ASTM C1107/C1107M-11

(Specification)

Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)

Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)

ABSTRACT
This specification covers packaged dry, hydraulic cement grout (nonshrink) intended for use under applied load where a change in height below initial placement height is to be avoided. Grouts covered are composed of hydraulic cement, fine aggregate, and other ingredients. They require only the addition of mixing water for use. The materials used as ingredients in packaged, dry, grout include hydraulic cement, fine aggregate, and other ingredients. The performance requirements of the specimens are presented in details. Grout mixtures shall be produced using the conditions prescribed. For smaller quantities of grout, the mortar-mixing apparatus shall be as specified. Mixer for grout performance qualifications shall be clean, pre-wetted, and drained and essentially free of hardened mortar and other foreign material that can be removed with a trowel or by reasonably striking with a hammer. The procedures for preliminary adjustment mixing and grout performance qualification are presented in details. Consistency testing shall be performed on the grout mixture. Determine the yield of the grout using the 400-mL cylindrical measure described.
SCOPE
1.1 This specification covers packaged dry, hydraulic cement grout (nonshrink) intended for use under applied load (such as to support a structure, a machine, and the like) where a change in height below initial placement height is to be avoided.
1.2 Grouts covered are composed of hydraulic cement, fine aggregate, and other ingredients. They require only the addition of mixing water for use.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4 The following safety hazards caveat pertains only to the test method portion of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
31-Mar-2011
ICS
91.100.10 - Cement. Gypsum. Lime. Mortar
Technical Committee
C09 - Concrete and Concrete Aggregates
Drafting Committee
C09.43 - Packaged Dry Combined Materials
Current Stage
Ref Project

Relations

Replaces
ASTM C1107/C1107M-08 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
Effective Date
01-Apr-2011
Replaced By
ASTM C1107/C1107M-13 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
Effective Date
01-May-2013
Referred By
ASTM C1857/C1857M-19 - Standard Test Method for Evaluating the Adhesion (Pull-Off) Strength of Concrete Repair and Overlay Mortar
Effective Date
01-Apr-2011
Referred By
ASTM C1821/C1821M-16(2021)e1 - Standard Practice for Installation of Underground Circular Precast Concrete Manhole Structures
Effective Date
01-Apr-2011
Referred By
ASTM C1600/C1600M-23 - Standard Specification for Rapid Hardening Hydraulic Cement
Effective Date
01-Apr-2011
Referred By
ASTM E2950-14(2020) - Standard Specification for Metal Canopy Systems
Effective Date
01-Apr-2011
Referred By
ASTM C1708/C1708M-19 - Standard Test Methods for Self-leveling Mortars Containing Hydraulic Cements
Effective Date
01-Apr-2011

Buy Standard

ASTM C1107/C1107M-11 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)ASTM C1107/C1107M-11 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
PreviousNext
Technical specification
ASTM C1107/C1107M-11 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
English language
5 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM C1107/C1107M-11 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)REDLINE ASTM C1107/C1107M-11 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
PreviousNext
Technical specification
REDLINE ASTM C1107/C1107M-11 - Standard Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
English language
5 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:C1107/C1107M −11
StandardSpecification for
1
Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
ThisstandardisissuedunderthefixeddesignationC1107/C1107M;thenumberimmediatelyfollowingthedesignationindicatestheyear
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* C157/C157M Test Method for Length Change of Hardened
Hydraulic-Cement Mortar and Concrete
1.1 This specification covers packaged dry, hydraulic ce-
C185 Test Method for Air Content of Hydraulic Cement
ment grout (nonshrink) intended for use under applied load
Mortar
(such as to support a structure, a machine, and the like) where
C305 Practice for Mechanical Mixing of Hydraulic Cement
a change in height below initial placement height is to be
Pastes and Mortars of Plastic Consistency
avoided.
C702 PracticeforReducingSamplesofAggregatetoTesting
1.2 Grouts covered are composed of hydraulic cement, fine
Size
aggregate, and other ingredients. They require only the addi-
C827 Test Method for Change in Height at Early Ages of
tion of mixing water for use.
Cylindrical Specimens of Cementitious Mixtures
1.3 The values stated in either SI units or inch-pound units C939 Test Method for Flow of Grout for Preplaced-
Aggregate Concrete (Flow Cone Method)
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each C1090 Test Method for Measuring Changes in Height of
Cylindrical Specimens of Hydraulic-Cement Grout
system shall be used independently of the other. Combining
values from the two systems may result in non-conformance C1437 Test Method for Flow of Hydraulic Cement Mortar
with the standard.
3. Terminology
1.4 The following safety hazards caveat pertains only to the
test method portion of this specification: This standard does
3.1 Definitions—For definitions of terms used in this
not purport to address all of the safety concerns, if any,
specification, refer to Terminology C125.
associated with its use. It is the responsibility of the user of this
3.2 Definitions of Terms Specific to This Standard:
standard to establish appropriate safety and health practices
3.2.1 consistency, flowable, n—a grout consistency having a
and determine the applicability of regulatory limitations prior
flow of 125 to 145 by the flow test in accordance with the
to use.
applicable provisions of Test Method C1437; the flow after 5
drops of the flow table in 3 s.
2. Referenced Documents
2 3.2.2 consistency, fluid, n—a grout consistency having a
2.1 ASTM Standards:
time of efflux of 10 to 30 s when tested by the flow cone
C109/C109M Test Method for Compressive Strength of
procedure of Test Method C939.
Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube
3.2.3 consistency, plastic, n—a grout consistency having a
Specimens)
flow of 100 to 125 by the flow test in accordance with the
C125 Terminology Relating to Concrete and Concrete Ag-
applicable provisions of Test Method C1437; the flow after 5
gregates
drops of the flow table in 3 s.
C138/C138M Test Method for Density (Unit Weight),Yield,
and Air Content (Gravimetric) of Concrete
4. Ordering Information
4.1 When the purchaser specifies that properties of the
1
This specification is under the jurisdiction of ASTM Committee C09 on
packaged,drygroutmeettherequirementsofthisspecification,
Concrete and Concrete Aggregatesand is the direct responsibility of Subcommittee
C09.43 on Packaged Dry Combined Materials.
also specify which, if any, of the optional requirements apply.
Current edition approved April 1, 2011. Published April 2011. Originally
4.2 When the grout is to be used in contact with stressed
approved in 1991. Last previous edition approved in 2008 as C1107/C1107M–08.
DOI: 10.1520/C1107_C1107M-11.
tendons or other corrosion-sensitive, load-bearing structural
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
members, the purchaser shall supply this information to the
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
manufacturer and obtain assurances that the material meets
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. relevant chloride, nitrite, nitrate, sulfide, and sulfate
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
C1107/C1107M−11
requirements, and any other material limitations imposed by 7. Sampling
the applicable codes and standards (See Note 1).
7.1
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:C1107/C1107M–08 Designation: C1107/C1107M – 11
Standard Specification for
1
Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
ThisstandardisissuedunderthefixeddesignationC1107/C1107M;thenumberimmediatelyfollowingthedesignationindicatestheyear
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers packaged dry, hydraulic cement grout (nonshrink) intended for use under applied load (such as to
support a structure, a machine, and the like) where a change in height below initial placement height is to be avoided.
1.2 Grouts covered are composed of hydraulic cement, fine aggregate, and other ingredients. They require only the addition of
mixing water for use.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.4 The following safety hazards caveat pertains only to the test method portion of this specification: This standard does not
purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to
establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
2. Referenced Documents
2
2.1 ASTM Standards:
C109/C109M Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
C125 Terminology Relating to Concrete and Concrete Aggregates
C138/C138M Test Method for Density (Unit Weight), Yield, and Air Content (Gravimetric) of Concrete
C157/C157M Test Method for Length Change of Hardened Hydraulic-Cement Mortar and Concrete
C185 Test Method for Air Content of Hydraulic Cement Mortar
C305 Practice for Mechanical Mixing of Hydraulic Cement Pastes and Mortars of Plastic Consistency
C702 Practice for Reducing Samples of Aggregate to Testing Size
C827 Test Method for Change in Height at Early Ages of Cylindrical Specimens of Cementitious Mixtures
C939 Test Method for Flow of Grout for Preplaced-Aggregate Concrete (Flow Cone Method)
C1090 Test Method for Measuring Changes in Height of Cylindrical Specimens of Hydraulic-Cement Grout
C1437 Test Method for Flow of Hydraulic Cement Mortar
3. Terminology
3.1 Definitions—For definitions of terms used in this specification, refer to Terminology C125.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 consistency, flowable, n—a grout consistency having a flow of 125 to 145 by the flow test in accordance with the
applicable provisions of Test Method C1437; the flow after 5 drops of the flow table in 3 s.
3.2.2 consistency, fluid, n—a grout consistency having a time of efflux of 10 to 30 s when tested by the flow cone procedure
of Test Method C939.
3.2.3 consistency, plastic, n—a grout consistency having a flow of 100 to 125 by the flow test in accordance with the applicable
provisions of Test Method C1437; the flow after 5 drops of the flow table in 3 s.
4. Ordering Information
4.1 When the purchaser specifies that properties of the packaged, dry grout meet the requirements of this specification, also
specify which, if any, of the optional requirements apply.
1
This specification is under the jurisdiction ofASTM Committee C09 on Concrete and ConcreteAggregates and is the direct responsibility of Subcommittee C09.43 on
Packaged Dry Combined Materials.
Current edition approved Oct.April 1, 2008.2011. Published November 2008.April 2011. Originally approved in 1991. Last previous edition approved in 20072008 as
C1107–07a.C1107/C1107M–08. DOI: 10.1520/C1107_C1107M-0811.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C1107/C1107M – 11
4.2 When the grout is to be used in contact with stressed tend
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1260-23(Test Method)
Standard Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method)

SIGNIFICANCE AND USE
4.1 This test method provides a means of detecting the potential of an aggregate intended for use in concrete for undergoing alkali-silica reaction resulting in potentially deleterious internal expansion. It is based on the NBRI Accelerated Test Method (1-4).3 It is especially useful for aggregates that react slowly or produce expansion late in the reaction. However, it does not evaluate combinations of aggregates with cementitious materials nor are the test conditions representative of those encountered by concrete in service.  
4.2 Because the specimens are exposed to a NaOH solution, the alkali content of the cement is not a significant factor in affecting expansions.  
4.3 Results of tests conducted on an aggregate as described herein should form a part of the basis for a decision as to whether precautions should be taken against excessive expansion due to alkali-silica reaction. Refer to Guide C1778 for the interpretation of the test results from Test Method C1260.
SCOPE
1.1 This test method permits detection, within 16 days, of the potential for deleterious alkali-silica reaction of aggregate in mortar bars.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. When this test method refers to combined-unit standards, the selection of the measurement systems is at the user’s discretion.  
1.3 The text of this test method refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this test method.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. A specific precautionary statement is given in the section on Reagents.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C1810/C1810M-23(Guide)
Standard Guide for Comparing Performance of Concrete-Making Materials Using Mortar Mixtures

SIGNIFICANCE AND USE
4.1 The results of mortar mixture tests can be suitable for comparing the relative performance of combinations of concrete-making materials such as fine aggregate, chemical admixtures, supplementary cementitious materials (SCMs), water, and hydraulic cement. Furthermore, this guide can be useful to identify unexpected performances due to combination of various materials. The relative trends in performance observed with the mortar method may suggest relative performance in concrete mixtures batched with the same materials and relative mixture proportions.  
4.2 While there are a number of ways to proportion and mix mortar mixtures, four procedures described in this guide have been used extensively for evaluating the performance of admixtures. Method A enables evaluation of materials using mixture proportions that correspond to specific job conditions. Method B can be used as a general mixture using fixed amounts of a standard sand, cement, and supplementary cementitious materials. Method C is a modified version of Test Method C359 to evaluate the impact of chemical admixtures on the early stiffening of a mortar prepared with specified amounts of job cement, a standard sand, and an amount of water that will produce a mortar with a specified initial penetration measured in accordance with Test Method C359. The measurements of penetration over time can be related to the early stiffening processes associated with false and flash set. Method D is a modified version of Test Method C185 whereby the mortar mixture can be prepared with various combinations of chemical admixtures, supplementary cementitious materials, and job water. Methods A and B would be most applicable for investigating material incompatibility issues associated with ready mixed concrete, while Method C would be applicable for concrete mixed for a short period of time in stationary mixers and transported to the forms in non-agitating equipment. Method D is suitable for all concrete mixing processes and is...
SCOPE
1.1 This guide provides information on how to compare the relative performance and potential incompatibility of combinations of concrete-making materials. Performance tests on fresh and early-age properties of mortar mixtures can be useful indicators of concrete performance using similar materials. The performance tests described in this guide include mortar-slump, mortar spread, mortar-workability retention, early stiffening of mortar, time of setting, air entrainment, and hydration kinetics.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with this guide. Some values only have SI units because the inch-pound equivalents are not used in guide.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Warning—Fresh hydraulic cementitious mixtures are caustic and may cause burns to skin and tissue upon prolonged exposure.2  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    12 pages
    English language
    sale 15% off
  • Guide
    12 pages
    English language
    sale 15% off
ASTM
ASTM C1090/C1090M-23(Test Method)
Standard Test Method for Measuring Changes in Height of Cylindrical Specimens of Hydraulic-Cement Grout

SIGNIFICANCE AND USE
4.1 This test method is intended to provide a means of assessing the ability of a hydraulic-cement grout to retain a stable volume during the stipulated testing period of 28 days, provided that the tendency to change height does not include the effects of drying caused by evaporation, uptake of moisture, carbonation, or exposure to temperatures outside the range 23.0 °C ± 2.0 °C [73 °F ± 3.5 °F] (Note 2). An exception is made when the options described in the section on test conditions are exercised.  
Note 2: This test method does not measure the change in height before setting (see Test Method C827/C827M).
SCOPE
1.1 This test method covers measurement of the changes in height of hydraulic-cement grout by the use of 75 mm by 150 mm [3 in. by 6 in.] cylinders, when the cylinders are protected so that the tendency to change in height does not include evaporation so as to cause drying, uptake of moisture, carbonation, or exposure to temperatures outside the range 23 °C ± 2.0 °C [73 °F ± 3.5 °F] or, optionally, to another specified temperature controlled within ±2.0 °C [±3.5 °F].  
1.2 If desired, this test method can be adapted to studies of changes in height involving either schedules or environmental treatment different from the standard procedures prescribed by this test method.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
Note 1: Sieve size is identified by its standard designation in Specification E11. The alternative designation given in parentheses is for information only and does not represent a different standard sieve size.  
1.4 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed skin and tissue upon prolonged exposure.2)  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM C827/C827M-23(Test Method)
Standard Test Method for Change in Height at Early Ages of Cylindrical Specimens of Cementitious Mixtures

SIGNIFICANCE AND USE
4.1 This test method provides a means for comparing the relative shrinkage or expansion of cementitious mixtures. It is particularly applicable to grouting, patching, and form-filling operations where the objective is to completely fill a cavity or other defined space with a freshly mixed cementitious mixture that will continue to fill the same space at time of hardening. It would be appropriate to use this test method as a basis for prescribing mixtures having restricted or specified volume change before the mixture becomes hard.  
4.2 This test method can be used for research purposes to provide information on volume changes taking place in cementitious mixtures between the time just after mixing and the time of hardening. However, the specimen used in this test method is not completely unrestrained so that the measurements are primarily useful for comparative purposes rather than as absolute values. Further, the degree of restraint to which the specimen is subjected varies with the viscosity and degree of hardening of the mixture.
SCOPE
1.1 This test method covers the determination of change in height of cylindrical specimens from the time of molding until the mixture is hard.  
1.2 This test method covers height change measurements at early ages for cementitious mixtures of paste, grout, mortar, and concrete.  
1.3 This test method is intended for determination of changes in height that occur from the time of placement until the specimen is fully hard. These include shrinkage or expansion due to hydration, settlement, evaporation, and other physical and chemical effects.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined  
1.5 The text of this test method refers to notes and footnotes that provide explanatory information. These notes and footnotes shall not be considered as requirements of the test method.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed skin and tissue upon prolonged exposure.2)  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C387/C387M-23(Specification)
Standard Specification for Packaged, Dry, Combined Materials for Concrete and High Strength Mortar

ABSTRACT
This specification covers the production, properties, packaging, and testing of packaged, dry, combined materials for concrete and mortars. Concrete mixtures covered by this specification includes high-early strength concrete, normal strength concrete, normal weight concrete, high-strength mortar, and mortars for unit masonry. The purchaser shall specify the material desired as concrete, high strength mortar, or mortar for use with unit masonry, and the respective physical requirements. Materials used as ingredients in packaged, dry, combined materials for mortar and concrete shall be composed of aggregates, air-entraining admixtures, blended cement, chemical admixtures, fly ash, ground granulated blast-furnace slag, hydrated lime, latex and powder polymer modifiers, masonry cement, mortar cement, Portland cement, and silica fume. All aggregates shall be dried, without disintegration, to specific moisture content The proportions of cementitious material and aggregate shall be such that the strength requirements will be met. Packaged, dry, combined materials for concrete, high strength mortar and mortar for use with unit masonry shall conform to the respective compressive strength requirements. Scales conforming to the standards will be used for sampling concretes from a single batch using a sufficient quantity. A slump test will be performed to check if additional water is required. In sampling mortar, the contents of an entire package of dry, combined material for mortar for unit masonry or for concrete mortar shall be used. Mortar mixing equipment, which must be provided with a bowl positioning adapter, shall be used to ensure clearance for the largest size aggregate in the mix being tested. The specification includes the following testing methods for mortar: compressive strength, density and yield, air content, and water retention.
SCOPE
1.1 This specification covers the production, properties, packaging, and testing of packaged, dry, combined materials for concrete and high strength mortar. The classifications of concrete and mortar covered are defined in Section 3.
Note 1: The scope of this standard does not cover mortars for unit masonry. Dry preblended mortars for unit masonry are covered by Specification C1714/C1714M.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Some values have only SI units because the inch-pound equivalents are not used in practice.  
1.3 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this standard.  
1.4 The following safety hazards caveat pertains only to the test method portion of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM C87/C87M-23(Test Method)
Standard Test Method for Effect of Organic Impurities in Fine Aggregate on Strength of Mortar

SIGNIFICANCE AND USE
5.1 This test method is of significance in making a final determination of the acceptability of fine aggregates with respect to the requirements of Specification C33/C33M concerning organic impurities.  
5.2 This test method is applicable to those samples which, when tested in accordance with Test MethodC40/C40M, have produced a supernatant liquid with a color darker than the standard listed in Table 1 of C40/C40M (Organic plate No. 3, Gardner Color Standard No. 14, Circular Disk No. 14 or prepared color solution).  
5.3 Many specifications provide for the acceptance of fine aggregate producing a darker color in the Test Method C40/C40M test, if testing by this test method indicates the strength of the mortar cubes prepared with the unwashed fine aggregate is comparable to the strength of mortar cubes made with the washed fine aggregate.
SCOPE
1.1 This test method covers the determination of the effect on mortar strength of the organic impurities in fine aggregate, whose presence is indicated using Test Method C40/C40M. Comparison is made between compressive strengths of mortar made with washed and unwashed fine aggregate.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Some values have only SI units because the inch-pound equivalents are not used in the practice.
Note 1: Sieve size is identified by its standard designation in Specification E11. The alternative designation given in parentheses is for information only and does not represent a different standard sieve size  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.(Warning—Fresh hydraulic cementitous mixtures are caustic and may cause chemical burns to exposed skin and tissue upon prolonged exposure.)2  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C1679-22(Practice)
Standard Practice for Measuring Hydration Kinetics of Hydraulic Cementitious Mixtures Using Isothermal Calorimetry

SIGNIFICANCE AND USE
5.1 Thermal power curves are used to evaluate the isothermal hydration kinetics of the combined mixture of different materials during the early period after being mixed with water. These isothermal power curves, or hydration profiles, may provide indications relative to setting characteristics, compatibility of different materials, sulfate balance and early strength development. The isothermal hydration profiles can also be used to evaluate the effects of compositions, proportions, and time of addition of materials as well as curing temperature. Special care must be used in evaluating extended retardation with paste specimens, which have been shown to overestimate the retardation of some mixtures containing cement, SCM, and admixtures.  
5.2 This procedure can be used to measure the effect of chemical admixtures on the cement hydration profile. In many cases, the addition of chemical admixture changes the kinetics of cement hydration.  
5.3 Although this technique has been used historically to understand issues related to setting and slump loss, it must be emphasized that isothermal calorimetry results cannot predict concrete performance definitely, either positively or negatively. Extensive verification in concrete at planned dosages and temperatures, and at higher dosages, is needed. Isothermal calorimetry is an effective tool to identify sensitivities, so that concrete testing can be efficiently planned and performed.  
5.4 This practice provides a means of assessing the relative hydration performance of various test mixtures compared with control mixtures that are prepared in a similar manner.  
5.5 The procedure and apparatus can be used to monitor the thermal power from pastes and mortars alone or in combination with chemical admixtures.  
5.6 The isothermal calorimeter described here can be used to measure the thermal power and heat of hydration of mortars prepared independently or obtained by wet sieving from concrete in accordance with Practice C172/C1...
SCOPE
1.1 This practice describes the apparatus and procedure for measuring relative differences in hydration kinetics of hydraulic cementitious mixtures, either in paste or mortar (see Note 1), including those containing admixtures, various supplementary cementitious materials (SCM), and other fine materials by measuring the thermal power using an isothermal calorimeter.
Note 1: Paste specimens are often preferred for mechanistic research when details of individual reaction peaks are important or for particular calorimetry configurations. Mortar specimens may give results that have better correlation with concrete setting and early strength development and are often preferred to evaluate different mixture proportions for concrete. Both paste and mortar studies have been found to be effective in evaluating concrete field problems due to incompatibility of materials used in concrete mixtures.  
1.2 This practice does not cover the measurement of heat of hydration. Heat of hydration can be determined according to Test Method C1702.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    15 pages
    English language
    sale 15% off
  • Standard
    15 pages
    English language
    sale 15% off
ASTM
ASTM C1709-22(Guide)
Standard Guide for Evaluation of Alternative Supplementary Cementitious Materials (ASCM) for Use in Concrete

SIGNIFICANCE AND USE
4.1 Supplementary cementitious materials (SCM) covered under existing ASTM specifications are fly ash, slag cement, raw and calcined natural pozzolans including calcined clays, silica fume, and ground-glass pozzolan. The use of these materials, and limits established in existing specifications, are based on data obtained from research programs, field testing, and long term performance monitoring. Performance of SCM in specific concrete mixtures is commonly verified through preconstruction testing. This guide provides an approach to assessing the properties of materials that are not covered under existing specifications, and for assessing the performance of those materials in concrete.  
4.2 If an ASCM does not yet have a significant record of performance in concrete, a comprehensive evaluation based on this Guide should be undertaken, and it should be recognized that this ASCM might be introduced for a specific project or into a limited marketplace to initially demonstrate its performance. The user should bear in mind the intended end use of the ASCM and use appropriate test methods to establish its suitability. An ASCM that demonstrates good performance through a comprehensive evaluation as outlined in this guide could then be considered to have access to broader markets and could be considered for inclusion in an ASTM standard for SCM. For this reason, the test program to demonstrate acceptable performance should include concrete mixtures with a range of characteristics specific to the ASCM’s intended use.  
4.3 In the absence of long-term durability or acceptable field performance, prospective users are advised to apply appropriate risk management and engineering practice in the use of an ASCM.
SCOPE
1.1 This guide is intended to provide a technical approach to the evaluation of alternative supplementary cementitious materials such as pozzolans and hydraulic materials that fall outside the scope of Specifications C618, C989/C989M, C1240, and C1866/C1866M. This guide provides the initial steps for a comprehensive evaluation of an ASCM that provides due diligence for its specific intended uses in concrete; however, it does not evaluate conformance to all possible performance criteria for all types of concrete mixtures.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 Performing the tests or meeting the test limits in this guide should not imply that the material tested meets the requirements of Specifications C618, C989/C989M, C1240, and C1866/C1866M. These materials should not be represented as such and each specific source is to be evaluated separately.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    5 pages
    English language
    sale 15% off
  • Guide
    5 pages
    English language
    sale 15% off
ASTM
ASTM C1753/C1753M-21a(Practice)
Standard Practice for Evaluating Early Hydration of Hydraulic Cementitious Mixtures Using Thermal Measurements

SIGNIFICANCE AND USE
5.1 This practice provides a means of assessing the relative early hydration performance of various test mixtures compared with control mixtures that are prepared in a similar manner.  
5.2 Thermal profiles are used to evaluate the hydration behavior of hydraulic cementitious mixtures after the addition of water. They may provide indications concerning setting characteristics, compatibility of different materials, sulfate balance, relative heat of hydration, and early strength development. They can be used to evaluate the effects of compositions, proportions, and time of addition of materials as well as the initial mixture and test temperatures. Thermal profile testing is an effective tool for identifying performance sensitivities or trends, and may help to reduce the number of concrete test mixtures required to develop and qualify mixtures, especially those to be subject to variable ambient environments. It may be used by concrete producers, materials suppliers, and other practitioners to support mixture development, selection of material types or sources, optimization of proportions, or troubleshooting of field problems.  
5.3 This practice can be used to understand concrete problems related to slump loss, setting, and early strength, but results may not predict field concrete performance. Performance verification with concrete is needed to quantify the trends identified using thermal testing.  
5.4 This practice can be used to evaluate the effects of chemical admixtures on the thermal profiles of cementitious mixtures. This can be especially useful in selecting dosages appropriate for different ambient conditions.  
5.5 Thermal measurement testing as described in this practice may have similar significance and use as isothermal calorimetry described by Practice C1679 or some types of near-adiabatic calorimetry. The selection of which practice or methods to use may depend on specific applications and circumstances. The thermal profiles obtained by this practic...
SCOPE
1.1 This practice describes the apparatus and procedure for evaluating relative differences in early hydration of hydraulic cementitious mixtures such as paste, mortar, or concrete, including those containing chemical admixtures, various supplementary cementitious materials (SCMs), and other finely divided materials, by measuring the temperature history of a specimen.  
1.2 Calorimetry is the measurement of heat lost or gained during a chemical reaction such as cement hydration; calorimetric measurements as a function of time can be used to describe and evaluate hydration and related early-age property development. Calorimetry may be performed under isothermal conditions (as described in Practice C1679) or under adiabatic or semi-adiabatic conditions. This practice cannot be described as calorimetry because no attempt is made to measure or compute the heat evolved from test specimens due to hydration, but it can in many cases be used for similar evaluations. Variables that should be considered in the application of this practice are discussed in the Appendix.  
1.3 Units—The values stated in either SI units or inch-pound units shall be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Some values have only SI units because the inch-pound equivalents are not used in practice.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Warning: Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2  
1.5 This...

  • Standard
    19 pages
    English language
    sale 15% off
  • Standard
    19 pages
    English language
    sale 15% off
ASTM
ASTM C1697-21(Specification)
Standard Specification for Blended Supplementary Cementitious Materials

SCOPE
1.1 This specification covers blended supplementary cementitious materials that result from the blending or intergrinding of two or three ASTM compliant supplementary cementitious materials, for use in concrete or mortar where hydraulic or pozzolanic action, or both, is desired. The supplementary cementitious materials include slag cement conforming to Specification C989/C989M, natural pozzolans and coal fly ash conforming to Specification C618 and silica fume conforming to Specification C1240.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
Note 1: The incorporation of supplementary cementitious materials as separate additions or as a manufactured blend may significantly alter the properties of fresh and hardened concrete. The user should be aware of these changes and is referred to the ACI Manual of Concrete Practice2 for information and guidelines. Specific reference is made to:    
ACI 232.1R  
Use of Natural Pozzolans in Concrete  
ACI 232.2R  
Use of Fly Ash in Concrete  
ACI 233R  
Slag Cement in Concrete and Mortar  
ACI 234R  
Guide for the Use of Silica Fume in Concrete  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off