Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)

Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)

ABSTRACT
This specification covers dry air-setting refractory mortar for use in laying and bonding refractory brick in ship boiler furnaces and wet air-setting refractory mortar for use in laying refractory brick in stationary boiler furnaces, bright annealing furnaces, controlled atmosphere furnaces, and furnaces heated by electric elements. The refractory mortar shall be of the following types: Type 1 and Type 2. The mortar shall be composed of finely ground heat-resistant clays, minerals, or a mixture of clays and minerals in either a dry or wet condition. Fineness test, heat soak, and bonding strength test shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers dry air-setting refractory mortar for use in laying and bonding refractory brick in ship boiler furnaces and wet air-setting refractory mortar for use in laying refractory brick in stationary boiler furnaces, bright annealing furnaces, controlled atmosphere furnaces, and furnaces heated by electric elements.
1.2 The values stated in inch-pound units are to be regarded as standard. The SI units in parentheses are for information purposes only and may be approximate.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Apr-2012
ICS
81.080 - Refractories
91.100.10 - Cement. Gypsum. Lime. Mortar
Technical Committee
F25 - Ships and Marine Technology
Drafting Committee
F25.07 - General Requirements
Current Stage
Ref Project

Relations

Replaces
ASTM F1097-91(2006) - Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)
Effective Date
01-May-2012

Buy Standard

ASTM F1097-91(2012) - Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)ASTM F1097-91(2012) - Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)
PreviousNext
Technical specification
ASTM F1097-91(2012) - Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:F1097 −91 (Reapproved 2012) An American National Standard
Standard Specification for
1
Mortar, Refractory (High-Temperature, Air-Setting)
This standard is issued under the fixed designation F1097; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope C199 Test Method for Pier Test for Refractory Mortars
3
2.2 Federal Specifications —The following documents shall
1.1 This specification covers dry air-setting refractory mor-
apply only when one or more of the requirements of S1 are
tar for use in laying and bonding refractory brick in ship boiler
furnaces and wet air-setting refractory mortar for use in laying specified in the contract or purchase order (see 4.1.3):
UU-S-48 Sacks, Shipping, Paper
refractory brick in stationary boiler furnaces, bright annealing
furnaces, controlled atmosphere furnaces, and furnaces heated PPP-B-35 Bags: Textile, Shipping, Burlap, Cotton and Wa-
terproof Laminated
by electric elements.
PPP-B-704 Pails: Shipping, Steel (1 through 12 gallon)
1.2 The values stated in inch-pound units are to be regarded
3
2.3 Military Standards —The following documents shall
as standard. The SI units in parentheses are for information
apply only when one or more of the requirements of S1 are
purposes only and may be approximate.
specified in the contract or purchase order (see 4.1.3):
1.3 This standard does not purport to address all of the
MIL-STD-105 Sampling Procedures and Tables for Inspec-
safety concerns, if any, associated with its use. It is the
tion by Attributes
responsibility of the user of this standard to establish appro-
MIL-STD-129 Marking for Shipment and Storage
priate safety, health, and environmental practices and deter-
mine the applicability of regulatory limitations prior to use.
3. Classification
1.4 This international standard was developed in accor-
3.1 The refractory mortar shall be of the following types:
dance with internationally recognized principles on standard-
3.1.1 Type 1—Dry.
ization established in the Decision on Principles for the
3.1.2 Type 2—Wet.
Development of International Standards, Guides and Recom-
mendations issued by the World Trade Organization Technical
4. Ordering Information
Barriers to Trade (TBT) Committee.
4.1 Orders for material under this specification shall include
2. Referenced Documents
the following information, as necessary to adequately describe
2
2.1 ASTM Standards:
the material:
C24 Test Method for Pyrometric Cone Equivalent (PCE) of
4.1.1 ASTM designation and year of issue,
Fireclay and High Alumina Refractory Materials
4.1.2 Type required (see 3.1), and
C27 Classification of Fireclay and High-Alumina Refractory
4.1.3 Optional requirements, if any (see S1).
Brick
C92 Test Methods for Sieve Analysis and Water Content of
5. Material
Refractory Materials
5.1 The mortar shall be composed of finely ground heat-
C133 Test Methods for Cold Crushing Strength and Modu-
resistant clays, minerals, or a mixture of clays and minerals in
lus of Rupture of Refractories
either a dry or wet condition.
C198 Test Method for Cold Bonding Strength of Refractory
5.1.1 Type 1, Dry—Mortar shall be furnished dry and shall
Mortar
be ready for use as soon as mixed with water. Mortar, after
being mixed with water and then dried, shall be capable of
1
This specification is under the jurisdiction of ASTM Committee F25 on Ships
being remixed with water.
and Marine Technology and is the direct responsibility of Subcommittee F25.07 on
5.1.2 Type 2, Wet—Mortar shall be furnished ready for use
General Requirements.
at a trowelling consistency and shall be easily mixed with
Current edition approved May 1, 2012. Published May 2012. Originally
approved in 1991. Last previous edition approved in 2006 as F1097 – 91 (2006). water to a dipping consistency.
DOI: 10.1520/F1097-91R12.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
3
Standards volume information, refer to the standard’s Document Summary page on Available from DLA Document Services, Building 4/D, 700 Robbins Ave.,
the ASTM website. Philadelphia, PA 19111-5094, http://quicksearch.dla.mil.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
F1097−91 (2012)
6. Performance Requirements composite. There shall be no evidence of failure to meet the
specified unit or average requirements.
6.1 Resistance to Heat Soaking—Mortar shall not soften nor
show any evidence of fusion, and the shrin
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM F1097-17(2022)(Specification)
Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)

ABSTRACT
This specification covers dry air-setting refractory mortar for use in laying and bonding refractory brick in ship boiler furnaces and wet air-setting refractory mortar for use in laying refractory brick in stationary boiler furnaces, bright annealing furnaces, controlled atmosphere furnaces, and furnaces heated by electric elements. The refractory mortar shall be of the following types: Type 1 and Type 2. The mortar shall be composed of finely ground heat-resistant clays, minerals, or a mixture of clays and minerals in either a dry or wet condition. Fineness test, heat soak, and bonding strength test shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers dry air-setting refractory mortar for use in laying and bonding refractory brick in ship boiler furnaces and wet air-setting refractory mortar for use in laying refractory brick in stationary boiler furnaces, bright annealing furnaces, controlled atmosphere furnaces, and furnaces heated by electric elements.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM F1097-17(2022)(Specification)
Standard Specification for Mortar, Refractory (High-Temperature, Air-Setting)

ABSTRACT
This specification covers dry air-setting refractory mortar for use in laying and bonding refractory brick in ship boiler furnaces and wet air-setting refractory mortar for use in laying refractory brick in stationary boiler furnaces, bright annealing furnaces, controlled atmosphere furnaces, and furnaces heated by electric elements. The refractory mortar shall be of the following types: Type 1 and Type 2. The mortar shall be composed of finely ground heat-resistant clays, minerals, or a mixture of clays and minerals in either a dry or wet condition. Fineness test, heat soak, and bonding strength test shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers dry air-setting refractory mortar for use in laying and bonding refractory brick in ship boiler furnaces and wet air-setting refractory mortar for use in laying refractory brick in stationary boiler furnaces, bright annealing furnaces, controlled atmosphere furnaces, and furnaces heated by electric elements.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM B637-23(Specification)
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for high-temperature service. Chemical analysis shall be performed on the alloy and shall conform to the chemical composition requirement in carbon, manganese, silicon, phosphorus, sulfur, chromium, cobalt, molybdenum, columbium, tantalum, titanium, aluminum, zirconium, boron, iron, copper, and nickel. The material shall follow recommended annealing treatment, solution treatment, stabilizing treatment, and precipitation hardening treatment. Tension testing, hardness testing and stress-rupture testing shall be performed on the material and shall comply to the required tensile strength, yield strength, elongation, reduction in area, and Brinell hardness.
SCOPE
1.1 This specification2 covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for moderate or high temperature service (Table 1).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM C596-23(Test Method)
Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement

SIGNIFICANCE AND USE
4.1 This test method establishes a selected set of conditions of temperature, relative humidity and rate of evaporation of the environment to which a mortar specimen of stated composition shall be subjected for a specified period of time during which its change in length is determined and designated “drying shrinkage.”  
4.2 The drying shrinkage of mortar as determined by this test method has a linear relation to the drying shrinkage of concrete made with the same cement and exposed to the same drying conditions.4 Hence this test method may be used when it is desired to develop data on the effect of a hydraulic cement on the drying shrinkage of concrete made with that cement.
SCOPE
1.1 This test method determines the change in length on drying of mortar bars containing hydraulic cement and graded standard sand.  
1.2 The values stated in SI units are to be regarded as standard. When combined standards are referenced, the selection of measurement system is at the user’s discretion subject to the requirements of the referenced standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure).2  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM F3337-23(Guide)
Standard Guide for Taking Property and Behavior Measurements on Weathered Fractions of Oil

SIGNIFICANCE AND USE
5.1 A standard procedure is necessary to establish property changes for spilled oils or petroleum products at different oil weathering stages.  
5.2 This procedure employs standardized equipment, and test procedures.  
5.3 This procedure should be performed at the stages of weathering corresponding to the spill conditions of interest.
SCOPE
1.1 This guide summarizes methods to fractionate oil by evaporative weathering and then measure the properties and behavior of the weathered oil. The results of this guide can provide oil behavior data for input into oil spill models and response method selection.  
1.2 This guide covers general procedures for oil weathering and behavior and does not cover all possible procedures which may be applicable to this topic.  
1.3 The results obtained using this guide are intended to provide baseline data for the behavior of oil and petroleum products when spilled and input to oil spill models.  
1.4 The results obtained using this guide can be used directly to predict certain facets of oil spill behavior or as input to oil spill models.  
1.5 The accuracy of the guide depends very much on the representative nature of the oil sample used. Certain oils can have different properties depending on their chemical contents at the moment a sample is taken.  
1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    4 pages
    English language
    sale 15% off
  • Guide
    4 pages
    English language
    sale 15% off
ASTM
ASTM F1210-23(Guide)
Standard Guide for Ecological Considerations for the Use of Oil Spill Dispersants in Freshwater and Other Inland Environments, Lakes and Large Water Bodies

SIGNIFICANCE AND USE
3.1 This guide is meant to aid response teams who may use it during spill response planning and spill events.  
3.2 This guide should be adapted to site specific circumstance.
SCOPE
1.1 This guide covers the use of oil spill dispersants to assist in the control of oil spills. The guide is written with the goal of minimizing the environmental impacts of oil spills; this goal is the basis on which the recommendations are made. Aesthetic and socioeconomic factors are not considered, although these and other factors are often important in spill response.  
1.2 Spill responders have available several means to control or clean up spilled oil. Chemical dispersants should be given equal consideration with other spill countermeasures.  
1.3 This is a general guide only. Oil, as used in this guide, includes crude oils and refined petroleum products. Differences between individual dispersants or between different oil products are not considered. The dispersibility of the oil with the chosen dispersant should be evaluated.  
1.4 The guide is organized by habitat type, for example, small ponds and lakes, rivers and streams, and land. It considers the use of dispersants primarily to protect habitats from impact (or to minimize impacts).  
1.5 This guide applies only to freshwater and other inland environments. It does not consider the direct application of dispersants to subsurface waters.  
1.6 In making dispersant use decisions, appropriate government authorities should be consulted as required by law.  
1.7 This guide does not address getting regulatory approval.  
1.8 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM D8139-23(Specification)
Standard Specification for Semi-Rigid, Closed-Cell Polypropylene Foam, Preformed Expansion Joint Fillers for Concrete Paving and Structural Construction

SCOPE
1.1 This specification covers preformed expansion joint fillers made from closed-cell polypropylene foam materials having suitable compressibility, recovery from compression, nonextruding, and weather-resistant characteristics.  
1.1.1 Type I, closed-cell polypropylene foam.  
1.2 These joint fillers are intended for use in concrete pavements in full-depth joints. There are several variations in size with typical thicknesses of 1/2 in. (12.7 mm), 3/4 in. (19.05 mm), and 1 in. (25.4 mm); typical widths of 31/2 in. (88.9 mm), 4 in. (101.6 mm), 5 in. (127 mm), 6 in. (152.5 mm), 7 in. (177.8 mm), 8 in. (203.2 mm), or 48 in. (1.2 m) sheet; and typical lengths of 5 ft (1.52 m) and 10 ft (3.05 m).  
1.3 The values stated in inch-pound units are to be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM D6390-23(Test Method)
Standard Test Method for Determination of Draindown Characteristics in Uncompacted Asphalt Mixtures

SIGNIFICANCE AND USE
5.1 This test method can be used to determine whether the amount of draindown measured for a given asphalt mixture is within specified acceptable levels. The test provides an evaluation of the draindown potential of an asphalt mixture during mixture design and/or during field production. This test is primarily used for mixtures with high coarse aggregate content such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the amount of draindown in an uncompacted asphalt mixture sample when the sample is held at elevated temperatures comparable to those encountered during the production, storage, transport, and placement of the mixture. The test is particularly applicable to mixtures such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D545-23(Test Method)
Standard Test Methods for Preformed Expansion Joint Fillers for Concrete Construction (Nonextruding and Resilient Types)

SIGNIFICANCE AND USE
3.1 The compression resistance perpendicular to the faces, the resistance to the extrusion during compression, and the ability to recover after release of the load are indicative of a joint filler's ability to continuously fill a concrete expansion joint and thereby prevent damage that might otherwise occur during thermal expansion. The asphalt content is a measure of the fiber-type joint filler's durability and life expectancy. In the case of cork-type fillers, the resistance to water absorption and resistance to boiling hydrochloric acid are relative measures of durability and life expectancy.
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 These test methods cover the physical properties associated with preformed expansion joint fillers. The test methods include:    
Property  
Section  
Expansion in Boiling Water  
7.1  
Recovery and Compression  
7.2  
Extrusion  
7.3  
Boiling in Hydrochloric Acid  
7.4  
Asphalt Content  
7.5  
Water Absorption  
7.6  
Density  
7.7
Note 1: Specific test methods are applicable only to certain types of joint fillers, as stated herein.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D517-23(Specification)
Standard Specification for Asphalt Plank

ABSTRACT
This specification covers asphalt plank used for bridge decks as well as for industrial floors. Asphalt planks shall be classified according to usage: Type Ia; Type Ib; and Type II. Asphalt plank shall be formed from a mixture of asphalt, fibers, modifiers, or a combination thereof, and mineral filler in such a manner as to produce a uniformly dense mass. The following test methods shall be intended to measure those attributes necessary to measure the ability of asphalt plank to provide a reasonably long and satisfactory service: absorption; brittleness; dimensions; and hardness.
SCOPE
1.1 This specification covers asphalt plank used for bridge decks as well as for industrial floors.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off