ASTM B320-60(2013)
(Practice)Standard Practice for Preparation of Iron Castings for Electroplating
Standard Practice for Preparation of Iron Castings for Electroplating
ABSTRACT
This practice covers preparation of iron castings for electroplating and is intended to assist electroplaters in establishing and maintaining a satisfactory pre-electroplating cycle for malleable iron, gray iron, nodular iron, and white iron castings. It is also intended to indicate certain foundry practices which will facilitate subsequent finishing. The seacoal content of the molding and facing sands should be maintained at the maximum practicable limits to minimize the occlusion of sand in the surfaces of the castings. The steps for the preparation of ferrous castings for electroplating are presented. The various solutions used for the treatment of malleable and gray iron castings should be maintained by chemical analysis so far as is practicable. When the amount of soil is excessive, particularly where no precleaning is done, it may be desirable to double the cleaning and pickling facilities. Where doubling the facilities is impossible or impracticable, similar economies may be obtained to a degree by providing cleaner and pickle tanks with overflow dams, sumps and pumps with which the solution may be recirculated. In electrified tanks removable electrodes should be employed in preference to using the tank as an electrode, to facilitate inspection and cleaning. All immersion rinse tanks should be equipped with dam-type overflows to ensure skimming of oil, grease, and light dirt from the surface of the water. The paper presents the cleaning procedure cycle generally used for racked parts which will subsequently electroplated in still tanks, semiautomatic equipment, and full-automatic equipment. The most reliable test of the effectiveness of the preplating cleaning cycle is the appearance of the electroplated part and its performance in service.
SCOPE
1.1 This practice is intended to assist electroplaters in establishing and maintaining a satisfactory pre-electroplating cycle for malleable iron, gray iron, nodular iron, and white iron castings. It is also intended to indicate certain foundry practices which will facilitate subsequent finishing. Most of the practices that follow have been based on experience with malleable and gray iron. However, since they are related to the other forms, the same practices will probably apply. Nodular iron is also known as spheroidal or ductile iron, which is defined as cast iron with the graphite substantially in spherical shape and substantially free of flake graphite.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in 2.1.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B320 − 60 (Reapproved 2013) Endorsed by American
Electroplaters’ Society
Endorsed by National
Association of Metal Finishers
Standard Practice for
Preparation of Iron Castings for Electroplating
This standard is issued under the fixed designation B320; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3. Foundry Practices
1.1 This practice is intended to assist electroplaters in 3.1 The seacoal content of the molding and facing sands
establishing and maintaining a satisfactory pre-electroplating should be maintained at the maximum practicable limits to
cycle for malleable iron, gray iron, nodular iron, and white iron minimize the occlusion of sand in the surfaces of the castings.
castings.Itisalsointendedtoindicatecertainfoundrypractices
3.2 Upon removal from the molds, castings should be
which will facilitate subsequent finishing. Most of the practices
subjected to an abrading action (such as tumbling, grit blasting,
that follow have been based on experience with malleable and
or shot blasting) to remove as much as practicable of the
gray iron. However, since they are related to the other forms,
occluded molding sand. Residual sand and scale may be
the same practices will probably apply. Nodular iron is also
removed, if necessary, by treatment in various proprietary
known as spheroidal or ductile iron, which is defined as cast
descaling baths. These are usually based on fused caustic soda,
iron with the graphite substantially in spherical shape and
some of which use chemical oxidizing or reducing agents and
substantially free of flake graphite.
others employ electrochemical action as well. This is particu-
1.2 This standard does not purport to address all of the
larly important in the case of castings that will be annealed, to
safety concerns, if any, associated with its use. It is the
prevent the burning on of sand during this operation. Castings
responsibility of the user of this standard to establish appro-
that will be warped or damaged by a blasting operation may be
priate safety and health practices and determine the applica-
pickled in a solution containing 200 to 250 mL/L of sulfuric
bility of regulatory limitations prior to use. Specific precau-
acid to remove occluded molding sand. See Warning state-
tionary statements are given in 2.1.
ment in 2.1.
3.3 Annealed castings should be given an additional abrad-
2. Reagents
ing as described in 3.2 to remove any scale that may have been
2.1 PurityofReagents—All acids and chemicals used in this
formed, as well as graphitic carbon that may be present at the
practice are technical grade. Diluted acid solutions are based
surface.
upon the following assay materials:
4. Nature of Cleaning
Hydrochloric acid (HCl): 31 mass %, density 1.16
g/mL
4.1 The preparation of ferrous castings for electroplating
Hydrofluoric acid (HF): 47 mass %, density 1.186
involves the following basic steps in the order named:
g/mL
4.1.1 The removal of oils, greases, residual polishing and
Sulfuric acid (H SO ): 93 mass %, density 1.83
2 4
g/mL
buffing compounds (if any), and shop dirt by cleaning,
(Warning—Use hydrofluoric acid with extreme care.)
4.1.2 The removal of oxide films and scales and the loos-
(Warning— Sulfuric acid should be slowly added to the
ening of surface carbon by pickling or by salt bath treatment
approximate amount of water required with rapid mixing, and
(see 3.2),
then after cooling, diluted to exact volume.)
4.1.3 The removal of smut caused by 4.1.2, and
4.1.4 Activation for electroplating.
2.2 Purity of Water—Ordinary industrial or potable water
may be used for preparing solutions and rinsing.
4.2 Where excessive amounts of cutting oils used in ma-
chining operations are present, it may be necessary to preclean
the parts before they reach the electroplating room. This may
require the use of organic solvents, vapor degreasers, washing
This practice is under the jurisdiction of ASTM Committee B08 on Metallic
and Inorganic Coatings and is the direct responsibility of Subcommittee B08.02 on
machines of the power-spray type, emulsion cleaners, or
Pre Treatment.
simple alkaline soak tanks. As short a time as possible should
Current edition approved Dec. 1, 2013. Published December 2013. Originally
elapse between this precleaning and the preplating cleaning
approvedin1960.Lastpreviouseditionapprovedin2008asB310–60(2008).DOI:
10.1520/B0320-60R13. cycle so as to prevent rusting of the parts. Where control of the
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
B320 − 60 (2013)
interval is not possible, parts should be left with a slightly 6. Procedure for Racked Parts
alkaline or very thin organic film.
6.1 The following cycle may generally be used for racked
parts which will subsequently be electroplated in still tanks,
5. Cleaning Solutions and Equipment
semiautomatic equipment, and full-automatic equipment:
6.1.1 Precleaning—When castings have been subjected to
5.1 The various solutions used for the treatment of mal-
machining, polishing, buffing, or similar finishing processes, it
leable and gray iron castings should be maintained by chemical
is desirable and frequently essential that lubricants and finish-
analysis so far as is practicable, such as determining the free
ing compounds be removed by precleaning immediately fol-
acid and iron concentrations of the acid baths and using tests
lowing such operations. This is especially important when the
recommended by the manufacturer, the effective components
lubricants contain unsaturated oils which, upon air oxidation,
of the proprietary cleaning solutions.
form films which are extremely difficult to remove. Preclean-
5.2 All solutions should be discarded before they lose their
ing methods as listed in 4.2 may be employed.
effectiveness, based on tests and experience.
6.2 Soak Cleaning—In the event precleaning of a heavily
5.3 Whentheamountofsoilisexcessive,particularlywhere
soiled part is impossible or impracticable, soak cleaning to
no precleaning is done, it may be desirable to double the
loosen oils and greases is recommended. The bath may be
cleaning and pickling facilities.Thus, while the first of any two
either an alkaline solution of such concentration as recom-
particular solutions becomes heavily contaminated, the second mended by the supplier, and operated at a temperature as close
remains relatively clean and effective for further use.When the to boiling as possible, or an emulsion-type cleaner operated as
specified by the supplier. In either case, agitation of the
first of a pair of solutions is discarded, it is replaced by the
second solution and a fresh second solution is prepared. This solution by air or solution pumping, or movement of the part,
will prove beneficial. The time may be 5 min or more.
system also reduces the possible carry-over of contaminants
such as oil and grease into subsequent solutions.
6.3 Rinse—If the soak cleaner used is incompatible with the
subsequent cleaner, a rinse is indicated. The supplier will
5.4 Where doubling the facilities is impossible or
normally suggest whether it is to be warm or cold, although a
impracticable, similar economies may be obtained to a degree
warm rinse (60°C) is usually desirable following alkaline soak
by providing cleaner and pickle tanks with overflow dams,
cleaning. In any case, agitation of the rinse water is desirable;
sumps and pumps with which the solution may be recirculated.
and, in the case of cold-water rinses, a spray upon leaving the
The pump intake should be located approximately half-way
tank is beneficial. The time of rinsing depends in part upon the
down the sump to preclude returning either settled-out solid
shape of the part, but should be no less than 10 s.
dirt or surface oil and grease to the processing tank. The outlet
should be near the bottom of the processing tank at the end
6.4 Anodic Cleaning—The part is made the anode in a
opposite to the overflow dam so as to create some solution
solution of a properly compounded alkaline cleaner of a
turbulence (for mechanical scrubbing benefits) and to ensure concentration recommended by the supplier. The cleaner
flow of contaminated solution to the dam.
should be free-rinsing, and of high conductivity to permit a
current density of 6 to 10A/dm at a tank potential of 6 to 9 V.
5.5 In electrified tanks removable electrodes should be
The solution temperature should be from 90 to 100°C, and the
employed in preference to using the tank as an electrode, to
cleaning time from 1 to 2 min.
facilitate inspection and cleaning. To ensure good circuitry,
6.5 Rinse—Thesupplierofaproprietarycleanerwillusually
positive contacts such as an inverted V hook for round bars
indicatewhetherhisproductrinsesmorefreelyinwarmorcold
should be used. In alkaline cleaner tanks, where clean contact
water. In general, rinsing should be done as described in 6.3,
is often a problem, submerged oversized steel tank rods are
but preferably in a separate tank. Where practicable to do so,
effective.
all rinses should be double rinses; that is, two separate rinses in
5.6 All immersion rinse tanks should be equipped with
succession, with the second cascading into the first for water
dam-type overflows to ensure skimming of oil, grease, and
economy.
light dirt from the surface of the water. Water inlets should be
6.6 Acid Pickling—This stage of the cycle is
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.