EN 10088-2:2024
(Main)Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resistant steels for general purposes
Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resistant steels for general purposes
This document specifies the technical delivery conditions for hot or cold rolled sheet/plate and strip of standard grades and special grades of corrosion resistant stainless steels for general purposes.
NOTE General purposes include the use of stainless steels in contact with foodstuffs.
The general technical delivery conditions specified in EN 10021 apply in addition to the specifications of this document, unless otherwise specified in the document.
This document does not apply to components manufactured by further processing of the product forms listed above with quality characteristics altered as a result of such further processing.
Nichtrostende Stähle - Teil 2: Technische Lieferbedingungen für Blech und Band aus korrosionsbeständigen Stählen für allgemeine Verwendung
Dieses Dokument legt die technischen Lieferbedingungen für warm- oder kaltgewalztes Blech und Band aus Standardgüten und Sondergüten korrosionsbeständiger nichtrostender Stähle für allgemeine Verwendung fest.
ANMERKUNG Allgemeine Verwendung schließt die Verwendung von nichtrostenden Stählen in Berührung mit Lebensmitteln ein.
Zusätzlich zu den Angaben dieses Dokumentes gelten, sofern in diesem Dokument nichts anderes festgelegt ist, die in EN 10021 festgelegten allgemeinen technischen Lieferbedingungen.
Dieses Dokument nicht für die durch Weiterverarbeitung der oben genannten Erzeugnisformen hergestellten Teile mit fertigungsbedingt abweichenden Gütemerkmalen.
Aciers inoxydables - Partie 2 : Conditions techniques de livraison des tôles et bandes en acier résistant à la corrosion pour usage général
Le présent document spécifie les conditions techniques de livraison des tôles et bandes laminées à chaud ou à froid produites dans des nuances standardisées ou des nuances spéciales d'aciers inoxydables résistant à la corrosion pour usage général.
NOTE L’usage général inclut l’utilisation des aciers inoxydables pour le contact alimentaire.
Les conditions techniques de livraison spécifiées dans l'EN 10021 s'appliquent en plus des spécifications du présent document, sauf en cas de spécification contraire dans le présent document.
Le présent document ne s'applique pas aux composants fabriqués par transformation ultérieure des produits énumérés ci-dessus, avec les modifications des caractéristiques de qualité qui en résultent.
Nerjavna jekla - 2. del: Tehnični dobavni pogoji za korozijsko odporne pločevine in trakove za splošno uporabo
Ta dokument določa tehnične dobavne pogoje za vroče ali hladno valjane pločevine in trakove iz korozijsko odpornih nerjavnih jekel standardnih in posebnih razredov za splošno uporabo.
OPOMBA: Splošna uporaba vključuje uporabo nerjavnih jekel v stiku z živili.
Skupaj s specifikacijami tega dokumenta se uporabljajo tudi splošni tehnični dobavni pogoji, ki so navedeni v standardu EN 10021, če ni drugače navedeno v tem dokumentu.
Ta dokument se ne uporablja za sestavne dele, ki so izdelani z dodatno predelavo oblik izdelkov, ki so navedeni zgoraj, pri čemer se kakovostne značilnosti posledično spremenijo zaradi dodatne predelave.
General Information
Relations
Overview
EN 10088-2:2024 - "Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes" specifies the technical delivery conditions for hot‑ or cold‑rolled sheet, plate and strip of standard and special grades of corrosion‑resistant stainless steels. The scope explicitly includes food contact applications. General delivery rules in EN 10021 apply in addition to this document. The standard replaces EN 10088-2:2014 and updates grade listings, chemical and mechanical requirements, testing and ordering information.
Key topics and technical requirements
- Product forms covered: hot-rolled and cold-rolled sheet, plate and strip for general purposes.
- Grade designation: Steel names and numeric identifiers follow EN 10027 (see Annex A for the full grade list).
- Chemical composition: Limits and product analysis tolerances for austenitic, ferritic, martensitic and duplex grades are specified (note: stainless steels are defined here as steels with ≥10.5% chromium and ≤1.20% carbon).
- Mechanical properties: Tensile properties at room (and where applicable elevated) temperature; options for measured testing or modelling (per EN 10373).
- Surface quality and dimensions: Surface condition, dimensional tolerances and shape tolerances referenced to applicable dimensional standards (Annex C).
- Formability and hardness: Requirements for formability at room temperature and hardness/strength levels, including cold‑worked conditions for some austenitic grades.
- Internal soundness and NDT: Verification of internal soundness for flat products ≥ 6 mm thickness via ultrasonic testing per EN 10307 where required.
- Inspection, testing and documentation: Extent of testing, sample selection, test methods and inspection documents (EN 10204 types).
- Ordering information & marking: Complete order designation elements (quantity, product form, dimensions, steel name/number, delivery condition, process route, optional tests, inspection document) and marking rules (Clause 8).
- Annexes: Annex A - list of grades; Annex B - guidelines for further processing/heat treatment; Annex C - dimensional standards.
- IP note: CEN flags that certain grades listed may be subject to patent claims (e.g., 1.4637, 1.4662, 1.4420, 1.4622, 1.4062, 1.4646, 1.4611, 1.4613).
Practical applications
This standard is used to specify supply quality for corrosion‑resistant stainless steel flat products intended for:
- Food processing and kitchen equipment (food‑contact suitability included)
- Chemical and process plant components
- Architectural cladding, façades and roofing
- General fabrication where corrosion resistance and defined mechanical/surface properties are required
Who should use this standard
- Steel manufacturers and mill quality teams
- Materials engineers and specifiers (procurement documents)
- Fabricators and metal‑forming shops
- QA/inspection teams and testing laboratories
- Designers and consultants specifying stainless steel sheet/plate/strip
Related standards
- EN 10021 (general technical delivery conditions)
- EN 10088-1 (list of stainless steels)
- EN 10307 (ultrasonic testing of flat products ≥ 6 mm)
- EN ISO series for tensile, hardness and corrosion testing referenced in the standard
Keywords: EN 10088-2, stainless steel sheet, stainless steel plate, stainless steel strip, technical delivery conditions, corrosion resisting steels, food contact stainless steel, stainless steel grades.
Standards Content (Sample)
SLOVENSKI STANDARD
01-december-2024
Nerjavna jekla - 2. del: Tehnični dobavni pogoji za korozijsko odporne pločevine in
trakove za splošno uporabo
Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of
corrosion resisting steels for general purposes
Nichtrostende Stähle - Teil 2: Technische Lieferbedingungen für Blech und Band aus
korrosionsbeständigen Stählen für allgemeine Verwendung
Aciers inoxydables - Partie 2: Conditions techniques de livraison des tôles et bandes en
acier de résistance à la corrosion pour usage général
Ta slovenski standard je istoveten z: EN 10088-2:2024
ICS:
77.140.20 Visokokakovostna jekla Stainless steels
77.140.50 Ploščati jekleni izdelki in Flat steel products and semi-
polizdelki products
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
EN 10088-2
EUROPEAN STANDARD
NORME EUROPÉENNE
September 2024
EUROPÄISCHE NORM
ICS 77.140.20; 77.140.50 Supersedes EN 10088-2:2014
English Version
Stainless steels - Part 2: Technical delivery conditions for
sheet/plate and strip of corrosion resistant steels for
general purposes
Aciers inoxydables - Partie 2 : Conditions techniques de Nichtrostende Stähle - Teil 2: Technische
livraison des tôles et bandes en acier résistant à la Lieferbedingungen für Blech und Band aus
corrosion pour usage général korrosionsbeständigen Stählen für allgemeine
Verwendung
This European Standard was approved by CEN on 6 November 2023.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this
European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references
concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN
member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by
translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management
Centre has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway,
Poland, Portugal, Republic of North Macedonia, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Türkiye and
United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
CEN-CENELEC Management Centre: Rue de la Science 23, B-1040 Brussels
© 2024 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 10088-2:2024 E
worldwide for CEN national Members.
Contents Page
European foreword . 3
Introduction . 5
1 Scope . 6
2 Normative references . 6
3 Terms and definitions . 7
4 Designation and ordering . 7
4.1 Designation of steel grades . 7
4.2 Designation to be used on ordering . 8
5 Classification of grades . 9
6 Requirements . 9
6.1 Steelmaking process . 9
6.2 Delivery condition . 9
6.3 Chemical composition . 9
6.4 Chemical corrosion resistance properties. 9
6.5 Mechanical properties . 10
6.6 Surface quality . 10
6.7 Internal soundness . 10
6.8 Formability at room temperature . 10
6.9 Dimensions, and tolerances on dimensions and shape . 11
6.10 Calculation of mass and tolerances on mass . 11
7 Inspection and testing . 11
7.1 General. 11
7.2 Agreement on tests and inspection documents . 11
7.3 Specific inspection and testing . 12
7.3.1 Extent of testing . 12
7.3.2 Selection and preparation of samples and test pieces . 12
7.4 Test methods . 13
7.5 Retests . 13
8 Marking . 13
Annex A (informative) List of all stainless steel grades that appear in the document . 51
Annex B (informative) Guidelines for further treatment (including heat treatment) in
fabrication . 53
Annex C (informative) Applicable dimensional standards . 60
Bibliography . 61
European foreword
This document (EN 10088-2:2024) has been prepared by Technical Committee CEN/TC 459 “ECISS -
European Committee for Iron and Steel Standardization ”, the secretariat of which is held by AFNOR.
This European Standard shall be given the status of a national standard, either by publication of an
identical text or by endorsement, at the latest by March 2025, and conflicting national standards shall be
withdrawn at the latest by March 2025.
This document supersedes EN 10088-2:2014.
In comparison with the previous edition, the following technical modifications have been made:
a) addition of austenitic grades 1.4382, 1.4420, 1.4678, 1.4682, addition of austenitic-ferritic (duplex)
grade 1.4637, addition of ferritic grade 1.4622, and addition of martensitic grade 1.4060;
b) chemical composition was changed for following grades: austenitic grades 1.4310, 1.4404, 1.4529,
ferritic grades 1.4003, 1.4521, and martensitic grades 1.4028, 1.4116;
c) removal of austenitic grades 1.4319, 1.4537, and removal of austenitic-ferritic (duplex) grade
1.4655;
d) permissible product analysis tolerances have been adjusted;
e) austenitic grade 1.4529 cold and hot rolled strip products have been added;
f) austenitic-ferritic (duplex) grades:
— 1.4162 cold and hot rolled strip max. product thicknesses, and mechanical property
requirements at room and elevated temperatures have been changed;
— 1.4362 hot rolled strip and plate, a mechanical property requirement has been changed;
— 1.4501 cold and hot rolled strip products have been added;
— 1.4662 cold and hot rolled strip max. product thicknesses have been changed;
g) ferritic grades 1.4509, 1.4513, 1.4520, 1.4526 hot rolled strip products have been added;
h) introduction of the possibility to use modelling for determination of the mechanical properties
measured by tensile testing;
i) addition of austenitic grades 1.4307, 1.4404, 1.4420, 1.4678 to cold worked process route, and
expansion of cold worked strength levels for austenitic grades 1.4401, 1.4571;
j) listing of types of process route has been revised;
k) Clause 8 “Marking” has been revised;
l) listing of grades in all tables has been revised;
m) new Annex A lists all grades that appear in this document by ascending steel number.
Through its sub-committee SC 5 “Steels for heat treatment, alloy steels, free-cutting steels and stainless steels”,
(secretariat: DIN).
EN 10088, under the general title Stainless steels, consists of the following parts:
— Part 1: List of stainless steels (including a table of European Standards, in which these stainless steels
are further specified, see Annex C);
— Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resistant steels for general
purposes;
— Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright
products of corrosion resistant steels for general purposes;
— Part 4: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for
construction purposes;
— Part 5: Technical delivery conditions for bars, rods, wire, sections and bright products of corrosion
resisting steels for construction purposes.
Any feedback and questions on this document should be directed to the users’ national standards body.
A complete listing of these bodies can be found on the CEN website.
According to the CEN-CENELEC Internal Regulations, the national standards organisations of the
following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia,
Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland,
Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Republic of North
Macedonia, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Türkiye and the United
Kingdom.
Introduction
The European Committee for Standardization (CEN) draws attention to the fact that it is claimed that
compliance with this document may involve the use of patents applied to eight steel grades, given in
Clause 8, Annex A and Annex B and which is claimed to be relevant for the following clause(s) of this
document:
Clauses: Clause 8, Annex A and Annex B
CEN takes no position concerning the evidence, validity and scope of these patent rights. The holders of
these patent rights have ensured CEN that they are willing to negotiate licenses, under reasonable and
non-discriminatory terms and conditions, with applicants throughout the world. In this respect, the
statements of the holders of these patent rights are registered with CEN. Information may be obtained
from:
Grade 1.4637, 1.4662
Outokumpu Stainless AB
SE-77480 Avesta, Sweden
Grade 1.4420, 1.4622
Outokumpu Oyj
FI-00180, Helsinki, Salmisaarenranta 11, Finland
Grade 1.4062
Ugitech
F-73403 Ugine Cedex, France
Grade 1.4062
Industeel
F-71200 Creusot, 56 Rue Clemenceau, France
Grade 1.4646, 1.4611, 1.4613
Acciai Speciali Terni
I-05100 Terni, Italy
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights other than those identified above. CEN shall not be held responsible for identifying any or
all such patent rights.
1 Scope
This document specifies the technical delivery conditions for hot or cold rolled sheet/plate and strip of
standard grades and special grades of corrosion resistant stainless steels for general purposes.
NOTE General purposes include the use of stainless steels in contact with foodstuffs.
The general technical delivery conditions specified in EN 10021 apply in addition to the specifications of
this document, unless otherwise specified in the document.
This document does not apply to components manufactured by further processing of the product forms
listed above with quality characteristics altered as a result of such further processing.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
EN 10021, General technical delivery conditions for steel products
EN 10027-1, Designation systems for steels — Part 1: Steel names
EN 10027-2, Designation systems for steels — Part 2: Numerical system
EN 10079, Definition of steel products
EN 10088-1:2023, Stainless steels — Part 1: List of stainless steels
EN 10151, Stainless steel strip for springs — Technical delivery conditions
EN 10163-2, Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections —
Part 2: Plate and wide flats
EN 10168, Steel products — Inspection documents — List of information and description
EN 10204, Metallic products — Types of inspection documents
EN 10307, Non-destructive testing — Ultrasonic testing of austenitic and austenitic-ferritic stainless steels
flat products of thickness equal to or greater than 6 mm (reflection method)
EN 10373, Determination of the physical and mechanical properties of steels using models
EN ISO 148-1, Metallic materials — Charpy pendulum impact test — Part 1: Test method (ISO 148-1)
EN ISO 377, Steel and steel products — Location and preparation of samples and test pieces for mechanical
testing (ISO 377)
EN ISO 3651-2, Determination of resistance to intergranular corrosion of stainless steels — Part 2: Ferritic,
austenitic and ferritic-austenitic (duplex) stainless steels — Corrosion test in media containing sulfuric acid
(ISO 3651-2)
EN ISO 4885, Ferrous materials — Heat treatments — Vocabulary (ISO 4885)
EN ISO 6506-1, Metallic materials — Brinell hardness test — Part 1: Test method (ISO 6506-1)
EN ISO 6507-1, Metallic materials — Vickers hardness test — Part 1: Test method (ISO 6507-1)
EN ISO 6508-1, Metallic materials — Rockwell hardness test — Part 1: Test (ISO 6508-1)
EN ISO 6892-1, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
(ISO 6892-1)
EN ISO 6892-2, Metallic materials — Tensile testing — Part 2: Method of test at elevated temperature
(ISO 6892-2)
EN ISO 14284, Steel and iron — Sampling and preparation of samples for the determination of chemical
composition (ISO 14284)
3 Terms and definitions
For the purposes of this document, the terms and definitions regarding types of heat treatment in
EN ISO 4885 and regarding product forms in EN 10079 and the following apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https://www.iso.org/obp/
— IEC Electropedia: available at https://www.electropedia.org/
3.1
stainless steels
steels with at least 10,5 % of chromium and maximum 1,20 % of carbon
[SOURCE: EN 10020:2000, 3.2.2]
Note 1 to entry: Stainless steels are further subdivided in accordance with their main property into corrosion
resistant steels, heat resistant steels and creep resistant steels.
3.2
corrosion resistant stainless steels
standard stainless steels (see 3.1) where its resistance to corrosion is of primary importance
3.3
general purposes
purposes other than the special purposes referred to in the Bibliography
3.4
standard grades
grades with a relatively good availability and a wider range of application
3.5
special grades
grades for special use and/or with limited availability
4 Designation and ordering
4.1 Designation of steel grades
The steel names and steel numbers (see Tables 1 to 4) were formed in accordance with EN 10027-1 and
EN 10027-2 respectively.
A complete overview of all grades that are in this document is given in Annex A.
4.2 Designation to be used on ordering
The complete designation for ordering a product according to this document shall contain the following
information:
— desired quantity (mass or pieces);
— product form (strip, sheet or plate);
— where an appropriate dimensional standard is available (see Annex C) the number of the standard,
plus any choice of requirements;
— if there is no dimensional standard, the nominal dimensions and tolerances required;
— type of material (steel);
— number of this document;
— steel name or steel number;
— if for the relevant steel in the table for the mechanical properties more than one treatment condition
is covered, the symbol for the desired heat treatment or cold worked condition;
— desired process route (see symbols in Table 6);
— if a verification of internal soundness is required, flat products with thickness ≥ 6 mm shall be tested
in accordance with EN 10307;
— any additional optional tests or inspections (see 7.2.3 d);
— standard designation for a test report 2.2 or, if required, any other type of inspection document in
accordance with EN 10204 (see 7.2.1).
EXAMPLE 10 plates according to EN ISO 18286 with thickness = 8 mm, width = 2 000 mm, length = 5 000 mm;
tolerances on width and length class B, flatness tolerance class N made of steel EN 10088-2 with the name
X5CrNi18-10 and the number 1.4301 in process route 1D (see Table 6), inspection certificate 3.1 as specified in
EN 10204:
10 plates EN ISO 18286 — 8 × 2000 × 5000 B N
Steel EN 10088-2 — X5CrNi18-10+1D
EN 10204 — 3.1
or
10 plates EN ISO 18286 — 8 × 2000 × 5000 B N
Steel EN 10088-2 — 1.4301+1D
EN 10204 — 3.1
5 Classification of grades
Steels covered in this document are classified according to their structures into:
— austenitic steels,
— austenitic-ferritic steels,
— ferritic steels,
— martensitic steels,
— precipitation hardening steels.
See also EN 10088-1:2023, Annex C.
6 Requirements
6.1 Steelmaking process
Unless a special steelmaking process is agreed at the time of enquiry and order, the steelmaking process
for steels conforming to this document shall be at the discretion of the manufacturer.
6.2 Delivery condition
The products shall be supplied in the delivery condition agreed at the time of enquiry and order by
reference to the process route given in Table 6 and, where different alternatives exist, to the treatment
conditions given in Tables 7 to 11, 17 and 18 (see also Annex B).
6.3 Chemical composition
6.3.1 The chemical composition requirements given in Tables 1 to 4 apply with respect to the chemical
composition according to the cast analysis.
Elements not quoted (“-”) or not listed in these tables shall not be intentionally added to the steel without
the agreement of the purchaser except for finishing the cast. All appropriate precautions shall be taken
to avoid the addition of such elements from scrap and other materials used in production which would
impair mechanical properties and the suitability of the steel.
6.3.2 The product analysis may deviate from the limiting values for the cast analysis given in Tables 1
to 4 by the values listed in Table 5.
6.4 Chemical corrosion resistance properties
For austenitic, austenitic-ferritic and ferritic steels the specification in Tables 7 to 9, referring to
resistance to intergranular corrosion as determined according to EN ISO 3651-2, applies (see also 7.4.6).
NOTE 1 EN ISO 3651-2 is not applicable for testing martensitic and precipitation hardening steels.
NOTE 2 The corrosion resistance of stainless steels is very dependent on the type of environment and can
therefore not always be clearly ascertained through laboratory tests. It is therefore advisable to draw on the
available experience of the use of the steels.
6.5 Mechanical properties
6.5.1 The mechanical properties at room temperature as specified in Tables 7 to 11 apply for the
relevant specified heat treatment condition. This does not apply to the process route 1U (hot rolled, not
heat treated, not descaled).
If by agreement at the time of ordering the products shall be supplied in a non-heat treated condition, the
mechanical properties specified in Tables 7 to 11 shall be obtained from reference test pieces which have
received the appropriate heat treatment (simulated heat treatment). For the process routes 1M and 2M
for patterned finish, the mechanical properties specified in Tables 7 to 11 also do not apply. In this case,
agreements shall be made at the time of enquiry and order, e.g. performing a bend test according to EN
ISO 7438.
For cold worked products, the tensile strength levels at ambient temperature as specified in Table 17
apply. The available tensile strength levels in the cold worked condition are indicated in Table 19.
Alternatively, cold worked products can be ordered according to their 0,2 % proof strength as given in
Tables 18 and 20.
NOTE Austenitic steels are insensitive to brittle fracture in the solution annealed condition. As they do not have
a pronounced transition temperature, which is characteristic of other steels, they are also useful for application at
cryogenic temperatures.
6.5.2 The values in Tables 12 to 16 apply for the 0,2 % and 1,0 % proof strength at elevated
temperatures.
6.5.3 In case of demand for larger thicknesses than stated in Tables 7 to 11, appropriate mechanical
property values shall be agreed at the time of enquiry and order.
6.6 Surface quality
Slight surface imperfections, inherent in the rolling process, are permitted.
When products are delivered in coil form, the degree and extent of such imperfections may be expected
to be greater, due to the impracticability of removing short lengths of coil. For hot rolled quarto plates
(symbol P in Tables 7 to 11), the requirements in EN 10163-2, class A2, apply unless otherwise agreed.
For other products, where necessary, more precise requirements on surface quality may be agreed at the
time of enquiry and order.
Products delivered with hot rolled or cold rolled finishes (see Table 6) shall, unless otherwise agreed, be
supplied with only one surface inspected to the required finish (the prime surface). In such instances, the
manufacturer should indicate the prime surface, by marking the material or the packaging, or by some
other agreed method. The default method is to mark the prime surface, and to make this surface the top
surface of plates, sheets and cut lengths, or the outside surface of coiled products.
6.7 Internal soundness
The products shall be free of internal defects which would exclude them from being used for their usual
purpose. For austenitic and austenitic-ferritic stainless steel flat products with a thickness ≥ 6 mm,
ultrasonic testing may be agreed at the time of enquiry and order in accordance with EN 10307.
6.8 Formability at room temperature
Cold formability may be verified by elongation in the tensile test.
6.9 Dimensions, and tolerances on dimensions and shape
The dimensions, and the tolerances on dimensions and shape shall be agreed at the time of enquiry and
order, as far as possible with reference to the dimensional standards listed in Annex C. EN ISO 18286
shall normally only be applied for product form P (individually hot rolled plates, i.e. “quarto plates”) and
not for product form H (continuously hot rolled strip, or sheet or plate cut off from it), for which
EN ISO 9444-2 shall be applied. When applying EN ISO 18286, tolerances on width and length class A
shall apply, unless specifically agreed otherwise at the time of enquiry and order.
6.10 Calculation of mass and tolerances on mass
6.10.1 The nominal mass shall be calculated by using the steel density given in Annex E of
EN 10088-1:2023 and the nominal dimensions of the steel product.
6.10.2 The dimensional standards listed in Annex C do not specify tolerances on mass, which therefore
may be agreed at the time of enquiry and order.
7 Inspection and testing
7.1 General
The appropriate process control, inspection, testing and modelling shall be carried out to ensure that the
product complies with the requirements of the order.
This includes the following:
— suitable frequency of verification of the dimensions of the products;
— adequate intensity of visual examination of the surface quality of the products;
— appropriate frequency and type of test to ensure that the correct grade of steel is used.
The nature and frequency of these verifications, examinations and tests is determined in the light of the
degree of consistency that has been determined by the evidence of the quality system. In view of this,
verifications by specific tests for these requirements are not necessary unless otherwise agreed.
7.2 Agreement on tests and inspection documents
7.2.1 Products complying with this document shall be ordered and delivered with one of the inspection
documents as specified in EN 10204. The type of document shall be agreed upon at the time of enquiry
and order. If the order does not contain any specification of this type, at least a test report 2.2 shall be
issued.
7.2.2 If it is agreed to issue a test report 2.2 in accordance with EN 10204, it shall indicate the following
information:
a) information groups A, B and Z of EN 10168;
b) results of the cast analysis in accordance with Table 1 to 4 with code numbers C71 to C92 in
EN 10168.
7.2.3 If the issuing of an inspection certificate 3.1 or 3.2 according to EN 10204 has been agreed,
specific inspections according to 7.3 shall be carried out and the following information shall be given in
the inspection document with the code numbers and details required by EN 10168:
a) information groups A, B and Z of EN 10168;
b) results of the cast analysis in accordance with Table 1 to 4 with code numbers C71 to C92 in
EN 10168;
c) results of all mandatory (m) tests according to Table 21;
d) results of any optional (o) test according to Table 21 or any further product verification agreed at the
time of enquiry and order.
7.3 Specific inspection and testing
7.3.1 Extent of testing
The tests to be carried out, either mandatorily (m) or optionally by agreement (o), and the composition
and size of the test units, and the number of sample products, samples and test pieces to be taken are
given in Table 21.
7.3.2 Selection and preparation of samples and test pieces
7.3.2.1 Sampling and sample preparation shall be in accordance with the requirements of
EN ISO 14284 and EN ISO 377. In addition, for the mechanical tests, the stipulations in 7.3.2.2 apply.
7.3.2.2 In accordance with Table 22, samples for tensile testing shall be taken from halfway between
the centre and a longitudinal edge. If it has been agreed that optional impact tests shall be carried out, the
test samples shall be taken from the same location.
The samples shall be taken from products in the delivery condition. If agreed, the samples may be taken
before flattening. For samples to be given a simulated heat treatment (see also 6.5.1) the conditions for
annealing, hardening and tempering shall be agreed.
7.3.2.3 Samples for hardness testing on martensitic steels and for optional testing of resistance to
intergranular corrosion shall be taken from the same location as those for the mechanical tests (see
7.3.2.2). The test pieces for testing of resistance to intergranular corrosion shall be pre-bend as shown in
Figure 1.
Key
1 rolling direction
Figure 1 — Test piece for determination of resistance to intergranular corrosion: direction of
bending in relation to the rolling direction
7.4 Test methods
7.4.1 The chemical analysis shall be carried out using appropriate European Standards. The choice of a
suitable physical or chemical method for the analysis shall be at the discretion of the manufacturer. If
requested, the manufacturer shall declare the test method used.
NOTE The list of available European Standards on chemical analysis is given in CEN/TR 10261.
7.4.2 Tensile testing at room temperature shall be carried out in accordance with EN ISO 6892-1 also
considering the additional or deviating conditions specified in Table 22, footnote a. The 0,2 % proof
strength, the tensile strength and the elongation after fracture shall be determined. For austenitic steels
only, also the 1,0 % proof strength shall be determined.
7.4.3 If a tensile test at elevated temperature has been ordered, this shall be carried out in accordance
with EN ISO 6892-2. As for room temperature testing (see 7.4.2), 0,2 % proof strength, and for austenitic
steels only, also the 1,0 % proof strength shall be determined.
7.4.4 For the determination of mechanical properties measured by tensile testing, the manufacturer
may use modelling with a verification method approved in accordance with EN 10373, if agreed with the
purchaser at the time of enquiry and order.
7.4.5 If an impact test has been ordered, it shall be carried out in accordance with EN ISO 148-1 on test
pieces with a V-notch and using a striker with a radius of 2 mm (KV ). The test result shall be determined
as an average value obtained from a set of at least three test pieces (see also EN 10021).
7.4.6 If a hardness test has been ordered, Brinell hardness test shall be carried out in accordance with
EN ISO 6506-1, Vickers hardness test in accordance with EN ISO 6507-1, and Rockwell hardness test in
accordance with EN ISO 6508-1.
7.4.7 The resistance to intergranular corrosion shall be tested in accordance with EN ISO 3651-2.
7.4.8 The tolerances on dimensions and form of the product, and the measurement of dimension and
form shall be in accordance with the requirements of the relevant dimensional standards (see also
Annex C).
7.5 Retests
See EN 10021.
8 Marking
8.1 Each product shall be marked on one surface, providing the information stated in Table 23, and
with the exceptions mentioned in 8.2.
8.2 For sheets or plates in bundles and strip in coil or where the surface is ground or polished, or in
case of an agreement with the customer at the time of enquiry and order not to mark the product, the
marking shall instead be applied to the packaging or to a tag securely attached to it.
8.3 The method of marking and the material of marking shall, unless otherwise agreed, be at the
discretion of the manufacturer. The marking shall be durable for at least one year in unheated storage
under cover. Corrosion resistance of the product shall not be impaired by marking.
Table 1 — Chemical composition (cast analysis) of austenitic corrosion resistant steels
a
Steel designation
% by mass
Name Number C Si Mn P S Cr Ni Mo N Cu Others
Standard grades
X2CrNiN18-7 1.4318 0,030 1,00 2,00 0,045 0,015 16,5 to 18,5 6,0 to 8,0 - 0,10 to 0,20 - -
X4CrNiCu18-7 1.4382 0,05 1,00 2,00 0,045 0,015 17,0 to 19,0 6,0 to 8,0 - 0,050 to 0,15 0,50 to 2,00 -
0,030 to
c
X10CrNi18-8 1.4310 2,00 2,00 0,045 0,015 16,0 to 19,0 6,0 to 9,5 0,80 0,10 -
-
0,15
b
X2CrNi18-9 1.4307 0,030 1,00 2,00 0,045 17,5 to 19,5 8,0 to 10,5 - 0,10 - -
0,015
0,15 to
X8CrNiS18-9 1.4305 0,10 1,00 2,00 0,045 17,0 to 19,0 8,0 to 10,0 - 0,10 1,00 -
0,35
b
X2CrNiN18-10 1.4311 0,030 1,00 2,00 0,045 0,015 17,5 to 19,5 8,5 to 11,5 - 0,12 to 0,22 - -
b
X5CrNi18-10 1.4301 0,07 1,00 2,00 0,045 17,5 to 19,5 8,0 to 10,5 - 0,10 - -
0,015
b
X6CrNiTi18-10 1.4541 0,08 1,00 2,00 0,045 17,0 to 19,0 9,0 to 12,0 - - - Ti: 5 × C to 0,70
0,015
b
X2CrNi19-11 1.4306 0,030 1,00 2,00 0,045 0,015 18,0 to 20,0 10,0 to 12,0 - 0,10 - -
b
X4CrNi18-12 1.4303 0,06 1,00 2,00 0,045 17,0 to 19,0 11,0 to 13,0 - 0,10 - -
0,015
b
X2CrNiMoN17-11-2 1.4406 0,030 1,00 2,00 0,045 0,015 16,5 to 18,5 10,0 to 12,5 2,00 to 2,50 0,12 to 0,22 - -
b
X2CrNiMo17-12-2 1.4404 0,030 1,00 2,00 0,045 16,5 to 18,5 10,0 to 13,0 2,00 to 3,00 0,10 - -
0,015
b
X5CrNiMo17-12-2 1.4401 0,07 1,00 2,00 0,045 0,015 16,5 to 18,5 10,0 to 13,0 2,00 to 2,50 0,10 - -
b
X6CrNiMoTi17-12-2 1.4571 0,08 1,00 2,00 0,045 0,015 16,5 to 18,5 10,5 to 13,5 2,00 to 2,50 - - Ti: 5 × C to 0,70
d
X2CrNiMoN21-9-1 * 1.4420 * 0,030 1,00 2,00 0,015 19,5 to 21,5 8,0 to 9,5 0,50 to 1,50 0,14 to 0,25 1,00 -
0,045
b
X2CrNiMo17-12-3 1.4432 0,030 1,00 2,00 0,045 0,015 16,5 to 18,5 10,5 to 13,0 2,50 to 3,00 0,10 - -
b
X2CrNiMo18-14-3 1.4435 0,030 1,00 2,00 0,045 17,0 to 19,0 12,5 to 15,0 2,50 to 3,00 0,10 - -
0,015
b
X2CrNiMoN17-13-5 1.4439 0,030 1,00 2,00 0,045 16,5 to18,5 12,5 to 14,5 4,0 to 5,0 0,12 to 0,22 - -
0,015
X1NiCrMoCu25-20-5 1.4539 0,020 0,70 2,00 0,030 0,010 19,0 to 21,0 24,0 to 26,0 4,0 to 5,0 0,15 1,20 to 2,00 -
a
Steel designation
% by mass
Name Number C Si Mn P S Cr Ni Mo N Cu Others
Special grades
0,030 to 1,50 to
X5CrNiCu19-6-2 1.4640 0,50 0,045 0,015 18,0 to 19,0 5,5 to 6,9 - 0,030 to 0,11 1,30 to 2,00 -
0,08 4,0
0,80 to
X2CrNiSi18-10 1.4682 0,030 2,00 0,045 0,015 17,5 to 19,5 9,0 to 11,0 0,40 to 0,80 0,10 - -
2,00
X5CrNiN19-9 1.4315 0,06 1,00 2,00 0,045 0,015 18,0 to 20,0 8,0 to 11,0 - 0,12 to 0,22 - -
X6CrNiNb18-10 1.4550 0,08 1,00 2,00 0,045 0,015 17,0 to 19,0 9,0 to 12,0 - - - Nb: 10 × C to 1,00
X8CrMnCuN17-8-3 1.4597 0,10 2,00 6,5 to 9,0 0,040 0,030 15,0 to 18,0 3,00 1,00 0,10 to 0,30 2,00 to 3,5 -
X8CrMnNi19-6-3 1.4376 0,10 1,00 5,0 to 8,0 0,045 0,015 17,0 to 20,5 2,00 to 4,5 - 0,30 - -
X2CrMnNiN17-7-5 1.4371 0,030 1,00 6,0 to 8,0 0,045 0,015 16,0 to 17,5 3,5 to 5,5 - 0,15 to 0,25 1,00 -
X12CrMnNiN17-7-5 1.4372 0,15 1,00 5,5 to 7,5 0,045 0,015 16,0 to 18,0 3,5 to 5,5 - 0,050 to 0,25 - -
0,20 to 14,0 to
b
X30MnCrN16-14 1.4678 1,00 0,045 12,0 to 16,0 - - 0,20 to 0,40 2,00 -
0,015
0,40 18,0
X9CrMnNiCu17-8-5-2 1.4618 0,10 1,00 5,5 to 9,5 0,070 0,010 16,5 to 18,5 4,5 to 5,5 - 0,15 1,00 to 2,50 -
7,5 to
X12CrMnNiN18-9-5 1.4373 0,15 1,00 0,045 0,015 17,0 to 19,0 4,0 to 6,0 - 0,050 to 0,25 - -
10,5
0,07 to 0,50 to
X11CrNiMnN19-8-6 1.4369 5,0 to 7,5 0,030 0,015 17,5 to 19,5 6,5 to 8,5 - 0,20 to 0,30 - -
0,15 1,00
0,02 to 10,5 to
X6CrMnNiCuN18-12-4-2 * 1.4646 * 1,00 0,050 0,015 17,0 to 19,0 3,5 to 4,5 0,50 0,20 to 0,30 1,50 to 3,00 -
0,10 12,5
X1CrNiSi18-15-4 1.4361 0,015 3,7 to 4,5 2,00 0,025 0,010 16,5 to 18,5 14,0 to 16,0 0,20 0,10 - -
X1CrNi25-21 1.4335 0,020 0,25 2,00 0,025 0,010 24,0 to 26,0 20,0 to 22,0 0,20 0,10 - -
X6CrNiMoNb17-12-2 1.4580 0,08 1,00 2,00 0,045 0,015 16,5 to 18,5 10,5 to 13,5 2,00 to 2,50 - - Nb: 10 × C to 1,00
b
X3CrNiMo17-12-3 1.4436 0,05 1,00 2,00 0,045 16,5 to 18,5 10,5 to 13,0 2,50 to 3,00 0,10 - -
0,015
X2CrNiMoN17-13-3 1.4429 0,030 1,00 2,00 0,045 0,015 16,5 to 18,5 11,0 to 14,0 2,50 to 3,00 0,12 to 0,22 - -
X2CrNiMoN18-12-4 1.4434 0,030 1,00 2,00 0,045 0,015 16,5 to 19,5 10,5 to 14,0 3,00 to 4,0 0,10 to 0,20 - -
a
Steel designation
% by mass
Name Number C Si Mn P S Cr Ni Mo N Cu Others
b
X2CrNiMo18-15-4 1.4438 0,030 1,00 2,00 0,045 0,015 17,5 to 19,5 13,0 to 16,0 3,00 to 4,0 0,10 - -
X1CrNiMoCuN20-18-7 1.4547 0,020 0,70 1,00 0,030 0,010 19,5 to 20,5 17,5 to 18,5 6,0 to 7,0 0,18 to 0,25 0,50 to 1,00 -
X1CrNiMoN25-22-2 1.4466 0,020 0,70 2,00 0,025 0,010 24,0 to 26,0 21,0 to 23,0 2,00 to 2,50 0,10 to 0,16 - -
2,00 to
X1CrNiMoCuNW24-22-6 1.4659 0,020 0,70 0,030 0,010 23,0 to 25,0 21,0 to 23,0 5,5 to 6,5 0,35 to 0,50 1,00 to 2,00 W: 1,50 to 2,50
4,0
2,00 to
X1CrNiMoCuN24-22-8 1.4652 0,020 0,50 0,030 0,005 23,0 to 25,0 21,0 to 23,0 7,0 to 8,0 0,45 to 0,55 0,30 to 0,60 -
4,0
X2CrNiMnMoN25-18-6-5 1.4565 0,030 1,00 5,0 to 7,0 0,030 0,015 24,0 to 26,0 16,0 to 19,0 4,0 to 5,0 0,30 to 0,60 - Nb: 0,15
X1NiCrMoCuN25-20-7 1.4529 0,020 0,75 2,00 0,030 0,010 19,0 to 21,0 24,0 to 26,0 6,0 to 7,0 0,15 to 0,25 0,50 to 1,50 -
X1NiCrMoCu31-27-4 1.4563 0,020 0,70 2,00 0,030 0,010 26,0 to 28,0 30,0 to 32,0 3,00 to 4,0 0,10 0,70 to 1,50 -
Elements not quoted (“-”) or not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions shall be
taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
a
Maximum values unless indicated otherwise.
b
Particular ranges of sulfur content may provide improvement of the following properties: For weldability, a controlled sulfur content of 0,008 % to 0,015 % is recommended and permitted; for
machinability a controlled sulfur content of 0,015 % to 0,030 % is recommended and permitted; for polishability, a controlled sulfur content of 0,015 % max. is recommended.
c
For cold worked applications a copper content can be specified up to 1,00 %.
d
For application according to the Pressure Equipment Directive (PED) the phosphorus content is restricted to max. 0,035 %.
* Patented steel grade.
Table 2 — Chemical composition (cast analysis) of austenitic-ferritic corrosion resistant steels
a
Steel designation
% by mass
Name Number C Si Mn P S Cr Ni Mo N Cu W
Standard grades
X2CrNiN22-2 * 1.4062 * 0,030 1,00 2,00 0,040 0,010 21,5 to 24,0 1,00 to 2,90 0,45 0,16 to 0,28 - -
X2CrNiN23-4 1.4362 0,030 1,00 2,00 0,035 0,015 22,0 to 24,5 3,5 to 5,5 0,10 to 0,60 0,050 to 0,20 0,10 to 0,60 -
X2CrMnNiN21-5-1 1.4162 0,04 1,00 4,0 to 6,0 0,040 0,015 21,0 to 22,0 1,35 to 1,90 0,10 to 0,80 0,20 to 0,25 0,10 to 0,80 -
X2CrMnNiMoN21-5-3 1.4482 0,030 1,00 4,0 to 6,0 0,035 0,030 19,5 to 21,5 1,50 to 3,50 0,10 to 0,60 0,050 to 0,20 1,00 -
b b
0,030 1,00 2,00 0,035 0,015 21,0 to 23,0 4,5 to 6,5 2,50 to 3,5 0,10 to 0,22 - -
X2CrNiMoN22-5-3 1.4462
2,50 to
X2CrNiMnMoCuN24-4-3-2 * 1.4662 * 0,030 0,70 0,035 0,005 23,0 to 25,0 3,00 to 4,5 1,00 to 2,00 0,20 to 0,30 0,10 to 0,80 -
4,0
Special grades
1,40 to 1,20 to
X2CrNiMoSi18-5-3 1.4424 0,030 0,035 0,015 18,0 to 19,0 4,5 to 5,2 2,50 to 3,00 0,050 to 0,10 - -
2,00 2,00
X2CrNiMnMoCuN21-3-1-1 * 1.4637 * 0,030 0,80 2,50 0,035 0,005 19,0 to 22,0 2,00 to 4,0 0,60 to 1,40 0,14 to 0,24 1,00 -
X2CrNiMoCuN25-6-3 1.4507 0,030 0,70 2,00 0,035 0,015 24,0 to 26,0 6,0 to 8,0 3,00 to 4,0 0,20 to 0,30 1,00 to 2,50 -
X2CrNiMoN25-7-4 1.4410 0,030 1,00 2,00 0,035 0,015 24,0 to 26,0 6,0 to 8,0 3,00 to 4,5 0,24 to 0,35 - -
X2CrNiMoCuWN25-7-4 1.4501 0,030 1,00 1,00 0,035 0,015 24,0 to 26,0 6,0 to 8,0 3,00 to 4,0 0,20 to 0,30 0,50 to 1,00 0,50 to 1,00
0,80 to
X2CrNiMoN29-7-2 1.4477 0,030 0,50 0,030 0,015 28,0 to 30,0 5,8 to 7,5 1,50 to 2,60 0,30 to 0,40 0,80 -
1,50
Elements not quoted (“-”) or not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions shall be
taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
a
Maximum values unless indicated otherwise.
b
By agreement, this grade can be delivered with a Pitting Resistance Equivalent number (PRE = Cr + 3,3 × Mo + 16 × N) greater than 34.
* Patented steel grade.
Table 3 — Chemical composition (cast analysis) of ferritic corrosion resistant steels
a
Steel designation
% by mass
Name Number C Si Mn P S Cr Ni Mo N Nb Ti Others
Standard grades
[6 × (C + N)] to
X2CrTi12 1.4512 0,030 1,00 1,00 0,040 0,015 10,5 to 12,5 - - - - -
c
0,65
X2CrNi12 1.4003 0,030 1,00 2,00 0,040 0,015 10,5 to12,5 0,30 to 1,00 - 0,030 - - -
X6CrNiTi12 1.4516 0,08 0,70 1,50 0,040 0,015 10,5 to 12,5 0,50 to 1,50 - - - 0,050 to 0,35 -
b
X6Cr13 1.4000 0,08 1,00 1,00 0,040 0,015 12,0 to 14,0 - - - - - -
b
X6CrAI13 1.4002 0,08 1,00 1,00 0,040 0,015 12,0 to 14,0 - - - - - Al: 0,10 to 0,30
[4 × (C + N) + 0,15]
b
X3CrTi17 1.4510 0,05 1,00 1,00 0,040 0,015 16,0 to 18,0 - - - - -
c
to 0,80
X3CrNb17 1.4511 0,05 1,00 1,00 0,040 0,015 16,0 to 18,0 - - - 12 × C to 1,00 - -
b
X6Cr17 1.4016 0,08 1,00 1,00 0,040 0,015 16,0 to 18,0 - - - - - -
b
X6CrMo17-1 1.4113 0,08 1,00 1,00 0,040 16,0 to 18,0 - 0,90 to 1,40 - - - -
0,015
[4 × (C + N) + 0,15]
X2CrMoTi18-2 1.4521 0,025 1,00 1,00 0,040 0,015 17,0 to 20,0 - 1,75 to 2,50 0,030 - -
c
to 0,80
Special grades
1,00 to
X2CrMnNiTi12 1.4600 0,030 1,00 0,040 0,015 11,0 to 13,0 0,30 to 1,00 - 0,025 - 6 × C to 0,35 -
2,50
X1CrNb15 1.4595 0,020 1,00 1,00 0,025 0,015 14,0 to 16,0 - - 0,020 0,20 to 0,60 - -
[4 × (C + N) + 0,15]
0,20 to Al: 1,50
X2CrSiTi15 1.4630 0,030 1,00 0,050 0,050 13,0 to 16,0 0,50 0,50 - -
c
1,50 Cu: 0,50
to 0,80
[4 × (C + N) + 0,15]
X2CrTi17 1.4520 0,025 0,50 0,50 0,040 0,015 16,0 to 18,0 - - 0,015 - -
c
to 0,80
X2CrNbZr17 1.4590 0,030 1,00 1,00 0,040 0,015 16,0 to 17,5 - - - 0,35 to 0,55 - Zr ≥ 7 × (C + N) + 0,15
X6CrNi17-1 1.4017 0,08 1,00 1,00 0,040 0,015 16,0 to 18,0 1,20 to 1,60 - - - - -
X2CrTiNb18 1.4509 0,030 1,00 1,00 0,040 0,015 17,5 to 18,5 - - - [3 × C + 0,30] to 1,00 0,10 to 0,60 -
a
Steel designation
% by mass
Name Number C Si Mn P S Cr Ni Mo N Nb Ti Others
0,20 to [3 × C + 0,30] to 1,00 Al: 0,20 to 1,50
X2CrAlSiNb18 1.4634 0,030 1,00 0,050 0,050 17,5 to 18,5 0,50 0,50 - -
c
1,50 Cu: 0,50
[4 × (C + N) + 0,15]
X2
...
Frequently Asked Questions
EN 10088-2:2024 is a standard published by the European Committee for Standardization (CEN). Its full title is "Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resistant steels for general purposes". This standard covers: This document specifies the technical delivery conditions for hot or cold rolled sheet/plate and strip of standard grades and special grades of corrosion resistant stainless steels for general purposes. NOTE General purposes include the use of stainless steels in contact with foodstuffs. The general technical delivery conditions specified in EN 10021 apply in addition to the specifications of this document, unless otherwise specified in the document. This document does not apply to components manufactured by further processing of the product forms listed above with quality characteristics altered as a result of such further processing.
This document specifies the technical delivery conditions for hot or cold rolled sheet/plate and strip of standard grades and special grades of corrosion resistant stainless steels for general purposes. NOTE General purposes include the use of stainless steels in contact with foodstuffs. The general technical delivery conditions specified in EN 10021 apply in addition to the specifications of this document, unless otherwise specified in the document. This document does not apply to components manufactured by further processing of the product forms listed above with quality characteristics altered as a result of such further processing.
EN 10088-2:2024 is classified under the following ICS (International Classification for Standards) categories: 77.140.20 - Stainless steels; 77.140.50 - Flat steel products and semi-products. The ICS classification helps identify the subject area and facilitates finding related standards.
EN 10088-2:2024 has the following relationships with other standards: It is inter standard links to EN 10088-2:2014. Understanding these relationships helps ensure you are using the most current and applicable version of the standard.
You can purchase EN 10088-2:2024 directly from iTeh Standards. The document is available in PDF format and is delivered instantly after payment. Add the standard to your cart and complete the secure checkout process. iTeh Standards is an authorized distributor of CEN standards.
Die Norm EN 10088-2:2024 legt die technischen Lieferbedingungen für warm- oder kaltgewalzte Bleche, Platten und Bänder aus rostbeständigen Edelstählen für allgemeine Zwecke fest. Diese Norm ist von großer Bedeutung, da sie die Qualität und Sicherheit von Materialien gewährleistet, die in Kontakt mit Lebensmitteln verwendet werden. Der umfassende Geltungsbereich der Norm, der sowohl Standard- als auch Sondergüten umfasst, zeigt ihre Relevanz in der Industrie, wo Korrosionsbeständigkeit und Hygiene von zentraler Bedeutung sind. Ein herausragendes Merkmal dieser Norm ist die klare Definition der technischen Anforderungen, die gewährleisten, dass die Materialien den hohen Standards für Lebensmittelsicherheit entsprechen. Darüber hinaus sind die allgemeinen technischen Lieferbedingungen aus der Norm EN 10021 ebenfalls enthalten, was die Konsistenz und Zuverlässigkeit der Spezifikationen erhöht. Die Kombination aus allgemeinen und spezifischen Bedingungen macht die Norm zu einem wertvollen Leitfaden für die Herstellung und Anwendung von rostbeständigen Edelstählen. Die Relevanz dieser Norm erstreckt sich über verschiedene Branchen, in denen rostbeständige Materialien von entscheidender Bedeutung sind. Die Anwendung dieser Norm fördert nicht nur die Sicherheit von Endprodukten, sondern unterstützt auch die Einhaltung internationaler Standards in der Lebensmittelindustrie. Zusammenfassend bietet die EN 10088-2:2024 eine solide Grundlage для die technischen Lieferbedingungen von rostbeständigen Edelstählen und sichert somit die Qualität und Benutzerfreundlichkeit für eine Vielzahl von Anwendungen.
The standard EN 10088-2:2024 serves a critical role in establishing the technical delivery conditions for hot or cold rolled sheets, plates, and strips made from corrosion resistant stainless steels. Its primary focus is on standard grades and special grades intended for general purposes, which importantly includes applications involving contact with foodstuffs. This aspect highlights the standard's relevance in industries where hygiene and safety are paramount, further reinforcing the significance of stainless steels in food-related applications. One of the strengths of this standard is its comprehensive specification, which addresses the needs for both standard and special grades of materials, offering flexibility and broad applicability in various industrial sectors. This is particularly advantageous for manufacturers and suppliers, as it ensures a consistent quality and performance of stainless steel products in varying conditions. Additionally, EN 10088-2:2024 clarifies that the general technical delivery conditions outlined in EN 10021 are applicable, creating a cohesive framework that facilitates better understanding and implementation. This interconnectedness enhances the usability of the document for professionals in materials science, engineering, and manufacturing sectors, ensuring that the quality and safety requirements are met comprehensively. However, it is important to acknowledge that this document does not extend to components that undergo further processing which may alter their quality characteristics. This delineation is crucial for manufacturers to understand the limits of the standard’s applicability, thereby guiding their production processes and ensuring compliance with the specific requirements outlined. In summary, EN 10088-2:2024 is an essential reference for anyone involved in the production or use of corrosion resistant stainless steels for general purposes, especially in contexts where hygiene is vital. Its detailed specifications and integration with broader technical standards empower stakeholders to maintain high-quality standards in their operations.
SIST EN 10088-2:2024は、一般目的の腐食抵抗ステンレス鋼のための板およびストリップに関する技術的納入条件を詳述した標準です。この文書は、標準グレードおよび特別グレードの熱間または冷間圧延されたシート、プレート、ストリップの技術的な納入条件を定めており、特に食品と接触する用途におけるステンレス鋼の利用を含む、広範な応用範囲をカバーしています。 EN 10088-2:2024の強みは、その包括的な技術基準にあります。腐食抵抗ステンレス鋼の特性を十分に活用できるように設計されており、特に一般目的に適した材料の選定とその利用方法についての詳細なガイダンスを提供しています。この標準は、品質管理や製品の製造プロセスにおいて、求められる技術的要件を明確に示しているため、製造業者やユーザーにとって非常に有用です。 また、EN 10088-2:2024は、一般的な技術納入条件としてEN 10021が適用されることを明記しており、より高い整合性と標準化を推進しています。ただし、この文書は、記載されている製品形状のさらなる加工によって品質特性が変更された部品には適用されないことを留意する必要があります。この点は、使用者が適切な製品を選定する際の重要な要素です。 全体として、SIST EN 10088-2:2024は、腐食抵抗ステンレス鋼の技術納入条件に関する重要な基準を提供しており、その実用性と適用範囲の広さから、製造業界における信頼性の高い指針となっています。
EN 10088-2:2024 문서는 일반 목적의 부식 저항성 스테인리스 강판 및 스트립에 대한 기술적 공급 조건을 규정합니다. 이 문서의 Scope는 일반적인 용도로 사용되는 스테인리스 강의 표준 및 특별 등급의 뜨거운 또는 차가운 롤링 시트/플레이트 및 스트립에 대한 공급 조건을 포함하고 있으며, 특히 식품과 접촉하는 용도에서의 사용을 고려하고 있습니다. 이 표준의 강점 중 하나는 일반적인 기술적 공급 조건이 EN 10021에 명시되어 있어, 사용자가 필요한 경우 추가적인 세부사항을 쉽게 이해하고 적용할 수 있도록 돕는다는 점입니다. 이는 부식 저항성 스테인리스 강의 사용을 위한 안정성과 일관성을 보장합니다. 또한, EN 10088-2:2024는 일반적인 목적을 위한 사용에 중점을 두기 때문에, 광범위한 산업 분야에서 해당 표준을 쉽게 적용할 수 있는 유연성을 제공합니다. 철강 제품이 아닌 최종 성형품에는 이 문서의 적용이 제외됨으로써, 특정 품질 특성이 변경된 상황에서는 보다 적합한 규정에 따라 관리될 수 있도록 합니다. 결론적으로, EN 10088-2:2024의 표준은 부식 저항성 스테인리스 강판 및 스트립의 기술적 공급 조건을 명확히 하여, 다양한 산업 분야에서의 사용에 매우 적합하며, 식품 접촉과 관련된 안전성 요구를 충족시킬 수 있는 중요한 문서입니다.
La norme EN 10088-2:2024, intitulée "Aciers inoxydables - Partie 2 : Conditions de livraison techniques pour tôles/plaques et bandes d'aciers inoxydables résistants à la corrosion pour usages généraux", joue un rôle fondamental dans le secteur de l'acier inoxydable. Son champ d'application est particulièrement pertinent car il définit les conditions techniques de livraison pour les tôles, plaques et bandes laminées à chaud ou à froid, que ce soit pour des grades standards ou spéciaux d'aciers inoxydables résistants à la corrosion. Un des principaux atouts de cette norme réside dans sa portée large, englobant les structures à destination générale, ce qui inclut également les applications en contact avec des denrées alimentaires. Cela souligne son importance dans les secteurs où la sécurité alimentaire et l'hygiène sont primordiales, garantissant que les matériaux en acier inoxydable respectent des critères stricts de qualité et de sécurité. En outre, il est essentiel de noter que les conditions générales de livraison techniques définies dans la norme EN 10021 s'appliquent en complément, renforçant ainsi la rigueur et la fiabilité des spécifications fournies par la norme EN 10088-2:2024. Cela assure une cohérence dans la qualité des matériaux tout en offrant des lignes directrices claires pour les utilisateurs. Cependant, il est important de préciser que cette norme ne s'applique pas aux composants fabriqués par un traitement ultérieur des formes de produits mentionnées, ce qui précise encore plus son domaine d'application et permet de limiter les interprétations erronées. Dans l'ensemble, la norme EN 10088-2:2024 est un document crucial pour tous les acteurs du marché des aciers inoxydables, fournissant un cadre normatif solide et pertinent qui favorise la qualité, la sécurité et l'efficacité dans l'utilisation des aciers inoxydables résistants à la corrosion pour des usages généraux.
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...