ASTM C31/C31M-10

(Practice)

Standard Practice for Making and Curing Concrete Test Specimens in the Field

Standard Practice for Making and Curing Concrete Test Specimens in the Field

SIGNIFICANCE AND USE
This practice provides standardized requirements for making, curing, protecting, and transporting concrete test specimens under field conditions.  
If the specimens are made and standard cured, as stipulated herein, the resulting strength test data when the specimens are tested are able to be used for the following purposes:  
Acceptance testing for specified strength,  
Checking adequacy of mixture proportions for strength, and  
Quality control.  
If the specimens are made and field cured, as stipulated herein, the resulting strength test data when the specimens are tested are able to be used for the following purposes:  
Determination of whether a structure is capable of being put in service,
Comparison with test results of standard cured specimens or with test results from various in-place test methods,  
Adequacy of curing and protection of concrete in the structure, or  
Form or shoring removal time requirements.
SCOPE
1.1 This practice covers procedures for making and curing cylinder and beam specimens from representative samples of fresh concrete for a construction project.  
1.2 The concrete used to make the molded specimens shall be sampled after all on-site adjustments have been made to the mixture proportions, including the addition of mix water and admixtures. This practice is not satisfactory for making specimens from concrete not having measurable slump or requiring other sizes or shapes of specimens.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. (WarningFresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed skin and tissue upon prolonged exposure. )
1.5 The text of this standard references notes which provide explanatory material. These notes shall not be considered as requirements of the standard.

General Information

Status
Historical
Publication Date
30-Sep-2010
ICS
91.100.30 - Concrete and concrete products
Technical Committee
C09 - Concrete and Concrete Aggregates
Drafting Committee
C09.61 - Testing for Strength
Current Stage
Ref Project

Relations

Replaced By
ASTM C31/C31M-12 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
Effective Date
01-Jul-2012

Buy Standard

ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the FieldASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
PreviousNext
Standard
ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the FieldREDLINE ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
PreviousNext
Standard
REDLINE ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the FieldREDLINE ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
PreviousNext
Standard
REDLINE ASTM C31/C31M-10 - Standard Practice for Making and Curing Concrete Test Specimens in the Field
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:C31/C31M–10
Standard Practice for
1
Making and Curing Concrete Test Specimens in the Field
This standard is issued under the fixed designation C31/C31M; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* C138/C138M Test Method for Density (Unit Weight),
Yield, and Air Content (Gravimetric) of Concrete
1.1 This practice covers procedures for making and curing
C143/C143M Test Method for Slump of Hydraulic-Cement
cylinder and beam specimens from representative samples of
Concrete
fresh concrete for a construction project.
C172 Practice for Sampling Freshly Mixed Concrete
1.2 The concrete used to make the molded specimens shall
C173/C173M Test Method for Air Content of Freshly
be sampled after all on-site adjustments have been made to the
Mixed Concrete by the Volumetric Method
mixture proportions, including the addition of mix water and
C231 Test Method for Air Content of Freshly Mixed Con-
admixtures. This practice is not satisfactory for making speci-
crete by the Pressure Method
mens from concrete not having measurable slump or requiring
C330 Specification for Lightweight Aggregates for Struc-
other sizes or shapes of specimens.
tural Concrete
1.3 The values stated in either SI units or inch-pound units
C403/C403M Test Method for Time of Setting of Concrete
are to be regarded separately as standard. The values stated in
Mixtures by Penetration Resistance
each system may not be exact equivalents; therefore, each
C470/C470M Specification for Molds for Forming Con-
system shall be used independently of the other. Combining
crete Test Cylinders Vertically
values from the two systems may result in non-conformance
C511 Specification for Mixing Rooms, Moist Cabinets,
with the standard.
Moist Rooms, and Water Storage Tanks Used in the
1.4 This standard does not purport to address all of the
Testing of Hydraulic Cements and Concretes
safety concerns, if any, associated with its use. It is the
C617 Practice for Capping Cylindrical Concrete Specimens
responsibility of the user of this standard to establish appro-
C1064/C1064M Test Method for Temperature of Freshly
priate safety and health practices and determine the applica-
Mixed Hydraulic-Cement Concrete
bility of regulatory limitations prior to use. (Warning—Fresh
4
2.2 American Concrete Institute Publication:
hydraulic cementitious mixtures are caustic and may cause
CP-1 Concrete Field Testing Technician, Grade I
chemical burns to exposed skin and tissue upon prolonged
2
309R Guide for Consolidation of Concrete
exposure. )
1.5 The text of this standard references notes which provide
3. Terminology
explanatory material. These notes shall not be considered as
3.1 For definitions of terms used in this practice, refer to
requirements of the standard.
Terminology C125.
2. Referenced Documents
4. Significance and Use
3
2.1 ASTM Standards:
4.1 This practice provides standardized requirements for
C125 Terminology Relating to Concrete and Concrete Ag-
making, curing, protecting, and transporting concrete test
gregates
specimens under field conditions.
4.2 If the specimens are made and standard cured, as
1
stipulated herein, the resulting strength test data when the
This practice is under the jurisdiction of ASTM Committee C09 on Concrete
and Concrete Aggregates and is the direct responsibility of Subcommittee C09.61
specimens are tested are able to be used for the following
on Testing for Strength.
purposes:
Current edition approved Oct. 1, 2010. Published November 2010. Originally
4.2.1 Acceptance testing for specified strength,
approved in 1920. Last previous edition approved in 2009 as C31/C31M–09. DOI:
10.1520/C0031_C0031M-10. 4.2.2 Checking adequacy of mixture proportions for
2
See Section on Safety Precautions, Manual ofAggregate and Concrete Testing,
strength, and
Annual Book of ASTM Standards, Vol. 04.02.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
4
Standards volume information, refer to the standard’s Document Summary page on Available fromAmerican Concrete Institute (ACI), P.O. Box 9094, Farmington
the ASTM website. Hills, MI 48333-9094, http://www.aci-int.org.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C31/C31M–10
TABLE 1 Tamping Rod Diameter Requirements
4.2.
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:C31/C31M–09 Designation:C31/C31M–10
Standard Practice for
1
Making and Curing Concrete Test Specimens in the Field
This standard is issued under the fixed designation C31/C31M; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This practice covers procedures for making and curing cylinder and beam specimens from representative samples of fresh
concrete for a construction project.
1.2 The concrete used to make the molded specimens shall be sampled after all on-site adjustments have been made to the
mixture proportions, including the addition of mix water and admixtures. This practice is not satisfactory for making specimens
from concrete not having measurable slump or requiring other sizes or shapes of specimens.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed
2
skin and tissue upon prolonged exposure. )
1.5 The text of this standard references notes which provide explanatory material. These notes shall not be considered as
requirements of the standard.
2. Referenced Documents
3
2.1 ASTM Standards:
C125 Terminology Relating to Concrete and Concrete Aggregates
C138/C138M Test Method for Density (Unit Weight), Yield, and Air Content (Gravimetric) of Concrete
C143/C143M Test Method for Slump of Hydraulic-Cement Concrete
C172 Practice for Sampling Freshly Mixed Concrete
C173/C173M Test Method for Air Content of Freshly Mixed Concrete by the Volumetric Method
C231 Test Method for Air Content of Freshly Mixed Concrete by the Pressure Method
C330 Specification for Lightweight Aggregates for Structural Concrete
C403/C403M Test Method for Time of Setting of Concrete Mixtures by Penetration Resistance
C470/C470M Specification for Molds for Forming Concrete Test Cylinders Vertically
C511 Specification for Mixing Rooms, Moist Cabinets, Moist Rooms, and Water Storage Tanks Used in the Testing of
Hydraulic Cements and Concretes
C617 Practice for Capping Cylindrical Concrete Specimens
C1064/C1064M Test Method for Temperature of Freshly Mixed Hydraulic-Cement Concrete
4
2.2 American Concrete Institute Publication:
CP-1 Concrete Field Testing Technician, Grade I
309R Guide for Consolidation of Concrete
3. Terminology
3.1 For definitions of terms used in this practice, refer to Terminology C125.
1
This practice is under the jurisdiction of ASTM Committee C09 on Concrete and Concrete Aggregates and is the direct responsibility of Subcommittee C09.61 on
Testing for Strength.
Current edition approved MayOct. 1, 2009.2010. Published May 2009.November 2010. Originally approved in 1920. Last previous edition approved in 20082009 as
C31/C31M–08b.C31/C31M–09. DOI: 10.1520/C0031_C0031M-109.
2
See Section on Safety Precautions, Manual of Aggregate and Concrete Testing, Annual Book of ASTM Standards, Vol. 04.02.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
Available from American Concrete Institute (ACI), P.O. Box 9094, Farmington Hills, MI 48333-9094, http://www.aci-int.org.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C31/C31M–10
4. Significance and Use
4.1 This practice provides standardized requirements for making, curing, protecting, and transporting concrete test specimens
under field conditions.
4.2 If the specimen
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:C31/C31M–09 Designation:C31/C31M–10
Standard Practice for
1
Making and Curing Concrete Test Specimens in the Field
This standard is issued under the fixed designation C31/C31M; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This practice covers procedures for making and curing cylinder and beam specimens from representative samples of fresh
concrete for a construction project.
1.2 The concrete used to make the molded specimens shall be sampled after all on-site adjustments have been made to the
mixture proportions, including the addition of mix water and admixtures. This practice is not satisfactory for making specimens
from concrete not having measurable slump or requiring other sizes or shapes of specimens.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed
2
skin and tissue upon prolonged exposure. )
1.5 The text of this standard references notes which provide explanatory material. These notes shall not be considered as
requirements of the standard.
2. Referenced Documents
3
2.1 ASTM Standards:
C125 Terminology Relating to Concrete and Concrete Aggregates
C138/C138M Test Method for Density (Unit Weight), Yield, and Air Content (Gravimetric) of Concrete
C143/C143M Test Method for Slump of Hydraulic-Cement Concrete
C172 Practice for Sampling Freshly Mixed Concrete
C173/C173M Test Method for Air Content of Freshly Mixed Concrete by the Volumetric Method
C231 Test Method for Air Content of Freshly Mixed Concrete by the Pressure Method
C330 Specification for Lightweight Aggregates for Structural Concrete
C403/C403M Test Method for Time of Setting of Concrete Mixtures by Penetration Resistance
C470/C470M Specification for Molds for Forming Concrete Test Cylinders Vertically
C511 Specification for Mixing Rooms, Moist Cabinets, Moist Rooms, and Water Storage Tanks Used in the Testing of
Hydraulic Cements and Concretes
C617 Practice for Capping Cylindrical Concrete Specimens
C1064/C1064M Test Method for Temperature of Freshly Mixed Hydraulic-Cement Concrete
4
2.2 American Concrete Institute Publication:
CP-1 Concrete Field Testing Technician, Grade I
309R Guide for Consolidation of Concrete
3. Terminology
3.1 For definitions of terms used in this practice, refer to Terminology C125.
1
This practice is under the jurisdiction of ASTM Committee C09 on Concrete and Concrete Aggregates and is the direct responsibility of Subcommittee C09.61 on
Testing for Strength.
Current edition approved MayOct. 1, 2009.2010. Published May 2009.November 2010. Originally approved in 1920. Last previous edition approved in 20082009 as
C31/C31M–08b.C31/C31M–09. DOI: 10.1520/C0031_C0031M-109.
2
See Section on Safety Precautions, Manual of Aggregate and Concrete Testing, Annual Book of ASTM Standards, Vol. 04.02.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
Available from American Concrete Institute (ACI), P.O. Box 9094, Farmington Hills, MI 48333-9094, http://www.aci-int.org.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C31/C31M–10
4. Significance and Use
4.1 This practice provides standardized requirements for making, curing, protecting, and transporting concrete test specimens
under field conditions.
4.2 If the specimen
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1293/C1293M-23(Test Method)
Standard Test Method for Determination of Length Change of Concrete Due to Alkali-Silica Reaction

SIGNIFICANCE AND USE
4.1 Alkali-silica reaction is a chemical interaction between some siliceous constituents of concrete aggregates and hydroxyl ions (1).5 The concentration of hydroxyl ion within the concrete is predominantly controlled by the concentration of sodium and potassium (2).  
4.2 This test method is intended to evaluate the potential of an aggregate or combination of an aggregate with pozzolan or slag to expand deleteriously due to any form of alkali-silica reactivity (3, 4).  
4.3 If testing an aggregate with pozzolan or slag, the results are used to establish minimum amounts of the specific pozzolan or slag needed to prevent deleterious expansion. Pozzolan or slag from a specific source can be tested individually or in combination with pozzolan or slag from other sources.  
4.4 When selecting a sample or deciding on the number of samples for test, it is important to recognize the variability in lithology of material from a given source, whether a deposit of sand, gravel, or a rock formation of any origin. For specific advice, see Guide C295/C295M.  
4.5 This test method is intended for evaluating the behavior of aggregates portland cement in concrete with an alkali (alkali metal oxide) content of 5.25 kg/m3 [8.85 lb/yd3] or in concrete containing pozzolan or slag with an alkali content proportionally reduced from 5.25 kg/m3 [8.85 lb/yd3] Na2O equivalent by the amount of pozzolan or slag replacing portland cement. This test method assesses the potential for deleterious expansion of concrete caused by alkali-silica reaction, of either coarse or fine aggregates, from tests performed under prescribed laboratory curing conditions that will probably differ from field conditions. Thus, actual field performance will not be duplicated due to differences in concrete alkali content, wetting and drying, temperature, other factors, or combinations of these (5).  
4.6 Results of tests conducted on an aggregate as described herein should form a part of the basis for a decision as ...
SCOPE
1.1 This test method covers the determination of the susceptibility of an aggregate or combination of an aggregate with pozzolan or slag for participation in expansive alkali-silica reaction by measurement of length change of concrete prisms.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as the standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.
Note 1: Sieve size is identified by its standard designation in Specification E11. The alternative designation given in parentheses is for information only and does not represent a different standard sieve size.  
1.3 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM C617/C617M-23(Practice)
Standard Practice for Capping Cylindrical Concrete Specimens

SIGNIFICANCE AND USE
3.1 This practice describes procedures for providing plane surfaces on the ends of freshly molded concrete cylinders, hardened cylinders, or drilled concrete cores when the end surfaces do not conform with the planeness and perpendicularity requirements of applicable standards. Practice C1231/C1231M describes alternative procedures using unbonded caps or pad caps.
SCOPE
1.1 This practice covers apparatus, materials, and procedures for capping freshly molded concrete cylinders with neat cement and hardened cylinders and drilled concrete cores with high-strength gypsum paste or sulfur mortar.  
1.2 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific precaution statements see 4.3.1 and 6.2.4.1.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM C873/C873M-23(Test Method)
Standard Test Method for Compressive Strength of Concrete Cylinders Cast in Place in Cylindrical Molds

ABSTRACT
This test method covers the determination of strength of cylindrical concrete specimens that have been molded in place using special molds attached to formwork. A concrete cylinder mold assembly consisting of a mold and a tubular support member is fastened within the concrete formwork prior to placement of the concrete. The elevation of the mold upper edge is adjusted to correspond to the plane of the finished slab surface. The mold support prevents direct contact of the slab concrete with the outside of the mold and permits its easy removal from the hardened concrete. Strength of cast-in-place cylinders may be used for various purposes, such as estimating the load-bearing capacity of slabs, determining the time of form and shore removal, and determining the effectiveness of curing and protection. Consolidation of concrete in the mold may be varied to simulate the conditions of placement. Internal vibration of concrete in the mold is prohibited except under special circumstances.
SIGNIFICANCE AND USE
4.1 Cast-in-place cylinder strength relates to the strength of concrete in the structure due to the similarity of curing conditions because the cylinder is cured within the slab. However, due to differences in moisture condition, degree of consolidation, specimen size, and length-diameter ratio, there is not a unique relationship between the strength of cast-in-place cylinders and cores of the same age. When cores can be drilled undamaged and tested in the same moisture condition as the cast-in-place cylinders, the strength of the cylinders can be expected to be on average 10 % higher than the cores at ages up to 91 days for specimens of the same size and length-diameter ratio.4  
4.2 Strength of cast-in-place cylinders may be used for various purposes, such as estimating the load-bearing capacity of slabs, determining the time of form and shore removal, and determining the effectiveness of curing and protection.
SCOPE
1.1 This test method covers the determination of strength of cylindrical concrete specimens that have been molded in place using special molds attached to formwork. This test method is limited to use in slabs where the depth of concrete is from 125 mm to 300 mm [5 in. to 12 in.].  
1.2 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C1758/C1758M-23(Practice)
Standard Practice for Fabricating Test Specimens with Self-Consolidating Concrete

SIGNIFICANCE AND USE
4.1 Existing practices and test methods for fabricating fresh concrete test specimens are not suited to SCC. This practice provides requirements and procedures for fabricating test specimens with SCC having a slump flow of 500 mm [20 in.] or greater.
SCOPE
1.1 This practice covers procedures for fabricating test specimens in the laboratory or field using a representative sample of fresh self-consolidating concrete (SCC). This practice is applicable to SCC with a nominal maximum aggregate size up to 25 mm [1 in.] and a slump flow of 500 mm [20 in.] or greater. If the slump flow is less than 500 mm [20 in.] follow the fabrication procedures described in the standard for which the test specimen is required.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed skin and tissue upon prolonged exposure.2)  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM C1621/C1621M-17(2023)(Test Method)
Standard Test Method for Passing Ability of Self-Consolidating Concrete by J-Ring

SIGNIFICANCE AND USE
5.1 This test method provides a procedure to determine the passing ability of self-consolidating concrete. This test method is applicable for laboratory use in comparing the passing ability of different concrete mixtures. It is also applicable in the field as a quality control test.  
5.2 The difference between the slump flow and J-Ring flow is an indication of the passing ability of the concrete. A difference less than 25 mm [1 in.] indicates good passing ability and a difference greater than 50 mm [2 in.] indicates poor passing ability. The orientation of the mold for the J-Ring test and for the slump flow test without the J-Ring shall be the same.  
5.3 This test method is limited to self-consolidating concrete with nominal maximum size of aggregate of up to 25 mm [1 in.].
SCOPE
1.1 This test method covers determination of the passing ability of self-consolidating concrete (SCC) by using the J-Ring in combination with a mold.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C1231/C1231M-23(Practice)
Standard Practice for Use of Unbonded Caps in Determination of Compressive Strength of Hardened Cylindrical Concrete Specimens

SIGNIFICANCE AND USE
4.1 This practice provides for using an unbonded capping system in testing hardened concrete cylinders made in accordance with Practices C31/C31M or C192/C192M, or cores obtained in accordance with Test Method C42/C42M in lieu of the capping systems described in Practice C617/C617M.  
4.2 The elastomeric pads deform in initial loading to conform to the contour of the ends of the test specimens and are restrained from excessive lateral spreading by plates and metal rings to provide a uniform distribution of load from the bearing blocks of the testing machine to the ends of the concrete or mortar specimens.
SCOPE
1.1 This practice covers requirements for a capping system using unbonded caps for testing concrete cylinders molded in accordance with Practice C31/C31M or C192/C192M, or cores obtained in accordance with Test Method C42/C42M. Unbonded neoprene caps of a defined hardness are permitted to be used for testing for a specified maximum number of reuses without qualification testing up to a certain concrete compressive strength level. Above that strength, level neoprene caps will require qualification testing. Qualification testing is required for all elastomeric materials other than neoprene regardless of the concrete strength.  
1.2 Unbonded caps are not to be used for acceptance testing of concrete with compressive strength below 10 MPa [1500 psi ] or above 80 MPa [12 000 psi].  
1.3 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined. Combining values from the two systems may result in non-conformance with the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Concrete specimens tested with unbonded caps rupture more violently than comparable specimens tested with bonded caps. The safety precautions given in the Manual of Aggregate and Concrete Testing are recommended.2)  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C142/C142M-17(2023)(Test Method)
Standard Test Method for Clay Lumps and Friable Particles in Aggregates

SIGNIFICANCE AND USE
4.1 This test method is of primary significance in determining the acceptability of aggregate with respect to the requirements of Specification C33/C33M.
SCOPE
1.1 This test method covers the approximate determination of clay lumps and friable particles in aggregates.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
Note 1: Sieve sizes openings are identified by their Specification E11 designation with their alternative Specification E11 designation given in parentheses for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM C1701/C1701M-17a(2023)(Test Method)
Standard Test Method for Infiltration Rate of In Place Pervious Concrete

SIGNIFICANCE AND USE
5.1 Tests performed at the same location across a span of years may be used to detect a reduction of infiltration rate of the pervious concrete, thereby identifying the need for remediation.  
5.2 The infiltration rate obtained by this method is valid only for the localized area of the pavement where the test is conducted. To determine the infiltration rate of the entire pervious pavement multiple locations must be tested and the results averaged.  
5.3 The field infiltration rate is typically established by the design engineer of record and is a function of the design precipitation event.  
5.4 This test method does not measure the influence on in-place infiltration rate due to sealing of voids near the bottom of the pervious concrete slab. Visual inspection of concrete cores is the best approach for determining sealing of voids near the bottom of the pervious concrete slab.
SCOPE
1.1 This test method covers the determination of the field water infiltration rate of in place pervious concrete.
Note 1: For permeable unit pavement systems, Test Method C1781/C1781M should be used. Test Method C1781/C1781M is functionally identical to this test method but includes added provisions for positioning and securing the test ring to a discontinuous surface. Both tests methods give comparable results  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The text of this standard references notes that provide explanatory material. These notes shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C173/C173M-23(Test Method)
Standard Test Method for Air Content of Freshly Mixed Concrete by the Volumetric Method

SIGNIFICANCE AND USE
4.1 This test method covers the determination of the air content of freshly mixed concrete. It measures the air contained in the mortar fraction of the concrete, but is not affected by air that may be present inside porous aggregate particles.  
4.1.1 Therefore, this is the appropriate test to determine the air content of concretes containing lightweight aggregates, air-cooled slag, and highly porous or vesicular natural aggregates.  
4.2 This test method requires the addition of sufficient isopropyl alcohol, when the meter is initially being filled with water, so that after the first or subsequent rollings little or no foam collects in the neck of the top section of the meter. If more foam is present than that equivalent to 2 % air above the water level, the test is declared invalid and must be repeated using a larger quantity of alcohol. Addition of alcohol to dispel foam any time after the initial filling of the meter to the zero mark is not permitted.  
4.3 The air content of hardened concrete may be either higher or lower than that determined by this test method. This depends upon the methods and amounts of consolidation effort applied to the concrete from which the hardened concrete specimen is taken; uniformity and stability of the air bubbles in the fresh and hardened concrete; accuracy of the microscopic examination, if used; time of comparison; environmental exposure; stage in the delivery, placement and consolidation processes at which the air content of the unhardened concrete is determined, that is, before or after the concrete goes through a pump; and other factors.
SCOPE
1.1 This test method covers determination of the air content of freshly mixed concrete containing any type of aggregate, whether it be dense, cellular, or lightweight.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The inch-pound units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The text of this standard references notes and footnotes that provide explanatory information. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM C138/C138M-23(Test Method)
Standard Test Method for Density (Unit Weight), Yield, and Air Content (Gravimetric) of Concrete

ABSTRACT
This test method covers determination of the density of freshly mixed concrete and gives formulas for calculating the unit weight, yield or relative yield, cement content, and air content of the concrete. Yield is defined as the volume of concrete produced from a mixture of known quantities of the component materials. The test method shall use the following apparatuses: balance or scale; tamping rod, which is a round straight steel rod having the tamping end rounded to a hemispherical tip; internal vibrator which may have rigid of flexible shafts, preferably powered by electric motors; measure, which is a cylindrical container made of steel or other suitable metal specified herein; strike-off plate; mallet; and scoop of a size large enough so each amount of concrete obtained from the sampling receptacle is representative and small enough so it is not spilled during placement in the measure.
SCOPE
1.1 This test method covers determination of the density (see Note 1) of freshly mixed concrete and gives formulas for calculating the yield, cement content, and air content of the concrete. Yield is defined as the volume of concrete produced from a mixture of known quantities of the component materials.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
Note 1: Unit weight was the previous terminology used to describe the property determined by this test method, which is mass per unit volume.  
1.3 The text of this test method refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.(Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off