ISO 15614-13:2012

Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 13: Upset (resistance butt) and flash welding

ISO 15614-13:2012 specifies tests for the qualification of welding procedure specifications applicable to upset (resistance butt) welding and flash welding of metallic materials, e.g. with solid, tubular, flat or circular cross-section. Its basic principles can also be applied to other resistance welding processes when this is stated in the specification. ISO 15614-13:2012 defines the conditions for carrying out tests and the limits of validity of a qualified welding procedure for all the practical welding operations that it covers. The tests required to qualify the procedure for a particular component or assembly depend on the performance and quality requirements of the component or assembly, as defined in the design specification. The tests are intended to be carried out in accordance with the requirements of ISO 15614-13:2012, unless more severe tests are specified by the relevant application standard or specification and when these apply. ISO 15614-13:2012 covers the following resistance welding processes, as defined in ISO 4063: 24 flash welding, using direct current or alternating current with various movement sequences, constant flashing and pulsed flashing; 25 resistance upset welding, using direct current or alternating current with various pressure sequences.

Descriptif et qualification d'un mode opératoire de soudage pour les matériaux métalliques — Épreuve de qualification d'un mode opératoire de soudage — Partie 13: Soudage en bout par résistance pure et soudage par étincelage

L'ISO 15614-13 spécifie des épreuves pour qualifier un descriptif de mode opératoire de soudage. Elle est applicable au soudage en bout par résistance pure et au soudage par étincelage des matériaux métalliques, par exemple des sections droites pleines ou tubulaires, plates ou circulaires. Ses principes de base peuvent être appliqués à d'autres procédés de soudage par résistance lorsque cela est indiqué dans la spécification. L'ISO 15614-13 définit les conditions d'exécution des épreuves de qualification et les limites de validité d'un mode opératoire qualifié, pour toutes les opérations pratiques de soudage qu'elle couvre. Les épreuves exigées pour la qualification du mode opératoire dans le cas d'un composant ou d'un assemblage particulier dépendent des exigences sur les performances et la qualité du composant ou de l'assemblage, telles que définies dans la spécification de conception. Les épreuves de qualification sont réalisées conformément aux exigences de l'ISO 15614-13, sauf si une norme d'application ou une spécification spécifie des essais plus sévères et que ceux-ci s'appliquent. L'ISO 15614-13 traite des procédés de soudage par résistance suivants, tels que définis dans l'ISO 4063:2009: 24 soudage par étincelage en courant continu ou en courant alternatif avec diverses séquences de mouvement, étincelage continu et étincelage intermittent; 25 soudage en bout par résistance pure, en courant continu ou en courant alternatif avec diverses séquences d'effort.

General Information

• Status: Withdrawn
• Publication Date: 25-Jun-2012
• Withdrawal Date: 25-Jun-2012
• ICS: 25.160.10 - Welding processes
• Technical Committee: ISO/TC 44/SC 6 - Resistance welding and allied mechanical joining
• Drafting Committee: ISO/TC 44/SC 6/WG 3 - Quality management and testing
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 18-Nov-2021

Relations

• Revised: ISO 15614-13:2021 - Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 13: Upset (resistance butt) and flash welding
• Effective Date: 23-Apr-2020
• Revises: ISO 15614-13:2005 - Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 13: Resistance butt and flash welding
• Effective Date: 28-Feb-2009

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 15614-13
Second edition
2012-07-01

Specification and qualification of welding
procedures for metallic materials —
Welding procedure test —
Part 13:
Upset (resistance butt) and flash welding
Descriptif et qualification d'un mode opératoire de soudage pour les
matériaux métalliques — Épreuve de qualification d'un mode opératoire
de soudage —
Partie 13: Soudage en bout par résistance pure et soudage par
étincelage




Reference number
ISO 15614-13:2012(E)
©
ISO 2012

---------------------- Page: 1 ----------------------
ISO 15614-13:2012(E)

COPYRIGHT PROTECTED DOCUMENT


©  ISO 2012
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland

ii © ISO 2012 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 15614-13:2012(E)
Contents Page
Foreword . iv
Introduction . vi
1  Scope . 1
2  Normative references . 1
3  Terms and definitions . 2
4  Preliminary welding procedure specification . 2
5  Welding procedure test . 3
6  Test pieces and test specimens . 3
6.1  General . 3
6.2  Shape and dimensions of test specimens . 3
6.3  Welding of components, test pieces or test specimens . 5
7  Testing and examination . 5
7.1  Extent of testing . 5
7.2  Non-destructive testing (NDT) . 5
7.3  Destructive tests . 6
7.4  Macrosection . 6
7.5  Hardness distribution . 6
7.6  Re-testing . 6
8  Range of qualification . 7
8.1  General . 7
8.2  Related to the manufacturer . 7
8.3  Related to the parent metal . 7
8.4  Welding procedures . 7
8.5  Test certificate . 7
9  Welding procedure qualification record . 7
Annex A (informative) Example of welding procedure qualification — Test certificate . 8
Annex B (informative) Example of welding procedure qualifications record form (WPQR) . 9

© ISO 2012 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 15614-13:2012(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 15614-13 was prepared by Technical Committee ISO/TC 44, Welding and allied processes,
Subcommittee SC 6, Resistance welding and allied mechanical joining.
This second edition cancels and replaces the first edition (ISO 15614-13:2005), which has been technically
revised.
ISO 15614 consists of the following parts, under the general title Specification and qualification of welding
procedures for metallic materials — Welding procedure test:
 Part 1: Arc and gas welding of steels and arc welding of nickel and nickel alloys
 Part 2: Arc welding of aluminium and its alloys
 Part 3: Fusion welding of non-alloyed and low-alloyed cast irons
 Part 4: Finishing welding of aluminium castings
 Part 5: Arc welding of titanium, zirconium and their alloys
 Part 6: Arc and gas welding of copper and its alloys
 Part 7: Overlay welding
 Part 8: Welding of tubes to tube-plate joints
 Part 9: Arc underwater hyperbaric wet welding
 Part 10: Hyperbaric dry welding:
 Part 11: Electron and laser beam welding
 Part 12: Spot, seam and projection welding
 Part 13: Upset (resistance butt) and flash welding
 Part 14: Laser-arc hybrid welding of steels, nickel and nickel alloys
iv © ISO 2012 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 15614-13:2012(E)
Requests for official interpretations of any aspect of this part of ISO 15614 should be directed to the
Secretariat of ISO/TC 44/SC 10 via your national standards body. A complete listing of these bodies can be
found at www.iso.org.
© ISO 2012 – All rights reserved v

---------------------- Page: 5 ----------------------
ISO 15614-13:2012(E)
Introduction
It is intended that all new welding procedure qualifications be carried out in accordance with this part of
ISO 15614 from the date of its issue.
However, this part of ISO 15614 does not invalidate previous welding procedure qualifications made to other
standards or specifications, provided the intent of its technical requirements is satisfied and the previous
welding procedure qualifications are relevant to the application and production work on which they are to be
employed.
Also, where additional tests have to be carried out to make the qualification technically equivalent, it is
necessary only to perform the additional tests on a test piece made in accordance with this part of ISO 15614.
The various parts of ISO 15614 comprise, in their turn, a series of International Standards on welding, details
of which are given in ISO 15607:2003, Annex A.
vi © ISO 2012 – All rights reserved

---------------------- Page: 6 ----------------------
INTERNATIONAL STANDARD ISO 15614-13:2012(E)

Specification and qualification of welding procedures for
metallic materials — Welding procedure test —
Part 13:
Upset (resistance butt) and flash welding
1 Scope
This part of ISO 15614 specifies tests for the qualification of welding procedure specifications applicable to
upset (resistance butt) welding and flash welding of metallic materials, e.g. with solid, tubular, flat or circular
cross-section. Its basic principles can also be applied to other resistance welding processes when this is
stated in the specification.
This part of ISO 15614 defines the conditions for carrying out tests and the limits of validity of a qualified
welding procedure for all the practical welding operations that it covers. The tests required to qualify the
procedure for a particular component or assembly depend on the performance and quality requirements of the
component or assembly, as defined in the design specification. The tests are intended to be carried out in
accordance with the requirements of this part of ISO 15614, unless more severe tests are specified by the
relevant application standard or specification and when these apply.
NOTE Specific service, material, or manufacturing conditions can require more comprehensive testing than specified
by this part of ISO 15614. Such tests can include microsections, fatigue or endurance tests, impact tests, radiographic
testing, ultrasonic testing, corrosion testing and tests of components or complete welded assemblies.
This part of ISO 15614 covers the following resistance welding processes, as defined in ISO 4063:
 24 flash welding, using direct current or alternating current with various movement sequences, constant
flashing and pulsed flashing;
 25 resistance upset welding, using direct current or alternating current with various pressure sequences.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 4063:2009, Welding and allied processes — Nomenclature of processes and reference numbers
ISO 4136, Destructive tests on welds in metallic materials — Transverse tensile test
ISO 5173, Destructive tests on welds in metallic materials — Bend tests
ISO 6520-2, Welding and allied processes — Classification of geometric imperfections in metallic materials —
Part 2: Welding with pressure
ISO 6892-1, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
© ISO 2012 – All rights reserved 1

---------------------- Page: 7 ----------------------
ISO 15614-13:2012(E)
ISO 9015-1, Destructive tests on welds in metallic materials — Hardness testing — Part 1: Hardness test on
arc welded joints
ISO 9015-2, Destructive tests on welds in metallic materials — Hardness testing — Part 2: Microhardness
testing of welded joints
ISO 11666, Non-destructive testing of welds — Ultrasonic testing of welded joints — Acceptance levels
ISO 14271, Resistance welding — Vickers hardness testing (low force and microhardness) of resistance spot,
projection, and seam welds
ISO 14732, Welding personnel — Approval testing of welding operators for fusion welding and of resistance
weld setters for fully mechanized and automatic welding of metallic materials
ISO 15607:2003, Specification and qualification of welding procedures for metallic materials — General rules
ISO/TR 15608:2005, Welding — Guidelines for a metallic materials grouping system
ISO 15609-5, Specification and qualification of welding procedures for metallic materials — Welding
procedure specification — Part 5: Resistance welding
ISO 15620:2000, Welding — Friction welding of metallic materials
ISO 17637, Non-destructive testing of welds — Visual testing of fusion-welded joints
ISO 17638, Non-destructive testing of welds — Magnetic particle testing
ISO 17639, Destructive tests on welds in metallic materials — Macroscopic and microscopic examination of
welds
ISO 17640, Non-destructive testing of welds — Ultrasonic testing — Techniques, testing levels, and
assessment
ISO 17643, Non-destructive testing of welds — Eddy current testing of welds by complex-plane analysis
ISO 20482, Metallic materials — Sheet and strip — Erichsen cupping test
ISO 23277, Non-destructive testing of welds — Penetrant testing of welds — Acceptance levels
ISO 23278, Non-destructive testing of welds — Magnetic particle testing of welds — Acceptance levels
ISO 23279, Non-destructive testing of welds — Ultrasonic testing — Characterization of indications in welds
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 15607 and ISO 6520-2 apply.
4 Preliminary welding procedure specification
The preliminary welding procedure specification (pWPS) shall be prepared in accordance with ISO 15609-5. It
shall specify all relevant parameters and requirements.
2 © ISO 2012 – All rights reserved

---------------------- Page: 8 ----------------------
ISO 15614-13:2012(E)
5 Welding procedure test
The manufacturing and testing of components and/or test pieces representing the type of welding used in
production shall be in accordance with Clauses 6 and 7.
The resistance weld setter who satisfactorily undertakes the welding procedure test in accordance with this
part of ISO 15614 shall be qualified for the appropriate range of qualification given in ISO 14732.
6 Test pieces and test specimens
6.1 General
The welded assembly tested shall be the actual component used in production or a standardized test piece
according to references included in 6.2.
Test specimens may be cut from the actual component if required. Test pieces are to be tested separately, in
accordance with 6.2.
6.2 Shape and dimensions of test specimens
6.2.1 General
The testing includes non-destructive testing (NDT) and/or destructive testing.
The selection of test types and the number of test specimens depends on the performance, safety and quality
requirements of the component or assembly and shall be established before any qualification is undertaken.
Examples are given in Table 1.
If not otherwise specified, test specimens of the shape and dimensions stipulated in 6.2.2 to 6.2.6 shall be
used.
© ISO 2012 – All rights reserved 3

---------------------- Page: 9 ----------------------
ISO 15614-13:2012(E)
Table 1 — Examples for testing and examination of test specimens
Extent of test
Test specimen Test type
Test class A Test class B
Bars/rods Visual examination Every weld Every weld
Penetrant t
...

NORME ISO
INTERNATIONALE 15614-13
Deuxième édition
2012-07-01


Descriptif et qualification d'un mode
opératoire de soudage pour les matériaux
métalliques — Épreuve de qualification
d'un mode opératoire de soudage —
Partie 13:
Soudage en bout par résistance pure et
soudage par étincelage
Specification and qualification of welding procedures for metallic
materials — Welding procedure test —
Part 13: Upset (resistance butt) and flash welding




Numéro de référence
ISO 15614-13:2012(F)
©
ISO 2012

---------------------- Page: 1 ----------------------
ISO 15614-13:2012(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT


©  ISO 2012
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Publié en Suisse

ii © ISO 2012 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 15614-13:2012(F)
Sommaire Page
Avant-propos . iv
1  Domaine d'application . 1
2  Références normatives . 1
3  Termes et définitions . 3
4  Descriptif de mode opératoire de soudage préliminaire . 3
5  Épreuve de qualification du mode opératoire de soudage . 3
6  Assemblages de qualification et éprouvettes . 3
6.1  Généralités . 3
6.2  Forme et dimensions des éprouvettes . 3
6.3  Soudage des composants, des assemblages de qualification ou des éprouvettes . 5
7  Essais et contrôle . 5
7.1  Étendue du contrôle . 5
7.2  Essais non destructifs (END) . 5
7.3  Essais destructifs . 6
7.4  Coupe macrographique . 6
7.5  Filiation de dureté . 6
7.6  Contre-essais . 6
8  Domaine de validité . 7
8.1  Généralités . 7
8.2  Fabricant . 7
8.3  Métaux de base . 7
8.4  Modes opératoires de soudage . 7
8.5  Certificat de qualification. 7
9  Procès-verbal de qualification du mode opératoire de soudage . 7
Annexe A (informative) Exemple de qualification de mode opératoire de soudage — Certificat de
qualification . 8
Annexe B (informative) Exemple de procès-verbal de qualification de mode opératoire de
soudage (PV-QMOS) . 9

© ISO 2012 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 15614-13:2012(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 15614-13 a été élaborée par le comité technique ISO/TC 44, Soudage et techniques connexes,
sous-comité SC 6, Soudage par résistance et assemblage mécanique allié.
Cette deuxième édition annule et remplace la première édition (ISO 15614-13:2005), qui a fait l'objet d'une
révision technique.
L'ISO 15614 comprend les parties suivantes, présentées sous le titre général Descriptif et qualification d'un
mode opératoire de soudage pour les matériaux métalliques — Épreuve de qualification d'un mode opératoire
de soudage:
 Partie 1: Soudage à l'arc et aux gaz des aciers et soudage à l'arc des nickels et alliages de nickel
 Partie 2: Soudage à l'arc de l'aluminium et de ses alliages
 Partie 3: Soudage par fusion des fontes non alliées et faiblement alliées
 Partie 4: Réparation par soudage pour les travaux de finition des pièces moulées en aluminium
 Partie 5: Soudage à l'arc sur titane, zirconium et leurs alliages
 Partie 6: Soudage à l'arc et aux gaz du cuivre et de ses alliages
 Partie 7: Rechargement par soudage
 Partie 8: Soudage de tubes sur plaques tubulaires
 Partie 9: Soudage hyperbare en pleine eau
 Partie 10: Soudage hyperbare en caisson
 Partie 11: Soudage par faisceau d'électrons et par faisceau laser
 Partie 12: Soudage par points, à la molette et par bossages
iv © ISO 2012 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO 15614-13:2012(F)
 Partie 13: Soudage en bout par résistance pure et soudage par étincelage
 Partie 14: Soudage hybride laser-arc des aciers, du nickel et des alliages de nickel
Il convient d'adresser les demandes d'interprétation officielles de l'un quelconque des aspects de la présente
partie de l'ISO 15614 au secrétariat de l'ISO/TC 44/SC 10 via votre organisme national de normalisation. La
liste exhaustive de ces organismes peut être trouvée à l'adresse www.iso.org.
© ISO 2012 – Tous droits réservés v

---------------------- Page: 5 ----------------------
ISO 15614-13:2012(F)
Introduction
Toutes nouvelles qualifications de modes opératoires de soudage sont à effectuer conformément à la
présente partie de l'ISO 15614 dès sa publication.
Toutefois, la présente partie de l'ISO 15614 n'invalide pas les qualifications de modes opératoires de soudage
existantes préalablement exécutées à partir d'autres normes ou spécifications, tant que l'intention des
exigences techniques est respectée, et que les qualifications existantes correspondent à l'application et au
travail de fabrication auxquels elles s'appliquent.
Également, si des essais complémentaires sont à réaliser pour obtenir une qualification techniquement
équivalente, il est seulement nécessaire d'effectuer les essais complémentaires sur un assemblage de
qualification exécuté conformément à la présente partie de l'ISO 15614.
Les différentes parties de l'ISO 15614 comprennent, à leur tour, une série de Normes internationales sur le
soudage dont le détail est donné dans l'ISO 15607:2003, Annexe A.

vi © ISO 2012 – Tous droits réservés

---------------------- Page: 6 ----------------------
NORME INTERNATIONALE ISO 15614-13:2012(F)

Descriptif et qualification d'un mode opératoire de soudage
pour les matériaux métalliques — Épreuve de qualification d'un
mode opératoire de soudage —
Partie 13:
Soudage en bout par résistance pure et soudage par étincelage
1 Domaine d'application
La présente partie de l'ISO 15614 spécifie des épreuves pour qualifier un descriptif de mode opératoire de
soudage. Elle est applicable au soudage en bout par résistance pure et au soudage par étincelage des
matériaux métalliques, par exemple des sections droites pleines ou tubulaires, plates ou circulaires. Les
principes de base de la présente partie de l'ISO 15614 peuvent être appliqués à d'autres procédés de
soudage par résistance lorsque cela est indiqué dans la spécification.
La présente partie de l'ISO 15614 définit les conditions d'exécution des épreuves de qualification et les limites
de validité d'un mode opératoire qualifié, pour toutes les opérations pratiques de soudage qu'elle couvre. Les
épreuves exigées pour la qualification du mode opératoire dans le cas d'un composant ou d'un assemblage
particulier dépendent des exigences sur les performances et la qualité du composant ou de l'assemblage,
telles que définies dans la spécification de conception. Les épreuves de qualification sont réalisées
conformément aux exigences de la présente partie de l'ISO 15614, sauf si une norme d'application ou une
spécification spécifie des essais plus sévères et que ceux-ci s'appliquent.
NOTE Des conditions de service, des matériaux ou des conditions de fabrication spécifiques peuvent exiger des
épreuves plus complètes que celles spécifiées dans la présente partie de l'ISO 15614. De telles épreuves peuvent inclure
des coupes micrographiques, des essais de fatigue ou d'endurance, des essais de flexion par choc, des contrôles par
radiographie, des contrôles par ultrasons, des essais de corrosion et des essais sur des composants ou des assemblages
soudés complets.
La présente partie de l'ISO 15614 traite des procédés de soudage par résistance suivants, tels que définis
dans l'ISO 4063:
 24 soudage par étincelage en courant continu ou en courant alternatif avec diverses séquences de
mouvement, étincelage continu et étincelage intermittent;
 25 soudage en bout par résistance pure, en courant continu ou en courant alternatif avec diverses
séquences d'effort.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 4063:2009, Soudage et techniques connexes — Nomenclature et numérotation des procédés
ISO 4136, Essais destructifs des soudures sur matériaux métalliques — Essai de traction transversale
© ISO 2012 – Tous droits réservés 1

---------------------- Page: 7 ----------------------
ISO 15614-13:2012(F)
ISO 5173, Essais destructifs des soudures sur matériaux métalliques — Essais de pliage
ISO 6520-2, Soudage et techniques connexes — Classification des défauts géométriques dans les soudures
des matières métalliques — Partie 2: Soudage avec pression
ISO 6892-1, Matériaux métalliques — Essai de traction — Partie 1: Méthode d'essai à température ambiante
ISO 9015-1, Essais destructifs des soudures sur matériaux métalliques — Essais de dureté — Partie 1: Essai
de dureté des assemblages soudés à l'arc
ISO 9015-2, Essais destructifs des soudures sur matériaux métalliques — Essais de dureté — Partie 2: Essai
de microdureté des assemblages soudés
ISO 11666, Contrôle non destructif des assemblages soudés — Contrôle par ultrasons — Niveaux
d'acceptation
ISO 14271, Soudage par résistance — Essai de dureté Vickers (force réduite et essai de microdureté) sur
soudures par résistance par points, par bossages et à la molette
ISO 14732, Personnel en soudage — Épreuve de qualification des opérateurs soudeurs pour le soudage par
fusion et des régleurs en soudage par résistance pour le soudage automatique et entièrement automatique
des matériaux métalliques
ISO 15607:2003, Descriptif et qualification d'un mode opératoire de soudage pour les matériaux
métalliques — Règles générales
ISO/TR 15608:2005, Soudage — Lignes directrices pour un système de groupement des matériaux
métalliques
ISO 15609-5, Descriptif et qualification d'un mode opératoire de soudage pour les matériaux métalliques —
Descriptif d'un mode opératoire de soudage — Partie 5: Soudage par résistance
ISO 15620:2000, Soudage — Soudage par friction des matériaux métalliques
ISO 17637, Contrôle non destructif des assemblages soudés — Contrôle visuel des assemblages soudés par
fusion
ISO 17638, Contrôle non destructif des assemblages soudés — Contrôle par magnétoscopie
ISO 17639, Essais destructifs des soudures sur matériaux métalliques — Examens macroscopique et
microscopique des assemblages soudés
ISO 17640, Contrôle non destructif des assemblages soudés — Contrôle par ultrasons — Techniques,
niveaux d'essai et évaluation
ISO 17643, Contrôle non destructif des assemblages soudés — Contrôle par courants de Foucault des
assemblages soudés avec analyse des signaux dans le plan complexe
ISO 20482, Matériaux métalliques — Tôles et bandes — Essai d'emboutissage Erichsen
ISO 23277, Contrôle non destructif des assemblages soudés — Contrôle par ressuage des soudures —
Niveaux d'acceptation
ISO 23278, Contrôle non destructif des assemblages soudés — Contrôle par magnétoscopie des soudures —
Niveaux d'acceptation
ISO 23279, Contrôle non destructif des assemblages soudés — Contrôle par ultrasons — Caractérisation des
indications dans les assemblages soudés
2 © ISO 2012 – Tous droits réservés

---------------------- Page: 8 ----------------------
ISO 15614-13:2012(F)
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l'ISO 15607 et l'ISO 6520-2
s'appliquent.
4 Descriptif de mode opératoire de soudage préliminaire
Le descriptif de mode opératoire de soudage préliminaire (DMOS-P) doit être préparé conformément à
l'ISO 15609-5. Il doit spécifier tous les paramètres et les exigences correspondants.
5 Épreuve de qualification du mode opératoire de soudage
La réalisation et les essais des composants et/ou des assemblages de qualification représentant le type de
soudage utilisé en fabrication doivent être en conformité avec les Articles 6 et 7.
L'opérateur de soudage par résistance qui a réalisé de manière satisfaisante l'épreuve de qualification du
mode opératoire de soudage en conformité avec la présente partie de l'ISO 15614 doit être qualifié pour le
domaine de validité correspondant donné dans l'ISO 14732.
6 Assemblages de qualification et éprouvettes
6.1 Généralités
L'assemblage soudé soumis aux essais doit être un composant réel utilisé en fabrication ou un assemblage
de qualification normalisé suivant les références indiquées en 6.2.
Les éprouvettes peuvent être prélevées, si requis, dans les composants réels. Les assemblages de
qualification sont soumis aux essais séparément conformément à 6.2.
6.2 Forme et dimensions des éprouvettes
6.2.1 Généralités
Les contrôles, examens et essais englobent les essais non destructifs (END) et/ou les essais destructifs.
Le choix des méthodes de contrôle et d'essai ainsi que du nombre d'éprouvettes dépend des exigences
relatives aux performances, à la sécurité et à la qualité du composant ou de l'assemblage et doit être défini
avant d'entreprendre toute qualification. Des exemples sont indiqués au Tableau 1.
Sauf s'il en est spécifié différemment, les éprouvettes présentant les formes et les dimensions stipulées en
6.2.2 à 6.2.6 doivent être utilisées.
6.2.2 Éprouvette pour essai de traction
L'éprouvette doit être préparée en prenant en compte l'ISO 4136 et l'ISO 6892-1 et toute norme référencée
par contrat ou spécification à appliquer.
6.2.3 Éprouvette pour essai de pliage
L'éprouvette doit être préparée conformément à l'ISO 5173.
© ISO 2012 – Tous droits réservés 3

---------------------- Page: 9 ----------------------
ISO 15614-13:2012(F)
Tableau 1 — Exemples pour l'examen et les essais sur éprouvettes
Étendue des essais
Éprouvette Type d'ess
...