ASTM D6111-19
(Test Method)Standard Test Method for Bulk Density And Specific Gravity of Plastic Lumber and Shapes by Displacement
Standard Test Method for Bulk Density And Specific Gravity of Plastic Lumber and Shapes by Displacement
SIGNIFICANCE AND USE
5.1 The specific gravity or density of a solid is a property that can be measured conveniently to follow physical changes in a sample, to indicate degree of uniformity among different sampling units or specimens, or to indicate the average density of a large item.
5.2 It is possible that variations in density of a particular plastic lumber or shapes specimen will be due to changes in crystallinity, loss of plasticizer/solvent content, differences in degree of foaming, or to other causes. It is possible that portions of a sample will differ in density because of difference in crystallinity, thermal history, porosity, and composition (types or proportions of resin, plasticizer, pigment, or filler).
Note 2: Reference is made to Test Method D1622/D1622M.
5.3 Density is useful for calculating strength to weight and cost to weight ratios.
5.4 If the cross-sectional area of the specimen is required for future testing on a particular sample, it is acceptable to determine it from a specific gravity measurement, see Eq 5.
SCOPE
1.1 This test method covers the determination of the bulk density and specific gravity of plastic lumber and shapes in their “as manufactured” form. As such, this is a test method for evaluating the properties of plastic lumber or shapes as a product and not a material property test method.
1.2 This test method is suitable for determining the bulk specific gravity or bulk density by immersion of the entire item or a representative cross section in water. This test method involves the weighing of a one piece specimen in water, using a sinker with plastics that are lighter than water. This test method is suitable for products that are wet by, but otherwise not affected by water for the duration of the test.
1.3 Plastic lumber and plastic shapes are currently made predominately from recycled plastics. However, this test method would also be applicable to similar manufactured plastic products made from virgin resins where the product is non-homogeneous in the cross-section.
1.4 The values stated in SI units are to be regarded as standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this test method.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D6111 −19
Standard Test Method for
Bulk Density And Specific Gravity of Plastic Lumber and
1
Shapes by Displacement
This standard is issued under the fixed designation D6111; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 2. Referenced Documents
2
2.1 ASTM Standards:
1.1 This test method covers the determination of the bulk
D618 Practice for Conditioning Plastics for Testing
density and specific gravity of plastic lumber and shapes in
D883 Terminology Relating to Plastics
their “as manufactured” form.As such, this is a test method for
D1622/D1622M Test Method forApparent Density of Rigid
evaluating the properties of plastic lumber or shapes as a
Cellular Plastics
product and not a material property test method.
3
D1898 Practice for Sampling of Plastics (Withdrawn 1998)
1.2 This test method is suitable for determining the bulk
D5033 GuideforDevelopmentofASTMStandardsRelating
specific gravity or bulk density by immersion of the entire item
to Recycling and Use of Recycled Plastics (Withdrawn
3
or a representative cross section in water. This test method
2007)
involves the weighing of a one piece specimen in water, using
D6108 Test Method for Compressive Properties of Plastic
a sinker with plastics that are lighter than water. This test
Lumber and Shapes
method is suitable for products that are wet by, but otherwise
E1 Specification for ASTM Liquid-in-Glass Thermometers
not affected by water for the duration of the test.
E12 Terminology Relating to Density and Specific Gravity
3
of Solids, Liquids, and Gases (Withdrawn 1996)
1.3 Plastic lumber and plastic shapes are currently made
E456 Terminology Relating to Quality and Statistics
predominately from recycled plastics. However, this test
E691 Practice for Conducting an Interlaboratory Study to
method would also be applicable to similar manufactured
Determine the Precision of a Test Method
plastic products made from virgin resins where the product is
E2935 Practice for Conducting Equivalence Testing in
non-homogeneous in the cross-section.
Laboratory Applications
1.4 The values stated in SI units are to be regarded as
3. Terminology
standard.
3.1 Definitions of Terms:
1.5 This standard does not purport to address all of the
3.1.1 Definitions of terms applying to this test method
safety concerns, if any, associated with its use. It is the
appear in Terminology D883 and Guide D5033. For terms
responsibility of the user of this standard to establish appro-
relating to precision and bias and associated issues, the terms
priate safety, health, and environmental practices and deter-
used in this test method are in accordance with the definitions
mine the applicability of regulatory limitations prior to use.
in Terminology E456.
NOTE 1—There is no known ISO equivalent to this test method. 3.1.2 density, bulk—theweightperunitvolumeofamaterial
including voids inherent in material as tested. (Terminology
1.6 This international standard was developed in accor-
D883)
dance with internationally recognized principles on standard-
3.1.2.1 Discussion—Specific gravity at 23/23°C can be
ization established in the Decision on Principles for the
3
converted to density 23°C, g/cm , as follows:
Development of International Standards, Guides and Recom-
23C 3
mendations issued by the World Trade Organization Technical D , g/cm 5 sp gr 23/23°C 30.9976 (1)
Barriers to Trade (TBT) Committee.
3.1.3 plastic lumber, n—a manufactured product made pri-
marily from plastic materials (filled or unfilled), typically used
1 2
This test method is under the jurisdiction ofASTM Committee D20 on Plastics For referenced ASTM standards, visit the ASTM website, www.astm.org, or
and is the direct responsibility of Subcommittee D20.20 on Plastic Lumber (Section contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
D20.20.01). Standards volume information, refer to the standard’s Document Summary page on
Current edition approved May 1, 2019. Published May 2019. Originally the ASTM website.
3
approved in 1997. Last previous edition approved in 2018 as D6111 - 18. DOI: The last approved version of this historical standard is referenced on
10.1520/D6111-19. www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D6111−19
as a building material for purposes similar to those of tradi- 5.3 Density is useful for calculating strength to weight and
tional lumber, which is usual
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D6111 − 18 D6111 − 19
Standard Test Method for
Bulk Density And Specific Gravity of Plastic Lumber and
1
Shapes by Displacement
This standard is issued under the fixed designation D6111; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This test method covers the determination of the bulk density and specific gravity of plastic lumber and shapes in their “as
manufactured” form. As such, this is a test method for evaluating the properties of plastic lumber or shapes as a product and not
a material property test method.
1.2 This test method is suitable for determining the bulk specific gravity or bulk density by immersion of the entire item or a
representative cross section in water. This test method involves the weighing of a one piece specimen in water, using a sinker with
plastics that are lighter than water. This test method is suitable for products that are wet by, but otherwise not affected by water
for the duration of the test.
1.3 Plastic lumber and plastic shapes are currently made predominately from recycled plastics. However, this test method would
also be applicable to similar manufactured plastic products made from virgin resins where the product is non-homogeneous in the
cross-section.
1.4 The values stated in SI units are to be regarded as standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of
regulatory limitations prior to use.
NOTE 1—There is no known ISO equivalent to this test method.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
D618 Practice for Conditioning Plastics for Testing
D883 Terminology Relating to Plastics
D1622D1622/D1622M Test Method for Apparent Density of Rigid Cellular Plastics
3
D1898 Practice for Sampling of Plastics (Withdrawn 1998)
3
D5033 Guide for Development of ASTM Standards Relating to Recycling and Use of Recycled Plastics (Withdrawn 2007)
D6108 Test Method for Compressive Properties of Plastic Lumber and Shapes
E1 Specification for ASTM Liquid-in-Glass Thermometers
3
E12 Terminology Relating to Density and Specific Gravity of Solids, Liquids, and Gases (Withdrawn 1996)
E456 Terminology Relating to Quality and Statistics
E691 Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
E2935 Practice for Conducting Equivalence Testing in Laboratory Applications
1
This test method is under the jurisdiction of ASTM Committee D20 on Plastics and is the direct responsibility of Subcommittee D20.20 on Plastic Lumber (Section
D20.20.01).
Current edition approved June 1, 2018May 1, 2019. Published June 2018May 2019. Originally approved in 1997. Last previous edition approved in 20132018 as
D6111 - 13a.D6111 - 18. DOI: 10.1520/D6111-18.10.1520/D6111-19.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
3
The last approved version of this historical standard is referenced on www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D6111 − 19
3. Terminology
3.1 Definitions:Definitions of Terms:
3.1.1 Definitions of terms applying to this test method appear in Terminology D883 and Guide D5033. For terms relating to
precision and bias and associated issues, the terms used in this test method are in accordance with the definitions in Terminology
E456.
3.1.2 density, bulk—the weight per unit volume of a material including voids inherent in material as tested. (Terminology D883)
3.1.2.1 Discussion—
3
Specific gravity at 23/23°C
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.