A04 - Iron Castings

ABSTRACT
This specification covers hubless cast iron soil pipe and fittings for use in gravity flow applications. These pipe and fittings are intended for non-pressure applications, as the selection of the proper size for sanitary drain, waste, vent, and storm drain systems allows free air space for gravity drainage. The pipe and fittings shall be iron castings suitable for installation and service for sanitary, storm drain, waste, and vent piping applications. The pipe and fittings shall meet all applicable requirements and tests given in this specification. Tensile test and chemical test shall be made to conform to the requirements specified. The pipe and fittings shall be uniformly coated with a material suitable for the purpose that is adherent, not brittle, and without a tendency to scale.
SCOPE
1.1 This specification covers hubless cast iron soil pipe and fittings for use in gravity flow applications. It establishes standards covering material, manufacture, mechanical and chemical properties, dimensions, coating, test methods, inspection, certification, and product marking for hubless cast iron soil pipe and fittings. These pipe and fittings are intended for non-pressure applications, as the selection of the proper size for sanitary drain, waste, vent, and storm drain systems allows free air space for gravity drainage.  
1.2 The EDP/ASA numbers indicated in this section represent a Uniform Industry Code adopted by the American Supply Association (ASA). A group designation prefix, 022, is assigned to hubless products, followed by the four-digit identification assigned to individual items and a check digit. This system has been instituted to facilitate EDP control through distribution channels, and is to be used universally in ordering and specifying product items. Those items with no EDP numbers are either new, special, or transitory and will be assigned numbers on subsequent prints of this specification.  
1.3 This specification covers pipe and fittings of the following patterns and applies to any other patterns that conform with the dimensions found in Tables 1 and 2 and all other applicable requirements given in this specification.2  
1.3.1 Lengths:    
Figures  
EDP/ASA Identification Numbers
for Hubless Pipe  
Fig. 1  
10 ft (3.0 m) in sizes and 5 ft. (1.5 m)
11/2 , 2, 3, 4, 5, 6, 8,
10, 12, and 15 in.  
Fig. 1, Fig. 2  
Method of Specifying Fittings  
Fig. 3  
1.3.2 Fittings:    
Quarter Bend  
Fig. 5  
Quarter Bend, Reducing  
Fig. 6  
Quarter Bend, with Side Opening  
Fig. 7  
Quarter Bend, with Heel Opening  
Fig. 8  
Quarter Bend, Tapped  
Fig. 9  
Quarter Bend, Double  
Fig. 10  
Quarter Bend, Long  
Fig. 11  
Short Sweep  
Fig. 12  
Long Sweep  
Fig. 13  
Long Sweep, Reducing  
Fig. 14  
Fifth Bend  
Fig. 15  
Sixth Bend  
Fig. 16  
Eighth Bend  
Fig. 17  
Eighth Bend, Long  
Fig. 18  
Sixteenth Bend  
Fig. 19  
Sanitary Tee  
Fig. 20  
Sanitary Tee with Side Opening  
Fig. 21  
Sanitary Tee with 2 in. Side Opening R or L/R and L  
Fig. 22  
Sanitary Tee, New Orleans Special with Side Opening  
Fig. 23  
Sanitary Tee with 45° Side Openings and New Orleans  
Fig. 24  
Sanitary Special Tee Tapped  
Fig. 25  
Sanitary Tapped Tee, Horizontal Twin  
Fig. 26  
Sanitary Tapped Tee, Double Vertical  
Fig. 27  
Y Branch  
Fig. 28  
Y Branch, Double  
Fig. 29  
Y Branch, Upright  
Fig. 30  
Upright Y Wide Center Florida Special  
Fig. 31  
Y Branch, Combination 1/8 Bend  
Fig. 32  
Y Branch, Combination 1/8 Bend Double  
Fig. 33  
Sanitary Cross  
Fig. 34  
Sanitary Cross with Side Opening  
Fig. 35  
Sanitary Cross, New Orleans, with Side Openings  
Fig. 36  
Sanitary Cross, New Orleans, with 45° Special and
Regular Side Openings  
Fig. 37  
Sanitary Cross, Tapped  
Fig. 38  
Test Tee  
Fig. 39  
Tapped Extension Piece  
Fig. 40  
Increaser-Reducer  
Fig. 41  
...

SIGNIFICANCE AND USE
4.1 The comparison of observed graphite particles with the structures shown in the charts give only purely descriptive information on the type, distribution, and size of the graphite in the sample being evaluated. It does not indicate, except in a very broad way, the origin of the graphite or the suitability of the iron-carbon alloy for a particular service.
SCOPE
1.1 This test method covers the classification of graphite in cast irons in terms of type, distribution, and size by visual comparison to reference photomicrographs. This test method is intended to be applicable for all iron-carbon alloys containing graphite particles, and may be applied to gray irons, malleable irons, compacted graphite irons, and the ductile (nodular) irons.  
1.2 The reference photomicrographs included in this test method are in no way to be construed as specifications. In an appropriate specification for a specific material where graphite microstructure is an important consideration, this test method may be used as a reference to concisely define the graphite microstructure required.  
1.3 These reference photomicrographs are offered primarily to permit accurate reporting of microstructures of cast irons and to facilitate the comparison of reports by different laboratories or investigators.  
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings that are statically cast in permanent molds. Castings under this specification are classified into a number of grades (A-SA, A-SB, A-SC, A-SS, A-CA, A-CB, A-CC, N-SA, N-SB, N-SC,N-SS, N-CA, N-CB and N-CC) based on the properties of separately cast test bars. The grades are designated A for annealed or N for normalized; followed by an S or a C to designate a solid or a cored casting; followed by an A, B, C, or S to designate the test bar to be poured with the castings. The cast test bar shall be selected on the basis of the controlling section size of the casting and shall have the specified dimensions (diameter and length). Castings may be produced in the as cast state provided the tensile strength and Brinell hardness requirements are met. The chemical composition and heat treatment shall be such as to produce these mechanical requirements as well. A suitable permanent mold design for separately cast test bars is described and the tension test requirements are detailed.
SCOPE
1.1 This specification covers gray iron castings that are statically cast in permanent molds.  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of a casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers austenitic ductile iron castings for compressors, expanders, pumps, valves, and other pressure-containing parts intended primarily for low-temperature service. The castings covered here are Type D-2M, Class 1, Class 2, Class 3, and Class 4. The castings shall be made in the electric-arc furnace, induction furnace, cupola, or any other furnace which is capable of producing castings. Heat and product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, silicon, manganese, nickel, chromium, and phosphorus. The castings shall undergo tension tests and impact tests, and shall conform to the following mechanical requirements: tensile strength, yield strength, elongation, Brinell hardness, and Charpy V-notch.
SCOPE
1.1 This specification2 covers austenitic ductile iron, Type D-2M, Classes 1 and 2, for compressors, expanders, pumps, valves, and other pressure-containing parts intended primarily for low-temperature service.  
1.2 These grades of austenitic ductile iron are characterized by having their graphite substantially in a spheroidal form and free of flake graphite. They are essentially free of carbides and contain sufficient alloy content to produce a stable austenitic matrix down to −423 °F [−252 °C] (liquid hydrogen).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3.1 Within the text, the SI units are shown in brackets.  
1.4 The following precautionary caveat pertains only to the test methods portion, Section 11, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers standard specification for three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges. Chemical analysis shall be performed in each lot and shall conform to the required chemical composition for phosphorous and sulfur. Tension test shall be conducted on each class of gray iron castings and shall conform to the specified values of tensile strength. Tension test specimens shall have threaded ends and shall conform to the prescribed dimensions.
SCOPE
1.1 This specification covers three classes of gray iron for castings intended for use as valve pressure-retaining parts, pipe fittings, and flanges.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
Note 1: The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification deals with abrasion-resistant cast irons used for mining, milling, earth-handling, and manufacturing industries. These alloys may be made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
SCOPE
1.1 This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.  
1.2 Simple and low-alloy white cast irons that consist essentially of iron carbides and pearlite are specifically excluded from this specification.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers malleable irons for castings made by the cupola process. The chemical composition of the iron shall be such as to produce materials that meet the mechanical property requirements. The tensile test methods for malleable iron are presented in details. At least three tensile test specimens shall be cast from a representative ladle of iron from each 4-h pour period during the purchaser's castings were poured. Only one test specimen need be tested to qualify each pour period and heat treatment batch provided the requirements of this specification are met by the test specimen. The microstructure of the malleable iron shall consist of temper carbon nodules uniformly distributed in a ferritic matrix and shall be free from excessive pearlite, massive carbides, and primary graphite. All castings, on visual examination shall be sound and free from obvious shrinkage and porosity.
SCOPE
1.1 This specification covers malleable irons for castings made by the cupola process.  
1.2 Without knowledge of casting geometry and process details, quantitative relationships cannot be stated between the properties of the iron in the various locations of a casting and those of a test bar cast from the same iron.  
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers general requirements and corresponding test methods for castings made of high-silicon molybdenum ferritic iron (SiMo). The requirements are prescribed for castings with microstructures of spheroidal graphite (SG) SiMo iron, compacted graphite (CG) SiMo iron, and mixed graphite or medium-nodularity graphite (MG) SiMo iron. MG iron microstructure is comprised of a mixture of spheroidal and compacted graphite shapes.
SCOPE
1.1 This specification covers castings made of high-silicon molybdenum ferritic iron, commonly known as SiMo. This specification includes castings with microstructures of spheroidal graphite (SG) SiMo iron, compacted graphite (CG) SiMo iron, and mixed graphite or medium-nodularity graphite (MG) SiMo iron. MG iron microstructure comprises a mixture of spheroidal and compacted graphite shapes. This standard specifies the condition, chemical composition, microstructure, and other technical requirements of three grades of ferritic cast irons, specified as SG SiMo, MG SiMo, and CG SiMo.  
1.2 No precise quantitative relationship can be stated between the properties of iron in the various locations of the same casting or between the properties of castings and those of a test specimen cast from the same iron.  
1.3 The values stated in SI units are to be regarded as standard. All chemical compositions are in mass percentage. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers high-silicon iron pipe and pipe fittings intended for corrosion-resistant service for both above- and below-grade construction. The castings shall be true to pattern, reasonable smooth, and free from defects that would make the castings unfit for the use for which they are intended. The material shall conform to the chemical composition requirements specified. All centrifugally cast high-silicon iron pipe shall be supplied in the as-cast condition. All other pipe and fittings shall be supplied in the stress-relieved condition; the stress relieving procedures are presented. Acid-proof joints for hub/plain-end pipe shall require the use of an acid-proof rope packing. No-hub pipe and fittings shall require a special acid resistant mechanical joint coupling. High-silicon iron pipe can be cut with either manual or hydraulic snap cutters. Hydrostatic testing shall be conducted on all castings.
SCOPE
1.1 This specification covers high-silicon iron pipe and pipe fittings intended for corrosion-resistant service for both above- and below-grade construction.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 Pipe and pipe fittings shall be the no-hub (MJ) or the hub and plain-end design.  
1.4 Pipe and pipe fittings shall be of the sizes specified in Table 1 and Table 2 and Figs. 1–71 or other sizes that shall be permitted to conform to the requirements given herein.      
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: Flange dimensions are 150 lb ANSI standard.
Note 2: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.    
Size, in.  
t, in.  
Weight, lb  
Working
Length, ft  
Overall Length  
2  
5/16  
0.31  
7  
7 ft 25/8 in.  
3  
5/16  
0.31  
7  
7 ft 25/8 in.  
4  
5/16  
0.31  
7  
7 ft 25/8 in.  
6  
13/32  
0.40  
7  
7 ft 3 in.  
8  
13/32  
0.40  
7  
7 ft 3 in.  
10  
5/8  
0.62  
7  
7 ft 37/8 in.  
12  
5/8  
0.62  
5  
5 ft 4 in.  
15  
7/8  
0.75  
5  
5 ft 41/8 in.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: Depth of seal on all traps shall be 21/2 in.
Note 2: 1 in. = 25.4 mm.  
Note 1: Depth of seal on all traps shall be 21/2 in.
Note 2: 1 in. = 25.4 mm.  
Note 1: Single hub vent is located on the inlet side. Depth of seal on 8 and 10 in. traps is 3 in. All others 21/2 in.
Note 2: 1 in. = 25.4 mm.  
Note 1: 1 in. = 25.4 mm.  
Note 1: 1 in...

SCOPE
1.1 This specification covers cast iron soil closet flanges for use in gravity flow plumbing drain, waste, and vent sanitary applications. It establishes standards covering material, manufacture, mechanical and chemical properties, coating, test methods, inspection, certification, product markings, dimensions, and dimensional tolerances for closet flanges. These closet flanges are not intended for pressure applications, as the selection of the proper size for sanitary drain, waste, vent, and storm drain systems allows free air space for gravity drainage  
1.2 The EDP/ASA numbers indicated in this section represent a Uniform Industry Code adopted by the American Supply Association (ASA). A group designation prefix, 022, is assigned to hubless products followed by the four-digit identification assigned to individual items and a check digit. This system has been instituted to facilitate EDP control through distribution channels, and is to be used universally in ordering and specifying product items. Those items with no EDP numbers are either new, special, or transitory and will be assigned numbers on subsequent prints of this specification.  
1.3 This specification covers closet flanges of the following patterns (7.1.1) and, when so designated, shall apply to any other patterns that conform with the applicable requirements given in this specification.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the materials, manufacturing practice, and corresponding test methods for special hubless cast iron soil pipe fittings used in a one-pipe combination vent and waste stack unvented for gravity flow applications. These fittings are intended for nonpressure applications, where the selection of the proper size for sanitary, drain, and waste systems allows free air space for gravity drainage. The fittings shall be iron castings suitable for installation and service for sanitary, storm drain, and waste vent piping applications. The castings shall be made of cast iron, produced by an established commercial method that provides control over chemical and mechanical properties.
This specification also covers dimensions, coating, mechanical and chemical tests for gray iron, methods of specifying fittings, sampling, inspection, certification, packaging and package marking, and product marking for hubless cast iron soil pipe fittings.
SCOPE
1.1 This specification covers special hubless cast iron soil pipe fittings for use in a one-pipe combination vent and waste stack unvented for gravity flow applications. It establishes standards covering material, manufacture, mechanical and chemical properties, dimensions, coating, test methods, inspection, certification, and product marking for hubless cast iron soil pipe fittings. These fittings are intended for nonpressure applications, where the selection of the proper size for sanitary, drain, and waste systems allows free air space for gravity drainage.
Note 1: The fittings covered by this standard are special fittings intended to be used for engineered designed systems and will require special approval by the authority having jurisdiction for use. It is not the intent of this standard to endorse or recommend the use of these fittings for these special applications.  
1.2 The EDP/ASA numbers indicated in this section represent a uniform industry code adopted by the American Supply Association (ASA). A group designation prefix, 022, is assigned to hubless products, followed by the four-digit identification assigned to individual items and a check digit. This system has been instituted to facilitate EDP control through distribution channels, and is to be used universally in ordering and specifying product items. Those items with no EDP numbers are new, special, or transitory, and will be assigned numbers on subsequent prints of this specification.  
1.3 This specification covers fittings of the following patterns and applies to any other patterns that conform with the applicable requirements given in this specification.
Note 2: The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.
Note 3: Some sellers of these fittings use the terms “aerator” and “de-aerator” fittings to describe the two types of fittings covered by this standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ductile iron gravity sewer pipe centrifugally cast with push-on joints. This also covers trench load design procedures for both cement-lined pipe and flexible-lined pipe. Maximum depths of cover tables are included for both types of linings. Each pipe shall be subjected to a hydrostatic test and maybe performed either before or after the outside coating and inside coating have been applied, but shall be performed before the application of cement-mortar lining or of a special lining. The standard acceptance tests and additional control tests shall also be performed.
SCOPE
1.1 This specification covers 4 to 64 in. ductile iron gravity sewer pipe, centrifugally cast, with push-on joints. This specification may be used for pipe with other types of joints, as may be agreed upon at the time of purchase.  
1.2 This specification covers trench load design procedures for both cement-lined pipe and flexible-lined pipe. Maximum depth of cover tables are included for both types of linings.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ductile iron castings suitable low temperature service. Castings shall be produced by casting or heat treatment and shall have essentially a ferritic structure that contains no massive carbides. The iron shall conform to the required chemical composition for carbon, silicon, phosphorus, magnesium, manganese, copper, nickel and chromium. The iron shall conform to the required tensile properties such as tensile strength, yield strength and elongation. Graphite contained in the microstructure shall be evaluated and the percentage of each graphite type shall be estimated. The surface of the casting shall be examined visually and shall be free from adhering sand, scale cracks, and hot tears.
SCOPE
1.1 This specification covers ductile iron castings suitable for service at temperatures of −40 °F [–40 °C] and above.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following precautionary statement pertains only to the test methods portion, Section 11, of this specification:  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ductile-iron culvert pipe centrifugally cast. The pipe shall be manufactured of ductile iron that meets the mechanical requirements such as tensile strength, yield strength, elongation, and impact value. The pipe shall be provided with suitable joints, such as push-on or other types of joints that prevent lateral displacement, but plain-end pipe for use with suitable couplings may be furnished. Standard wall thickness and weight values of push-on joint pipe are given. Pressure Class ductile iron pipe in Type 5 trench is illustrated. All pipe shall be coated inside and outside with an asphaltic material. Acceptance tests by tension and Charpy impact testing shall be performed. The standard test specimens for these testing methods are detailed.
SCOPE
1.1 This specification covers 14 to 64 in. ductile iron culvert pipe, centrifugally cast.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following safety hazards caveat pertains only to the test methods portions, Sections 6 and 7, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts such as pressure vessels, the design strength of which is based on the gray iron portion of the cylinder, and for service at the specified temperatures. The melting procedure shall be optional with the foundry and the casting process shall be controlled to produce a metallurgical bond between the chilled white iron exterior and gray iron interior. The chilled white iron exterior shall be made to the specified minimum hardness and the gray iron portion of the roll shall conform to the applicable class as determined by design requirements. The roll shall conform to the tensile strength requirement to be determined by tensile test and shall meet the required thickness. All surfaces shall be machined or ground, or both, prior to the rolls being placed into service.
SCOPE
1.1 This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure-containing parts, the design strength of which is based on the gray iron portion of the cylinder. The castings are suitable for service at temperatures up to 450 °F [232 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards statement pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron and there shall be no gradient of mottled iron these layers. Both the white and the gray irons may be melted by any suitable melting process. The white iron portion of the casting shall be produced by chemistry rather than chilling. A chemical analysis of the white and gray irons shall be taken and the chemical compositions shall be controlled to obtain the required mechanical properties. The white iron (Types I, II, III, and IV) shall conform to the specified Brinell hardness and the gray iron (Class Nos. 20, 25, 30, and 35) shall conform to the specified tensile strength. The minimum thickness of the white iron layer is given. Hardness and tension tests of the cast dual metal shall be performed.
SCOPE
1.1 This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron. There shall be no gradient of mottled iron between the white iron and the gray iron.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.2.1 Within the text, the SI units are shown in brackets.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers malleable iron flanges, pipe fittings, and valve parts, including parts to be assembled for use in railroad, marine, and other heavy duty service applications. The sizes, shapes, and dimensions of the fittings shall conform to the requirements specified. The iron shall be produced under constant control of chemical composition and physical properties. Records of the chemical composition of the iron and of the physical properties of the test specimens shall be systematically made and maintained.
SCOPE
1.1 This specification covers malleable iron flanges, pipe fittings, and valve parts, including parts to be assembled for use in railroad, marine, and other heavy-duty service applications where fittings furnished in accordance with American National Standard for Malleable Iron Threaded Fittings, Classes 150 and 300 (ANSI B16.3) are not considered adequate.  
1.2 Service shall include up to 650 °F (345 °C).2  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standards for castings of ferritic, pearlitic, tempered pearlitic, and tempered martensitic grades of malleable iron used in automotive products and industries. Castings shall be heat treated and shall be of Grades M3210, M4504, M5003, M5503, M7002, and M8501. Materials shall conform to the specified hardness range. Materials shall follow specified microstructure requirements based on distribution of temper-carbon nodules in the metal matrix. All grades shall have a minimum concentration of spheroidal primary carbides in the microstructure.
SCOPE
1.1 This specification covers castings of ferritic, pearlitic, tempered pearlitic, and tempered martensitic grades of malleable iron used in the products of the automotive and allied industries. Castings shall be heat treated to meet this specification.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ductile iron castings that are subsequently heat treated by an austempering process. The chemical composition requirements may be agreed upon between the manufacturer, heat treater, and the purchaser. Requirements for the microstructure constituents such as graphite, ausferrite (acicular ferrite and high carbon, stable austenite), pearlite, and martensite are prescribed. The iron shall conform to the mechanical property requirements including tensile strength, yield strength, elongation, impact energy, and Brinell hardness. Castings shall be heat treated by an austempering process detailed in this specification. The standard specimens for tension and Charpy impact tests are illustrated.
SCOPE
1.1 This specification covers ductile iron castings that are subsequently heat treated by an austempering process as defined in 9.1.  
1.2 The application of the austempering heat treatment extends the range of properties achievable in ductile iron castings.  
1.3 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of castings and those of a test specimen cast from the same iron (see Appendix X1). However, austempering heat treatment will tend to diminish any differences in mechanical properties.  
1.4 The production of castings, machining (if required), and the austempering heat treatments may be performed by different manufacturers, as covered in Section 13. The purchaser should establish by contract agreement, at the time of ordering, the responsibility of the various parties for meeting the specification requirements.  
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5.1 Exception—Within the text, the SI units are shown in brackets.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standards for high-silicon iron castings of Grades 1, 2, and 3 intended for severe environment corrosion-resistant services. The alloy shall be produced by any melting and casting process, or combination of processes that will be capable of meeting the specified contents of carbon, manganese, silicon, chromium, molybdenum, and copper. Reference analysis methods are given for each chemical component. Transverse bend test and hydrostatic test shall be performed. Material shall conform to minimum load at center and minimum deflection at center requirements.
SCOPE
1.1 This specification covers high-silicon cast iron castings intended for corrosion-resistant service.  
1.2 This specification covers three grades as shown in Table 1. Selection of grade depends on the corrosive service to be experienced by the casting. All three grades are suited for application in severe corrosive environments. However, Grade 2 is particularly suited for application in strong chloride environments, and Grade 3 is recommended for impressed current anodes.    
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 The following safety hazards caveat pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ferritic malleable castings for general engineering usage. The castings are classified as Grade 32510. The chemical composition of the iron shall be such as to produce the structural and mechanical properties required by this specification. Tension test may be machined from the standard cast bar to the required dimensions. The microstructure of the malleable iron shall consist of temper carbon nodules distributed through ferritic matrix and shall be free of excessive pearlite, massive carbides, and primary graphite. All castings, on visual examination, shall be sound and free of obvious shrinkage and porosity. The castings shall conform to the dimensions given by this specification.
SCOPE
1.1 This specification2 covers ferritic malleable castings for general engineering usage at temperatures from normal ambient to approximately 400 °C [750 °F].  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers austenitic ductile iron castings used for their resistance to heat, corrosion and wear. The castings shall be melt processed using cupolas, air furnaces, electric furnaces or crucible furnaces. The iron castings shall undergo magnetic permeability test. Samples taken from test coupons, broken test specimens, or castings shall conform to the required chemical compositions of carbon, silicon, manganese, phosphorus, nickel and chromium. Mechanical tests shall be performed wherein the iron casting specimens shall conform to the required values of tensile strength, yield strength, elongation and Brinell hardness.
SCOPE
1.1 This specification covers austenitic ductile iron castings, which are used primarily for their resistance to heat, corrosion, and wear, and for other special purposes.  
1.2 Austenitic ductile iron, also known as austenitic nodular iron or austenitic spheroidal iron, is characterized by having its graphite substantially in a spheroidal form and substantially free of flake graphite. It contains some carbides and sufficient alloy content to produce an austenitic structure.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This index identifies specifications that cover ductile iron pressure pipe suitable for carrying water and other liquids under pressure.  
Note 1: The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.2 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification deals with compacted graphite iron castings. These materials shall be examined metallographically for the acceptance graphite formation. The acceptable graphite formation in the microstructure of the test coupon or casting lug shall contain 80% minimum Type IV graphite. The iron shall conform to the requirements for tensile properties: tensile strength, yield strength, and elongation. Test bars and test coupons shall be cast in dried, baked, or chemically bonded molds consisting of an aggregate of silica sand with appropriate bonders and shall be subjected to the same thermal treatment as the castings they represent.
SCOPE
1.1 This specification covers castings made of compacted graphite iron, which is described as cast iron with the graphite in compacted (vermiform) shapes and essentially free of flake graphite in the bulk of the casting.  
1.2 No precise quantitative relationship can be stated between the properties of iron in the various locations of the same casting and those of a test bar cast from the same iron (see Appendix X1).  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3.1 Exception—The inch-pound units in Figs. 1-3 are standard. SI units are added for information only.  
Note 1: The length of the keel block shall be 6 in. (152 mm).  
FIG. 3 Mold for Modified Keel Block  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers pearlitic malleable iron castings for general. The chemical composition of the iron shall be such as to produce the mechanical properties required by this specification. Hardness test and tensile test shall be made to conform to the requirements specified. The microstructure of the pearlitic malleable iron shall consist of temper carbon nodules uniformly distributed in a matrix of ferrite, pearlite, and tempered transformation products of austenite. All castings on visual examination, shall be sound and free from obvious shrinkage and porosity.
SCOPE
1.1 This specification covers pearlitic malleable iron castings for general engineering usage at temperatures from normal ambient to approximately 750 °F [400 °C].  
1.1.1 For continuous service at temperatures up to 1200 °F [650 °C], design factors should be incorporated to compensate for possible property changes, as demonstrated by Marshall and Sommer2 and by Pearson.3  
1.2 Without knowledge of casting geometry and process details, no quantitative relationship can be stated between the properties of the iron in the various locations of a casting and those of a test bar cast from the same iron.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ductile iron castings for use in pressure containing paper mill dryer rolls. The castings shall be stress relieved through heat treatment and shall undergo chemical analysis and conform to the required chemical composition in total carbon, silicon, phosphorus, and sulfur. Tension test specimens shall be obtained from test coupons poured from the same iron as the castings represented and shall conform to the prescribed mechanical properties such as yield strength, tensile strength, and elongation. Hardness test shall be conducted on the material and shall meet the required Brinell hardness value.
SCOPE
1.1 This specification covers ductile iron castings for use in pressure-containing paper mill dryer rolls at temperatures up to 450 °F [230 °C].  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of a casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3.1 Exception—Within the text, the SI units are shown in brackets.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standard requirements for ductile iron castings for pressure-retaining parts for use at elevated temperatures. Castings are classified by grades based on mechanical property requirements. These iron castings shall meet the specified values of tensile strength, yield strength, elongation and hardness. Chemical analysis shall be performed wherein the casting shall conform to the required chemical composition for carbon, silicon, and phosphorous. The material shall meet the required tensile properties, hardness, and microstructure. The iron casting shall undergo pressure test after machining. The thickness of any repaired section in relation to the size of the plug used shall be indicated. The minimum radius of repaired sections of cylinders or cones in relation to the size of plug used shall not exceed the prescribed limit. Other defective areas may also be repaired by plugging provided the minimum ligament between plugs in adjacent areas shall not be less than twice the distance from the nearest plug. Three Y-blocks shall be utilized as test coupons. The material shall undergo the following test methods: tension test, chemical analysis, yield strength test, and hardness test.
SCOPE
1.1 This specification covers ductile iron castings for pressure-retaining parts for use at elevated temperatures. Castings of all grades are suitable for use up to 450 °F. For temperatures above 450 °F and up to 650 °F, only Grade 60-40-18 castings are suitable (Note 1).  
1.2 Valves, flanges, pipe fittings, pumps, and other piping components are generally manufactured in advance and supplied from stock by the manufacturer, jobber, or dealer.  
1.3 For supplemental casting requirements, Specification A834 may be utilized.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.
Note 1: For service other than as specified in this section, reference should be made to Specification A536 for Ductile Iron Castings.2  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This practice covers the standard materials and installation procedures for polyethylene encasement to be applied to underground installations of ductile iron pipe for water or other liquids. It may also be used for polyethylene encasement of fittings, valves, and other appurtenances to ductile iron pipe systems. Linear low-density and high-density cross-laminated polyethylene films shall be manufactured of virgin polyethylene material, and shall conform to the required group, density, dielectric strength, and volume resistivity specifications. The polyethylene encasement material shall also be in accordance to the tensile strength, elongation, dielectric strength, impact resistance, and propagation tear resistance requirements. The polyethylene encasement shall be installed in such a way that it shall prevent contact between the pipe and the surrounding backfill and bedding material without intending to be a completely airtight or watertight enclosure. The polyethylene film shall be fitted to the contour of the pipe with sufficient slack to prevent stretching the polyethylene bridging irregular surfaces. For installations below the water table or in areas subject to tidal actions, or both, it is recommended that tube-form polyethylene be used with both ends sealed as thoroughly as possible with adhesive tape or plastic tie straps at the joint overlap.
SCOPE
1.1 This practice covers materials and installation procedures for polyethylene encasement to be applied to underground installations of ductile iron pipe. It may also be used for polyethylene encasement of fittings, valves, and other appurtenances to ductile iron pipe systems.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.2.1 Important SI values are provided in brackets. Also, certain important SI values appear without brackets or parentheses.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts of the design strength of which is based on the gray iron portion of the cylinder. The white iron portion of the cylinder shall be made to a minimum hardness and the casting process shall be controlled to produce a metallurgical bond between the two metal layers. All surfaces shall be machined prior to the cylinders being placed into service. The tensile strength of the cast irons shall be measured by tension testing while the thickness of the white cast iron shall be determined by ultrasonic testing.
SCOPE
1.1 This specification2 covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure-containing parts, the design strength of which is based on the gray iron portion of the cylinder. These castings are suitable for service at temperatures up to 450 °F [230 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification describes the properties of devices or assemblies suitable for use as flexible transition couplings for underground drainage and sewer piping systems. Couplings that may include bushings or inserts, and meet the requirements of this specification are suitable for joining plain end pipe or fittings. Couplings shall be permitted to have a center stop, the components shall be designed so that the elastomeric material is compressed to form a hydrostatic seal when the joint is assembled. Assemblies shall be tested in different areas and each component shall conform to specified physical and mechanical requirements, namely: hardness, tensile strength, elongation, heat aging, hardness, ozone resistance, water absorption, and chemical resistance for the elastomeric materials; tension band performance, torque resistance, free running torque for the stainless steel materials; and deflection sealing resistance, and shear loading resistance for the joint assemblies.
SCOPE
1.1 This specification describes the properties of devices or assemblies suitable for use as flexible transition couplings, hereinafter referred to as “couplings,” for underground drainage and sewer piping systems.  
1.2 Flexible transition couplings that conform to the requirements of this standard are suitable for joining plain-end pipe or fittings. The pipe to be joined shall be of similar or dissimilar materials, size, or both.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The ASTM standards referenced herein shall be considered mandatory.  
1.5 The committee with jurisdiction over this standard is not aware of another comparable standard for materials covered in this standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars. The surface of the casting shall be free of adhering sand, scale, cracks, and hot tears, as determined by visual examination. The test bars are designated into S, A, B, and C categories, according to the thickness of its controlling wall section. The casting shall be subjected to a tension test to determine its tensile strength.
SCOPE
1.1 This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars.  
1.1.1 This specification subordinates chemical composition to tensile strength.  
1.2 Castings produced to this specification are graded on the basis of minimum tensile strength obtained in special test coupons designed to standardize cooling rate. The tensile strength developed in certain casting sections may vary from test coupon values (see X1.2).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method deals with gray irons that are to be free of chill in the casting and to chilled irons that are to have a specific depth of chill in the casting. The purpose of the test is to determine the chilling tendencies of cast iron. The two tests are wedge test and chill test. Both tests shall be made in a core which may either be single cores or gang cores and a pouring practice shall be performed. The wedge test is generally better adapted to the higher strength gray irons. The accelerated cooling rate that shall induce the formation of a chill shall be brought about through the design of the test specimen. The chill test is better adapted to the softer grades of gray iron and should be used if the casting have a specified depth of chill. The chill in this type of test shall be induced by casting one edge of the test specimen against a metal or graphite chilled plate or block. Wedge test is simpler than chill test since in the wedge test, maintenance of chill blocks or plates is not necessary.
SCOPE
1.1 These test methods for chill testing apply to gray irons that are to be free of chill in the casting and to chilled irons that are to have a specific depth of chill in the casting. Two test methods for determining the chilling tendencies of cast iron are covered as follows. For many applications, either test method will be satisfactory if test pieces of the proper dimensions are selected.  
1.1.1 Test Method A, Wedge Test—This test is adapted for the higher-strength gray irons. The accelerated cooling rate to induce the formation of a chill is brought about through the design of the test specimen. This test method is simpler than Test Method B since maintenance of chill blocks or plates is not necessary.  
1.1.2 Test Method B, Chill Test—This test is adapted for the softer grades of gray iron and should be used if the casting is to have a specified depth of chill. The chill in this type of test is induced by casting one edge of the test specimen against a metal or graphite chilled plate or block.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered to be part of the standard.  
1.2.1 The metric equivalency charts in Figs. 1 and 2 are provided for information only.  
in.  
mm  
in.  
mm  
in.  
mm  
1/32  
0.8  
3/8  
9.5  
1  
25.4  
1/16  
1.6  
7/16  
12.1  
11/4  
31.8  
3/32  
2.4  
1/2  
12.7  
11/2  
38.1  
1/8  
3.2  
9/16  
14.3  
13/4  
44.4  
3/16  
4.8  
11/16  
17.5  
2  
50.8  
1/4  
6.4  
3/4  
19.0  
21/2  
63.5    
5/16  
7.9  
13/16  
20.6  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
These test methods cover the details of impact testing apparatus, test specimens, and procedures for cast iron, including gray iron, white iron, malleable iron, ductile iron, and austempered ductile iron, but not including chilled rolls or rolls with white iron skins. The Charpy-type impact test shall be employed for testing gray and white irons. The single-blow Charpy impact test for gray and white irons shall be carried out in a pendulum-type impact machine. The test specimens shall have a plain cylindrical form, machined or ground to a smooth finish and shall conform to the specified values of diameter, length, and span. The standard notch Charpy bar impact test specimen shall be employed. Characterization of the fracture toughness of any cast iron should be based upon testing three specimens.
SCOPE
1.1 These test methods for impact testing cover the details of apparatus, test specimens, and procedures for cast iron, including gray iron, white iron, malleable iron, ductile iron, and austempered ductile iron, but not including chilled rolls or rolls with white iron skins.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers material and performance requirements for plasticized PVC compression gaskets used in the connection of residential and commercial vitreous china plumbing fixtures to 2-, 3-, and 4-in. sanitary drain lines. These type gaskets are inserted into and compress against the inside diameter of the sewer pipe, closet or urinal flange while attaching to the vitreous china plumbing fixture with a flexible adhesive. The result is a gas- and watertight seal.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers thermoplastic elastomeric (TPE) gasket materials for preformed elastomeric gaskets used in shielded and non-shielded mechanical couplings for gravity flow drain, waste, and vent (DWV), sewer, sanitary, and storm plumbing systems. Couplings include those that join similar and dissimilar piping sizes and materials. Gaskets shall be made of virgin thermoplastic elastomeric compound containing only clean reworked thermoplastic elastomer material. Gasket materials shall conform to specified values of the following physical requirements: hardness, elongation, tensile strength, heat aging, tear strength, water absorption, ozone resistance, compression set, oil immersion in IRM 903 oil, and stretch test for spliced gaskets.
SCOPE
1.1 This specification covers thermoplastic elastomeric (TPE) gasket materials for preformed elastomeric gaskets used in shielded and non-shielded mechanical couplings. These couplings are used in gravity flow drain, waste, and vent (DWV), sewer, sanitary, and storm plumbing systems. They include couplings to join similar and dissimilar piping sizes and material.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method covers the standard material criteria and test method for compression gaskets used in joining hub and spigot cast iron soil pipe and fittings for sanitary drain, waste, vent, and storm piping applications. The gaskets shall be made of a compound containing a thermoset elastomer and shall consist of one or more sealing ring(s) that compress to provide an airtight and watertight seal. Compression gaskets shall have an integral flange to prevent the gasket from rolling into the hub during installation and shall be designed to permit expansion, contraction, and deflection of assembled piping. The gaskets shall be restrained and subjected to hydrostatic pressure and the joint assembly performance shall be evaluated using the restrained hydrostatic joint testing apparatus wherein a water pressure gauge is used to ensure the accuracy of the test pressures.
SCOPE
1.1 Several different types of compression gaskets are available for use in connection with hub and spigot cast iron soil pipe and fittings. The purpose of this test method is to establish material criteria and test procedures for compression gaskets used in joining hub and spigot cast iron soil pipe and fittings for sanitary drain, waste, vent, and storm drain piping applications in accordance with the general needs of producers, distributors, and users.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the performance of shielded transition couplings using flexible PVC gaskets to join dissimilar DWV pipe and fittings above and below ground. The gaskets shall be permitted to be spliced or molded. The elastomeric gasket shall be free from imperfections and porosity that affects its use and serviceability. Clamps assembly screws or bolts shall not have screw-driver slots. Each coupling shall undergo deflection test, shear test, and unrestrained hydrostatic joint test.
SCOPE
1.1 This specification describes the properties of devices or assemblies suitable for use as mechanical couplings using thermoplastic elastomeric (TPE) gaskets, hereinafter referred to as couplings, for joining drain, waste, and vent (DWV), sewer, sanitary, and storm plumbing systems for above and below ground use.  
1.2 The pipe to be joined shall be of similar or dissimilar materials or size, or both.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The ASTM standards referenced herein shall be considered mandatory.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers cast gray iron soil pipe and fittings for use in gravity flow plumbing, drain, waste and vent sanitary, and storm water applications. These pipe and fittings are not intended for pressure applications. The cast iron shall be produced by an established commercial method that provides control over chemical and physical properties. Castings shall be sound, true to pattern, and of compact close grain that permits drilling and cutting by ordinary methods and its interior surface shall be reasonably smooth and free from defects. Ferrous scrap, pig iron, and any recycled ferrous material to be used in the melting operation shall be screened for radioactivity. Tension test shall include breaking load, machined diameter, and tensile strength. Chemical test shall conform to the chemical composition requirements prescribed for phosphorous, sulfur, chromium, titanium, aluminum, lead, and carbon equivalent. Dimension requirements for hub, spigot, barrel, grooves, water seal and trap, and threads of the pipe and fittings are detailed. The pipe and fittings shall be uniformly coated with a material suitable for the purpose.
SCOPE
1.1 This specification covers cast iron soil pipe and fittings for use in gravity flow plumbing, drain, waste and vent sanitary, and storm water applications. It establishes standards covering material, manufacture, mechanical and chemical properties, coating, test methods, inspection, certification, product markings, dimensions, and dimensional tolerances for extra-heavy and service cast iron soil pipe and fittings. These pipe and fittings are not intended for pressure applications as the selection of the proper size for sanitary drain, waste, vent, and storm drain systems allows free air space for gravity drainage.  
1.2 This specification covers pipe and fittings of the following patterns and, when so designated, shall apply to any other patterns that conform with the dimensions found in Tables 1 and 2 and all other applicable requirements given in this specification.  
1.2.1 Pipe:    
Tables  
Extra heavy, 21/2 ft (0.75 m), 31/2 ft (1.0 m), 5 ft (1.5 m), 10 ft (3.0 m) lengths  
1, 2    
Service, 21/2 ft (0.75 m), 31/2 ft (1.0 m), 5 ft (1.5 m), 10 ft (3.0 m)  
1, 2    
Outside dimensions (for detailing)  
X1.1  
1.2.2 Fittings:    
Tables  
1/4 bends; long 1/4 bends  
3, 4    
1/4 bends, long low-hub  
5    
1/4 bends, low heel; high heel  
6, 7    
1/4 bends, short sweep; long sweep  
8    
1/4 bends, reducing long sweep  
9    
1/5 bends  
10    
1/6 bends  
10    
1/8 bends; long 1/8 bends  
11    
1/16 bends  
11    
Y branches  
12, 13    
Y branches, combination 1/8 bends, single  
14    
Y branches, combination 1/8 bends, double  
14    
Sanitary T branches, single  
15    
Sanitary T branches, double  
15    
Sanitary T branches, cleanout  
16    
Tapped sanitary T branches, single  
17    
Tapped sanitary T branches, double  
17    
T branches, single and double  
18    
Tapped T branches, single  
19    
Tapped T branches, double  
19    
T branches, cleanout  
20    
-45° offset fitting  
21    
Double hubs  
22    
Long double hubs  
22    
Reducers  
23    
Increasers  
24, 25    
P traps  
26, 27    
Deep seal P traps  
28    
Running traps  
29    
Screw plugs (brass)  
30    
Blind plugs  
31    
Iron-body ferrules  
32    
Side inlets  
Fig. 3    
Closet bends  
33    
Tapping bosses  
34    
Reducing 1/4 bend SV  
35    
Combination Y and 1/8 bend  
36    
‘H’ branch fitting  
37  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on ...

ABSTRACT
This specification deals with the performance of shielded transition couplings to join dissimilar DWV pipe and fittings above ground. All steel parts made from round stock shall be 300 series stainless steel. The elastomeric gasket shall consist of one piece and shall have an inside center stop-ring spaced equal distance from the ends. The clamp assembly shall be tested to withstand the stated installation torque. The following shall also be done: deflection test, shear test, and unrestrained hydrostatic joint test.
SCOPE
1.1 This specification covers the performance of shielded transition couplings to join dissimilar DWV pipe and fittings above ground up to and including 15-in. pipe and fittings. This standard is intended to cover reducing couplings used to join pipes and fittings of different sizes, materials, and different outside diameters.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The committee with jurisdiction over this standard is not aware of any comparable standards published by other organizations.  
1.4 The following precaution comment pertains only to the test method portion, Section 7, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings for products of the automobile, truck, tractor and allied industries. The materials shall be classified into eight grades (G1800, G2500, G3000, G3500, G4000, G2500a, G3500b and G3500c) based on the range of their casting hardness, chemical composition and microstructure. Grades G1800 and G2500 shall be annealed. Alloy gray iron automotive camshafts of grade designation G4000d shall conform to the required values of casting hardness, chemical compositions of chromium, molybdenum, and nickel and microstructure. The cam areas of camshaft casting shall undergo selective hardening by flame or induction hardening and shall conform to the required values of depth and surface hardness.
SCOPE
1.1 This specification applies to gray iron castings, cast in sand molds, used in the products of the automobile, truck, tractor, and allied industries.  
1.2 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. The types of castings covered here are: Type 1, Type 1b, Type 2, Type 2b, Type 3, Type 4, Type 5, and Type 6. The materials shall be manufactured by melting in any furnace that produces castings which includes cupolas, air furnaces, electric furnaces, crucible furnaces, and so forth. Heat and product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, silicon, manganese, nickel, copper, chromium, sulfur, and molybdenum. The materials shall undergo a nonmagnetic test which is based on the material's attraction to a small steel horseshoe-type magnet and a magnetic permeability test in the event that nonmagnetic castings are specified. Tension tests shall be performed wherein specimens shall conform to required tensile strength and Brinell hardness.
SCOPE
1.1 This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. Austenitic gray iron is characterized by uniformly distributed graphite flakes, some carbides, and the presence of sufficient alloy content to produce an austenitic structure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the standard common requirements for iron castings to be used for general industrial applications. The castings shall be made in a workman-like manner and shall conform to the dimensions on drawings furnished by the purchaser before manufacture is started. A lot shall consist of one of the following: all the metal from a single heating in a batch-type melting furnace; all the metal poured from two or more batch-type melting furnaces into a single ladle or a single casting; or all the metal poured from a continuous melting furnace for a given period of time between changes in charge, processing conditions, or aim-for chemistry, whichever is the shorter period. Specimens shall undergo tension tests and shall conform to the specified tensile strength requirements. Chemical analysis such as spectrographic methods shall be performed to determine the chemical composition which shall be in accordance to the carbon content requirement of the specimen. Visual inspection shall also be done to ensure that the casting surface is free of adhering sand, scale, cracks, and hot tears.
SCOPE
1.1 This specification covers a group of requirements that are mandatory requirements when used in conjunction with the following iron casting specifications issued by ASTM:    
ASTM Specification2  
A47/A47M  
A48/A48M  
A197/A197M  
A220/A220M  
A278/A278M  
A319  
A395/A395M  
A436  
A439/A439M  
A518/A518M  
A532/A532M  
A536  
A571/A571M  
A823  
A842  
A874/A874M  
A897/A897M  
1.2 This specification also covers a group of supplementary requirements which may be applied to the above specifications as indicated herein. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order.  
1.3 The requirements of the individual material specification, and this general specification, shall prevail in the sequence named.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings exposed to elevated temperatures for non-pressure containing parts such as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots. The three classes of gray iron covered here are: Class I, possessing superior thermal shock resistance; Class II, possessing average thermal shock resistance and moderately good tensile strength; and Class III, possessing a higher tensile strength than either Classes I or II. It is the intention of this specification to classify the irons in accordance with their carbon content equivalent, wherein the equation for its calculation is given herein.
SCOPE
1.1 This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots.  
Note 1: This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400 °F (760 °C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved.  
1.2 The three classes of gray iron covered by this specification are as follows:  
1.2.1 Class I,  possessing superior resistance to thermal shock,  
1.2.2 Class II,  possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30 000 psi (207 MPa) may be expected), and  
1.2.3 Class III,  possessing a higher tensile strength than either Class I or II (tensile strengths as high as 40 000 psi (276 MPa) may be expected).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron for castings suitable for pressure-containing parts at elevated temperatures. Castings shall be stress-relieved by placing them in a suitable furnace and heating them uniformly to the temperatures and for the times specified. Castings to be used at a particular temperature range shall undergo heat treatment and cooling. Chemical analysis shall be performed on each class of castings and shall meet the maximum requirement for carbon, phosphorus and sulfur. Iron used in supplying castings shall conform to the required tensile strength. Separately cast test bars having the required dimensions shall be poured from the same lot as the castings represented. The test bars shall be cast in dried siliceous sand molds maintained at approximately room temperature. Tension test shall be performed on each lot and materials shall conform to the tensile requirements specified.
SCOPE
1.1 This specification2 covers gray iron for castings suitable for pressure-containing parts for use at temperatures up to 650 °F (350 °C).  
1.2 Classes of Iron:  
1.2.1 Castings of all classes are suitable for use up to 450 °F (230 °C). For temperatures above 450 °F and up to 650 °F, only Class 40, 45, 50, 55, and 60 castings are suitable.  
1.2.2 Castings of all classes are suitable for use up to 230 °C. For temperatures above 230 °C and up to 350 °C, only Class 275, 300, 325, 350, 380, and 415 castings are suitable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers the materials and testing of cast iron couplings for joining hubless cast iron soil pipe and fittings for sizes 11/2 to 10 in.  
1.2 It is the purpose of this specification to furnish information as to the characteristics of a particular sleeve type coupling when applied to cast iron soil pipe and fittings manufactured in accordance with Specification A888, latest revision, and CISPI Designation 301, latest revision.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The following precautionary caveat pertains only to the test method portion, Section 8, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers preformed rubber gaskets used to seal joints in cast iron soil pipe and fittings. Gaskets shall be made of a properly vulcanized virgin rubber as the sole elastomer with no scrap or reclaim. Gaskets shall conform to the required physical properties such as hardness, elongation, tensile strength, tear strength and compression. The gasket material shall be tested for effects of heat aging. They shall be tested for weight increase due to water absorption and shall also be tested for volume decrease due to oil absorption. Gasket material shall be tested for ozone resistance.
SCOPE
1.1 This specification covers preformed rubber gaskets used to seal joints in cast iron soil pipe and fittings.  
1.2 The committee with jurisdiction over this standard is not aware of another comparable standard for materials covered in this standard.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The following safety hazards caveat pertains only to the test methods section of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the performance evaluation of heavy duty shielded couplings to join hubless cast iron soil pipe and fittings. Physical properties of all stainless steel and gaskets shall comply with the specified values. Requirements for the elastomeric gasket, clamp assembly, and couplings such as coupling width are detailed. The test apparatus for deflection test, shear test, and unrestrained hydrostatic joint test are illustrated.
SCOPE
1.1 This specification covers the evaluation of the performance of heavy-duty shielded couplings to join hubless cast iron soil pipe and fittings.  
1.2 Couplings covered by this standard shall have nominal dimensions as found in Table 1 and Fig. 1.  
FIG. 1 Typical Center Stop Detail  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The following precautionary caveat pertains only to the test method portion, Section 7, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the materials and testing of shield hubless couplings to join hubless cast iron soil pipe and fittings. Gaskets shall comply with the required physical and chemical properties, dimensions, and material specifications. The rubber gasket shall conform to the required physical requirements such as tensile strength, elongation, durometer, accelerated aging, compression set, oil immersion, ozone cracking, tear resistance, and water absorption. The shield and clamp assembly shall be made of material conforming to the requirements such as tensile strength and hardness. All parts shall be made of 300 series stainless steel, namely: Type 301; Type 304; Type 300; Type 301; and Type 305. The material shall also undergo physical tests like deflection, shear, and unstrained hydrostatic tests.
SCOPE
1.1 This specification covers the materials and testing of shielded hubless couplings to join hubless cast iron soil pipe and fittings.  
1.2 Several different types of hubless couplings are available for use in hubless cast iron sanitary and storm drain, waste, and vent piping applications to connect hubless cast iron soil pipe and fittings by using a sleeve-type, or some other type coupling device. It is the purpose of this specification to furnish information as to the characteristics of one such sleeve-type couplings when applied to cast iron soil pipe and fittings manufactured in accordance with Specification A888, latest revision, and CISPI 301, latest revision.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The committee with jurisdiction over this standard is aware of other comparable standard published by the Cast Iron Soil Pipe Institute, CISPI 310, FM 1680 published by Factory Mutual, and Specification C1540 published by ASTM.  
1.5 The following precautionary caveat pertains only to the test method portion, Section 7, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers ductile iron castings, also known as spheroidal or nodular iron, that is described as cast iron with the graphite substantially spheroidal in shape and essentially free of other forms of graphite. Appropriate heat treatment shall be identified according to grades, as follows: a full ferritizing anneal for 60-40-18; a quench and temper, or normalize and temper, or isothermal heat treatment for 100-70-03 and 120-90-02; and as-cast for 65-45-12 and 80-55-06. Castings shall be tested and conform to specified tensile requirements such as tensile strength, yield strength, and elongation. When indicated in the contract or purchase order, castings shall also adhere to special requirements like hardness, chemical composition, microstructure, pressure tightness, radiographic soundness, magnetic particle inspection dimensions, and surface finish.
SCOPE
1.1 This specification covers castings made of ductile iron, also known as spheroidal or nodular iron, which is described as cast iron with the graphite substantially spheroidal in shape and essentially free of other forms of graphite, as defined in Terminology A644.  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of castings and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.