ISO 8840:2021
(Main)Refractory materials — Determination of bulk density of granular materials (grain density)
Refractory materials — Determination of bulk density of granular materials (grain density)
This document specifies three methods for the determination of the bulk density of granular refractory materials (grain density) having a grain size larger than 2 mm: — Method 1: mercury method with vacuum; — Method 2: arrested water absorption method; — Method 3: vacuum method with spin dryer option according to ISO 5017. Method 1 is intended as the reference method. NOTE Depending on the nature of the material tested, the three methods can give different results. Any statement of the value of a bulk density can therefore be accompanied by an indication of the method used or to be used in case of dispute. The same method can be used for the determination of the volume of the sample, for selecting and preparing the sample, for calculating the bulk density and for presenting the test report.
Matériaux réfractaires — Détermination de la masse volumique apparente des matériaux en grains (masse volumique des grains)
Le présent document spécifie trois méthodes permettant de déterminer la masse volumique apparente des matériaux réfractaires en grains (masse volumique des grains) dont la granulométrie est supérieure à 2 mm: — Méthode 1: méthode au mercure sous vide; — Méthode 2: méthode par arrêt de l’absorption d’eau; — Méthode 3: méthode sous vide avec option d’essorage conformément à l’ISO 5017. La méthode 1 est la méthode de référence. NOTE Selon la nature du matériau soumis à l’essai, les trois méthodes peuvent donner des résultats différents. Tout énoncé de la valeur d’une masse volumique apparente peut par conséquent s’accompagner d’une mention de la méthode utilisée ou à utiliser en cas de litige. La même méthode peut être utilisée pour déterminer le volume de l’échantillon, pour choisir et préparer l’échantillon, pour calculer sa masse volumique apparente et pour présenter le rapport d’essai.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 8840
Second edition
2021-09
Refractory materials — Determination
of bulk density of granular materials
(grain density)
Matériaux réfractaires — Détermination de la masse volumique
apparente des matériaux en grains (masse volumique des grains)
Reference number
©
ISO 2021
© ISO 2021
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2021 – All rights reserved
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Sampling . 2
6 Preparation, number and test size of samples . 2
6.1 Preparation of samples . 2
6.2 Number of samples . 2
6.3 Mass of test samples . 2
7 Determination of mass of test sample . 2
8 Determination of volume of test sample — Method 1: Mercury method with vacuum .3
8.1 Principle . 3
8.2 Apparatus . 4
8.3 Determination of mass of empty vacuum pycnometer . 5
8.4 Determination of mass of pycnometer filled with mercury . 6
8.5 Determination of mass of pycnometer containing test sample and filled with mercury . 6
8.6 Calculation of volume of test sample . 6
9 Determination of volume of test sample — Method 2: Arrested water absorption method .7
9.1 Apparatus . 7
9.2 Determination of volume of test sample . 7
9.3 Calculation of results . 8
10 Determination of bulk density of test sample — Method 3: Vacuum method with
spin dryer option . 8
10.1 Principle . 8
10.2 Apparatus and materials . 8
10.3 Procedure . 9
10.3.1 Determination of the mass of dry test piece (m ). 9
10.3.2 Soaking of the test sample .10
10.3.3 Determination of the apparent mass of the immersed test sample (m )
and the mass of the soaked test sample (m ) .10
10.4 Calculation of results .12
10.4.1 Calculation of the volume of the test sample (V ) .12
R
10.4.2 Calculation of the bulk density of the test sample (ρ ) .12
R
10.5 Precision and bias .12
10.5.1 Interlaboratory data .12
10.5.2 Precision.12
10.5.3 Bias .13
11 Test report .13
Bibliography .14
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www .iso .org/
iso/ foreword .html.
This document was prepared by Technical Committee 33, Refractories.
This second edition cancels and replaces the first edition (ISO 8840:1987), which has been technically
revised.
The main changes compared to the previous edition are as follows:
— a new method according to ISO 5017 has been added. It is identical to the method given in EN 993-18
with a suggested improvement to avoid the most influencing factor of the operator.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2021 – All rights reserved
INTERNATIONAL STANDARD ISO 8840:2021(E)
Refractory materials — Determination of bulk density of
granular materials (grain density)
1 Scope
This document specifies three methods for the determination of the bulk density of granular refractory
materials (grain density) having a grain size larger than 2 mm:
— Method 1: mercury method with vacuum;
— Method 2: arrested water absorption method;
— Method 3: vacuum method with spin dryer option according to ISO 5017.
Method 1 is intended as the reference method.
NOTE Depending on the nature of the material tested, the three methods can give different results. Any
statement of the value of a bulk density can therefore be accompanied by an indication of the method used or to
be used in case of dispute.
The same method can be used for the determination of the volume of the sample, for selecting and
preparing the sample, for calculating the bulk density and for presenting the test report.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 383, Laboratory glassware — Interchangeable conical ground joints
ISO 385-1, Laboratory glassware — Burettes — Part 1: General requirements
ISO 5017, Dense shaped refractory products — Determination of bulk density, apparent porosity and true
porosity
ISO 8656, Refractory products — Raw materials and unshaped products — Sampling
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
grain density
bulk density of granular material
ratio of the mass of a quantity of the material to the total volume of its grains, including the volume of
any closed pores (3.2) within the grains
3.2
closed pore
pore that is not penetrated by a liquid in which the grains are immersed
4 Principle
Measurement of the volume of a given mass of a granular material by displacement of a liquid.
5 Sampling
Sampling shall be carried out in accordance with ISO 8656 or with another standard sampling scheme
agreed between the interested parties.
6 Preparation, number and test size of samples
6.1 Preparation of samples
The material to be tested shall consist of fractions or groups of fractions with grain sizes above 2 mm.
Laboratory samples shall be produced by sieving, after any preliminary comminution of the material
above 5,6 mm grain size. Test results can be affected by the comminution technique and the equipment
used.
Any dust or loose particles adhering to the grains shall be removed before testing by washing or, with
materials sensitive to moisture or humidity, by air blowing.
To improve reproducibility, it is recommended to reduce the distribution of grains from between 2 mm
and 5,6 mm to between 3 mm and 4 mm.
6.2 Number of samples
Take at least three test samples from the laboratory sample and carry out one determination of bulk
density on each test sample.
6.3 Mass of test samples
The mass of test samples depends on the grain size and the homogeneity of the material. Recommended
sizes are shown in Table 1.
Table 1 — Mass of test samples
Size of test samples
Grain fraction
Method
g
mm
Good homogeneity Poor homogeneity
1 100 200
2,0 to 5,6
2 50 50
3,0 to 4,0 3 200 200
7 Determination of mass of test sample
Dry the test sample to constant mass in the drying oven maintained at 110 ± 5 °C and allow it to cool to
ambient tem
...
INTERNATIONAL ISO
STANDARD 8840
Second edition
2021-09
Refractory materials — Determination
of bulk density of granular materials
(grain density)
Matériaux réfractaires — Détermination de la masse volumique
apparente des matériaux en grains (masse volumique des grains)
Reference number
©
ISO 2021
© ISO 2021
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2021 – All rights reserved
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Sampling . 2
6 Preparation, number and test size of samples . 2
6.1 Preparation of samples . 2
6.2 Number of samples . 2
6.3 Mass of test samples . 2
7 Determination of mass of test sample . 2
8 Determination of volume of test sample — Method 1: Mercury method with vacuum .3
8.1 Principle . 3
8.2 Apparatus . 4
8.3 Determination of mass of empty vacuum pycnometer . 5
8.4 Determination of mass of pycnometer filled with mercury . 6
8.5 Determination of mass of pycnometer containing test sample and filled with mercury . 6
8.6 Calculation of volume of test sample . 6
9 Determination of volume of test sample — Method 2: Arrested water absorption method .7
9.1 Apparatus . 7
9.2 Determination of volume of test sample . 7
9.3 Calculation of results . 8
10 Determination of bulk density of test sample — Method 3: Vacuum method with
spin dryer option . 8
10.1 Principle . 8
10.2 Apparatus and materials . 8
10.3 Procedure . 9
10.3.1 Determination of the mass of dry test piece (m ). 9
10.3.2 Soaking of the test sample .10
10.3.3 Determination of the apparent mass of the immersed test sample (m )
and the mass of the soaked test sample (m ) .10
10.4 Calculation of results .12
10.4.1 Calculation of the volume of the test sample (V ) .12
R
10.4.2 Calculation of the bulk density of the test sample (ρ ) .12
R
10.5 Precision and bias .12
10.5.1 Interlaboratory data .12
10.5.2 Precision.12
10.5.3 Bias .13
11 Test report .13
Bibliography .14
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www .iso .org/
iso/ foreword .html.
This document was prepared by Technical Committee 33, Refractories.
This second edition cancels and replaces the first edition (ISO 8840:1987), which has been technically
revised.
The main changes compared to the previous edition are as follows:
— a new method according to ISO 5017 has been added. It is identical to the method given in EN 993-18
with a suggested improvement to avoid the most influencing factor of the operator.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2021 – All rights reserved
INTERNATIONAL STANDARD ISO 8840:2021(E)
Refractory materials — Determination of bulk density of
granular materials (grain density)
1 Scope
This document specifies three methods for the determination of the bulk density of granular refractory
materials (grain density) having a grain size larger than 2 mm:
— Method 1: mercury method with vacuum;
— Method 2: arrested water absorption method;
— Method 3: vacuum method with spin dryer option according to ISO 5017.
Method 1 is intended as the reference method.
NOTE Depending on the nature of the material tested, the three methods can give different results. Any
statement of the value of a bulk density can therefore be accompanied by an indication of the method used or to
be used in case of dispute.
The same method can be used for the determination of the volume of the sample, for selecting and
preparing the sample, for calculating the bulk density and for presenting the test report.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 383, Laboratory glassware — Interchangeable conical ground joints
ISO 385-1, Laboratory glassware — Burettes — Part 1: General requirements
ISO 5017, Dense shaped refractory products — Determination of bulk density, apparent porosity and true
porosity
ISO 8656, Refractory products — Raw materials and unshaped products — Sampling
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
grain density
bulk density of granular material
ratio of the mass of a quantity of the material to the total volume of its grains, including the volume of
any closed pores (3.2) within the grains
3.2
closed pore
pore that is not penetrated by a liquid in which the grains are immersed
4 Principle
Measurement of the volume of a given mass of a granular material by displacement of a liquid.
5 Sampling
Sampling shall be carried out in accordance with ISO 8656 or with another standard sampling scheme
agreed between the interested parties.
6 Preparation, number and test size of samples
6.1 Preparation of samples
The material to be tested shall consist of fractions or groups of fractions with grain sizes above 2 mm.
Laboratory samples shall be produced by sieving, after any preliminary comminution of the material
above 5,6 mm grain size. Test results can be affected by the comminution technique and the equipment
used.
Any dust or loose particles adhering to the grains shall be removed before testing by washing or, with
materials sensitive to moisture or humidity, by air blowing.
To improve reproducibility, it is recommended to reduce the distribution of grains from between 2 mm
and 5,6 mm to between 3 mm and 4 mm.
6.2 Number of samples
Take at least three test samples from the laboratory sample and carry out one determination of bulk
density on each test sample.
6.3 Mass of test samples
The mass of test samples depends on the grain size and the homogeneity of the material. Recommended
sizes are shown in Table 1.
Table 1 — Mass of test samples
Size of test samples
Grain fraction
Method
g
mm
Good homogeneity Poor homogeneity
1 100 200
2,0 to 5,6
2 50 50
3,0 to 4,0 3 200 200
7 Determination of mass of test sample
Dry the test sample to constant mass in the drying oven maintained at 110 ± 5 °C and allow it to cool to
ambient tem
...
NORME ISO
INTERNATIONALE 8840
Deuxième édition
2021-09
Matériaux réfractaires —
Détermination de la masse volumique
apparente des matériaux en grains
(masse volumique des grains)
Refractory materials — Determination of bulk density of granular
materials (grain density)
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2021
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 1
4 Principe. 2
5 Échantillonnage .2
6 Préparation, nombre et taille des échantillons . 2
6.1 Préparation des échantillons . 2
6.2 Nombre d’échantillons . 2
6.3 Masse des échantillons pour essai . 2
7 Détermination de la masse d’un échantillon pour essai . 3
8 Détermination du volume d’un échantillon pour essai — Méthode 1: méthode au
mercure sous vide . 3
8.1 Principe . 3
8.2 Appareillage . 4
8.3 Détermination de la masse à vide du pycnomètre . 5
8.4 Détermination de la masse du pycnomètre rempli de mercure . 6
8.5 Détermination de la masse du pycnomètre contenant l’échantillon pour essai et
le mercure . 6
8.6 Calcul du volume de l’échantillon pour essai . 6
9 Détermination du volume de l’échantillon pour essai — Méthode 2: méthode par
arrêt de l’absorption d’eau .7
9.1 Appareillage . 7
9.2 Détermination du volume de l’échantillon pour essai . 7
9.3 Calcul des résultats . 8
10 Détermination de la masse volumique apparente de l’échantillon pour essai —
Méthode 3: méthode sous vide avec option d’essorage . 8
10.1 Principe . 8
10.2 Appareillage et matériaux . 8
10.3 Mode opératoire . 9
10.3.1 Détermination de la masse de l’éprouvette sèche (m ) . 9
10.3.2 Trempage de l’échantillon pour essai. 10
10.3.3 Détermination de la masse apparente de l’échantillon pour essai immergé
(m ) et de la masse de l’échantillon pour essai imbibé (m ) . 10
5 3
10.4 Calcul des résultats . 12
10.4.1 Calcul du volume de l’échantillon pour essai (V ) .12
R
10.4.2 Calcul de la masse volumique apparente de l’échantillon pour essai (ρ ) .12
R
10.5 Fidélité et biais.12
10.5.1 Données interlaboratoires .12
10.5.2 Fidélité . 12
10.5.3 Biais . .13
11 Rapport d’essai .13
Bibliographie .14
iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L’attention est attirée sur le fait que certains des éléments du présent document peuvent faire l’objet
de droits de brevet. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié de tels droits
de brevet. Les détails concernant les références aux droits de brevet identifiés lors de l’élaboration du
document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par
l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www.iso.org/iso/fr/avant-propos.html.
Le présent document a été élaboré par le comité technique ISO/TC 33, Matériaux réfractaires.
Cette deuxième édition annule et remplace la première édition (ISO 8840:1987), qui a fait l’objet d’une
révision technique.
Les principales modifications par rapport à l’édition précédente sont les suivantes:
— une nouvelle méthode conforme à l’ISO 5017 a été ajoutée. Elle est identique à la méthode indiquée
dans l’EN 993-18 avec une amélioration suggérée pour éviter le facteur qui a le plus d’influence, à
savoir l’opérateur.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.html.
iv
NORME INTERNATIONALE ISO 8840:2021(F)
Matériaux réfractaires — Détermination de la masse
volumique apparente des matériaux en grains (masse
volumique des grains)
1 Domaine d’application
Le présent document spécifie trois méthodes per mettant de déterminer la masse volumique apparente
des matériaux réfractaires en grains (masse volumique des grains) dont la granulométrie est supérieure
à 2 mm:
— Méthode 1: méthode au mercure sous vide;
— Méthode 2: méthode par arrêt de l’absorption d’eau;
— Méthode 3: méthode sous vide avec option d’essorage conformément à l’ISO 5017.
La méthode 1 est la méthode de référence.
NOTE Selon la nature du matériau soumis à l’essai, les trois méthodes peuvent donner des résultats
différents. Tout énoncé de la valeur d’une masse volumique apparente peut par conséquent s’accompagner d’une
mention de la méthode utilisée ou à utiliser en cas de litige.
La même méthode peut être utilisée pour déterminer le volume de l’échantillon, pour choisir et préparer
l’échantillon, pour cal culer sa masse volumique apparente et pour présenter le rapport d’essai.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 383, Verrerie de laboratoire — Assemblages coniques rodés interchangeables
ISO 385-1, Verrerie de laboratoire — Burettes — Partie 1: Spécifications générales
ISO 5017, Produits réfractaires façonnés denses — Détermination de la masse volumique apparente, de la
porosité ouverte et de la porosité totale
ISO 8656, Produits réfractaires — Échantillonnage des matières premières et des matériaux non façonnés
préparés
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
3.1
masse volumique des grains
masse volumique apparente d’un matériau en grains
rapport de la masse d’une quantité de matériau au volume total de ses grains, y compris le volume de
tous les pores fermés (3.2) à l’intérieur des grains
3.2
pore fermé
pore qui n’est pas pénétré par le liquide dans lequel les grains sont immergés
4 Principe
Mesurage du volume d’une masse donnée de matériau en grains, par déplacement d’un liquide.
5 Échantillonnage
L’échantillonnage doit être effectué conformément à l’ISO 8656 ou à toute autre méthode normalisée
agréée entre les parties intéressées.
6 Préparation, nombre et taille des échantillons
6.1 Préparation des échantillons
Le matériau soumis à essai doit se composer de fragments de grains isolés ou agglomérés d
...
2024-05-22
ISO 8840:2021(frF)
Deuxième édition:
2021-09
ISO/TC 33
Secrétariat: BSI
Matériaux réfractaires — Détermination de la masse volumique
apparente des matériaux en grains (masse volumique des grains)
Refractory materials — Determination of bulk density of granular materials (grain density)
ISO 8840:2021(frF)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2021
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvreoeuvre, aucune
partie de cette publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé,
électronique ou mécanique, y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans
autorisation écrite préalable. Une autorisation peut être demandée à l’ISO à l’adresse ci-après ou au comité membre
de l’ISO dans le pays du demandeur.
ISO copyright office
CP 401 • Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, GenèveGeneva
Tel. Phone: + 41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Website: www.iso.org
Publié en Suisse
ii © ISO 2021 – Tous droits réservés
ii © ISO 2021 – Tous droits réservés
ISO 8840:2021(frF)
Sommaire Page
Avant-propos . vi
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
5 Échantillonnage . 2
6 Préparation, nombre et taille des échantillons . 2
6.1 Préparation des échantillons . 2
6.2 Nombre d’échantillons . 2
6.3 Masse des échantillons pour essai . 2
7 Détermination de la masse d’un échantillon pour essai . 3
8 Détermination du volume d’un échantillon pour essai — Méthode 1: méthode au mercure sous
vide 3
8.1 Principe . 3
8.2 Appareillage . 3
8.3 Détermination de la masse à vide du pycnomètre . 5
8.4 Détermination de la masse du pycnomètre rempli de mercure . 6
8.5 Détermination de la masse du pycnomètre contenant l’échantillon pour essai et le mercure . 6
8.6 Calcul du volume de l’échantillon pour essai . 6
9 Détermination du volume de l’échantillon pour essai — Méthode 2: méthode par arrêt de
l’absorption d’eau . 7
9.1 Appareillage . 7
9.2 Détermination du volume de l’échantillon pour essai . 7
9.3 Calcul des résultats . 8
10 Détermination de la masse volumique apparente de l’échantillon pour essai — Méthode 3:
méthode sous vide avec option d’essorage. 8
10.1 Principe . 8
10.2 Appareillage et matériaux . 8
10.3 Mode opératoire . 10
10.3.1 Détermination de la masse de l’éprouvette sèche (m ) . 10
10.3.2 Trempage de l’échantillon pour essai . 10
10.3.3 Détermination de la masse apparente de l’échantillon pour essai immergé (m ) et de la masse
de l’échantillon pour essai imbibé (m ) . 10
10.4 Calcul des résultats . 12
10.4.1 Calcul du volume de l’échantillon pour essai (V ) . 12
R
10.4.2 Calcul de la masse volumique apparente de l’échantillon pour essai (ρ ) . 12
R
10.5 Fidélité et biais . 12
ISO 8840:2021(frF)
10.5.1 Données interlaboratoires . 12
10.5.2 Fidélité . 13
10.5.3 Biais. 13
11 Rapport d’essai. 13
Bibliographie . 15
Avant-propos iv
1 Domaine d’application 1
2 Références normatives 1
3 Termes et définitions 1
4 Principe 2
5 Échantillonnage 2
6 Préparation, nombre et taille des échantillons 2
6.1 Préparation des échantillons 2
6.2 Nombre d’échantillons 2
6.3 Masse des échantillons pour essai 2
7 Détermination de la masse d’un échantillon pour essai 3
8 Détermination du volume d’un échantillon pour essai — Méthode 1 : méthode au mercure sous
vide 3
8.1 Principe 3
8.2 Appareillage 3
8.3 Détermination de la masse à vide du pycnomètre 4
8.4 Détermination de la masse du pycnomètre rempli de mercure 4
8.5 Détermination de la masse du pycnomètre contenant l’échantillon pour essai et le mercure 4
8.6 Calcul du volume de l’échantillon pour essai 5
9 Détermination du volume de l’échantillon pour essai — Méthode 2 : méthode par arrêt de
l’absorption d’eau 5
9.1 Appareillage 6
9.2 Détermination du volume de l’échantillon pour essai 6
9.3 Calcul des résultats 6
10 Détermination de la masse volumique apparente de l’échantillon pour essai —
Méthode 3 : méthode sous vide avec option d’essorage 6
10.1 Principe 6
10.2 Appareillage et matériaux 7
10.3 Mode opératoire 8
10.3.1 Détermination de la masse de l’éprouvette sèche (m ) 8
10.3.2 Trempage de l’échantillon pour essai 8
10.3.3 Détermination de la masse apparente de l’échantillon pour essai immergé (m ) et de la masse de
l’échantillon pour essai imbibé (m ) 8
iv © ISO 2021 – Tous droits réservés
iv © ISO 2021 – Tous droits réservés
ISO 8840:2021(frF)
10.4 Calcul des résultats 9
10.4.1 Calcul du volume de l’échantillon pour essai (V ) 9
R
10.4.2 Calcul de la masse volumique apparente de l’échantillon pour essai (ρ ) 9
R
10.5 Fidélité et biais 10
10.5.1 Données interlaboratoires 10
10.5.2 Fidélité 10
10.5.3 Biais 10
11 Rapport d’essai 11
Bibliographie 12
ISO 8840:2021(frF)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en
général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit
de faire partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales
et non gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore
étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne la
normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directiveswww.iso.org/directives).
L’attention est attirée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de brevet. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié de tels droits de
brevet. Les détails concernant les références aux droits de brevet identifiés lors de l’élaboration du
document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par
).
l’ISO (voir www.iso.org/brevetswww.iso.org/brevets
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www.iso.org/iso/fr/avant-propos.htmlwww.iso.org/iso/fr/avant-
propos.html.
Le présent document a été élaboré par le comité technique ISO/TC 33, Matériaux réfractaires.
Cette deuxième édition annule et remplace la première édition (ISO 8840:1987), qui a fait l’objet d’une
révision technique.
Les principales modifications par rapport à l’édition précédente sont les suivantes:
— — une nouvelle méthode conforme à l’ISO 5017 a été ajoutée. Elle est identique à la méthode
indiquée dans l’EN 993-18 avec une amélioration suggérée pour éviter le facteur qui a le plus
d’influence, à savoir l’opérateur.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.htmlwww.iso.org/fr/members.html.
vi © ISO 2021 – Tous droits réservés
vi © ISO 2021 – Tous droits réservés
NORME INTERNATIONALE ISO 8840:2021(F)
Matériaux réfractaires — Détermination de la masse volumique
apparente des matériaux en grains (masse volumique des grains)
1 Domaine d’application
Le présent document spécifie trois méthodes permettantper-mettant de déterminer la masse volumique
apparente des matériaux réfractaires en grains (masse volumique des grains) dont la granulométrie est
supérieure à 2 mm:
— — Méthode 1: méthode au mercure sous vide;
— — Méthode 2: méthode par arrêt de l’absorption d’eau;
— — Méthode 3: méthode sous vide avec option d’essorage conformément à l’ISO 5017.
La méthode 1 est la méthode de référence.
NOTE Selon la nature du matériau soumis à l’essai, les trois méthodes peuvent donner des résultats différents.
Tout énoncé de la valeur d’une masse volumique apparente peut par conséquent s’accompagner d’une mention de
la méthode utilisée ou à utiliser en cas de litige.
La même méthode peut être utilisée pour déterminer le volume de l’échantillon, pour choisir et préparer
l’échantillon, pour calculercal-culer sa masse volumique apparente et pour présenter le rapport d’essai.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 383, Verrerie de laborato
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.