ASTM E1461-13(2022)
(Test Method)Standard Test Method for Thermal Diffusivity by the Flash Method
Standard Test Method for Thermal Diffusivity by the Flash Method
SIGNIFICANCE AND USE
5.1 Thermal diffusivity is an important transient thermal property, required for such purposes such as design applications, determination of safe operating temperature, process control, and quality assurance.
5.2 The flash method is used to measure values of thermal diffusivity, α, of a wide range of solid materials. It is particularly advantageous because of simple specimen geometry, small specimen size requirements, rapidity of measurement and ease of handling.
5.3 Under certain strict conditions, specific heat capacity of a homogeneous isotropic opaque solid specimen can be determined when the method is used in a quantitative fashion (see Appendix X2).
5.4 Thermal diffusivity results, together with related values of specific heat capacity (Cp) and density (ρ) values, can be used in many cases to derive thermal conductivity (λ), according to the relationship:
SCOPE
1.1 This test method covers the determination of the thermal diffusivity of primarily homogeneous isotropic solid materials. Thermal diffusivity values ranging from 0.1 to 1000 (mm)2 s-1 are measurable by this test method from about 75 to 2800 K.
1.2 Practice E2585 is adjunct to this test method and contains detailed information regarding the use of the flash method. The two documents are complementing each other.
1.3 This test method is a more detailed form of Test Method C714, having applicability to much wider ranges of materials, applications, and temperatures, with improved accuracy of measurements.
1.4 This test method is intended to allow a wide variety of apparatus designs. It is not practical in a test method of this type to establish details of construction and procedures to cover all contingencies that might offer difficulties to a person without pertinent technical knowledge, or to restrict research and development for improvements in the basic technique.
1.5 This test method is applicable to the measurements performed on essentially fully dense (preferably, but low porosity would be acceptable), homogeneous, and isotropic solid materials that are opaque to the applied energy pulse. Experience shows that some deviation from these strict guidelines can be accommodated with care and proper experimental design, substantially broadening the usefulness of the method.
1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.7 For systems employing lasers as power sources, it is imperative that the safety requirement be fully met.
1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.9 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: E1461 − 13 (Reapproved 2022)
Standard Test Method for
Thermal Diffusivity by the Flash Method
This standard is issued under the fixed designation E1461; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 1.9 This international standard was developed in accor-
dance with internationally recognized principles on standard-
1.1 Thistestmethodcoversthedeterminationofthethermal
ization established in the Decision on Principles for the
diffusivity of primarily homogeneous isotropic solid materials.
2 -1 Development of International Standards, Guides and Recom-
Thermal diffusivity values ranging from 0.1 to 1000 (mm) s
mendations issued by the World Trade Organization Technical
are measurable by this test method from about 75 to 2800 K.
Barriers to Trade (TBT) Committee.
1.2 Practice E2585 is adjunct to this test method and
contains detailed information regarding the use of the flash 2. Referenced Documents
method. The two documents are complementing each other. 2
2.1 ASTM Standards:
1.3 This test method is a more detailed form ofTest Method C714 Test Method for Thermal Diffusivity of Carbon and
C714, having applicability to much wider ranges of materials, Graphite by Thermal Pulse Method
applications, and temperatures, with improved accuracy of E228 Test Method for Linear Thermal Expansion of Solid
measurements. Materials With a Push-Rod Dilatometer
E2585 Practice for Thermal Diffusivity by the Flash Method
1.4 This test method is intended to allow a wide variety of
apparatus designs. It is not practical in a test method of this
3. Terminology
typetoestablishdetailsofconstructionandprocedurestocover
3.1 Definitions of Terms Specific to This Standard:
all contingencies that might offer difficulties to a person
3.1.1 thermal conductivity, λ, of a solid material—the time
without pertinent technical knowledge, or to restrict research
rate of steady heat flow through unit thickness of an infinite
and development for improvements in the basic technique.
slab of a homogeneous material in a direction perpendicular to
1.5 This test method is applicable to the measurements
the surface, induced by unit temperature difference. The
performed on essentially fully dense (preferably, but low
property must be identified with a specific mean temperature,
porosity would be acceptable), homogeneous, and isotropic
since it varies with temperature.
solid materials that are opaque to the applied energy pulse.
3.1.2 thermal diffusivity, α, of a solid material—the property
Experience shows that some deviation from these strict guide-
givenbythethermalconductivitydividedbytheproductofthe
lines can be accommodated with care and proper experimental
density and heat capacity per unit mass.
design, substantially broadening the usefulness of the method.
3.2 Description of Symbols and Units Specific to This
1.6 The values stated in SI units are to be regarded as
Standard:
standard. No other units of measurement are included in this
3.2.1 D—diameter, m.
standard.
-1 -1
3.2.2 C —specific heat capacity, J·g ·K .
p
1.7 For systems employing lasers as power sources, it is
3.2.3 k—constant depending on percent rise.
imperative that the safety requirement be fully met.
3.2.4 K—correction factors.
1.8 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the
3.2.5 K,K —constants depending on β.
1 2
responsibility of the user of this standard to establish appro-
3.2.6 L—specimen thickness, mm.
priate safety, health, and environmental practices and deter-
3.2.7 t—response time, s.
mine the applicability of regulatory limitations prior to use.
3.2.8 t —half-rise time or time required for the rear face
1/2
temperature rise to reach one half of its maximum value, s.
ThistestmethodisunderthejurisdictionofASTMCommitteeE37onThermal
Measurements and is the direct responsibility of Subcommittee E37.05 on Thermo-
physical Properties. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved April 1, 2022. Published April 2022. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1992. Last previous edition approved in 2013 as E1461 – 13. DOI: Standards volume information, refer to the standard’s Document Summary page on
10.1520/E1461-13R22. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
E1461 − 13 (2022)
3.2.9 t*—dimensionless time (t*=4α t/D ).
s T
3.2.10 T—temperature, K.
3.2.11 α—thermal diffusivity, (mm) /s.
3.2.12 β—fraction of pulse duration required to reach maxi-
mum intensity.
3.2.13 ρ—density, g/(cm) .
-1 -1
3.2.14 λ—thermal conductivity, W·m ·K .
1 1
3.2.15 ∆t —T(5t ⁄2)/T(t ⁄2 ).
FIG. 2 Schematic of the Flash Method
1 1
3.2.16 ∆t —T(10t ⁄2)/T(t ⁄2 ).
3.2.17 ∆T —temperature difference between baseline and
max
maximum rise, K.
3.2.18 τ—pulse duration (see Fig. 1).
3.3 Description of Subscripts Specific to This Standard:
3.3.1 x—percent rise.
3.3.2 R—ratio.
3.3.3 max—maximum.
3.3.4 p—constant pressure.
4. Summary of Test Method
4.1 A small, thin disc specimen is subjected to a high- FIG. 3 Characteristic Thermal Curve for the Flash Method
intensity short duration radiant energy pulse (Fig. 2). The
energy of the pulse is absorbed on the front surface of the
specimen and the resulting rear face temperature rise (thermal
curve) is recorded. The thermal diffusivity value is calculated 5.2 The flash method is used to measure values of thermal
diffusivity, α, of a wide range of solid materials. It is particu-
from the specimen thickness and the time required for the rear
face temperature rise to reach a percentage of its maximum larly advantageous because of simple specimen geometry,
value (Fig. 3). When the thermal diffusivity of the specimen is small specimen size requirements, rapidity of measurement
to be determined over a temperature range, the measurement and ease of handling.
must be repeated at each temperature of interest.
5.3 Under certain strict conditions, specific heat capacity of
a homogeneous isotropic opaque solid specimen can be deter-
NOTE 1—This test method is described in detail in a number of
publications (1, 2) and review articles (3, 4, 5).Asummary of the theory
mined when the method is used in a quantitative fashion (see
can be found in Appendix X1.
Appendix X2).
5.4 Thermal diffusivity results, together with related values
5. Significance and Use
of specific heat capacity (C ) and density (ρ) values, can be
p
5.1 Thermal diffusivity is an important transient thermal
used in many cases to derive thermal conductivity (λ), accord-
property, required for such purposes such as design
ing to the relationship:
applications, determination of safe operating temperature,
λ 5 α C ρ (1)
process control, and quality assurance.
p
6. Interferences
The boldface numbers given in parentheses refer to a list of references at the
6.1 In principle, the thermal diffusivity is obtained from the
end of the text.
thickness of the specimen and from a characteristic time
function describing the propagation of heat from the front
surface of the specimen to its back surface. The sources of
uncertainties in the measurement are associated with the
specimen itself, the temperature measurements, the perfor-
mance of the detector and of the data acquisition system, the
data analysis and more specifically the finite pulse time effect,
the nonuniform heating of the specimen and the heat losses
(radiativeandconductive).Thesesourcesofuncertaintycanbe
considered systematic, and should be carefully considered for
each experiment. Errors random in nature (noise, for example)
can be best estimated by performing a large number of repeat
experiments. The relative standard deviation of the obtained
FIG. 1 Laser Pulse Shape resultsisagoodrepresentationoftherandomcomponentofthe
E1461 − 13 (2022)
uncertainty associated with the measurement. Guidelines in 7.5.1 The data acquisition system must be of an adequate
performing a rigorous evaluation of these factors are given in speed to ensure that resolution in determining half-rise time on
(6). the thermal curve is no more than 1 % of the half-rise time, for
the fastest thermal curve for which the system is qualified.
7. Apparatus
7.6 Measurement of specimen’s temperature is performed
The essential components of the apparatus are shown in Fig.
using calibrated temperature sensors such as a thermocouple,
4. These are the flash source, specimen holder, environmen-
optical pyrometer, platinum resistance temperature detector
tal enclosure (optional), temperature detector and recording
(RTD), etc.The temperature sensor shall be in intimate contact
device.
with or trained on the sample holder, in close proximity of the
7.1 The flash source may be a pulse laser, a flash lamp, or
specimen.
other device capable to generate a short duration pulse of
NOTE 3—Touching the specimen with thermocouples is not recom-
substantial energy. The duration of the pulse should be less
mended. Embedding thermocouples into the specimen is not acceptable.
than 2 % of the time required for the rear face temperature rise
7.7 The temperature controller and/or programmer are to
to reach one half of its maximum value (see Fig. 3).
bring the specimen to the temperatures of interest.
NOTE 2—Apulse length correction may be applied (7, 8, 9) permitting
use of pulse durations greater than 0.5 %.
8. Test Specimen
7.1.1 The energy of the pulse hitting the specimen’s surface
8.1 The usual specimen is a thin circular disc with a front
must be spatially uniform in intensity.
surface area less than that of the energy beam. Typically,
7.2 An environmental control chamber is required for mea- specimens are 10 to 12.5 mm in diameter (in special cases, as
surements above and below room temperature. small as 6 mm diameter and as large as 30 mm diameter have
been reported as used successfully). The optimum thickness
7.3 The temperature detector can be a thermocouple, infra-
depends upon the magnitude of the estimated thermal
red detector, optical pyrometer, or any other sensor that can
diffusivity, and should be chosen so that the time to reach half
provide a linear electrical output proportional to a small
of the maximum temperature falls within the 10 to 1000 ms
temperature rise. It shall be capable of detecting 0.05 K change
range. Thinner specimens are desired at higher temperatures to
above the specimen’s initial temperature. The detector and its
minimize heat loss corrections; however, specimens should
associated amplifier must have a response time not more than
alwaysbethickenoughtoberepresentativeofthetestmaterial.
2 % of the half-rise time value.
Typically, thicknesses are in the 1 to 6 mm range.
7.4 The signal conditioner includes the electronic circuit to
8.2 Specimens must be prepared with faces flat and parallel
bias out the ambient temperature reading, spike filters,
within 0.5 % of their thickness, in order to keep the error in
amplifiers, and analog-to-digital converters.
thermal diffusivity due to the measured average thickness, to
7.5 Data Recording:
less than 1 %. Non-uniformity of either surface (craters,
scratches, markings) should be avoided
8.3 Specimen Surface Preparation—It is a good practice to
apply a very thin, uniform graphite or other high emissivity
coating on both faces of the specimen to be tested, prior to
performing the measurements. The coating may be applied by
spraying, painting, sputtering, etc. This will improve the
capability of the specimen to absorb the energy applied,
especiallyincaseofhighlyreflectivematerials.Fortransparent
materials, a layer of gold, silver, or other opaque materials
mustbedepositedfirst,followedbygraphitecoating.Forsome
opaque reflective materials, grit blasting of the surface can
provide sufficient pulse absorption and emissivity, especially at
higher temperatures, where coatings may not be stable or may
react with the material.
9. Calibration and Verification
9.1 It is important to periodically verify the performance of
a device and to establish the extent these errors may affect the
data generated. This can be accomplished by testing one or
several materials whose thermal diffusivity is well known (see
Appendix X3).
9.1.1 The use of reference materials to establish validity of
the data on unknown materials can lead to unwarranted
statements on accuracy. The use of references is only valid
FIG. 4 Block Diagram of a Flash System when the properties of the reference (including half-rise times
E1461 − 13 (2022)
and thermal diffusivity values) are similar to those of the α 5 0.13879L /t (2)
½
unknown and the temperature-rise curves are determined in an
Check the validity of the experiment by calculating α at a
identical manner for the reference and unknown.
minimum of two other points on the rise curve.The equation is
9.1.2 An important check of the validity of data (in addition
as follows:
to the comparison of the rise curve with the theoretical model),
α 5 k L /t (3)
x x
when corrections have been applied, is to vary the specimen
thickness. Since the half times vary as L , decreasing the
where:
specimen thickness by one-half should decrease the half time
t = the time required for the temperature rise to reach x
x
toone-fourthofitsoriginalvalue.Thus,ifoneobtainsthesame
percent of ∆T . Values of k are given in Table 1.
max x
thermal diffusivity value (appropriate heat loss corrections
11.1.1 Ideally, the calculated values of α for different values
being applied) with representative specimens from the same
of x should all be the same. If the values at 25, 50 and 75 %
materialofsignificantlydifferentthicknesses,theresultscanbe
∆T liewithin 62 %,theoverallaccuracyisprobablywithin
max
assumed valid.
65 % at the half-rise time. If the α values lie outside of this
range, the response curve should be analyzed further to see if
10. Procedure
thermal radiation heat loss, finite-pulse time or non-uniform
10.1 For commercially produced systems, follow manufac-
heating effects are present.
turer’s instructions.
11.1.2 Thermal radiation heat loss effects are most readily
10.2 The testing procedure must contain the following determined from the temperature of the spe
...
Questions, Comments and Discussion