ISO 13947:2024

Metallic powders — Test method for the determination of non-metallic inclusions in metal powders using a powder-forged specimen

This document specifies a metallographic test method for determining the non-metallic inclusion level in metal powders using a powder-forged specimen. This test method is applicable to repress powder-forged test specimens in which there has been minimal lateral flow ( This test method can also be applied to determine the non-metallic inclusion content of powder-forged steel parts. However, in parts where there has been a significant amount of material flow, the near-neighbour separation distance needs to be changed, or the inclusion sizes agreed between the parties need to be adjusted. This test method is not applicable for determining the non-metallic inclusion level of parts that have been forged such that the core region contains porosity. At the magnification used for this test method, residual porosity is hard to distinguish from inclusions. Too much residual porosity makes a meaningful assessment of the inclusion population impossible. This test method can also be applied to materials that contain manganese sulphide (admixed or prealloyed), provided the near-neighbour separation distance is changed from 30 µm to 15 µm.

Poudres métalliques — Méthode d’essai permettant de déterminer la teneur en inclusions non métalliques dans les poudres métalliques à l’aide d’une éprouvette frittée-forgée

Le présent document spécifie une méthode d’essai métallographique permettant de déterminer la teneur en inclusions non métalliques dans les poudres métalliques à l’aide d’une éprouvette frittée-forgée. La méthode d’essai est applicable aux éprouvettes frittées-forgées par recompression dans lesquelles s’est produit un écoulement latéral minime ( Cette méthode d’essai peut également être utilisée pour déterminer la teneur en inclusions non métalliques dans les pièces d’acier frittées-forgées. Toutefois, pour les pièces présentant un écoulement de matériau significatif, soit la distance de séparation du proche voisin requiert une modification soit les tailles des inclusions convenues entre les parties requièrent un ajustement. Cette méthode d’essai ne permet pas de déterminer la teneur en inclusions non métalliques des pièces frittées-forgées de telle sorte que leur cœur présente de la porosité. Avec le grossissement utilisé dans cette méthode d’essai, la porosité résiduelle est difficile à distinguer des inclusions. Trop de porosité résiduelle rend impossible l’évaluation significative de la population d’inclusions. Cette méthode d’essai peut aussi s’appliquer aux matériaux contenant du sulfure de manganèse (comme adjuvant ou en préalliage), sous réserve que la distance de séparation du proche voisin soit réduite de 30 µm à 15 µm.

General Information

• Status: Published
• Publication Date: 24-Nov-2024
• ICS: 77.160 - Powder metallurgy
• Technical Committee: ISO/TC 119/SC 2 - Sampling and testing methods for powders (including powders for hardmetals)
• Drafting Committee: ISO/TC 119/SC 2 - Sampling and testing methods for powders (including powders for hardmetals)
• Current Stage: 6060 - International Standard published
• Start Date: 25-Nov-2024
• Due Date: 25-Nov-2024
• Completion Date: 25-Nov-2024

Relations

• Revises: ISO 13947:2011 - Metallic powders — Test method for the determination of non-metallic inclusions in metal powders using a powder-forged specimen
• Effective Date: 22-Oct-2022

Standards Content (Sample)

International
Standard
ISO 13947
Third edition
Metallic powders — Test method for
2024-11
the determination of non-metallic
inclusions in metal powders using a
powder-forged specimen
Poudres métalliques — Méthode d’essai permettant de
déterminer la teneur en inclusions non métalliques dans les
poudres métalliques à l’aide d’une éprouvette frittée-forgée
Reference number
© ISO 2024
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Significance and use . 3
6 Apparatus . 3
6.1 Metallographic microscope .3
7 Test piece . 3
8 Procedure . 4
8.1 Preparation of specimens .4
8.2 Measurement of non-metallic inclusion content .4
9 Test report . 4
10 Precision and bias . 5
Bibliography . 6

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 119, Powder metallurgy, Subcommittee SC 2,
Sampling and testing methods for powders (including powders for hardmetals), in collaboration with the
European Committee for Standardization (CEN) Technical Board, in accordance with the Agreement on
technical cooperation between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 13947:2011), which has been technically
revised.
The main changes are as follows:
— added option of hardening by quenching directly after forging.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
International Standard ISO 13947:2024(en)
Metallic powders — Test method for the determination of
non-metallic inclusions in metal powders using a powder-
forged specimen
WARNING — This document does not purport to address all of the safety problems, if any, associated
with its use. It is the responsibility of the user of this document to establish appropriate safety and
health practices and to determine the applicability of regulatory limitations prior to use.
1 Scope
This document specifies a metallographic test method for determining the non-metallic inclusion level in
metal powders using a powder-forged specimen. This test method is applicable to repress powder-forged
test specimens in which there has been minimal lateral flow (<1 %). The core region of the powder-forged
test specimen must not contain porosity detectable at 100x magnification.
This test method can also be applied to determine the non-metallic inclusion content of powder-forged steel
parts. However, in parts where there has been a significant amount of material flow, the near-neighbour
separation distance needs to be changed, or the inclusion sizes agreed between the parties need to be
adjusted.
This test method is not applicable for determining the non-metallic inclusion level of parts that have been
forged such that the core region contains porosity. At the magnification used for this test method, residual
porosity is hard to distinguish from inclusions. Too much residual porosity makes a meaningful assessment
of the inclusion population impossible.
This test method can also be applied to materials that contain manganese sulphide (admixed or prealloyed),
provided the near-neighbour separation distance is changed from 30 µm to 15 µm.
2 Normative references
The following documents are referred to in the text in such a
...

Norme
internationale
ISO 13947
Troisième édition
Poudres métalliques — Méthode
2024-11
d’essai permettant de déterminer
la teneur en inclusions non
métalliques dans les poudres
métalliques à l’aide d’une
éprouvette frittée-forgée
Metallic powders — Test method for the determination of non-
metallic inclusions in metal powders using a powder-forged
specimen
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2024
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 2
5 Signification et utilisation . 3
6 Appareillage . 3
6.1 Microscopie métallographique .3
7 Prise d’essai . 4
8 Mode opératoire . 4
8.1 Préparation des éprouvettes .4
8.2 Mesurage de la teneur en inclusions non métalliques .4
9 Rapport d’essai . 5
10 Précision et biais . . 5
Bibliographie . 6

iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
https://www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de brevet.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir le lien suivant : www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 119, Métallurgie des poudres,
sous-comité SC 2, Échantillonnage et méthodes d’essais des poudres (y compris les poudres pour
métaux-durs) en collaboration avec le comité technique du Comité européen de normalisation
(CEN) conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 13947:2011), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes :
— ajout de la possibilité de solidification par refroidissement directement après frittage-forgeage
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/members.html.

iv
Norme internationale ISO 13947:2024(fr)
Poudres métalliques — Méthode d’essai permettant de
déterminer la teneur en inclusions non métalliques dans les
poudres métalliques à l’aide d’une éprouvette frittée-forgée
AVERTISSEMENT — Le présent document n’a pas pour but de traiter tous les problèmes de sécurité
qui sont, le cas échéant, liés à son utilisation. Il incombe à l’utilisateur du présent document d’établir,
avant de l’utiliser, des pratiques d’hygiène et de sécurité appropriées et de déterminer l’applicabilité
des restrictions réglementaires.
1 Domaine d’application
Le présent document spécifie une méthode d’essai métallographique permettant de déterminer la teneur en
inclusions non métalliques dans les poudres métalliques à l’aide d’une éprouvette frittée-forgée. La méthode
d’essai est applicable aux éprouvettes frittées-forgées par recompression dans lesquelles s’est produit un
écoulement latéral minime (< 1 %). Le cœur de l’éprouvette frittée-forgée ne doit pas présenter de porosité
détectable à un grossissement de 100 X.
Cette méthode d’essai peut également être utilisée pour déterminer la teneur en inclusions non métalliques
dans les pièces d’acier frittées-forgées. Toutefois, pour les pièces présentant un écoulement de matériau
significatif, soit la distance de séparation du proche voisin requiert une modification soit les tailles des
inclusions convenues entre les parties requièrent un ajustement.
Cette méthode d’essai ne permet pas de déterminer la teneur en inclusions non métalliques des pièces
frittées-forgées de telle sorte que leur cœur présente de la porosité. Avec le grossissement utilisé dans cette
méthode d’essai, la porosité résiduelle est difficile à distinguer des inclusions. Trop de porosité résiduelle
rend impossible l’évaluation significative de la population d’inclusions.
Cette méthode d’essai peut aussi s’appliquer aux matériaux contenant du sulfure de manganèse (comme
adjuvant ou en préalliage), sous réserve que la distance de séparation du proche voisin soit réduite de 30 µm
à 15 µm.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendement
...