ISO 3953:1977

Metallic powders — Determination of tap density

Poudres métalliques — Détermination de la masse volumique après tassement

General Information

• Status: Withdrawn
• Publication Date: 31-Dec-1976
• Withdrawal Date: 31-Dec-1976
• ICS: 77.160 - Powder metallurgy
• Technical Committee: ISO/TC 119 - Powder metallurgy
• Drafting Committee: ISO/TC 119 - Powder metallurgy
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 01-Nov-1985

Relations

• Revised: ISO 3953:1985 - Metallic powders — Determination of tap density
• Effective Date: 15-Apr-2008
• Revised: ISO 3953:1993 - Metallic powders — Determination of tap density
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL STANDARD 3953
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION *METLIYHAPOZIHAR OPïAHR3AUHR IJO CTAHnAPTJ43AUIIU *ORGANISATION INTERNATIONALE DE NORMALISATION
*
Metallic powders - Determination of tap density
Poudres métalliques - Détermination de la masse volumique après tassement
First edition - 1977-01 -15
UDC 621.762 : 669-492.2 : 531.754.2 Ref. No. IS0 3953-1977 (E)
Descriptors : powder metallurgy, metal powder, physical tests, density measurement, bulk density.
3 pages
Price based on

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 member bodies). The work of developing
International Standards is carried out through IS0 technical committees. Every
member body interested in a subject for which a technical committee has been set
up has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated
to the member bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 3953 was developed by Technical Committee
ISO/TC 119, Powder metallurgical materials and products, and was circulated to
the member bodies in October 1975.
It has been approved by the member bodies of the following countries :
Austria Japan Sweden
Canada Mexico Turkey
Czech os1 ova kia Poland
United Kingdom
France
Portugal U.S.A.
Germany Romania
U.S.S.R.
Italy Yugoslavia
Spain
No member body expressed disapproval of the document.
O international Organization for Standardization, 1977
Printed in Switzerland

---------------------- Page: 2 ----------------------
I NTE RNATl ON AL STANDARD IS0 3953-1977 (E)
Metallic powders - Determination of tap density
1 SCOPE AND FIELD OF APPLICATION 4.3 In m th ?e 6.3.1), an apparatus is I d which
permits the tapping of the graduated cylinder against a firm
This International Standard specifies methods for the
base. The tapping shall be such that a densification of the
0
determination of tap density, i.e. the density of a powder
powder can take place without any loosening of its surface
a container under specified
that has been tapped in
layers. The stroke shall be 3 mm and the tapping frequency
conditions.
shall be between 100 and 300 taps per minute. An example
of a tapping apparatus is shown in the figure.
2 PRINCIPLE
4.4 An alternative test method (method 2, see6.3.2). similar
This test consists in tapping a specified amount of powder
to method 1, consists in tapping the cylinder by hand against
in a container, either by means of a tapping apparatus or
a hard rubber slab (about 100 mm x 100 mm x5 mm).
by hand, until no further decrease of the volume of the
powder takes place. The mass of the powder divided by its
5 SAMPLING
volume after the test gives its tap density.
5.1 For the quantities of powder required for each test,
3 SYMBOLS AND DESIGNATIONS
see table 2.
TABLE 1
TABLE 2
Symbol Designation Unit
Cylinder capacity Apparent density Mass of test portion
cm3 gicm3 9
Tap density
~
Mass of the powder
1 O0 >1 100 i- 0.5
Volume of the tapped powder cm3
1 O0 <1 50 ? 0.2
25 >7 1 O0 ? 0.5
25 2 to 7 50 ? 0.2
4 APPARATUS
25 <2 20 i- 0.1
4.1 Balance, of appropriate capacity and accuracy to
satisfy the requirements shown in table 2.
5.2 In general, the powder should be tested in the as-
received condition. In certain instances the powder may be
4.2 Graduated glass cylinder, calibrated to contain
dried. However, if the powder is susceptible to oxidation,
100cm3, the height of the graduated portion being
gas. If
the drying should
...

II
NORME INTERNATIONALE 3953
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .MEXAYHAPOnHAR OPïAHM3AUHR no CTAHAAPTM3AUHH.ORGANISATION INTERNATIONALE DE NORMALISATION
e
Poudres métalliques - Détermination de la masse volumique
après tassement
Metallic powders - Determination of tap density
Première édition - 1977-01 -15
I
U.
-
CDU 621.762 669-492.2 : 531.754.2
Réf. no : IS0 3953-1977 (FI
*
l-
m
Descripteurs : métallurgie des poudres, poudre métallique, essai physique, mesurage de densité, masse volumique apparente.
r?
Lo
m
m
O
52
Prix basé sur 3 pages

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de 1'60). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
et non
correspondant. Les organisations internationales, gouvernementales
gouvernementales, en liaison avec I'ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont
soumis aux comités membres pour approbation, avant leur acceptation comme
Normes internationales par le Conseil de I'ISO.
La Norme internationale IS03953 a été élaborée par le comité technique
ISO/TC 119, Matières premières et produits de la métallurgie des poudres, et a été
soumise aux comités membres en octobre 1975.
Les comités membres des pays suivants l'ont approuvée :
Allemagne Suède
Japon
Autriche Mexique
Tchécoslovaquie
Canada Pologne
Turquie
Portugal U.R.S.S.
Espagne
France Roumanie
U.S.A.
Italie Royaume-Uni
Yougoslavie
Aucun comité membre ne l'a désapprouvée.
O Organisation internationale de normalisation, 1977 O
imprimé en Suisse

---------------------- Page: 2 ----------------------
~~ ~
NORME INTERNATIONALE IS0 3953-1977 (F)
Poudres métalliques - Détermination de la masse volumique
après tassement
1 OBJET ET DOMAINE D'APPLICATION 4.3 Pour la méthode 1 (voir 6.3.1). on utilise un appareil
permettant de frapper le cylindre gradué sur un support
La présente Norme internationale spécifie des méthodes
rigide. La frappe doit se faire dans des conditions telles
pour déterminer la masse volumique après tassement, c'est-
qu'il y ait densification de la poudre sans que les couches
à-dire la masse volumique d'une poudre tassée dans un
supérieures se fluidifient. La hauteur de chute doit être de
@
récipient dans des conditions déterminées.
3 mm et la fréquence de la chute doit être comprise entre
100 et 300 coups par minute. Un exemple d'appareillage
est donné à la figure.
2 PRlNCiPE
Cet essai consiste à tasser une quantité déterminée de
4.4 Une autre méthode d'essai (méthode 2, voir 6.3.2),
poudre dans un récipient soit au moyen d'un appareil, soit
semblable à la première, consiste à frapper le cylindre a la
à la main, jusqu'a ce qu'on n'observe plus de diminution du
main sur une plaque de caoutchouc dur (environ
volume. Le quotient de la masse de la poudre par son
100 x 100 x 5 mm).
volume après essai, représente la masse volumique après
tassement.
5 ÉCHANTILLONNAGE
5.1 Pour les quantités nécessaires a chaque essai, voir
3 SYMBOLES ET DÉSIGNATIONS
tableau 2.
TABLEAU 1
TABLEAU 2
Désignation 1 Unité
~
Contenance Masse volumique Masse de la
I Masse volumique après tassement I gicm3 du cylindre apparente prise d'essai
cm3
Masse de la poudre
Volume de la poudre tassée
>1 100 * 0.5
50 ? 0,2
25 >7 lOO? 0.5
4 APPAREILLAGE
25 2à7 50 ? 0.2
4.1 Balance, d'une capacité et d'une précision répondant
25 <2 20 * 0.1
aux exigences du tableau 2.
5.2 La poudre devrait, en général, être essayée dans les
4.2 Cylindre en verre gradué, pouvant contenir 100 cm3,
la hauteur de la partie graduée étant d'environ 175 mm. Ces conditions de réception. Dans certains cas, elle peut être
graduations doivent être espacées de 1 cm
...