ASTM D3450-00(2010)

(Test Method)

Standard Test Method for Washability Properties of Interior Architectural Coatings

Standard Test Method for Washability Properties of Interior Architectural Coatings

SIGNIFICANCE AND USE
Interior architectural paints are often discolored by dirt and other soilant materials. This test method covers the relative ease and completeness of removal of a specific soilant from such a surface by scrubbing. The greater the ease of soil removal with a minimum of film erosion, the greater the useful service life is expected to be.
Results obtained by this test method do not necessarily correlate with all types of soilants.
Semigloss finishes generally require only the nonabrasive type cleaner for good soilant removal, whereas flat paints may require the abrasive type.
SCOPE
1.1 This test method covers the determination of the relative ease of removing soilant discolorations from the dried film of an interior coating by washing with either an abrasive or nonabrasive cleaner.  
1.2 This test method is limited to coatings having a CIE-Y reflectance of 60 % or more, as measured in accordance with Test Method E1347.
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
31-May-2010
ICS
87.040 - Paints and varnishes
Technical Committee
D01 - Paint and Related Coatings, Materials, and Applications
Drafting Committee
D01.42 - Architectural Coatings
Current Stage
Ref Project

Relations

Replaces
ASTM D3450-00(2005) - Standard Test Method for Washability Properties of Interior Architectural Coatings
Effective Date
01-Jun-2010
Replaced By
ASTM D3450-00(2010)e1 - Standard Test Method for Washability Properties of Interior Architectural Coatings
Effective Date
01-Jun-2010
Referred By
ASTM D5146-10(2019) - Standard Guide to Testing Solvent-Borne Architectural Coatings
Effective Date
01-Jun-2010
Referred By
ASTM D4213-08(2016) - Standard Test Method for Scrub Resistance of Paints by Abrasion Weight Loss
Effective Date
01-Jun-2010
Referred By
ASTM D16-23 - Standard Terminology for Paint, Related Coatings, Materials, and Applications
Effective Date
01-Jun-2010
Referred By
ASTM D3730-17(2022) - Standard Guide for Testing High-Performance Interior Architectural Wall Coatings
Effective Date
01-Jun-2010
Referred By
ASTM D5324-16(2022) - Standard Guide for Testing Water-Borne Architectural Coatings
Effective Date
01-Jun-2010
Referred By
ASTM D4828-94(2020) - Standard Test Methods for Practical Washability of Organic Coatings
Effective Date
01-Jun-2010

Buy Standard

ASTM D3450-00(2010) - Standard Test Method for Washability Properties of Interior Architectural CoatingsASTM D3450-00(2010) - Standard Test Method for Washability Properties of Interior Architectural Coatings
PreviousNext
Standard
ASTM D3450-00(2010) - Standard Test Method for Washability Properties of Interior Architectural Coatings
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D3450–00(Reapproved2010)
Standard Test Method for
Washability Properties of Interior Architectural Coatings
This standard is issued under the fixed designation D3450; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope 3.1.1 soilant, n—a discoloring substance that clings to the
surfaceofacoating,whosedispersedcolorcomponentisnotin
1.1 Thistestmethodcoversthedeterminationoftherelative
solution and therefore does not penetrate into the film.
ease of removing soilant discolorations from the dried film of
3.1.1.1 Discussion—soilant differs from stain in that the
an interior coating by washing with either an abrasive or
colorant of a stain is in solution and, therefore, can penetrate
nonabrasive cleaner.
into the film.
1.2 This test method is limited to coatings having a CIE-Y
reflectance of 60 % or more, as measured in accordance with
4. Summary of Test Method
Test Method E1347.
4.1 The test material is applied to a black plastic panel and
1.3 The values stated in SI units are to be regarded as the
allowed to dry for 7 days. The reflectance of the film is
standard. The values given in parentheses are for information
measured (R ) and then a soilant consisting of carbon black
only.
dispersed in mineral oil is applied on the film. The panel is
1.4 This standard does not purport to address all of the
placed on a glass plate in a washability machine and the film is
safety concerns, if any, associated with its use. It is the
washed with either an abrasive or nonabrasive scrub medium
responsibility of the user of this standard to establish appro-
for100cycles.Thepanelisrinsedanddriedandthereflectance
priate safety and health practices and determine the applica-
in the stained area is read (R ). The ratio of the reflectance,
bility of regulatory limitations prior to use.
R /R , is a measure of the degree to which the soilant has been
2 1
2. Referenced Documents removed.
2.1 ASTM Standards:
5. Significance and Use
D562 Test Method for Consistency of Paints Measuring
5.1 Interior architectural paints are often discolored by dirt
Krebs Unit (KU)Viscosity Using a Stormer-TypeViscom-
andothersoilantmaterials.Thistestmethodcoverstherelative
eter
ease and completeness of removal of a specific soilant from
D1193 Specification for Reagent Water
such a surface by scrubbing. The greater the ease of soil
D1210 Test Method for Fineness of Dispersion of Pigment-
removal with a minimum of film erosion, the greater the useful
Vehicle Systems by Hegman-Type Gage
service life is expected to be.
E70 Test Method for pH of Aqueous Solutions With the
5.2 Results obtained by this test method do not necessarily
Glass Electrode
correlate with all types of soilants.
E1347 Test Method for Color and Color-Difference Mea-
5.3 Semigloss finishes generally require only the nonabra-
surement by Tristimulus Colorimetry
sive type cleaner for good soilant removal, whereas flat paints
3. Terminology may require the abrasive type.
3.1 Definitions of Terms Specific to This Standard:
6. Apparatus
6.1 Washability Tester, also referred to as a straight line
This test method is under the jurisdiction of ASTM Committee D01 on Paint
washability machine.
and Related Coatings, Materials, andApplications and is the direct responsibility of
6.1.1 Accessory Apparatus:
Subcommittee D01.42 on Architectural Coatings.
CurrenteditionapprovedJune1,2010.PublishedJuly2010.Originallyapproved
in 1975. Last previous edition approved in 2005 as D3450 – 00 (2005). DOI:
10.1520/D3450-00R10. Model AG 8100 from BYK-Gardner, Inc., Gardner Laboratory, 2435 Linden
For referenced ASTM standards, visit the ASTM website, www.astm.org, or Lane, Silver Spring, MD 20910 and Model “D” from Paul N. Gardner Co., Inc., 316
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM N. E. First St., Pompano Beach ,FL 33060 were used originally in this test method.
Standards volume information, refer to the standard’s Document Summary page on See RR D01-1065. Straight-line washability testers may be adapted to meet the
the ASTM website. requirements of this method.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
D3450–00 (2010)
6.1.1.1 Glass Plate, measured to fit, 454 by 165 by 6.3 mm 7.6.1 MixcomponentsanddispersetoaHegmanfinenessof
7 1 1
(17 ⁄8 by 6 ⁄2 by ⁄4 in.). 7 (0.5 mils or 13 µm) or when measured in accordance with
6.1.1.2 Stainless Steel Pan. Test Method D1210.
6.1.1.3 “C” Clamps. 7.7 Scrub Media (Note 1).
,
9 8
6.1.1.4 Scale, standard. 7.7.1 Nonabrasive Medium consisting of the following:
6.1.1.5 White Blotter.
6.1.1.6 Holder, brass, measuring 95 by 76 by 25.4 mm (3 ⁄4
grams
A
Water 89.6
by 3 by 1 in.).
Hydroxyethyl cellulose 2.0
6.2 U-Shaped Film Caster, having both a 0.18-mm (7-
12,8
Detergent 4.0
mil) clearance by 132 mm width and a 0.25-mm (10-mil) Trisodium phosphate, anhydrous 4.0
B
Acetic acid glacial 0.3
clearance by 138 mm width.
13,8
Preservative 0.1
6.3 Film Applicator, 76 mm (3 in.) width with 76-µm
100.0
(3-mil) clearance. A
Vary to achieve a final consistency of 165 to 220 g (75 to 85 Krebs Units) with
a Stormer Viscometer in accordance with Test Method D562.
6.4 Suction Plate for drawdowns (large size).
B
Vary to achieve a final pH from 9.5 to 10.0 in accordance with Test Method
6.5 45°, 0° Reflectometer, with green filter, as specified in
E70.
Test Method E1347.
9,8
7.7.2 Abrasive Medium, consisting of the following:
6.6 Balance, with 0.1-g scale graduation.
grams
6.7 Fineness of Dispersion Gage, as specified in Test A
Water 49.4
Hydroxyethyl cellulose 0.8
Method D1210.
Ammonium hydroxide 28 % ---
12,8
Detergent 2.0
7. Reagents and Materials
Trisodium phosphate, anhydrous 2.0
14,8
Silica 45.0
7.1 Purity of Reagents—Reagent grade chemicals shall be
B
Acetic acid, glacial 0.7
used in all tests. Unless otherwise indicated, it is intended that
13,8
Preservative 0.1
all reagents shall conform to the specifications of the Commit-
100.0
tee onAnalytical Reagents of theAmerican Chemical Society,
A
Vary to achieve a final consistency of 475 to 600 g (110 to 120 Krebs Units)
where such specifications are available. Other grades may be
with the Stormer Viscometer in accordance with Test Method D562.
B
used, provided it is first ascertained that the reagent is of
Vary to achieve a final pH of 9.5 to 10.0 in accordance with Test Method E70.
7.8 Slowly add the hydroxethyl cellulose to the water while
sufficiently high purity to permit its use without lessening the
accuracy of the determination. stirring mechanically. Stir until uniform and then slowly add 2
to 3 drops of 28 % ammonium hydroxide solution while
7.2 Purity of Water—Unless otherwise indicated, reference
towatershallbeunderstoodtomeanreagentwaterconforming mixing and continue mixing until the solution turns clear. In
the order shown, add the other ingredients separately, stirring
to Type IV of Specification D1193.
7.3 Black Plastic Panels. continuously. Be sure each item is uniformly dispersed before
,
7 8
adding the next one. Add the silica slowly to ensure uniform
7.4 Sponge .
7.5 Masking Tape. dispersion. Finally, add the preservative and adjust the pH with
,
9 8
glacial acetic acid.
7.6 Soilant Medium, consisting of the following:
grams
NOTE 1—When a referee test is made, prepare fresh medium or use
Mineral oil, USP heavy 60
standardized scrub medium from a previously unopened container that is
Odorless mineral spirits 32
10,8
no more than 1 year old.
Carbon black 8
8. Preparation of Apparatus
8.1 Washability Machine—The washability machine should
be leveled before use and operated at 37 6 1 cpm; each cycle
The Dow film caster from BYK-Gardner, was used originally in this test
method.
consisting of a complete forward and reverse stroke. Adjust
Reagent Chemicals, American Chemical Society Specifications, American
tautnessofthecableswithaspringscaletoapproximately5lb.
Chemical Society, Washington, DC. For suggestions on the testing of reagents not
8.2 Sponge and Holder—Addsufficientweighttotheholder
listed by the American Chemical Society, see Analar Standards for Laboratory
Chemicals, BDH Ltd., Poole, Dorset, U.K., and the United States Pharmacopeia in the form of lead sheets or other flat weights to give a
and N
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D7488-11(2024)(Test Method)
Standard Test Method for Open Time of Latex Paints

SIGNIFICANCE AND USE
5.1 Latex paints dry very quickly which often causes difficulty in final appearance of painted areas, especially paints formulated below 100g/L VOC where lower amounts of solvents are in the formulated latex paint. This method is a means of determining the time available before a test paint cannot be worked into a previously painted area.
SCOPE
1.1 This test method covers a procedure to determine the length of time a latex paint remains “wet” or “open” enough to allow for brush-in and repair.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D2091-96(2024)(Test Method)
Standard Test Method for Print Resistance of Lacquers

SIGNIFICANCE AND USE
4.1 An unsatisfactory appearance can result from pressure deformation of a film inherently too soft or containing residual solvent. This test method is primarily used to evaluate the resistance of a lacquer finish to printing under the conditions of packaging, shipping, and warehousing.
SCOPE
1.1 This test method covers the resistance of dried lacquer films to imprinting.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D8090-24(Test Method)
Standard Test Method for Particle Size Distribution of Paints and Pigments Using Dynamic Imaging Methods

SIGNIFICANCE AND USE
5.1 By following this test method, the particle size, particle size distribution and particle shape of particulates in liquid paint and pigment dispersions can be measured.  
5.2 Particle size, particle size distribution and particle shape have a great effect on the color, opacity and gloss of paints. Reproducing these characteristics is critical to the quality and performance of the paint produced.  
5.3 The dynamic imaging instrument is useful during manufacturing to detect oversize particles as well as the required size distribution of particles in order to provide quality and consistency from batch to batch.
SCOPE
1.1 This test method covers the determination of particle size distribution of liquid paints and pigmented liquid coatings by Dynamic Image Analysis. This method includes the reporting of particles ≥1 µm in size and up to 300 µm in size.
Note 1: Shape is used to classify particles, droplets and bubbles and is not a reporting requirement.
Note 2: The term paint(s) as used in this document includes liquid paint and liquid pigmented coatings.  
1.1.1 Some paints may be too viscous to flow through the imaging instrument without dilution which may be used to help the paint flow as long as significant contamination is not introduced into the paint.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D2369-24(Test Method)
Standard Test Method for Volatile Content of Coatings

SIGNIFICANCE AND USE
4.1 This test method is the procedure of choice for determining volatiles in coatings for the purpose of calculating the volatile organic content in coatings under specified test conditions. The weight percent solids content (nonvolatile matter) may be determined by difference. This information is useful to the paint producer and user and to environmental interests for determining the volatiles emitted by coatings.
SCOPE
1.1 This test method describes a procedure for the determination of the weight percent volatile content of solventborne and waterborne coatings. Test specimens are heated at 110 °C ± 5 °C for 60 min.  
Note 1: The coatings used in these round-robin studies represented air-dried, air-dried oxidizing, heat-cured baking systems, and also included multicomponent paint systems.  
1.2 Sixty minutes at 110 °C ± 5 °C is a general purpose test method based on the precision obtained with both solventborne and waterborne coatings (see Section 9).  
1.3 This test method is viable for coatings wherein one or more parts may, at ambient conditions, contain liquid coreactants that are volatile until a chemical reaction has occurred with another component of the multi-package system.  
Note 2: Committee D01 has run round-robin studies on volatiles of multicomponent paint systems. The only change in procedure is to premix the weighed components in the correct proportions and allow the specimens to stand at room temperature for 1 h prior to placing them into the oven.  
1.4 Test Method D5095 for Determination of the Nonvolatile Content in Silanes, Siloxanes and Silane-Siloxane Blends Used in Masonry Water Repellent Treatments is the standard method for nonvolatile content of these types of materials.  
1.5 Test Methods D5403 for Volatile Content of Radiation Curable Materials is the standard method for determining nonvolatile content of radiation curable coatings, inks and adhesives.  
1.6 Test Method D6419 for Volatile Content of Sheet-Fed and Coldset Web Offset Printing Inks is the method of choice for these types of printing inks.  
1.7 This test method may not be applicable to all types of coatings. Other procedures may be substituted with mutual agreement between the producer and the user.  
Note 3: If unusual decomposition or degradation of the specimen occurs during heating, the actual time and temperature used to cure the coating in practice may be substituted for the time and temperature specified in this test method, subject to mutual agreement between the producer and the user. The U.S. EPA Reference Method 24 specifies 110 °C ± 5 °C for 1 h for coatings.
Note 4: Practice D3960 for Determining Volatile Organic Compound (VOC) Content of Paints and Related Coatings describes procedures and calculations and provides guidance on selecting test methods to determine VOC content of solventborne and waterborne coatings.  
1.8 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D2064-24(Test Method)
Standard Test Method for Print Resistance of Architectural Paints

SIGNIFICANCE AND USE
5.1 The ability of a coating to resist printing is important because its appearance is adversely affected if the smoothness of the coating film is altered by contact with another surface, particularly one with a texture. Interior paint systems, particularly gloss and semigloss on window sills and other horizontal surfaces, often have objects such as flower pots placed on them that may tend to leave a permanent impression. This tendency for a paint film to “print” is a function of the hardness of the coating, the pressure, temperature, humidity, and the duration of time that the object is in contact with the painted surface.
SCOPE
1.1 This test method covers an accelerated procedure for evaluating the print resistance of architectural paints. It differs from print resistance Test Method D2091 in that the latter is concerned with lacquer finishes under packaging, shipping, and warehousing conditions, whereas this test method is concerned with decorative coatings undergoing random on-site pressure contact.  
Note 1: Printing should not be confused with blocking, which is measured in Test Method D4946. The former relates to the indentation of a surface, and the latter, the sticking together of two surfaces.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4213-24(Test Method)
Standard Test Method for Scrub Resistance of Paints by Abrasion Weight Loss

SIGNIFICANCE AND USE
4.1 Interior paint films often become soiled, especially near doorways, windows, and play areas, and frequently need to be cleaned by scrubbing. This test method covers the determination of the relative resistance of paints to erosion when scrubbed.  
4.2 The precision of scrub resistance measurements in absolute physical values, such as Test Methods D2486 (cycles-to-failure or this test method, microlitres per 100 cycles), is poor due to the relatively large effect of subtle and difficult-to-control variables in test conditions. The test method described herein minimizes this problem by using a standard calibration panel as an integral part of each scrubbing operation and relating its weight loss to that of the paint film under test to establish the latter's scrub resistance.
Note 1: The numerical scrub resistance values obtained by this test method are of significance only in relation to the specific calibration panel types with which the value is obtained. Thus, for example, a scrub resistance value of 83 with a Type X calibration panel would be reported as 83X.  
4.3 Results obtained by this test method do not necessarily represent the scrub resistance that might be determined if the test film is allowed to dry before testing appreciably longer than the seven-day period specified herein.  
4.4 Results obtained by this test method do not necessarily relate to ease of soil or stain removal (also referred to as “cleanability” or “cleansability”). To test for those characteristics use Test Methods D3450 and D4828.
FIG. 1 Alignment of Panels for Scrubbing
SCOPE
1.1 This test method covers an accelerated procedure for determining the resistance of paints to erosion caused by scrubbing. (Note: The term wet abrasion is sometimes used for scrubbing, and wet abrasion resistance or scrubbability for scrub resistance.) Although scrub resistance tests are intended primarily for interior coatings, they are sometimes used with exterior coatings as an additional measure of film performance.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D3023-98(2024)(Practice)
Standard Practice for Determination of Resistance of Factory-Applied Coatings on Wood Products to Stains and Reagents

SIGNIFICANCE AND USE
3.1 When used in conjunction with Guide D333, this practice will provide a comprehensive evaluation of resistance to stains caused by chemical reagents and household chemicals.  
3.2 This practice applies only to coatings applied in sufficient quantity to form a continuous film. It is recommended that the dry film thickness of the coating under test be reported.  
3.3 Results from stain tests conducted in accordance with this practice distinguish differences between coatings.
SCOPE
1.1 This practice covers evaluation of clear factory-applied coating systems on wood substrates.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D6441-05(2024)(Test Method)
Standard Test Methods for Measuring the Hiding Power of Powder Coatings

SIGNIFICANCE AND USE
5.1 Contrast ratio at a specified film thickness is a useful hiding power parameter for production control and purchasing specifications.  
5.2 The greater the hiding power, the less coating is required per unit area to obtain adequate hiding. Knowledge of hiding power is therefore important in regard to coating costs and for comparing coating value.
SCOPE
1.1 These test methods determine and report the hiding power of a powder coating with respect to two parameters:  
1.1.1 Test Method A—Contrast Ratio at a given film thickness  
1.1.2 Test Method B—Film thickness at 0.98 (98 %) contrast ratio.
Note 1: The measured parameters follow powder coating industry practice by measuring hiding power in relation to film thickness, rather than the “Spreading Rate” function employed in Test Methods D344 and D2805 and other hiding power test methods.
Note 2: Hiding power is photometrically defined as the spreading rate at 0.98 contrast ratio. See definitions of spreading rate and hiding power in Terminology D16, D2805, and the Paint and Coatings Testing Manual.
Note 3: The contrast ratio 0.98 is conventionally accepted in the coatings industry as representing “complete” hiding for reflectometric hiding power measurements. But visually, as well as photometrically, it is slightly less than complete.  
1.2 These test methods cover the determination of the hiding power of powder coatings applied by electrostatic spraying.  
1.3 These test methods determine hiding power by means of reflectometric and thickness gauge measurements. They are limited to coatings having a minimum CIE-Y reflectance of 15 %.  
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D4958-24(Test Method)
Standard Test Method for Comparison of the Brush Drag of Latex Paints

SIGNIFICANCE AND USE
5.1 As the brush drag of a paint increases, any natural tendency on the part of the painter to overspread the paint is reduced. When all other factors are held constant, increased brush drag will result in greater film thickness with consequent improvement in durability and hiding. Conversely, sometimes it might be preferred to have a lesser degree of brush drag for easier application (that is, the amount of time and effort in applying a paint to a specific area is reduced with a lesser degree of brush drag).  
5.2 This test method provides a standardized brushout procedure for the evaluation of brush drag as an alternative to customary informal ad hoc procedures. Its objective is to maximize the reliability and precision with which this characteristic may be determined.
Note 1: The brush drag of paints is directly related to their high-shear viscosity. There is generally good rank order agreement between results obtained by this method and Test Method D4287. The sensitivity of this brushout method has been found sufficient to distinguish between brushability corresponding to high-shear viscosity differences not lower than 0.3 poise (0.03 Pa.s). Round robin data show that rank order agreement between the brushout and viscometric methods is poor when both latex and solvent-borne paints are part of the same comparison group. This is the result of these two paint types having markedly different rheological properties that affect the relative perception of brush drag.3
SCOPE
1.1 This test method is a standardized brushout procedure for comparing the brush drag of architectural type solvent-borne paints.  
1.2 With slight modifications this test method is also applicable to solvent-borne paints.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D2794-93(2024)(Test Method)
Standard Test Method for Resistance of Organic Coatings to the Effects of Rapid Deformation (Impact)

SIGNIFICANCE AND USE
5.1 Coatings attached to substrates are subjected to damaging impacts during the manufacture of articles and their use in service. In its use over many years, this test method for impact resistance has been found to be useful in predicting the performance of organic coatings for their ability to resist cracking caused by impacts.
SCOPE
1.1 This test method covers a procedure for rapidly deforming by impact a coating film and its substrate and for evaluating the effect of such deformation.  
1.2 This test method should be restricted to testing in only one laboratory when numerical values are used because of the poor reproducibility of the method. Interlaboratory agreement is improved when ranking is used in place of numerical values.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off