ISO 2361:2025

Electrodeposited nickel coatings on magnetic and non-magnetic substrates — Measurement of coating thickness — Magnetic method

This document specifies the method for non-destructive thickness measurement via the magnetic type of electrodeposited nickel coatings, also called “e-nickel”, on magnetic or non-magnetic substrates. It is possible that the method is not applicable to autocatalytic (electroless) nickel coatings, since these coatings are often non-magnetic due to their chemical composition. For the purposes of this document, two types of substrates are distinguished: a) nickel coatings on magnetic substrates (type A coatings); b) nickel coatings on non-magnetic substrates (type B coatings). Not all instruments are applicable to both types of coating. The effective measuring ranges of instruments using the principle of magnetic attraction are up to 50 µm for type A coatings and up to 25 µm for type B coatings. For instruments using the principle of reluctance, the effective ranges are much greater, up to 1 mm or even more. This method is applicable to both types of coatings.

Revêtements électrolytiques de nickel sur substrat magnétique et non magnétique — Mesurage de l’épaisseur du revêtement — Méthode magnétique

Le présent document spécifie une méthode de mesurage non destructif de l’épaisseur des revêtements électrolytiques de nickel de type magnétique, également appelés «e-nickel», sur substrat magnétique ou non magnétique. Il est possible que la méthode ne soit pas applicable à des revêtements autocatalytiques de nickel (nickelage chimique), car ces revêtements sont souvent non magnétiques du fait de leur composition chimique. Pour les besoins du présent document, on distingue deux types de substrats: a) les revêtements de nickel sur substrat magnétique (revêtements de type A); b) les revêtements de nickel sur substrat non magnétique (revêtements de type B). Tous les instruments ne peuvent pas être utilisés sur les deux types de revêtements. Les instruments basés sur le principe de l’attraction magnétique ont une plage de mesure efficace allant jusqu’à 50 µm dans le cas de revêtements de type A et allant jusqu’à 25 µm pour les revêtements de type B. Pour les instruments utilisant le principe de réluctance, la plage de mesure efficace est bien supérieure, jusqu’à 1 mm ou même plus. La présente méthode est applicable aux deux types de revêtements.

General Information

• Status: Published
• Publication Date: 26-Jun-2025
• ICS: 25.220.40 - Metallic coatings
• Technical Committee: ISO/TC 107 - Metallic and other inorganic coatings
• Drafting Committee: ISO/TC 107 - Metallic and other inorganic coatings
• Current Stage: 6060 - International Standard published
• Start Date: 27-Jun-2025
• Due Date: 13-Oct-2026
• Completion Date: 27-Jun-2025

Relations

• Consolidates: ISO 16404:2020 - Space systems — Programme management — Requirements management
• Effective Date: 11-Nov-2023
• Revises: ISO 2361:1982 - Electrodeposited nickel coatings on magnetic and non-magnetic substrates — Measurement of coating thickness — Magnetic method
• Effective Date: 11-Nov-2023

Standards Content (Sample)

International
Standard
ISO 2361
Third edition
Electrodeposited nickel coatings
2025-06
on magnetic and non-magnetic
substrates — Measurement of coating
thickness — Magnetic method
Revêtements électrolytiques de nickel sur substrat magnétique
et non magnétique — Mesurage de l’épaisseur du revêtement —
Méthode magnétique
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle of measurement . 2
5 Factors affecting the measuring accuracy . 2
5.1 Type A coatings: Nickel on a magnetic substrate .2
5.1.1 Magnetic properties of the basis metal .2
5.1.2 Basis metal thickness .3
5.1.3 Direction of mechanical working of the basis metal .3
5.1.4 Residual magnetism .3
5.2 Type B coatings: Nickel on a non-magnetic substrate, coating on the back of the
substrate .3
5.3 Type A and B coatings .3
5.3.1 Coating thickness .3
5.3.2 Edge effects .3
5.3.3 Curvature .3
5.3.4 Surface roughness .4
5.3.5 Magnetic fields .4
5.3.6 Foreign particles .4
5.3.7 Magnetic properties of the coating .4
5.3.8 Probe pressure and orientation .4
5.3.9 Base material thickness .4
6 Calibration of instruments . 4
6.1 General .4
6.2 Calibration standards .5
7 Procedure . 5
7.1 General .5
7.2 Basis metal thickness (type A coatings only) .5
7.3 Direction of mechanical working (type A coatings only) .5
7.4 Edge effects .5
7.5 Curvature .5
7.6 Number of readings .6
7.7 Residual magnetism (Type A coatings) .6
7.8 Surface cleanliness .6
7.9 Techniques .6
7.10 Positioning of the probe .6
7.11 Measuring on hot surfaces .6
7.12 Measuring underwater .7
8 Accuracy requirement . 7
9 Test report . 7
Bibliography . 8

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 107, Metallic and other inorganic coatings, in
collaboration with the European Committee for Standardization (CEN) Technical Committee CEN/TC 262,
Metallic and other inorganic coatings, including for corrosion protection and corrosion testing of metals and
alloys, in accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 2361:1982), which has been technically
revised.
The main changes are as follows:
— the nickel measuring methods were split into Type A, Type B and Type A and B;
— common measurement ranges were added for every method;
— subclauses on the factors that influence the measurement uncertainty were added;
— restructured and split into clauses and subclauses;
— Clause 9 on the test report was added;
— editorial changes were made.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
International Standard ISO 2361:2025(en)
Electrodeposited nickel coatings on magnetic and non-
magnetic substrates — Measurement of coating thickness —
Magnetic method
1 Scope
This document specifies the method for non-destructive thickness measurement via the magnetic type of
electrodeposited nickel coatings, also called “e-nickel”, on magnetic or non-magnetic substrates.
It is possible that the method is not applicable to autocatalytic (electroless) nickel coatings, since these
coatings are often non-magnetic due to their chemical composition.
For the purposes of this document, two types of substrates are distinguished:
a) nickel coatings on magnetic substrates (type A coatings);
b) nickel coatings on non-magnetic substrates (type B coatings).
Not all instruments are applicable to both types of coating.
The effective measuring ranges of instruments using the principle of magnetic attraction are up to 50 µm
for type A coatings and up to 25 µm for type B coatings.
For instruments using the principle of reluctance, the effective ranges are much greater, up to 1 mm or even
more. This method is applicable to both types of coatings.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 1463, Metallic and oxide coatings — Measurement of coating thickness — Microscopical method
ISO 2064, Metallic and other inorganic coatings — Definitions and conventions concerning the measurement of
thickness
ISO 2177, Metallic coatings — Measurement of coating thickness — Coulometric method by anodic dissolution
3 Terms and definitions
For the purposes of t
...

Norme
internationale
ISO 2361
Troisième édition
Revêtements électrolytiques de
2025-06
nickel sur substrat magnétique
et non magnétique — Mesurage
de l’épaisseur du revêtement —
Méthode magnétique
Electrodeposited nickel coatings on magnetic and non-
magnetic substrates — Measurement of coating thickness —
Magnetic method
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2025
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe de mesure . 2
5 Facteurs influençant la précision de mesure . 2
5.1 Revêtements de type A: nickel sur un substrat magnétique .2
5.1.1 Propriétés magnétiques du métal de base .2
5.1.2 Épaisseur du métal de base .3
5.1.3 Sens d’usinage du métal de base .3
5.1.4 Magnétisme résiduel .3
5.2 Revêtements de type B: nickel sur un substrat non magnétique, revêtement au dos du
substrat .3
5.3 Revêtements de types A et B .3
5.3.1 Épaisseur du revêtement .3
5.3.2 Effets de bord .3
5.3.3 Courbure .3
5.3.4 Rugosité de surface .4
5.3.5 Champs magnétiques .4
5.3.6 Particules étrangères .4
5.3.7 Propriétés magnétiques du revêtement .4
5.3.8 Pression et orientation du palpeur .4
5.3.9 Épaisseur du matériau de base .4
6 Étalonnage des instruments. 4
6.1 Généralités .4
6.2 Étalons .5
7 Mode opératoire . 5
7.1 Généralités .5
7.2 Épaisseur du métal de base (revêtements de type A seulement) .5
7.3 Sens d’usinage (revêtements de type A seulement) .5
7.4 Effets de bord .5
7.5 Courbure .5
7.6 Nombre de lectures .6
7.7 Magnétisme résiduel (revêtements de type A) .6
7.8 Propreté de la surface .6
7.9 Techniques .6
7.10 Positionnement du palpeur .6
7.11 Mesurage sur des surfaces chaudes . .6
7.12 Mesurage sous l’eau .7
8 Exigences relatives à la précision . 7
9 Rapport d’essai . 7
Bibliographie . 8

iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de brevet.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/iso/fr/avant-propos.html.
Le présent document a été élaboré par le comité technique ISO/TC 107, Revêtements métalliques et autres
revêtements inorganiques, en collaboration avec le comité technique CEN/TC 262, Revêtements métalliques
et inorganiques, incluant ceux pour la protection contre la corrosion et les essais de corrosion des métaux et
alliages, du Comité européen de normalisation (CEN), conformément à l’accord de coopération technique
entre l’ISO et le CEN (Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 2361:1982), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— les méthodes de mesure du nickel ont été divisées en type A, type B et types A et B;
— des plages de mesure habituelles ont été ajoutées pour chaque méthode;
— des paragraphes sur les facteurs qui influencent l’incertitude de mesure ont été ajoutés;
— la norme a été restructurée et divisée en articles et paragraphes;
— l’Article 9 concernant le rapport d’essai a été ajouté;
— des modifications éditoriales ont été apportées.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
Norme internationale ISO 2361:2025(fr)
Revêtements électrolytiques de nickel sur substrat
magnétique et non magnétique — Mesurage de l’épaisseur du
revêtement — Méthode magnétique
1 Domaine d’application
Le présent document spécifie une méthode de mesurage non destructif de l’épaisseur des revêtements
électrolytiques de nickel de type magnétique, également appelés «e-nickel», sur substrat magnétique ou non
magnétique.
Il est possible que la méthode ne soit pas applicable à des revêtements autocatalytiques de nickel (nickelage
chimique), car ces revêtements sont souvent non magnétiques du fait de leur composition chimique.
Pour les besoins du présent document, on distingue deux types de substrats:
a) les revêtements de nickel sur substrat magnétique (revêtements de type A);
b) les revêtements de nickel sur substrat non magnétique (revêtements de type B).
Tous les instruments ne peuvent pas être utilisés sur les deux types de revêtements.
Les instruments basés sur le principe de l’attraction magnétique ont une plage de mesure efficace allant
jusqu’à 50 µm dans le cas de revêtements de type A et allant jusqu’à 25 µm pour les revêtements de type B.
Pour les instruments utilisant le principe de réluctance, la plage de mesure efficace est bien supérieure,
jusqu’à 1 mm ou même plus. La présente méthode est applicable aux deux types de revêtements.
2 Références n
...