ASTM D790-15e1

Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials

SIGNIFICANCE AND USE
5.1 Flexural properties as determined by this test method are especially useful for quality control and specification purposes. They include:  
5.1.1 Flexural Stress (σf)—When a homogeneous elastic material is tested in flexure as a simple beam supported at two points and loaded at the midpoint, the maximum stress in the outer surface of the test specimen occurs at the midpoint. Flexural stress is calculated for any point on the load-deflection curve using equation (Eq 3) in Section 12 (see Notes 5 and 6).
Note 5: Eq 3 applies strictly to materials for which stress is linearly proportional to strain up to the point of rupture and for which the strains are small. Since this is not always the case, a slight error will be introduced if Eq 3 is used to calculate stress for materials that are not true Hookean materials. The equation is valid for obtaining comparison data and for specification purposes, but only up to a maximum fiber strain of 5 % in the outer surface of the test specimen for specimens tested by the procedures described herein.
Note 6: When testing highly orthotropic laminates, the maximum stress may not always occur in the outer surface of the test specimen.5 Laminated beam theory must be applied to determine the maximum tensile stress at failure. If Eq 3 is used to calculate stress, it will yield an apparent strength based on homogeneous beam theory. This apparent strength is highly dependent on the ply-stacking sequence of highly orthotropic laminates.  
5.1.2 Flexural Stress for Beams Tested at Large Support Spans (σf)—If support span-to-depth ratios greater than 16 to 1 are used such that deflections in excess of 10 % of the support span occur, the stress in the outer surface of the specimen for a simple beam is reasonably approximated using equation (Eq 4) in 12.3 (see Note 7).
Note 7: When large support span-to-depth ratios are used, significant end forces are developed at the support noses which will affect the moment in a simple supported...
SCOPE
1.1 These test methods are used to determine the flexural properties of unreinforced and reinforced plastics, including highmodulus composites and electrical insulating materials utilizing a three-point loading system to apply a load to simply supported beam (specimen). The method is generally applicable to both rigid and semi-rigid materials, but flexural strength cannot be determined for those materials that do not break or that do not fail yield in the outer surface of the test specimen within the 5.0 % strain limit.  
1.2 Test specimens of rectangular cross section are injection molded or, cut from molded or extruded sheets or plates, or cut from molded or extruded shapes. Specimens must be solid and uniformly rectangular. The specimen rests on two supports and is loaded by means of a loading nose midway between the supports.  
1.3 Measure deflection in one of two ways; using crosshead position or a deflectometer. Please note that studies have shown that deflection data obtained with a deflectometer will differ from data obtained using crosshead position. The method of deflection measurement shall be reported.  
Note 1: Requirements for quality control in production environments are usually met by measuring deflection using crosshead position. However, more accurate measurement may be obtained by using an deflection indicator such as a deflectometer.
Note 2: Materials that do not rupture by the maximum strain allowed under this test method may be more suited to a 4-point bend test. The basic difference between the two test methods is in the location of the maximum bending moment and maximum axial fiber stresses. The maximum axial fiber stresses occur on a line under the loading nose in 3-point bending and over the area between the loading noses in 4-point bending. A four-point loading system method can be found in Test Method D6272.  
1.4 The values stated in SI units are to be regarded as the standard. The val...

General Information

• Status: Historical
• Publication Date: 30-Nov-2015
• ICS: 29.035.20 - Plastics and rubber insulating materials
• Technical Committee: D20 - Plastics
• Drafting Committee: D20.10 - Mechanical Properties

Relations

• Replaces: ASTM D790-15 - Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials
• Effective Date: 01-Dec-2015
• Referred By: ASTM F2418-19 - Standard Specification for Polypropylene (PP) Corrugated Wall Stormwater Collection Chambers
• Effective Date: 01-Dec-2015
• Referred By: ASTM F2376-23 - Standard Practice for Classification, Design, Manufacture, Construction, and Operation of Water Slide Systems
• Effective Date: 01-Dec-2015
• Referred By: ASTM D707-15(2023) - Standard Classification System and Basis for Specification for Cellulose Acetate Butyrate Molding and Extrusion Compounds (CAB)
• Effective Date: 01-Dec-2015
• Referred By: ASTM F1264-16e1 - Standard Specification and Test Methods for Intramedullary Fixation Devices
• Effective Date: 01-Dec-2015
• Referred By: ASTM G210-13(2023) - Standard Practice for Operating the Severe Wastewater Analysis Testing Apparatus
• Effective Date: 01-Dec-2015
• Referred By: ASTM D4101-17e1 - Standard Classification System and Basis for Specification for Polypropylene Injection and Extrusion Materials
• Effective Date: 01-Dec-2015
• Referred By: ASTM D6263-23 - Standard Specification for Extruded Rods and Bars Made From Rigid Poly(Vinyl Chloride) (PVC) and Chlorinated Poly(Vinyl Chloride) (CPVC)
• Effective Date: 01-Dec-2015
• Referred By: ASTM D7032-21 - Standard Specification for Establishing Performance Ratings for Wood-Plastic Composite and Plastic Lumber Deck Boards, Stair Treads, Guards, and Handrails
• Effective Date: 01-Dec-2015
• Referred By: ASTM D6456-10(2018) - Standard Specification for Finished Parts Made from Polyimide Resin
• Effective Date: 01-Dec-2015
• Referred By: ASTM D3748-14(2019) - Standard Practice for Evaluating High-Density Rigid Cellular Plastics
• Effective Date: 01-Dec-2015
• Referred By: ASTM F3219-19 - Standard Specification for 3 to 30 in. (75 To 750 mm) Polypropylene (PP) Corrugated Single Wall Pipe and Fittings
• Effective Date: 01-Dec-2015
• Referred By: ASTM D3350-21 - Standard Specification for Polyethylene Plastics Pipe and Fittings Materials
• Effective Date: 01-Dec-2015
• Referred By: ASTM C581-20 - Standard Practice for Determining Chemical Resistance of Thermosetting Resins Used in Glass-Fiber-Reinforced Structures Intended for Liquid Service
• Effective Date: 01-Dec-2015
• Referred By: ASTM D5989-18 - Standard Specification for Extruded and Monomer Cast Shapes Made from Nylon (PA)
• Effective Date: 01-Dec-2015

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
´1
Designation: D790 − 15
StandardTest Methods for
Flexural Properties of Unreinforced and Reinforced Plastics
1
and Electrical Insulating Materials
This standard is issued under the fixed designation D790; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1
ε NOTE—Editorially corrected 4.3 in January 2016.
1. Scope* 1.4 The values stated in SI units are to be regarded as the
standard. The values provided in parentheses are for informa-
1.1 These test methods are used to determine the flexural
tion only.
properties of unreinforced and reinforced plastics, including
1.5 The text of this standard references notes and footnotes
highmodulus composites and electrical insulating materials
that provide explanatory material. These notes and footnotes
utilizing a three-point loading system to apply a load to simply
(excluding those in tables and figures) shall not be considered
supported beam (specimen). The method is generally appli-
as requirements of the standard.
cable to both rigid and semi-rigid materials, but flexural
strength cannot be determined for those materials that do not
1.6 This standard does not purport to address all of the
break or that do not fail yield in the outer surface of the test
safety concerns, if any, associated with its use. It is the
specimen within the 5.0 % strain limit.
responsibility of the user of this standard to establish appro-
priate safety and health practices and determine the applica-
1.2 Test specimens of rectangular cross section are injection
bility of regulatory limitations prior to use.
molded or, cut from molded or extruded sheets or plates, or cut
from molded or extruded shapes. Specimens must be solid and
NOTE 3—This standard and ISO 178 address the same subject matter,
but differ in technical content.
uniformly rectangular.The specimen rests on two supports and
is loaded by means of a loading nose midway between the
2. Referenced Documents
supports.
2
2.1 ASTM Standards:
1.3 Measure deflection in one of two ways; using crosshead
D618 Practice for Conditioning Plastics for Testing
positionoradeflectometer.Pleasenotethatstudieshaveshown
D638 Test Method for Tensile Properties of Plastics
that deflection data obtained with a deflectometer will differ
D883 Terminology Relating to Plastics
from data obtained using crosshead position. The method of
D2309 Tests for Rubber Property—Compression Set In-
deflection measurement shall be reported.
3
duced by Nuclear Radiation (Withdrawn 1981)
D4000 Classification System for Specifying Plastic Materi-
NOTE 1—Requirements for quality control in production environments
are usually met by measuring deflection using crosshead position.
als
However, more accurate measurement may be obtained by using an
D4101 Specification for Polypropylene Injection and Extru-
deflection indicator such as a deflectometer.
sion Materials
NOTE 2—Materials that do not rupture by the maximum strain allowed
D5947 Test Methods for Physical Dimensions of Solid
underthistestmethodmaybemoresuitedtoa4-pointbendtest.Thebasic
Plastics Specimens
differencebetweenthetwotestmethodsisinthelocationofthemaximum
D6272 Test Method for Flexural Properties of Unreinforced
bending moment and maximum axial fiber stresses. The maximum axial
fiberstressesoccuronalineundertheloadingnosein3-pointbendingand
and Reinforced Plastics and Electrical Insulating Materi-
over the area between the loading noses in 4-point bending. A four-point
als by Four-Point Bending
loading system method can be found in Test Method D6272.
E4 Practices for Force Verification of Testing Machines
1 2
These test methods are under the jurisdiction of ASTM Committee D20 on For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Plastics and are the direct responsibility of Subcommittee D20.10 on Mechanical contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
Properties. Standards volume information, refer to the standard’s Document Summary page on
Current edition approved Dec. 1, 2015. Published January 2016. Originally the ASTM website.
3
approved in 1970. Last previous edition approved in 2010 as D790 – 10. DOI: The last approved version of this historical standard is referenced on
10.1520/D0790-15. www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
´1
D790 − 15
introduced if Eq 3 is used
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´1
Designation: D790 − 15 D790 − 15
Standard Test Methods for
Flexural Properties of Unreinforced and Reinforced Plastics
1
and Electrical Insulating Materials
This standard is issued under the fixed designation D790; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1
ε NOTE—Editorially corrected 4.3 in January 2016.
1. Scope*
1.1 These test methods are used to determine the flexural properties of unreinforced and reinforced plastics, including
highmodulus composites and electrical insulating materials utilizing a three-point loading system to apply a load to simply
supported beam (specimen). The method is generally applicable to both rigid and semi-rigid materials, but flexural strength cannot
be determined for those materials that do not break or that do not fail yield in the outer surface of the test specimen within the
5.0 % strain limit.
1.2 Test specimens of rectangular cross section are injection molded or, cut from molded or extruded sheets or plates, or cut
from molded or extruded shapes. Specimens must be solid and uniformly rectangular. The specimen rests on two supports and is
loaded by means of a loading nose midway between the supports.
1.3 Measure deflection in one of two ways; using crosshead position or a deflectometer. Please note that studies have shown
that deflection data obtained with a deflectometer will differ from data obtained using crosshead position. The method of deflection
measurement shall be reported.
NOTE 1—Requirements for quality control in production environments are usually met by measuring deflection using crosshead position. However,
more accurate measurement may be obtained by using an deflection indicator such as a deflectometer.
NOTE 2—Materials that do not rupture by the maximum strain allowed under this test method may be more suited to a 4-point bend test. The basic
difference between the two test methods is in the location of the maximum bending moment and maximum axial fiber stresses. The maximum axial fiber
stresses occur on a line under the loading nose in 3-point bending and over the area between the loading noses in 4-point bending. A four-point loading
system method can be found in Test Method D6272.
1.4 The values stated in SI units are to be regarded as the standard. The values provided in parentheses are for information only.
1.5 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes
(excluding those in tables and figures) shall not be considered as requirements of the standard.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
NOTE 3—This standard and ISO 178 address the same subject matter, but differ in technical content.
2. Referenced Documents
2
2.1 ASTM Standards:
D618 Practice for Conditioning Plastics for Testing
D638 Test Method for Tensile Properties of Plastics
D883 Terminology Relating to Plastics
3
D2309 Tests for Rubber Property—Compression Set Induced by Nuclear Radiation (Withdrawn 1981)
D4000 Classification System for Specifying Plastic Materials
1
These test methods are under the jurisdiction of ASTM Committee D20 on Plastics and are the direct responsibility of Subcommittee D20.10 on Mechanical Properties.
Current edition approved Dec. 1, 2015. Published January 2016. Originally approved in 1970. Last previous edition approved in 2010 as D790 – 10. DOI:
10.1520/D0790-15.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
3
The last approved version of this historical standard is referenced on www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
´1
D790 − 15
D4101 Specification for Polypropylene Inje
...