ISO 5182:1978

Materials for resistance welding electrodes and ancillary equipment

Matériaux pour électrodes de soudage par résistance et equipements annexes

General Information

• Status: Withdrawn
• Publication Date: 31-Oct-1978
• Withdrawal Date: 31-Oct-1978
• ICS: 25.160.20 - Welding consumables
• Technical Committee: ISO/TC 44 - Welding and allied processes
• Drafting Committee: ISO/TC 44 - Welding and allied processes
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 01-Mar-1991

Relations

• Revised: ISO 5182:1991 - Welding — Materials for resistance welding electrodes and ancillary equipment
• Effective Date: 15-Apr-2008
• Consolidated By: ISO 2151:2004 - Acoustics — Noise test code for compressors and vacuum pumps — Engineering method (Grade 2)
• Effective Date: 06-Jun-2022

Standards Content (Sample)

INTERNATIONAL STANDARD 5182
INTERNATIONAL ORGANIZATION FOR STANDARDlZATION*MEW(AYHAPO&4AR OPTAHMJAUMR flû CTAH~AFTM3AUHH.ORGANlSATlON INTERNATIONALE DE NORMALISATION
Materials for resistance welding electrodes and ancillary
equipment
Matériaux pour électrodes de soudage par résistance et équipements annexes
First edition - 1978-11-15
a
w
-
UDC 621.791 .O37 Ref. No. IS0 5182-1978 (E)
P
O!
Descriptors : welding, resistance welding electrodes, copper, copper alloys, sintered products, materials specifications, resistivity, hardness,
c,
c utilization, marking.
LrJ
s
Price based on 6 pages
I

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 member bodies). The work of developing
International Standards is carried out through IS0 technical committees. Every
member body interested in a subject for which a technical committee has been set
up has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with 60, also take part in the work.
Draft International Standards adopted by the technical committees are circulated
to the member bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 51 82 was developed by Technical Committee
ISO/TC 44, Welding, and was circulated to the member bodies in September 1976.
It has been approved by the member bodies of the following countries :
Belgium Italy Romania
Canada Korea, Rep. of South Africa, Rep. of
Denmark Mexico Spain
Finland Netherlands Sweden
France New Zealand Switzerland
Germany, F.R. Norway U.S.A.
India Philippines Yugoslavia
Israel Portugal
The member body of the following country expressed disapproval of the document
on technical grounds :
United Kingdom
O International Olginization for Standardization, 1978 O
Printed in Switzerland

---------------------- Page: 2 ----------------------
~ ~~
IS0 5182-1978 (E)
INTERNATIONAL STANDARD
Materials for resistance welding electrodes and ancillary
equipment
ISO3489, Wrought copper and copper alloys - Drawn
1 SCOPE AND FIELD OF APPLICATION
round bars - Dimensions and tolerances.’ )
This International Standard specifies the characteristics of
IS0 3490, Wrought copper and copper alloys - Drawn
materials for resistance welding electrodes and ancillary
hexagonal bars - Dimensions and tolerances.’
equipment which are used for carrying current and
transmitting force to the work.
IS0 3491, Wrought copper and copper alloys - Drawn
square bars - Dimensions and tolerances.‘
2 REFERENCES
ISO3492, Wrought copper and copper alloys - Drawn
round wire - Dimensions and tolerances. ’
ISOIR 399, Vickers hardness test for copper and copper
alloys (Test loads from 2,5 to 50 kgf).
IEC Publication 468, Method of measurement of resistivity
of metallic materials.
ISO/R 403, Brinell hardness test for copper and copper
alloys.
3 DEFINITION
IS0 428, Wrought copper-aluminium alloys - Chemical
composition and forms of wrought products.
For the purpose of this International Standard, the
following definition applies.
I SOI R 1 1 87, Special wrought copper alloys.
softening temperature : The maximum temperature that,
ISOIR 1336, Wrought alloyed coppers.
if maintained for 2 h, will result in a reduction in ambient
ISOIR 1337, Wrought coppers.
temperature hardness of a maximum of 15 % of the “as
received” value.
IS0 1634, Wrought copper and copper alloys - Rolled flat
products (plate, sheet, strip) - Mechanical properties.
4 CLASSIFICATION
IS0 1637, Wrought copper and copper alloys - Solid
products supplied in straight lengths - Mechanical
4.1 Group A - Coppers and copper alloys
properties.
This sub-clause defines four types of material, namely :
IS0 1639, Wrought copper alloys - Extruded sections -
Mechanical properties.
Type 1 : Non-heat-treatable alloys of high conductivity
and medium hardness, the wrought forms of which are
IS0 1640, Wrought copper alloys - Forgings - Mechanical
given their strengths by cold working during manu-
properties.
facture.
IS0 2713, Copper and copper alloys - Rockwell hardness
Type 2 : Alloys which are harder than type 1 and in
test (B, F and G scales).
which the mechanical properties have been developed
IS0 3486, Wrought copper and copper alloys - Cold-rolled by heat treatment during manufacture or by a combi-
nation of heat treatment and cold working.
flat products delivered in straight lengths (sheet) - Dimen-
sions and tolerances.’
Type 3 : Heat-treated alloys which have superior
mechanical properties to type 2 but a lower electrical
IS0 3487, Wrought copper and copper alloys - Cold-rolled
conductivity than either type 1 or type 2.
flat products in coils or on reels (strip) - Dimensions and
tolerances. 1 )
Type 4 : Alloys having certain specialized properties
which may, in some cases, be obtained either by cold
IS0 3488, Wrought copper and copper alloys - Extruded
round, square and hexagonal bars - Dimensions and working or by heat treatment. Alloys of this type are
not necessarily interchangeable with each other.
tolerances. 1 )
1) At present at the stage of draft.
1

---------------------- Page: 3 ----------------------
IS0 5182-1978 (E)
4.2 Group B - Sintered materials welding, and their properties are therefore different from those of
materials used for general purposes. For certain of these alloys,
This group comprises six types of material based upon the
information on tensile strength, 0,2 % proof stress and elongations
may be obtained if required from the following IS0 publications
constituents used :
for mechanical properties of coppers and copper alloys : IS0 1634,
IS0 1637, IS0 1639, IS0 1640.
Types 10 and 11 : Sintered products of copper and
tungsten.
5.4 Electrical properties
Type 12 : A sintered product of copper and tungsten
carbide. Electrical conductivities of materials shall be not less than
those given in table 2.
Type 13 : A sintered and worked product of molyb-
denum.
6 METHODS OF TEST
Type 14 : A sintered and worked product of tungsten.
6.1 The Vickers hardness test with 30 kg load shall be
Type 15 : A sintered product of silver and tungsten.
carried out in accordance with ISO/R 399.
5 SPECIFICATION
6.2 The electrical properties shall be measured in
accordance with IEC publication 468, where the size of the
5.1 Requirements sample permits. When it is not possible to use this method,
the test shall be carried out as agreed between the supplier,
The materials shall comply with the required characteristics
the purchaser and a mutually acceptable arbitrator.
set out in table 2.
6.3 Hardness and conductivity tests normally guarantee
5.2 Chemical composition
the quality of the material and allow verification of the
softening temperature. The softening temperature test is
The compositions and maximum impurities for some of the
not normally carried out on each batch of material.
materials are standardized in the IS0 publications listed
in table 1.
Pending the finalization of a standard method for carrying
out the softening temperature test, the test can only be
TABLE 1 - IS0 p
...

NORME INTERNATIONALE 5182
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION*MEWYHAPOLlHAR OPrAHHJAUHR no CTAHAAPTH3AUMH.ORGANlSATlON INTERNATIONALE DE NORMALISATION
a
ril) Matériaux pour électrodes de soudage par résistance et
équipements annexes
Materials for resistance welding electrodes and ancillary equipment
Première édition - 1978-1 1-15
a
IL
-
Réf. no : IS0 5182-1978 (F)
CDU 621,791,037
R
z
Descripteurs : soudage, électrode de soudage par résistance, cuivre, alliage de cuivre, produit fritte, spécification de matière, résistivité,
N
s- dureté, utilisation, marquage.
v>
8
Prix basé sur 6 pages

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont
soumis aux comités membres pour approbation, avant leur acceptation comme
le Conseil de I'ISO.
Normes internationales par
La Norme internationale IS0 5182 a été élaborée par le comité technique
ISO/TC 44, Soudure, et a été soumise aux comités membres en septembre 1976.
Les comités membres des pays suivants l'ont approuvée :
Afrique du Sud, Rép. d' France Philippines
Allemagne, R.F. Inde Portugal
Belgique Israël Roumanie
Canada Italie
Suède
Corée, Rép. de Mexique
Suisse
Danemark Norvège
U.S.A.
Espagne Nouvelle-Zélande
Yougoslavie
Finlande Pays-Bas
Le comité du pays suivant l'a désapprouvée pour des
membre raisons techniques :
Royaume-Uni
O Organisation internationale de normalisation, 1978 O
Imprimé en Suisse

---------------------- Page: 2 ----------------------
~~
IS0 5182-1978 (F)
NORME INTERNATIONALE
Matériaux pour électrodes de soudage par résistance et
équipements annexes
e
1 OBJET ET DOMAINE D’APPLICATION IS0 3487, Cuivre et alliages de cuivre corroyés - Produits
plats laminés à froid livrés sur bobines ou en couronnes
La présente Norme internationale spécifie les caractéris-
- Dimensions et tolérances. ’
(bandes)
tiques des matériaux conducteurs pour électrodes de
IS0 3488, Cuivre et alliages de cuivre corroyés - Barres
soudage par résistance et équipements annexes pour le
transport du courant et pour transmettre l‘effort de tréfilées de section circulaire, carrée ou hexagonale -
soudage. Dimensions et tolérances.‘ )
IS0 3489, Cuivre et alliages de cuivre corroyés - Barres
étirées de section circulaire - Dimensions et tolérances.‘
2 RÉFÉRENCES
IS0 3490. Cuivre et alliages de cuivre corroyés - Barres
ISOIR 399, Essai de dureté Vickers pour le cuivre et les
alliages de cuivre (Charges d’essai comprises entre 2,5 et étirées de section hexagonale - Dimensions et tolérances.’ 1
50 kgf).
IS0 3491, Cuivre et alliages de cuivre corroyés - Barres
ISOIR 403, Essai de dureté Brinell pour le cuivre et les étirées de section carrée - Dimensions et tolérances.’ ’
alliages de cuivre.
IS0 3492, Cuivre et alliages de cuivre corroyés - Fils étirés
IS0 428, Alliages cuivre-aluminium corroyés - Composi- de section circulaire - Dimensions et tolérances.‘ )
tion chimique et formes des produits corroyés.
Publication CE1 468, Méthode de mesure de la résistivité
ISOIR 1187, Alliages de cuivre spéciaux corroyés. des matériaux métalliques.
a
ISOIR 1336, Cuivres alliés corroyés.
3 DÉFINITION
ISOIR 1337, Cuivres corroyés.
Dans le cadre de la présente Norme internationale, la défini-
IS0 1634, Cuivre et alliages de cuivre corroyés - Produits
tion suivante est applicable :
laminés plats (plaques, tôles, bandes) - Caractéristiques
mécaniques.
température d’amolissement : Valeur maximale de tempé-
rature qui, lorsqu‘elle est maintenue durant 2 h, provoque
IS0 1637, Cuivre et alliages de cuivre corroyés - Produits
une réduction maximale de 15 % de la valeur de dureté, à
pleins livrés en longueurs droites - Caractéristiques méca-
la température ambiante.
niques.
IS0 1639, Alliages de cuivre corroyés - Profilés filés -
4 CLASSIFICATION
Caractéristiques mécaniques.
4.1 Groupe A - Cuivre et alliages de cuivre
IS0 1640, Alliages de cuivre corroyés - Pièces forgées -
Caractéristiques mécaniques.
Le présent paragraphe définit quatre types de matériaux,
à savoir :
IS0 2713, Cuivre et alliages de cuivre - Essai de dureté
GI.
Rockwell (Echelles B, F,
Type 1 : Alliages ne pouvant subir de traitement ther-
mique, à conductivité élevée, et de dureté, dont les
IS0 3486, Cuivre et alliages de cuivre corroyés - Produits
formes corroyées acquièrent leur résistance par écrouis-
plats laminés à froid livrés en longueurs droites (tôles) -
sage pendant la mise en œuvre.
Dimensions et tolérances. ’
1) Actuellement au stade de projet.
1

---------------------- Page: 3 ----------------------
' IS0 5182-1978 (FI
Type 2 : Alliages plus durs que le type 1, dont les pro- 5.3 Propriétés mécaniques
priétés mécaniques sont renforcées par un traitement
La dureté des matériaux ne pas être inférieure à la
thermique pendant la mise en œuvre ou par la combi-
valeur donnée dans le tableau
naison d'un traitement thermique et d'un écrouissage.
NOTE - Ces matériaux sont
Type 3 : Alliages traités thermiquement ayant les pro-
priétés mécaniques supérieures à celles du type 2, mais
une conductivité inférieure à celle des types 1 et 2.
Type 4 : Alliages possédant certaines propriétés spéciales
obtenues dans certains cas, soit par écrouissage, soit par
IS0 1639 et IS0 1640.
traitement thermique. Ces alliages ne sont pas forcément
interchangeables avec les autres.
5.4 Propriétés électriques
4.2 Groupe B - Matériaux frittés
a
La conductivité électrique deq matériaux ne doit pas être
Ce groupe comprend six types de matériaux suivant les
constituants employés :
Types 10 et 11 : Produits frittés à base de cuivre et de 6 MÉTHODES D'ESSAI
tungstène.
Type 12 : Produit fritté à base de cuivre et de carbure
de tungstène.
Type 13 : Produit fritté à base de molybdène.
Type 14 : Produit fritté à base de tungstène.
Type 15 : Produit fritté à base d'argent et de tungstène.
5 SP~CIFICATIONS
5.1 Exigences
Les matériaux doivent répondre aux exigences indiquées lot de matériau.
a
dans le tableau 2.
5.2 Composition chimique
fournisseur et l'acheteur.
Les compositions et teneurs maximales en impuretés de
certains matériaux sont normalisées dans les publications
IS0 énumérées dans le tableau 1, 7 MARQUAGE
TABLEAU 1 - Publications IS0 relatives à la composition
Les matériaux doivent être repérés par leur groupe, leur
I chimique
type et un numéro (voir tableau 2).
Désignation Publication IS0 Exemples : Cu Crl doit être ré éré par A 211 - IS0 5182.
r
W75 Cu doit être r péré par B 10 - IS0 5182.
CU-ETP ISO/R 1337
Cu cdl lSO/R 1336
8 APPLICATION
Cu Crl ISO/R 1336
1
Voir l'annexe A pour des exemples types d'application.
Cu Co2 Be ISO/R 1187
Cu Ni2 Si ISOIR 1187
Cu Be2 Co Ni lSO/R 1187
9 CONVERSION DES VALEURS DE DURETÉ
Cu All0 Fe5 N
...