kSIST prEN ISO 13585:2023
(Main)Brazing - Qualification testing of brazers and brazing operators (ISO 13585:2021)
Brazing - Qualification testing of brazers and brazing operators (ISO 13585:2021)
This document specifies requirements for qualification testing of brazers and brazing operators for metallic materials.
This document gives general provisions on quality requirements for brazing (see Annex A).
This document applies to the following brazing processes according to ISO 857-2 and ISO 4063:2009 with local and global heating:
— 911 Infrared brazing;
— 912 Flame brazing, torch brazing;
— 913 Laser beam brazing;
— 914 Electron beam brazing;
— 916 Induction brazing;
— 918 Resistance brazing;
— 919 Diffusion brazing;
— 921 Furnace brazing;
— 922 Vacuum brazing;
— 923 Dip-bath brazing;
— 924 Salt-bath brazing;
— 925 Flux bath brazing;
— 926 Immersion brazing;
— 972 Arc weld brazing.
This document is not applicable to personnel operating brazing equipment who do not have any direct influence on the quality of the brazed joint, for example, personnel performing exclusively loading/unloading the brazing unit or just initiating the brazing cycle in automatic brazing.
The principles of this document can be applied to other brazing processes and brazing of materials not listed.
This document does not apply to brazing for aerospace applications covered by ISO 11745.
Hartlöten - Prüfung von Hartlötern und Bedienern von Hartlöteinrichtungen (ISO 13585:2021)
Brasage fort - Essais de qualification des braseurs et des opérateurs braseurs en brasage fort (ISO 13585:2021)
Trdo spajkanje - Preskušanje za kvalifikacijo spajkalcev in operaterjev (ISO 13585:2021)
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
oSIST prEN ISO 13585:2023
01-januar-2023
Trdo spajkanje - Preskušanje usposobljenosti spajkalcev in upravljavcev (ISO
13585:2021)
Brazing - Qualification testing of brazers and brazing operators (ISO 13585:2021)
Hartlöten - Prüfung von Hartlötern und Bedienern von Hartlöteinrichtungen (ISO
13585:2021)
Brasage fort - Essais de qualification des braseurs et des opérateurs braseurs en
brasage fort (ISO 13585:2021)
Ta slovenski standard je istoveten z: prEN ISO 13585
ICS:
03.100.30 Vodenje ljudi Management of human
resources
25.160.50 Trdo in mehko lotanje Brazing and soldering
oSIST prEN ISO 13585:2023 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
oSIST prEN ISO 13585:2023
---------------------- Page: 2 ----------------------
oSIST prEN ISO 13585:2023
INTERNATIONAL ISO
STANDARD 13585
Second edition
2021-12
Brazing — Qualification testing of
brazers and brazing operators
Brasage fort — Essais de qualification des braseurs et des opérateurs
braseurs en brasage fort
Reference number
ISO 13585:2021(E)
© ISO 2021
---------------------- Page: 3 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2021
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
© ISO 2021 – All rights reserved
---------------------- Page: 4 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Symbols and abbreviated terms.3
5 Essential variables and range of qualification . 4
5.1 General . 4
5.2 Brazing process. 5
5.3 Brazer qualification . 5
5.3.1 Product type . 5
5.3.2 Type of joint . 5
5.3.3 Parent material group(s) . 5
5.3.4 Filler metals and brazing filler application . 6
5.3.5 Dimensions . 6
5.3.6 Filler metal flow direction . 7
5.4 Brazing operator qualification . 7
5.4.1 Type of equipment . . 7
5.4.2 Filler metals and brazing filler application . 7
6 Examination and testing . 7
6.1 Supervision . 7
6.2 Brazing conditions . 8
6.3 Test piece . 8
6.4 Assessment of work pieces . 8
6.5 Extent of testing . 8
6.6 Visual testing . 8
6.7 Non-destructive testing . 9
6.8 Destructive testing . 9
6.9 Additional examination and testing . 9
7 Acceptance requirements for test pieces . 9
8 Re-tests. 9
9 Period of validity .10
9.1 Initial qualification . 10
9.2 Prolongation . 10
10 Certificate .10
11 Designation .11
Annex A (informative) Quality requirements for brazing .12
Annex B (informative) Brazer qualification test certificate .13
Annex C (informative) Brazing operator qualification test certificate .15
Annex D (informative) Other non-essential variables .16
Annex E (normative) Material grouping system .17
Annex F (informative) Examples of test pieces.19
Bibliography .21
iii
© ISO 2021 – All rights reserved
---------------------- Page: 5 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 44, Welding and allied processes
Subcommittee SC 11, Qualification requirements for welding and allied processes personnel.
This second edition cancels and replaces the first edition (ISO 13585:2012), which has been technically
revised.
The main changes compared to the previous edition are as follows:
— brazing processes, in accordance with ISO 4063:2009, covered by this document, have been moved
to the scope;
— Clause 3 has been updated and additional terms have been defined;
— additional symbols and abbreviated terms have been added to Clause 4;
— Clause 5 has been significantly revised and updated including clarifications on brazing operator
qualification;
— material grouping has been moved to new Annex E;
— Clause 6 has been updated to refer to ISO or technically equivalent standards;
— the period of validity and prolongation of qualifications has been revised to 5 years in Clause 9.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
Official interpretations of ISO/TC 44 documents, where they exist, are available from this page:
https://committee.iso.org/sites/tc44/home/interpretation.html.
iv
© ISO 2021 – All rights reserved
---------------------- Page: 6 ----------------------
oSIST prEN ISO 13585:2023
INTERNATIONAL STANDARD ISO 13585:2021(E)
Brazing — Qualification testing of brazers and brazing
operators
1 Scope
This document specifies requirements for qualification testing of brazers and brazing operators for
metallic materials.
This document gives general provisions on quality requirements for brazing (see Annex A).
This document applies to the following brazing processes according to ISO 857-2 and ISO 4063:2009
with local and global heating:
— 911 Infrared brazing;
— 912 Flame brazing, torch brazing;
— 913 Laser beam brazing;
— 914 Electron beam brazing;
— 916 Induction brazing;
— 918 Resistance brazing;
— 919 Diffusion brazing;
— 921 Furnace brazing;
— 922 Vacuum brazing;
— 923 Dip-bath brazing;
— 924 Salt-bath brazing;
— 925 Flux bath brazing;
— 926 Immersion brazing;
— 972 Arc weld brazing.
This document is not applicable to personnel operating brazing equipment who do not have any direct
influence on the quality of the brazed joint, for example, personnel performing exclusively loading/
unloading the brazing unit or just initiating the brazing cycle in automatic brazing.
The principles of this document can be applied to other brazing processes and brazing of materials not
listed.
This document does not apply to brazing for aerospace applications covered by ISO 11745.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 857-2, Welding and allied processes — Vocabulary — Part 2: Soldering and brazing processes and
related terms
1
© ISO 2021 – All rights reserved
---------------------- Page: 7 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
ISO 4063:2009, Welding and allied processes — Nomenclature of processes and reference numbers
ISO 17672, Brazing — Filler metals
ISO 17779, Brazing — Specification and qualification of brazing procedures for metallic materials
ISO 18279:2003, Brazing — Imperfections in brazed joints
ISO/TR 25901-1, Welding and allied processes — Vocabulary — Part 1: General terms
EN 12797, Brazing — Destructive tests of brazed joints
EN 12799, Brazing — Non-destructive examination of brazed joints
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 857-2, ISO/TR 25901-1 and
the following apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
brazing
joining process using filler metal (3.12) with a liquidus temperature above 450 °C
[SOURCE: ISO 857-2:2005, 3.1.2.]
3.2
brazer
person who holds and manipulates the device for heating the brazing area by hand
Note 1 to entry: The brazer verifies compliance with the pBPS or BPS prior to and during brazing.
3.3
brazing operator
person who controls or adjusts brazing parameters for mechanized brazing (3.5) or sets up brazing
parameters for automatic brazing (3.6)
Note 1 to entry: The brazing operator verifies compliance with the pBPS or BPS prior to and during the brazing
cycle.
3.4
manual brazing
brazing (3.1) where the required brazing conditions are maintained by hand
3.5
mechanized brazing
brazing (3.1) where the required brazing conditions are maintained by mechanical or electronic means
but can be manually varied during the process
3.6
automatic brazing
brazing (3.1) in which all operations are performed without brazing operator (3.3) intervention during
the process
Note 1 to entry: Manual adjustment of brazing variables by the brazing operator during brazing is not possible.
2
© ISO 2021 – All rights reserved
---------------------- Page: 8 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
3.7
brazing procedure specification
BPS
document that has been qualified and provides the required variables of the brazing procedure to
ensure repeatability during production brazing
3.8
preliminary brazing procedure specification
pBPS
document containing the required variables of the brazing procedure which is not yet qualified
3.9
manufacturer
workshop or site (or both) which is (are) under the same technical and quality management
3.10
examiner
person who has been appointed to verify compliance with the applicable standard
Note 1 to entry: In certain cases, an external independent examiner can be required.
[SOURCE: ISO/TR 25901-1:2016, 2.5.29]
3.11
examining body
organization that has been appointed to verify compliance with the applicable standard
Note 1 to entry: In certain cases, an external independent examining body can be required.
[SOURCE: ISO/TR 25901-1:2016, 2.5.30]
3.12
filler metal
added metal applied to brazed joints
Note 1 to entry: Filler metal can be in the form of wire, inserts, powder, pastes, foil, etc.
3.13
flux
non-metallic material which, when molten, promotes wetting by removing existing oxide or other
detrimental films from the surfaces to be joined and prevents their re-formation during the joining
operation
[SOURCE: ISO 857-2:2005, 3.2.2]
3.14
test piece
brazed assembly which is used for testing purposes
3.15
test specimen
part or portion cut from the test piece (3.14) in order to perform specified destructive testing
[SOURCE: ISO/TR 25901-1:2016, 2.2.1.6]
4 Symbols and abbreviated terms
t material thickness
L overlap length
3
© ISO 2021 – All rights reserved
---------------------- Page: 9 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
D outside pipe diameter
T product type pipe
P product type plate
BJ butt joint
LJ lap joint
TJ T-joint
FF face fed
PP pre-placed
H horizontal flow
VU vertical up flow
VD vertical down flow
Where the full wording is not used, the symbols listed above and brazing process reference numbers in
Clause 1 shall be used when completing the qualification test certificate (see Annexes B and C).
5 Essential variables and range of qualification
5.1 General
The qualification of brazers, (see 5.3) and brazing operators, (see 5.4) is based on essential variables
in accordance with Table 1. For each essential variable, a range of qualification is defined and brazing
outside that range of qualification requires a new qualification test.
Table 1 — Essential variables for brazer and brazing operator qualification
Essential variable Brazer Brazing operator
Brazing process number X X
in accordance with ISO 4063:2009
Product type: T or P X —
Type of joint: BJ, LJ or TJ X —
Parent material group(s) X —
in accordance with Annex E
Brazing filler metal classification X —
in accordance with ISO 17672
Brazing filler application, FF or PP X X
Dimensions: t, D, L X —
Filler metal flow direction: H, VU X —
or VD
Type of equipment — X
NOTE There can be other variables that the manufacturer deems to be essential in certain applications,
e.g. constraint on access for the torch, purging gas, etc., which need separate qualification (see Annex D).
The brazer or brazing operator who undertakes the brazing procedure test satisfactorily in accordance
with this document is qualified provided that the relevant testing requirements of this document are
met.
4
© ISO 2021 – All rights reserved
---------------------- Page: 10 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
5.2 Brazing process
Each qualification test qualifies only one brazing process (see Clause 1). A change of brazing process
requires a new qualification test.
When applicable, the furnace atmosphere is limited to the same type of atmosphere, e.g. reducing or
inert, carburizing or decarburizing, and hydrogen or disassociated ammonia, as used in the test.
For brazing processes where fuel gases apply, the qualification is limited to the same type of fuel gas
and flame as used in the test.
5.3 Brazer qualification
5.3.1 Product type
Manual brazing of one product type qualifies for other product types in accordance with Table 2.
Table 2 — Range of qualification for product type
Dimensions in millimetres
Product type for test piece Range of qualification
Plate Plate and pipe
Pipe D ≤ 100 Pipe
Pipe D > 100 Pipe and plate
5.3.2 Type of joint
Range of qualification for type of joint is given by Table 3.
Table 3 — Range of qualification for type of joint
Type of joint in test piece Range of qualification
Butt joint Butt joint
Lap joint Lap joint
T-joint T-joint
5.3.3 Parent material group(s)
In order to minimize the number of brazer qualification tests, parent materials are assigned to
M-number groupings (see Annex E).
The parent material used in the brazer qualification test qualifies the brazer for brazing of all other
parent materials within the same M-number grouping (see Table 4).
Parent materials that do not appear in Annex E, require separate qualification and only qualify that
material.
5
© ISO 2021 – All rights reserved
---------------------- Page: 11 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
Table 4 — Range of qualification for parent material
Test piece material
a,b
Range of qualification
(see Annex E)
100, 110, 120, 170 100, 110, 120, 170
130, 140, 150, 160, 180 130, 140, 150, 160, 180
200, 210, 220 200, 210, 220
300, 310, 320, 330, 340, 350, 360 300, 310, 320, 330, 340, 350, 360
400, 410, 420, 430 400, 410, 420, 430
500 500
600 600
700 700
800 800
a
For a test piece material used for brazer qualification, the brazer is qualified to braze all
materials and all combinations of materials given in the same row.
b
When test piece material from two rows are used for brazer qualification, the brazer is qualified
to braze all material combinations in each row and combinations between those rows.
5.3.4 Filler metals and brazing filler application
The brazing filler metal type, based on its class in accordance with ISO 17672 or other standards that
provide equivalent technical conditions, qualifies other filler metal types within the same class.
One filler metal form (for example from preformed ring to paste) only qualifies for the same form.
A test with a flux classified in accordance with ISO 18496, or other standards that provide equivalent
technical conditions, only qualifies for brazing within that same classification.
The brazing filler metal application qualifies for other filler metal applications in accordance with
Table 5.
Table 5 — Range of qualification for brazing filler application
Test piece brazing filler application Range of qualification
Face fed Face fed, Pre-placed
Pre-placed Pre-placed
NOTE Face fed”, also known as “applied to the mouth of the joint”, can be manually or mechanically
fed while brazing.
5.3.5 Dimensions
The brazer qualification test of brazed joints is based on the material thickness, outside pipe diameter
and overlap length. The ranges of qualification are specified in Table 6.
For dissimilar material thicknesses of test pieces, the range of qualification is based on the thickness of
each plate (or pipe).
It is not intended that material thicknesses or outside pipe diameters should be measured precisely, but
rather the general philosophy behind the values given in Table 6 should be applied.
For test pieces of different outside pipe diameters and parent material thicknesses, the brazer is
qualified to:
— the larger diameter and below (see Table 6);
— twice the larger parent material thickness and below (see Table 6).
6
© ISO 2021 – All rights reserved
---------------------- Page: 12 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
Table 6 — Range of qualification for dimensions
Dimensions Test piece Range of qualification
Material thickness, t (mm) t ≤2t
a
Outside pipe diameter, D (mm) D ≤D
a
Overlap length, L (mm) L ≤1,25L
NOTE If material thicknesses differ (see Figure F.5), the lower limit is based on the thinnest and the
upper limit is based on the thickest thickness.
a
If applicable.
5.3.6 Filler metal flow direction
The brazing of one filler metal flow direction qualifies for other flow directions in accordance with
Table 7.
For personnel qualification, an angular deviation of maximum ±15° from filler metal flow positions
applies.
Table 7 — Range of qualification for filler metal flow direction
Filler metal flow direction
Illustrations Range of qualification
of the test piece
Horizontal flow and
Horizontal flow
vertical down-flow
Vertical down-flow Vertical down-flow
Vertical up-flow All flow directions
5.4 Brazing operator qualification
5.4.1 Type of equipment
If mechanized or automatic brazing is used for the test, the range of qualification is limited to the
brazing process and type of equipment only (see 6.2).
5.4.2 Filler metals and brazing filler application
If mechanized or automatic brazing is used for the test, the range of qualification is limited to the
method of brazing filler application in accordance with Table 5.
6 Examination and testing
6.1 Supervision
The brazing of test pieces shall be witnessed by the examiner or examining body. The testing shall be
verified by the examiner or examining body.
The test pieces shall be marked with the identification of the examiner and the brazer before brazing
starts.
7
© ISO 2021 – All rights reserved
---------------------- Page: 13 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
The examiner or examining body may stop the test if the brazing conditions are not correct or if it
appears that the brazer or brazing operator does not have the skill to fulfil the requirements.
6.2 Brazing conditions
The qualification test of brazers and brazing operators shall follow a pBPS or BPS prepared in
accordance with ISO 17779. The brazing time for the test piece shall correspond to the working time
under usual production conditions.
The brazer or brazing operator shall prepare the parts (e.g. mechanical preparation, cleaning) or accept
the preparation, set up the heating means and conduct the necessary verification to carry out the test in
accordance with the pBPS or BPS.
NOTE It can be of value to otherwise imitate production conditions for the qualification test as far as
possible.
6.3 Test piece
The test piece may be any design of joint which is relevant to the end work. Typically, this is a basic lap
or butt joint in sheet material or a sleeve joint in tube (for examples of applicable joint configurations,
see Annex F).
NOTE It is possible that requirements concerning test piece design are given in the applicable product
standard.
6.4 Assessment of work pieces
When assembling the test piece, the brazer or brazing operator:
— shall assess the work pieces for:
a) joint fit up;
b) joint gap;
c) degree or absence of local deformation; and
— is permitted to refuse the test piece components if the brazer or brazing operator considers that
these are not in accordance with the written pBPS or BPS.
6.5 Extent of testing
Each test piece shall be tested by visual testing and one or more of the following tests:
a) ultrasonic test;
b) radiographic test;
c) peel test;
d) macroscopic examination;
e) bend test.
6.6 Visual testing
All joints shall be visually examined [see Annex A, item j)] in accordance with EN 12799 or technically
equivalent standards. It can be necessary to cut open the brazed assembly to offer an internal
examination. Therefore, the test may be destructive.
8
© ISO 2021 – All rights reserved
---------------------- Page: 14 ----------------------
oSIST prEN ISO 13585:2023
ISO 13585:2021(E)
6.7 Non-destructive testing
Any non-destructive testing performed shall be carried out in accordance with EN 12799 or technically
equivalent standards.
6.8 Destructive testing
Any destructive testing performed shall be carried out in accordance with EN 12797 or technically
equivalent standards. The details of testing procedure and test specimen shall be established before
any testing is undertaken.
6.9 Additional examination and testing
Additional testing may be carried out as appropriate or as agreed:
— non-destructive test methods, for example:
a) penetrant testing;
b) leak testing
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.