ASTM A635/A635M-13
(Specification)Standard Specification for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural, High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, General Requirements for
Standard Specification for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural, High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, General Requirements for
ABSTRACT
This specification covers the general requirements for hot-rolled, heavy-thickness, and high-strength low-alloy with improved formability sheet and strip coils. These coils are normally produced from rimmed, capped, or semi-killed steel. Steels may be produced as ingot-cast or strand-cast. Cast or heat analysis shall be made to determine the conformance with the requirements. For steels other than non-killed (capped or rimmed), product analysis may be made. The chemical analysis shall conform to the specified amounts of carbon, manganese, phosphorus, sulfur, silicon, and copper. Steels may or may not be subjected to tension test requirement. Specimen preparation and test methods are discussed. The mechanical property requirements, number of specimens, test locations, and specimen orientation shall be in accordance with the applicable product specification. Tolerances for the dimensions of sheet and strip coils are specified.
SCOPE
1.1 This specification covers the general requirements for hot-rolled, heavy-thickness sheet and strip in coils.
1.2 It applies to Specifications A414/A414M, A424/A424M, and A1018/A1018M.
1.3 This material is available only in coils described as follows:
Size Limits, Coils Only
Product
Width, in. [mm]
Thickness, in. [mm]
Strip
over 8 to 12, incl
[over 200 through 300]
0.230 to 1.000, incl
[from 6.0 through 25]
Sheet
All WidthsA
All Widths
0.230 to 1.000, incl
[from 6.0 through 25] A Hot-rolled heavy thickness sheet in coils less than 12 in. [300 mm] and less in width must have slit edges. Hot-rolled heavy thickness coils 12 in. [300 mm] and wider with mill edge is considered hot-rolled heavy thickness strip.Note 1—The changes in width limits with the publication of A635/A635M – 06a result in a change in tensile testing direction for material from 0.180 in. [4.5 mm] to 0.230 in. exclusive [6.0 mm exclusive] over 48 in. [1200 mm] wide as that material is now covered by Specification A568/A568M – 06a. The purchaser is advised to discuss this change with the supplier.
1.4 In case of any conflict in requirements, the requirements of the individual material specification shall prevail over those of this general specification.
1.5 Annex A1 lists permissible variations in dimensions and mass (see Note 2) in SI [metric] units. The values listed are not exact conversions of the values listed in the inch-pound tables, but instead are rounded or rationalized values. Conformance to Annex A1 is mandatory when the “M” specification is used. Note 2—The term weight is used when inch-pound units are the standard. However, under SI, the preferred term is mass.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.7 This specification and the applicable material specifications are expressed in both inch-pound units and SI units. However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound units.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A635/A635M −13
StandardSpecification for
Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled,
Alloy, Carbon, Structural, High-Strength Low-Alloy, and
High-Strength Low-Alloy with Improved Formability, General
1
Requirements for
This standard is issued under the fixed designationA635/A635M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
NOTE 2—The term weight is used when inch-pound units are the
1. Scope*
standard. However, under SI, the preferred term is mass.
1.1 This specification covers the general requirements for
1.6 The values stated in either SI units or inch-pound units
hot-rolled, heavy-thickness sheet and strip in coils.
are to be regarded separately as standard. The values stated in
1.2 It applies to Specifications A414/A414M, A424/
each system may not be exact equivalents; therefore, each
A424M, and A1018/A1018M.
system shall be used independently of the other. Combining
1.3 This material is available only in coils described as values from the two systems may result in non-conformance
with the standard.
follows:
Size Limits, Coils Only
1.7 This specification and the applicable material specifica-
Product Width, in. [mm] Thickness, in. [mm]
tions are expressed in both inch-pound units and SI units.
However, unless the order specifies the applicable “M” speci-
Strip over 8 to 12, incl 0.230 to 1.000, incl
[over 200 through 300] [from 6.0 through 25]
fication designation (SI units), the material shall be furnished
A
Sheet All Widths 0.230 to 1.000, incl
to inch-pound units.
All Widths
[from 6.0 through 25]
A 2. Referenced Documents
Hot-rolled heavy thickness sheet in coils less than 12 in. [300 mm] and less in
width must have slit edges. Hot-rolled heavy thickness coils 12 in. [300 mm] and 2
2.1 ASTM Standards:
wider with mill edge is considered hot-rolled heavy thickness strip.
A370 Test Methods and Definitions for Mechanical Testing
NOTE 1—The changes in width limits with the publication of A635/
of Steel Products
A635M – 06a result in a change in tensile testing direction for material
A414/A414M Specification for Steel, Sheet, Carbon, and
from 0.180 in. [4.5 mm] to 0.230 in. exclusive [6.0 mm exclusive] over 48
High-Strength, Low-Alloy for Pressure Vessels
in. [1200 mm] wide as that material is now covered by Specification
A568/A568M – 06a. The purchaser is advised to discuss this change with A424/A424M Specification for Steel, Sheet, for Porcelain
Enameling
the supplier.
A700 Practices for Packaging, Marking, and Loading Meth-
1.4 In case of any conflict in requirements, the requirements
ods for Steel Products for Shipment
of the individual material specification shall prevail over those
A568/A568M Specification for Steel, Sheet, Carbon,
of this general specification.
Structural,andHigh-Strength,Low-Alloy,Hot-Rolledand
Cold-Rolled, General Requirements for
1.5 AnnexA1 lists permissible variations in dimensions and
A751 Test Methods, Practices, and Terminology for Chemi-
mass (see Note 2) in SI [metric] units.The values listed are not
cal Analysis of Steel Products
exact conversions of the values listed in the inch-pound tables,
A941 TerminologyRelatingtoSteel,StainlessSteel,Related
but instead are rounded or rationalized values. Conformance to
Alloys, and Ferroalloys
Annex A1 is mandatory when the “M” specification is used.
A1018/A1018M Specification for Steel, Sheet and Strip,
Heavy-Thickness Coils, Hot-Rolled, Carbon,
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
2
A01.19 on Steel Sheet and Strip. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Oct. 1, 2013. Published October 2013. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1970. Last previous edition approved in 2009 as A635/A635M – 09b. Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/A0635_A0635M-13. the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A635/A635M−13
Commercial, Drawing, Structural, High-Strength Low- such as leveling, cutting to length, testing, inspection,
Alloy, High-Strength Low-Alloy with Improved blanking, slitting, pickling, cold rolling, heat treating, coating,
F
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: A635/A635M − 09b A635/A635M − 13
Standard Specification for
Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled,
Alloy, Carbon, Structural, High-Strength Low-Alloy, and
High-Strength Low-Alloy with Improved Formability, General
1
Requirements for
This standard is issued under the fixed designation A635/A635M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers the general requirements for hot-rolled, heavy-thickness sheet and strip in coils.
1.2 It applies to Specifications A414/A414M, A424/A424M, and A1018/A1018M.
1.3 This material is available only in coils described as follows:
Size Limits, Coils Only
Product Width, in. [mm] Thickness, in. [mm]
Strip over 8 to 12, incl 0.230 to 1.000, incl
[over 200 through 300] [from 6.0 through 25]
A
Sheet All Widths 0.230 to 1.000, incl
All Widths
[from 6.0 through 25]
A
Hot-rolled heavy thickness sheet in coils less than 12 in. [300 mm] and less in width must have slit edges. Hot-rolled heavy thickness coils 12 in. [300 mm] and wider
with mill edge is considered hot-rolled heavy thickness strip.
NOTE 1—The changes in width limits with the publication of A635/A635M – 06a result in a change in tensile testing direction for material from 0.180
in. [4.5 mm] to 0.230 in. exclusive [6.0 mm exclusive] over 48 in. [1200 mm] wide as that material is now covered by Specification A568/A568M – 06a.
The purchaser is advised to discuss this change with the supplier.
1.4 In case of any conflict in requirements, the requirements of the individual material specification shall prevail over those of
this general specification.
1.5 Annex A1 lists permissible variations in dimensions and mass (see Note 2) in SI [metric] units. The values listed are not
exact conversions of the values listed in the inch-pound tables, but instead are rounded or rationalized values. Conformance to
Annex A1 is mandatory when the “M” specification is used.
NOTE 2—The term weight is used when inch-pound units are the standard. However, under SI, the preferred term is mass.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.7 This specification and the applicable material specifications are expressed in both inch-pound units and SI units. However,
unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound
units.
2. Referenced Documents
2
2.1 ASTM Standards:
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.19
on Steel Sheet and Strip.
Current edition approved Nov. 1, 2009Oct. 1, 2013. Published December 2009October 2013. Originally approved in 1970. Last previous edition approved in 2009 as
A635/A635M – 09a.A635/A635M – 09b. DOI: 10.1520/A0635_A0635M-09B.10.1520/A0635_A0635M-13.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A635/A635M − 13
A414/A414M Specification for Steel, Sheet, Carbon, and High-Strength, Low-Alloy for Pressure Vessels
A424/A424M Specification for Steel, Sheet, for Porcelain Enameling
A700 Practices for Packaging, Marking, and Loading Methods for Steel Products for Shipment
A568/A568M Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled,
General Requirements for
A751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
A941 Terminology Relating to Steel
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.