Standard Test Method for Slump Flow of Self-Consolidating Concrete

SIGNIFICANCE AND USE
This test method provides a procedure to determine the slump flow of self-consolidating concrete in the laboratory or the field.
This test method is used to monitor the consistency of fresh, unhardened self-consolidating concrete and its unconfined flow potential.
It is difficult to produce self-consolidating concrete that is both flowable and nonsegregating using coarse aggregates larger than 25 mm [1 in.]. Therefore, this test method is considered applicable to self-consolidating concrete having coarse aggregate up to 25 mm [1 in.] in size. Appendix X1 provides non-mandatory visual rating criteria that may be used to classify the ability of a self-consolidating concrete mixture to resist segregation (stability).
The rate at which the concrete spreads is related to its viscosity. Appendix X1 provides a non-mandatory procedure that may be used to provide an indication of relative viscosity of self-consolidating concrete mixtures.
SCOPE
1.1 This test method covers the determination of slump flow of self-consolidating concrete.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. (WARNING—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure. )

General Information

Status
Historical
Publication Date
31-Jul-2009
Current Stage
Ref Project

Relations

Buy Standard

Standard
ASTM C1611/C1611M-09b - Standard Test Method for Slump Flow of Self-Consolidating Concrete
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
REDLINE ASTM C1611/C1611M-09b - Standard Test Method for Slump Flow of Self-Consolidating Concrete
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:C1611/C1611M–09b
Standard Test Method for
1
Slump Flow of Self-Consolidating Concrete
ThisstandardisissuedunderthefixeddesignationC1611/C1611M;thenumberimmediatelyfollowingthedesignationindicatestheyear
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* C173/C173M Test Method for Air Content of Freshly
Mixed Concrete by the Volumetric Method
1.1 This test method covers the determination of slump flow
C670 Practice for Preparing Precision and Bias Statements
of self-consolidating concrete.
for Test Methods for Construction Materials
1.2 The values stated in either SI units or inch-pound units
are to be regarded separately as standard. The values stated in
3. Terminology
each system may not be exact equivalents; therefore, each
3.1 For definitions of terms used in this test method, refer to
system shall be used independently of the other. Combining
Terminology C125.
values from the two systems may result in non-conformance
3.2 Definitions of Terms Specific to This Standard:
with the standard.
3.2.1 halo, n—an observed cement paste or mortar ring that
1.3 The text of this standard references notes and footnotes
has clearly separated from the coarse aggregate, around the
that provide explanatory material. These notes and footnotes
outside circumference of concrete after flowing from the mold.
(excluding those in tables and figures) shall not be considered
3.2.2 spread, n—the distance of lateral flow of concrete
as requirements of the standard.
during the slump-flow test.
1.4 This standard does not purport to address all of the
3.2.3 stability, n—the ability of a concrete mixture to resist
safety concerns, if any, associated with its use. It is the
segregation of the paste from the aggregates.
responsibility of the user of this standard to establish appro-
3.2.4 viscosity, n—resistance of a material to flow under an
priate safety and health practices and determine the applica-
applied shearing stress.
bility of regulatory limitations prior to use. (WARNING—
Fresh hydraulic cementitious mixtures are caustic and may
4. Summary of Test Method
cause chemical burns to skin and tissue upon prolonged
2 4.1 A sample of freshly mixed concrete is placed in a mold
exposure. )
eitherintheuprightorinvertedposition.Theconcreteisplaced
inoneliftwithouttampingorvibration.Themoldisraised,and
2. Referenced Documents
3 the concrete is allowed to spread. After spreading ceases, two
2.1 ASTM Standards:
diameters of the concrete mass are measured in approximately
C125 Terminology Relating to Concrete and Concrete Ag-
orthogonal directions. Slump flow is the average of the two
gregates
diameters.
C143/C143M Test Method for Slump of Hydraulic-Cement
Concrete
5. Significance and Use
C172 Practice for Sampling Freshly Mixed Concrete
5.1 This test method provides a procedure to determine the
slump flow of self-consolidating concrete in the laboratory or
the field.
1
This test method is under the jurisdiction of ASTM Committee C09 on
5.2 This test method is used to monitor the consistency of
Concrete and ConcreteAggregates and is the direct responsibility of Subcommittee
C09.47 on Self-Consolidating Concrete. fresh, unhardened self-consolidating concrete and its uncon-
Current edition approved Aug. 1, 2009. Published September 2009. Originally
fined flow potential.
approved in 2009. Last previous edition approved in 2009 as C1611/C1611M – 09a.
5.3 It is difficult to produce self-consolidating concrete that
DOI: 10.1520/C1611_C1611M-09B.
2
is both flowable and nonsegregating using coarse aggregates
Section on Safety Precautions, Manual of Aggregate and Concrete Testing,
Annual Book of ASTM Standards, Vol. 04.02.
larger than 25 mm [1 in.]. Therefore, this test method is
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
considered applicable to self-consolidating concrete having
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
coarse aggregate up to 25 mm [1 in.] in size. Appendix X1
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. provides non-mandatory visual rating criteria that may be used
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C1611/C1611M–09b
the two filling procedures can be obtained in the round robin test report
to classify the ability of a self-consolidating concrete mixture
available from ASTM headquarters.
to resist segregation (stability).
NOTE 3—Filling the mold with concrete by using mu
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:C1611/C1611M–09a Designation:C1611/C1611M–09b
Standard Test Method for
1
Slump Flow of Self-Consolidating Concrete
This standard is issued under the fixed designation C 1611/C 1611M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This test method covers the determination of slump flow of self-consolidating concrete.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes
(excluding those in tables and figures) shall not be considered as requirements of the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use. (WARNING—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin
2
and tissue upon prolonged exposure. )
2. Referenced Documents
3
2.1 ASTM Standards:
C 125 Terminology Relating to Concrete and Concrete Aggregates
C 143/C 143M Test Method for Slump of Hydraulic-Cement Concrete
C 172 Practice for Sampling Freshly Mixed Concrete
C 173/C 173M Test Method for Air Content of Freshly Mixed Concrete by the Volumetric Method
C 670 Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials
3. Terminology
3.1 For definitions of terms used in this test method, refer to Terminology C 125.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 halo, n—an observed cement paste or mortar ring that has clearly separated from the coarse aggregate, around the outside
circumference of concrete after flowing from the mold.
3.2.2 spread, n—the distance of lateral flow of concrete during the slump-flow test.
3.2.3 stability, n—the ability of a concrete mixture to resist segregation of the paste from the aggregates.
3.2.4 viscosity, n—resistance of a material to flow under an applied shearing stress.
4. Summary of Test Method
4.1 Asample of freshly mixed concrete is placed in a mold shaped aseither in the frustum of a cone.upright or inverted position.
The concrete is placed in one lift without tamping or vibration. The mold is raised, and the concrete is allowed to spread. After
spreading ceases, two diameters of the concrete mass are measured in approximately orthogonal directions, and slumpdirections.
Slump flow is the average of the two diameters.
5. Significance and Use
5.1 This test method provides a procedure to determine the slump flow of self-consolidating concrete in the laboratory or the
field.
1
This test method is under the jurisdiction of ASTM Committee C09 on Concrete and Concrete Aggregates and is the direct responsibility of Subcommittee C09.47 on
Self-Consolidating Concrete.
Current edition approved JuneAug. 1, 2009. Published JulySeptember 2009. Originally approved in 2009. Last previous edition approved in 2009 as C 1611/
C 1611M – 09a.
2
Section on Safety Precautions, Manual of Aggregate and Concrete Testing, Annual Book of ASTM Standards, Vol. 04.02.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C1611/C1611M–09b
5.2 This test method is used to monitor the consistency of fresh, unhardened self-consolidating concrete and its unconfined flow
potential.
5.3 It is difficult to produce self-consolidating concrete that is both flowable and nonsegregating using coarse aggregates larger
than 25 mm [1 in.]. Therefore, this test method is considered applicable to self-consolidating concrete having coars
...

Questions, Comments and Discussion