ISO 3107:2022

Dentistry — Zinc oxide-eugenol cements and non-eugenol zinc oxide cements

This document specifies requirements for zinc oxide-eugenol cements suitable for use in restorative dentistry for temporary cementation, for bases and as temporary restorations. This document also specifies requirements for non-eugenol zinc oxide cements containing zinc oxide and oil(s) other than eugenol for temporary cementation.

Médecine bucco-dentaire — Ciments à l’oxyde de zinc-eugénol et à l'oxyde de zinc sans eugénol

Le présent document définit les exigences des ciments à l’oxyde de zinc-eugénol, destinés à être utilisés en médecine bucco-dentaire restauratrice pour scellement temporaire, fonds de cavité et bases, et comme restauration temporaire. Le présent document définit également les exigences des ciments à l'oxyde de zinc sans eugénol contenant de l’oxyde de zinc et une ou des huiles autres que l’eugénol pour scellement temporaire.

General Information

• Status: Published
• Publication Date: 14-Sep-2022
• ICS: 11.060.10 - Dental materials
• Technical Committee: ISO/TC 106/SC 1 - Filling and restorative materials
• Drafting Committee: ISO/TC 106/SC 1 - Filling and restorative materials
• Current Stage: 6060 - International Standard published
• Start Date: 15-Sep-2022
• Due Date: 03-Jun-2023
• Completion Date: 15-Sep-2022

Relations

• Revises: ISO 3107:2011 - Dentistry — Zinc oxide/eugenol cements and zinc oxide/non-eugenol cements
• Effective Date: 06-Jun-2022
• Consolidates: ISO 37162:2020 - Smart community infrastructures — Smart transportation for newly developing areas
• Effective Date: 06-Jun-2022

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 3107
Fifth edition
2022-09
Dentistry — Zinc oxide-eugenol
cements and non-eugenol zinc oxide
cements
Médecine bucco-dentaire — Ciments à l’oxyde de zinc-eugénol et à
l'oxyde de zinc sans eugénol
Reference number
ISO 3107:2022(E)
© ISO 2022

---------------------- Page: 1 ----------------------
ISO 3107:2022(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2022
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
  © ISO 2022 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 3107:2022(E)
Contents Page
Foreword .iv
Introduction .v
1 S c op e . 1
2 Nor m at i ve r ef er enc e s . 1
3 Terms and definitions . 1
4 Classification . 1
5 R e qu i r ement s . 1
5.1 P erformance requirements . 1
5.2 B iocompatibility . 2
6 S a mpl i n g . 2
7 Te s t me t ho d s . 2
7.1 P reparation of test specimens . 2
7.1.1 A mbient c ond it ion s . 2
7.1.2 P rocedure for mixing . 2
7.2 D etermination of setting time . 2
7.2.1 A pparatus . 2
7.2.2 Procedure . 3
7.2.3 Treatment of results . 3
7.3 D etermination of compressive strength . 3
7.3.1 Apparatus . 3
7.3.2 Preparation of test specimens . 5
7.3.3 P rocedure . 5
7.3.4 Treatment of results . 6
7.4 D etermination of film thickness . 6
7.4.1 Apparatus . 6
7.4.2 Procedure . 6
7.4.3 T reatment of results . 6
7.5 D etermination of acid-soluble arsenic fraction . 7
7.5.1 Preparation of test sample . 7
7.5.2 P rocedure . 8
7.5.3 C ompliance . 8
8 Marking, labelling and packaging .8
8.1 Packaging . 8
8.2 M arking and instructions for use . 8
Bibliography .10
iii
© ISO 2022 – All rights reserved

---------------------- Page: 3 ----------------------
ISO 3107:2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 106, Dentistry, Subcommittee SC 1, Filling
and restorative materials, in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 55, Dentistry, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This fifth edition cancels and replaces the fourth edition (ISO 3107:2011), of which it constitutes a
minor revision.
— replace “zinc oxide/eugenol cement” with “zinc oxide-eugenol cement”,
— replace “non-eugenol cement” with “non-eugenol zinc oxide cement”, and
— replace “aromatic oils” with “oil(s) other than eugenol”.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
  © ISO 2022 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 3107:2022(E)
Introduction
Specific qualitative and quantitative requirements for freedom from biological hazard are not included
in this document, but it is intended that in assessing possible biological or toxicological hazards,
reference be made to ISO 10993-1 and ISO 7405.
v
© ISO 2022 – All rights reserved

---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 3107:2022(E)
Dentistry — Zinc oxide-eugenol cements and non-eugenol
zinc oxide cements
1 S cope
This document specifies requirements for zinc oxide-eugenol cements suitable for use in restorative
dentistry for temporary cementation, for bases and as temporary restorations.
This document also specifies requirements for non-eugenol zinc oxide cements containing zinc oxide
and oil(s) other than eugenol for temporary cementation.
2 Normat ive references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 1942, Dentistry — Vocabulary
ISO 2590, General method for the determination of arsenic — Silver diethyldithiocarbamate photometric
method
ISO 3696:1987, Water for analytical laboratory use — Specification and test methods
ISO 8601-1, Date and time — Representations for information interchange — Part 1: Basic rules
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 1942 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Classification
For the purposes of this document, the following classification for cements is used, based on their
intended use:
a) Type I: for temporary cementation;
b) Type II: for bases and temporary restorations.
5 Requirements
5.1 Performance requirements
When tested in accordance with the appropriate test methods specified in Clause 7, Type I and Type II
cements shall comply with the performance requirements specified in Table 1.
1
© ISO 2022 – All rights reserved

---------------------- Page: 6 ----------------------
ISO 3107:2022(E)
Table 1 — Requirements
Type Setting time at 37 °C Compressive strength Film thickness Acid-soluble arsenic
at 24 h mass fraction
a
min MPa µm mg/kg
minimum maximum minimum maximum maximum maximum
Type I 1,5 10 35 25 2
Type II 1,5 10 5 N/A 2
N/A: not applicable
a
mg/kg is the equivalent of ppm; ppm is a deprecated unit.
5.2 Biocompatibility
For guidance on biocompatibility, see ISO 10993-1 and ISO 7405.
6 S ampling
The test sample shall consist of packages prepared for retail sale from the same batch containing
enough material to carry out the specified tasks plus an allowance for repeats. 50 g should be sufficient.
7 Test methods
7.1 Pr eparation of test specimens
Prepare the test material in accordance with the manufacturer's instructions (see 8.2).
7.1.1 Ambient conditions
Prepare and test all specimens at (23 ± 2) °C and a relative humidity of (50 ± 5) %. Before the start of
mixing, condition the test samples and apparatus in these conditions f
...

NORME ISO
INTERNATIONALE 3107
Cinquième édition
2022-09
Médecine bucco-dentaire — Ciments à
l’oxyde de zinc-eugénol et à l'oxyde de
zinc sans eugénol
Dentistry — Zinc oxide-eugenol cements and non-eugenol zinc oxide
cements
Numéro de référence
ISO 3107:2022(F)
© ISO 2022

---------------------- Page: 1 ----------------------
ISO 3107:2022(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2022
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
  © ISO 2022 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 3107:2022(F)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 1
4 Classification . 1
5 Exigences . 2
5.1 Exigences de performance . 2
5.2 Biocompatibilité . 2
6 Échantillonnage .2
7 Méthodes d’essai . 2
7.1 Préparation des éprouvettes . 2
7.1.1 Conditions ambiantes . 2
7.1.2 Mode opératoire utilisé pour le mélange . 2
7.2 Détermination du temps de prise . 2
7.2.1 Appareillage. 2
7.2.2 Mode opératoire . . 3
7.2.3 Traitement des résultats . 4
7.3 Détermination de la résistance à la compression . 4
7.3.1 Appareillage. 4
7.3.2 Préparation des éprouvettes . 5
7.3.3 Mode opératoire . . 6
7.3.4 Traitement des résultats . 6
7.4 Détermination de l’épaisseur du film . 7
7.4.1 Appareillage. 7
7.4.2 Mode opératoire . . 7
7.4.3 Traitement des résultats . 7
7.5 Détermination d’une fraction acido-soluble d’arsenic . 8
7.5.1 Préparation de l’échantillon pour essai . 8
7.5.2 Mode opératoire . . 9
7.5.3 Conformité . 9
8 Marquage, étiquetage et emballage.9
8.1 Emballage . 9
8.2 Marquage et instructions d’utilisation . 9
Bibliographie .11
iii
© ISO 2022 – Tous droits réservés

---------------------- Page: 3 ----------------------
ISO 3107:2022(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 106, Médecine bucco-dentaire, sous-
comité SC 1, Produits pour obturation et restauration, en collaboration avec le comité technique CEN/
TC 55, Médecine bucco-dentaire, du Comité européen de normalisation (CEN), conformément à l’accord
de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette cinquième édition annule et remplace la quatrième édition (ISO 3107:2011), dont elle constitue
une révision mineure.
— remplacer «ciments à base d'oxyde de zinc-eugénol» par «ciments à l'oxyde de zinc-eugénol»,
— remplacer «ciments sans eugénol» par «ciments à l'oxyde de zinc sans eugénol», et
— remplacer «des huiles aromatiques destinés à un scellement temporaire» par «une ou des huiles
autres que l’eugénol pour scellement temporaire».
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.html.
iv
  © ISO 2022 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO 3107:2022(F)
Introduction
Les exigences qualitatives et quantitatives spécifiques à l’élimination de risques biologiques ne sont pas
incluses dans la présente Norme internationale, mais il est recommandé, lors de l’évaluation des risques
biologiques ou toxicologiques éventuels, de se référer à l’ISO 10993-1 et l’ISO 7405.
v
© ISO 2022 – Tous droits réservés

---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 3107:2022(F)
Médecine bucco-dentaire — Ciments à l’oxyde de zinc-
eugénol et à l'oxyde de zinc sans eugénol
1 Domaine d’application
Le présent document définit les exigences des ciments à l’oxyde de zinc-eugénol, destinés à être utilisés
en médecine bucco-dentaire restauratrice pour scellement temporaire, fonds de cavité et bases, et
comme restauration temporaire.
Le présent document définit également les exigences des ciments à l'oxyde de zinc sans eugénol
contenant de l’oxyde de zinc et une ou des huiles autres que l’eugénol pour scellement temporaire.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s’applique (y compris les
éventuels amendements).
ISO 1942, Médecine bucco-dentaire — Vocabulaire
ISO 2590, Méthode générale de dosage de l’arsenic — Méthode photométrique au diéthyldithiocarbamate
d’argent
ISO 3696:1987, Eau pour laboratoire à usage analytique — Spécification et méthodes d'essai
ISO 8601-1, Date et heure — Représentations pour l'échange d'information — Partie 1: Règles de base
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 1942 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp/ ui/ fr/
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
4 Classification
Pour les besoins du présent document, la classification suivante des ciments est utilisée, en fonction de
leur utilisation prévue:
a) Type I: pour scellement temporaire;
b) Type II: pour bases et restaurations temporaires.
1
© ISO 2022 – Tous droits réservés

---------------------- Page: 6 ----------------------
ISO 3107:2022(F)
5 Exigences
5.1 Exigences de performance
Lorsqu’ils sont soumis à essai conformément aux méthodes d’essai appropriées indiquées dans l’Article 7,
les ciments de types I et II doivent être conformes aux exigences de performance spécifiées dans le
Tableau 1.
Tableau 1 — Exigences
Type Temps de prise à 37 ºC Résistance à la compres- Épaisseur du Fraction acido-so-
sion après 24 h film luble d’arsenic
a
min MPa µm mg/kg
minimum maximum minimum maximum maximum maximum
Type I 1,5 10 35 25 2
Type II 1,5 10 5 N/A 2
N/A: non applicable
a
mg/kg est équivalent à ppm; le ppm est déconseillé.
5.2 Biocompatibilité
Pour des recommandations sur la biocompatibilité, voir l’ISO 10993-1 et l’ISO 7405.
6 Échantillonnage
L’échantillon pour essai doit comporter les conditionnements préparés à partir d’un même lot pour
la vente au détail et contenant suffisamment de matériau pour effectuer les tâches spécifiées tout en
prévoyant une marge pour la répétition des essais. Il convient que 50 g soient suffisants.
7 Méthodes d’essai
7.1 Préparation des éprouvettes
Préparer le matériau d’essai conformément aux instructions du fabricant (voir 8.2).
7.1.1 Conditions ambiantes
Préparer et soumettre à essai toutes les éprouvettes à une température de (23 ± 2) °C et à une humidité
relative de (50 ± 5) %. Avant de commencer le mélange, conditionner les éprouvettes et l’appareillage
dans ces conditions pendant au moins 1 h.
7.1.2 Mode opératoire utilisé pour le mélange
Mélanger une quantité de ciment suffisante pour garantir que la préparation de chaque éprouvette est
effectuée à partir d’un seul mélange. Préparer un nouveau mélange pour chaque éprouvette.
7.2 Détermination du temps de prise
7.2.1 Appareillage
7.2.1.1 Enceinte, pouvant être maintenue à une température de (37 ± 1) °C et à une humidité relative
de (95 ± 5) %.
2
  © ISO 2022 – Tous droits réservés

---------------------- Page: 7 ----------------------
ISO 3107:2022(F)
7.2.1.2 Pénétromètre à aiguille
7.2.1.2.1 Pour les matériaux de type I, un pénétromètre à aiguille d’une masse de (100 ± 0,5) g, avec
une aiguille à pointe cylindrique, d’une longueur d’environ 5 mm et dont le diamètre de l’extrémité plate
est de (2,0 ± 0,1) mm.
7.2.1.2.2 Pour les matériaux de type II, un pénétromètre à aig
...

ISO/TC 106/SC 1
Date: 2022-03-2125
ISO/FDIS 3107:2022(E)
ISO/TC 106/SC 1
Secretariat: AFNOR
Dentistry — Zinc oxide/eugenol cements and zinc oxide/non-eugenol cements
Médecine bucco-dentaire — Ciments dentaires à base d'oxyde de zinc-eugénol et à base
d'oxyde de zinc sans eugénol

---------------------- Page: 1 ----------------------
ISO/FDIS 3107:2022(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2022
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of
this publication may be reproduced or utilized otherwise in any form or by any means, electronic or
mechanical, including photocopying, or posting on the internet or an intranet, without prior written
permission. Permission can be requested from either ISO at the address below or ISO’sISO's member body
in the country of the requester.
ISO Copyright Office
Ch. de Blandonnet 8 • CP 401 • CH-1214 Vernier, Geneva , Switzerland
Tel. Phone: + 41 22 749 01 11
Email: [e-mail] + 41 22 749 09 47
[e-mail]
www.iso.org

Website: www.iso.org
Published in Switzerland.
© ISO 2022 – All rights reserved
ii

---------------------- Page: 2 ----------------------
ISO/FDIS 3107:2022(E)
Contents Page
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Classification . 1
5 Requirements . 2
5.1 Performance requirements . 2
5.2 Biocompatibility. 2
6 Sampling . 2
7 Test methods . 2
7.1 Preparation of test specimens . 2
7.1.1 Ambient conditions . 2
7.1.2 Procedure for mixing . 2
7.2 Determination of setting time . 3
7.2.1 Apparatus . 3
7.2.2 Procedure . 3
7.2.3 Treatment of results . 4
7.3 Determination of compressive strength . 4
7.3.1 Apparatus . 4
7.3.2 Preparation of test specimens . 5
7.3.3 Procedure . 6
7.3.4 Treatment of results . 6
7.4 Determination of film thickness . 6
7.4.1 Apparatus . 6
7.4.2 Procedure . 7
7.4.3 Treatment of results . 7
7.5 Determination of acid-soluble arsenic fraction . 8
7.5.1 Preparation of test sample . 8
7.5.2 Procedure . 9
7.5.3 Compliance . 9
8 Marking, labelling and packaging . 9
8.1 Packaging . 9
8.2 Marking and instructions for use . 9
Bibliography . 11
© ISO 2022 – All rights reserved
iii

---------------------- Page: 3 ----------------------
ISO/FDIS 3107:2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any
patent rights identified during the development of the document will be in the Introduction and/or on
the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the World
Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 106, Dentistry, Subcommittee SC 1, Filling
and restorative materials, in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 55, Dentistry, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This fifth edition cancels and replaces the fourth edition (ISO 3107:2011), which has been editorially
revised to keep the consistency of the “Terms and definitions” defined in ISO 1942. The changes
compared to the previous edition are as follows:of which it constitutes a minor revision.
— replace "“zinc oxide/eugenol cement"” with "“zinc oxide-eugenol cement",”,
— replace "“non-eugenol cement"” with "“non-eugenol zinc oxide cement",”, and,
— replace "“aromatic oils"” with "“oil(s) other than eugenol".”.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
© ISO 2022 – All rights reserved
iv

---------------------- Page: 4 ----------------------
ISO/FDIS 3107:2022(E)
Introduction
Specific qualitative and quantitative requirements for freedom from biological hazard are not included
in this document, but it is intended that in assessing possible biological or toxicological hazards, reference
be made to ISO 10993-1 and ISO 7405.
© ISO 2022 – All rights reserved
v

---------------------- Page: 5 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 3107:2022(E)

Dentistry — Zinc oxide/eugenol cements and zinc oxide/non-
eugenol cements
1 Scope
This document specifies requirements for zinc oxide-eugenol cements suitable for use in restorative
dentistry for temporary cementation, for bases and as temporary restorations.
This document also specifies requirements for non-eugenol zinc oxide cements containing zinc oxide and
oil(s) other than eugenol for temporary cementation.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 1942, Dentistry — Vocabulary
ISO 2590, General method for the determination of arsenic — Silver diethyldithiocarbamate photometric
method
ISO 3696:1987, Water for analytical laboratory use — Specification and test methods
ISO 8601-1, Date and time — Representations for information interchange — Part 1: Basic rules
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 1942 apply.
ISO and IEC maintain terminologicalterminology databases for use in standardization at the following
addresses:
— ISO Online browsing platform: available at https://www.iso.org/obp
— IEC Electropedia: available at https://www.electropedia.org/
4 Classification
For the purposes of this document, the following classification for cements is used, based on their
intended use:
a) Type I: for temporary cementation;
b) Type II: for bases and temporary restorations.
© ISO 2022 – All rights reserved
1

---------------------- Page: 6 ----------------------
ISO/FDIS 3107:2022(E)
5 Requirements
5.1 Performance requirements
When tested in accordance with the appropriate test methods specified in Clause 7, Type I and Type II
cements shall comply with the performance requirements specified in Table 1.
Table 1 — Requirements
Type Setting time at 37 °C Compressive strength Film thickness Acid-soluble arsenic
at 24 h mass fraction
a
 min MPa µm mg/kg

min.mini max.maxi min.minim max.maxi max.maximum max.maximum
mum mum um mum
Type I 1,5 10  35 25 2
Type II 1,5 10 5  N/A 2
N/A: not applicable
a
mg/kg is the equivalent of ppm; ppm is a deprecated unit.
5.2 Biocompatibility
For guidance on biocompatibility, see ISO 10993-1 and ISO 7405.
6 Sampling
The test sample shall consist of packages prepared for retail sale from the same batch containing enough
material to carry out the specified tasks plus an allowance for repeats. 50 g should be sufficient.
7 Test methods
7.1 Preparation of test specimens
Prepare the test material in accordance with the manufacturer's instructions (see 8.2).
7.1.1 Ambient conditions
Prepare and test all specimens at (23 ±± 2) °C and a relative humidity of (50 ±± 5) %. Before the start of
mixing, condition the test samples and apparatus in these conditions for at least 1 h.
7.1.2 Procedure for mixing
Mix sufficient cement to ensure that the preparation of each specimen is completed from one mix. Prepare
a fresh mix for each specimen.
7.2 Determination of setting time
7.2.1 Apparatus
7.2.1.1 Cabinet, capable of being maintained at a temperature of (37 ±± 1) °C and a relative humidity of
(95 ±± 5) %.
7.2.1.2 Indenter needle
© ISO 2022 – All rights reserved
2

---------------------- Page: 7 ----------------------
ISO/FDIS 3107:2022(E)
7.2.1.2.1 For Type I materials, an indenter needle of mass (100 ±± 0,5) g with a tip which is cylindrical
for a distance of approximately 5 mm and has a flat end of diameter (2,0 ±± 0,1) mm.
7.2.1.2
...

FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 3107
ISO/TC 106/SC 1
Dentistry — Zinc oxide/eugenol
Secretariat: AFNOR
cements and zinc oxide/non-eugenol
Voting begins on:
2022-05-23 cements
Voting terminates on:
Médecine bucco-dentaire — Ciments dentaires à base d'oxyde de zinc-
2022-08-15
eugénol et à base d'oxyde de zinc sans eugénol
ISO/CEN PARALLEL PROCESSING
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 3107:2022(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
NATIONAL REGULATIONS. © ISO 2022

---------------------- Page: 1 ----------------------
ISO/FDIS 3107:2022(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2022
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
  © ISO 2022 – All rights reserved

---------------------- Page: 2 ----------------------
ISO/FDIS 3107:2022(E)
Contents Page
Foreword .iv
Introduction .v
1 S c op e . 1
2 Nor m at i ve r ef er enc e s . 1
3 Terms and definitions . 1
4 Classification . 1
5 R e qu i r ement s . 1
5.1 P erformance requirements . 1
5.2 B iocompatibility . 2
6 S a mpl i n g . 2
7 Te s t me t ho d s . 2
7.1 P reparation of test specimens . 2
7.1.1 A mbient c ond it ion s . 2
7.1.2 P rocedure for mixing . 2
7.2 D etermination of setting time . 2
7. 2 .1 A pp a r at u s . 2
7. 2 . 2 P r o c e du r e . 3
7.2.3 Treatment of results . 3
7.3 D etermination of compressive strength . 3
7. 3 .1 A pp a r at u s . 3
7.3.2 Preparation of test specimens . 5
7. 3 . 3 P r o c e du r e . 5
7.3.4 Treatment of results . 6
7.4 D etermination of film thickness . 6
7.4 .1 A pp a r at u s . 6
7.4 . 2 P r o c e du r e . 6
7.4.3 T reatment of results . 6
7.5 Determination of acid-soluble arsenic fraction . 7
7.5.1 Preparation of test sample . 7
7. 5 . 2 P r o ce du r e . 8
7. 5 . 3 C ompl i a nce . 8
8 Marking, labelling and packaging .8
8.1 Packaging . 8
8.2 M arking and instructions for use . 8
Bibliography .10
iii
© ISO 2022 – All rights reserved

---------------------- Page: 3 ----------------------
ISO/FDIS 3107:2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 106, Dentistry, Subcommittee SC 1, Filling
and restorative materials, in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 55, Dentistry, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This fifth edition cancels and replaces the fourth edition (ISO 3107:2011), of which it constitutes a
minor revision.
— replace “zinc oxide/eugenol cement” with “zinc oxide-eugenol cement”,
— replace “non-eugenol cement” with “non-eugenol zinc oxide cement”, and
— replace “aromatic oils” with “oil(s) other than eugenol”.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
  © ISO 2022 – All rights reserved

---------------------- Page: 4 ----------------------
ISO/FDIS 3107:2022(E)
Introduction
Specific qualitative and quantitative requirements for freedom from biological hazard are not included
in this document, but it is intended that in assessing possible biological or toxicological hazards,
reference be made to ISO 10993-1 and ISO 7405.
v
© ISO 2022 – All rights reserved

---------------------- Page: 5 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 3107:2022(E)
Dentistry — Zinc oxide/eugenol cements and zinc oxide/
non-eugenol cements
1 S cope
This document specifies requirements for zinc oxide-eugenol cements suitable for use in restorative
dentistry for temporary cementation, for bases and as temporary restorations.
This document also specifies requirements for non-eugenol zinc oxide cements containing zinc oxide
and oil(s) other than eugenol for temporary cementation.
2 Normat ive references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 1942, Dentistry — Vocabulary
ISO 2590, General method for the determination of arsenic — Silver diethyldithiocarbamate photometric
method
ISO 3696:1987, Water for analytical laboratory use — Specification and test methods
ISO 8601-1, Date and time — Representations for information interchange — Part 1: Basic rules
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 1942 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Classification
For the purposes of this document, the following classification for cements is used, based on their
intended use:
a) Type I: for temporary cementation;
b) Type II: for bases and temporary restorations.
5 Requirements
5.1 Performance requirements
When tested in accordance with the appropriate test methods specified in Clause 7, Type I and Type II
cements shall comply with the performance requirements specified in Table 1.
1
© ISO 2022 – All rights reserved

---------------------- Page: 6 ----------------------
ISO/FDIS 3107:2022(E)
Table 1 — Requirements
Type Setting time at 37 °C Compressive strength Film thickness Acid-soluble arsenic
at 24 h mass fraction
a
min MPa µm mg/kg
minimum maximum minimum maximum maximum maximum
Type I 1,5 10 35 25 2
Type II 1,5 10 5 N/A 2
N/A: not applicable
a
mg/kg is the equivalent of ppm; ppm is a deprecated unit.
5.2 Biocompatibility
For guidance on biocompatibility, see ISO 10993-1 and ISO 7405.
6 S ampling
The test sample shall consist of packages prepared for retail sale from the same batch containing
enough material to carry out the specified tasks plus an allowance for repeats. 50 g should be sufficient.
7 Test methods
7.1 Pr eparation of test specimens
Prepare the test material in accordance with the manufacturer's instructions (see 8.2).
7.1.1 Ambient conditions
Prepare a
...

PROJET
NORME ISO/FDIS
FINAL
INTERNATIONALE 3107
ISO/TC 106/SC 1
Médecine bucco-dentaire — Ciments à
Secrétariat: AFNOR
l’oxyde de zinc-eugénol et à l'oxyde de
Début de vote:
2022-05-23 zinc sans eugénol
Vote clos le:
Dentistry — Zinc oxide-eugenol cements and non-eugenol zinc oxide
2022-08-15
cements
TRAITEMENT PARALLÈLE ISO/CEN
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/FDIS 3107:2022(F)
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
TION NATIONALE. © ISO 2022

---------------------- Page: 1 ----------------------
ISO/FDIS 3107:2022(F)
PROJET
NORME ISO/FDIS
FINAL
INTERNATIONALE 3107
ISO/TC 106/SC 1
Médecine bucco-dentaire — Ciments à
Secrétariat: AFNOR
l’oxyde de zinc-eugénol et à l'oxyde de
Début de vote:
2022-05-23 zinc sans eugénol
Vote clos le:
Dentistry — Zinc oxide-eugenol cements and non-eugenol zinc oxide
2022-08-15
cements
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2022
TRAITEMENT PARALLÈLE ISO/CEN
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
LES DESTINATAIRES DU PRÉSENT PROJET SONT
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
ISO copyright office
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
Tél.: [phone]
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
E-mail: [e-mail]
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/FDIS 3107:2022(F)
Web: www.iso.org
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
Publié en Suisse
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
ii
  © ISO 2022 – Tous droits réservés
TION NATIONALE. © ISO 2022

---------------------- Page: 2 ----------------------
ISO/FDIS 3107:2022(F)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 1
4 Classification . 1
5 Exigences . 2
5.1 Exigences de performance . 2
5.2 Biocompatibilité . 2
6 Échantillonnage .2
7 Méthodes d’essai . 2
7.1 Préparation des éprouvettes . 2
7.1.1 Conditions ambiantes . 2
7.1.2 Mode opératoire utilisé pour le mélange . 2
7.2 Détermination du temps de prise . 2
7.2.1 Appareillage. 2
7.2.2 Mode opératoire . . 3
7.2.3 Traitement des résultats . 4
7.3 Détermination de la résistance à la compression . 4
7.3.1 Appareillage. 4
7.3.2 Préparation des éprouvettes . 5
7.3.3 Mode opératoire . . 6
7.3.4 Traitement des résultats . 6
7.4 Détermination de l’épaisseur du film . 7
7.4.1 Appareillage. 7
7.4.2 Mode opératoire . . 7
7.4.3 Traitement des résultats . 7
7.5 Détermination d’une fraction acido-soluble d’arsenic . 8
7.5.1 Préparation de l’échantillon pour essai . 8
7.5.2 Mode opératoire . . 9
7.5.3 Conformité . 9
8 Marquage, étiquetage et emballage.9
8.1 Emballage . 9
8.2 Marquage et instructions d’utilisation . 9
Bibliographie .11
iii
© ISO 2022 – Tous droits réservés

---------------------- Page: 3 ----------------------
ISO/FDIS 3107:2022(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 106, Médecine bucco-dentaire, sous-
comité SC 1, Produits pour obturation et restauration, en collaboration avec le comité technique CEN/
TC 55, Médecine bucco-dentaire, du Comité européen de normalisation (CEN), conformément à l’accord
de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette cinquième édition annule et remplace la quatrième édition (ISO 3107:2011), dont elle constitue
une révision mineure.
— remplacer «ciments à base d'oxyde de zinc-eugénol» par «ciments à l'oxyde de zinc-eugénol»,
— remplacer «ciments sans eugénol» par «ciments à l'oxyde de zinc sans eugénol», et
— remplacer «des huiles aromatiques destinés à un scellement temporaire» par «une ou des huiles
autres que l’eugénol pour scellement temporaire».
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.html.
iv
  © ISO 2022 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO/FDIS 3107:2022(F)
Introduction
Les exigences qualitatives et quantitatives spécifiques à l’élimination de risques biologiques ne sont pas
incluses dans la présente Norme internationale, mais il est recommandé, lors de l’évaluation des risques
biologiques ou toxicologiques éventuels, de se référer à l’ISO 10993-1 et l’ISO 7405.
v
© ISO 2022 – Tous droits réservés

---------------------- Page: 5 ----------------------
PROJET FINAL DE NORME INTERNATIONALE ISO/FDIS 3107:2022(F)
Médecine bucco-dentaire — Ciments à l’oxyde de zinc-
eugénol et à l'oxyde de zinc sans eugénol
1 Domaine d’application
Le présent document définit les exigences des ciments à l’oxyde de zinc-eugénol, destinés à être utilisés
en médecine bucco-dentaire restauratrice pour scellement temporaire, fonds de cavité et bases, et
comme restauration temporaire.
Le présent document définit également les exigences des ciments à l'oxyde de zinc sans eugénol
contenant de l’oxyde de zinc et une ou des huiles autres que l’eugénol pour scellement temporaire.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s’applique (y compris les
éventuels amendements).
ISO 1942, Médecine bucco-dentaire — Vocabulaire
ISO 2590, Méthode générale de dosage de l’arsenic — Méthode photométrique au diéthyldithiocarbamate
d’argent
ISO 3696:1987, Eau pour laboratoire à usage analytique — Spécification et méthodes d'essai
ISO 8601-1, Date et heure — Représentations pour l'échange d'information — Partie 1: Règles de base
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 1942 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp/ ui/ fr/
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
4 Classification
Pour les besoins du présent document, la classification suivante des ciments est utilisée, en fonction de
leur utilisation prévue:
a) Type I: pour scellement temporaire;
b) Type II: pour bases et restaurations temporaires.
1
© ISO 2022 – Tous droits réservés

---------------------- Page: 6 ----------------------
ISO/FDIS 3107:2022(F)
5 Exigences
5.1 Exigences de performance
Lorsqu’ils sont soumis à essai conformément aux méthodes d’essai appropriées indiquées dans l’Article 7,
les ciments de types I et II doivent être conformes aux exigences de performance spécifiées dans le
Tableau 1.
Tableau 1 — Exigences
Type Temps de prise à 37 ºC Résistance à la compres- Épaisseur du Fraction acido-so-
sion après 24 h film luble d’arsenic
a
min MPa µm mg/kg
minimum maximum minimum maximum maximum maximum
Type I 1,5 10 35 25 2
Type II 1,5 10 5 N/A 2
N/A: non applicable
a
mg/kg est équivalent à ppm; le ppm est déconseillé.
5.2 Biocompatibilité
Pour des recommandations sur la biocompatibilité, voir l’ISO 10993-1 et l’ISO 7405.
6 Échantillonnage
L’échantillon pour essai doit comporter les conditionnements préparés à partir d’un même lot pour
la vente au détail et contenant suffisamment de matériau pour effectuer les tâches spécifiées tout en
prévoyant une marge pour la répétition des essais. Il convient que 50 g soient suffisants.
7 Méthodes d’essai
7.1 Préparation des éprouvettes
Préparer le matériau d’essai conformément aux instructions du fabricant (voir 8.2).
7.1.1 Conditions ambiantes
Préparer et soumettre à essai toutes les éprouvettes à une température de (23 ± 2) °C et à une humidité
relative de (50 ± 5) %. Avant de commencer le mélange, conditionner les éprouvettes et l’appareillage
dans ces conditions pendant au moins 1 h.
7.1.2 Mode opératoire utilisé pour le mélange
Mélanger une quantité de ciment suff
...