SIST ISO 4386-3:2020
(Main)Plain bearings - Metallic multilayer plain bearings - Part 3: Non-destructive penetrant testing
Plain bearings - Metallic multilayer plain bearings - Part 3: Non-destructive penetrant testing
This document specifies a non‑destructive penetrant testing for determining bond defects and discontinuities in the sliding surface of the bearing.
The penetration method is used to detect
a) bond defects in the transitional area between the bearing backing/bearing material on the end faces and joint faces of multilayer plain bearings which cannot be detected by the ultrasonic testing method specified in ISO 4386‑1, and
b) discontinuities in the sliding surface of the bearing.
The penetration method is applicable, in principle, to finished multilayer plain bearings.
The bond test is usually carried out on cast multilayer plain bearings, with a backing consisting of steel, cast steel or cast bronze. It can also be used as a non-production method to aid detection of manufacturing process defects with other bearing material types. Bearing backings which cannot be tin-plated, or only with difficulty, such as perlitic cast iron, rust-resistant steel and cast aluminium, cannot be tested since no bond is possible between the bearing material and bearing backing.
Paliers lisses - Paliers lisses métalliques multicouches - Partie 3: Contrôle non destructif par ressuage
Drsni ležaji - Večslojni kovinski ležaji - 3. del: Preskušanje s penetracijo brez porušitve
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
SIST ISO 4386-3:2020
01-september-2020
Drsni ležaji - Večslojni kovinski ležaji - 3. del: Preskušanje s penetracijo brez
porušitve
Plain bearings - Metallic multilayer plain bearings - Part 3: Non-destructive penetrant
testing
Paliers lisses - Paliers lisses métalliques multicouches - Partie 3: Contrôle non destructif
par ressuage
Ta slovenski standard je istoveten z: ISO 4386-3:2018
ICS:
21.100.10 Drsni ležaji Plain bearings
SIST ISO 4386-3:2020 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST ISO 4386-3:2020
---------------------- Page: 2 ----------------------
SIST ISO 4386-3:2020
INTERNATIONAL ISO
STANDARD 4386-3
Second edition
2018-07
Plain bearings — Metallic multilayer
plain bearings —
Part 3:
Non-destructive penetrant testing
Paliers lisses — Paliers lisses métalliques multicouches —
Partie 3: Contrôle non destructif par ressuage
Reference number
ISO 4386-3:2018(E)
©
ISO 2018
---------------------- Page: 3 ----------------------
SIST ISO 4386-3:2020
ISO 4386-3:2018(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2018
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2018 – All rights reserved
---------------------- Page: 4 ----------------------
SIST ISO 4386-3:2020
ISO 4386-3:2018(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Safety precautions . 1
5 Preparation of test surface . 2
5.1 General . 2
5.2 Mechanical pre-cleaning . 2
5.3 Chemical pre-cleaning . 2
5.4 Drying . 2
6 Application of penetrant . 2
7 Removal of excess penetrant. 2
8 Application of the developer . 3
8.1 General . 3
8.2 Restriction . 3
9 Inspection . 3
9.1 Bond defects . 3
9.2 Sliding surface . 3
10 Subsequent cleaning . 3
11 Test report . 3
Annex A (normative) Designation classes and acceptance criteria . 5
© ISO 2018 – All rights reserved iii
---------------------- Page: 5 ----------------------
SIST ISO 4386-3:2020
ISO 4386-3:2018(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 123, Plain bearings, Subcommittee SC 2,
Materials and lubricants, their properties, characteristics, test methods and testing conditions.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
This second edition cancels and replaces the first edition (ISO 4386-3:1992), which has been technically
revised. The main changes compared to the previous edition are as follows:
— The Scope has been changed.
— Normative references have been updated.
— A new Clause 3 Terms and definitions has been added.
— The document has been restructured.
— All clauses have been technically revised.
— The figures in Annex A have been updated.
— The Bibliography has been deleted.
A list of all the parts in the ISO 4386 series can be found on the ISO website.
iv © ISO 2018 – All rights reserved
---------------------- Page: 6 ----------------------
SIST ISO 4386-3:2020
INTERNATIONAL STANDARD ISO 4386-3:2018(E)
Plain bearings — Metallic multilayer plain bearings —
Part 3:
Non-destructive penetrant testing
1 Scope
This document specifies a non-destructive penetrant testing for determining bond defects and
discontinuities in the sliding surface of the bearing.
The penetration method is used to detect
a) bond defects in the transitional area between the bearing backing/bearing material on the end
faces and joint faces of multilayer plain bearings which cannot be detected by the ultrasonic testing
method specified in ISO 4386-1, and
b) discontinuities in the sliding surface of the bearing.
The penetration method is applicable, in principle, to finished multilayer plain bearings.
The bond test is usually carried out on cast multilayer plain bearings, with a backing consis
...
INTERNATIONAL ISO
STANDARD 4386-3
Second edition
2018-07
Plain bearings — Metallic multilayer
plain bearings —
Part 3:
Non-destructive penetrant testing
Paliers lisses — Paliers lisses métalliques multicouches —
Partie 3: Contrôle non destructif par ressuage
Reference number
ISO 4386-3:2018(E)
©
ISO 2018
---------------------- Page: 1 ----------------------
ISO 4386-3:2018(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2018
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2018 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 4386-3:2018(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Safety precautions . 1
5 Preparation of test surface . 2
5.1 General . 2
5.2 Mechanical pre-cleaning . 2
5.3 Chemical pre-cleaning . 2
5.4 Drying . 2
6 Application of penetrant . 2
7 Removal of excess penetrant. 2
8 Application of the developer . 3
8.1 General . 3
8.2 Restriction . 3
9 Inspection . 3
9.1 Bond defects . 3
9.2 Sliding surface . 3
10 Subsequent cleaning . 3
11 Test report . 3
Annex A (normative) Designation classes and acceptance criteria . 5
© ISO 2018 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 4386-3:2018(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 123, Plain bearings, Subcommittee SC 2,
Materials and lubricants, their properties, characteristics, test methods and testing conditions.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
This second edition cancels and replaces the first edition (ISO 4386-3:1992), which has been technically
revised. The main changes compared to the previous edition are as follows:
— The Scope has been changed.
— Normative references have been updated.
— A new Clause 3 Terms and definitions has been added.
— The document has been restructured.
— All clauses have been technically revised.
— The figures in Annex A have been updated.
— The Bibliography has been deleted.
A list of all the parts in the ISO 4386 series can be found on the ISO website.
iv © ISO 2018 – All rights reserved
---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 4386-3:2018(E)
Plain bearings — Metallic multilayer plain bearings —
Part 3:
Non-destructive penetrant testing
1 Scope
This document specifies a non-destructive penetrant testing for determining bond defects and
discontinuities in the sliding surface of the bearing.
The penetration method is used to detect
a) bond defects in the transitional area between the bearing backing/bearing material on the end
faces and joint faces of multilayer plain bearings which cannot be detected by the ultrasonic testing
method specified in ISO 4386-1, and
b) discontinuities in the sliding surface of the bearing.
The penetration method is applicable, in principle, to finished multilayer plain bearings.
The bond test is usually carried out on cast multilayer plain bearings, with a backing consisting
of steel, cast steel or cast bronze. It can also be used as a non-production method to aid detection of
manufacturing process defects with other bearing material types. Bearing backings which cannot be
tin-plated, or only with difficulty, such as perlitic cast iron, rust-resistant steel and cast aluminium,
cannot be tested since no bond is possible between the bearing material and bea
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.