ISO 3927:1977

Metallic powders, excluding powders for hardmetals — Determination of compactibility (compressibility) in uniaxial compression

Poudres métalliques, à l'exclusion des poudres pour métaux-durs — Détermination de la compressibilité sous compression uniaxiale

General Information

• Status: Withdrawn
• Publication Date: 31-Dec-1976
• Withdrawal Date: 31-Dec-1976
• ICS: 77.160 - Powder metallurgy
• Technical Committee: ISO/TC 119 - Powder metallurgy
• Drafting Committee: ISO/TC 119 - Powder metallurgy
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 01-Jun-1985

Relations

• Revised: ISO 3927:1985 - Metallic powders, excluding powders for hardmetals — Determination of compactibility (Compressibility) in uniaxial compression
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL STANDARD 3927
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION *MEXfiYHAPOfiHAII OPiAHMSAUHll Il0 CTAHLIAPTU3ALIHA.ORGANlSATlON INTERNATIONALE DE NORMALISATION
Metallic powders, excluding powders for hardmetals -
Determination of compactibility (eompressibility) in uniaxial
corn p ress i on
Poudres métalliques, à l'exclusion des poudres pour métaux-durs - Détermination de la compressibilité sous
compression uniaxiale
First edition - 1977-01 -15
Ref. No. IS0 3927-1977 (E)
UDC 621.762.4 : 539.58
Descriptors : powder metallurgy, metal powder, tests, compression tests, compressibility.
Price based on 4 pages

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 member bodies). The work of developing
International Standards is carried out through IS0 technical committees. Every
member body interested in a subject for which a technical committee has been set
up has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO. also take part in the work.
Draft International Standards adopted by the technical committees are circulated
to the member bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 3927 was drawn up by Technical Committee
ISO/TC 119, Powder metallurgical materials and products, and was circulated
to the member bodies in October 1975.
It has been approved by the member bodies of the following countries :
Sweden
Austria Italy
Turkey
Brazil Japan
Canada Mexico United Kingdom
U.S.A.
Czechoslovakia Poland
U.S.S.R.
Egypt, Arab Rep. of Portugal
Romania Yugoslavia
France
Spain
Germany
No member body expressed disapproval of the document.
O International Organization for Standardization, 1977 O
Printed in Switzerland

---------------------- Page: 2 ----------------------
~~
IS0 3927-1977 (E)
INTERNATIONAL STANDARD
Metallic powders, excluding powders for hardmetals -
Determination of compactibility (compressibility) in uniaxial
compression
1 SCOPE AND FIELD OF APPLICATION 4.1.2 The rectangular die should be capable of making
compacts 30 mm x 12 mm and of thickness 5 to 7 mm. A
This International Standard specifies methods to measure
recommended tool design is shown in figure 2.
the extent to which a metallic powder is compacted when
subjected to uniaxial compressive loading in a confining
4.2 Press, capable of applying forces up to about 500 kN
die under specified conditions.
with a minimum accuracy of +: 2 % and adjustable to permit
an even increase of the force at a rate not higher than
This test method is not applicable to powders for hard-
50 kN/s.
metals.
4.3 Balance, capable of weighing at least 1OOg to an
accuracy off 0,Ol g.
2 PRINCIPLE
The test consists in compacting a powder uniaxially in a
4.4 Micrometer or other suitable measuring device for
confining die by double-action pressing. Samples of the
measuring the dimensions of the compacts to an accuracy
powder may be pressed either at a single specified pressure
of f 0,Ol mm.
or at a series of specified pressures. After ejection from the
die, the density of the compacts is determined.
The density obtained in the former case represents the
5 SAMPLING
compactibility of the powder at the specified pressure.
The quantity of the test sample shall be chosen to give the
The densities obtained in the latter case can be utilized
required number of test pieces (see clause 7) with the
for drawing the compactibility (compressibility) curve of
dimensions specified in 4.1. If necessary, preliminary tests
the powder, i.e. a plot of the density as a function of the
should be made in order to establish the quantity of
compacting pressure.
powder which is needed for fulfilling this requirement.
3 SYMBOLS AND DESIGNATIONS
6 PROCEDURE
Symbol Designation Unit
6.1 Cleaning of the die and punches
Compacti bility
Wipe the die cavity and the punches with soft and clean
Mass of the compact
paper towelling soaked with an appropriate solvent such as
acetone. Allow the solvent to evaporate.
Volume of the comoact cm3
6.2 Powder testing conditions
If the compactibility is measure
...

I
NORME INTERNATIONALE 3927
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION *MEEnYHAPOWAR OPiAHH3AUHR i70 CTAH~APTH3AUAA.ORGANlSATION INTERNATIONALE DE NORMALISATION
0
Poudres métalliques, à l'exclusion des poudres pour métaux-
durs - Détermination de la compressibilité sous compression
uniaxiale
Metallic powders, excluding powders for hardmetals - Determination of compactibility (compressibility) in
uniaxiai compression
Première édition - 1977-01 -15
1
U.
-
CDU 621.762.4 : 539.58 Réf. no : IS0 3927-1977 (FI
r-
r-
q
Descripteurs : métallurgie des poudres, poudre métallique, essai, essai de compression, compressibilité.
r-
w
a>
(?
8
Prix basé sur 4 pages

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont
soumis aux comités membres pour approbation, avant leur acceptation comme
Normes internationales par le Conseil de I'ISO.
La Norme internationale IS0 3927 a été établie par le comité technique
ISOTrC 119, Matières premières et produits de la métallurgie des poudres, et a été
soumise aux comités membres en octobre 1975.
Elle a été approuvée par les comités membres des pays suivants :
Allemagne Italie Suède
Autriche Japon Tchécoslovaquie
Brésil Mexique Turquie
Canada Pologne U.R.S.S.
Egypte, Rép. arabe d' Portugal U.S.A.
Roumanie Yougoslavie
Espagne
France Royaume-Uni
Aucun comité membre n'a désapprouvé le document.
O Organisation internationale de normalisation, 1977 O
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORME INTERNATIONALE IS0 3927-1977 (F)
Poudres métalliques, à l‘exclusion des poudres pour métaux-
durs - Détermination de la compressibilité sous compression
uniax iale
1 OBJET ET DOMAINE D‘APPLICATION 4.1.2 La matrice rectangulaire doit permettre de réaliser
des comprimés de 30 mm X 12 mm et d‘une épaisseur de
La présente Norme internationale spécifie des méthodes
5 à 7 mm. Un outillage recommandé est donné à la figure 2.
pour mesurer l’aptitude d‘une poudre métallique à être
comprimée Jorsqu’elle est soumise dans une matrice à une
4.2 Presse, pouvant appliquer des forces jusqu’à environ
charge de compression uniaxiale dans des conditions
500 kN, avec une précision minimale de i: 2%, et réglable
déterminées.
afin de permettre un accroissement uniforme de la force
n‘excédant pas 50 kN/s.
Cette méthode d’essai ne s’applique pas aux poudres pour
métaux-durs.
4.3 Balance, permettant de peser au moins 1OOg à
k 0,Ol g près.
2 PRINCIPE
4.4 Micromètre, ou tout autre appareil permettant de
L’essai consiste à comprimer une poudre par compression
mesurer les dimensions des comprimés à * 0,Ol mm près.
uniaxiale bilatérale dans une matrice. Les échantillons de
poudre peuvent être comprimés soit à une seule pression
spécifiée, soit à une série de pressions déterminées. Après
5 ÉCHANTILLONNAGE
éjection de la matrice, on détermine la masse volumique
des comprimés.
La quantité d’échantillon doit être choisie en fonction du
nombre requis d’éprouvettes (voir chapitre 7) ayant les
La masse volumique obtenue dans le premier cas représente
dimensions spécifiées en 4.1. Si nécessaire, on effectuera
la compressibilité de la poudre à une pression donnée. Les
des essais préliminaires afin de définir la quantité de poudre
masses volumiques obtenues dans le second cas peuvent
nécessaire pour remplir ces conditions.
servir à tracer la courbe de compressibilité de la poudre,
en portant la masse volumique en fonction de la pression
de compression. 6 MODE OPÉRATOIRE
6.1 Nettoyage de la matrice et des poinçons
3 SYMBOLES ET DÉSIGNATIONS
Nettoyer la matrice et les poinçons avec du papier joseph
propre imbibé d‘un solvant approprié tel que l’acétone.
Symbole Désignation Unité Laisser le solvant s’évaporer.
Compressibilité
6.2 Conditions d’essai de la poudre
Masse du comprimé
Volume du comprimé cm3
Les poudres ne contenant pas de lubrifiant peuvent
6.2.1
être essayées :
Si la compressibilité est mesurée à une seule pression, par
a) dans une matrice non lubrifiée (attention : un
exemple 400 N/mm*, le symbole s‘écrira P,,+,~~).
grippage ou u
...