ISO 683-2:2016
(Main)Heat-treatable steels, alloy steels and free-cutting steels — Part 2: Alloy steels for quenching and tempering
Heat-treatable steels, alloy steels and free-cutting steels — Part 2: Alloy steels for quenching and tempering
ISO 683-2:2016 specifies the technical delivery requirements for - semi-finished products, hot formed, e.g. blooms, billets, slabs (see Note 1), - bars (see Note 1), - wire rod, finished flat products, and - hammer or drop forgings (see Note 1) manufactured from the direct hardening alloy steels and the alloy flame- and induction-hardening steels listed in Table 3 and supplied in one of the heat-treatment conditions given for the different types of products in Table 1 and in one of the surface conditions given in Table 2. The steels are, in general, intended for the manufacture of quenched and tempered or austempered (see 3.2 and Note 2) and flame- or induction-hardened machine parts (see Tables 8 and 9). The requirements for mechanical properties given in ISO 683-2:2016 are restricted to the sizes given in the relevant Table 8. NOTE 1 Hammer-forged semi-finished products (blooms, billets, slabs, etc.), seamless rolled rings and hammer-forged bars are in the following covered under semi-finished products or bars and not under the term "hammer and drop forgings". NOTE 2 For the purposes of simplification, the term "quenched and tempered" is, unless otherwise indicated, used in the following also for the austempered condition. NOTE 3 For International Standards relating to steels complying with the requirements for the chemical composition in Table 3, however, supplied in other product forms or treatment conditions than given above or intended for special applications, and for other related International Standards, see the Bibliography. NOTE 4 ISO 683-2 :2016 does not apply to bright products and bars and wire rod for cold heading. For such products, see ISO 683‑18 and ISO 4954. In special cases, variations in these technical delivery requirements or additions to them can form the subject of an agreement at the time of enquiry and order (see 5.2 and Annex B). In addition to ISO 683-2:2016, the general technical delivery requirements of ISO 404 are applicable.
Aciers pour traitement thermique, aciers alliés et aciers pour décolletage — Partie 2: Aciers alliés pour trempe et revenu
Cette partie de l'ISO 683 spécifie les conditions techniques de livraison des: — demi-produits laminés à chaud, comme par exemple les blooms, billettes et brames (voir Note 1); — barres (voir Note 1), — fils machine, — produits plats finis, et — pièces forgées par martelage ou estampage (voir Note 1) fabriqués à partir d'aciers non alliés à trempe directe et d'aciers non alliés par trempe au chalumeau et par induction énumérés dans le Tableau 3 et livrés dans l'un des états de traitement thermique donnés pour les différents types de produits dans le Tableau 1 et dans l'un des états de surface donnés dans le Tableau 2. D'une manière générale, ces aciers sont destinés à la fabrication de pièces mécaniques trempées et revenues ou ayant subi un procédé de trempe étagée bainitique (voir 3.2 et Note 2) ou à la fabrication de pièces mécaniques trempées par induction ou au chalumeau (voir Tableau 8 et 9). Les exigences en matière de caractéristiques mécaniques données dans cette partie de l'ISO 683 sont limitées aux dimensions données dans le Tableau 8. NOTE 1 Les demi-produits forgés par martelage (blooms, billettes, brames, etc.), les couronnes laminées sans soudure et les barres forgées par martelage figurent parmi les demi-produits ou les barres, et non sous l'appellation «pièces forgées par martelage ou estampage». NOTE 2 Dans un but de simplification, l'expression «trempé et revenu» est aussi, sauf indication contraire, utilisée dans les parties suivantes pour l'état «trempe étagée bainitique». NOTE 3 Pour les Normes internationales relatives aux aciers qui sont conformes aux exigences de composition chimique du Tableau 3, mais fournis sous d'autres formes de produits ou dans des états de traitement autres que ceux indiqués ci-dessus, ou qui sont destinés à des applications spéciales, ainsi que pour d'autres Normes internationales analogues, voir la Bibliographie. NOTE 4 La présente partie de l'ISO 683 ne s'applique pas aux produits transformés à froid, barres et fils machine pour frappe à froid. Pour ces produits, voir les ISO 683‑18 et ISO 4954. Dans certains cas particuliers, il est possible de déroger aux présentes conditions techniques de livraison ou d'en ajouter d'autres, à condition que le fabricant et l'acheteur en conviennent au moment de l'appel d'offres et de la commande (voir 5.2 et Annexe B). En plus de cette partie de l'ISO 683, les conditions générales techniques de livraison de l'ISO 404 sont applicables.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 683-2
Second edition
2016-07-01
Heat-treatable steels, alloy steels and
free-cutting steels —
Part 2:
Alloy steels for quenching and
tempering
Aciers pour traitement thermique, aciers alliés et aciers pour
décolletage —
Partie 2: Aciers alliés pour trempe et revenu
Reference number
ISO 683-2:2016(E)
©
ISO 2016
---------------------- Page: 1 ----------------------
ISO 683-2:2016(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2016, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2016 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 683-2:2016(E)
Contents Page
Foreword .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Classification and designation . 3
4.1 Classification . 3
4.2 Designation . 3
5 Information to be supplied by the purchaser. 3
5.1 Mandatory information . 3
5.2 Options and/or supplementary or special requirements . 3
5.3 Ordering example . 4
6 Manufacturing process . 4
6.1 General . 4
6.2 Deoxidation . 4
6.3 Heat-treatment condition and surface condition at delivery . 4
6.3.1 Heat-treatment condition . 4
6.3.2 Particular surface conditions . 4
6.4 Traceability of the cast . 4
7 Requirements . 5
7.1 Chemical composition, mechanical properties and hardenability . 5
7.1.1 General. 5
7.1.2 Chemical composition . 5
7.1.3 Mechanical properties . 5
7.1.4 Hardenability . 5
7.1.5 Surface hardness . 5
7.2 Machinability . 5
7.3 Cold shearability . 5
7.4 Grain size . 6
7.5 Non-metallic inclusions . 6
7.5.1 Microscopic inclusions . 6
7.5.2 Macroscopic inclusions . 6
7.6 Internal soundness . 6
7.7 Surface quality . 6
7.8 Decarburization . 7
7.9 Shape, dimensions and tolerances . 7
8 Inspection . 7
8.1 Testing procedures and types of documents . 7
8.2 Frequency of testing . 7
8.3 Specific inspection and testing . 8
8.3.1 Verification of the hardenability, hardness and mechanical properties . 8
8.3.2 Visual and dimensional inspection . 8
9 Test methods . 8
9.1 Chemical analysis . 8
9.2 Mechanical tests . 8
9.2.1 Tensile test . 8
9.2.2 Impact test . 8
9.3 Hardness and hardenability tests . 8
9.3.1 Hardness in treatment conditions +A and +S . 8
9.3.2 Verification of hardenability . 9
9.3.3 Surface hardness . 9
9.4 Retests . 9
© ISO 2016 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 683-2:2016(E)
10 Marking . 9
Annex A (normative) Ruling sections for mechanical properties .31
Annex B (normative) Supplementary or special requirements .35
Annex C (informative) Designation of steels given in this part of ISO 683 and of comparable
grades covered in various designation systems.37
Annex D (informative) Dimensional standards applicable to products complying with this
part of ISO 683 .39
Bibliography .40
iv © ISO 2016 – All rights reserved
---------------------- Page: 4 ----------------------
ISO 683-2:2016(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment,
as well as information about ISO’s adherence to the World Trade Organization (WTO) principles in the
Technical Barriers to Trade (TBT) see the following URL: www.iso.org/iso/foreword.html.
The committee responsible for this document is ISO/TC 17, Steel, Subcommittee SC 4, Heat treatable and
alloy steels.
This second edition cancels and replaces the first edition (ISO 683-2:2012), of which it constitutes a
minor revision.
ISO 683 consists of the following parts, under the general title Heat-treatable steels, alloy steels and free-
cutting steels:
— Part 1: Non-alloy steels for quenching and tempering
— Part 2: Alloy steels for quenching and tempering
— Part 3: Case-hardening steels
— Part 4: Free-cutting steels
— Part 5: Nitriding steels
— Part 14: Hot-rolled steels for quenched and tempered springs
— Part 15: Valve steels for internal combustion engines
— Part 17: Ball and roller bearing steels
— Part 18: Bright steel products
© ISO 2016 – All rights reserved v
---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 683-2:2016(E)
Heat-treatable steels, alloy steels and free-cutting steels —
Part 2:
Alloy steels for quenching and tempering
1 Scope
This part of ISO 683 specifies the technical delivery requirements for
— semi-finished products, hot formed, e.g. blooms, billets, slabs (see Note 1),
— bars (see Note 1),
— wire rod,
— finished flat products, and
— hammer or drop forgings (see Note 1)
manufactured from the direct hardening alloy steels and the alloy flame- and induction-hardening
steels listed in Table 3 and supplied in one of the heat-treatment conditions given for the different types
of products in Table 1 and in one of the surface conditions given in Table 2.
The steels are, in general, intended for the manufacture of quenched and tempered or austempered
(see 3.2 and Note 2) and flame- or induction-hardened machine parts (see Tables 8 and 9).
The requirements for mechanical properties given in this part of ISO 683 are restricted to the sizes
given in the relevant Table 8.
NOTE 1 Hammer-forged semi-finished products (blooms, billets, slabs, etc.), seamless rolled rings and
hammer-forged bars are in the following covered under semi-finished products or bars and not under the term
“hammer and drop forgings”.
NOTE 2 For the purposes of simplification, the term “quenched and tempered” is, unless otherwise indicated,
used in the following also for the austempered condition.
NOTE 3 For International Standards relating to steels complying with the requirements for the chemical
composition in Table 3, however, supplied in other product forms or treatment conditions than given above or
intended for special applications, and for other related International Standards, see the Bibliography.
NOTE 4 This part of ISO 683 does not apply to bright products and bars and wire rod for cold heading. For
such products, see ISO 683-18 and ISO 4954.
In special cases, variations in these technical delivery requirements or additions to them can form the
subject of an agreement at the time of enquiry and order (see 5.2 and Annex B).
In addition to this part of ISO 683, the general technical delivery requirements of ISO 404 are applicable.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 148-1, Metallic materials — Charpy pendulum impact test — Part 1: Test method
© ISO 2016 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO 683-2:2016(E)
ISO 377, Steel and steel products — Location and preparation of samples and test pieces for mechanical testing
ISO 404:2013, Steel and steel products — General technical delivery requirements
ISO 642, Steel — Hardenability test by end quenching (Jominy test)
ISO 643, Steels — Micrographic determination of the apparent grain size
ISO 3887, Steels — Determination of depth of decarburization
1)
ISO 4885:— , Ferrous products — Heat treatments — Vocabulary
ISO 4948-1, Steels — Classification — Part 1: Classification of steels into unalloyed and alloy steels based
on chemical composition
ISO 4948-2, Steels — Classification — Part 2: Classification of unalloyed and alloy steels according to main
quality classes and main property or application characteristics
ISO/TS 4949, Steel names based on letter symbols
ISO 4967, Steel — Determination of content of non-metallic inclusions — Micrographic method using
standard diagrams
ISO 6506-1, Metallic materials — Brinell hardness test — Part 1: Test method
ISO 6508-1, Metallic materials — Rockwell hardness test — Part 1: Test method (scales A, B, C, D, E, F, G, H,
K, N, T)
ISO 6892-1, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
ISO 6929, Steel products — Vocabulary
ISO 7788, Steel — Surface finish of hot-rolled plates and wide flats — Delivery requirements
ISO 9443, Heat-treatable and alloy steels — Surface quality classes for hot-rolled round bars and wire
rods — Technical delivery conditions
ISO 10474, Steel and steel products — Inspection documents
ISO 14284, Steel and iron — Sampling and preparation of samples for the determination of chemical
composition
3 Terms and definitions
For the purposes of this document, the definitions in ISO 377, ISO 4885, ISO 4948-1, ISO 4948-2,
ISO 6929, ISO 14284, and the following apply.
NOTE For deviations from these terms and definitions, see Notes 1 and 2 of Clause 1.
3.1
ruling section
section for which the specified mechanical properties shall apply
Note 1 to entry: Independent of the actual shape and dimensions of the cross-section of the product, the size of its
ruling section is always given by a diameter. This corresponds to the diameter of an “equivalent round bar”. That
is a round bar which will show the same cooling rate as the actual ruling section of the product concerned at its
position for taking the test pieces, when being cooled from austenitizing temperature.
1) Under preparation. Stage at the time of publication: ISO/DIS 4885:2016.
2 © ISO 2016 – All rights reserved
---------------------- Page: 7 ----------------------
ISO 683-2:2016(E)
3.2
austempering
isothermal heat treatment for producing bainitic or ausferritic structure of a work piece
Note 1 to entry: The final cooling to ambient temperature is not at a specific rate.
2)
[SOURCE: ISO 4885:— , 3.11]
3.3
alloy steel
as defined in ISO 4948-1:1982, 3.1.3
4 Classification and designation
4.1 Classification
The classification of the relevant steel grades is according to ISO 4948-1 and ISO 4948-2. All steel grades
covered by this part of ISO 683 are alloy special steels.
4.2 Designation
For the steel grades covered by this part of ISO 683, the steel names as given in the relevant tables are
allocated in accordance with ISO/TS 4949.
5 Information to be supplied by the purchaser
5.1 Mandatory information
The manufacturer shall obtain the following information from the purchaser at the time of enquiry
and order:
a) quantity to be delivered;
b) designation of the product form (slab, bloom, billet, round bar, wire rod, wide flat, sheet, plate, strip,
forging, etc.);
c) either the designation of the dimensional standard and the dimensions and tolerances selected
from this (see 7.9) or, for example in the case of drop forgings, the designation of the drawing or any
other document covering the dimensions and tolerances required for the product;
d) reference to this part of ISO 683, i.e. ISO 683-2;
e) the designation of the steel grade given in Table 3;
f) the symbol for the required heat-treatment condition (see Table 1, column 2);
g) standard designation for a test report 2.2 or, if required any other type of inspection document in
accordance with ISO 10474 or according to another regional standard, e.g. EN 10204 or JIS G 0415.
5.2 Options and/or supplementary or special requirements
Several options are specified in this part of ISO 683 and listed below. If the purchaser does not indicate
any of these options, the products will be supplied in accordance with the basic specifications of this
part of ISO 683 (see 5.1):
a) if another surface condition than “hot worked” or a special surface quality is required, the surface
condition (see Table 2) and the surface quality (see 7.7);
2) Under preparation. Stage at the time of publication: ISO/DIS 4885:2016.
© ISO 2016 – All rights reserved 3
---------------------- Page: 8 ----------------------
ISO 683-2:2016(E)
b) any requirement for the hardenability (+H, +HH, +HL) for special steels (see 7.1.4 and Tables 5 to 7);
c) any supplementary requirement that shall be complied with, the symbol and, where necessary, the
details of this supplementary requirement (see Annex B);
d) any requirement for the verification of non-metallic inclusion content (see 7.5);
e) verification of hardenability and, if agreed, the information about calculation of the hardenability
(see 9.3.2);
f) any requirement regarding the permissible depth of decarburization (see 7.8);
g) suitability of bars and rod for bright drawing (see 7.7.4);
h) any requirement relating to the removal of surface defects (see 7.7.5).
5.3 Ordering example
EXAMPLE Fifty hot-rolled round bars according to ISO 1035-1 with a nominal diameter of 40 mm and a
nominal length of 8 000 mm with diameter tolerance according to class S and with length tolerance according to
class L2 of ISO 1035-4 made of steel grade ISO 683-2, 42CrMo4 (see Table 3) in the heat-treatment condition +S
(see Table 1), surface blast cleaned (+BC) (see Table 2), product analysis/option B.4 with an inspection certificate
3.1 according to ISO 10474:
50 round bars ISO 1035 – 40,0S × 8 000L2
ISO 683-2 – 42CrMo4+S +BC option B.4
ISO 10474 – 3.1
6 Manufacturing process
6.1 General
The manufacturing process of the steel and of the products is, with the restrictions given by the
requirements in 6.2 to 6.4, left to the discretion of the manufacturer.
For minimum reduction ratio or minimum thickness deformation ratio of rolled and forged products,
see B.5.
6.2 Deoxidation
All steels shall be deoxidized.
6.3 Heat-treatment condition and surface condition at delivery
6.3.1 Heat-treatment condition
The products shall be delivered in one of the heat-treatment conditions given in Table 1, lines 2 to 6 as
agreed during time of enquiry and order.
6.3.2 Particular surface conditions
If so agreed at the time of enquiry and order, the products shall be delivered in one of the particular
surface conditions given in Table 2, lines 3 to 6.
6.4 Traceability of the cast
Each product shall be traceable to the cast (see Clause 10).
4 © ISO 2016 – All rights reserved
---------------------- Page: 9 ----------------------
ISO 683-2:2016(E)
7 Requirements
7.1 Chemical composition, mechanical properties and hardenability
7.1.1 General
Table 1 shows the combinations of usual heat-treatment conditions at delivery, product forms and
requirements, as specified in Tables 3 to 9.
Except where steels are ordered in the quenched and tempered condition, this part of ISO 683 makes
for the alloyed steels provisions to be supplied with or without hardenability requirements (see Table 1,
columns 8 and 9).
7.1.2 Chemical composition
The chemical composition determined by cast analysis shall comply with the values in Table 3.
Permissible deviations between the limiting values for cast analysis and the values for product analysis
are given in Table 4.
The product analysis shall be carried out when specified at the time of the enquiry and order (see B.4).
7.1.3 Mechanical properties
Where the steel is ordered without hardenability requirements, the requirements for mechanical
properties specified in Tables 7 or 8 apply as appropriate for the particular heat treatment condition.
In this case, the hardenability values given in Table 5 are for guidance purposes only.
The mechanical property values given in Table 8 apply to test pieces in the quenched and tempered
condition, which have been taken and prepared in accordance with Figure 2 or Figures 3 and 4 (see also
footnote a to Table 1).
7.1.4 Hardenability
Where the steel is ordered using the designations given in Table 5 or 6 to normal (see Table 5) or to
narrowed (see Table 6) hardenability requirements, the values of hardenability given in Table 5 or 6,
respectively apply in addition to the requirements cited in Table 1, columns 9.1 and 9.2. (see footnote b
to Table 3).
7.1.5 Surface hardness
For the surface hardness of alloy steels after flame or induction hardening, the specifications in
Table 9 apply.
7.2 Machinability
All steels are machinable in the condition “soft annealed”. Where improved machinability is required,
grades with a specified sulfur range and/or with a specific treatment should be ordered to improve
machinability (see also Table 1, line 6).
7.3 Cold shearability
7.3.1 Under suitable shearing conditions (avoiding local stress peaks, preheating, application of blades
with a profile adapted to that of the product, etc.) all steels are cold shearable in the soft annealed (+A)
condition.
© ISO 2016 – All rights reserved 5
---------------------- Page: 10 ----------------------
ISO 683-2:2016(E)
7.3.2 Steel grades 34Cr4, 37Cr4, 41Cr4, 25CrMo4, 34CrMo4, 42CrMo4 and 41CrNiMo2 with maximum
and specified range S-content, boron-alloy steel grades 33MnCrB5-2 and 39MnCrB6-2 and the
corresponding +H, +HH and +HL grades (see Tables 3 and 5 to 7) are, under suitable conditions, also cold
shearable when being delivered in the condition “treated to improve shearability (+S)” with the hardness
requirements given in Table 7.
7.3.3 Under suitable conditions, steel grades 20MnB5, 30MnB5, 39MnB5 and 27MnCrB5-2, and
the corresponding grades with requirements on hardenability (see Table 5), are cold shearable in the
untreated condition.
7.4 Grain size
All steels shall have a fine grain structure with an austenite grain size of 5 or finer when tested in
accordance with ISO 643. For verification, see B.2.
7.5 Non-metallic inclusions
7.5.1 Microscopic inclusions
The special steels shall have a certain degree of cleanness; however, verification of the non-metallic
inclusion content requires a special agreement. If there is such an agreement at the time of enquiry
and order, the microscopic non-metallic inclusion content shall be determined to an agreed procedure
and within agreed limits in accordance with ISO 4967 or another standard, e.g. regional standards
EN 10247 or JIS G 0555.
For grades with specified minimum sulfur content, the agreement should not include sulfides.
7.5.2 Macroscopic inclusions
This requirement is applicable to the verification of the macroscopic inclusions in special steels. If
verification is agreed, the method and acceptance limits shall be agreed at the time of enquiry and order.
7.6 Internal soundness
Where appropriate, requirements relating to the internal soundness of the products shall be agreed at
the time of enquiry and order (see B.3).
7.7 Surface quality
7.7.1 All products shall have a smooth surface finish appropriate to the manufacturing process applied.
7.7.2 Minor surface imperfections, which may occur also under normal manufacturing conditions,
such as prints originating from rolled-in scale, are not to be regarded as defects.
7.7.3 Bars and wire rod shall be delivered with surface class 1za2 according to ISO 9443 and hot-rolled
plates and wide flats are delivered with a surface according ISO 7788 unless otherwise agreed at the time
of enquiry and order.
Where no International Standard on the surface quality of steel products exists, detailed requirements
referring to this chara
...
FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 683-2
ISO/TC 17/SC 4
Heat-treatable steels, alloy steels and
Secretariat: DIN
free-cutting steels —
Voting begins
on: 2016-03-25
Part 2:
Voting terminates
Alloy steels for quenching and
on: 2016-05-25
tempering
Aciers pour traitement thermique, aciers alliés et aciers pour
décolletage —
Partie 2: Aciers alliés pour trempe et revenu
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 683-2:2016(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
©
NATIONAL REGULATIONS. ISO 2016
---------------------- Page: 1 ----------------------
ISO/FDIS 683-2:2016(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2016, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2016 – All rights reserved
---------------------- Page: 2 ----------------------
ISO/FDIS 683-2:2016(E)
Contents Page
Foreword .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Classification and designation . 3
4.1 Classification . 3
4.2 Designation . 3
5 Information to be supplied by the purchaser. 3
5.1 Mandatory information . 3
5.2 Options and/or supplementary or special requirements . 3
5.3 Ordering example . 4
6 Manufacturing process . 4
6.1 General . 4
6.2 Deoxidation . 4
6.3 Heat-treatment condition and surface condition at delivery . 4
6.3.1 Heat-treatment condition . 4
6.3.2 Particular surface conditions . 4
6.4 Traceability of the cast . 4
7 Requirements . 5
7.1 Chemical composition, mechanical properties and hardenability . 5
7.1.1 General. 5
7.1.2 Chemical composition . 5
7.1.3 Mechanical properties . 5
7.1.4 Hardenability . 5
7.1.5 Surface hardness . 5
7.2 Machinability . 5
7.3 Cold shearability . 5
7.4 Grain size . 6
7.5 Non-metallic inclusions . 6
7.5.1 Microscopic inclusions . 6
7.5.2 Macroscopic inclusions . 6
7.6 Internal soundness . 6
7.7 Surface quality . 6
7.8 Decarburization . 7
7.9 Shape, dimensions and tolerances . 7
8 Inspection . 7
8.1 Testing procedures and types of documents . 7
8.2 Frequency of testing . 7
8.3 Specific inspection and testing . 8
8.3.1 Verification of the hardenability, hardness and mechanical properties . 8
8.3.2 Visual and dimensional inspection . 8
9 Test methods . 8
9.1 Chemical analysis . 8
9.2 Mechanical tests . 8
9.2.1 Tensile test . 8
9.2.2 Impact test . 8
9.3 Hardness and hardenability tests . 8
9.3.1 Hardness in treatment conditions +A and +S . 8
9.3.2 Verification of hardenability . 9
9.3.3 Surface hardness . 9
9.4 Retests . 9
© ISO 2016 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO/FDIS 683-2:2016(E)
10 Marking . 9
Annex A (normative) Ruling sections for mechanical properties .31
Annex B (normative) Supplementary or special requirements .35
Annex C (informative) Designation of steels given in this part of ISO 683 and of comparable
grades covered in various designation systems.37
Annex D (informative) Dimensional standards applicable to products complying with this
part of ISO 683 .39
Bibliography .40
iv © ISO 2016 – All rights reserved
---------------------- Page: 4 ----------------------
ISO/FDIS 683-2:2016(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment,
as well as information about ISO’s adherence to the World Trade Organization (WTO) principles in the
Technical Barriers to Trade (TBT) see the following URL: www.iso.org/iso/foreword.html.
The committee responsible for this document is ISO/TC 17, Steel, Subcommittee SC 4, Heat treatable and
alloy steels.
This second edition cancels and replaces the first edition (ISO 683-2:2012), of which constitutes a minor
revision.
ISO 683 consists of the following parts, under the general title Heat-treatable steels, alloy steels and free-
cutting steels:
— Part 1: Non-alloy steels for quenching and tempering
— Part 2: Alloy steels for quenching and tempering
— Part 3: Case-hardening steels
— Part 4: Free-cutting steels
— Part 5: Nitriding steels
— Part 14: Hot-rolled steels for quenched and tempered springs
— Part 15: Valve steels for internal combustion engines
— Part 17: Ball and roller bearing steels
— Part 18: Bright steel products
© ISO 2016 – All rights reserved v
---------------------- Page: 5 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 683-2:2016(E)
Heat-treatable steels, alloy steels and free-cutting steels —
Part 2:
Alloy steels for quenching and tempering
1 Scope
This part of ISO 683 specifies the technical delivery requirements for
— semi-sinished products, hot formed, e.g. blooms, billets, slabs (see Note 1),
— bars (see Note 1),
— wire rod,
— finished flat products, and
— hammer or drop forgings (see Note 1)
manufactured from the direct hardening alloy steels and the alloy flame- and induction-hardening
steels listed in Table 3 and supplied in one of the heat-treatment conditions given for the different types
of products in Table 1 and in one of the surface conditions given in Table 2.
The steels are, in general, intended for the manufacture of quenched and tempered or austempered
(see 3.2 and Note 2) and flame- or induction-hardened machine parts (see Tables 8 and 9).
The requirements for mechanical properties given in this part of ISO 683 are restricted to the sizes
given in the relevant Table 8.
NOTE 1 Hammer-forged semi-finished products (blooms, billets, slabs, etc.), seamless rolled rings and
hammer-forged bars are in the following covered under semi-finished products or bars and not under the term
“hammer and drop forgings”.
NOTE 2 For the purposes of simplification, the term “quenched and tempered” is, unless otherwise indicated,
used in the following also for the austempered condition.
NOTE 3 For International Standards relating to steels complying with the requirements for the chemical
composition in Table 3, however, supplied in other product forms or treatment conditions than given above or
intended for special applications, and for other related International Standards, see the Bibliography.
NOTE 4 This part of ISO 683 does not apply to bright products and bars and wire rod for cold heading. For
such products, see ISO 683-18 and ISO 4954.
In special cases, variations in these technical delivery requirements or additions to them can form the
subject of an agreement at the time of enquiry and order (see 5.2 and Annex B).
In addition to this part of ISO 683, the general technical delivery requirements of ISO 404 are applicable.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 148-1, Metallic materials — Charpy pendulum impact test — Part 1: Test method
© ISO 2016 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO/FDIS 683-2:2016(E)
ISO 377, Steel and steel products — Location and preparation of samples and test pieces for mechanical testing
ISO 404:2013, Steel and steel products — General technical delivery requirements
ISO 642, Steel — Hardenability test by end quenching (Jominy test)
ISO 643, Steels — Micrographic determination of the apparent grain size
ISO 3887, Steels — Determination of depth of decarburization
ISO 4885, Ferrous products — Heat treatments — Vocabulary
ISO 4948-1, Steels — Classification — Part 1: Classification of steels into unalloyed and alloy steels based
on chemical composition
ISO 4948-2, Steels — Classification — Part 2: Classification of unalloyed and alloy steels according to main
quality classes and main property or application characteristics
ISO/TS 4949, Steel names based on letter symbols
ISO 4967, Steel — Determination of content of non-metallic inclusions — Micrographic method using
standard diagrams
ISO 6506-1, Metallic materials — Brinell hardness test — Part 1: Test method
ISO 6508-1, Metallic materials — Rockwell hardness test — Part 1: Test method (scales A, B, C, D, E, F, G, H,
K, N, T)
ISO 6892-1, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
ISO 6929, Steel products — Vocabulary
ISO 7788, Steel — Surface finish of hot-rolled plates and wide flats — Delivery requirements
ISO 9443, Heat-treatable and alloy steels — Surface quality classes for hot-rolled round bars and wire
rods — Technical delivery conditions
ISO 10474, Steel and steel products — Inspection documents
ISO 14284, Steel and iron — Sampling and preparation of samples for the determination of chemical
composition
3 Terms and definitions
For the purposes of this document, the definitions in ISO 377, ISO 4885, ISO 4948-1, ISO 4948-2,
ISO 6929, ISO 14284, and the following apply.
NOTE For deviations from these terms and definitions, see Notes 1 and 2 of Clause 1.
3.1
ruling section
section for which the specified mechanical properties shall apply
Note 1 to entry: Independent of the actual shape and dimensions of the cross-section of the product, the size of its
ruling section is always given by a diameter. This corresponds to the diameter of an “equivalent round bar”. That
is a round bar which will show the same cooling rate as the actual ruling section of the product concerned at its
position for taking the test pieces, when being cooled from austenitizing temperature.
2 © ISO 2016 – All rights reserved
---------------------- Page: 7 ----------------------
ISO/FDIS 683-2:2016(E)
3.2
austempering
heat treatment for producing ADI cast iron, involving austenitizing followed by isothermal tempering at
a temperature above Ms to ensure partial transformation of the austenite to ferrite
Note 1 to entry: The final cooling to ambient temperature is not at a specific rate.
[SOURCE: ISO 4885:1996, 3.11, modified]
3.3
non-alloy steel
non-alloy steel as defined in ISO 4948-1:1982, 3.1.2
4 Classification and designation
4.1 Classification
The classification of the relevant steel grades is according to ISO 4948-1 and ISO 4948-2. All steel grades
covered by this part of ISO 683 are alloy special steels.
4.2 Designation
For the steel grades covered by this part of ISO 683, the steel names as given in the relevant tables are
allocated in accordance with ISO/TS 4949.
5 Information to be supplied by the purchaser
5.1 Mandatory information
The manufacturer shall obtain the following information from the purchaser at the time of enquiry
and order:
a) quantity to be delivered;
b) designation of the product form (slab, bloom, billet, round bar, wire rod, wide flat, sheet, plate, strip,
forging, etc.);
c) either the designation of the dimensional standard and the dimensions and tolerances selected
from this (see 7.9) or, for example in the case of drop forgings, the designation of the drawing or any
other document covering the dimensions and tolerances required for the product;
d) reference to this part of ISO 683, i.e. ISO 683-2;
e) the designation of the steel grade given in Table 3;
f) the symbol for the required heat-treatment condition (see Table 1, column 2);
g) standard designation for a test report 2.2 or, if required any other type of inspection document in
accordance with ISO 10474 or according to another regional standard, e.g. EN 10204 or JIS G 0415.
5.2 Options and/or supplementary or special requirements
Several options are specified in this part of ISO 683 and listed below. If the purchaser does not indicate
any of these options, the products will be supplied in accordance with the basic specifications of this
part of ISO 683 (see 5.1):
a) if another surface condition than “hot worked” or a special surface quality is required, the surface
condition (see Table 2) and the surface quality (see 7.7);
© ISO 2016 – All rights reserved 3
---------------------- Page: 8 ----------------------
ISO/FDIS 683-2:2016(E)
b) any requirement for the hardenability (+H, +HH, +HL) for special steels (see 7.1.4 and Tables 5 to 7);
c) any supplementary requirement that shall be complied with, the symbol and, where necessary, the
details of this supplementary requirement (see Annex B);
d) any requirement for the verification of non-metallic inclusion content (see 7.5);
e) verification of hardenability and, if agreed, the information about calculation of the hardenability
(see 9.3.2);
f) any requirement regarding the permissible depth of decarburization (see 7.8);
g) suitability of bars and rod for bright drawing (see 7.7.4);
h) any requirement relating to the removal of surface defects (see 7.7.5).
5.3 Ordering example
EXAMPLE Fifty hot-rolled round bars according to ISO 1035-1 with a nominal diameter of 40 mm and a
nominal length of 8 000 mm with diameter tolerance according to class S and with length tolerance according to
class L2 of ISO 1035-4 made of steel grade ISO 683-2, 42CrMo4 (see Table 3) in the heat-treatment condition +S
(see Table 1), surface blast cleaned (+BC) (see Table 2), product analysis/option B.4 with an inspection certificate
3.1 according to ISO 10474:
50 round bars ISO 1035 – 40,0S × 8 000L2
ISO 683-2 – 42CrMo4+S +BC option B.4
ISO 10474 – 3.1
6 Manufacturing process
6.1 General
The manufacturing process of the steel and of the products is, with the restrictions given by the
requirements in 6.2 to 6.4, left to the discretion of the manufacturer.
For minimum reduction ratio or minimum thickness deformation ratio of rolled and forged products,
see B.5.
6.2 Deoxidation
All steels shall be deoxidized.
6.3 Heat-treatment condition and surface condition at delivery
6.3.1 Heat-treatment condition
The products shall be delivered in one of the heat-treatment conditions given in Table 1, lines 2 to 6 as
agreed during time of enquiry and order.
6.3.2 Particular surface conditions
If so agreed at the time of enquiry and order, the products shall be delivered in one of the particular
surface conditions given in Table 2, lines 3 to 6.
6.4 Traceability of the cast
Each product shall be traceable to the cast (see Clause 10).
4 © ISO 2016 – All rights reserved
---------------------- Page: 9 ----------------------
ISO/FDIS 683-2:2016(E)
7 Requirements
7.1 Chemical composition, mechanical properties and hardenability
7.1.1 General
Table 1 shows the combinations of usual heat-treatment conditions at delivery, product forms and
requirements, as specified in Tables 3 to 9.
Except where steels are ordered in the quenched and tempered condition, this part of ISO 683 makes
for the alloyed steels provisions to be supplied with or without hardenability requirements (see Table 1,
columns 8 and 9).
7.1.2 Chemical composition
The chemical composition determined by cast analysis shall comply with the values in Table 3.
Permissible deviations between the limiting values for cast analysis and the values for product analysis
are given in Table 4.
The product analysis shall be carried out when specified at the time of the enquiry and order (see B.4).
7.1.3 Mechanical properties
Where the steel is ordered without hardenability requirements, the requirements for mechanical
properties specified in Tables 7 or 8 apply as appropriate for the particular heat treatment condition.
In this case, the hardenability values given in Table 5 are for guidance purposes only.
The mechanical property values given in Table 8 apply to test pieces in the quenched and tempered
condition, which have been taken and prepared in accordance with Figure 2 or Figures 3 and 4 (see also
footnote a to Table 1).
7.1.4 Hardenability
Where the steel is ordered using the designations given in Table 5 or 6 to normal (see Table 5) or to
narrowed (see Table 6) hardenability requirements, the values of hardenability given in Table 5 or 6,
respectively apply in addition to the requirements cited in Table 1, columns 9.1 and 9.2. (see footnote b
to Table 3).
7.1.5 Surface hardness
For the surface hardness of alloy steels after flame or induction hardening, the specifications in
Table 9 apply.
7.2 Machinability
All steels are machinable in the condition “soft annealed”. Where improved machinability is required,
grades with a specified sulfur range and/or with a specific treatment should be ordered to improve
machinability (see also Table 1, line 6).
7.3 Cold shearability
7.3.1 Under suitable shearing conditions (avoiding local stress peaks, preheating, application of blades
with a profile adapted to that of the product, etc.) all steels are cold shearable in the soft annealed (+A)
condition.
© ISO 2016 – All rights reserved 5
---------------------- Page: 10 ----------------------
ISO/FDIS 683-2:2016(E)
7.3.2 Steel grades 34Cr4, 37Cr4, 41Cr4, 25CrMo4, 34CrMo4, 42CrMo4 and 41CrNiMo2 with maximum
and specified range S-content, boron-alloy steel grades 33MnCrB5-2 and 39MnCrB6-2 and the
corresponding +H, +HH and +HL grades (see Tables 3 and 5 to 7) are, under suitable conditions, also cold
shearable when being delivered in the condition “treated to improve shearability (+S)” with the hardness
requirements given in Table 7.
7.3.3 Under suitable conditions, steel grades 20MnB5, 30MnB5, 39MnB5 and 27MnCrB5-2, and
the corresponding grades with requirements on hardenability (see Table 5), are cold shearable in the
untreated condition.
7.4 Grain size
All steels shall have a fine grain structure with an austenite grain size of 5 or finer when tested in
accordance with ISO 643. For verification, see B.2.
7.5 Non-metallic inclusions
7.5.1 Microscopic inclusions
The special steels shall have a certain degree of cleanness; however, verification of the non-metallic
inclusion content requires a special agreement. If there is such an agreement at the time of enquiry
and order, the microscopic non-metallic inclusion content shall be determined to an agreed procedure
and within agreed limits in accordance with ISO 4967 or another standard, e.g. regional standards
EN 10247 or JIS G 0555.
For grades with specified minimum sulfur content, the agreement should not include sulfides.
7.5.2 Macroscopic inclusions
This requirement is applicable to the verification of the macroscopic inclusions in special steels. If
verification is agreed, the method and acceptance limits shall be agreed at the time of enquiry and order.
7.6 Internal soundness
Where appropriate, requirements relating to the internal soundness of the products shall be agreed at
the time of enquiry and order (see B.3).
7.7 Surface quality
7.7.1 All products shall have a smooth surface
...
NORME ISO
INTERNATIONALE 683-2
Deuxième édition
2016-07-01
Aciers pour traitement thermique,
aciers alliés et aciers pour
décolletage —
Partie 2:
Aciers alliés pour trempe et revenu
Heat-treatable steels, alloy steels and free-cutting steels —
Part 2: Alloy steels for quenching and tempering
Numéro de référence
ISO 683-2:2016(F)
©
ISO 2016
---------------------- Page: 1 ----------------------
ISO 683-2:2016(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2016
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2016 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 683-2:2016(F)
Sommaire Page
Avant-propos .v
1 Domaine d'application . 1
2 Références normatives . 2
3 Termes et définitions . 2
4 Classification et désignation . 3
4.1 Classification . 3
4.2 Désignation . 3
5 Informations à fournir par l'acheteur . 3
5.1 Informations obligatoires . 3
5.2 Options et/ou exigences supplémentaires ou particulières . 4
5.3 Exemple de commande . 4
6 Procédé d'élaboration . 4
6.1 Généralités . 4
6.2 Désoxydation . 4
6.3 État de traitement thermique et état de surface à la livraison . 5
6.3.1 État de traitement thermique . 5
6.3.2 État de surface particulier . 5
6.4 Traçabilité de la coulée . 5
7 Exigences . 5
7.1 Composition chimique, caractéristiques mécaniques et trempabilité . 5
7.1.1 Généralités . 5
7.1.2 Composition chimique . 5
7.1.3 Caractéristiques mécaniques . 5
7.1.4 Trempabilité . 5
7.1.5 Dureté de la surface . . 6
7.2 Usinabilité . 6
7.3 Aptitude au cisaillage à froid . 6
7.4 Taille de grain . 6
7.5 Inclusions non métalliques . 6
7.5.1 Inclusions microscopiques . 6
7.5.2 Inclusions macroscopiques . 6
7.6 Santé interne . 7
7.7 Qualité de surface . 7
7.8 Décarburation . 7
7.9 Forme, dimensions et tolérances . 7
8 Contrôle. 7
8.1 Procédures d'essai et types de documents . 7
8.2 Fréquence des essais . 8
8.3 Contrôle et essai spécifiques . 8
8.3.1 Vérification de la trempabilité, de la dureté et des caractéristiques mécaniques . 8
8.3.2 Contrôles visuels et dimensionnels . 8
9 Méthodes d'essai . 9
9.1 Analyse chimique . 9
9.2 Essais mécaniques . 9
9.2.1 Essai de traction . 9
9.2.2 Essai de résilience . 9
9.3 Essais de dureté et de trempabilité . 9
9.3.1 Dureté aux états de traitement +A et +S . 9
9.3.2 Vérifications de la trempabilité . 9
9.3.3 Dureté de la surface . .10
9.4 Contre-essais .10
© ISO 2016 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 683-2:2016(F)
10 Marquage .10
Annexe A (normative) Sections déterminantes pour les caractéristiques mécaniques .32
Annexe B (normative) Exigences supplémentaires ou particulières .36
Annexe C (informative) Comparaison des désignations d'aciers indiquées dans cette partie
de l'ISO 683 avec d'autres nuances d'acier présentées dans d'autres systèmes de
désignation .38
Annexe D (informative) Normes dimensionnelles applicables aux produits conformes à
cette partie de l'ISO 683 .40
Bibliographie .41
iv © ISO 2016 – Tous droits réservés
---------------------- Page: 4 ----------------------
ISO 683-2:2016(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l'ISO liés à l'évaluation
de la conformité, ou pour toute information au sujet de l'adhésion de l'ISO aux principes de l’Organisation
mondiale du commerce (OMC) concernant les obstacles techniques au commerce (OTC), voir le lien
suivant: www .iso .org/iso/fr/avant -propos .html.
Le comité chargé de l'élaboration du présent document est l’ISO/TC 17, Acier, sous-comité SC 4, Aciers
pour traitements thermiques et aciers alliés.
Cette troisième édition annule et remplace la deuxième édition (ISO 683-2:2012), qui a fait l’objet d’une
révision mineure.
L’ISO 683 est constituée des parties suivantes, présentées sous le titre général Aciers pour traitement
thermique, aciers alliés et aciers pour décolletage:
— Partie 1: Aciers non alliés pour trempe et revenu
— Partie 2: Aciers alliés pour trempe et revenu
— Partie 3: Aciers pour cémentation
— Partie 4: Aciers pour décolletage
— Partie 5: Aciers pour nitruration
— Partie 14: Aciers laminés à chaud pour ressorts trempés et revenus
— Partie 15: Aciers pour soupapes de moteurs à combustion interne
— Partie 17: Aciers pour roulements
— Partie 18: Produits en aciers transformés à froid
© ISO 2016 – Tous droits réservés v
---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 683-2:2016(F)
Aciers pour traitement thermique, aciers alliés et aciers
pour décolletage —
Partie 2:
Aciers alliés pour trempe et revenu
1 Domaine d'application
Cette partie de l’ISO 683 spécifie les conditions techniques de livraison des:
— demi-produits laminés à chaud, comme par exemple les blooms, billettes et brames (voir Note 1);
— barres (voir Note 1),
— fils machine,
— produits plats finis, et
— pièces forgées par martelage ou estampage (voir Note 1)
fabriqués à partir d'aciers non alliés à trempe directe et d'aciers non alliés par trempe au chalumeau et
par induction énumérés dans le Tableau 3 et livrés dans l'un des états de traitement thermique donnés
pour les différents types de produits dans le Tableau 1 et dans l'un des états de surface donnés dans le
Tableau 2.
D'une manière générale, ces aciers sont destinés à la fabrication de pièces mécaniques trempées et
revenues ou ayant subi un procédé de trempe étagée bainitique (voir 3.2 et Note 2) ou à la fabrication de
pièces mécaniques trempées par induction ou au chalumeau (voir Tableau 8 et 9).
Les exigences en matière de caractéristiques mécaniques données dans cette partie de l’ISO 683 sont
limitées aux dimensions données dans le Tableau 8.
NOTE 1 Les demi-produits forgés par martelage (blooms, billettes, brames, etc.), les couronnes laminées
sans soudure et les barres forgées par martelage figurent parmi les demi-produits ou les barres, et non sous
l'appellation «pièces forgées par martelage ou estampage».
NOTE 2 Dans un but de simplification, l'expression «trempé et revenu» est aussi, sauf indication contraire,
utilisée dans les parties suivantes pour l'état «trempe étagée bainitique».
NOTE 3 Pour les Normes internationales relatives aux aciers qui sont conformes aux exigences de composition
chimique du Tableau 3, mais fournis sous d’autres formes de produits ou dans des états de traitement autres
que ceux indiqués ci-dessus, ou qui sont destinés à des applications spéciales, ainsi que pour d'autres Normes
internationales analogues, voir la Bibliographie.
NOTE 4 La présente partie de l'ISO 683 ne s'applique pas aux produits transformés à froid, barres et fils
machine pour frappe à froid. Pour ces produits, voir les ISO 683-18 et ISO 4954.
Dans certains cas particuliers, il est possible de déroger aux présentes conditions techniques de
livraison ou d'en ajouter d'autres, à condition que le fabricant et l'acheteur en conviennent au moment
de l'appel d'offres et de la commande (voir 5.2 et Annexe B).
En plus de cette partie de l'ISO 683, les conditions générales techniques de livraison de l'ISO 404 sont
applicables.
© ISO 2016 – Tous droits réservés 1
---------------------- Page: 6 ----------------------
ISO 683-2:2016(F)
2 Références normatives
Les documents ci-après, dans leur intégralité ou non, sont des références normatives indispensables à
l'application du présent document. Pour les références datées, seule l'édition citée s'applique. Pour les
références non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
ISO 148-1, Matériaux métalliques — Essai de flexion par choc sur éprouvette Charpy — Partie 1:
Méthode d'essai
ISO 377, Acier et produits en acier — Position et préparation des échantillons et éprouvettes pour essais
mécaniques
ISO 404:2013, Aciers et produits sidérurgiques — Conditions générales techniques de livraison
ISO 642, Acier — Essai de trempabilité par trempe en bout (essai Jominy)
ISO 643, Aciers — Détermination micrographique de la grosseur de grain apparente
ISO 3887, Aciers — Détermination de la profondeur de décarburation
1)
ISO 4885:—, Matériaux ferreux — Traitements thermiques — Vocabulaire
ISO 4948-1, Aciers — Classification — Partie 1: Classification en aciers alliés et en aciers non alliés basée
sur la composition chimique
ISO 4948-2, Aciers — Classification — Partie 2: Classification des aciers alliés et aciers non alliés en fonction
des principales classes de qualité et des caractéristiques principales de propriétés ou d'application
ISO/TS 4949, Désignations des aciers fondées sur des lettres symboles
ISO 4967, Aciers — Détermination de la teneur en inclusions non métalliques — Méthode micrographique à
l’aide d’images types
ISO 6506-1, Matériaux métalliques — Essai de dureté Brinell — Partie 1: Méthode d'essai
ISO 6508-1, Matériaux métalliques — Essai de dureté Rockwell — Partie 1: Méthode d'essai
ISO 6892-1, Matériaux métalliques — Essai de traction — Partie 1: Méthode d'essai à température ambiante
ISO 6929, Produits en acier — Vocabulaire
ISO 7788, Acier — État de surface des tôles et larges-plats laminés à chaud — Conditions de livraison
ISO 9443, Classes de qualité de surface des barres et fils-machine laminés à chaud
ISO 10474, Aciers et produits sidérurgiques — Documents de contrôle
ISO 14284, Fontes et aciers — Prélèvement et préparation des échantillons pour la détermination de la
composition chimique
3 Termes et définitions
Pour les besoins du présent document, les définitions données dans l'ISO 377, l'ISO 4885, l'ISO 4948-1,
l'ISO 4948-2, l'ISO 6929, ISO 14284 et les suivants s'appliquent.
NOTE Pour les variantes de ces termes et définitions, voir les Notes 1 et 2 de l'Article 1.
1) En cours d’élaboration. Étape au moment de la publication: ISO/DIS 4885:2016.
2 © ISO 2016 – Tous droits réservés
---------------------- Page: 7 ----------------------
ISO 683-2:2016(F)
3.1
section déterminante
section pour laquelle les caractéristiques mécaniques spécifiées doivent s'appliquer
Note 1 à l'article: Quelles que soient la forme et les dimensions réelles de la section transversale du produit, la
taille de la section déterminante est toujours donnée sous la forme d'un diamètre, c'est-à-dire d'une barre ronde
qui, aura, pour refroidir à partir de la température d'austénitisation, la même vitesse de refroidissement que la
section déterminante réelle du produit considéré à l'emplacement de prélèvement des éprouvettes.
3.2
trempe étagée bainitique
traitement thermique isotherme pour la fabrication d'une structure bainitique ou austénoferritique
d'une pièce à usiner
Note 1 à l'article: Le refroidissement final jusqu'à la température ambiante ne fait pas l'objet de spécifications
particulières.
2)
[SOURCE: ISO 4885:— , 3.11]
3.3
acier allié
défini dans l'ISO 4948-1:1982, 3.1.3
4 Classification et désignation
4.1 Classification
La classification des nuances d'acier appropriées est appliquée conformément à l'ISO 4948-1 et à
l'ISO 4948-2. Toutes les nuances d'acier concernées par cette partie de l'ISO 683 sont des aciers
spéciaux alliés.
4.2 Désignation
Pour les nuances d'acier concernées par cette partie de l'ISO 683, les noms des aciers tels qu'ils sont
donnés dans les tableaux correspondants sont attribués conformément à l'ISO/TS 4949.
5 Informations à fournir par l'acheteur
5.1 Informations obligatoires
L'acheteur doit fournir les informations suivantes au moment de l'appel d'offres et de la commande:
a) la quantité à livrer;
b) la désignation de la forme du produit (brame, bloom, billette, barre ronde, fils machine, large plat,
feuillard, tôle, bande, pièce forgée, etc.);
c) soit la désignation de la norme dimensionnelle et les dimensions et les tolérances choisies à partir
de celle-ci (voir 7.9), soit, par exemple, dans le cas de pièces forgées par estampage, la désignation
de l'étirage ou de tout autre document concernant les dimensions et les tolérances requises pour le
produit;
d) la référence à cette partie de l'ISO 683, c'est-à-dire, l'ISO 683-2;
e) la désignation des nuances d'acier est donnée dans le Tableau 3;
f) le symbole de l'état de traitement thermique requis (voir Tableau 1, colonne 2);
2) En cours d’élaboration. Étape au moment de la publication : ISO/DIS 4885:2016.
© ISO 2016 – Tous droits réservés 3
---------------------- Page: 8 ----------------------
ISO 683-2:2016(F)
g) la désignation normalisée correspondant au rapport d'essai (2.2) ou, sur demande, à tout autre
document de contrôle conforme à l'ISO 10474, ou, selon une autre norme régionale comme
l'EN 10204 ou la JIS G 0415.
5.2 Options et/ou exigences supplémentaires ou particulières
Un certain nombre d'options sont spécifiées dans cette partie de l'ISO 683 et sont répertoriées ci-
dessous. Si l'acheteur ne précise pas vouloir mettre en œuvre l'une de ces options, les produits seront
commandés conformément aux spécifications de base de cette partie de l'ISO 683 (voir 5.1):
a) Si un état de surface autre que l'état «écroui à chaud» ou une qualité particulière de surface est
requis, l'état de surface (voir Tableau 2) et la qualité de surface (voir 7.7);
b) exigences de trempabilité (+H, +HH, +HL) pour aciers spéciaux (voir 7.1.4 et Tableaux 5 à 7);
c) exigences supplémentaires qui doivent être respectées selon le symbole et, le cas échéant, les
détails de cette exigence supplémentaire (voir Annexe B);
d) exigences relatives à la vérification de la teneur en inclusions non métalliques (voir 7.5);
e) vérifications de la trempabilité et, le cas échéant, informations relatives au calcul de la trempabilité
(voir 9.3.2);
f) exigences relatives à la profondeur admissible de décarburation (voir 7.8);
g) aptitude des barres et des fils machine à l'étirage à froid (voir 7.7.4);
h) exigences relatives à l'élimination des défauts superficiels (voir 7.7.5);
5.3 Exemple de commande
EXEMPLE Cinquante barres rondes laminées à chaud avec un diamètre nominal de 40 mm et une longueur
nominale de 8 000 mm suivant l'ISO 1035-1 avec une tolérance de diamètre de classe S et de longueur de classe L2
selon l'ISO 1035-4, fabriquées en nuance d'acier ISO 683-2, 42CrMo4 (voir Tableau 3), suivant la condition de
traitement thermique +S (voir Tableau 1), une surface grenaillée (+BC) (voir Tableau 2), une analyse sur produit/
option B.4 avec un certificat d'inspection 3.1 tel que spécifié dans l'ISO 10474:
50 barres rondes ISO 1035 – 40,0S × 8 000L2
ISO 683-2 – 42CrMo4+S +BC option B.4
ISO 10474 – 3.1
6 Procédé d'élaboration
6.1 Généralités
Le procédé d'élaboration de l'acier et des produits est laissé au choix du fabricant sous réserve des
limites données par les exigences indiquées de 6.2 à 6.4.
Pour le degré minimal de réduction ou le degré minimal de déformation de l'épaisseur sur les produits
laminés et forgés, voir B.5.
6.2 Désoxydation
Tous les aciers doivent être désoxydés.
4 © ISO 2016 – Tous droits réservés
---------------------- Page: 9 ----------------------
ISO 683-2:2016(F)
6.3 État de traitement thermique et état de surface à la livraison
6.3.1 État de traitement thermique
Les produits doivent être livrés dans l'un des états de traitement thermique spécifiés dans le Tableau 1,
lignes 2 à 6 comme convenu au moment de l'appel d'offres et de la commande.
6.3.2 État de surface particulier
Par accord au moment de l'appel d'offres et de la commande, les produits doivent être livrés dans l'un
des états de surface particuliers spécifiés dans le Tableau 2, lignes 3 à 6.
6.4 Traçabilité de la coulée
Chaque produit doit pouvoir être retracé jusqu'à la coulée (voir Article 10).
7 Exigences
7.1 Composition chimique, caractéristiques mécaniques et trempabilité
7.1.1 Généralités
Le Tableau 1 présente les combinaisons d'états habituels de traitement thermique à la livraison, de
formes de produit et d'exigences requises aux Tableaux 3 à 9.
Sauf lorsque les aciers sont commandés à l'état trempé et revenu, cette partie de la norme ISO 683
prévoit que les dispositions relatives aux aciers alliés doivent être fournies avec ou sans exigences de
trempe (voir Tableau 1, colonnes 8 et 9).
7.1.2 Composition chimique
La composition chimique déterminée par analyse de coulée doit être conforme aux valeurs présentées
dans le Tableau 3.
Les écarts admissibles entre les valeurs limites de l'analyse de coulée et les valeurs de l'analyse sur
produit sont présentés dans le Tableau 4.
L'analyse sur produit doit être réalisée lorsque cela est spécifié au moment de l'appel d'offres et de la
commande (voir B.4).
7.1.3 Caractéristiques mécaniques
Lorsque l'acier est commandé sans exigences de trempabilité, les exigences relatives aux caractéristiques
mécaniques spécifiées dans les Tableaux 7 ou 8 s'appliquent notamment à l'état particulier du traitement
thermique.
Dans ce cas, les valeurs de trempabilité spécifiées dans le Tableau 5 sont données à titre d'indication
seulement.
Les valeurs de propriété mécanique données dans le Tableau 8 s'appliquent aux éprouvettes à l'état
trempé et revenu qui ont été prélevées et préparées selon la Figure 2 ou aux Figures 3 et 4 (voir
également la note de bas de tableau a du Tableau 1).
7.1.4 Trempabilité
Lorsque l'acier est commandé en utilisant les désignations données dans le Tableau 5 ou 6, pour les
exigences de trempabilité normales (voir Tableau 5) ou pour les exigences de trempabilité réduites
© ISO 2016 – Tous droits réservés 5
---------------------- Page: 10 ----------------------
ISO 683-2:2016(F)
(voir Tableau 6), les valeurs de trempabilité spécifiées au Tableau 5 ou 6 , s'appliquent respectivement
en plus des exigences citées au Tableau 1, colonnes 9.1 et 9.2. (voir note de bas de tableau b au Tableau 3).
7.1.5 Dureté de la surface
Pour la dureté des zones superficielles de trempe des aciers alliés pour trempe au chalumeau ou par
induction, les spécifications du Tableau 9 s'appliquent.
7.2 Usinabilité
Tous les aciers à l'état «adouci» sont usinables. Lorsqu'une usinabilité plus importante est nécessaire,
il convient de commander des nuances avec une gamme de soufre spécifiée et/ou avec un traitement
spécifique pour améliorer l’usinabilité (voir également Tableau 1, ligne 6).
7.3 Aptitude au cisaillage à froid
7.3.1 Dans des conditions de cisaillage appropriées (pas de crête de contraintes localisées,
préchauffage, utilisation de lames de profil adapté à celui du produit, etc.), tous les aciers sont cisaillables
à froid à l'état adouci (+A).
7.3.2 Les nuances d'acier 34Cr4, 37Cr4, 41Cr4, 25CrMo4, 34CrMo4, 42CrMo4 et 41CrNiMo2 à teneur
maximale et spécifiée S, les nuances d'aciers alliés au bore 33MnCrB5-2 et 39MnCrB6-2, ainsi que les
exigences +H, +HH et +HL correspondantes (voir Tableau 3 et Tabl
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.