ISO 16834:2012
(Main)Welding consumables — Wire electrodes, wires, rods and deposits for gas shielded arc welding of high strength steels — Classification
Welding consumables — Wire electrodes, wires, rods and deposits for gas shielded arc welding of high strength steels — Classification
ISO 16834:2012 specifies requirements for classification of wire electrodes, wires, rods and all-weld metal deposits in the as-welded condition and in the post-weld heat-treated (PWHT) condition for gas shielded metal arc welding and tungsten inert-gas welding of high-strength steels with a minimum yield strength greater than 500 MPa, or a minimum tensile strength greater than 570 MPa. One wire electrode can be tested and classified with different shielding gases. ISO 16834:2012 is a combined specification providing for classification utilizing a system based upon the yield strength and the average impact energy of 47 J of all-weld metal, or utilizing a system based upon the tensile strength and the average impact energy of 27 J of all-weld metal.
Produits consommables pour le soudage — Fils-électrodes, fils, baguettes et dépôts pour le soudage à l'arc sous flux gazeux des aciers à haute résistance — Classification
L'ISO 16834:2012 spécifie les exigences relatives à la classification des fils-électrodes, des fils, des baguettes et du métal fondu à l'état brut de soudage ou après traitement thermique après soudage (PWHT) pour le soudage à l'arc sous protection gazeuse et le soudage TIG des aciers à haute résistance ayant une limite d'élasticité minimale supérieure à 500 MPa, ou une limite de résistance à la traction de 570 MPa. Un fil-électrode peut être soumis aux essais et classifié en utilisant différents gaz de protection. L'ISO 16834:2012 propose une spécification mixte permettant une classification utilisant soit un système basé sur la limite d'élasticité et l'énergie de rupture moyenne de 47 J pour le métal fondu hors dilution, soit un système basé sur la résistance à la traction et l'énergie de rupture moyenne de 27 J pour le métal fondu hors dilution.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 16834
Second edition
2012-05-01
Welding consumables — Wire electrodes,
wires, rods and deposits for gas shielded
arc welding of high strength steels —
Classification
Produits consommables pour le soudage — Fils-électrodes, fils,
baguettes et dépôts pour le soudage à l'arc sous flux gazeux des aciers
à haute résistance — Classification
Reference number
©
ISO 2012
© ISO 2012
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2012 – All rights reserved
Contents Page
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Classification . 2
4 Symbols and requirements . 3
4.1 Symbol for the product/process . 3
4.2 Symbol for strength and elongation properties of all-weld metal . 3
4.3 Symbol for impact properties of all-weld metal . 4
4.4 Symbol for shielding gas . 4
4.5 Symbol for the chemical composition of wire electrodes, wires and rods . 5
4.6 Symbol for condition of post-weld heat treatment . 5
5 Mechanical tests . 9
5.1 Preheating and interpass temperatures . 9
5.2 Welding conditions and pass sequence . 10
5.3 Post-weld heat-treated condition . 10
6 Chemical analysis . 11
7 Rounding procedure . 11
8 Retest . 11
9 Technical delivery conditions . 11
10 Examples of designation . 12
Bibliography . 14
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 16834 was prepared by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee
SC 3, Welding consumables.
This second edition cancels and replaces the first edition (ISO 16834:2006), which has been technically
revised.
The main changes compared to the previous edition are:
a) in 4.4, the separation between the A and B side has been eliminated;
b) in Table 3B, the chemical composition has been changed for 4M31 and N5M3;
c) footnote a to Table 3B has been redrafted to give more precision;
d) the designation examples in Clause 10 have been modified.
Requests for official interpretations of any aspect of this International Standard should be directed to the
Secretariat of ISO/TC 44/SC 3 via your national standards body. A complete listing of these bodies can be
found at www.iso.org.
iv © ISO 2012 – All rights reserved
Introduction
This International Standard recognizes that there are two somewhat different approaches in the global market
to classifying a given wire electrode, wire, rod or deposit, and allows for either or both to be used to suit a
particular market need. Application of either type of classification designation (or of both where suitable)
identifies a product as classified in accordance with this International Standard. The classification in
[1]
accordance with system A is mainly based on EN 12534:1999 . The classification in accordance with
system B is mainly based upon standards used around the Pacific Rim. Future revisions will aim to merge the
two systems into a single classification system.
This International Standard provides a classification for the designation of wire electrodes, wires, rods and
deposits in terms of their chemical composition and, where required, in terms of the yield strength, tensile
strength and elongation of the all-weld metal. The ratio of yield to tensile strength of weld metal is generally
higher than that of the parent metal. Users should note that matching weld metal yield strength to parent metal
yield strength does not necessarily ensure that the weld metal tensile strength matches that of the parent
material. Thus, where the application requires matching tensile strength, selection of the consumable should
be made by reference to column 3 of Table 1A or 1B, as appropriate.
INTERNATIONAL STANDARD ISO 16834:2012(E)
Welding consumables — Wire electrodes, wires, rods and
deposits for gas shielded arc welding of high strength steels —
Classification
1 Scope
This International Standard specifies requirements for classification of wire electrodes, wires, rods and all-
weld metal deposits in the as-welded condition and in the post-weld heat-treated (PWHT) condition for gas
shielded metal arc welding and tungsten inert-gas welding of high-strength steels with a minimum yield
strength greater than 500 MPa, or a minimum tensile strength greater than 570 MPa. One wire electrode can
be tested and classified with different shielding gases.
This International Standard is a combined specification providing for classification utilizing a system based
upon the yield strength and the average impact energy of 47 J of all-weld metal, or utilizing a system based
upon the tensile strength and the average impact energy of 27 J of all-weld metal.
e) Clauses, subclauses and tables which carry the suffix letter “A” are applicable only to wire electrodes,
wires, rods and deposits classified according to the system based upon the yield strength and the
average impact energy of 47 J of all-weld metal under this International Standard.
f) Clauses, subclauses and tables which carry the suffix letter “B” are applicable only to wire electrodes,
wires, rods and deposits classified according to the system based upon the tensile strength and the
average impact energy of 27 J of all-weld metal under this International Standard.
g) Clauses, subclauses and tables which do not have either the suffix letter “A” or the suffix letter “B” are
applicable to all wire electrodes, wires, rods and deposits classified under this International Standard.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 544, Welding consumables — Technical delivery conditions for filler materials and fluxes — Type of
product, dimensions, tolerances and markings
ISO 13916, Welding — Guidance on the measurement of preheating temperature, interpass temperature and
preheat maintenance temperature
ISO 14175:2008, Welding consumables — Gases and gas mixtures for fusion welding and allied processes
ISO 14344, Welding consumables — Procurement of filler materials and fluxes
ISO 15792-1:2000, Welding consumables — Test methods — Part 1: Test methods for all-weld metal test
specimens in steel, nickel and nickel alloys
ISO 80000-1:2009, Quantities and units — Part 1: General
3 Classification
Classification designations are based upon two approaches to indicate the tensile properties and the impact
properties of the all-weld metal obtained with a given wire electrode, wire or rod. The two designation
approaches include additional designators for some other classification requirements, but not all, as is clear
from the following clauses. In most cases, a given commercial product can be classified according to the
classification requirements in both systems. Then either or both classification designations can be used for the
product.
A wire electrode, wire or rod shall be classified in accordance with its chemical composition in Table 3A or
Table 3B. A weld deposit shall be classified with additional symbols in accordance with the mechanical
properties of its all-weld metal, using a shielding gas from a specific group.
3A Classification by yield strength and 3B Classification by tensile strength and
47 J impact energy 27 J impact energy
The classification is divided into six parts: The classification is divided into five parts:
1) the first part gives a symbol indicating the 1) the first part gives a symbol indicating the
product/process to be identified; product/process to be identified;
2) the second part gives a symbol indicating the 2) the second part gives a symbol indicating the
strength and elongation of all-weld metal (see strength and elongation of the all-weld metal in
Table 1A); either the as-welded or post-weld heat-treated
condition (see Table 1B);
3) the third part gives a symbol indicating the 3) the third part gives a symbol indicating the
impact properties of all-weld metal (see impact properties of all-weld metal in the same
Table 2); condition as specified for the tensile strength
(see Table 2). The letter “U” after this designa-
tor indicates that the deposit meets an average
optional requirement of 47 J at the designated
Charpy test temperature;
4) the fourth part gives a symbol indicating the 4) the fourth part gives a symbol indicating the
shielding gas used (see 4.4); shielding gas used (see 4.4);
5) the fifth part gives a symbol indicating the 5) the fifth part gives a symbol indicating the
chemical composition of the wire electrode, wire chemical composition of the wire electrode, wire
or rod used (see Table 3A); or rod used (see Table 3B).
6) the sixth part gives a symbol indicating the
post-weld heat treatment in case this is applied
(see 4.6A).
2 © ISO 2012 – All rights reserved
4 Symbols and requirements
4.1 Symbol for the product/process
The symbol for the wire electrode, wire or rod used in the arc welding process shall be the letter G (gas
shielded metal arc welding) and/or W (gas shielded arc welding with non-consumable tungsten electrode).
4.2 Symbol for strength and elongation properties of all-weld metal
4.2A Classification by yield strength and 4.2B Classification by tensile strength and
47 J impact energy 27 J impact energy
The symbol in Table 1A indicates yield strength, The symbol in Table 1B indicates yield strength,
tensile strength and elongation of the all-weld metal tensile strength and elongation of the all-weld metal
in the as-welded condition determined in in the as-welded condition or in the post-weld heat-
accordance with Clause 5. treated condition determined in accordance with
Clause 5.
Table 1A — Symbol for tensile properties of Table 1B — Symbol for tensile properties of all-
all-weld metal weld metal
(Classification by yield strength (Classification by tensile strength
and 47 J impact energy) and 27 J impact energy)
a
Symbol Minimum Tensile Minimum Minimum Tensile Minimum
Symbol
a b b c
strength strength
yield strength elongation yield strength elongation
MPa
...
NORME ISO
INTERNATIONALE 16834
Deuxième édition
2012-05-01
Produits consommables pour le
soudage — Fils-électrodes, fils,
baguettes et dépôts pour le soudage à
l'arc sous flux gazeux des aciers à haute
résistance — Classification
Welding consumables — Wire electrodes, wires, rods and deposits for
gas shielded arc welding of high strength steels — Classification
Numéro de référence
©
ISO 2012
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2012
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2012 – Tous droits réservés
Sommaire Page
Avant-propos . iv
Introduction . v
1 Domaine d'application . 1
2 Références normatives . 1
3 Classification . 2
4 Symboles et exigences . 3
4.1 Symbole du produit et/ou du procédé . 3
4.2 Symbole des caractéristiques de résistance et d'allongement du métal fondu hors
dilution . 3
4.3 Symbole de la résistance à la flexion par choc du métal fondu hors dilution . 4
4.4 Symbole du gaz de protection . 5
4.5 Symbole de la composition chimique des fil-électrodes, fils et baguettes . 5
4.6 Symbole de l'état de traitement thermique après soudage . 5
5 Essais mécaniques . 9
5.1 Températures de préchauffage et entre passes . 9
5.2 Conditions de soudage et séquence des passes . 10
5.3 État de traitement thermique après soudage . 11
6 Analyse chimique . 11
7 Mode opératoire d’arrondissage . 12
8 Contre-essai . 12
9 Conditions techniques de livraison . 12
10 Exemples de désignation . 12
Bibliographie . 15
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 16834 a été élaborée par le comité technique ISO/TC 44, Soudage et techniques connexes,
sous-comité SC 3, Produits consommables pour le soudage.
Cette deuxième édition annule et remplace la première édition (ISO 16834:2006), qui a fait l'objet d'une
révision technique.
Les principaux changements par rapport à l’édition précédente sont les suivants:
a) en 4.4, la distinction entre les classifications A et B a été supprimée;
b) dans le Tableau 3B, la composition chimique pour 4M31 et N5M3 a été modifiée;
c) la note a dans le Tableau 3B a été révisée afin de la rendre plus précise;
d) les exemples de désignation dans l’Article 10 ont été révisés.
Il convient d'adresser les demandes d'interprétation officielles de l'un quelconque des aspects de la présente
Norme internationale au secrétariat de l'ISO/TC 44/SC 3 via votre organisme national de normalisation. La
liste exhaustive de ces organismes peut être trouvée à l'adresse www.iso.org.
iv © ISO 2012 – Tous droits réservés
Introduction
La présente Norme internationale tient compte du fait qu'il existe deux approches quelque peu différentes
pour classifier, au niveau du marché mondial, un fil-électrode, un fil, une baguette ou un dépôt donné et
permet l'utilisation de l'une de ces deux approches ou des deux à la fois, pour répondre à une exigence
spécifique du marché. L'utilisation, pour la classification, de l'un de ces deux types de désignation (ou des
deux, s'il y a lieu) permet l'identification d'un produit classifié suivant la présente Norme internationale. La
[1]
classification suivant le système A est principalement basée sur l'EN 12534:1999 . La classification suivant
le système B est principalement basée sur les normes utilisées dans la zone Pacifique. Les révisions futures
viseront à fusionner les deux approches au sein d'un système de classification unique.
La présente Norme internationale décrit un système de classification de la désignation des fils-électrodes, fils,
baguettes et dépôts d'après leur composition chimique et, si nécessaire, d'après la limite d'élasticité, la
résistance à la traction et l'allongement à la rupture du métal fondu hors dilution. Le rapport entre la limite
d'élasticité et la résistance à la traction du métal fondu est généralement plus élevé que celui du métal de
base. Il est à noter qu'une bonne correspondance des limites d'élasticité du métal fondu et du métal de base
ne garantit pas nécessairement que la résistance à la traction du métal fondu corresponde à celle du métal de
base. Ainsi, lorsque l'application exige cette correspondance, il est nécessaire de choisir le produit
consommable en référence à la colonne 3 du Tableau 1A ou 1B, selon le cas.
NORME INTERNATIONALE ISO 16834:2012(F)
Produits consommables pour le soudage — Fils-électrodes, fils,
baguettes et dépôts pour le soudage à l'arc sous flux gazeux
des aciers à haute résistance — Classification
1 Domaine d'application
La présente Norme internationale spécifie les exigences relatives à la classification des fils-électrodes, des fils,
des baguettes et des dépôts de métal fondu hors dilution à l'état brut de soudage ou après traitement
thermique après soudage (PWHT) pour le soudage à l'arc sous protection gazeuse et le soudage TIG des
aciers à haute résistance ayant une limite d'élasticité minimale supérieure à 500 MPa, ou une limite de
résistance à la traction supérieure à 570 MPa. Un fil-électrode peut être soumis aux essais et classifié en
utilisant différents gaz de protection.
La présente Norme internationale propose une spécification mixte permettant une classification utilisant soit
un système basé sur la limite d'élasticité et l'énergie de rupture moyenne de 47 J pour le métal fondu hors
dilution, soit un système basé sur la résistance à la traction et l'énergie de rupture moyenne de 27 J pour le
métal fondu hors dilution.
a) Les articles, les paragraphes et les tableaux qui portent le suffixe «A» ne sont applicables qu'aux fils-
électrodes, fils, baguettes et dépôts classifiés d'après le système basé sur la limite d'élasticité et l'énergie
de rupture moyenne de 47 J pour le métal fondu hors dilution conformément à la présente Norme
internationale.
b) Les articles, les paragraphes et les tableaux qui portent le suffixe «B» ne sont applicables qu'aux fils-
électrodes, fils, baguettes et dépôts classifiés d'après le système basé sur la résistance à la traction et
l'énergie de rupture moyenne de 27 J pour le métal fondu hors dilution conformément à la présente
Norme internationale.
c) Les articles, les paragraphes et les tableaux qui ne portent ni le suffixe «A», ni le suffixe «B» sont
applicables à tous les fils-électrodes, fils, baguettes et dépôts classifiés conformément à la présente
Norme internationale.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 544, Produits consommables pour le soudage — Conditions techniques de livraison des matériaux
d'apport et des flux — Type de produit, dimensions, tolérances et marquage
ISO 13916, Soudage — Lignes directrices pour le mesurage de la température de préchauffage, de la
température entre passes et de la température de maintien du préchauffage
ISO 14175:2008, Produits consommables pour le soudage — Gaz et mélanges gazeux pour le soudage par
fusion et les techniques connexes
ISO 14344, Produits consommables pour le soudage — Approvisionnement en matériaux d'apport et flux
ISO 15792-1:2000, Produits consommables pour le soudage — Méthodes d'essai — Partie 1: Méthodes
d'essai pour les éprouvettes de métal fondu hors dilution pour le soudage de l'acier, du nickel et des alliages
de nickel
ISO 80000-1:2009, grandeurs et unités — Partie 1: Généralités
3 Classification
Les désignations des classifications reposent sur deux méthodes pour indiquer les caractéristiques de traction
et de résistance à la flexion par choc du métal fondu hors dilution obtenu avec un fil-électrode, un fil ou une
baguette donné(e). Les deux méthodes de désignation comportent des indicateurs supplémentaires pour
certaines autres exigences de classification, mais pas toutes, comme il est précisé dans la suite de la
présente Norme internationale. Dans la plupart des cas, un produit commercial donné peut être classifié dans
les deux systèmes selon les exigences de classification. Il est alors possible d'utiliser pour le produit l'un des
deux systèmes de désignation, ou les deux systèmes.
Un fil-électrode, un fil ou une baguette doit être classifié conformément à sa composition chimique figurant
dans le Tableau 3A ou le Tableau 3B. Un métal fondu doit être classifié avec des symboles supplémentaires
selon les propriétés mécaniques du métal fondu hors dilution, en utilisant un gaz de protection d'un groupe
spécifique.
3A Classification d'après la limite d'élasticité 3B Classification d'après la résistance à la
et l'énergie de rupture de 47 J traction et l'énergie de rupture de 27 J
La classification est divisée en six parties. La classification est divisée en cinq parties.
1) La première partie donne le symbole du produit 1) La première partie donne le symbole du produit
et/ou du procédé à identifier. et/ou du procédé à identifier.
2) La deuxième partie donne le symbole de la 2) La deuxième partie donne le symbole de la
résistance et de l'allongement du métal fondu résistance et de l'allongement du métal fondu
hors dilution (voir Tableau 1A). hors dilution soit à l'état brut de soudage, soit
après traitement thermique après soudage (voir
Tableau 1B).
3) La troisième partie donne le symbole de la 3) La troisième partie donne le symbole de la
résistance à la flexion par choc du métal fondu résistance à la flexion par choc du métal fondu
hors dilution (voir Tableau 2). hors dilution dans le même état que celui
spécifié pour la résistance à la traction (voir
Tableau 2). La lettre «U» placée après cet
indicateur indique que le dépôt satisfait à
l'exigence moyenne facultative de 47 J à la
température d'essai Charpy désignée.
4) La quatrième partie donne le symbole du type 4) La quatrième partie donne le symbole du type
de gaz de protection utilisé (voir 4.4). de gaz de protection utilisé (voir 4.4).
5) La cinquième partie donne le symbole de la 5) La cinquième partie donne le symbole de la
composition chimique du fil-électrode, du fil ou composition chimique du fil-électrode, du fil ou
de la baguette util
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.