ISO 683-18:1976

Heat-treated steels, alloy steels and free-cutting steels — Part 18: Wrought unalloyed steels in the normalized, or normalized and cold-drawn, or hot-rolled and cold-drawn condition

Aciers pour traitement thermique, aciers alliés et aciers pour décolletage — Partie 18: Aciers corroyés non alliés normalisés, ou normalisés et étirés à froid, ou laminés à chaud et étirés à froid

General Information

• Status: Withdrawn
• Publication Date: 31-May-1976
• Withdrawal Date: 31-May-1976
• ICS: 77.140.10 - Heat-treatable steels
• ICS: 77.140.20 - Stainless steels
• Technical Committee: ISO/TC 17/SC 4 - Heat treatable and alloy steels
• Drafting Committee: ISO/TC 17/SC 4 - Heat treatable and alloy steels
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 26-Dec-1996

Relations

• Revised: ISO 683-18:1996 - Heat-treatable steels, alloy steels and free- cutting steels — Part 18: Bright products of unalloyed and low alloy steels
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL STANDARD 683 /XViii
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .MEYnYHAPOflHAI OPrAHbi3AUMR no CTAHnAPTH3AUHM .ORGANISATION INTERNATIONALE DE NORMALISATION
Heat-treated steels, alloy steels and free-cutting steels -
Part 18 : Wrought unalloyed steels in the normalized, or
normalized and cold-drawn, or hot-rolled and cold-drawn
condition
Aciers pour traitement thermique, aciers alliés et aciers pour décolletage - Dix-huitième partie : Aciers
corroyés non allies normalisés, ou normalisés et étirés à froid, ou laminés à chaud et étirés a froid
First edition - 1976-06-01
L
I
Lu
-
(D
+
U DC 669.14/. 15.01 8.2 Ref. No. IS0 683/XV111-1976 (E)
-
- -
>
Descriptors : iron and steel products, rolled products, cold drawn products, heat treatable steels. unalloyed steels, materials specifications,
. X
chemical composition, mechanical properties, tests, acceptance inspection.
z
Price based on 6 pages

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 Member Bodies). The work of developing
International Standards is carried out through IS0 Technical Committees. Every
Member Body interested in a subject for which a Technical Committee has been set
up has the right to be represented on that Committee. International organizations,
Y
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the Technical Committees are circulated
to the Member Bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 683/XVI II was drawn up by Technical Committee
ISO/TC 17, Steel, and circulated to the Member Bodies in November 1974.
It has been approved by the Member Bodies of the following countries :
Austria India South Africa, Rep. of
Belgium I ran Spain
Bulgaria Ireland Sweden
Canada Italy Switzerland
Czechoslovakia Japan Turkey
Denmark Mexico United Kingdom
Finland Netherlands U.S.S.R.
Germany Poland Yugoslavia
Hungary Romania
The Member Bodies of the following countries expressed disapproval of the
document on technical grounds :
Australia
U.S.A.
O International Organization for Standardization, 1976
Printed in Switzerland

---------------------- Page: 2 ----------------------
IS0 683/XVlII-1976 (E]
I NTE RNATl ON AL STAN DARD
Heat-treated steels, alloy steels and free-cutting steels -
Part 18 : Wrought unalloyed steels in the normalized, or
normalized and cold-drawn, or hot-rolled and cold-drawn
condition
TABLE 1 - Types of condition of delivery
SCOPE AND FIELD OF APPLICATION
1
1.1 This International Standard gives specifications for
~~
unalloyed wrought steels in
Types of condition
Requirements
of delivery 1)
a) the normalized condition, ot
-~
L b) the normalized and subsequently cold drawn
Chemical composition
xxx
condition, or
Mechanical properties for final dimensions
c) the hot rolled and subsequently cold drawn
~ in the normalized condition
X
condition,
- in the nolmalized , cold-drawn, or
which are usually intended for mechanical purposes, for
X
hot-rolled + cold-drawn condition
example foi machine parts
1) The numbers and letters indicating the type of condition 01
1.2 This lnteinational Standard cornprises the four set ies
delivery follow a co-ordinated series throughout all relevant IS0
of steels listed in table 2, which diffei in their phosphorus
publications
and sulphur contents The series designated with suffixes
"a" oi "b" have irnpioved machinability
3.2.2 The chemical composition expressed by the cast
analysis shall be in accordance with table 2.
3.2.2.1 If ordered to condition of delivery type 1 (see
2 REFERENCES
table I), the values given in table 3 for the permissible
deviations between the values specified in table 2 and the
IS0 82, Steel ~- Tensile testing.
product analysis of products up to 160 mm diameter apply
IS0 89, Steel - Tensile testing of wire.
Above 160 mm diameter, the permissible deviations shall be
agreed at the time of enquiry and order.
ISOIR 377, Selection and preparation of samples and test
pieces for wrought steel.
3.2.2.2 If ordered to condition of delivery types 5(n) ot
ISO/R 404, General technical delivery requirements for
6(n), the mechanical properties specified in table 4 01
steel.
table 5 shall be the governing criteria for acceptance In
such cases, the cast analysis may deviate slightly from the
values shown in table 2
3 REQUIREMENTS
3.2.3 If ordered to condition of delivery type 5(n) the
mechanical properties shall be those shown in table 4; if
3.1 Production processes
ordered to condition of delivery type 6(n) they shall be
those given in table 5.
Unless otherwise agreed in the order, the processes used in
making the steel and the product are left to the discretion
3.2.3.1 The values apply to test pieces taken in the
of the manufacturer, but the steel shall be killed. When he
direction of the metal fibre, the axis of the test piece
so requests, the user shall be informed what steelmaking
corresponding to that shown in the figure.
process is being used.
3.2 Chemical composition and mechanical properties
3.3 Tolerances on dimensions and mass
3.2.1 The steels covered by this International Standard
The tolerances allowable on dimensions and mass shall be
shall be ordered and delivered in accordance with table 1.
stated on the order as in accordance with the appropriate
International Standard. However, in cases where one does
The type of condition of delivery, according to table 1,
not exist the tolerances shall be stated on the order.
shall be stated at the time of enquiry and order.
1

---------------------- Page: 3 ----------------------
IS0 683/XVlll-l976 (E)
4.3 Test methods
4 TESTING
4.3.1 The tensile test shall be carried out in accordance
4.1 Number of sample products
with IS0 82 or IS0 89.
4.3.2 In cases of dispute, the methods for the chemical
4.1 .I Chemical composition
analyses shall be those established by the relevant
The cast analysis shall be given by the manufacturer. If a
International Standards. If no International Standards are
product analysis is required by the purchaser, at least one
available, the methods may be agreed upon and specified at
sample product shall be taken from each cast.
the time of enquiry and order.
4.1.2 Mechanical properties
4.4 Retests
4.1.2.1 For material supplied in the normalized condition
For retests ISO/R 404 is valid.
(type of condition of delivery 5(n) of table l), one sample
product shall be taken from each size grouping from each
4.5 Certification of the tests
normalized batch from each cast for testing in accordance
with table 4.
For certification ISO/R 404 is valid, acceptable documents
being as follows :
4.1.2.2 If the product is continuously normalized, one
sample pr
...

NORME INTERNATIONALE 683 IXVIII
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION *MEXilYHAPOflHAR OPT.AHM3AlIMR no CTAHLlAPTM3AUMM -ORGANISATION INTERNATIONALE DE NORMALISATION
L
Aciers pour traitement thermique, aciers alliés et aciers pour
décolletage - Dix-huitième partie : Aciers corroyés non aliiés
normalisés, ou normalisés et étirés à froid, ou laminés à chaud
et étirés à froid
Heat-treated steels, alloy steels and freecutting steels - Part 18 : Wrought unalloyed steels in the
normalized, or normalized and cold-drawn, or hot-rolled and cold-drawn condition
Première édition -- 1976-06-01
CDU 669.14/. 15.018.2 Réf. no : IS0 683/XVlll-1976 (F)
Descripteurs : produit sidérurgique, laminé, produit étiré a froid, acier pour traitement thermique, acier non allié, spécification de matière,
composition chimique, propriété mécanique, essai, essai de réception.
basé sur 6 pages
Prix

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation Internationale de Normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (Comités Membres ISO). L'élaboration des
Normes Internationales est confiée aux Comités Techniques 1S0. Chaque Comité
Membre intéressé par une étude a le droit de faire partie du Comité Technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO, participent également aux travaux.
Les Projets de Normes Internationales adoptés par les Comités Techniques sont
soumis aux Comités Membres pour approbation, avant leur acceptation comme
Normes Internationales par le Conseil de I'ISO.
La Norme Internationale IS0 683/XVlll a été établie par le Comité Technique
ISO/TC 17, Acier, et soumise aux Comités Membres en novembre 1974.
Elle a été approuvée par les Comités Membres des pays suivants :
Hongrie Roumanie
Afrique du Sud, Rép. d'
Inde Royaume-Uni
Allemagne
Iran Suède
Autriche
Irlande Su isse
Belgique
Italie
Bulgarie Tchécoslovaquie
Turquie
Canada Japon
U.R.S.S.
Danemark Mexique
Yougoslavie
Espagne Pays-Bas
Finlande Pologne
Les Comités Membres des pays suivants ont désapprouvé le document pour des
raisons techniques :
Australie
U.S.A.
O Organisation Internationale de Normalisation, 1976 0
Imprimé en Suisse

---------------------- Page: 2 ----------------------
IS0 683/XVI I I -1976 (F)
NORME INTERNATIONALE
Aciers pour traitement thermique, aciers alliés et aciers pour
décolletage - Dix-huitième partie : Aciers corroyés non alliés
normalisés, ou normalisés et étirés à froid, ou laminés à chaud
et étirés à froid
1 OBJET ET DOMAINE D'APPLICATION TABLEAU 1 - Étatsde livraison
1.1 La présente Norme Internationale donne les
États
spécifications des aciers corroyés non alliés, à l'état Caractéristiques
de livraison 1)
a) normalisé, ou sini
-
L b) normalisé, puis étiré à froid, ou
Composition chimique
X
Propriétés mécaniques pour les dimensions
laminé à chaud, puis étiré a froid,
c)
finales
normalement utilisés en mécanique, par exemple pour les
- à l'état normalisé
éléments de machine.
- normalisé i étiré a froid, ou
X
laminé a chaud t etire a froid
1.2 La présente Norme Internationale comprend les quatre
séries d'aciers énumérés au tableau 2, qui diffèrent de par
1) Les numeros et les lettres indiquant les types de condition de
leur teneui en phosphore et en soufre. Les séries
livraison sont conformes à une série unifiée dans toutes les
accompagnées des suffixes «a» ou «b» présentent une
publications IS0 appropriées
meilleure usinabilité.
3.2.2 La composition chimique exprimée par l'analyse de
coulée doit être conforme au tableau 2.
3.2.2.1 Si la commande spécifie l'état de livraison 1 (voir
2 REFERENCES
tableau I), on tiendra compte des valeurs données au
IS0 82, Acier - Essai de traction.
tableau 3, de la tolérance admissible entre les valeurs
2 et l'analyse sur produits d'au plus
spécifiées au tableau
IS0 89, Acier - Essai de traction des fils.
160 mm de diamètre. Au-dessus de 160 mm de diamètre, les
ISOIR 377, Prélèvement et préparation des échantillons et
tolérances admissibles doivent faire l'objet d'un accord au
des éprouvettes pour l'acier corroyé.
L moment de l'offre et de la commande.
ISOIR 404, Conditions générales techniques de livraison
3.2.2.2 Si la commande spécifie l'état de livraison 5(n) ou
pour l'acier.
6(n), ce sont les propriétés mécaniques figurant
respectivement aux tableaux 4 et 5 qui représenteront les
critères déterminants de la réception. Dans ce cas, l'analyse
de coulée pourra s'écarter légèrement des valeurs données
3 CARACTERISTIQUES REQUISES
dans le tableau 2.
3.1 Procédés d'élaboration
3.2.3 Si la commande spécifie l'état de livraison 5(n), les
propriétés doivent être celles du tableau 4. Si la commande
Sauf convention contraire a la commande, les procédés
spécifie l'état de livraison 6(n), ce seront celles du tableau 5.
d'élaboration de l'acier et de fabrication du produit sont
laissés au choix du producteur. Toutefois l'acier doit être
3.2.3.1 Les valeurs s'appliquent à des éprouvettes prélevées
calmé. Sur sa demande, l'utilisateur doit être informé du
dans le sens des fibres du métal, l'axe de l'éprouvette
procédé utilisé pour l'élaboration de l'acier.
correspondant à la figure.
3.2 Composition chimique et propriétés mécaniques
3.3 Tolérances sur les dimensions et les masses
3.2.1 Les aciers conformes à la présente Norme
Les tolérances admissibles sur les dimensions et les masses
Internationale doivent être commandés et livrés selon les
doivent être indiquées dans la commande comme étant
indications du tableau 1.
conformes à la Norme Internationale correspondante. AU
cas où une telle norme n'existerait pas, on doit préciser ces
L'état de livraison doit être indiqué au moment de l'offre et
de la commande, conformément au tableau 1. tolérances à la commande.
1

---------------------- Page: 3 ----------------------
IS0 683/XVIll-1976 (F)
4.3 Méthodes d‘essai
4 ESSAIS
4.3.1 L’essai de traction doit être réalisé conformément
4.1 Nombre d‘échantillons
aux prescriptions de 1‘1S0 82 ou de I’ISO 89.
4.3.2 En cas de désaccord, les méthodes d‘analyses
4.1.1 Composition chimique
chimiques doivent être celles qui sont établies par les
L’analyse de coulée doit être indiquée par le producteur. Si
Normes Internationales appropriées. Si celles-ci ne sont pas
une analyse sur produit est requise par l‘acheteur, un
disponibles, ces méthodes peuvent être fixées d’un commun
échantillon de produit au moins doit être prélevé sur
accord et spécifiées au moment de l’offre et de la
chaque coulée.
commande.
4.1.2 Propriétés mécaniques
4.4 Contre-essais
4.1.2.1 Pour les matériaux fournis a l‘état normalisé (état
Pour les contre-essais, I’ISO/R 404 est applicable.
de livraison 5(n) du tableau 1). on doit prélever un
échantillon de produit de chaque catégorie de dimensions
4.5 Homologation des essais
par lot normalisé de chaque coulée, pour être soumis a
l’essai conformément au tableau 4.
Les attestations d‘essai sont celles prévues dans
l‘lSO/R 404, à savoir :
4.1.2.2 Si le produit est normalisé de façon continue, on
doit prélever un échantillon de produit pour essai par lo
...