CEN/TS 14751:2004
(Main)Welding - Use of time-of-flight diffraction technique (TOFD) for examination of welds
Welding - Use of time-of-flight diffraction technique (TOFD) for examination of welds
This document specifies the application of the time-of-flight diffraction (TOFD) technique for the semi-, or fully- automated ultrasonic testing of fusion welded joints in metallic materials equal to and above 6 mm thickness. It is primarily intended for use on full penetration welded joints of simple geometry in plates, pipes, and vessels, where both the weld and parent material are low alloyed carbon steel. Where specified and appropriate, TOFD may also be used on other types of materials that exhibit low ultrasonic attenuation (especially that due to scatter).
Where material dependent ultrasonic parameters are specified in this document, they are based on steels having a sound velocity of (5920 ± 50) m/s for longitudinal waves, and (3255 ± 30) m/s for transverse waves. This has to be taken into account when examining materials with a different velocity.
This document makes reference to the basic pre-standard ENV 583 6 and provides guidance on the specific capabilities and limitations of TOFD for the detection, location, sizing and characterisation of discontinuities in fusion welded joints. TOFD may be used as a stand-alone method or in combination with other NDT methods or techniques, both for manufacturing inspection (pre-service) and for in-service inspection.
This document specifies four examination levels (A, B, C, D) corresponding to an increasing level of inspection reliability. Guidance on the selection of examination levels is provided.
This document permits assessment of indications for acceptance purposes. This assessment is based on the evaluation of transmitted, reflected and diffracted ultrasonic signals within a generated TOFD image.
This document does not include acceptance levels for discontinuities.
Schweißverbindungen - Anwendung der Beugungslaufzeittechnik (TOFD) für die Prüfung von Schweißverbindungen
Diese Technische Spezifikation legt die Anwendung der Beugungslaufzeit- (TOFD-)Technik bei der halb- oder vollautomatischen Ultraschallprüfung von Schmelzschweißverbindungen in metallischen Werkstoffen mit einer Dicke von mindestens 6 mm fest. Sie ist insbesondere für die Anwendung an durchgeschweißten Verbindungen einfacher Geometrie in Platten, Rohren und Behältern vorgesehen, bei denen Schweißnaht und Grundwerkstoff aus niedriglegiertem Kohlenstoffstahl bestehen. Sofern festgelegt und sinnvoll, darf die TOFD-Technik auch auf andere Werkstoffarten angewendet werden, die eine geringe Ultraschallschwächung aufweisen (dies gilt insbesondere für die durch Streuung verursachte Ultraschallschwächung).
Sofern in dieser Technischen Spezifikation werkstoffabhängige Ultraschallparameter festgelegt sind, beruhen diese auf Stählen mit einer Schallgeschwindigkeit von (5 920 ± 50) m/s für Longitudinalwellen und (3 255 ± 30) m/s für Transversalwellen. Dies ist bei der Prüfung von Werkstoffen mit anderer Schallgeschwin-digkeit zu berücksichtigen.
Die vorliegende Technische Spezifikation nimmt Bezug auf die Vornorm ENV 583-6 und liefert einen Leitfaden hinsichtlich der besonderen Fähigkeiten und Einschränkungen der TOFD-Technik beim Auffinden, der Ortung, dem Ausmessen und der Charakterisierung von Inhomogenitäten in Schmelzschweißverbindungen. Die TOFD-Technik darf selbständig oder in Verbindung mit weiteren Verfahren oder Techniken der zerstörungsfreien Prüfung sowohl für die Prüfung während der Herstellung (vor der Inbetriebnahme) als auch für die Prüfung während des Betriebes angewendet werden.
Diese Technische Spezifikation legt vier Prüfklassen (A, B, C, D) fest, die einem zunehmenden Grad der Zuverlässigkeit der Prüfung entsprechen. Ein Leitfaden für die Auswahl der Prüfklassen wird angeführt.
Die vorliegende Technische Spezifikation erlaubt die Beurteilung von Anzeigen zum Zwecke der Bestimmung der Zulässigkeit. Diese Beurteilung beruht auf der Bewertung übertragener,
Soudage - Utilisation de la technique de diffraction des temps de vol (méthode TOFD) pour le contrôle des soudures
Le présent document spécifie l�application de la technique de diffraction des temps de vol (méthode TOFD)
pour le contrôle par ultrasons semi-automatique ou entièrement automatique des assemblages soudés par
fusion de matériaux métalliques d�épaisseur égale ou supérieure à 6 mm. Cette technique est essentiellement
destinée à être utilisée sur des joints soudés à pleine pénétration de géométrie simple sur plaques, tubes et
récipients dans lesquels le métal de base et le métal fondu sont tous les deux constitués d�acier au carbone
faiblement allié. Dans le cas où son utilisation est spécifiée et qu�elle s�avère appropriée, la méthode TOFD
peut également être utilisée sur d�autres types de matériaux qui présentent une atténuation ultrasonore faible
(spécialement celle due à la dispersion).
Lorsque les paramètres ultrasonores dépendant du matériau sont spécifiés dans le présent document, ils sont
basés sur les aciers qui présentent une vitesse de propagation sonore de (5920 ± 50) m/s pour les ondes
longitudinales et (3 255 ± 30) m/s pour les ondes transversales. Cette condition doit être prise en compte lors
de l�examen de matériaux ayant des vitesses de propagation différentes.
Le présent document fait référence à la pré-norme de base ENV 583-6 et fournit des lignes directrices sur les
possibilités et les limitations spécifiques de la méthode TOFD pour la détection, la localisation, le
dimensionnement et la caractérisation des discontinuités dans les joints soudés par fusion. La méthode TOFD
peut être utilisée de manière autonome ou en combinaison avec d�autres méthodes ou techniques de contrôle
non-destructif, aussi bien pour le contrôle de fabrication (avant service) que pour le contrôle en cours de
service.
Varjenje – Uporaba tehnike zvočne poti (TOFD) za preiskavo zvarov
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
01-januar-2005
9DUMHQMH±8SRUDEDWHKQLNH]YRþQHSRWL 72)' ]DSUHLVNDYR]YDURY
Welding - Use of time-of-flight diffraction technique (TOFD) for examination of welds
Schweißverbindungen - Anwendung der Beugungslaufzeittechnik (TOFD) für die Prüfung
von Schweißverbindungen
Soudage - Utilisation de la technique de diffraction des temps de vol (méthode TOFD)
pour le contrôle des soudures
Ta slovenski standard je istoveten z: CEN/TS 14751:2004
ICS:
25.160.40 Varjeni spoji in vari Welded joints
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
TECHNICAL SPECIFICATION
CEN/TS 14751
SPÉCIFICATION TECHNIQUE
TECHNISCHE SPEZIFIKATION
November 2004
ICS 25.160.40
English version
Welding - Use of time-of-flight diffraction technique (TOFD) for
examination of welds
Soudage - Utilisation de la technique de diffraction des Schweißverbindungen - Anwendung der
temps de vol (méthode TOFD) pour le contrôle des Beugungslaufzeittechnik (TOFD) für die Prüfung von
soudures Schweißverbindungen
This Technical Specification (CEN/TS) was approved by CEN on 11 July 2004 for provisional application.
The period of validity of this CEN/TS is limited initially to three years. After two years the members of CEN will be requested to submit their
comments, particularly on the question whether the CEN/TS can be converted into a European Standard.
CEN members are required to announce the existence of this CEN/TS in the same way as for an EN and to make the CEN/TS available
promptly at national level in an appropriate form. It is permissible to keep conflicting national standards in force (in parallel to the CEN/TS)
until the final decision about the possible conversion of the CEN/TS into an EN is reached.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,
Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36 B-1050 Brussels
© 2004 CEN All rights of exploitation in any form and by any means reserved Ref. No. CEN/TS 14751:2004: E
worldwide for CEN national Members.
Contents Page
Foreword.4
1 Scope .5
2 Normative references .5
3 Terms and definitions .6
4 General remarks on the capabilities of the technique.6
5 Examination levels.7
6 Information required prior to testing .7
6.1 Items to be defined by specification.7
6.2 Specific information required by the operator before testing .8
6.3 Written test instruction .8
7 Requirements for personnel and equipment .8
7.1 Personnel qualifications .8
7.2 Equipment .8
7.2.1 Ultrasonic equipment and display .8
7.2.2 Ultrasonic probes .9
7.2.3 Scanning mechanisms.9
8 Preparation for testing .9
8.1 Volume to be inspected .9
8.2 Set up of probes.9
8.3 Scan increment setting .10
8.4 Geometry considerations .10
8.5 Preparation of scanning surfaces.11
8.6 Temperature .11
8.7 Couplant .11
8.8 Provision of datum points .11
9 Testing of base material.11
10 Range and sensitivity settings.11
10.1 Settings.11
10.1.1 General.11
10.1.2 Time window .11
10.1.3 Time-to-depth conversion.12
10.1.4 Sensitivity settings .12
10.2 Checking of the settings .12
10.3 Reference blocks .13
10.3.1 General.13
10.3.2 Material .13
10.3.3 Dimensions and shape.13
10.3.4 Reference reflectors .13
11 Weld testing.14
12 Interpretation and analysis of TOFD images .14
12.1 General.14
12.2 Assessing the quality of the TOFD image.14
12.3 Identification of relevant indications .15
12.4 Classification of relevant indications .15
12.4.1 General.15
12.4.2 Indications from surface breaking discontinuities .15
12.4.3 Indications from embedded discontinuities.16
12.4.4 Unclassified indications .16
12.5 Determination of location and size.16
12.5.1 Location.16
12.5.2 Sizing .16
12.6 Evaluation against acceptance criteria.16
13 Test report.17
13.1 General .17
13.2 Information relating to object under test .17
13.3 Information relating to equipment .17
13.4 Information relating to test technique.17
13.5 Information relating to test results .17
Annex A (informative) Reference blocks .18
A.1 Thickness requirements .18
A.1.1 Maximum thickness .18
A.1.2 Minimum thickness .18
A.2 Reference reflectors.19
A.3 Typical reference blocks.21
Annex B (informative) Examples of typical scans .23
B.1 Satisfactory and unsatisfactory TOFD-images .23
B.2 Typical TOFD-images of discontinuities in fusion welded joints.28
B.3 TOFD-images of geometrical features .32
Bibliography.35
Foreword
This document (CEN/TS 14751:2004) has been prepared by Technical Committee CEN/TC 121 “Welding”,
the secretariat of which is held by DIN.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to announce this Technical Specification: Austria, Belgium, Czech Republic, Denmark,
Finland, France, Germany, Greece, Hungary Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, Norway,
Portugal, Slovakia, Spain, Sweden, Switzerland and the United Kingdom.
1 Scope
This document specifies the application of the time-of-flight diffraction (TOFD) technique for the semi-, or fully-
automated ultrasonic testing of fusion welded joints in metallic materials equal to and above 6 mm thickness.
It is primarily intended for use on full penetration welded joints of simple geometry in plates, pipes, and
vessels, where both the weld and parent material are low alloyed carbon steel. Where specified and
appropriate, TOFD may also be used on other types of materials that exhibit low ultrasonic attenuation
(especially that due to scatter).
Where material dependent ultrasonic parameters are specified in this document, they are based on steels
having a sound velocity of (5920 ± 50) m/s for longitudinal waves, and (3255 ± 30) m/s for transverse waves.
This has to be taken into account when examining materials with a different velocity.
This document makes reference to the basic pre-standard ENV 583-6 and provides guidance on the specific
capabilities and limitations of TOFD for the detect
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.