ASTM C188-16
(Test Method)Standard Test Method for Density of Hydraulic Cement
Standard Test Method for Density of Hydraulic Cement
ABSTRACT
This test method covers the determination of the density of hydraulic cement. Its particular usefulness is in connection with the design and control of concrete mixtures. The density of hydraulic cement is defined as the mass of a unit volume of the solids. The apparatus to be used is a Le Chatelier flask which is circular in cross-section. This flask shall be thoroughly annealed before being graduated. They shall be of sufficient thickness to ensure reasonable resistance to breakage. Each flask shall bear a permanent identification number and the stopper, if not interchangeably ground, shall bear the same number. Interchangeable ground-glass parts shall be marked on both members with the standard-taper symbol, followed by the size designation. The standard temperature shall be indicated, and the unit of capacity shall be shown by the letters “mL” placed above the highest graduation mark. Kerosene, free of water, or naphtha shall be used in the density determination. The flask shall be filled with either of the liquids mentioned to a point on the stem between the 0 and the 1-mL mark. The inside of the flask shall be dried above the level of the liquid, if necessary, after pouring. The first reading shall be recorded after the flask has been immersed in the water bath. A quantity of cement shall be introduced in small increments at the same temperature as the liquid. A vibrating apparatus may be used to accelerate the introduction of the cement into the flask and to prevent the cement from sticking to the neck. After all the cement has been introduced, the stopper shall be placed in the flask and the flask shall be rolled in an inclined position, or gently whirl it in a horizontal circle, so as to free the cement from air until no further air bubbles rise to the surface of the liquid. If a proper amount of cement has been added, the level of the liquid will be in its final position at some point of the upper series of graduations. The final reading shall be recorded after the flask has been immersed in the water bath. The difference between the first and the final readings represents the volume of liquid displaced by the mass of cement used in the test. The cement density can now be determined.
SIGNIFICANCE AND USE
4.1 This test method provides a procedure for the determination of density of hydraulic cement samples using non-instrumental techniques.
SCOPE
1.1 This test method covers the determination of the density of hydraulic cement. Its particular usefulness is in connection with the design and control of concrete mixtures.
1.2 The density of hydraulic cement is defined as the mass of a unit volume of the solids.
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4 Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: C188 − 16 American Association State
Highway and Transportation Officials Standard
AASHTO No.: T133
Standard Test Method for
1
Density of Hydraulic Cement
This standard is issued under the fixed designation C188; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope* Coke by Helium Pycnometer
1.1 This test method covers the determination of the density
3. Terminology
of hydraulic cement. Its particular usefulness is in connection
with the design and control of concrete mixtures.
3.1 Definitions—For definitions of terms used in this test
1.2 The density of hydraulic cement is defined as the mass method, refer to Terminology C125.
of a unit volume of the solids.
4. Significance and Use
1.3 The values stated in SI units are to be regarded as
standard. No other units of measurement are included in this
4.1 This test method provides a procedure for the determi-
standard.
nation of density of hydraulic cement samples using non-
1.4 Warning—Fresh hydraulic cementitious mixtures are instrumental techniques.
caustic and may cause chemical burns to skin and tissue upon
2
prolonged exposure.
5. Apparatus
1.5 This standard does not purport to address all of the
5.1 Le Chatelier flask—The standard flask, which is circular
safety concerns, if any, associated with its use. It is the
in cross section, with shape and dimensions conforming
responsibility of the user of this standard to establish appro-
essentially to Fig. 1 (Note). The requirements in regard to
priate safety and health practices and determine the applica-
tolerance, inscription and length, spacing, and uniformity of
bility of regulatory limitations prior to use.
graduation will be rigidly observed. There shall be a space of
at least 10 mm between the highest graduation mark and the
2. Referenced Documents
lowest point of grinding for the glass stopper.
3
2.1 ASTM Standards:
5.1.1 The material of construction shall be excellent quality
C114 Test Methods for Chemical Analysis of Hydraulic
glass, transparent and free of striae. The glass shall be
Cement
chemically resistant and shall have small thermal hysteresis.
C125 Terminology Relating to Concrete and Concrete Ag-
The flasks shall be thoroughly annealed before being gradu-
gregates
ated. They shall be of sufficient thickness to ensure reasonable
C604 Test Method for True Specific Gravity of Refractory
resistance to breakage.
Materials by Gas-Comparison Pycnometer
5.1.2 The neck shall be graduated from 0 to 1 mL and from
C670 Practice for Preparing Precision and Bias Statements
18 to 24 mL in 0.1-mL graduations. The error of any indicated
for Test Methods for Construction Materials
capacity shall not be greater than 0.05 mL.
D2638 Test Method for Real Density of Calcined Petroleum
5.1.3 Each flask shall bear a permanent identification num-
ber and the stopper, if not interchangeably ground, shall bear
1
This test method is under the jurisdiction ofASTM Committee C01 on Cement
the same number. Interchangeable ground-glass parts shall be
and is the direct responsibility of Subcommittee C01.25 on Fineness.
marked on both members with the standard-taper symbol,
Current edition approved Dec. 15, 2016. Published December 2016. Originally
followed by the size designation. The standard temperature
approved in 1944. Last previous edition approved in 2015 as C188 – 15. DOI:
10.1520/C0188-16.
shall be indicated, and the unit of capacity shall be shown by
2
Section on Safety, Manual of Cement Testing, Annual Book of ASTM
the letters “mL” placed above the highest graduation mark.
Standards, Vol. 04.01.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
5.2 Kerosine, free of water, or naphtha, having a density
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
greater than 0.73 g/mLat 23 6 2°C shall be used in the density
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. determination.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
C188 − 16
readingofliquidheightaftertheflaskhasbeenimmersedinthe
water bath (Note 3) in accordance with 6.4.
NOTE 2—It is advisable to use a rubber pad on the table top when filling
or rolling the flask.
NOTE 3—Before the cement has been added to the flask, a loose-fitting,
lead-ring weight around the stem of the fla
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: C188 − 15 C188 − 16 American Association State
Highway and Transportation Officials Standard
AASHTO No.: T133
Standard Test Method for
1
Density of Hydraulic Cement
This standard is issued under the fixed designation C188; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope*
1.1 This test method covers the determination of the density of hydraulic cement. Its particular usefulness is in connection with
the design and control of concrete mixtures.
1.2 The density of hydraulic cement is defined as the mass of a unit volume of the solids.
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4 Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon
2
prolonged exposure.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
3
2.1 ASTM Standards:
C114 Test Methods for Chemical Analysis of Hydraulic Cement
C125 Terminology Relating to Concrete and Concrete Aggregates
C604 Test Method for True Specific Gravity of Refractory Materials by Gas-Comparison Pycnometer
C670 Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials
D2638 Test Method for Real Density of Calcined Petroleum Coke by Helium Pycnometer
3. Terminology
3.1 Definitions—For definitions of terms used in this test method, refer to Terminology C125.
4. Significance and Use
4.1 This test method provides a procedure for the determination of density of hydraulic cement samples using non-instrumental
techniques.
5. Apparatus
5.1 Le Chatelier flask—The standard flask, which is circular in cross section, with shape and dimensions conforming essentially
to Fig. 1 (Note). The requirements in regard to tolerance, inscription and length, spacing, and uniformity of graduation will be
rigidly observed. There shall be a space of at least 10 mm between the highest graduation mark and the lowest point of grinding
for the glass stopper.
5.1.1 The material of construction shall be excellent quality glass, transparent and free of striae. The glass shall be chemically
resistant and shall have small thermal hysteresis. The flasks shall be thoroughly annealed before being graduated. They shall be
of sufficient thickness to ensure reasonable resistance to breakage.
1
This test method is under the jurisdiction of ASTM Committee C01 on Cement and is the direct responsibility of Subcommittee C01.25 on Fineness.
Current edition approved Oct. 1, 2015Dec. 15, 2016. Published October 2015December 2016. Originally approved in 1944. Last previous edition approved in 20142015
as C188 – 14. – 15. DOI: 10.1520/C0188-15.10.1520/C0188-16.
2
Section on Safety, Manual of Cement Testing, Annual Book of ASTM Standards, Vol. 04.01.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
C188 − 16
Note—Variations of a few millimetres in such dimensions as total height of flask, diameter of base, and so forth, are to be expected and will not be considered sufficient
cause for rejection. The dimensions of the flask shown in Fig. 1 apply only to new flasks and not to flasks in use which meet the other requirements of this test method.
FIG. 1 Le Chatelier Flask for Density Test
5.1.2 The neck shall be graduated from 0 to 1 mL and from 18 to 24 mL in 0.1-mL graduations. The error of any indicated
capacity shall not be greater than 0.05 mL.
5.1.3 Each flask shall bear a permanent identification number and the stopper, if not interchangeably ground, shall bear the same
number. Interchang
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.