Standard Specification for Tin Mill Products, Black Plate, Double Reduced

ABSTRACT
This specification covers doubled-reduced black plate tin mill products produced from low-carbon cold-reduced steel, furnished in coils and cut sizes, for use predominantly in the manufacture of containers. The product, which is normally supplied with trimmed edges, may be specified "as rolled," without the removal of the rolling solution, and with no additional surface or oiling treatment, or "cleaned" with the rolling solution removed, with or without surface treatment and oiling. The rolling direction must be specified on cut lengths and will be indicated by underlining the slit (rolling width) dimension. Surfaces may polished in either the ground roll finish (base metal finish), or smooth finish with grit lines (7C finish).
SCOPE
1.1 This specification covers double-reduced black plate, produced from low-carbon cold-reduced steel, furnished in coils and cut sizes, for use predominantly in the manufacture of containers. The product may be specified “as rolled,” without the removal of the rolling solution, and with no additional surface or oiling treatment. It may also be specified “cleaned” with the rolling solution removed, with or without surface treatment and oiling. This product is normally supplied with trimmed edges.
1.2 This specification is applicable to orders in either inch-pound units (as A 650) which is supplied in thicknesses 0.0050 in. to 0.0113 in. or SI units [as A 650M] which is supplied in thicknesses from 0.127 to 0.287 mm.
1.3 The values stated in either inch-pound or SI units are to be regarded as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.

General Information

Status
Historical
Publication Date
30-Sep-2008
Current Stage
Ref Project

Relations

Buy Standard

Technical specification
ASTM A650/A650M-03(2008) - Standard Specification for Tin Mill Products, Black Plate, Double Reduced
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview
Technical specification
REDLINE ASTM A650/A650M-03(2008) - Standard Specification for Tin Mill Products, Black Plate, Double Reduced
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: A650/A650M −03(Reapproved 2008)
Standard Specification for
1
Tin Mill Products, Black Plate, Double Reduced
This standard is issued under the fixed designationA650/A650M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 3.1.1.1 As rolled, with the rolling solution not removed,
3.1.1.2 Cleaned, with the rolling solution removed, not
1.1 This specification covers double-reduced black plate,
reoiled,
produced from low-carbon cold-reduced steel, furnished in
3.1.1.3 Cleaned and oiled, with the rolling solution removed
coilsandcutsizes,forusepredominantlyinthemanufactureof
and reoiled,
containers. The product may be specified “as rolled,” without
3.1.1.4 Cleaned, chemically treated and oiled, with the
the removal of the rolling solution, and with no additional
rolling solution removed, chemically treated and reoiled.
surface or oiling treatment. It may also be specified “cleaned”
3.1.2 Thickness (see Specification A623 [Specification
with the rolling solution removed, with or without surface
A623M]),
treatment and oiling. This product is normally supplied with
3.1.3 Width,
trimmed edges.
3.1.4 Length, for cut sizes only,
1.2 This specification is applicable to orders in either
3.1.5 Rolling direction must be specified by underlining the
inch-pound units (as A650) which is supplied in thicknesses
slit (rolling width) for cut sizes (see 4.1),
0.0050 in. to 0.0113 in. or SI units [as A650M] which is
3.1.6 Steel type (see Specification A623 [Specification
supplied in thicknesses from 0.127 to 0.287 mm.
A623M]),
1.3 The values stated in either inch-pound or SI units are to
3.1.7 Mechanical designation requirements (see Specifica-
be regarded as standard.Within the text, the SI units are shown
tion A623 [Specification A623M]),
in brackets. The values stated in each system are not exact
3.1.8 Intended application,
equivalents; therefore, each system must be used indepen-
3.1.9 Quantity, in base boxes [SITAS] (see Note 5),
dently of the other. Combining values from the two systems
3.1.10 On coils, specify minimum or range of acceptable
may result in nonconformance with this specification.
inside diameters. The standard inside diameter is approxi-
mately 16 in. if ordered to Specification A650 [410 mm if
2. Referenced Documents
ordered to Specification A650M]. Coils should be specified to
2
2.1 ASTM Standards: a maximum coil weight if ordered to Specification A650 [mass
A623 Specification for Tin Mill Products, General Require-
if ordered to Specification A650M] or maximum outside
ments diameter,
A623M Specification for Tin Mill Products, General Re-
3.1.11 Packaging,
quirements [Metric]
3.1.12 Special requirements where applicable, and
3.1.13 ASTM specification number and year of issue
3. Ordering Information
(A650/A650M – 88).
3.1 Orders for material under this specification shall include
NOTE 1—A typical ordering description is as follows: 1200 base boxes
the following information, as required and applicable, to 1
double-reduced black plate, cleaned and oiled, 60-lb base weight, 33 ⁄16
adequately describe the desired materials.
in. by coil, MR, DR8 CA, for 401 by 411 can bodies to ASTM
Specification A650/A650M - XX. [250 SITAS, double-reduced black
3.1.1 Name of material (double-reduced black plate),
plate, cleaned and oiled, 0.17 mm thickness, 840 mm by coil, MR, DR8
CA, for 99 mm can bodies to ASTM Specification A650/A650M.]
NOTE 2—A typical ordering description for cut sizes is as follows: 500
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
base boxes, double-reduced black plate, cleaned and oiled, 60-lb base
Stainless Steel and Related Alloysand is the direct responsibility of Subcommittee
1
weight MR, DR8 CA, 7C, 28 by 33 ⁄16 in., for 401 by 411 can bodies in
A01.20 on Tin Mill Products.
accordance with Specification A650/A650M - XX. [100 SITAS, double-
Current edition approved Oct. 1, 2008. Published October 2008. Originally
reduced black plate, cleaned and oiled, MR, DR8 CA, 7C, 0.28 mm
approved in 1971. Last previous edition approved in 2003 as A650/A650M – 03.
thickness, 781 by 773 mm, for 401 by 411 can bodies in accordance with
DOI: 10.1520/A0650_A0650M-03R08.
2 Specification A650M/A 650M - XX.]
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
NOTE 3—The production of coils does not afford the same opportunity
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on for inspection, grading, and sorting as does the production of cut sizes.
the ASTM website
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A 650/A 650M–98 Designation: A 650/A 650M – 03 (Reapproved 2008)
Standard Specification for
1
Tin Mill Products, Black Plate, Double Reduced
This standard is issued under the fixed designationA650/A650M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This specification covers double-reduced black plate, produced from low-carbon cold-reduced steel, furnished in coils and
cut sizes, for use predominantly in the manufacture of containers. The product may be specified “as rolled,’’rolled,” without the
removal of the rolling solution, and with no additional surface or oiling treatment. It may also be specified “cleaned’’“cleaned”
with the rolling solution removed, with or without surface treatment and oiling. This product is normally supplied with trimmed
edges.
1.2 This specification is applicable to orders in either inch-pound units (as A 650) which is supplied in thicknesses from 50-lb
base weight (0.0055 in.) 0.0050 in. to 103-lb base weight (0.0113 in.) 0.0113 in. or SI units [as A 650M] which is supplied in
thicknesses from 0.140.127 to 0.290.287 mm.
1.3 The values stated in either inch-pound or SI units are to be regarded as standard. Within the text, the SI units are shown
in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the
other. Combining values from the two systems may result in nonconformance with this specification.
2. Referenced Documents
2
2.1 ASTM Standards:
A 623 Specification for Tin Mill Products, General Requirements
A 623M Specification for Tin Mill Products, General Requirements [Metric]
3. Ordering Information
3.1 Ordersformaterialunderthisspecificationshallincludethefollowinginformation,asrequiredandapplicable,toadequately
describe the desired materials.
3.1.1 Name of material (double-reduced black plate),
3.1.1.1 As rolled, with the rolling solution not removed,
3.1.1.2 Cleaned, with the rolling solution removed, not reoiled,
3.1.1.3 Cleaned and oiled, with the rolling solution removed and reoiled,
3.1.1.4 Cleaned, chemically treated and oiled, with the rolling solution removed, chemically treated and reoiled.
3.1.2 Thickness (see Specification A 623 [Specification A 623M]),
3.1.3 Width,
3.1.4 Length, for cut sizes only,
3.1.5 Rolling direction must be specified by underlining the slit (rolling width) for cut sizes (see 4.1),
3.1.6 Steel type (see Specification A 623 [Specification A 623M]),
3.1.7 Mechanical designation requirements (see Specification A 623 [Specification A 623M]),
3.1.8 Intended application,
3.1.9 Quantity, in base boxes [SITAS] (see Note 4Note 5),
3.1.10 On coils, specify minimum or range of acceptable inside diameters. The standard inside diameter is approximately 16
in. if ordered to Specification A 650 [410 mm if ordered to Specification A 650M]. Coils should be specified to a maximum coil
weight if ordered to Specification A 650 [mass if ordered to Specification A 650M] or maximum outside diameter,
3.1.11 Packaging,
3.1.12 Special requirements where applicable, and
3.1.13 ASTM specification number and year of issue (A 650/A 650M – 88).
1
ThisspecificationisunderthejurisdictionofASTMCommitteeA-1A01onSteel,StainlessSteel,SteelandRelatedAlloysandisthedirectresponsibilityofSubcommittee
A01.20 on Tin Mill Products.
Current edition approved March 10, 1998.Oct. 1, 2008. Published October 1998.2008. Originally published as A650–71.approved in 1971. Last previous edition
A650–88(1995).approved in 2003 as A 650/A 650M – 03.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book ofASTM Standards
, Vol 01.06.volume information, refer to the standard’s Document Summary page on the ASTM website.
*ASummary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
A 650/A 650M – 03 (2008)
1
NOTE 1—Atypical ordering description is as follows: 1200 base boxes double-reduced black plate, cleaned and oiled, 60-lb base weight, 28 by 33 ⁄16
in. by coil, MR, DR8 CA, for 401 by 411 can bodies to ASTM Specification A650.
A 650/A 650M - XX. [250 SITAS, double-reduced black pl
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.