Plastics — Determination of temperature of deflection under load — Part 1: General test method

1.1 This document gives a general test method for the determination of the temperature of deflection under load (flexural stress under three-point loading) of plastics. Different types of test specimen and different constant loads are defined to suit different types of material. 1.2 ISO 75-2 gives specific requirements for plastics (including filled plastics and fibre-reinforced plastics in which the fibre length, prior to processing, is up to 7,5 mm) and ebonite, while ISO 75-3 gives specific requirements for high-strength thermosetting laminates and long-fibre-reinforced plastics in which the fibre length, prior to processing, is greater than 7,5 mm. 1.3 The methods specified are suitable for assessing the relative behaviour of different types of material at elevated temperature under load at a specified rate of temperature increase. The results obtained do not necessarily represent maximum applicable temperatures because, in practice, essential factors, such as time, loading conditions and nominal surface stress, can differ from the test conditions. True comparability of data can only be achieved for materials having the same room-temperature flexural modulus. 1.4 The methods specify preferred dimensions for the test specimens. 1.5 Data obtained using the test methods described are not intended to be used to predict actual end-use performance. The data are not intended for design analysis or prediction of the endurance of materials at elevated temperatures. 1.6 This method is commonly known as the heat deflection temperature or heat distortion temperature (HDT) test, although there is no official document using this designation.

Plastiques — Détermination de la température de fléchissement sous charge — Partie 1: Méthode d'essai générale

1 Domaine d'application 1.1 Le présent document décrit une méthode d'essai générale permettant de déterminer la température de fléchissement sous charge (contrainte de flexion sous mise en charge en trois points) des plastiques. Différents types d'éprouvettes et différentes charges constantes sont définis pour correspondre à des types de matériaux différents. 1.2 L'ISO 75-2 fournit des exigences particulières pour les plastiques (incluant les plastiques chargés et les plastiques renforcés de fibres, dans lesquels la longueur de fibre avant l'emploi est inférieure ou égale à 7,5 mm) et l'ébonite, et l'ISO 75-3 fournit des exigences particulières pour les stratifiés thermodurcissables à haute résistance et les plastiques renforcés de fibres longues, dans lesquels la longueur de fibre avant l'emploi est supérieure à 7,5 mm. 1.3 Les méthodes spécifiées permettent d'évaluer le comportement relatif sous charge des divers types de matériaux à température élevée, avec une élévation de la température à une vitesse spécifiée. Les résultats obtenus ne représentent pas nécessairement les températures maximales d'utilisation car, dans la pratique, des facteurs essentiels tels que le temps, les conditions de mise en charge et la contrainte superficielle nominale peuvent différer des conditions adoptées pour l'essai. Une comparabilité exacte des données ne peut être obtenue que pour des matériaux ayant le même module de flexion à température ambiante. 1.4 Les méthodes spécifient les dimensions recommandées pour les éprouvettes. 1.5 Les données obtenues en utilisant les méthodes d'essais décrites ne sont pas destinées à être utilisées pour prédire de véritables performances d'usage. Les données ne sont pas destinées à être utilisées pour les analyses de conception ou pour prévoir la résistance des matériaux à des températures élevées. 1.6 La présente méthode est communément connue sous le nom d'essai de déformation à chaud ou de fléchissement à chaud (HDT) bien qu'il n'existe pas de document officiel utilisant cette désignation.

General Information

Status
Published
Publication Date
27-Feb-2020
Current Stage
6060 - International Standard published
Start Date
28-Feb-2020
Completion Date
28-Feb-2020
Ref Project

RELATIONS

Buy Standard

Standard
ISO 75-1:2020 - Plastics -- Determination of temperature of deflection under load
English language
10 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 75-1:2020 - Plastiques -- Détermination de la température de fléchissement sous charge
French language
10 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (sample)

INTERNATIONAL ISO
STANDARD 75-1
Fourth edition
2020-02
Plastics — Determination of
temperature of deflection under
load —
Part 1:
General test method
Plastiques — Détermination de la température de fléchissement sous
charge —
Partie 1: Méthode d'essai générale
Reference number
ISO 75-1:2020(E)
ISO 2020
---------------------- Page: 1 ----------------------
ISO 75-1:2020(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2020

All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may

be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting

on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address

below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2020 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 75-1:2020(E)
Contents Page

Foreword ........................................................................................................................................................................................................................................iv

1 Scope ................................................................................................................................................................................................................................. 1

2 Normative references ...................................................................................................................................................................................... 1

3 Terms and definitions ..................................................................................................................................................................................... 2

4 Principle ........................................................................................................................................................................................................................ 3

5 Apparatus ..................................................................................................................................................................................................................... 3

5.1 Means of producing a flexural stress ................................................................................................................................... 3

5.2 Heating equipment .............................................................................................................................................................................. 4

5.3 Weights .......................................................................................................................................................................................................... 5

5.4 Temperature-measuring instrument ................................................................................................................................... 5

5.5 Deflection-measuring instrument .......................................................................................................................................... 5

5.6 Micrometers and gauges ................................................................................................................................................................. 5

6 Test specimens........................................................................................................................................................................................................ 6

6.1 General ........................................................................................................................................................................................................... 6

6.2 Shape and dimensions ...................................................................................................................................................................... 6

6.3 Specimen inspection .......................................................................................................................................................................... 6

6.4 Number of test specimens ............................................................................................................................................................. 6

7 Conditioning .............................................................................................................................................................................................................. 6

8 Procedure..................................................................................................................................................................................................................... 7

8.1 Calculation of force to be applied............................................................................................................................................ 7

8.2 Initial temperature of the heating equipment ............................................................................................................. 8

8.3 Conducting the test ............................................................................................................................................................................. 8

9 Expression of results ........................................................................................................................................................................................ 8

10 Precision ....................................................................................................................................................................................................................... 9

11 Test report ................................................................................................................................................................................................................... 9

Bibliography .............................................................................................................................................................................................................................10

© ISO 2020 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 75-1:2020(E)
Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards

bodies (ISO member bodies). The work of preparing International Standards is normally carried out

through ISO technical committees. Each member body interested in a subject for which a technical

committee has been established has the right to be represented on that committee. International

organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.

ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of

electrotechnical standardization.

The procedures used to develop this document and those intended for its further maintenance are

described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the

different types of ISO documents should be noted. This document was drafted in accordance with the

editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).

Attention is drawn to the possibility that some of the elements of this document may be the subject of

patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of

any patent rights identified during the development of the document will be in the Introduction and/or

on the ISO list of patent declarations received (see www .iso .org/ patents).

Any trade name used in this document is information given for the convenience of users and does not

constitute an endorsement.

For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and

expressions related to conformity assessment, as well as information about ISO's adherence to

the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see

www .iso .org/ iso/ foreword .html.

This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 2,

Mechanical behavior, in collaboration with the European Committee for Standardization (CEN) Technical

Committee CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation between

ISO and CEN (Vienna Agreement).

This fourth edition cancels and replaces the third edition (ISO 75-1:2013), which has been technically

revised. The main changes compared to the previous edition are as follows:

— specification for the temperature difference between the middle and the ends of the test specimens

has been removed;

— specification for the position of the tip of the temperature sensor has been widened;

— editorial changes have been applied.
A list of all parts in the ISO 75 series can be found on the ISO website.

Any feedback or questions on this document should be directed to the user’s national standards body. A

complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2020 – All rights reserved
---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 75-1:2020(E)
Plastics — Determination of temperature of deflection
under load —
Part 1:
General test method
1 Scope

1.1 This document gives a general test method for the determination of the temperature of deflection

under load (flexural stress under three-point loading) of plastics. Different types of test specimen and

different constant loads are defined to suit different types of material.

1.2 ISO 75-2 gives specific requirements for plastics (including filled plastics and fibre-reinforced

plastics in which the fibre length, prior to processing, is up to 7,5 mm) and ebonite, while ISO 75-3 gives

specific requirements for high-strength thermosetting laminates and long-fibre-reinforced plastics in

which the fibre length, prior to processing, is greater than 7,5 mm.

1.3 The methods specified are suitable for assessing the relative behaviour of different types of

material at elevated temperature under load at a specified rate of temperature increase. The results

obtained do not necessarily represent maximum applicable temperatures because, in practice, essential

factors, such as time, loading conditions and nominal surface stress, can differ from the test conditions.

True comparability of data can only be achieved for materials having the same room-temperature flexural

modulus.
1.4 The methods specify preferred dimensions for the test specimens.

1.5 Data obtained using the test methods described are not intended to be used to predict actual

end-use performance. The data are not intended for design analysis or prediction of the endurance of

materials at elevated temperatures.

1.6 This method is commonly known as the heat deflection temperature or heat distortion temperature

(HDT) test, although there is no official document using this designation.
2 Normative references

The following documents are referred to in the text in such a way that some or all of their content

constitutes requirements of this document. For dated references, only the edition cited applies. For

undated references, the latest edition of the referenced document (including any amendments) applies.

ISO 75-2, Plastics — Determination of temperature of deflection under load — Part 2: Plastics and ebonite

ISO 75-3, Plastics — Determination of temperature of deflection under load — Part 3: High-strength

thermosetting laminates and long-fibre-reinforced plastics
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 16012, Plastics — Determination of linear dimensions of test specimens
IEC 60584-1, Thermocouples — Part 1: EMF specifications and tolerances

IEC 60751, Industrial platinum resistance thermometers and platinum temperature sensors

© ISO 2020 – All rights reserved 1
---------------------- Page: 5 ----------------------
ISO 75-1:2020(E)
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.

ISO and IEC maintain terminological databases for use in standardization at the following addresses:

— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at http:// www .electropedia .org/
3.1
flexural strain

nominal fractional change in length of an element of the outer surface of the test specimen at midspan

Note 1 to entry: It is expressed as a dimensionless ratio or a percentage (%).
3.2
flexural strain increase
specified increase in flexural strain (3.1) that takes place during heating
Note 1 to entry: It is expressed as a percentage (%).
3.3
deflection

distance over which the top or bottom surface of the test specimen at midspan deviates during flexure

from its original position
Note 1 to entry: It is expressed in millimetres (mm).
3.4
standard deflection

increase in deflection (3.3) corresponding to the flexural strain increase (3.2), Δε , at the surface of the

test specimen, and which is specified in ISO 75-2 or ISO 75-3
Note 1 to entry: It is expressed in millimetres (mm). See Formula (4).
3.5
flexural stress
nominal stress at the outer surface of the test specimen at midspan
Note 1 to entry: It is expressed in megapascals (MPa).
3.6
load

force, applied to the test specimen at midspan, which results in a defined flexural stress (3.5)

Note 1 to entry: It is expressed in newtons (N). See Formulae (1) to (3).
3.7
temperature of deflection under load

temperature at which the deflection (3.3) of the test specimen reaches the standard deflection (3.4) as

the temperature is increased
Note 1 to entry: It is expressed in degrees Celsius (°C).
2 © ISO 2020 – All rights reserved
---------------------- Page: 6 ----------------------
ISO 75-1:2020(E)
4 Principle

A standard test specimen is subjected to three-point bending under a constant load in the flatwise

position to produce one of the flexural stresses given in the relevant part of ISO 75. The temperature is

raised at a uniform rate, and the temperature at which the standard deflection, corresponding to the

specified increase in flexural strain, occurs is measured.
5 Apparatus
5.1 Means of producing a flexural stress

The apparatus shall be constructed essentially as shown in Figure 1. It consists of a rigid metal frame

in which a rod shall move freely in the vertical direction. One end of the rod is fitted with a weight-

carrying plate and the other end is equipped with a loading edge. The base of the frame is fitted with

test-specimen supports. These supports and the vertical members of the frame are made of a material

having the same coefficient of linear expansion as the rod.

The test-specimen supports consist of metal pieces that are cylindrical in the contact area and with

their lines of contact with the s
...

NORME ISO
INTERNATIONALE 75-1
Quatrième édition
2020-02
Plastiques — Détermination de la
température de fléchissement sous
charge —
Partie 1:
Méthode d'essai générale
Plastics — Determination of temperature of deflection under load —
Part 1: General test method
Numéro de référence
ISO 75-1:2020(F)
ISO 2020
---------------------- Page: 1 ----------------------
ISO 75-1:2020(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2020

Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette

publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,

y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut

être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.

ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2020 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 75-1:2020(F)
Sommaire Page

Avant-propos ..............................................................................................................................................................................................................................iv

1 Domaine d’application ................................................................................................................................................................................... 1

2 Références normatives ................................................................................................................................................................................... 1

3 Termes et définitions ....................................................................................................................................................................................... 2

4 Principe .......................................................................................................................................................................................................................... 3

5 Appareillage .............................................................................................................................................................................................................. 3

5.1 Moyens de produire une contrainte de flexion ........................................................................................................... 3

5.2 Dispositif de chauffage ..................................................................................................................................................................... 4

5.3 Poids ................................................................................................................................................................................................................. 5

5.4 Instrument de mesure de la température ....................................................................................................................... 5

5.5 Instrument de mesure du fléchissement .......................................................................................................................... 5

5.6 Micromètres et calibres ................................................................................................................................................................... 5

6 Éprouvettes ................................................................................................................................................................................................................ 6

6.1 Généralités .................................................................................................................................................................................................. 6

6.2 Forme et dimensions ......................................................................................................................................................................... 6

6.3 Vérification des éprouvettes ........................................................................................................................................................ 6

6.4 Nombre d’éprouvettes ...................................................................................................................................................................... 6

7 Conditionnement ................................................................................................................................................................................................. 6

8 Mode opératoire.................................................................................................................................................................................................... 7

8.1 Calcul de la force à appliquer...................................................................................................................................................... 7

8.2 Température initiale du dispositif de chauffage ........................................................................................................ 8

8.3 Réalisation de l’essai .......................................................................................................................................................................... 8

9 Expression des résultats............................................................................................................................................................................... 9

10 Fidélité ............................................................................................................................................................................................................................ 9

11 Rapport d’essai ....................................................................................................................................................................................................... 9

Bibliographie ...........................................................................................................................................................................................................................10

© ISO 2020 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 75-1:2020(F)
Avant-propos

L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes

nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est

en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude

a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,

gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.

L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui

concerne la normalisation électrotechnique.

Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont

décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents

critères d'approbation requis pour les différents types de documents ISO. Le présent document a été

rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www

.iso .org/ directives).

L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de

droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable

de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant

les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de

l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de

brevets reçues par l'ISO (voir www .iso .org/ brevets).

Les appellations commerciales éventuellement mentionnées dans le présent document sont données

pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un

engagement.

Pour une explication de la nature volontaire des normes, la signification des termes et expressions

spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion

de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles

techniques au commerce (OTC), voir le lien suivant: www .iso .org/ iso/ fr/ avant -propos.

Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 2,

Comportement mécanique, en collaboration avec le comité technique CEN/TC 249, Plastiques, du Comité

européen de normalisation (CEN) conformément à l’Accord de coopération technique entre l’ISO et le

CEN (Accord de Vienne).

Cette quatrième édition annule et remplace la troisième édition (ISO 75-1:2013), qui a fait l’objet d’une

révision technique. Les principales modifications par rapport à l’édition précédente sont les suivantes:

— la spécification de la différence de température entre le centre et les extrémités des éprouvettes a

été supprimée;

— la spécification de la position de la touche du capteur thermique a été élargie;

— des modifications éditoriales ont été effectuées.

Une liste de toutes les parties de la série ISO 75 se trouve sur le site web de l’ISO.

Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent

document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes

se trouve à l’adresse www .iso .org/ fr/ members .html.
iv © ISO 2020 – Tous droits réservés
---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 75-1:2020(F)
Plastiques — Détermination de la température de
fléchissement sous charge —
Partie 1:
Méthode d'essai générale
1 Domaine d’application

1.1 Le présent document décrit une méthode d’essai générale permettant de déterminer la température

de fléchissement sous charge (contrainte de flexion sous mise en charge en trois points) des plastiques.

Différents types d’éprouvettes et différentes charges constantes sont définis pour correspondre à des

types de matériaux différents.

1.2 L’ISO 75-2 fournit des exigences particulières pour les plastiques (incluant les plastiques chargés

et les plastiques renforcés de fibres, dans lesquels la longueur de fibre avant l’emploi est inférieure

ou égale à 7,5 mm) et l’ébonite, et l’ISO 75-3 fournit des exigences particulières pour les stratifiés

thermodurcissables à haute résistance et les plastiques renforcés de fibres longues, dans lesquels la

longueur de fibre avant l’emploi est supérieure à 7,5 mm.

1.3 Les méthodes spécifiées permettent d’évaluer le comportement relatif sous charge des divers types

de matériaux à température élevée, avec une élévation de la température à une vitesse spécifiée. Les

résultats obtenus ne représentent pas nécessairement les températures maximales d’utilisation car, dans

la pratique, des facteurs essentiels tels que le temps, les conditions de mise en charge et la contrainte

superficielle nominale peuvent différer des conditions adoptées pour l’essai. Une comparabilité

exacte des données ne peut être obtenue que pour des matériaux ayant le même module de flexion à

température ambiante.
1.4 Les méthodes spécifient les dimensions recommandées pour les éprouvettes.

1.5 Les données obtenues en utilisant les méthodes d’essais décrites ne sont pas destinées à être

utilisées pour prédire de véritables performances d’usage. Les données ne sont pas destinées à être

utilisées pour les analyses de conception ou pour prévoir la résistance des matériaux à des températures

élevées.

1.6 La présente méthode est communément connue sous le nom d’essai de déformation à chaud ou de

fléchissement à chaud (HDT) bien qu’il n’existe pas de document officiel utilisant cette désignation.

2 Références normatives

Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des

exigences du présent document. Pour les références datées, seule l'édition citée s'applique. Pour les

références non datées, la dernière édition du document de référence s'applique (y compris les éventuels

amendements).

ISO 75-2, Plastiques — Détermination de la température de fléchissement sous charge — Partie 2:

Plastiques et ébonite

ISO 75-3, Plastiques — Détermination de la température de fléchissement sous charge — Partie 3: Stratifiés

thermodurcissables à haute résistance et plastiques renforcés de fibres longues
© ISO 2020 – Tous droits réservés 1
---------------------- Page: 5 ----------------------
ISO 75-1:2020(F)
ISO 291, Plastiques — Atmosphères normales de conditionnement et d'essai
ISO 16012, Plastiques — Détermination des dimensions linéaires des éprouvettes

IEC 60584-1, Couples thermoélectriques — Partie 1: Spécifications et tolérances en matière de FEM

IEC 60751, Thermomètres à résistance de platine industriels et capteurs thermométriques en platine

3 Termes et définitions

Pour les besoins du présent document, les termes et définitions suivants s’appliquent.

L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en

normalisation, consultables aux adresses suivantes:

— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp

— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org
3.1
déformation en flexion

variation partielle nominale de la longueur d’un élément à la surface externe de l’éprouvette, au milieu

de la portée

Note 1 à l'article: Elle est exprimée sous forme de rapport sans dimension ou en pourcentage (%).

3.2
accroissement de la déformation en flexion

accroissement spécifié de la déformation en flexion (3.1) qui se produit au cours du chauffage

Note 1 à l'article: Il est exprimé en pourcentage (%).
3.3
fléchissement

distance sur laquelle la surface supérieure ou inférieure de l’éprouvette a dévié par rapport à sa position

initiale au cours de la flexion, au milieu de la portée
Note 1 à l'article: Il est exprimé en millimètres (mm).
3.4
fléchissement normalisé

accroissement du fléchissement (3.3) correspondant à l’accroissement de la déformation en flexion (3.2),

Δε , à la surface de l’éprouvette, et qui est spécifié dans l’ISO 75-2 ou l’ISO 75-3

Note 1 à l'article: Il est exprimé en millimètres (mm). Voir la Formule (4).
3.5
contrainte de flexion
contrainte nominale à la surface externe de l’éprouvette au milieu de la portée
Note 1 à l'article: Elle est exprimée en mégapascals (MPa).
2 © ISO 2020 – Tous droits réservés
---------------------- Page: 6 ----------------------
ISO 75-1:2020(F)
3.6
charge

force, appliquée à l’éprouvette au milieu de la portée, qui se traduit par une contrainte de flexion

(3.5) définie

Note 1 à l'article: Elle est exprimée en newtons (N). Voir les Formules (1) à (3).

3.7
température de fléchissement sous charge

température à laquelle le fléchissement (3.3) de l’éprouvette atteint le fléchissement normalisé (3.4) au

cours de l’élévation de la température
Note 1 à l'article: Elle est exprimée en degrés Celsius (°C).
4 Principe

Une éprouvette normalisée, positionnée à plat, est soumise à une charge constante de flexion en trois

points engendrant l’une des contraintes de flexion données dans la partie pertinente de l’ISO 75. La

température est élevée à une vitesse uniforme, et la température à laquelle se produit le fléchissement

normalisé, correspondant à l’accroissement spécifié de la déformation en flexion, est mesurée.

5 Appareillage
5.1 Moyens de produire une contrainte de flexion

L’appareillage doit être construit essentiellement selon les indications de la Figure 1. Il consiste en un

cadre métallique rigide dans lequel une tige doit se déplacer librement à la verticale. L’une des extrémités

de cette tige est pourvue d’un plateau support du poids et l’autre d’un poinçon de mise en charge. La

base du cadre est fixée aux supports de l’éprouvette. Ces supports et les parties verticales du cadre sont

réalisés en un matériau ayant le même coefficient de dilatation thermique linéique que la tige.

Les supports de l’éprouvette sont constitués par des éléments métalliques, cylindriques dans la zone

de contact avec l’éprouvette et dont les lignes de contact sont dans un plan horizontal. La portée, c’est-

à-dire la distance entre les lignes de contact, est indiquée dans l’ISO 75-2 ou l’ISO 75-3. Les supports

sont fixés à la base du cadre de façon que la force verticale soit appliquée sur l’éprouvette, au milieu de

la portée (±1 mm), par le poinçon de mise en charge. Les arêtes de contact des supports sont parallèles

au poinçon de mise en charge et perpendiculaires à l’axe longitudinal de l
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.