This document specifies a method for determining the cross tensional strength of the bonded plates of carbon fibre reinforced plastics (CFRPs) to metal assemblies, with a standard specimen loaded in cross tension and under specified conditions of preparation, conditioning and testing. This method is intended for testing those bonded plates used in bonding carbon fibre reinforced plastics (CFRPs) to metal assemblies.
- Standard11 pagesEnglish languagesale 15% off
This document specifies a method for determining the lap-shear strength of the adhesive joint between carbon fibre-reinforced plastics (CFRPs) and metal adherends, using a standard specimen loaded in tension and under specified conditions of preparation, conditioning and testing. This method is intended for assessing the suitability of adhesives to be used for bonding a carbon fibre reinforced plastic (CFRPs) to a metal.
- Standard7 pagesEnglish languagesale 15% off
- Standard7 pagesEnglish languagesale 15% off
This document specifies the test method for the determination of adhesive fracture energy of adhesively bonded plates of carbon fibre reinforced plastic (CFRP) and metal using a double cantilever beam (DCB) specimen. The test method is also applicable to bonded joints between metals and other composite materials, such as glass fibre reinforced plastics.
- Standard22 pagesEnglish languagesale 15% off
- Standard22 pagesEnglish languagesale 15% off
This document specifies the apparatus, the reagents and the procedure to be used in conducting the neutral salt spray (NSS), acetic acid salt spray (AASS) and copper-accelerated acetic acid salt spray (CASS) tests for assessment of the galvanic corrosion resistance of joints and bonded structures between carbon fibre reinforced plastics (CFRPs) and metallic materials, with or without permanent or temporary insulation for the galvanic current.
- Standard19 pagesEnglish languagesale 15% off
- Standard19 pagesEnglish languagesale 15% off
This International Standard specifies test specimens and procedures for fatigue testing at ambient conditions, under repeated tensile loading, generating cross-tension loading to the bonded plates of carbon fibre reinforced plastics (CFRPs) to metal assemblies. The specimen undergoes cyclically stress, comprising an alternating stress on a static stress which represents the mean stress. This allows for estimating the safety condition regarding the fatigue resistance of joints. The method is intended for testing bonded plates used in bonding CFRPs to metal assemblies.
- Draft14 pagesEnglish languagesale 15% off
- Draft14 pagesEnglish languagesale 15% off
Frequently Asked Questions
ISO/TC 61/SC 13/WG 7 is a Subcommittee within the International Organization for Standardization (ISO). It is named "Composites and metal assemblies". This committee has published 5 standards.
ISO/TC 61/SC 13/WG 7 develops ISO standards in the area of Information technology. Currently, there are 5 published standards from this subcommittee.
The International Organization for Standardization (ISO) is an independent, non-governmental international organization that develops and publishes international standards. Founded in 1947 and headquartered in Geneva, Switzerland, ISO brings together experts from 170+ member countries to share knowledge and develop voluntary, consensus-based standards that support innovation and provide solutions to global challenges.
A Subcommittee (SC) in ISO operates under a Technical Committee and focuses on a specific subset of the TC's scope. Subcommittees develop standards and technical specifications in their specialized area, reporting to their parent Technical Committee. They may also have working groups for detailed technical work.