ASTM D4287-00(2023)
(Test Method)Standard Test Method for High-Shear Viscosity Using a Cone/Plate Viscometer
Standard Test Method for High-Shear Viscosity Using a Cone/Plate Viscometer
SIGNIFICANCE AND USE
4.1 The viscosity value obtained by this test method gives information about the flow properties of the material under high-shear conditions similar to those encountered during application: brushing (see Test Method D4958), spraying, electrostatic disk, or roll coating.
4.2 This test method is suitable for all paints and varnishes whether they are Newtonian in behavior or not. However, due to the narrow gap between the stationary and rotary parts of high-shear viscometers, this test method is more reproducible for paints having finer pigment dispersions as determined by Test Method D1210.
SCOPE
1.1 This test method covers the determination of the viscosity of paints, varnishes, and related products at a rate of shear of 12 000 s−1.
1.2 Paints and varnishes that dry very rapidly may not give reproducible results with this test method. Measurements made at elevated temperatures may also give poor precision due to loss of volatiles and to drying.
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D4287 − 00 (Reapproved 2023)
Standard Test Method for
1
High-Shear Viscosity Using a Cone/Plate Viscometer
This standard is issued under the fixed designation D4287; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope D4958 Test Method for Comparison of the Brush Drag of
Latex Paints
1.1 This test method covers the determination of the viscos-
ity of paints, varnishes, and related products at a rate of shear
3. Summary of Test Method
−1
of 12 000 s .
3.1 The material to be tested is placed between the cone and
1.2 Paints and varnishes that dry very rapidly may not give
plate of a cone/plate viscometer, then subjected to a high shear
reproducible results with this test method. Measurements made
rate while the viscosity is determined.
at elevated temperatures may also give poor precision due to
loss of volatiles and to drying.
4. Significance and Use
1.3 The values stated in SI units are to be regarded as 4.1 The viscosity value obtained by this test method gives
standard. No other units of measurement are included in this
information about the flow properties of the material under
standard. high-shear conditions similar to those encountered during
application: brushing (see Test Method D4958), spraying,
1.4 This standard does not purport to address all of the
electrostatic disk, or roll coating.
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro-
4.2 This test method is suitable for all paints and varnishes
priate safety, health, and environmental practices and deter-
whether they are Newtonian in behavior or not. However, due
mine the applicability of regulatory limitations prior to use.
to the narrow gap between the stationary and rotary parts of
1.5 This international standard was developed in accor-
high-shear viscometers, this test method is more reproducible
dance with internationally recognized principles on standard-
for paints having finer pigment dispersions as determined by
ization established in the Decision on Principles for the
Test Method D1210.
Development of International Standards, Guides and Recom-
5. Apparatus
mendations issued by the World Trade Organization Technical
Barriers to Trade (TBT) Committee.
5.1 Cone/Plate Type Viscometer, with cone/speed combina-
−1
tion producing a rate of shear of 12 000 s . The viscometer
2. Referenced Documents
must provide a viscosity measurement rage of either 0 (P) to
2
2.1 ASTM Standards:
10 (P) or 0 (P) to 5 (P) at the above mentioned shear rate. With
D1210 Test Method for Fineness of Dispersion of Pigment-
higher viscosity materials, other cones and speeds may be used
Vehicle Systems by Hegman-Type Gage
upon agreement between the producer and the user, but it
D3925 Practice for Sampling Liquid Paints and Related
should be noted that these may give lower shear rates not truly
Pigmented Coatings
representative of application conditions. Refer to Fig. 1 and
Fig. 2 of an analog and digital cone and plate viscometer.
1
This test method is under the jurisdiction of ASTM Committee D01 on Paint
NOTE 1—The SI units for viscosity are pascal-seconds (Pa·s = 10 P, 1
and Related Coatings, Materials, and Applications and is the direct responsibility of
mPa·s = 1 cP).
Subcommittee D01.24 on Physical Properties of Liquid Paints & Paint Materials.
Current edition approved Oct. 1, 2023. Published October 2023. Originally
6. Reagents and Materials
approved in 1983. Last previous edition approved in 2019 as D4287 – 00 (2019).
DOI: 10.1520/D4287-00R23.
6.1 Water or Solvent—The viscometer should be zeroed
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
according to the manufacturer’s specification. Zeroing proce-
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
dures that require liquid may be satisfied with water or a low
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. viscosity solvent such as xylene or mineral spirits.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D4287 − 00 (2023)
FIG. 2 Digital Cone and Plate Viscometer
8. Preparation of Apparatus
8.1 The viscometer should be zeroed on a daily basis when
in
...
Questions, Comments and Discussion