ISO 3303-1:2020

Rubber- or plastics-coated fabrics - Determination of bursting strength - Part 1: Steel-ball method

This document specifies a method for the determination of the bursting strength of rubber or plastics coated fabrics, using a mechanically operated steel ball.

Supports textiles revêtus de caoutchouc ou de plastique — Détermination de la résistance à l'éclatement — Partie 1: Méthode utilisant une bille d'acier

Le présent document spécifie une méthode de détermination de la résistance à l'éclatement des supports textiles revêtus de caoutchouc ou de plastique, au moyen d'une bille d'acier actionnée mécaniquement.

General Information

• Status: Published
• Publication Date: 15-Sep-2020
• ICS: 59.080.40 - Coated fabrics
• Technical Committee: ISO/TC 45/SC 4 - Products (other than hoses)
• Drafting Committee: ISO/TC 45/SC 4/WG 13 - Coated fabrics
• Current Stage: 9093 - International Standard confirmed
• Start Date: 10-Jun-2025
• Completion Date: 13-Dec-2025

Relations

• Consolidates: ISO 6546:2018 - Road vehicles - Collection of accident data for evaluation of occupant restraint performance
• Effective Date: 06-Jun-2022
• Revises: ISO 3303-1:2012 - Rubber- or plastics-coated fabrics - Determination of bursting strength - Part 1: Steel-ball method
• Effective Date: 03-Mar-2018

Overview

ISO 3303-1:2020 specifies the steel-ball method for determination of the bursting strength of rubber- or plastics-coated fabrics. The procedure reproduces an impact-type failure representative of service conditions and is especially useful for materials prone to necking (for example coated fabrics with knitted substrates). The method supports quality control, comparative testing and performance assessment.

Key Topics

• Principle: A test piece is clamped in rigid coaxial apertures and a polished steel ball is driven at a fixed speed against the specimen until rupture. Measured outputs are the rupturing force (newtons) and ball displacement (millimetres).
• Sample size and pieces: Five test pieces are taken across the usable width, avoiding edges and reused areas. The smaller test-piece dimension shall exceed the clamping diameter by at least 12 mm.
• Apparatus:
  • Power-driven testing machine with electronic force measurement and a crosshead displacement monitor (force system to class 2 of ISO 7500-1:2018).
  • Bursting attachment with internal ring diameter 45.0 mm ± 0.5 mm and a polished steel ball 25.20 mm ± 0.02 mm (alternative 38.00 mm ± 0.02 mm may be used but results might not be comparable).
  • Clamping surfaces grooved concentrically (groove spacing and depth specified in the standard).
  • Immersion equipment, distilled/deionized water, wetting agent and blotting paper for wet tests.
• Test parameters: Ball travel rate 300 mm/min ± 30 mm/min. Read force and displacement to the required accuracy (force in newtons, displacement to 0.1 mm as specified).
• Conditioning and timing: Conditioning atmospheres follow ISO 2231. Minimum interval between manufacture and testing is 16 h. Specific conditioning durations are given for single- and double-sided coatings.

Applications

This test is applied where a realistic, multidirectional measure of coated-fabric strength is needed. Typical uses include:

• Incoming quality control of coated fabrics for covers, tents, inflatable products and protective materials.
• Comparative performance assessment between formulations, coatings or substrate constructions.
• Evaluations where tensile tests are inadequate due to necking or multidirectional stress conditions.

Practical benefits:

• Reproducible measure of impact-rupture behaviour.
• Provides both force and displacement data useful for material specification and supplier acceptance.

Related Standards

• ISO 2231: Standard atmospheres for conditioning and testing (referenced for conditioning and testing atmospheres).
• ISO 7500-1:2018: Calibration and verification of force-measuring systems for uniaxial testing machines (force-measurement calibration requirements).

Test Report (required items)

The test report shall reference ISO 3303-1:2020 and include sample identification, conditioning method and atmosphere, test conditions, mean rupturing force and displacement (mean of five tests) and the test date.

For implementation, refer to the full ISO 3303-1:2020 text for apparatus drawings, detailed clamping groove dimensions, sampling notes and exact procedural tolerances.

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 3303-1
Second edition
2020-09
Rubber- or plastics-coated fabrics —
Determination of bursting strength —
Part 1:
Steel-ball method
Supports textiles revêtus de caoutchouc ou de plastique —
Détermination de la résistance à l'éclatement —
Partie 1: Méthode utilisant une bille d'acier
Reference number
©
ISO 2020
© ISO 2020
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii © ISO 2020 – All rights reserved

Contents Page
Foreword .iv
Introduction .vi
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus and reagents . 1
6 Sampling . 2
7 Preparation of test pieces . 3
8 Time-interval between manufacture and testing. 3
9 Atmosphere for conditioning and testing . 3
9.1 For conditioning . 3
9.2 For testing . 3
10 Procedure. 3
11 Test report . 4
Bibliography . 5
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso .org/
iso/ foreword .html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products,
Subcommittee SC 4, Products (other than hoses), in collaboration with the European Committee for
Standardization (CEN) Technical Committee CEN/TC 248, Textiles and textile products, in accordance
with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This second edition cancels and replaces the first edition (ISO 3303-1:2012), which has been technically
revised.
The main changes compared to the previous edition are as follows:
— in Clause 2, ISO 7500-1:2018 has been added for the calibration of force measurement system;
— the title of Clause 5 has been changed to “Apparatus and reagents”;
— reagents have been added to Clause 5;
— in 5.1, the testing machine has been changed to that of power driven, equipped with an electronic
force measurement system and an electronic crosshead displacement monitor.
— in 5.2 and bibliography, EN 12332-1 has been deleted as it was replaced with this document;
— in Figure 1, the round direction of clamp has been modified;
— in 5.6, blotting paper has been added;
— in 7.3, the preparation of wet test pieces has been specified.
— in 9.1, the recommendations on conditioning for fabrics coated on one side or on both sides have
been added separately;
— in 10.6, procedure for wet test pieces has been specified.
A list of all parts in the ISO 3303 series can be found on the ISO website.
iv © ISO 2020 – All rights reserved

Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/ members .html.
Introduction
The bursting strength of coated fabrics is often used as a measure of the multidirectional modulus of
the material, as opposed to tensile properties which only provide guidance to the coated-fabric strength
in one plane. In addition, bursting strength is more appropriate for testing materials prone to necking,
such as coated fabrics with knitted substrates.
The method described in this document, which employs a steel ball, is useful as it represents an impact
failure typical of one which would be experienced in s
...

NORME ISO
INTERNATIONALE 3303-1
Deuxième édition
2020-09
Supports textiles revêtus de
caoutchouc ou de plastique —
Détermination de la résistance à
l'éclatement —
Partie 1:
Méthode utilisant une bille d'acier
Rubber- or plastics-coated fabrics — Determination of bursting
strength —
Part 1: Steel-ball method
Numéro de référence
©
ISO 2020
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2020
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii © ISO 2020 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .vi
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 1
5 Appareillage et réactifs . 2
6 Échantillonnage . 3
7 Préparation des éprouvettes . 3
8 Délai entre la fabrication et l'essai . 3
9 Atmosphères de conditionnement et d'essai . 3
9.1 Conditionnement . 3
9.2 Essais . 4
10 Mode opératoire. 4
11 Rapport d'essai . 4
Bibliographie . 5
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/ directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/ brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l'intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l'Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/ iso/ fr/ avant -propos .html.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomères, sous-comité SC 4, Produits (autres que tuyaux), en collaboration avec le Comité européen
de normalisation (CEN), le comité technique CEN/TC 248, Textiles et produits textiles, conformément à
l'Accord de coopération technique entre l'ISO et le CEN (Accord de Vienne).
Cette deuxième édition annule et remplace la première édition (ISO 3303-1:2012), qui a fait l'objet d'une
révision technique.
Les principales modifications par rapport à l'édition précédente sont les suivantes:
— dans l’Article 2, l’ISO 7500-1:2018 a été ajoutée pour l'étalonnage des systèmes de mesure de la force;
— le titre de l’Article 5 a été modifié en « Appareillage et réactifs »;
— « réactifs » a été ajouté dans l’ Article 5;
— en 5.1, la machine d'essai a été changée en machine entraînée par un moteur et munie d'un système
électronique de mesure de la force et d'un dispositif de contrôle électronique de déplacement de
traverse;
— en 5.2 et dans la Bibliographie, l’EN 12332-1 a été supprimée, car elle a été remplacée par le présent
document;
— dans la Figure 1, le sens de l'arrondi de la mâchoire a été modifié;
— en 5.6, le papier buvard a été ajouté;
— en 7.3, la préparation des éprouvettes humides a été spécifiée;
iv © ISO 2020 – Tous droits réservés

— en 9.1, les recommandations de conditionnement des supports textiles revêtus d'un seul côté ou des
deux côtés a été ajoutée de manière séparée;
— en 10.6, le mode opératoire pour les éprouvettes humides a été spécifié.
Une liste de toutes les parties de la série ISO 3303 se trouve sur le site Web de l'ISO.
Il convient que l'utilisateur adresse tout retour d'information ou toute question concernant le présent
document à l'organisme national de normalisation de son pays.
Une liste exhaustive desdits organismes se trouve à l'adresse www .iso .org/ fr/ members .html.
Introduction
La résistance à l'éclatement des supports textiles revêtus est souvent utilisée pour mesurer le
comportement multidirectionnel du matériau, par opposition aux propriétés en traction qui donnent
uniquement des indications sur la résistance des supports textiles dans un seul plan. De plus, la
résistance à l'éclatement est plus adaptée aux essais portant sur des matériaux pouvant montrer une
tendance à la striction, comme les supports textiles revêtus produits à partir de structures tricotées.
La méthode décrite dans le présent document utilise une bille d'acier. Cette méthode permet de
provoquer une rupture similaire à celles qui peuvent se produire lors d'un impact en service.
vi © ISO 2020 – Tous droits réservés

NORME INTERNATIONALE ISO 3303-1:2020(F)
Supports textiles revêtus de caoutchouc ou de plastique —
Détermination de la résistance à l'éclatement —
Partie 1:
Méthode utilisant une bille d'
...