact sur la surface fonctionnelle ne peut être évitée, son emplacement doit être spécifié par l'acheteur. L'aspect

doit être uniforme et de la couleur convenue. Des échantillons approuvés de produits doivent être utilisés pour

comparaison [voir 4.1 b)].
7.2 Épaisseur locale

L'épaisseur de dépôt spécifiée dans la désignation constitue l'épaisseur locale minimale. L'épaisseur locale

minimale des dépôts électrolytiques doit, sauf spécification contraire de la part de l'acheteur, être mesurée en tout

point de la surface fonctionnelle pouvant être atteint par une bille de 20 mm de diamètre.

L'épaisseur de la couche appliquée par électrodéposition doit être mesurée à l'aide de l'une des méthodes indiquées

à l'annexe C.
7.3 Dépôts de nickel à double couche ou à triple couche

Les exigences applicables aux dépôts de nickel à double couche ou à triple couche sont récapitulées dans le

Tableau 7.
7.4 Adhérence

Le dépôt doit adhérer suffisamment au métal de base, de même que les diverses couches d'un dépôt multicouche

de nickel entre elles, pour que le dépôt satisfasse aux conditions de l'essai à la lime ou de l'essai de choc thermique

spécifiées dans l'ISO 2819. Il ne doit se produire ni décollement du dépôt de son support, ni séparation des couches

du dépôt.

NOTE Il incombe à l'applicateur du dépôt de s'assurer que la méthode de préparation de surface avant électrodéposition permet

d'obtenir une surface qui satisfasse aux exigences du présent paragraphe.

7.5 Résistance à la corrosion par essais CASS, Corrodkote et au brouillard salin acétique

Les pièces revêtues doivent être soumises à l'un des essais de corrosion indiqué dans le Tableau 8 pendant le temps

convenu correspondant au numéro particulier de condition d'utilisation. L'essai particulier à utiliser dans chaque cas

doit être spécifié par l'acheteur. Les essais de corrosion décrits dans l'ISO 4541 et l'ISO 9227 sont utiles pour le

contrôle de la continuité et de la qualité du dépôt, mais la durée et les résultats de ces essais ne sont pas liés à la

durée de vie de la pièce finie. Une fois les pièces soumises à l'essai approprié de corrosion, elles doivent être

examinées et évaluées conformément à l'ISO 10289. L'évaluation minimale après l'essai de corrosion doit être égale

à 9.
7.6 Exigences d'essai STEP

Lorsque l'acheteur le spécifie, les différences de potentiel électrochimique entre les différentes couches de nickel

des dépôts multicouches doivent être mesurées au moyen de l'essai STEP décrit dans l’ASTM B764-94.

Dans les dépôts de nickel à triple couche, la différence de potentiel STEP entre la couche de nickel spéciale

d'activité élevée et la couche brillante de nickel se situe dans une plage comprise entre 15 mV et 35 mV, et la couche

avec une activité élevée est toujours plus active (anodique) que la couche brillante de nickel.

ISO 2003 – Tous droits réservés 11
---------------------- Page: 16 ----------------------
ISO 1456:200
...

Questions, Comments and Discussion