ISO 16220:2000/Cor 1:2000

Magnesium and magnesium alloys — Magnesium alloy ingots and castings — Technical Corrigendum 1

Magnésium et alliages de magnésium — Lingots et pièces moulées en alliages de magnésium — Rectificatif technique 1

General Information

• Status: Withdrawn
• Publication Date: 22-Nov-2000
• Withdrawal Date: 22-Nov-2000
• ICS: 77.150.20 - Magnesium products
• Technical Committee: ISO/TC 79/SC 5 - Magnesium and alloys of cast or wrought magnesium
• Drafting Committee: ISO/TC 79/SC 5 - Magnesium and alloys of cast or wrought magnesium
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 14-Mar-2005

Relations

• Revised: SIST ISO 16220:2005 - Magnesium and magnesium alloys -- Magnesium alloy ingots and castings
• Effective Date: 12-May-2008
• Revised: ISO 16220:2005 - Magnesium and magnesium alloys — Magnesium alloy ingots and castings
• Effective Date: 15-Apr-2008
• Corrects: ISO 16220:2000 - Magnesium and magnesium alloys — Magnesium alloy ingots and castings
• Effective Date: 06-Jun-2022
• Child: ISO 16220:2000 - Magnesium and magnesium alloys — Magnesium alloy ingots and castings
• Effective Date: 15-Apr-2008
• Child: SIST ISO 16220:2002 - Magnesium and magnesium alloys -- Magnesium alloy ingots and castings
• Effective Date: 12-May-2008

Standards Content (Sample)

INTERNATIONAL STANDARD ISO 16220:2000
TECHNICAL CORRIGENDUM 1
Published 2000-11-15
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION � МЕЖДУНАРОДНАЯОРГАНИЗАЦИЯПОСТАНДАРТИЗАЦИИ � ORGANISATION INTERNATIONALE DE NORMALISATION
Magnesium and magnesium alloys —
Magnesium alloy ingots and castings
TECHNICAL CORRIGENDUM 1
Magnésium et alliages de magnésium — Lingots et pièces moulées en magnésium
RECTIFICATIF TECHNIQUE 1
Technical Corrigendum 1 to International Standard ISO 16220:2000 was prepared by Technical Committee
ISO/TC 79, Light metals and their alloys, Subcommittee SC 5, Magnesium and alloys of cast or wrought
magnesium.
Page 3
Table 1
Replace the existing table with the one on page 2 of this document. In particular, see the values for Zn content.
Page 4
Table 2
Replace the existing table with the one on page 3 of this document. In particular, see the values for Zn content and
Cu content.
ICS 77.150.20 Ref. No. ISO 16220:2000/Cor.1:2000(E)
© ISO 2000 – All rights reserved
Printed in Switzerland

---------------------- Page: 1 ----------------------
ISO 16220:2000/Cor.1:2000(E)
2 © ISO 2000 – All rights reserved
Table 1 — Chemical composition of magnesium alloy ingots
Alloy group Material designation Composition
%bymass
a b
In accordance In accordance min. or Mg Al Zn Mn RE Zr Ag Y Li Si Fe Cu Ni Others
with ISO 2092 with EN 1753 max.
(each)
ISO-MgAl8Zn1 EN-MB21110 min. Balance 7,2 0,45 0,17 – – – – – – – – – –
max. 8,5 0,9 0,40 – – – – – 0,05 0,004 0,025 0,001 0,01
MgAlZn ISO-MgAl9Zn1 (A) EN-MB21120 min. Balance 8,5 0,45 0,17 – – – – – – – – – –
max. 9,5 0,9 0,40 – – – – – 0,05 0,004 0,025 0,001 0,01
ISO-MgAl9Zn1 (B) EN-MB21121 min. Balance 8,0 0,3 0,1 – – – – – – – – – –
max. 10,0 1,0 0,50 – – – – – 0,3 0,03 0,20 0,01 0,05
ISO-MgAl2Mn EN-MB21210 min. Balance 1,7 – 0,35 – – – – – – – – – –
max. 2,5 0,20 0,60 – – – – – 0,05 0,004 0,008 0,001 0,01
MgAlMn ISO-MgAl5Mn EN-MB21220 min. Balance 4,5 – 0,28 – – – – – – – – – –
max. 5,3 0,20 0,50 – – – – – 0,05 0,004 0,008 0,001 0,01
ISO-MgAl6Mn EN-MB21230 min. Balance 5,6 – 0,26 – – – – – – – – – –
max. 6,4 0,20 0,50 – – – – – 0,05 0,004 0,008 0,001 0,01
MgAlSi ISO-MgAl2Si EN-MB21310 min. Balance 1,9 – 0,2 – – – – – 0,7 – – – –
max. 2,5 0,20 0,6 – – – – – 1,2 0,004 0,008 0,001 0,01
ISO-MgAl4Si EN-MB21320 min. Balance 3,7 – 0,2 – – – – – 0,7 – – – –
max. 4,8 0,20 0,6 – – – – – 1,2 0,004 0,008 0,001 0,01
MgZnCu ISO-MgZn6Cu3Mn EN-MB32110 min. Balance – 5,5 0,25 – – – – – – – 2,4 – –
max. 0,2 6,5 0,75 – – – – – 0,20 0,05 3,0 0,01 0,01
c
MgZnREZr ISO-MgZn4RE1Zr EN-MB35110 min. Balance – 3,5 – 1,00 0,1 – – – – – – – –
max. – 5,0 0,15 1,75 1,0 – – – 0,01 0,01 0,03 0,005 0,01
ISO-MgRE3Zn2Zr EN-MB65120 min. Balance – 2,0 – 2,4 0,1 – – – – – – – –
max. – 3,0 0,15 4,0 1,0 – – – 0,01 0,01 0,03 0,005 0,01
d
MgREAgZr ISO-MgAg2RE2Zr EN-MB65210 min. Balance – – – 2,0 0,1 2,0 – – – – – – –
max. – 0,2 0,15 3,0 1,0 3,0 – – 0,01 0,01 0,03 0,005 0,01
ISO-MgRE2Ag1Zr EN-MB65220 min. Balance – – – 1,5 0,1 1,3 – – – – 0,05 – –
max. – 0,2 0,15 3,0 1,0 1,7 – – 0,01 0,01 0,10 0,005 0,01
e, f
MgYREZr ISO-MgY5RE4Zr EN-MB95310 min. Balance – – – 1,5 0,1 – 4,75 – – – – – –
max. – 0,20 0,15 4,0 1,0 – 5,5 0,20 0,01 0,01 0,03 0,005 0,01
ISO-MgY4RE3Zr EN-MB95320 min. Balance – – – 2,4 0,1 – 3,7 – – – – – –
max. – 0,20 0,15 4,4 1,0 – 4,3 0,20 0,01 0,01 0,03 0,005 0,01
a
For maximum manganese content, see annex B.
b
RE = Rare earth metals.
c
Cerium-rich.
d
Neodymium-rich.
e
Neodymium- and heavy R
...

NORME INTERNATIONALE ISO 16220:2000
RECTIFICATIF TECHNIQUE 1
Publié 2000-11-15
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION � МЕЖДУНАРОДНАЯОРГАНИЗАЦИЯПОСТАНДАРТИЗАЦИИ � ORGANISATION INTERNATIONALE DE NORMALISATION
Magnésium et alliages de magnésium —
Lingots et pièces moulées en magnésium
RECTIFICATIF TECHNIQUE 1
Magnesium and magnesium alloys — Magnesium alloy ingots and castings
TECHNICAL CORRIGENDUM 1
Le Rectificatif technique 1 à la Norme internationale ISO 16220:2000 a été élaboré par le comité technique
ISO/TC 79, Métaux légers et leurs alliages, sous-comité SC 5, Magnésium et alliages de magnésium, moulés ou
corroyés.
Page 3
Tableau 1
Remplacer le tableau existant par celui de la page 2 du présent document. En particulier, voir les valeurs de teneur
en Zn.
Page 4
Tableau 2
Remplacer le tableau existant par celui de la page 3 du présent document. En particulier, voir les valeurs de teneur
en Zn et de teneur en Cu.
o
ICS 77.150.20 Réf. n ISO 16220:2000/Cor.1:2000(F)
© ISO 2000 – Tous droits réservés
ImpriméenSuisse

---------------------- Page: 1 ----------------------
ISO 16220:2000/Cor.1:2000(F)
2 © ISO 2000 – Tous droits réservés
Tableau 1 — Composition chimique des lingots en alliages de magnésium
Groupe Désignation du matériau Composition
d'alliages
% en masse
a b
Conformément Conformément min. ou Mg Al Zn Mn RE Zr Ag Y Li Si Fe Cu Ni Autres
à l'ISO 2092 à l'EN 1753 max.
(chacun)
ISO-MgAl8Zn1 EN-MB21110 min. Le reste 7,2 0,45 0,17 – – – – – – – – – –
max. 8,5 0,9 0,40 – – – – – 0,05 0,004 0,025 0,001 0,01
MgAlZn ISO-MgAl9Zn1 (A) EN-MB21120 min. Le reste 8,5 0,45 0,17 – – – – – – – – – –
max. 9,5 0,9 0,40 – – – – – 0,05 0,004 0,025 0,001 0,01
ISO-MgAl9Zn1 (B) EN-MB21121 min. Le reste 8,0 0,3 0,1 – – – – – – – – – –
max. 10,0 1,0 0,50 – – – – – 0,3 0,03 0,20 0,01 0,05
ISO-MgAl2Mn EN-MB21210 min. Le reste 1,7 – 0,35 – – – – – – – – – –
max. 2,5 0,20 0,60 – – – – – 0,05 0,004 0,008 0,001 0,01
MgAlMn ISO-MgAl5Mn EN-MB21220 min. Le reste 4,5 – 0,28 – – – – – – – – – –
max. 5,3 0,20 0,50 – – – – – 0,05 0,004 0,008 0,001 0,01
ISO-MgAl6Mn EN-MB21230 min. Le reste 5,6 – 0,26 – – – – – – – – – –
max. 6,4 0,20 0,50 – – – – – 0,05 0,004 0,008 0,001 0,01
MgAlSi ISO-MgAl2Si EN-MB21310 min. Le reste 1,9 – 0,2 – – – – – 0,7 – – – –
max. 2,5 0,20 0,6 – – – – – 1,2 0,004 0,008 0,001 0,01
ISO-MgAl4Si EN-MB21320 min. Le reste 3,7 – 0,2 – – – – – 0,7 – – – –
max. 4,8 0,20 0,6 – – – – – 1,2 0,004 0,008 0,001 0,01
MgZnCu ISO-MgZn6Cu3Mn EN-MB32110 min. Le reste – 5,5 0,25 – – – – – – – 2,4 – –
max. 0,2 6,5 0,75 – – – – – 0,20 0,05 3,0 0,01 0,01
c
MgZnREZr ISO-MgZn4RE1Zr EN-MB35110 min. Le reste – 3,5 – 1,00 0,1 – – – – – – – –
max. – 5,0 0,15 1,75 1,0 – – – 0,01 0,01 0,03 0,005 0,01
ISO-MgRE3Zn2Zr EN-MB65120 min. Le reste – 2,0 – 2,4 0,1 – – – – – – – –
max. – 3,0 0,15 4,0 1,0 – – – 0,01 0,01 0,03 0,005 0,01
d
MgREAgZr ISO-MgAg2RE2Zr EN-MB65210 min. Le reste – – – 2,0 0,1 2,0 – – – – – – –
max. – 0,2 0,15 3,0 1,0 3,0 – – 0,01 0,01 0,03 0,005 0,01
ISO-MgRE2Ag1Zr EN-MB65220 min. Le reste – – – 1,5 0,1 1,3 – – – – 0,05 – –
max. – 0,2 0,15 3,0 1,0 1,7 – – 0,01 0,01 0,10 0,005 0,01
e, f
MgYREZr ISO-MgY5RE4Zr EN-MB95310 min. Le reste – – – 1,5 0,1 – 4,75 – – – – – –
max. – 0,20 0,15 4,0 1,0 – 5,5 0,20 0,01 0,01 0,03 0,005 0,01
ISO-MgY4RE3Zr EN-MB95320 min. Le reste – – – 2,4 0,1 – 3,7 – – – – – –
max. – 0,20 0,15 4,4 1,0 – 4,3 0,20 0,01 0,01 0,03 0,005 0,01
a
Pour la teneur maximale en manganèse, voir annexe B.
b
RE = Métaux en terre rare.
c
Richeencérium.
d
Richeennéodyme.
e
Richeennéodyme et en RE lourds.
f