Standard Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, General Requirements for

ABSTRACT
This specification covers the general requirements for carbon, structural, and high-strength, low alloy steel sheets in coils and cut lengths. The steel sheets shall be manufactured by hot-rolling, cold-rolling or temper rolling. Cold-rolled sheets shall undergo annealing after being cold reduced to thickness. Products shall undergo cast or heat analysis, product, check, or verification analysis, and sampling. Product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, manganese, phosphorus, sulfur, silicon, copper, nickel, chromium, molybdenum, vanadium, columbium, niobium, titanium, aluminum, and nitrogen. Mechanical properties of the materials shall conform to the following properties: tensile strength, yield strength, and bending strength. Thickness, length, width and flatness tolerances and allowances for cold-rolled and hot-rolled sheets are indicated. Steel may be produced as ingot-cast or strand-cast.
SCOPE
1.1 This specification covers the general requirements for steel sheet in coils and cut lengths. It applies to the following specifications that describe carbon steel, structural steel, and high-strength, low-alloy steel (HSLA) furnished as hot-rolled sheet and cold-rolled sheet: Specifications A414/A414M, A424, A606, A659/A659M, A794, A1008/A1008M, A1011/A1011M, and A1039/A1039M.  
1.2 This specification is not applicable to hot-rolled heavy-thickness carbon sheet coils (Specification A635/A635M).  
1.3 In case of any conflict in requirements, the requirements of the individual material specification shall prevail over those of this general specification.  
1.4 For the purposes of determining conformance with this and the appropriate product specification referenced in 1.1, values shall be rounded to the nearest unit in the right hand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E29.  
1.5 Annex A1 lists permissible variations in dimensions and mass (see Note 1) in SI [metric] units. The values listed are not exact conversions of the values listed in the inch-pound tables, but instead are rounded or rationalized values. Conformance to Annex A1 is mandatory when the “M” specification is used. Note 1—The term weight is used when inch-pound units are the standard. However, under SI the preferred term is  mass.  
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.7 This specification and the applicable material specifications are expressed in both inch-pound units and SI units. However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound units.

General Information

Status
Historical
Publication Date
30-Apr-2013
Current Stage
Ref Project

Relations

Buy Standard

Technical specification
ASTM A568/A568M-13 - Standard Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, General Requirements for
English language
30 pages
sale 15% off
Preview
sale 15% off
Preview
Technical specification
REDLINE ASTM A568/A568M-13 - Standard Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, General Requirements for
English language
30 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A568/A568M −13
StandardSpecification for
Steel, Sheet, Carbon, Structural, and High-Strength, Low-
Alloy, Hot-Rolled and Cold-Rolled, General Requirements
1
for
This standard is issued under the fixed designationA568/A568M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* 1.7 This specification and the applicable material specifica-
tions are expressed in both inch-pound units and SI units.
1.1 This specification covers the general requirements for
However, unless the order specifies the applicable “M” speci-
steel sheet in coils and cut lengths. It applies to the following
fication designation (SI units), the material shall be furnished
specifications that describe carbon steel, structural steel, and
to inch-pound units.
high-strength, low-alloy steel (HSLA) furnished as hot-rolled
sheet and cold-rolled sheet: Specifications A414/A414M,
2. Referenced Documents
A424, A606, A659/A659M, A794, A1008/A1008M, A1011/
2
2.1 ASTM Standards:
A1011M, and A1039/A1039M.
A370Test Methods and Definitions for Mechanical Testing
1.2 This specification is not applicable to hot-rolled heavy-
of Steel Products
thickness carbon sheet coils (Specification A635/A635M).
A414/A414MSpecification for Steel, Sheet, Carbon, and
High-Strength, Low-Alloy for Pressure Vessels
1.3 Incaseofanyconflictinrequirements,therequirements
A424SpecificationforSteel,Sheet,forPorcelainEnameling
of the individual material specification shall prevail over those
A606 Specification for Steel, Sheet and Strip, High-
of this general specification.
Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, with
1.4 For the purposes of determining conformance with this
Improved Atmospheric Corrosion Resistance
and the appropriate product specification referenced in 1.1,
A635/A635M Specification for Steel, Sheet and Strip,
values shall be rounded to the nearest unit in the right hand
Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon,
place of figures used in expressing the limiting values in
Structural, High-Strength Low-Alloy, and High-Strength
accordance with the rounding method of Practice E29.
Low-Alloy with Improved Formability, General Require-
1.5 AnnexA1listspermissiblevariationsindimensionsand
ments for
mass(seeNote1)inSI[metric]units.Thevalueslistedarenot
A659/A659MSpecification for Commercial Steel (CS),
exact conversions of the values listed in the inch-pound tables,
Sheet and Strip, Carbon (0.16 Maximum to 0.25 Maxi-
butinsteadareroundedorrationalizedvalues.Conformanceto
mum Percent), Hot-Rolled
Annex A1 is mandatory when the “M” specification is used.
A700Practices for Packaging, Marking, and Loading Meth-
ods for Steel Products for Shipment
NOTE 1—The term weight is used when inch-pound units are the
A751Test Methods, Practices, and Terminology for Chemi-
standard. However, under SI the preferred term is mass.
cal Analysis of Steel Products
1.6 The values stated in either SI units or inch-pound units
A794Specification for Commercial Steel (CS), Sheet, Car-
are to be regarded separately as standard. The values stated in
bon (0.16 % Maximum to 0.25 % Maximum), Cold-
each system may not be exact equivalents; therefore, each
Rolled
system shall be used independently of the other. Combining
A941TerminologyRelatingtoSteel,StainlessSteel,Related
values from the two systems may result in non-conformance
Alloys, and Ferroalloys
with the standard.
A1008/A1008MSpecification for Steel, Sheet, Cold-Rolled,
Carbon, Structural, High-Strength Low-Alloy, High-
Strength Low-Alloy with Improved Formability, Solution
1
This specification is under the jurisdiction ofASTM Committee A01 on Steel,
Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee
2
A01.19 on Steel Sheet and Strip. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved May 1, 2013. Published May 2013. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1966. Last previous edition approved in 2011 as A568/A568M–11b. Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/A0568_A0568M-13. the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
A568/A568M−13
Hardened, and Bake Hardenable
Coils and Cut Lengths
Width, in. Thickness, in.
A1011/A1011MSpecification for Steel, Sheet an
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: A568/A568M − 11b A568/A568M − 13
Standard Specification for
Steel, Sheet, Carbon, Structural, and High-Strength, Low-
Alloy, Hot-Rolled and Cold-Rolled, General Requirements
1
for
This standard is issued under the fixed designation A568/A568M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers the general requirements for steel sheet in coils and cut lengths. It applies to the following
specifications that describe carbon steel, structural steel, and high-strength, low-alloy steel (HSLA) furnished as hot-rolled sheet
and cold-rolled sheet: Specifications A414/A414M, A424, A606, A659/A659M, A794, A1008/A1008M, A1011/A1011M, and
A1039/A1039M.
1.2 This specification is not applicable to hot-rolled heavy-thickness carbon sheet coils (Specification A635/A635M).
1.3 In case of any conflict in requirements, the requirements of the individual material specification shall prevail over those of
this general specification.
1.4 For the purposes of determining conformance with this and the appropriate product specification referenced in 1.1, values
shall be rounded to the nearest unit in the right hand place of figures used in expressing the limiting values in accordance with
the rounding method of Practice E29.
1.5 Annex A1 lists permissible variations in dimensions and mass (see Note 1) in SI [metric] units. The values listed are not
exact conversions of the values listed in the inch-pound tables, but instead are rounded or rationalized values. Conformance to
Annex A1 is mandatory when the “M” specification is used.
NOTE 1—The term weight is used when inch-pound units are the standard. However, under SI the preferred term is mass.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.7 This specification and the applicable material specifications are expressed in both inch-pound units and SI units. However,
unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound
units.
2. Referenced Documents
2
2.1 ASTM Standards:
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A414/A414M Specification for Steel, Sheet, Carbon, and High-Strength, Low-Alloy for Pressure Vessels
A424 Specification for Steel, Sheet, for Porcelain Enameling
A606 Specification for Steel, Sheet and Strip, High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, with Improved
Atmospheric Corrosion Resistance
A635/A635M Specification for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural,
High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, General Requirements for
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.19
on Steel Sheet and Strip.
Current edition approved Oct. 1, 2011May 1, 2013. Published October 2011May 2013. Originally approved in 1966. Last previous edition approved in 2011 as
A568/A568M – 11a.A568/A568M – 11b. DOI: 10.1520/A0568_A0568M-11b.10.1520/A0568_A0568M-13.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
A568/A568M − 13
A659/A659M Specification for Commercial Steel (CS), Sheet and Strip, Carbon (0.16 Maximum to 0.25 Maximum Percent),
Hot-Rolled
A700 Practices for Packaging, Marking, and Loading Methods for Steel Products for Shipment
A751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
A794 Specification for Commercial Steel (CS), Sheet, Carbon (0.16
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.