ASTM

ASTM C182-88(1998)

(Test Method)

Standard Test Method for Thermal Conductivity of Insulating Firebrick

Standard Test Method for Thermal Conductivity of Insulating Firebrick

SCOPE
1.1 This test method supplements Test Method C201, and shall be used in conjunction with that test method to determine the thermal conductivity of insulating firebrick.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are provided for information only.
1.3 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
09-Sep-1998
ICS
81.080 - Refractories
Technical Committee
C08 - Refractories
Drafting Committee
C08.02 - Thermal Properties
Current Stage
Ref Project

Relations

Replaced By
ASTM C182-88(2004) - Standard Test Method for Thermal Conductivity of Insulating Firebrick
Effective Date
01-Sep-2004
Referred By
ASTM C1470-20 - Standard Guide for Testing the Thermal Properties of Advanced Ceramics
Effective Date
10-Sep-1998
Referred By
ASTM C201-93(2019)e1 - Standard Test Method for Thermal Conductivity of Refractories
Effective Date
10-Sep-1998
Referred By
ASTM C417-21 - Standard Test Method for Thermal Conductivity of Unfired Monolithic Refractories
Effective Date
10-Sep-1998
Referred By
ASTM C202-19 - Standard Test Method for Thermal Conductivity of Refractory Brick
Effective Date
10-Sep-1998

Buy Standard

ASTM C182-88(1998) - Standard Test Method for Thermal Conductivity of Insulating FirebrickASTM C182-88(1998) - Standard Test Method for Thermal Conductivity of Insulating Firebrick
PreviousNext
Standard
ASTM C182-88(1998) - Standard Test Method for Thermal Conductivity of Insulating Firebrick
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: C 182 – 88 (Reapproved 1998)
Standard Test Method for
Thermal Conductivity of Insulating Firebrick
This standard is issued under the fixed designation C 182; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 5. Test Sample
1.1 This test method supplements Test Method C 201, and 5.1 The test sample shall be selected and prepared as
shall be used in conjunction with that test method to determine described in the Test Sample and Preparation section of Test
the thermal conductivity of insulating firebrick. Method C 201.
1.2 The values stated in inch-pound units are to be regarded
6. Installation of Thermocouples in Test Specimen
as the standard. The values given in parentheses are provided
6.1 Thermocouples—Calibrated thermocouples shall be
for information only.
1.3 This standard does not purport to address all of the embedded in the test specimen at three points for measuring the
temperature. Chromel-Alumel thermocouples shall be used for
safety problems, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro- temperatures below 1400°F (760°C), and above that tempera-
ture platinum-10 % rhodium/platinum thermocouples shall be
priate safety and health practices and determine the applica-
bility of regulatory limitations prior to use. used. The platinum thermocouples may also be used at the
lower temperatures, but the electromotive force (emf) will not
2. Referenced Documents
be as high as when using base-metal thermocouples. Wire of
2.1 ASTM Standards: AWG 28 (0.320 mm) shall be used for making either type of
C 155 Classification of Insulating Firebrick thermocouple.
C 201 Test Method for Thermal Conductivity of Refracto- 6.2 Installation of Thermocouples— Holes for the thermo-
ries couple wires shall be drilled through the 4 ⁄2-in. (114-mm)
E 220 Method for Calibration of Thermocouples by Com- dimension of the test specimen by the use of a drilling jig so as
parison Techniques to obtain accurate placement of the thermocouples. The three
thermocouples shall be located so that the hot junction of the
3. Significance and Use
first couple is 0.20 in. (5.1 mm) below the hot face of the test
3.1 The thermal conductivity of insulating firebrick (IFB) is
specimen, the junction of the second at the midpoint, and the
a property required for the selection of IFB for a specific junction of the third 0.20 in. above the cold face. The
thermal performance. Users select brick to provide a specified
thermocouple wires leading out from the hot junctions shall be
heat-loss and cold-face temperature without exceeding the located in planes parallel to the calorimeter surface. In order to
temperature limitation of the brick. This test method estab-
have the hot junctions over the center of the calorimeter, they
lishes placement of thermocouples and the positioning of test shall be located on an axis passing through the center of and at
samples in the calorimeter. This test method must be used with
right angles to the 9 by 4 ⁄2-in. (228 by 114-mm) area of the test
Test Method C 201. specimen.
NOTE 1—Insulating firebrick that cannot be prepared to this precision
4. Apparatus
because of the structure of the product, should be prepared in accordance
4.1 The apparatus shall consist of that described in the
with the instructions for fireclay dense refractories.
Apparatus section of Test Method C 201 with the addition of
7. Set-Up of Test Sample and Silicon Carbide Slab
thermocouples, drilling jig, and refractory fiber paper as
1 1
described in Sections 6 and 7.
7.1 Two strips of refractory fiber paper 13 ⁄2 by ⁄2 by 0.02
in. (343 by 13 by 0.5 mm) shall be placed along the 13 ⁄2-in.
1 dimension of the inner guard at the outside edges, as shown in
This test method is under the jurisdiction of ASTM Committee C-8 on
Refractories and is the direct responsibility of Subcommittee C08.02 on Thermal Fig. 1. Twelve strips of refractory fiber paper 2 by ⁄2 by 0.02
Stress Resistance.
in. (51 by 13 by 0.5 mm) shall be placed on the outer guard at
Current edition approved June 24, 1988. Published September 1988. Originally
published as C 182 – 43 T. Last previous edition C 182 – 83.
Annual Book of ASTM Standards, Vol 15.01.
3 4
Annual Book of ASTM Standards, Vol 14.03. Method E 220 specifies calibration procedures for thermocouples.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
C 182
Group 30 or 32 (see Classification C 155) insulating firebrick
cut to measure ⁄8 in. (10 mm) square and 1.00 in. (25.4 mm)
in length.
8. Procedure
8.1 Place the heating chamber in position, start the water
flowing through the calorimeter assembly, and supply the
current to the heating unit. Above a temperature of 1470°F
(800°C), the furnace atmosphere shall contain a minimum of
0.5 % oxygen with zero % combustibles. Take the atmosphere
sample from the furnace chamber proper, preferably as near the
test specimen as possible. Maintain the rate of water flow
through the calorimeter between 120 and 200 g/min, and
determine by weighing the quantity of water collected during a
measured time period. The mass of water collected shall be not
less than 200 g and shall be weighed to an accuracy of 60.5 g.
The rate of flow shall be constant within6 1 % during the test
period.
8.2 Allow the furnace to reach a condition of steady state of
heat flow (test period), which shall be that condition when the
measured flow of heat into the calorime
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C133-24(Test Method)
Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories

SIGNIFICANCE AND USE
3.1 The cold strength of a refractory material is an indication of its suitability for use in refractory construction. (It is not a measure of performance at elevated temperatures.)  
3.2 These test methods are for determining the room temperature flexural strength in three-point bending (cold modulus of rupture) or compressive strength (cold crushing strength), or both, for all refractory products.  
3.3 Considerable care must be used to compare the results of different determinations of the cold crushing strength or modulus of rupture. The specimen size and shape, the nature of the specimen faces (that is, as-formed, sawed, or ground), the orientation of those faces during testing, the loading geometry, and the rate of load application may all significantly affect the numerical results obtained. Comparisons of the results between different determinations should not be made if one or more of these parameters differ between the two determinations.  
3.4 The relative ratio of the largest grain size to the smallest specimen dimension may significantly affect the numerical results. For example, smaller cut specimens containing large grains may present different results than the bricks from which they were cut. Under no circumstances should 6 in. by 1 in. by 1 in. (152 mm by 25 mm by 25 mm) specimens be prepared and tested for materials containing grains with a maximum grain dimension exceeding 0.25 in. (6.4 mm).  
3.5 This test method is useful for research and development, engineering application and design, manufacturing process control, and for developing purchasing specifications.
SCOPE
1.1 These test methods cover the determination of the cold crushing strength and the modulus of rupture (MOR) of dried or fired refractory shapes of all types.  
1.2 The test methods appear in the following sections:    
Test Method  
Sections    
Cold Crushing Strength  
4 to 8  
Modulus of Rupture  
9 to 13  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM C210-95(2024)(Test Method)
Standard Test Method for Reheat Change of Insulating Firebrick

SIGNIFICANCE AND USE
3.1 Insulating firebrick (IFB) are classified by their bulk density and reheat change (see Classification C155). This test method defines thermal stability by measurement of IFB's reheat change following 24 h at a test temperature.  
3.2 Since this test exposes the entire sample to an isothermal temperature condition, the user should be aware that most applications for IFB involve a thermal gradient which may cause the IFB's dimensions to change differentially.
SCOPE
1.1 This test method covers the determination of the permanent linear (and volume) change of insulating firebrick upon reheating under prescribed conditions.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C456-18(2023)(Test Method)
Standard Test Method for Hydration Resistance of Basic Bricks and Shapes

SIGNIFICANCE AND USE
2.1 This test method compares relative resistance to hydration of basic refractory brick and shapes in laboratory tests.  
2.2 This test method allows an estimate to be made of the relative potential for hydration.  
2.3 The test method is used in industry and in some cases it is used for specification purposes.  
2.4 The results must be carefully used as a means of predicting whether or not basic brick or shapes will hydrate under actual conditions of storage or service.
SCOPE
1.1 This test method covers measurement of the relative resistance of basic brick and shapes to hydration.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C492-92(2023)(Test Method)
Standard Test Method for Hydration of Granular Dead-Burned Refractory Dolomite

SIGNIFICANCE AND USE
3.1 The hydration of dead-burned dolomite grains is an important aspect of both manufacturing and using such grains. Moisture from any source will cause the grains to partially disintegrate, eventually making the dead-burned dolomite unfit for use. This test method may prove useful for determining, in a relative manner, which grains are more resistant to hydration than others.  
3.2 Data from one laboratory might help in establishing internal limits for determining whether a particular batch of grain is suitable for refractory production. However, this test method takes great care to run, and is not recommended as a quality control test. Possibly, a specification might be developed between two parties if sufficient care in establishing the bias between the laboratories is carried out.
SCOPE
1.1 This test method covers the determination of the amount of hydration of a granular dead-burned refractory dolomite when exposed to moist air.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM C1223-19(2023)(Test Method)
Standard Test Method for Testing of Glass Exudation from AZS Fusion-Cast Refractories

SIGNIFICANCE AND USE
4.1 This test method was developed for use both by manufacturers as a process control tool for the production of AZS fusion-cast refractories, and by glass manufacturers in the selection of refractories and design of glass-melting furnaces.  
4.2 The results may be considered as representative of the potential for an AZS refractory (specifically, in the tested region) to contribute to glass defect formation during the furnace production operation.  
4.3 The procedures and results may be applied to other refractory types or applications (that is, reheat furnace skid rail brick) in which glass exudation is considered to be important.
SCOPE
1.1 This test method covers a procedure for causing the exudation of a glassy phase to the surface of fusion-cast specimens by subjecting them to temperatures corresponding to glass furnace operating temperatures.  
1.2 This test method covers a procedure for measuring the exudate as the percent of volume increase of the specimen after cooling.  
1.3 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3.1 Exception—The balance required for this test method uses only SI units (Section 7).  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C134-95(2023)(Test Method)
Standard Test Methods for Size, Dimensional Measurements, and Bulk Density of Refractory Brick and Insulating Firebrick

SIGNIFICANCE AND USE
3.1 Refractory brick are used as modular units in furnace construction and should not deviate significantly from the intended configuration with respect to size, bulk density, flat surfaces, and right angles. These test methods are particularly suited for use under field conditions and provide a means to determine whether the brick meets the requirements considered necessary to assure a satisfactory refractory construction.
SCOPE
1.1 These test methods cover procedures for measuring size, dimensional measurement, bulk density, warpage, and squareness of rectangular dense refractory brick and rectangular insulating firebrick. More precise determination of bulk density of refractory brick can be made by Test Methods C20. Stack height is generally determined only for dense refractories.  
Note 1: Test Methods C830 and Test Method C914 are also used to determine bulk density of refractory brick, by different procedures.  
1.2 The test methods appear in the following order:    
Sections    
Size and Bulk Density  
4 through 7    
Warpage of Refractory Brick  
8 through 10    
Squareness of Refractory Brick  
11 through 14  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C987-10(2023)(Test Method)
Standard Test Method for Vapor Attack on Refractories for Furnace Superstructures

SIGNIFICANCE AND USE
2.1 This test method provides a guide for evaluating the resistance of refractories in glass-melting furnace superstructures to vapor attack. This test method may also be useful for evaluating refractories in other applications where vapor attack occurs.  
2.2 An electric-heated furnace is recommended. Water vapor and other atmospheric components in a gas- or fuel-fired furnace may participate in the chemical and physical reactions being studied. Results may differ, therefore, depending upon the nature and type of firing employed.  
2.3 The degree of correlation between this test method and service performance is not fully determinable. This is intended to be an accelerated test method that generates a substantial degree of reaction in a relatively short amount of time. This acceleration may be accomplished by changing the composition and/or concentration of the reactants, increasing temperatures, or by performing the test in an isothermal environment.  
2.4 Since the test method may not accurately simulate the service environment, observed results of this test method may not be representative of those found in service. It is imperative that the user understand and consider how the results of this test method may differ from those encountered in service. This is particularly likely if the reaction products, their nature, or their degree differ from those normally found in the actual service environment.  
2.5 It is incumbent upon the user to understand that this is an aggressive, accelerated test method and to be careful in interpreting the results. If, for example, the reaction species have never been found in a real-world furnace, then this test method should not necessarily be considered valid to evaluate the refractory in question.
SCOPE
1.1 This test method covers a procedure for comparing the behavior of refractories in contact with vapors under conditions intended to simulate the environment within a glass-melting or other type of furnace when refractories are exposed to vapors from raw batch, molten glass, fuel, fuel contaminants, or other sources. This procedure is intended to accelerate service conditions for the purpose of determining in a relatively short time the interval resistance to fluxing, bloating, shrinkage, expansion, mineral conversion, disintegration, or other physical changes that may occur.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C830-00(2023)(Test Method)
Standard Test Methods for Apparent Porosity, Liquid Absorption, Apparent Specific Gravity, and Bulk Density of Refractory Shapes by Vacuum Pressure

SIGNIFICANCE AND USE
3.1 Apparent porosity, water absorption, apparent specific gravity, and bulk density are primary properties of refractory shapes. These properties are widely used in the evaluation and comparison of product quality and as part of the criteria for selection and use of refractory products in a variety of industrial applications. These test methods are used for determining any or all of these properties and are particularly useful for testing hydratable products.  
3.2 These test methods are primary standard methods that are suitable for use in quality control, research and development, establishing criteria for and evaluating compliance with specifications, and providing data for design purposes.  
3.3 Fundamental assumptions inherent in these test methods are:  
3.3.1 The test specimens conform to the requirements for size, configuration, and original faces,  
3.3.2 The open pores of the test specimens are fully impregnated with liquid during the vacuum-pressure treatment, and  
3.3.3 The blotting of the saturated test specimens is performed as specified in a consistent and uniform manner to avoid withdrawing liquid from the pores.  
3.3.4 Deviation from any of these assumptions adversely affects the test results.  
3.4 In laboratory studies involving castable specimen, a bias was noted between formed 2 in. by 2 in. by 2 in. (50 mm by 50 mm by 50 mm) and specimens quartered from larger 9 in. by 4.5 in. by 2.5 in. (228 mm by 114 mm by 64 mm) cast specimens. Additionally, an error in the apparent porosity determination was found on castables whenever the specimens were heated to 1500 °F (816 °C) and then exposed to water as a saturation media. The error was attributed to reactivity of cement with water and subsequent re-hydration of cement phases. The higher the cement level of the castable, the greater the error noted. It was concluded that an error in porosity values could occur for refractory materials having a potential to form hydrated species with water. T...
SCOPE
1.1 These test methods cover the determination of the following properties of refractory shapes:  
1.1.1 Apparent porosity,  
1.1.2 Liquid absorption,  
1.1.3 Apparent specific gravity, and  
1.1.4 Bulk density.  
1.2 These test methods are applicable to all refractory shapes except those that chemically react with both water and mineral spirits. When testing a material capable of hydration or other chemical reaction with water but which does not chemically react with mineral spirits, mineral spirits is substituted for water and appropriate corrections for the density differences are applied when making calculations.  
1.3 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3.1 Exception—The apparatus used in this standard is only available in SI units.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Test Methods C20 cover procedures for testing properties of refractories that are not attacked by water.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C604-18(2023)(Test Method)
Standard Test Method for True Specific Gravity of Refractory Materials by Gas-Comparison Pycnometer

SIGNIFICANCE AND USE
4.1 The true specific gravity of a material is the ratio of its true density, determined at a specific temperature, to the true density of water, determined at a specific temperature. Thus, the true specific gravity of a material is a primary property which is related to chemical and mineralogical composition.  
4.2 This test method is particularly useful for hydratable materials that are not suitable for test with Test Method C135.  
4.3 For refractory raw materials and products, the true specific gravity is a useful value for: classification, detecting differences in chemical composition between supposedly like samples, indicating mineralogical phases or phase changes, calculating total porosity when the bulk density is known, and for any other test method that requires this value for the calculation of results.  
4.4 This test method is a primary standard method which is suitable for use in specifications, quality control, and research and development. It can also serve as a referee test method in purchasing contracts or agreements.  
4.5 Fundamental assumptions inherent in this test method are the following:  
4.5.1 The sample is representative of the material in general,  
4.5.2 The total sample has been reduced to the particle size specified,  
4.5.3 No contamination has been introduced during processing of the sample,  
4.5.4 The ignition of the sample has eliminated all free or combined water without inducing sintering or alteration,  
4.5.5 An inert gas (helium) has been used in the test, and  
4.5.6 The test method has been conducted in a meticulous manner.  
4.5.7 Deviation from any of these assumptions negates the usefulness of the results.  
4.6 In interpreting the results of this test method, it must be recognized that the specified sample particle size is significantly finer than specified for Test Method C135. Even this finer particle size for the sample does not preclude the presence of some closed pores, and the amount of residual close...
SCOPE
1.1 This test method covers the determination of the true specific gravity of solid materials, and is particularly useful for materials that easily hydrate which are not suitable for test with Test Method C135. This test method may be used as an alternate for Test Methods C135, C128, and C188 for determining true specific gravity.  
1.2 Units—The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.2.1 Exception—In 7.3, the equivalent SI unit is expressed in parentheses.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1407-23(Practice)
Standard Practice for Calculating Areas, Volume, and Linear Change of Refractory Shapes

SIGNIFICANCE AND USE
3.1 Fireclay steel-teeming nozzles and sleeves are classified by volume reheat change. Bloating of some refractories results in irregular reheat dimensions, which are difficult to measure. This practice determines the volume without depending upon physical linear measurements.  
3.2 Blast furnace checkers that have irregular cross-sections are classified by “creep properties.” This practice determines the average cross-sectional area.
SCOPE
1.1 This practice covers the methods of calculating areas, volumes, and linear changes of irregularly shaped refractory specimens.  
1.2 The specimens must have a constant cross-sectional area over a length (L).  
1.3 The values stated in SI units are to be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
  • Standard
    2 pages
    English language
    sale 15% off