Standard Specification for Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service

ABSTRACT
This specification covers carbon steel castings for valves, flanges, fittings, or other pressure-containing parts for high-temperature service and of quality suitable for assembly with other castings or wrought-steel parts by fusion welding. Covered here are three grades of carbon steel (Grades WCA, WCB, and WCC), the selection of which shall depend on the design and service conditions, mechanical properties, and the high temperature characteristics. Castings shall be heat treated and furnished, as appropriate to their design and chemical composition, in the annealed, or normalized, or normalized and tempered conditions after they have been allowed to cool below the transformation range. Furnace temperatures for heat treating shall be effectively controlled by pyrometer. Steel castings shall adhere to chemical composition and tensile property requirements, which include tensile strength, yield strength, elongation, and reduction of area. The surface of castings shall be free of adhering elements such as sand, cracks, hot tears, and other discontinuities, and as such be repair welded when judged appropriate.
SCOPE
1.1 This specification2 covers carbon steel castings for valves, flanges, fittings, or other pressure-containing parts for high-temperature service and of quality suitable for assembly with other castings or wrought-steel parts by fusion welding.  
1.2 Three grades, WCA, WCB, and WCC, are covered in this specification. Selection will depend upon design and service conditions, mechanical properties, and the high temperature characteristics.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

General Information

Status
Historical
Publication Date
30-Apr-2014
Current Stage
Ref Project

Relations

Buy Standard

Technical specification
ASTM A216/A216M-14 - Standard Specification for Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview
Technical specification
REDLINE ASTM A216/A216M-14 - Standard Specification for Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A216/A216M −14 Endorsedby Manufacturers Standardization Society
of the Valve and Fittings Industry
Endorsed by American Foundrymen’s Society
Used in USDOE-NE Standards
Standard Specification for
Steel Castings, Carbon, Suitable for Fusion Welding, for
1
High-Temperature Service
This standard is issued under the fixed designationA216/A216M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope* 2.2 Manufacturers’StandardizationSocietyoftheValveand
4
2 Fittings Industry Standard:
1.1 This specification covers carbon steel castings for
SP 55 Steel Castings for Valve, Flanges, and Fittings, and
valves, flanges, fittings, or other pressure-containing parts for
Other Components (Visual Method)
high-temperature service and of quality suitable for assembly
with other castings or wrought-steel parts by fusion welding.
3. General Conditions for Delivery
1.2 Three grades, WCA, WCB, and WCC, are covered in
3.1 Except for investment castings, castings furnished to
this specification. Selection will depend upon design and
this specification shall conform to the requirements of Speci-
service conditions, mechanical properties, and the high tem-
fication A703/A703M, including any supplementary require-
perature characteristics.
ments that are indicated in the purchase order. Failure to
1.3 The values stated in either SI units or inch-pound units comply with the general requirements of Specification A703/
A703M constitutes nonconformance with this specification. In
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each case of conflict between the requirements of this specification
and Specification A703/A703M, this specification shall pre-
system shall be used independently of the other. Combining
values from the two systems may result in non-conformance vail.
with the standard.
3.2 Steel investment castings furnished to this specification
shall conform to the requirements of Specification A985/
2. Referenced Documents
A985M, including any supplementary requirements that are
3
2.1 ASTM Standards:
indicated in the purchase order. Failure to comply with the
A488/A488M Practice for Steel Castings, Welding, Qualifi-
general requirements of Specification A985/A985M consti-
cations of Procedures and Personnel
tutes nonconformance with this specification. In case of con-
A703/A703M Specification for Steel Castings, General
flict between the requirements of this specification and Speci-
Requirements, for Pressure-Containing Parts
fication A985/A985M, Specification A985/A985M shall
A985/A985M Specification for Steel Investment Castings
prevail.
General Requirements, for Pressure-Containing Parts
4. Ordering Information
1 4.1 The inquiry and order should include or indicate the
This specification is under the jurisdiction ofASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee following:
A01.18 on Castings.
4.1.1 A description of the casting by pattern number or
Current edition approved May 1, 2014. Published May 2014. Originally
drawing (dimensional tolerances shall be included on the
approved in 1939. Last previous edition approved in 2012 as A216/A216M – 12.
casting drawing),
DOI: 10.1520/A0216_A0216M-14.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specifi-
4.1.2 Grade of steel,
cation SA-216/SA-216M in Section II of that code.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
4
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM AvailablefromManufacturersStandardizationSocietyoftheValveandFittings
Standards volume information, refer to the standard’s Document Summary page on Industry (MSS), 127 Park St., NE, Vienna, VA 22180-4602, http://www.mss-
the ASTM website. hq.com.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
A216/A216M−14
TABLE 2 Tensile Requirements
4.1.3 Options in the specification,
4.1.4 Whether the castings are to be produced using the Grade Grade Grade
WCA WCB WCC
investment casting process, and
4.1.5 The supplementary requirements desired including the
standards of acceptance.
Tensile strength, ksi 60 to 85 70 to 95 70 to 95
[MPa] [415 to 585] [485 to 655] [485 to 655]
A
5. Heat Treatment
Yield strength, min, 30 [205] 36 [250] 40 [275]
ksi [MPa
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: A216/A216M − 12 A216/A216M − 14 Endorsed by Manufacturers Standardization Society
of the Valve and Fittings Industry
Endorsed by American Foundrymen’s Society
Used in USDOE-NE Standards
Standard Specification for
Steel Castings, Carbon, Suitable for Fusion Welding, for
1
High-Temperature Service
This standard is issued under the fixed designation A216/A216M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope*
2
1.1 This specification covers carbon steel castings for valves, flanges, fittings, or other pressure-containing parts for
high-temperature service and of quality suitable for assembly with other castings or wrought-steel parts by fusion welding.
1.2 Three grades, WCA, WCB, and WCC, are covered in this specification. Selection will depend upon design and service
conditions, mechanical properties, and the high temperature characteristics.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
2. Referenced Documents
3
2.1 ASTM Standards:
A488/A488M Practice for Steel Castings, Welding, Qualifications of Procedures and Personnel
A703/A703M Specification for Steel Castings, General Requirements, for Pressure-Containing Parts
A985/A985M Specification for Steel Investment Castings General Requirements, for Pressure-Containing Parts
4
2.2 Manufacturers’ Standardization Society of the Valve and Fittings Industry Standard:
SP 55 Steel Castings for Valve, Flanges, and Fittings, and Other Components (Visual Method)
3. General Conditions for Delivery
3.1 Except for investment castings, castings furnished to this specification shall conform to the requirements of Specification
A703/A703M, including any supplementary requirements that are indicated in the purchase order. Failure to comply with the
general requirements of Specification A703/A703M constitutes nonconformance with this specification. In case of conflict between
the requirements of this specification and Specification A703/A703M, this specification shall prevail.
3.2 Steel investment castings furnished to this specification shall conform to the requirements of Specification A985/A985M,
including any supplementary requirements that are indicated in the purchase order. Failure to comply with the general requirements
of Specification A985/A985M constitutes nonconformance with this specification. In case of conflict between the requirements of
this specification and Specification A985/A985M, Specification A985/A985M shall prevail.
4. Ordering Information
4.1 The inquiry and order should include or indicate the following:
4.1.1 A description of the casting by pattern number or drawing (dimensional tolerances shall be included on the casting
drawing),
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.18
on Castings.
Current edition approved Nov. 1, 2012May 1, 2014. Published November 2012May 2014. Originally approved in 1939. Last previous edition approved in 20082012 as
A216/A216M – 08.A216/A216M – 12. DOI: 10.1520/A0216_A0216M-12.10.1520/A0216_A0216M-14.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-216/SA-216M in Section II of that code.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
Available from Manufacturers Standardization Society of the Valve and Fittings Industry (MSS), 127 Park St., NE, Vienna, VA 22180-4602, http://www.mss-hq.com.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
A216/A216M − 14
4.1.2 Grade of steel,
4.1.3 Options in the specification,
4.1.4 Whether the castings are to be
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.