SIST ISO 1772:1995

Laboratory crucibles in porcelain and silica

Three types of crucibels are specified: Type 1, low form, type 2 medium form and type 3 tall form bases an a height/diameter ratio of 0,63; 0,8 and 1,25 resp. Further two types of lid are described: type D, a lid of slightly domed shape and typ R, a recessed lid. Material and construction are specified, shape and dimensions are shown in drawings and in a table.

Creusets de laboratoire en porcelaine et en silice

Laboratorijski talilni lončki iz porcelana in čistega stekla

General Information

• Status: Published
• Publication Date: 31-Jul-1995
• ICS: 71.040.20 - Laboratory ware and related apparatus
• Technical Committee: I12 - Imaginarni 12 Imaginarni TC za ISO področje - vzdrževani privzeti ISO standardi
• Current Stage: 6060 - National Implementation/Publication (Adopted Project)
• Start Date: 01-Aug-1995
• Due Date: 01-Aug-1995
• Completion Date: 01-Aug-1995
• Ref Project: ISO 1772:1975 - Laboratory crucibles in porcelain and silica

Overview

SIST ISO 1772:1995 specifies international standards for laboratory crucibles made from porcelain and silica, widely used in general laboratory applications. The document defines three crucible types based on their height-to-diameter ratios, as well as two lid types designed to ensure optimal handling and stability. Materials, construction requirements, and dimensional specifications are clearly outlined to support consistency, safety, and compatibility in lab environments globally.

This standard caters to laboratories needing reliable crucibles for tasks involving high-temperature chemical analysis and sample processing. By adhering to ISO 1772 specifications, manufacturers and users benefit from standardized sizes, materials, and design features that ensure repeatability and reliability in experimental procedures.

Key Topics

• Crucible Types:

  • Type 1 (Low form) with height/diameter ratio of 0.63
  • Type 2 (Medium form) with height/diameter ratio of 0.8
  • Type 3 (Tall form) with height/diameter ratio of 1.25

• Lid Types:

  • Type D: Slightly domed lids with a central ring or protrusion for easy lifting by crucible tongs or wire supports
  • Type R: Recessed lids with design optimizations for ease of removal

• Material Requirements:

  • Porcelain crucibles must be glazed on the surface (excluding base and edges optionally) and conform to ISO/R 1775
  • Silica crucibles must be made from vitrified glassy silica, either translucent or transparent

• Dimensional Specifications:

  • Sizes are standardized with specific diameters and heights, allowing cross-compatibility
  • Diameter increments are multiples of 10 mm, with height adjusted accordingly to meet the ratio
  • Wall thickness varies depending on material but must ensure structural integrity and thermal stability

• Markings and Identification:

  • Each crucible and lid must be clearly marked with the type and nominal diameter (e.g., "1/30" for Type 1, 30 mm diameter)
  • Manufacturer’s name or trademark must also be displayed for traceability

• Stability and Construction:

  • Crucibles must stand steady on flat surfaces without wobbling
  • Lid designs facilitate safe handling and prevent contamination during heating processes

Applications

ISO 1772 laboratory crucibles are essential tools across many scientific and industrial fields, including:

• Chemical and petrochemical laboratories for melting, ashing, and calcination at high temperatures
• Environmental labs performing sample digestion and residue analysis
• Metallurgical applications requiring contamination-free, heat-resistant containers
• Educational laboratories requiring standardized equipment for reproducible experimental work

The standardization of crucible dimensions and materials assists labs in selecting compatible lids and accessories, reducing the risk of experimental errors due to mismatched equipment. Manufacturers can produce versatile crucibles knowing they meet internationally accepted quality and dimensional criteria.

Related Standards

• ISO 1775 - Laboratory Porcelain Apparatus: Specifications and Test Methods
• Other ISO standards related to laboratory glassware and ceramic materials may complement ISO 1772 to ensure comprehensive quality across lab equipment

Adherence to ISO 1772 combined with referencing complementary ISO material standards ensures maximum safety, durability, and usability for laboratory crucibles made of porcelain and silica. This contributes to enhanced laboratory efficiency and confidence in high-temperature experimental results.

---

Keywords: ISO 1772, laboratory crucibles, porcelain crucibles, silica crucibles, crucible dimensions, laboratory equipment, high-temperature crucibles, crucible lids, ISO porcelain standards, laboratory glassware standards.

Standards Content (Sample)

SLOVENSKI STANDARD
01-avgust-1995
/DERUDWRULMVNLWDOLOQLORQþNLL]SRUFHODQDLQþLVWHJDVWHNOD
Laboratory crucibles in porcelain and silica
Creusets de laboratoire en porcelaine et en silice
Ta slovenski standard je istoveten z: ISO 1772:1975
ICS:
71.040.20 Laboratorijska posoda in Laboratory ware and related
aparati apparatus
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

INTERNATIONAL STANDARD
1772.
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .ME)KflYHAPOAHAA OPI-AHM3ALUM l-Io CTAHAAPTM3AUMM~ORGANISATION INTERNATIONALE DE NORMALISATION
Laboratory crucibles in porcelain and silica
Creusets de labora toire en porcelaine et en silice
First edition - 1975-09-01
Ref. No. ISO 1772-1975 (E)
UDC 542.232.5.004.1
Descriptors : Jabot-atm-y glassware, crucibles, porcelain, Silicon dioxide, specifications, designation.
Price based on 4 pages
FOREWORD
ISO (the International Organization for Standardization) is a worldwide federation
of national Standards institutes (ISO Member Bodies). The work of developing
International Standards is carried out through ISO Technical Committees. Every
Member Body interested in a subject for which a Technical Committee has been set
up has the right to be represented on that Committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the Technical Committees are circulated
to the Member Bodies for approval before their acceptance as International
Standards by the ISO Council.
Prior to 1972, the results of the work of the Technical Committees were published
as ISO Recommendations; these documents are now in the process of being
transformed into International Standards. As part of this process, Technical
Committee ISO/TC 48 has reviewed ISO Recommendation R 1772 and found it
technically suitable for transformation. International Standard ISO 1772 therefore
replaces ISO Recommendation R 1772-1970 to which it is technically identical.
ISO Recommendation R 1772 was approved by the Member Bodies of the
following countries :
Austria India South Africa, Rep. of
Belgium Iran
Spain
Canada I reland Thailand
Turkey
Colombia I taly
Czechoslovakia Korea, Dem. P. Rep. of United Kingdom
Egypt, Arab Rep. of Netherlands U.S.A.
France New Zealand
U.S.S.R.
Germany Peru Yugoslavia
Greece Poland
No Member Body expressed disapproval of the Recommendation.
No Member Body disapproved the transformation of ISO/R 1772 into an
International Standard.
0 International Organkation for Standardkation, 1975 l
Printed in Switzerland
INTERNATIONAL STANDARD ISO 17724975 (E)
Laboratory crucibles in porcelain and silica
1 SCOPE AND FIELD OF APPLICATION 5 SERIES OF SIZES
This International Standard specifies requirements for an The series of sizes of crucibles shall be as shown in the
internationally acceptable series of porcelain and silica table.
crucibles and lids for general laboratory requirements.
NOTE - No values of nominal capacity are specified, but it is
recommended that manufacturers should state these for the
NOTES
information of users, on the basis that :
1 It is recognized that some sizes of crucible iarger than those
nominal capacity = approximately 75 % of Overflow capacity.
listed may be needed for use in laboratories for special purposes. It
is recommended that such larger sizes should be designed within the
general framework of this International Standard, i.e. by selecting a
suitable multiple of 10 mm as the nominal external top diameter,
6 MATERIAL
and applying one of the three Standard ratios in Order to obtain the
nominal height.
6.1 Porcelain crucibles and lids shall be made from
vitrified porcelain with a glazed surface, but the bases and
2 This International Standard does not deal with laboratory
rims of the crucibles need not necessarily be glazed. The
crucibles made of materials other than porcelain and silica (for
other ceramic materials, metals, plastics
example, glass and
porcelain used shall satisfy the requirements of ISO 1775.
material& Nevertheless, it is expected that the types, sizes and
dimensions specified herein may provide useful guidance for those
NOTE - The sizes and dimensions included in this International
concerned with the manufacture or standardization of crucibles
Standard may also conveniently be applied to crucibles of unglazed
made of such other materials, and that it may become possible to
porcelain.
in
...

INTERNATIONAL STANDARD
1772.
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .ME)KflYHAPOAHAA OPI-AHM3ALUM l-Io CTAHAAPTM3AUMM~ORGANISATION INTERNATIONALE DE NORMALISATION
Laboratory crucibles in porcelain and silica
Creusets de labora toire en porcelaine et en silice
First edition - 1975-09-01
Ref. No. ISO 1772-1975 (E)
UDC 542.232.5.004.1
Descriptors : Jabot-atm-y glassware, crucibles, porcelain, Silicon dioxide, specifications, designation.
Price based on 4 pages
FOREWORD
ISO (the International Organization for Standardization) is a worldwide federation
of national Standards institutes (ISO Member Bodies). The work of developing
International Standards is carried out through ISO Technical Committees. Every
Member Body interested in a subject for which a Technical Committee has been set
up has the right to be represented on that Committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the Technical Committees are circulated
to the Member Bodies for approval before their acceptance as International
Standards by the ISO Council.
Prior to 1972, the results of the work of the Technical Committees were published
as ISO Recommendations; these documents are now in the process of being
transformed into International Standards. As part of this process, Technical
Committee ISO/TC 48 has reviewed ISO Recommendation R 1772 and found it
technically suitable for transformation. International Standard ISO 1772 therefore
replaces ISO Recommendation R 1772-1970 to which it is technically identical.
ISO Recommendation R 1772 was approved by the Member Bodies of the
following countries :
Austria India South Africa, Rep. of
Belgium Iran
Spain
Canada I reland Thailand
Turkey
Colombia I taly
Czechoslovakia Korea, Dem. P. Rep. of United Kingdom
Egypt, Arab Rep. of Netherlands U.S.A.
France New Zealand
U.S.S.R.
Germany Peru Yugoslavia
Greece Poland
No Member Body expressed disapproval of the Recommendation.
No Member Body disapproved the transformation of ISO/R 1772 into an
International Standard.
0 International Organkation for Standardkation, 1975 l
Printed in Switzerland
INTERNATIONAL STANDARD ISO 17724975 (E)
Laboratory crucibles in porcelain and silica
1 SCOPE AND FIELD OF APPLICATION 5 SERIES OF SIZES
This International Standard specifies requirements for an The series of sizes of crucibles shall be as shown in the
internationally acceptable series of porcelain and silica table.
crucibles and lids for general laboratory requirements.
NOTE - No values of nominal capacity are specified, but it is
recommended that manufacturers should state these for the
NOTES
information of users, on the basis that :
1 It is recognized that some sizes of crucible iarger than those
nominal capacity = approximately 75 % of Overflow capacity.
listed may be needed for use in laboratories for special purposes. It
is recommended that such larger sizes should be designed within the
general framework of this International Standard, i.e. by selecting a
suitable multiple of 10 mm as the nominal external top diameter,
6 MATERIAL
and applying one of the three Standard ratios in Order to obtain the
nominal height.
6.1 Porcelain crucibles and lids shall be made from
vitrified porcelain with a glazed surface, but the bases and
2 This International Standard does not deal with laboratory
rims of the crucibles need not necessarily be glazed. The
crucibles made of materials other than porcelain and silica (for
other ceramic materials, metals, plastics
example, glass and
porcelain used shall satisfy the requirements of ISO 1775.
material& Nevertheless, it is expected that the types, sizes and
dimensions specified herein may provide useful guidance for those
NOTE - The sizes and dimensions included in this International
concerned with the manufacture or standardization of crucibles
Standard may also conveniently be applied to crucibles of unglazed
made of such other materials, and that it may become possible to
porcelain.
include them in this International Standard at some future date.
6.2 Silica crucibles and lids shall be made from vitreous
silica, either translucent or transparent.
2 REFERENCE
ISO 1775, Porcelain labora tot-y appara tus - Requiremen ts
7 DETAILS OF CONSTRUCTION
and methods of test.
7.1 General design
3 TYPES OF CRUCIBLE
The general design of the crucibles is illustrated in figure 1;
that
...

NORME INTERNATIONALE
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION l MEXAYHAPOAHAR OPI-AHM3ALUi5I l-l0 CTAH~APT;13ALJMM *ORGANISATION INTERNATIONALE DE NORMALISATION
Creusets de laboratoire en porcelaine et en silice
Laboratory crucibles in porcelain and silica
Première édition - 1975-09-01
Réf. no : ISO 1772-1975 (F)
CDU 542.232.5.004.1
Descripteurs : verrerie de laboratoire, creuset, porcelaine, silice, spécification, désignation.
Prix basé sur 4 pages
AVANT-PROPOS
L’ISO (Organisation Internationale de Normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (Comités Membres 60). L’élaboration de
Normes Internationales est confiée aux Comités Techniques ISO. Chaque Comité
Membre intéressé par une étude a le droit de faire partie du Comité Technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO, participent également aux travaux.
Les Projets de Normes Internationales adoptés par les Comités Techniques sont
soumis aux Comités Membres pour approbation, avant leur acceptation comme
Normes Internationales par le Conseil de I’ISO.
Avant 1972, les résultats des travaux des Comités Techniques étaient publiés
comme Recommandations ISO; maintenant, ces documents sont en cours de
transformation en Normes Internationales. Compte tenu de cette procédure, le
Comité Technique ISO/TC 48 a examiné la Recommandation ISO/R 1772 et est
du point de vue technique, être transformée en Norme
d’avis qu’elle peut,
Internationale
Internationale. La présente Norme remplace donc la
Recommandation ISO/R 1772-1970 à laquelle elle est techniquement identique.
La Recommandation lSO/R 1772 avait été approuvée par les Comités Membres des
pays suivants :
Afrique du Sud, Rép. d’ France
Pologne
Grèce
Allemagne Royaume-Uni
Autriche Inde Tchécoslovaquie
Belgique Iran Thaïlande
Canada Irlande Turquie
Colombie Italie U.R.S.S.
Corée, Rép. Dém. P. de Nouvelle-Zélande U.S.A.
Égypte, Rép. arabe d’ Pays-Bas Yougoslavie
Espagne Pérou
Aucun Comité Membre n’avait désapprouvé la Recommandation.
Aucun Comité Membre n’a désapprouvé la transformation de la Recommandation
lSO/R 1772 en Norme Internationale.
0 Organisation Internationale de Normalisation, 1975 l
Imprimé en Suisse
ISO 17724975 (F)
NORME INTERNATIONALE
Creusets de laboratoire en porcelaine et en silice
1 OBJET ET DOMAINE D’APPLICATION 5 SÉRIES DE TAILLES
La présente Norme Internationale fixe des spécifications Les séries de tailles des creusets doivent être conformes aux
pour une série internationalement acceptable de creusets et indications du tableau.
de couvercles en silice et en porcelaine pour les utilisations
NOTE - Aucune valeur n’a été spécifiée pour la capacité nominale,
générales de laboratoire.
mais il est recommandé que les fabricants donnent cette indication
aux utilisateurs pour leur information, en prenant la base suivante :
NOTES
capacité nominale = environ 75 % de la capacité de débordement.
1 II est reconnu que certaines tailles de creusets plus grandes que
celles mentionnées dans ce document sont nécessaires dans les
laboratoires pour des usages particuliers. II est recommandé que ces
creusets soient concus dans le cadre général de cette Norme
6 MATÉRIAU
Internationale, c’est-à-dire en choisissant un diamètre extérieur
nominal mesuré à la partie supérieure du creuset, multiple de
6.1 Les creusets et les couvercles en porcelaine doivent
10 mm, et en lui appliquant l’un des trois rapports prévus pour
être fabriqués à partir d’une porcelaine vitrifiée dont la
obtenir la hauteur nominale désirée.
surface soit vernie, mais il n’est pas nécessaire que la base et
2 La présente Norme Internationale ne concerne pas les creusets de
les bords des creusets soient vernis. La porcelaine utilisée
laboratoire fabriqués en matériaux autres que la silice et la
doit être conforme aux spécifications de l’lSO/R 1775.
porcelaine (par exemple : verre et autres matériaux en céramique,
métaux, matières plastiques). Néanmoins, il est souhaité que les
NOTE - Les tailles et les dimensions spécifiées dans la présente
types, tailles et dimensions mentionnés dans la présente Norme
Norme Internationale peuvent également être appliquées pour les
Internationale puissent fournir un guide utile aux personnes
creusets en porcelaine non vernie.
intéressées à la fabrication ou à la normalisation des creusets
fabriqués dans de tels matériaux, de manière que ces creusets
6.2 Les creusets et les couvercles en silice doivent être
puissent être inclus dans cette Norme Internationale à une date
fabriqués en silice vitreuse, soit translucide soit
ultérieure.
transparente.
2 RÉFÉRENCE
7 DÉTAILS DE CONSTRUCTION
ISO 1775, Appareils de laboratoire en porcelaine -
Spécifica Cons et méthodes d’essai. 7.1 Forme générale
La forme générale des creusets est illustrée par la figure 1;
celle des couvercles est présen
...

NORME INTERNATIONALE
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION l MEXAYHAPOAHAR OPI-AHM3ALUi5I l-l0 CTAH~APT;13ALJMM *ORGANISATION INTERNATIONALE DE NORMALISATION
Creusets de laboratoire en porcelaine et en silice
Laboratory crucibles in porcelain and silica
Première édition - 1975-09-01
Réf. no : ISO 1772-1975 (F)
CDU 542.232.5.004.1
Descripteurs : verrerie de laboratoire, creuset, porcelaine, silice, spécification, désignation.
Prix basé sur 4 pages
AVANT-PROPOS
L’ISO (Organisation Internationale de Normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (Comités Membres 60). L’élaboration de
Normes Internationales est confiée aux Comités Techniques ISO. Chaque Comité
Membre intéressé par une étude a le droit de faire partie du Comité Technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO, participent également aux travaux.
Les Projets de Normes Internationales adoptés par les Comités Techniques sont
soumis aux Comités Membres pour approbation, avant leur acceptation comme
Normes Internationales par le Conseil de I’ISO.
Avant 1972, les résultats des travaux des Comités Techniques étaient publiés
comme Recommandations ISO; maintenant, ces documents sont en cours de
transformation en Normes Internationales. Compte tenu de cette procédure, le
Comité Technique ISO/TC 48 a examiné la Recommandation ISO/R 1772 et est
du point de vue technique, être transformée en Norme
d’avis qu’elle peut,
Internationale
Internationale. La présente Norme remplace donc la
Recommandation ISO/R 1772-1970 à laquelle elle est techniquement identique.
La Recommandation lSO/R 1772 avait été approuvée par les Comités Membres des
pays suivants :
Afrique du Sud, Rép. d’ France
Pologne
Grèce
Allemagne Royaume-Uni
Autriche Inde Tchécoslovaquie
Belgique Iran Thaïlande
Canada Irlande Turquie
Colombie Italie U.R.S.S.
Corée, Rép. Dém. P. de Nouvelle-Zélande U.S.A.
Égypte, Rép. arabe d’ Pays-Bas Yougoslavie
Espagne Pérou
Aucun Comité Membre n’avait désapprouvé la Recommandation.
Aucun Comité Membre n’a désapprouvé la transformation de la Recommandation
lSO/R 1772 en Norme Internationale.
0 Organisation Internationale de Normalisation, 1975 l
Imprimé en Suisse
ISO 17724975 (F)
NORME INTERNATIONALE
Creusets de laboratoire en porcelaine et en silice
1 OBJET ET DOMAINE D’APPLICATION 5 SÉRIES DE TAILLES
La présente Norme Internationale fixe des spécifications Les séries de tailles des creusets doivent être conformes aux
pour une série internationalement acceptable de creusets et indications du tableau.
de couvercles en silice et en porcelaine pour les utilisations
NOTE - Aucune valeur n’a été spécifiée pour la capacité nominale,
générales de laboratoire.
mais il est recommandé que les fabricants donnent cette indication
aux utilisateurs pour leur information, en prenant la base suivante :
NOTES
capacité nominale = environ 75 % de la capacité de débordement.
1 II est reconnu que certaines tailles de creusets plus grandes que
celles mentionnées dans ce document sont nécessaires dans les
laboratoires pour des usages particuliers. II est recommandé que ces
creusets soient concus dans le cadre général de cette Norme
6 MATÉRIAU
Internationale, c’est-à-dire en choisissant un diamètre extérieur
nominal mesuré à la partie supérieure du creuset, multiple de
6.1 Les creusets et les couvercles en porcelaine doivent
10 mm, et en lui appliquant l’un des trois rapports prévus pour
être fabriqués à partir d’une porcelaine vitrifiée dont la
obtenir la hauteur nominale désirée.
surface soit vernie, mais il n’est pas nécessaire que la base et
2 La présente Norme Internationale ne concerne pas les creusets de
les bords des creusets soient vernis. La porcelaine utilisée
laboratoire fabriqués en matériaux autres que la silice et la
doit être conforme aux spécifications de l’lSO/R 1775.
porcelaine (par exemple : verre et autres matériaux en céramique,
métaux, matières plastiques). Néanmoins, il est souhaité que les
NOTE - Les tailles et les dimensions spécifiées dans la présente
types, tailles et dimensions mentionnés dans la présente Norme
Norme Internationale peuvent également être appliquées pour les
Internationale puissent fournir un guide utile aux personnes
creusets en porcelaine non vernie.
intéressées à la fabrication ou à la normalisation des creusets
fabriqués dans de tels matériaux, de manière que ces creusets
6.2 Les creusets et les couvercles en silice doivent être
puissent être inclus dans cette Norme Internationale à une date
fabriqués en silice vitreuse, soit translucide soit
ultérieure.
transparente.
2 RÉFÉRENCE
7 DÉTAILS DE CONSTRUCTION
ISO 1775, Appareils de laboratoire en porcelaine -
Spécifica Cons et méthodes d’essai. 7.1 Forme générale
La forme générale des creusets est illustrée par la figure 1;
celle des couvercles est présen
...