SIST EN 1562:2012
(Main)Founding - Malleable cast irons
Founding - Malleable cast irons
This European Standard specifies requirements for malleable cast iron used in the manufacture of castings. This standard specifies two groups of material, namely whiteheart malleable cast iron and blackheart malleable cast iron. Each group is represented by several grades of material. Classification is given on the basis of mechanical properties determined on separately cast test pieces. This standard specifies 0,2 % proof stress values when required by the purchaser. This standard does not cover chemical composition requirements.
Gießereiwesen - Temperguss
Diese Europäische Norm legt die Sorten für und die zugehörigen Anforderungen an Temperguss fest.
Diese Europäische Norm legt, basierend auf den an Gussproben gemessenen mechanischen Eigenschaften, fünf Sorten von entkohlend geglühten Temperguss und neun Sorten von nichtentkohlend geglühten Temperguss fest.
Diese Europäische Norm legt Werte für die Brinellhärte fest, die nur bestimmt werden, wenn diese Werte vom Käufer verlangt werden.
Diese Europäische Norm enthält nicht die Technischen Lieferbedingungen für Temperguss. Es sollte auf EN 1559 1 [3] und EN 1559 3 [4] Bezug genommen werden.
Diese Europäische Norm enthält keine Angaben über die chemische Zusammensetzung mit Ausnahme von Phosphor (siehe Abschnitt 6).
Die Temperguss-Sorte EN-GJMB-300-6 (5.4100) darf für keinerlei Druckgeräteanwendungen verwendet werden, auch nicht für z. B. Druckgeräteanwendungen die nicht unter die Druckgeräte-Richtlinie 97/23/EG, fallen.
Fonderie - Fonte malléable
La présente Norme européenne définit les nuances et les exigences correspondantes relatives aux fontes malléables.
La présente Norme européenne spécifie cinq nuances de fonte malléable à cœur blanc et neuf nuances de fonte malléable à cœur noir, en se basant sur leurs propriétés mécaniques mesurées sur des échantillons coulés (qui sont les éprouvettes).
La présente Norme européenne spécifie les valeurs de dureté Brinell, déterminées uniquement lorsqu'elles sont demandées par l'acheteur.
Cette Norme européenne ne couvre pas les conditions techniques de fourniture de pièces moulées en fonte malléable. Il convient de se référer à l’EN 1559-1 [3] et l’EN 1559-3 [4].
La présente Norme européenne ne couvre pas les exigences en matière de composition chimique, sauf pour le phosphore (voir l’Article 6).
La fonte malléable de nuance EN-GJMB-300-6 (5.4100) ne doit être utilisée pour aucune application sous pression, c’est-à-dire aussi les applications sous pression non couvertes par la Directive Equipements sous Pression 97/23/EC.
Livarstvo - Temprana litina
Ta evropski standard določa razrede in ustrezne zahteve za temprano litino. Ta evropski standard določa pet razredov bele temprane litine in devet razredov črne temprane litine na podlagi mehanskih lastnosti, izmerjenih na litih vzorcih (ki so preskusni kosi). Ta evropski standard določa vrednosti trdote po Brinellu, ki se izmerijo le, kadar te vrednosti zahteva kupec.
General Information
Relations
Standards Content (Sample)
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Livarstvo - Temprana litinaGießereiwesen - TempergussFonderie - Fonte malléableFounding - Malleable cast irons77.140.80Železni in jekleni ulitkiIron and steel castingsICS:Ta slovenski standard je istoveten z:EN 1562:2012SIST EN 1562:2012en,fr,de01-maj-2012SIST EN 1562:2012SLOVENSKI
STANDARDSIST EN 1562:1998/A1:2006SIST EN 1562:19981DGRPHãþD
SIST EN 1562:2012
EUROPEAN STANDARD NORME EUROPÉENNE EUROPÄISCHE NORM
EN 1562
March 2012 ICS 77.080.10 Supersedes EN 1562:1997English Version
Founding - Malleable cast irons
Fonderie - Fontes malléables
Gießereiwesen - Temperguss This European Standard was approved by CEN on 14 January 2012.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre:
Avenue Marnix 17,
B-1000 Brussels © 2012 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 1562:2012: ESIST EN 1562:2012
EN 1562:2012 (E) 2 Contents Page Foreword .3Introduction .41Scope .52Normative references .53Terms and definitions .54Designation .65Order information .66Manufacture .67Requirements .77.1General .77.2Tensile strength and elongation .77.30,2 % Proof strength .77.4Brinell hardness .77.5Impact energy .78Samples . 108.1General . 108.2Cast samples . 109Test methods . 129.1Tensile test . 129.20,2 % proof strength . 129.3Brinell hardness . 129.4Impact test . 1310Retests . 1310.1Need for retests. 1310.2Test validity . 1310.3Non-conforming test results . 1410.4Heat treatment of samples and castings . 1411Inspection documentation . 14Annex A (informative)
Comparison of malleable cast iron material designations according EN 1560 and ISO/TR 15931 [1], [6] . 15Annex B (informative)
Un-notched impact test . 16Annex C (Informative)
Significant technical changes between this European standard and the previous edition . 17Annex ZA (informative)
Relationship between this European Standard and the Essential Requirements of EU Directive 97/23/EC . 18Bibliography . 19SIST EN 1562:2012
EN 1562:2012 (E) 3 Foreword This document (EN 1562:2012) has been prepared by Technical Committee CEN/TC 190 “Foundry technology”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2012, and conflicting national standards shall be withdrawn at the latest by September 2012. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 1562:1997. This document has been prepared under a mandate given to CEN by the European Commission and the European Free Trade Association, and supports essential requirements of EU Directive(s). For relationship with EU Directive(s), see informative Annex ZA, which is an integral part of this document. Within its programme of work, Technical Committee CEN/TC 190 requested CEN/TC 190/WG 6 “Malleable cast iron” to revise EN 1562:1997. Annex C provides details of significant technical changes between this European Standard and the previous edition. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom.
SIST EN 1562:2012
EN 1562:2012 (E) 4 Introduction This European Standard classifies malleable cast irons into two groups. The first group is concerned with decarburized irons referred to as whiteheart malleable cast iron. The second group is non-decarburized irons referred to as blackheart malleable cast iron. Both groups, except completely decarburized whiteheart malleable cast iron, contain free carbon as graphite, called temper carbon. Both groups have grades with structures that can range from ferrite to pearlite and/or other transformation products of austenite. Materials are designated in terms of tensile strength and percentage elongation. Weldablility is an important property of malleable cast irons. Malleable cast irons have good impact resistance and ductility at low temperatures. In this standard, a new designation system by number, as established in EN 1560 [1], is given. NOTE This designation system by number is based on the principles and the structure as set out in EN 10027-2 [2] and so corresponds with the European numbering system for steel and other materials. Some malleable cast iron grades can be used for pressure equipment. The permitted material grades of malleable cast iron for pressure applications and the conditions for their use are given in specific product or application standards. For the design of pressure equipment, specific design rules apply. Annex ZA gives information relating to the conformance of permitted malleable cast iron grades to the Pressure Equipment Directive 97/23/EC. SIST EN 1562:2012
EN 1562:2012 (E) 5 1 Scope This European Standard defines grades and the corresponding requirements for malleable cast irons. This European standard specifies five grades of whiteheart malleable cast iron and nine grades of blackheart malleable cast iron, based on mechanical properties measured on cast samples (which are test pieces). This European Standard specifies Brinell hardness values determined only when these values are requested by the purchaser. This European Standard does not cover technical delivery conditions for malleable cast iron castings. Reference should be made to EN 1559-1 [3] and EN 1559-3 [4]. This European Standard does not cover chemical composition, except phosphorous (see Clause 6). Grade EN-GJMB-300-6 (5.4100) malleable cast iron shall not be used for any pressure application, e. g. also pressure applications not covered by the Pressure Equipment Directive 97/23/EC. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 764-5:2002, Pressure equipment — Part 5: Compliance and inspection — Documentation of materials EN 10204:2004, Metallic products — Types of inspection documents EN ISO 148-1:2010, Metallic materials — Charpy pendulum impact test — Part 1: Test method
(ISO 148-1:2009) EN ISO 6506-1, Metallic materials — Brinell hardness test — Part 1: Test method (ISO 6506-1) EN ISO 6892-1:2009, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
(ISO 6892-1:2009) 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 malleable cast iron cast material, mainly iron and carbon based, which solidifies in the as-cast condition with a graphite-free (white) structure and achieves its final properties after a heat treatment 3.2 whiteheart malleable cast iron cast material, mainly iron and carbon based, which is cast white and then given a heat treatment in a decarburizing atmosphere to produce a material which is partially or entirely decarburized. Any remaining graphite is in the form of temper carbon 3.3 blackheart malleable cast iron cast material, mainly iron and carbon based, which is cast white and then given a non-decarburizing heat treatment, to produce a material in which all graphite is in the form of temper carbon SIST EN 1562:2012
EN 1562:2012 (E) 6 3.4 primary graphite graphite which precipitates in the flake form during solidification Note 1 to entry: Primary graphite is more correctly referred to as eutectic graphite. 3.5 cast sample quantity of material cast to represent the cast material, including separately cast sample and side-by-side cast sample 3.6 separately cast sample sample cast in a separate sand mould under representative manufacturing conditions and material grade 3.7 side-by-side cast sample sample cast in the mould alongside the casting, with a joint running system 3.8 relevant wall thickness wall thickness representative of the casting, defined for the determination of the size of the cast samples to which the mechanical properties apply 4 Designation The material shall be designated either by symbol or by number as given in Table 1 or Table 2. NOTE Comparison of EN 1562 grade designations to the grades from ISO 5922:2005 [5], is given in Annex A.
5 Order information The following information shall be supplied by the purchaser: a) the number of this European Standard; b) the designation of the material; c) the relevant wall thickness of the casting; d) any special requirements. All requirements shall be agreed between the manufacturer and the purchaser by the time of acceptance of the order e.g. technical delivery conditions according to EN 1559-1 and EN 1559-3. 6 Manufacture The method of manufacture of malleable cast iron as well as its chemical composition and heat treatment shall be left to the discretion of the manufacturer, who shall ensure compliance with the property requirements given in this European Standard for the material ordered. NOTE To produce structures such as ferrite, pearlite or other transformation products of austenite, both material types (groups) depend upon either the malleablising heat treatment or the subsequent additional heat treatment and/or additions of alloying elements. For castings intended to be given additional treatment (such as galvanizing) and/or in the case of castings for use at low temperatures to optimize the impact energy of the material, the phosphorous content should not exceed 0,10 %. SIST EN 1562:2012
EN 1562:2012 (E) 7 For malleable cast iron materials to be used in special applications, the chemical composition and any special heat treatment may be the subject of an agreement between the manufacturer and the purchaser by the time of acceptance of the order. 7 Requirements 7.1 General The property values apply to malleable cast irons cast in sand moulds or moulds of comparable thermal behaviour. Subject to amendments to be agreed upon in the order, they can apply to castings obtained by alternative methods, when agreed between the manufacturer and purchaser by the time of acceptance of the order. The material designation is based on the minimum mechanical properties obtained in cast samples with a diameter of 12 mm. Mechanical properties are wall thickness dependent as shown in Tables 1, 2 and 3. 7.2 Tensile strength and elongation When tested in accordance with 9.1, the values of tensile strength and percentage elongation after fracture (hereafter referred to as elongation) shall be in accordance with the requirements specified in Tables 1, 2 and 3. 7.3 0,2 % Proof strength When requested by the purchaser and agreed at the time of acceptance of the order, 0,2 % proof strength shall be determined in accordance with 9.2 and the values shall be in accordance with the requirements specified in Tables 1, 2 and 3. 7.4 Brinell hardness Brinell hardness and its range values shall only be specified when agreed between the manufacturer and the purchaser by the time of acceptance of the order. Guidance values for Brinell hardness are listed in Tables 1, 2 and 3. The method of testing and sampling shall be agreed in accordance with the method specified in 9.3.
7.5 Impact energy The minimum impact energy values measured on V-notched test pieces machined from cast samples given in Table 3 at room temperature, if applicable, shall only be determined if specified by the purchaser by the time of acceptance of the order. Impact energy testing is normally requested for EN-GJMB-350-10 only. The method of testing shall be in accordance with 9.4. NOTE If the purchaser requires impact testing to be performed on whiteheart malleable cast iron or other grades of blackheart malleable cast irons, then the Charpy un-notched test should be used (see informative Annex B).
SIST EN 1562:2012
EN 1562:2012 (E) 8 Table 1 — Mechanical properties of whiteheart malleable cast irons Material designation Relevant wall thickness Nominal diameter of test
piece
Tensile strength Elongation 0,2 % proof strength Brinell hardness(for informationonly) t d Rm A3,4 Rp0,2 mm mm MPa % MPa HBW Symbol Number
min. min. min. max.
EN-GJMW-350-4 5.4200
230 t ≤ 3
6 270 10 — a 3 < t ≤ 5
9 310
5 — 5 < t ≤ 7 12 350
4 — t > 7 15 360
3 —
EN-GJMW-360-12b 5.4201
200 t ≤ 3
6 280 16 — a 3 < t ≤ 5
9 320 15 170 5 < t ≤ 7 12 360 12 190 t > 7 15 370
7 200
EN-GJMW-400-5 5.4202
220 t ≤ 3
6 300 12 — a 3 < t ≤ 5
9 360
8 200 5 < t ≤ 7 12 400
5 220 t >
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.